TW522143B - Method of manufacturing ceramic pot - Google Patents

Abstract

A method of manufacturing ceramic pot comprises grinding zirconium oxide and heat resistant ceramic glazing reagent batchwise to form a mixture; spraying the glazing mixture to the surface of a green pot; and firing the green pot in a kiln at 1200 DEG C or higher for 16 hours to form a product. The surface of the pot thus made is free from scratching, peeling off and sticking after frying or cooking for a long time.

Description

522143 A7 B7 V. Description of the invention (/) The pot body (commonly known as non-stick pot) of the horses currently on the market, because of the emphasis on the surface / face and surface of the pot, the use of M and boiled rice, high temperature resistance, The cooking of food * will not be affected by the oil and will cause a state of dipping the pan. Therefore, the pan is popular among consumers after it is on the market. However, in order to achieve the above-mentioned advantages of today's pot pans, Yu Zhishi uses a stack of unsaturated plastic fats and organic materials, 1 «on the silk surface, and finally applies BM to dry, Μ Ma becomes a pot The surface of the body is smooth and smooth. Ft. During the conventional manufacturing process (such as the first one), the organic materials will produce micro-toxic artifacts as soon as they are used. After long-term use in the pot body, the The surface is split or detached, and even scratches are generated. For consumers, not only is the pot body almost the same as other pot bodies, the food in the cooking process is also affected by the falling off of the surface. Environmental protection. In view of the aforementioned lack of knowledge, the inventor has engaged in many years of experience, and Huishu has sincerely improved it. Finally, a "manufacturing method of the pottery pot body" was invented, so that after the formation of the porcelain tungsten body, not only was the cooking process performed. Alas, the surface is still finished! At the same time, it can be used for a long time and is very environmentally friendly, which is the main purpose of the present invention. According to the ceramic pot body made according to the present invention, the manufacturing process is to first use zirconia (ZRO) thermal ceramic glaze to grind in batches to form a mixed steel, and then print it by the Consumer Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs ---- ------- (Please read the precautions on the back before filling in this page) f _ Glaze is applied to the surface rate of the ceramic weave, and the formation is sent to the kiln Μ1200PM for 16 hours to become one Finished product to achieve the expected effect of the true frontal. In order to make the Junju reviewing committee _ truly understand that the present invention is to achieve the former purpose, the manufacturing process and operating technical methods are required. The following formulas and figures are detailed below: This paper size applies Chinese national standards ( CNS) A4 specification (210X297 mm) 522143 Printed by the Consumer Cooperatives of the Central Standards Bureau of the Ministry of Economic Affairs A7 B7 V. Description of the invention (>) [Schematic representation] The first diagram is a flow chart of the method for making ceramic silk for the piano . The second figure is a flowchart of a method for manufacturing a porcelain pot according to the present invention. 0 [Illustration of drawing number] (1 > Zirconia (2) Heat-resistant ceramic _ glaze medicine U) Ceramic pot bad body (4) Glazing and glazing "5 ) Kiln (6) over 120010 calcined (7) finished product According to the present invention, the ceramic pot body, M finished product (7) is shown, please refer to the second picture, in which: zirconium oxide (ZRO) 30% is selected first (1) Grinding with 70% (2) heat-resistant ceramic glaze in batches to form a mixture, which is pre-constructed and converted into a ceramic pot bad body (3), spray the mixture and glaze (4) on the ceramic On the surface of the pot bad body (3), it is then sent to the kiln (5) in a bismuth at 12001C K for 16 hours, to form a ceramic pot body finished product (t). Its front heat-resistant ceramic glaze (2 > is composed of special feldspar 68-60%, zinc oxide 1-2%, barium carbonate 0.5-1.5¾, oxide name 6-8¾, silicon oxide 10-12.5¾, magnesium oxide 2- 4¾, Calcium oxide 1-23 :, iron oxide 0Μ3ί, chromium oxide 0-2: ¾, manganese oxide 0-2¾, and oxide, cobalt 0-2¾. The bad body of the pottery deaf pot (3) is made of ceramic clay. 30-35%, special feldspar 44.5-40¾, alumina 6-8¾, magnesia oxide 3%, oxidized sand 10.2-13.2¾, and iron oxide 0.3-0.8¾. The finished product (7) is formed at During the 16 hours of calcination on the Μ, the temperature is stable, and the spray glaze and glaze (4) mixture can be completely compatible with the ceramic pot. The paper size applies the Chinese National Standard (CNS) Α4 specification (210X297 mm) ------ ----- (Please read the notes on the back before filling in this page) Order 522143 Α7 Β7 V. Description of the invention (λ) (3) Fusion, after the finished product (7) is made, its surface is quite smooth 4 Do not need to apply K surface treatment. Under high temperature resistance, it can be used for a long time without scratches or falling on the surface. To sum up According to the invention, the manufacturing method of the front stab used in the present invention, and the ceramic pot body formed does not injure the surface when in use, and at the same time has a guarantee, which fully meets the application requirements of the invention patent. Patent Application _ Panjun Bureau has granted this invention patent early. ----------- (Please read the precautions on the back before filling out this page) ^ 11 Printed by the Consumer Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs This paper size applies to China National Standard (CNS) Α4 specification (210 × 297 mm)

Claims (1)

522143 '1 1 申请, patent application Fanzhan-a "a method of manufacturing ceramic pot", which includes the use of zirconium oxide (ZR0) 30! «And heat-resistant ceramic glaze 70¾ batch grinding to form a mixture, With a ceramic pot body, spray glaze and apply glaze on the surface, and send the ceramic pot body into the kiln and calcined at 1200 TCM for 16 hours to become a finished product, which is a feature of its manufacturing method. 2. As described in the "Method of Manufacturing Ceramic Pot" described in item 1 of the scope of the patent application, the heat-resistant ceramic glaze is made of special feldspar 68-60¾, zinc oxide 1-2! «, Barium carbonate 0 · 5-1 · 5%, alumina 6-8 »;, silicon oxide 10-12.5¾, magnesium oxide, calcium oxide 1-2%, iron oxide 0-«, chromium oxide 0-2S !, manganese oxide 0-2¾, cobalt oxide 0 -2S: Combined. 3. As described in the "Method for Manufacturing Ceramic Carcass" as described in item 1 of the scope of the patent application, the ceramic pot failure system consists of ceramic clay 30-35%, special feldspar 44.5-40¾, alumina 6-8 »:, oxidation Magnesium 1-3¾, silicon oxide 10.2-1.32 8 :, iron oxide 0.3-0.8¾. ---------- (Please read the notes on the back before filling out this page) -Order—, 1 · The paper size printed by the Staff Consumer Cooperative of the Central Standards Bureau of the Ministry of Economic Affairs applies to Chinese National Standards (CNS) Α4 Specifications (210 × 297 mm)