US20070140891A1 - Process for the preparation of semiconducting ceramics composed of metal oxides, in particular of tin oxide, especially for varistors - Google Patents

Process for the preparation of semiconducting ceramics composed of metal oxides, in particular of tin oxide, especially for varistors Download PDF

Info

Publication number
US20070140891A1
US20070140891A1 US11/541,562 US54156206A US2007140891A1 US 20070140891 A1 US20070140891 A1 US 20070140891A1 US 54156206 A US54156206 A US 54156206A US 2007140891 A1 US2007140891 A1 US 2007140891A1
Authority
US
United States
Prior art keywords
oxide
process according
powder
weight
oxides
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/541,562
Other languages
English (en)
Inventor
Mehrdad Hassanzadeh
Celine Machado-Bailly
Renaud Metz
Ramon Puyane
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Grid Solutions SAS
Original Assignee
Areva T&D SAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Areva T&D SAS filed Critical Areva T&D SAS
Priority to US11/541,562 priority Critical patent/US20070140891A1/en
Publication of US20070140891A1 publication Critical patent/US20070140891A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/453—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on zinc, tin, or bismuth oxides or solid solutions thereof with other oxides, e.g. zincates, stannates or bismuthates
    • C04B35/457—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on zinc, tin, or bismuth oxides or solid solutions thereof with other oxides, e.g. zincates, stannates or bismuthates based on tin oxides or stannates
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B13/00—Oxygen; Ozone; Oxides or hydroxides in general
    • C01B13/14—Methods for preparing oxides or hydroxides in general
    • C01B13/32—Methods for preparing oxides or hydroxides in general by oxidation or hydrolysis of elements or compounds in the liquid or solid state or in non-aqueous solution, e.g. sol-gel process
    • C01B13/322—Methods for preparing oxides or hydroxides in general by oxidation or hydrolysis of elements or compounds in the liquid or solid state or in non-aqueous solution, e.g. sol-gel process of elements or compounds in the solid state
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/62605—Treating the starting powders individually or as mixtures
    • C04B35/62645—Thermal treatment of powders or mixtures thereof other than sintering
    • C04B35/6265—Thermal treatment of powders or mixtures thereof other than sintering involving reduction or oxidation
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/62605—Treating the starting powders individually or as mixtures
    • C04B35/62645—Thermal treatment of powders or mixtures thereof other than sintering
    • C04B35/62665—Flame, plasma or melting treatment
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/62605—Treating the starting powders individually or as mixtures
    • C04B35/62645—Thermal treatment of powders or mixtures thereof other than sintering
    • C04B35/6268—Thermal treatment of powders or mixtures thereof other than sintering characterised by the applied pressure or type of atmosphere, e.g. in vacuum, hydrogen or a specific oxygen pressure
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/628—Coating the powders or the macroscopic reinforcing agents
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/628—Coating the powders or the macroscopic reinforcing agents
    • C04B35/62802—Powder coating materials
    • C04B35/62805—Oxide ceramics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/653—Processes involving a melting step
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01C—RESISTORS
    • H01C17/00—Apparatus or processes specially adapted for manufacturing resistors
    • H01C17/06—Apparatus or processes specially adapted for manufacturing resistors adapted for coating resistive material on a base
    • H01C17/065—Apparatus or processes specially adapted for manufacturing resistors adapted for coating resistive material on a base by thick film techniques, e.g. serigraphy
    • H01C17/06506—Precursor compositions therefor, e.g. pastes, inks, glass frits or green body
    • H01C17/06513—Precursor compositions therefor, e.g. pastes, inks, glass frits or green body characterised by the resistive component
    • H01C17/06533—Precursor compositions therefor, e.g. pastes, inks, glass frits or green body characterised by the resistive component composed of oxides
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01C—RESISTORS
    • H01C7/00—Non-adjustable resistors formed as one or more layers or coatings; Non-adjustable resistors made from powdered conducting material or powdered semi-conducting material with or without insulating material
    • H01C7/10—Non-adjustable resistors formed as one or more layers or coatings; Non-adjustable resistors made from powdered conducting material or powdered semi-conducting material with or without insulating material voltage responsive, i.e. varistors
    • H01C7/105—Varistor cores
    • H01C7/108—Metal oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3241—Chromium oxides, chromates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3251—Niobium oxides, niobates, tantalum oxides, tantalates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3262—Manganese oxides, manganates, rhenium oxides or oxide-forming salts thereof, e.g. MnO
    • C04B2235/3267—MnO2
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/327—Iron group oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3275—Cobalt oxides, cobaltates or cobaltites or oxide forming salts thereof, e.g. bismuth cobaltate, zinc cobaltite
    • C04B2235/3277—Co3O4
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/404—Refractory metals
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/405—Iron group metals
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5436—Particle size related information expressed by the size of the particles or aggregates thereof micrometer sized, i.e. from 1 to 100 micron
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/77—Density
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance

