US20170073902A1 - Packaging material and method for making the same - Google Patents

Packaging material and method for making the same Download PDF

Info

Publication number
US20170073902A1
US20170073902A1 US15/122,039 US201415122039A US2017073902A1 US 20170073902 A1 US20170073902 A1 US 20170073902A1 US 201415122039 A US201415122039 A US 201415122039A US 2017073902 A1 US2017073902 A1 US 2017073902A1
Authority
US
United States
Prior art keywords
precursor
fibers
strength
image layer
strength layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/122,039
Other languages
English (en)
Inventor
Lokendra Pal
Xulong Fu
Xiaoqi Zhou
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hewlett Packard Development Co LP
Original Assignee
Hewlett Packard Development Co LP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hewlett Packard Development Co LP filed Critical Hewlett Packard Development Co LP
Assigned to HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P. reassignment HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: FU, XULONG, PAL, LOKENDRA, ZHOU, XIAOQI
Publication of US20170073902A1 publication Critical patent/US20170073902A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H27/00—Special paper not otherwise provided for, e.g. made by multi-step processes
    • D21H27/10—Packing paper
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21F—PAPER-MAKING MACHINES; METHODS OF PRODUCING PAPER THEREON
    • D21F9/00—Complete machines for making continuous webs of paper
    • D21F9/02—Complete machines for making continuous webs of paper of the Fourdrinier type
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
    • D21H17/63—Inorganic compounds
    • D21H17/66—Salts, e.g. alums
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H27/00—Special paper not otherwise provided for, e.g. made by multi-step processes
    • D21H27/30—Multi-ply
    • D21H27/38—Multi-ply at least one of the sheets having a fibrous composition differing from that of other sheets

Definitions

  • Packaging materials may be made on a papermaking machine, such as a Fourdrinier Machine. Papermaking generally involves forming a web of fibers on a conveyer belt (often referred to as a wire), pressing the fibers to drain water from the web, and then drying the pressed web. The papermaking process may also include calendering, where a roll is used to smooth the dried web.
  • FIG. 1 is a flow diagram depicting several examples of a method for making a packaging material
  • FIG. 2 is a cross-sectional view depicting an example of the packaging material including an image layer and a strength layer;
  • FIG. 3 is a cross-sectional view depicting another example of the packaging material including the image layer in contact with one opposed surface of the strength layer and a second strength layer in contact with another opposed surface of the strength layer;
  • FIG. 4 is a cross-sectional view depicting yet another example of the packaging material including the strength layer made up of two sub-strength layers and respective image layers in contact with outer opposed surfaces of the strength layer.
  • Examples of the packaging material disclosed herein include a multi-layered structure with a di-valent or multi-valent salt present (e.g., distributed) throughout an image layer, which is positioned as at least one of the outermost layers of the structure.
  • Examples of the multi-layered structure also include a strength layer. It is believed that the image layer enhances the print quality characteristics of the multi-layered structure, and the strength layer enhances the durability of the multi-layered structure.
  • the di-valent or multi-valent salt remains in the image layer, at least in part because the strength layer includes softwood fibers of a specific length that form a fiber mat with relatively low porosity that acts as a barrier to the salt. This fiber mat reduces salt migration from the image layer through the strength layer during the papermaking process.
  • the presence of the salt in the outermost image layer(s) is desirable for enhancing the compatibility of the packaging material with inkjet inks subsequently printed thereon.
  • the salt provides the packaging material with an ink fixing characteristic.
  • the methods for making the packaging material disclosed herein are streamlined, in part because the salt may be added to the image layer during the forming process. As such, additional offline coating and/or printing processes are not required.
  • the methods disclosed herein enable a traditional papermaking machine (e.g., a paperboard duo Fourdriner machine having multiple headboxes) to be used, even when the machine does not include a surface sizing station.
  • FIG. 1 the steps of various examples of the method 100 for making examples of the packaging material are illustrated. Different examples of the method 100 are denoted by the different arrows between the boxes. For example, one example of the method is shown by the bold arrows, and includes steps 102 through 112 . Examples of the resulting packaging materials are shown in FIG. 2 through FIG. 4 . The specific layered structures shown in FIG. 2 through FIG. 4 will be described throughout the discussion of FIG. 1 .
  • suitable pulps stocks are formed for the image layer(s) and the strength layer(s). All of the pulp stocks described in conjunction with the method(s) disclosed herein initially contain water along with at least one type of fiber for making a particular layer. It is to be understood that when the pulp stock is dried, there may be some minimal loss of the fiber(s) in the final layer that is formed.
  • Examples of the pulp stock for the image layer(s) include about 99% water.
  • the remaining components in the image layer(s) pulp stocks are the hardwood fibers, and the salt. In some instances, no other components are added. In other instances, other fibers and/or additives may be included in the image layer pulp stock.
  • the hardwood fibers included in the image layer pulp stock have an average length ranging from about 0.5 mm to about 1.5 mm. These relatively short fibers improve the formation and smoothness of the packaging material. In addition, it is believed that ink applied to an image layer including relatively short fibers may be distributed more precisely.
  • the hardwood fibers are present in an amount ranging from about 70 wt % to about 100 wt % of a total wt % of the solid components (i.e., total solids wt %) of the image layer pulp stock.
  • suitable hardwood fibers include pulp fibers derived from deciduous trees (angiosperms), such as birch, aspen, oak, beech, maple, and eucalyptus. The hardwood fibers may be bleached or unbleached hardwood fibers.
  • the pulp stock may also include up to 20 wt % of fibers other than the hardwood fibers.
  • These other fibers may be a different type of fiber from, but have the same length as, the hardwood fiber.
  • the other fibers may be natural fibers, virgin fibers, recycled fibers, non-deinkable fibers, unbleached fibers, synthetic fibers, mechanical fibers, or combinations thereof.
  • One example of the other fibers includes softwood fibers.
  • the hardwood fibers and/or other fibers may be