Definitions

  • the invention relates to a process for the preparation of semiconducting ceramics composed of metal oxides, more specifically of semiconducting ceramics, composed of one or more base metal oxides, such as tin oxide SnO 2 and of one or more doping metal oxides.
  • Such semiconducting ceramics are used in particular to manufacture resistors which are nonlinear as a function of the voltage and in particular varistors, which are used, for example, in low-, medium- and high-voltage lightning arresters or voltage-limiting components associated, for example, with an item of electrical or electronic equipment.
  • the technical field of the invention can thus be defined very generally as that of ceramics based on metal oxides and of their preparation and more particularly as that of ceramics exhibiting a resistance which is nonlinear as a function of the voltage, such as varistors.
  • Resistors which are nonlinear as a function of the voltage such as varistors, based on silicon carbide, selenium rectifiers and p-n junction diodes made of silicon or germanium, have been widely used for the voltage stabilization of electrical circuits or the suppression of normally high overvoltages induced in electrical circuits.
  • resistors are essentially composed of sintered bodies of zinc oxide ZnO optionally comprising one or more additives or doping agents chosen, for example, from metal oxides.
  • the documents FR-A-2 174 174, FR-A-2 174 175, FR-A-2 174 176 and FR-A-2 194 026 disclose varistors formed of a sintered body essentially composed of ZnO with, as additives, Bi 2 O 3 , Sb 2 O 3 and Co 3 O 4 .
  • JP-A-49 105196 (1974) discloses an improvement in the electrical properties of varistors made of ZnO by doping a mixture of ZnO, NiO 2 , BaO and TiO 2 with 1 mol % of SnO 2 ; this mixture is subsequently compacted and sintered at 1350° C. in air.
  • JP-A-48 099695 (1973) and JP-A-49 041897 (1974) provide formulations which can be expressed, for example, by: Bi 2 O 3 7 parts; (ZnO) 0.87 (SnO 2 ) 0.12 (YF 3 ) 0.01 100 parts, and which make it possible to achieve electrical characteristics of varistors which are highly varied, simply by modifying the Bi 2 O 3 content.
  • compositions for varistors predominantly based on SnO 2 instead of ZnO comprise SnO 2 (up to 70 mol %), ZnO and Sb 2 O 3 doped with Bi 2 O 3 , V 2 O 5 , Nb 2 O 5 , Cr 2 O 3 or Mn 2 O 3 .
  • compositions make it possible to obtain high nonlinearity coefficients, the maximum value indicated for the latter being 30.
  • compositions for varistors based on SnO 2 are disclosed in the documents JP-A-49 129192 (1974) and JP-A-49 129193 (1974). These compositions are defined generally by the following compositions as mol %: 40 to 99.85 of SnO 2 , 0.05 to 30 of Sb 2 O 3 and 0.1 to 50 mol % of CoO.
  • the ceramics prepared from a mixture composed of 99.9 mol % of SnO 2 , 0.05 mol % of Sb 2 O 3 and 0.05 mol % of Bi 2 O 3 or from a mixture composed of 99.85 mol % of SnO 2 , 0.05 mol % of Sb 2 O 3 and 0.1 mol % of CoO, compacted and sintered, have electrical properties of varistors which are relatively mediocre, with ⁇ and V s values respectively of less than 10 and 25 V.
  • varistors based on SnO 2 have only really taken off since 1995, with the studies mentioned in the paper by S. A. Pianaro, P. R. Bueno, E. Longo and J. A. Varela, “A new SnO 2 -based varistor system”, which describes in particular a varistor composition comprising, as mol %: 98.9% of SnO 2 , 1% of CoO, 0.05% of Nb 2 O 5 and 0.05% of Cr 2 O 3 .
  • This composition exhibits advantageous electrical properties, in particular a nonlinearity coefficient ⁇ of 41 and a maximum electrical field before breakdown E s of 400 V/mm, which are associated with monophase structures, the grain boundaries of which are apparently devoid of precipitated phases.
  • the document BR-A-96 00174-7 discloses metal oxide compositions for varistors composed essentially of tin oxide (SnO 2 ) doped with various metal oxides, such as cobalt oxide and niobium oxide.
  • a typical composition comprises from 97.5 to 99.45% of tin dioxide (SnO 2 ), from 0.5 to 2.0% of cobalt oxide (CoO) and from 0.05 to 0.3% of niobium oxide (Nb 2 O 5 ). These compositions are subsequently subjected to sintering at a temperature of 1300 to 1350° C. to give a ceramic.
  • the semiconducting ceramic materials for semiconducting ceramic pellets or varistors used for protecting from overvoltages are generally prepared from their constituent oxides in the pulverulent form.
  • the semiconducting ceramic materials most widely used at the moment are prepared from pulverulent oxides composed of the predominant oxide, which is ZnO, and doping oxides, such as nickel, chromium, manganese, magnesium, bismuth, antimony, silicon or cobalt oxides, and the like.
  • the conventional chemical processes for the preparation of ceramic materials thus consists in weighing the constituent oxides, in mixing them and in milling them, and in then forming a mixture in an aqueous medium in order to obtain a slip.
  • This slip is atomized and dried (spray drying) to form agglomerates of a few hundred microns, which are subsequently shaped by pressing and then sintered at high temperature.
  • metal electrodes are deposited and the component is coated, on its other surfaces, with a material which provides electrical insulation and physicochemical and mechanical protection.
  • the PADO process is disclosed in the document FR-A-2 674 157 and, with some variations in comparison with the document FR-A-2 674 157, in the document EP-A1-0 580 912 and in the document U.S. Pat. No. 5,322,642.
  • the base components or starting materials for producing the powder intended to give the semiconducting ceramic are no longer metal oxides but alloys or mixtures of metals which are only subsequently oxidized, either in the solid phase or in the liquid phase or in the vapour phase.
  • the PADO process disclosed, for example, in the document FR-A-2 674 157, comprises the following successive steps:
  • the ingot obtained can be reduced to a powder by milling or to chips by machining, so that the ingot, the powder or the chips can be left under an appropriate atmosphere for the purpose of their oxidation.
  • the powder is compacted in the form of pellets by cold pressing, followed by sintering at high temperature.
  • the product obtained by the process is composed of an alloy of zinc oxide and of doping products composed of oxides of at least some of the following metals: Ni, Cr, Mg, Mn, Bi, Sb, Si and Co (on page 5, line 32, it is copper which is mentioned); tin is not mentioned.
  • EP-A1-0 580 912 discloses more fully a process of “PADO” type for the manufacture of a homogeneous powder formed of metal oxides from alloys of metals in which the following successive steps are carried out:
  • a ceramic for example a semiconducting ceramic, based on metal oxides
  • the powder formed of oxides which is obtained is compacted, for example in the form of a pellet, and the compacted product is sintered at a temperature of greater than or equal to 800° C.
  • This process applies in particular to the manufacture of semiconductors based on zinc oxide which are doped with oxides of Ni, Cr, Mg, Mn, Bi, Sb, Co (or Cu); again, tin is not mentioned.
  • the powder with a predetermined particle size can be obtained by direct spraying of the liquid alloy recovered or else by casting the liquid alloy in an ingot mould in a neutral or reducing atmosphere, followed by melting the ingot to give a liquid alloy which is sprayed for the purpose of obtaining solid fine components or grains of homogeneous composition.
  • the “PADO” process for example disclosed in the document FR-A-2 674 157 and in the document EP-A1-0 580 912, makes it possible, without having recourse to one or more milling and mixing stages, which are often sources of pollution, to obtain a mixture formed of a perfectly homogeneous powder formed of oxides which can never be obtained by conventional processes employing large milling and heating devices.
  • the perfectly homogeneous powder obtained exhibits a homogeneity at a molecular level which had never been achieved until then.
  • the “PADO” process introduces an answer to the problem of homogeneity of the powders only in the context of the preparation of powders formed of oxides and then of semiconducting ceramics specifically based on zinc oxide (ZnO) and not in the case of ceramics based on other oxides, in particular of ceramics based on tin oxide (SnO 2 ).
  • the aim of the present invention is to provide a process for the preparation of ceramics based on oxides of metals which meets, inter alia, the needs listed above.
  • the aim of the present invention is, in addition, to provide a process for the preparation of ceramics based on oxides of metals which does not exhibit the disadvantages, limitations, failings and drawbacks of the processes of the prior art, in particular of the “PADO” process, and which solves the problems of the processes of the prior art.
  • the process according to the invention can be defined as a process of “PADO” type applied to tin and more specifically to an alloy of tin and of doping metals and which is employed in order to prepare ceramics formed of doped tin oxide.
  • the varistors obtained exhibit better electrical characteristics than the varistors of the prior art, in particular obtained by the “PADO” process, for example better ⁇ and E s properties than those obtained with varistors based on zinc oxide.
  • the electrical characteristics of the varistors prepared by the process according to the invention according to this first embodiment are also better than those of the varistors based on tin dioxide of the documents JP-A-49 108590, JP-A-49 047898, JP-A-49 129192, JP-A-49 129193, JP-A-05 129106 and JP-A-05 129167, the ⁇ values of which are low and always less than 30.
  • the present invention relates neither to the process for the preparation of an alloy nor to the atomization of the latter.
  • the invention may be defined generally as being the application of the “PADO” process to SnO 2 .
  • the physicochemical history of a powder is determining in the chemistry of the solid. Consequently, the results obtained with the process of the invention were unpredictable and absolutely uncertain as a person skilled in the art knows that the chemistry of tin is very different from that of zinc.
  • the powder to be compacted is, when a partial oxidation has been carried out, a composite composed of metal (metals) and of metal oxide(s).
  • the compacted powders are mixtures of metal (metals) and of metal oxides obtained by partial oxidation of the metal powders.
  • the raw ceramic (before sintering and after shaping) comprises tin metal and other metals, which is never the case in the prior art and which is not under any circumstances suggested by the prior art.
  • a metal-ceramic composite is subjected to sintering.
  • the oxide or oxides of doping metals can be chosen from oxides of cobalt, chromium, manganese, niobium, tantalum, transition metals, such as Zn, and lanthanide metals.
  • the other doping metal or metals placed in the crucible can likewise be chosen from the abovementioned doping metals and the salts of metals placed in the crucible can likewise be chosen from the salts of the abovementioned metals.
  • the oxide or oxides of doping metals are chosen from cobalt, manganese, niobium and tantalum oxides.
  • the ceramic comprises, as doping metal oxides, simultaneously, at the same time, cobalt oxide, manganese oxide, niobium oxide and tantalum oxide.
  • the proportion by weight of the tin and of the other doping metal or metals and/or salt or salts of doping metals placed in the crucible is preferably such that it makes it possible to obtain a ceramic comprising a proportion of tin oxide of greater than or equal to 90% by weight, preferably of greater than or equal to 95% by weight, more preferably of greater than or equal to 99% by weight, better still of greater than or equal to 99.995% by weight.
  • the proportion by weight of the other doping metal or metals and/or salt or salts of doping metals placed in the crucible is such that it makes it possible to obtain a ceramic comprising, as complement to 100% by weight of tin oxide, less than 10% by weight, preferably less than 5% by weight, more preferably less than 1% by weight and better still less than 0.005% by weight of oxides of doping metals.
  • the proportion of the other doping metal or metals and/or salt or salts of doping metals in the crucible is such that it makes it possible preferably to obtain a ceramic comprising, as complement to 100% by weight of tin oxide, one or more among the following oxides in the following proportions by weight:
  • the unexpected adapting of the “PADO” process to ceramics based on SnO 2 is carried out optimally if specific doping agents are preferably added to the ceramics.
  • Oxides of doping agents which are particularly preferred are chosen from cobalt, manganese, niobium and tantalum oxides, such as Co 3 O 4 , MnO 2 , Nb 2 O 5 and Ta 2 O 5 , preferably in the proportions mentioned above.
  • a preferred ceramic will comprise the addition of all four of these doping oxides, preferably in the proportions mentioned above.
  • this ceramic will have the following composition by weight (as % by weight):
  • the SnO 2 makes it possible to use a smaller number of doping agents, these doping agents being used in amounts which are lower overall and these doping agents in addition being chosen from doping agents which are less polluting, less toxic and cleaner.
  • the relative content of doping agents with respect to the base metal oxide or reference oxide is generally 10 times less (10 times less doping agents) in ceramics based on SnO 2 .
  • the % of doping agents is of the order of 2%, in particular 1.76%, in the above example, whereas it is generally of the order of 10% in the case of ZnO formulations.
  • toxic doping agents such as antimony oxide, are preferably not employed.
  • the alloy powder with a predetermined particle size can be prepared by cooling, preferably rapidly or suddenly (quenching), the homogeneous liquid mixture or alloy of metals, so as to solidify it, while retaining the chemical homogeneity of the mixture or alloy of liquid metals (high temperature), and by then dividing the solidified homogeneous alloy of metals to give a powder formed of alloy of metals with a predetermined particle size.
  • the cooling of the homogeneous liquid mixture or alloy of metals so as to solidify or set it can be carried out by casting the liquid mixture or alloy of metals in an ingot mould under a neutral or reducing atmosphere and by then cooling the ingot obtained.
  • the dividing of the solidified homogeneous alloy can be carried out in the liquid phase by melting it again to give a homogeneous liquid alloy of metals which is sprayed or atomized by a stream of gas or of liquid and rapidly cooled (quenched).
  • the powder formed of alloy of metals with a predetermined particle size can also be prepared directly from the homogeneous liquid alloy of metals resulting from the second stage of the process by spraying or atomization with a stream of gas or of liquid and rapid cooling (“quenching”).
  • the stream of gas can be a stream of neutral or reducing gas, such as hydrogen, nitrogen, argon or their mixtures.
  • the stream of gas can be a stream of oxidizing gas, such as air, air enriched in oxygen, or oxygen optionally enriched in water vapour.
  • the dividing of the solidified homogeneous alloy of metals can also be carried out in the solid phase by abrasion or milling.
  • the powder formed of alloy of metals can optionally be separated into several particle size fractions.
  • the powder formed of alloy of metals may be completely oxidized, that is to say that the oxidized powder comprises 100% by weight of oxide.
  • the oxide powder may be only partially oxidized.
  • the powder formed of alloy of metals may be partially oxidized to a percentage of 50 to 99.90% by weight, preferably of 55 to 80 or 85% by weight, more preferably of 60 to 70% by weight, that is to say that the oxidized powder comprises from 50 to 99.90% by weight of oxide, preferably from 55 to 80 or 85% by weight of oxide and more preferably from 60 to 70% by weight of oxide.
  • the powder formed of alloy of metals is partially oxidized to a percentage of 64% by weight.
  • the complete or partial oxidation of the particles of the powder formed of alloy of metals with a predetermined particle size can be carried out by bringing the said particles into contact with an oxidizing gas from a temperature and/or for a period of time which is (are) sufficient to produce a desired percentage of oxides of metals in the powder, for example for the oxidation to be complete.
  • a residence of one minute at 900° C. is sufficient to oxidize a monolayer of metal particles with a mean diameter of 20 to 40 microns.
  • thermogravimetric analysis For example, in the case of pure tin, a temperature of 900° C. for 15 minutes makes it possible to completely oxidize the tin to give tin oxide.
  • the degree of oxidation of the particles is, in the case of tin, controlled or conditioned essentially by the temperature of the stationary oxidation phase and not by its duration, as in the case of zinc.
  • the oxidizing gas can be chosen from gases comprising oxygen optionally enriched in water vapour and/or in carbon dioxide, such as air, air enriched in oxygen, oxygen, or air enriched in carbon dioxide and/or in water vapour; or mixtures of CO and of CO 2 .
  • the operation of bringing the particles into contact with the oxidizing gas can be carried out at a temperature of greater than or equal to 400° C., for example from 400 to 950° C.
  • the duration of this contacting operation is generally from 6 hours to 1 second, preferably from 4 hours to 2 seconds.
  • the contacting operation can thus be carried out, for example, for 4 hours at 400° C. or 2 seconds at 900° C.
  • the aim is to prepare a powder comprising oxides (case of partial oxidation) or composed of oxides (case of complete oxidation) which is finely divided, which is homogeneous, which has segregations which are as limited as possible, which is isotropic and which has a surface condition which has to facilitate the subsequent densification.
  • the powder has a particle size which is generally submicronic in mean size (for example, mean diameter) of the particles.
  • the completely or partially oxidized homogeneous powder can be shaped by compacting it in the form of pellets, for example by cold pressing.
  • the sintering can be carried out at a temperature of 1100 to 1350° C. for a period of time generally of greater than or equal to 30 minutes, preferably from 30 minutes to 2 hours.
  • the doping metal oxide(s) added to the completely or partially oxidized tin powder are chosen from cobalt, chromium, manganese, niobium and tantalum oxides, transition metal oxides, such as zinc oxide, and oxides of lanthanide metals, such as lanthanum oxide.
  • the oxide(s) of doping metals are chosen from cobalt, manganese, niobium and tantalum oxides.
  • the ceramic comprises, as doping metal oxides of, simultaneously, at the same time, cobalt oxide, manganese oxide, niobium oxide and tantalum oxide.
  • the doping metal oxide(s) are added to the partially or completely oxidized tin powder in a percentage by weight such that it makes it possible to obtain a ceramic comprising a proportion of tin oxide of greater than or equal to 90% by weight, preferably of greater than or equal to 95% by weight, more preferably of greater than or equal to 99% by weight and better still of greater than or equal to 99.995% by weight.
  • the doping metal oxide or oxides can thus be added to the partially or completely oxidized tin powder in a percentage by weight such that it makes it possible to obtain a ceramic comprising, as complement to 100% by weight of tin oxide, less than 10% by weight, preferably less than 5% by weight, more preferably less than 1% by weight and better still less than 0.005% by weight of oxides of doping metals.
  • the doping metal oxide(s) are added to the partially or completely oxidized tin powder in a percentage by weight such that it makes it possible to obtain a ceramic comprising, as complement to 100% by weight of tin oxide, one or more among the following oxides in the following proportions by weight:
  • Oxides of doping agents which are particularly preferred are chosen from cobalt, manganese, niobium and tantalum oxides, such as Co 3 O 4 , MnO 2 , Nb 2 O 5 and Ta 2 O 5 , preferably in the proportions mentioned above.
  • a preferred ceramic will comprise the addition of all four of these doping oxides, preferably in the proportions mentioned above.
  • this ceramic will have the following composition by weight (as % by weight):
  • the metal powder for example tin powder, with a predetermined particle size can be prepared in the liquid phase by melting the bulk tin to give a liquid metal which is sprayed or atomized by a stream of gas or of liquid and cooled, quenched.
  • the liquid tin can be sprayed or atomized by a stream of neutral or reducing gas, such as nitrogen.
  • the tin powder with a predetermined particle size can be prepared in the solid phase by abrasion or milling.
  • the tin powder can be separated into several particle size fractions.
  • the tin powder may be completely oxidized to a percentage of 100%.
  • the tin powder may be only partially oxidized.
  • the tin powder may be oxidized to a percentage of 50 to 99.90% by weight, preferably of 55 to 80 or 85% by weight, more preferably of 60 to 70% by weight, that is to say that the oxidized powder comprises from 50 to 99.90% by weight of oxide, preferably from 55 to 80 or 85% by weight of oxide, more preferably from 60 to 70% by weight of oxide; better still, the powder is oxidized to a percentage of 64% by weight.
  • a residence of one minute is sufficient to oxidize a monolayer of metal particles with a mean diameter of 20 to 40 microns at 900° C.
  • the tin powder can be partially or completely oxidized by bringing the said powder into contact with an oxidizing gas from a temperature and/or for a period of time which is (are) sufficient to produce a desired percentage of tin oxide in the powder.
  • control of the degree of oxidation is, in the case of tin, essentially controlled by the temperature of the stationary phase and not by its duration, as in the case of zinc.
  • the operation in which the particles are brought into contact with the oxidizing gas can be carried out at a temperature of greater than or equal to 400° C., for example from 400 to 950° C., for a period of time of 1 second to 6 hours, preferably of 2 seconds to 4 hours.
  • the oxidizing gas can be chosen from gases comprising oxygen optionally enriched in water vapour and/or in carbon dioxide, such as air, air enriched in oxygen, oxygen, or air enriched in carbon dioxide and/or in water vapour; or mixtures of CO and of CO 2 .
  • the process according to the invention in the second embodiment can be defined as a process of “PADO” type applied to tin which is employed in order to prepare ceramics based on doped tin oxide, the doping metals being added in the form of oxides to the powder subjected to the sintering and not in the form of metals or of salts to the crucible at the beginning of the process.
  • PADO PADO
  • the two embodiments of the process according to the invention are related by the same inventive concept, which is the surprising application of the PADO process to tin in order to prepare ceramics for varistors.
  • this second embodiment of the process of the invention comprises a specific sequence of steps, themselves specific, which is neither described nor suggested in the prior art.
  • a partial or complete oxidation of the tin powder is then carried out.
  • step of the process which consists in adding one or more doping oxides to the partially or completely oxidized tin powder, is also specific to the process according to the invention in this embodiment.
  • the powder subjected to sintering then comprises tin metal, tin oxide and the oxides of doping metals added.
  • FIG. 1 is a diagrammatic view in vertical section of an atomization device for preparing a powder formed of alloy of metals with a predetermined particle size, each of the particles of which is homogeneous.
  • This process can be defined as being a “PADO” process adapted to a specific alloy based on Sn.
  • tin, as base metal that is to say as metal, the oxide of which is the base oxide of the ceramic to be prepared, and one or more other doping metals mentioned above and/or more salts of these doping metals, preferably in the proportions defined above, are placed in a crucible or any other receptacle suitable for the melting of metals.
  • base metal oxide this base metal oxide being, in the present case, tin oxide SnO 2
  • base metal oxide as used in the present description is used generally to indicate that this oxide is predominant by weight in the final sintered ceramic, that is to say that this oxide generally represents 50% by weight or more, preferably more than 50% by weight, of the final ceramic; the more preferred proportions of the base metal oxide (greater than or equal to 90, 95, 99 or 99.995% by weight) have been given above.
  • doping agent is a term commonly used by a person skilled in the art in this field of the art.
  • salt is such as commonly used in inorganic chemistry and includes chlorides, nitrates, and the like, but also in particular oxides.
  • the final ceramic can optionally comprise, in addition to the base metal oxide and the doping metal oxide, in particular, impurities and/or other additives.
  • impurities is understood to mean substances which occur by chance, without being desired, in the ceramic and the term “additives” is understood to mean substances deliberately added to the ceramic in order to obtain one or more specific properties.
  • the semiconducting ceramic is composed of a base metal oxide and at least one doping metal oxide.
  • the tin and the said doping metals and/or salts of doping metals are melted under a neutral or reducing atmosphere, for example hydrogen, while mixing the molten metals in order to obtain a homogeneous liquid mixture or alloy of metals (tin and doping metals).
  • a neutral or reducing atmosphere for example hydrogen
  • the salt or salts optionally present may decompose, for example if they are nitrates.
  • the possible contamination caused by this decomposition is very slight, as the actual result of the very low content of doping agents.
  • This first step and this second step are conventional steps which can easily be carried out by the man skilled in the art, for example using the device (oven) described in the document FR-A-2 674 157 (FIG. 1) and in the document EP-A1-0 580 912, to the description of which reference may be made.
  • a powder formed of alloy of metals with a predetermined particle size, each of the particles of which is homogeneous, is prepared from the said homogeneous liquid mixture or alloy of metals.
  • the said predetermined particle size can be obtained directly or else on conclusion of an optional sieving operation.
  • This powder formed of alloy of metals can be prepared directly by spraying or atomizing, without preliminary cooling, the liquid alloy prepared in the second step by a stream of gas or of liquid.
  • the cooling operation can be carried out by casting the liquid alloy of metals in an ingot mould under a neutral or reducing atmosphere and by then cooling the ingot obtained, likewise under a neutral or reducing atmosphere.
  • the alloy if it has been produced in a silica container sealed under vacuum comprising the various metals, this container having been subsequently heated in an oven and regularly agitated in order to obtain a homogeneous liquid mixture, can finally be cooled by a quenching intended to solidify the alloy obtained.
  • the solidified homogeneous alloy of metals such as an ingot
  • the liquid used for the atomization can be water.
  • the gas used for the atomization or spraying can be a reducing or neutral gas chosen, for example, from hydrogen, nitrogen, argon and their mixtures.
  • the gas used for the atomization or spraying can be an oxidizing gas, such as air, optionally enriched in oxygen and/or in water vapour, or oxygen, so that the fine particles of molten alloy are sprayed to give fine particles which are at the same time partially oxidized and cooled.
  • an oxidizing gas such as air, optionally enriched in oxygen and/or in water vapour, or oxygen, so that the fine particles of molten alloy are sprayed to give fine particles which are at the same time partially oxidized and cooled.
  • the alloy particles are necessarily subsequently subjected to complete or partial oxidation prior to shaping and sintering.
  • the spraying is generally carried out at a temperature of 400 to 1000° C., whereas, in the case where the gas used is a neutral or reducing gas, the spraying is generally carried out at a temperature of 230 to 1000° C.
  • the dividing, atomizing or spraying of the alloy can be carried out with a device such as that described in the documents FR-A-2 674 157 (FIG. 2) and EP-A-0 580 912 (FIG. 2), to the description of which reference may be made.
  • the dividing, atomizing or spraying in the liquid phase can also be carried out by atomizing the mixture, alloy or liquid with a stream of gas, for example with nitrogen gas, using the device described in FIG. 1 .
  • This device comprises three parts: a part intended for the melting of the alloy (or of the metal, in the case of the second embodiment of the invention: see below); a chamber which is the atomizer proper, which is provided at its base with a spray nozzle; and a tube or rod for blocking the spray nozzle and for measuring the temperature at this nozzle.
  • the entire device is heated via electrical resistors and flushed with neutral gas, such as argon (other than the atomizing gas), in order to protect the liquid from any premature oxidation which might promote segregation of the oxides.
  • neutral gas such as argon (other than the atomizing gas)
  • the alloy or the metal ( 1 ) is melted in a receptacle ( 2 ) heated via a heating resistor ( 3 ) and equipped with a thermocouple ( 4 ).
  • This receptacle is fitted into a branch connection ( 5 ) equipped with a ground adapter ( 6 ) situated in the side wall ( 8 ) of the atomizer ( 7 ); the latter has the form of a substantially elongated vertical cylindrical chamber.
  • the adapter ( 6 ) makes it possible to rotate the receptacle ( 2 ) containing the alloy (or the metal) between two positions: a first “bottom” position (in solid lines), in which the alloy (or the metal) is heated and melted, and a second “top” position (in dotted lines), in which the molten liquid alloy (or metal) can be transferred into the chamber of the atomizer.
  • the molten alloy is kept molten in the lower part of the chamber of the atomizer ( 7 ) by heating electrical resistors ( 9 ).
  • a pipe ( 10 ) which emerges in the side wall of the chamber of the atomizer conveys a stream of inert gas ( 11 ), such as argon, into the chamber and prevents any oxidation of the molten alloy or metal.
  • a flow orifice ( 12 ) for the liquid alloy (or metal) occurs at the base of the chamber of the atomizer, which orifice is blocked by a rod or tube ( 13 ) equipped at its centre with a thermocouple ( 14 ).
  • the tube or rod ( 13 ) is raised and a thin stream of liquid alloy (or metal) flows via the orifice into a nozzle ( 15 ).
  • the latter is surrounded by an annular cavity ( 16 ) which receives a side feed of stream of atomizing gas, such as nitrogen, via a pipe ( 17 ) also equipped with heating electrical resistors ( 18 ).
  • the thin stream or flow of liquid alloy (or metal) which issues under the effect of gravity from the end of the nozzle is sprayed or atomized by virtue of the partial vacuum produced by the gas, such as nitrogen, stream ring which surrounds the molten alloy flowing through the nozzle ( 15 ).
  • the gas such as nitrogen
  • the droplets of liquid alloy or metal are subsequently cooled, preferably rapidly cooled, that is to say quenched, in order to recover an alloy (or metal) powder.
  • the solidified homogeneous alloy of metals (or metal) can also be divided in the solid phase, for example by abrasion, milling or machining. This spraying or atomizing in the solid phase is generally carried out at the boiling point of nitrogen at 1 bar, namely ⁇ 196° C.
  • the powder may already exhibit the desired particle size; if not, it is subjected, for example, to a sieving operation.
  • alloy powder (or metal powder, in the second embodiment) can subsequently be separated into several particle size fractions by sieving or any other separation process.
  • All the powder or only a predetermined particle size fraction for example the particle size fraction comprising the particles with a diameter of less than 40 ⁇ m, is subjected to the following stage of the process, which consists of a complete or partial oxidation of the alloy powder obtained above.
  • partial oxidation is understood to mean that the final powder comprises a proportion of oxide(s) of less than 100% by weight; preferably, the proportion of oxide(s) is 50 to 99.9% by weight; preferably it is from 55 to 80% or 85% by weight; more preferably it is from 60 to 70% by weight.
  • This complete or partial oxidation is generally carried out while avoiding coalescence of the particles: this can be obtained by varying the physical parameters related to the technique used, such as the temperature, the pressure, the rate, and the like, or by virtue of the technology employed: for example, use may be made of a fluidized, pulverulent bed.
  • This complete or partial oxidation is generally carried out by bringing the alloy powder (or metal powder) into contact with an oxidizing gas from a temperature and/or for a period of time which is (are) sufficient for the oxidation to be complete or for the desired percentage of oxide(s) in the powder to be obtained.
  • a residence of one minute is sufficient to oxidize a monolayer of metal particles with a mean diameter of 20 to 40 microns at 900° C.
  • the oxidizing gas can be any oxidizing gas suitable for this purpose but it is generally chosen from gases comprising oxygen optionally enriched in water vapour and/or in carbon dioxide, such as air, air enriched in oxygen, oxygen, or air enriched in carbon dioxide and/or in water vapour; or mixtures of CO and of CO 2 .
  • the operation in which the alloy (or metal) particles are brought into contact with the oxidizing gas can be carried out at a temperature ranging from 60 to 1000° C. but is generally carried out at a high temperature, namely a temperature of greater than or equal to 400° C., for example from 400 to 950° C.
  • This contacting operation is carried out for a period of time sufficient for the oxidation to be complete or for the desired percentage of oxide(s) in the powder to be obtained.
  • This period of time can be easily determined by a person skilled in the art, for using oxidation curves found during preliminary experiments, which give the exact amount of alloy oxidized as a function of the temperature and of the period of time.
  • the powder formed of oxide(s) which is obtained has a particle size which is generally submicronic in mean size (for example, mean diameter) of the particles.
  • the powder formed of oxide(s) which is obtained is subsequently shaped in a known way, for example compacted in the form of pellets of ceramics, by cold pressing, for example by uniaxial cold pressing, using an organic or inorganic binder, such as water.
  • the powder shaped or compacted, for example in the form of pellets, is subsequently sintered in a known way at high temperature, generally at a temperature of 1100 to 1350° C., for a period of time of greater than or equal to 30 minutes, preferably from 30 minutes to 2 hours, for example at 1350° C. for one hour, in order to densify it.
  • the densified ceramics obtained on conclusion of the process according to this first embodiment can be used in varistors, they being metallized beforehand.
  • This process may be defined in particular as being a “PADO” process applied to a pure tin and not to an alloy of tin and of doping agents.
  • pure bulk tin is provided, for example in the form of lumps or shot or ingots.
  • a tin powder with a predetermined particle size is prepared from the pure bulk tin.
  • the tin powder with a predetermined particle size can be prepared in the liquid phase by melting the bulk tin to give a liquid metal which is sprayed or atomized with a stream of neutral or reducing gas, for example chosen from hydrogen, nitrogen, argon and their mixtures, or else with a stream of oxidizing gas.
  • a stream of neutral or reducing gas for example chosen from hydrogen, nitrogen, argon and their mixtures, or else with a stream of oxidizing gas.
  • the tin powder with a predetermined particle size can be prepared in the solid phase by abrasion or milling under conditions already described for the first embodiment.
  • All or only a predetermined particle size fraction for example the particle size fraction comprising the particles with a diameter of less than 40 ⁇ m, is subjected to the following step of the process, which consists of a partial or complete oxidation of the metal powder obtained above.
  • partial oxidation in contrast to the prior art, where a complete oxidation is carried out, is understood to mean that only a portion of the said metal powder is oxidized and that a powder comprising, for example, both tin dioxide and tin metal is obtained.
  • the tin powder is partially oxidized to a percentage of 50 to 99.9% by weight, preferably of 55 to 80% or 85% by weight, more preferably of 60 to 70% by weight, that is to say that the oxidized powder comprises 50 to 99.90% by weight, preferably from 55 to 80% or 85% by weight, more preferably from 60 to 70% by weight of oxide and the remainder of free metal, that is to say of free Sn.
  • the tin powder is oxidized to a percentage of 64% by weight, that is to say that it comprises, for example, by weight, 64% of SnO 2 and 36% of tin.
  • the partial or complete oxidation of the metal powder, for example of the tin powder, with a predetermined particle size is carried out by bringing the said powder into contact with an oxidizing gas at a temperature and for a period of time sufficient to obtain a desired percentage (for example, within the ranges defined above) of tin oxide, which percentage can reach 100% of tin oxide in the partially or totally oxidized powder.
  • the contacting operation is carried out for a period of time sufficient to produce the desired percentage of oxide in the powder; this period of time can be easily determined by a person skilled in the art, for example using oxidation curves, as has been described above.
  • one or more powdered doping metal oxide(s) is (are) added to the partially or completely, totally, oxidized tin powder.
  • the oxide or oxides of doping metals added to the partially or totally oxidized tin powder can be chosen from all suitable oxides of doping metals.
  • the oxides are generally chosen from cobalt, chromium, manganese, niobium and tantalum oxides, transition metal oxides, such as zinc oxide and lanthanide metal oxides, such as lanthanum oxide.
  • the oxides can be commercially available oxides or oxides prepared by any known process, indeed even by the “PADO” process.
  • the oxide or oxides of doping metal are added to the completely or partially oxidized tin powder in a percentage by weight such that it makes it possible to obtain a ceramic comprising, as complement to 100% by weight of tin oxide, the desired percentage of the doping metal oxides.
  • the doping oxide or oxides can be added in a percentage by weight such that they make it possible to obtain a ceramic comprising, as complement to 100% by weight of metal oxide, for example of tin oxide:
  • the powders are mixed using known processes.
  • the shaping and sintering stages are carried out under the same conditions as for the first embodiment, optionally with slight adjustments.
  • This example illustrates the first embodiment of the process according to the invention, in which the “PADO” process is adapted in order to prepare tin oxide doped with oxides of certain metals in specific proportions.
  • a ceramic which has the following composition by weight (as % by weight):
  • the “PADO” process is carried out on the five starting metals: tin and then cobalt, manganese, niobium and tantalum as doping agents.
  • a liquid alloy is first prepared from these five metals. It is subsequently quenched in order to set the composition of the alloy obtained.
  • the alloy is subsequently placed in an atomizer, where it is sprayed by a stream of nitrogen gas to give an alloy powder.
  • the alloy is prepared and is atomized on an experimental laboratory prototype.
  • the alloy is prepared in a silica container sealed under vacuum, which receives the various solid metals in the desired proportions.
  • This container is subsequently heated in an oven at 1100° C. and regularly agitated in order to produce a homogeneous liquid mixture.
  • the molten alloy is then atomized, which carries out the quenching intended to solidify the alloy obtained so as to retain the homogeneity thereof acquired at high temperatures.
  • the alloy is atomized or divided to give a powder in an atomizer or atomizing device, such as that described in FIG. 1 .
  • the particle size fraction of the particles with a diameter of less than 40 ⁇ m is separated from the whole of the powder for the continuation of the process.
  • the powder corresponding to this fraction is subsequently completely oxidized to give an oxide powder; the complete oxidation is carried out by placing the alloy powder in an oven under an atmosphere of air and by maintaining it at a temperature of 900° C. for a period of time of 5 minutes.
  • this resulting powder is shaped under a pressure of 3 tonnes in a die equipped with two moving cylinders and then sintered at 1350° C. for 2 hours with a rise and a fall in temperature of 3° C./minute in order to result in a bulk ceramic.
  • the electrical characteristics of the ceramics obtained after metallization are as follows: the nonlinearity coefficient ⁇ is 47 (measured around 10 ⁇ 3 A/cm 2 ) and the threshold field E s is 450 V/mm (measured for 10 ⁇ 3 A/cm 2 ).
  • This example illustrates the second embodiment of the process according to the invention, in which the “PADO” process is modified by carrying out a partial (and no longer complete) oxidation of a tin powder (and no longer of an alloy powder) and in which the doping oxides are added to the oxidized powder, in this case partially oxidized powder, before the sintering.
  • a ceramic which has a composition by weight similar to that of Example 1:
  • the “PADO” process is carried out on a starting product which is pure bulk tin.
  • the latter is first atomized under nitrogen in order to produce a tin metal powder.
  • the main parameters relating to the atomizing gas are a pressure of 3 bar, a flow rate of 45 l/minute and a temperature of 700° C.
  • the atomizing device described in FIG. 1 is employed.
  • the powder is sieved, so as to retain only the particle size fraction of less than 40 ⁇ m.
  • This powder is subsequently partially oxidized to 64% by weight, that is to say that it comprises, by weight, 64% of tin dioxide SnO 2 and 36% of tin.
  • This partial oxidation is carried out by placing the tin powder in an oven under an atmosphere of air, by raising the temperature at the rate of 3° C./minute up to 750° C. and by observing a stationary phase at this temperature for a duration limited to 5 minutes, before quenching with air.
  • the doping oxides (Co 3 O 4 , Nb 2 O 5 and Ta 2 O 5 ) in the powder form are then added in the desired amounts to the metal-ceramic powder.
  • This combined product is subsequently mixed and then shaped and sintered under the same conditions as Example 1 to give a ceramic.
  • the electrical characteristics of the ceramics obtained after metallization are as follows: the nonlinearity coefficient ⁇ is 53 (measured around 10 ⁇ 3 A/cm 2 ) and the threshold field E s is 308 V/mm (measured for 10 ⁇ 3 A/cm 2 ).

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Manufacturing & Machinery (AREA)
  • Ceramic Engineering (AREA)
  • Organic Chemistry (AREA)
  • Structural Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Electromagnetism (AREA)
  • Plasma & Fusion (AREA)
  • Compositions Of Oxide Ceramics (AREA)
  • Thermistors And Varistors (AREA)
  • Apparatuses And Processes For Manufacturing Resistors (AREA)
US11/541,562 2005-01-24 2006-10-03 Process for the preparation of semiconducting ceramics composed of metal oxides, in particular of tin oxide, especially for varistors Abandoned US20070140891A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US11/541,562 US20070140891A1 (en) 2005-01-24 2006-10-03 Process for the preparation of semiconducting ceramics composed of metal oxides, in particular of tin oxide, especially for varistors

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
FR0550203 2005-01-24
FR0550203A FR2881134B1 (fr) 2005-01-24 2005-01-24 Procede de preparation de ceramiques semi-conductrices constituees d'oxydes de metaux, notamment d'oxyde d'etain en particulier pour les varistances
US33852106A 2006-01-23 2006-01-23
US11/541,562 US20070140891A1 (en) 2005-01-24 2006-10-03 Process for the preparation of semiconducting ceramics composed of metal oxides, in particular of tin oxide, especially for varistors

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
US33852106A Continuation 2005-01-24 2006-01-23

Publications (1)

Publication Number Publication Date
US20070140891A1 true US20070140891A1 (en) 2007-06-21

Family

ID=35063018

Family Applications (1)

Application Number Title Priority Date Filing Date
US11/541,562 Abandoned US20070140891A1 (en) 2005-01-24 2006-10-03 Process for the preparation of semiconducting ceramics composed of metal oxides, in particular of tin oxide, especially for varistors

Country Status (4)

Country Link
US (1) US20070140891A1 (fr)
EP (1) EP1683880A3 (fr)
CN (1) CN1870185B (fr)
FR (1) FR2881134B1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110014102A1 (en) * 2009-02-12 2011-01-20 A123 Systems, Inc. Materials and methods for the removal of sulfur compounds from feedstock
WO2014187360A1 (fr) * 2013-05-23 2014-11-27 Shenzhen Byd Auto R & D Company Limited Oxyde d'etain dope et procede pour la metallisation selective de substrat isolant
US20150035192A1 (en) * 2013-08-01 2015-02-05 University Of North Dakota Porous ceramic and method of making
US9633802B2 (en) 2013-08-09 2017-04-25 Schneider Electric Industries Sas Vacuum bulb, circuit-breaker pole including such a vacuum bulb, and method to manufacture such devices
CN114149258A (zh) * 2021-12-29 2022-03-08 全球能源互联网研究院有限公司 一种具有叠层结构的压电陶瓷及其制备方法和应用

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN100471819C (zh) * 2007-05-16 2009-03-25 中材高新材料股份有限公司 激光吸收陶瓷粉体材料及其制备方法
CN101533694B (zh) * 2009-04-07 2012-03-14 山东电力研究院 一种具备液体蒸发冷却功能的新型高能量ZnO避雷器
CN114315341A (zh) * 2021-12-28 2022-04-12 广州市石基耐火材料厂 含锰高纯锡陶瓷及其制备方法、含锰高纯锡砖和应用
CN115709288B (zh) * 2022-11-28 2024-09-17 桂林金格电工电子材料科技有限公司 一种银氧化锡氧化镧触头材料的制备方法

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5322642A (en) * 1992-07-28 1994-06-21 Ferraz Method of manufacturing semiconductors from homogeneous metal oxide powder

Family Cites Families (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1031651A (en) * 1964-01-31 1966-06-02 Welwyn Electric Ltd Improvements in the manufacture of oxide mixes
FR2174175A1 (en) 1972-03-01 1973-10-12 Matsushita Electric Industrial Co Ltd Zinc oxide based nonlinear resistors - for use as overvoltage suppressors and contg. cobalt fluoride
FR2174174A1 (en) 1972-03-01 1973-10-12 Matsushita Electric Industrial Co Ltd Voltage dependent resistance - consisting of electrodes fixed to sintered body composed of oxides of zinc, bismuth, antimony, and
US3806765A (en) 1972-03-01 1974-04-23 Matsushita Electric Industrial Co Ltd Voltage-nonlinear resistors
JPS5417155B2 (fr) 1972-03-31 1979-06-27
CA986235A (en) 1972-07-26 1976-03-23 Takeshi Masuyama Voltage-nonlinear resistors
JPS551685B2 (fr) 1972-08-30 1980-01-16
JPS5224233B2 (fr) 1972-09-18 1977-06-29
JPS5529574B2 (fr) 1973-02-14 1980-08-05
JPS5550368B2 (fr) 1973-02-20 1980-12-17
JPS5247158B2 (fr) 1973-04-16 1977-11-30
JPS5240760B2 (fr) 1973-04-16 1977-10-14
US4519838A (en) * 1982-09-15 1985-05-28 Elkem Metals Company Apparatus and process for producing predominately iron alloy containing magnesium
FR2674157B1 (fr) * 1991-03-19 1993-07-30 Deshayes Rene Procede de fabrication d'alliage de metaux pour la production d'une poudre homogene et produit obtenu par sa mise en óoeuvre.
JPH05129106A (ja) 1991-10-31 1993-05-25 Taiyo Yuden Co Ltd 半導体磁器物質
JP3094569B2 (ja) 1991-11-08 2000-10-03 松下電器産業株式会社 アルミ電解コンデンサの製造方法
BR9600174A (pt) 1996-01-22 1997-10-07 Siderurgica Nacional Sa Composições varistoras à base de dióxido de estanho com elevada propriedade não linear e processamento

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5322642A (en) * 1992-07-28 1994-06-21 Ferraz Method of manufacturing semiconductors from homogeneous metal oxide powder

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110014102A1 (en) * 2009-02-12 2011-01-20 A123 Systems, Inc. Materials and methods for the removal of sulfur compounds from feedstock
US8956479B2 (en) 2009-02-12 2015-02-17 A123 Systems Llc Materials and methods for the removal of sulfur compounds from feedstock
WO2014187360A1 (fr) * 2013-05-23 2014-11-27 Shenzhen Byd Auto R & D Company Limited Oxyde d'etain dope et procede pour la metallisation selective de substrat isolant
US9869025B2 (en) 2013-05-23 2018-01-16 Byd Company Limited Doped tin oxide and method for selective metallization of insulating substrate
US20150035192A1 (en) * 2013-08-01 2015-02-05 University Of North Dakota Porous ceramic and method of making
US9633802B2 (en) 2013-08-09 2017-04-25 Schneider Electric Industries Sas Vacuum bulb, circuit-breaker pole including such a vacuum bulb, and method to manufacture such devices
CN114149258A (zh) * 2021-12-29 2022-03-08 全球能源互联网研究院有限公司 一种具有叠层结构的压电陶瓷及其制备方法和应用

Also Published As

Publication number Publication date
FR2881134B1 (fr) 2007-04-20
EP1683880A2 (fr) 2006-07-26
CN1870185B (zh) 2010-12-08
FR2881134A1 (fr) 2006-07-28
CN1870185A (zh) 2006-11-29
EP1683880A3 (fr) 2012-02-08

Similar Documents

Publication Publication Date Title
US6620346B1 (en) Varistors based on nanocrystalline powders produced by mechanical grinding
US6060165A (en) Metal powder and process for preparing the same
JP5094276B2 (ja) 圧粉コア及びその製造方法
KR950001661B1 (ko) 알루미늄계 산화물, 그의 성형품 및 알루미늄계 산화물의 제조방법
JP3277823B2 (ja) 金属粉末の製造方法
EP2185304B1 (fr) Procédé de fabrication d'une poudre d'alliage à multiples éléments contenant de l'argent et au moins deux éléments ne contenant pas d'argent
CN102057074A (zh) A1基合金溅射靶材的制造方法
US20170301845A1 (en) P-type thermoelectric material, thermoelectric element and method for producing p-type thermoelectric material
JPS63274736A (ja) ニオブ合金
CN1870185B (zh) 制备用于变阻器的包含金属氧化物的半导体陶瓷的方法
JPS6089557A (ja) 溶射用粉末材料およびその製造方法
TW201739723A (zh) 氧化物燒結體及濺鍍靶材以及它們的製造方法
KR20180060265A (ko) 산화도가 제어된 Bi-Te계 열전 재료의 제조 방법
JPH0514779B2 (fr)
EP0834369B1 (fr) Préparation de poudre métallique par décomposition
US5322642A (en) Method of manufacturing semiconductors from homogeneous metal oxide powder
EP0532788B1 (fr) Procédé de production d'un ferrite doux magnétique moulé
KR20190119744A (ko) 저 산소 열전 분말 및 그 소결체 제조 방법
US4202686A (en) Process for manufacturing fine powder of metal
JP2623188B2 (ja) バリスタ及びその製造方法
JP6877090B2 (ja) 導電フィラー用粉末
JP2000114606A (ja) シリコン−ゲルマニウム系熱電材料及びその製造方法
JPH0742530B2 (ja) 低酸素合金成形体の製造法
JPH06128609A (ja) Ａｇ−Ｃｕ系合金粉の製造方法
EP1841713A1 (fr) Procede de preparation de ceramiques semi-conductrices constituees d'oxydes de metaux tel que l'etain en particulier pour les varistances

Legal Events

Date Code Title Description
STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION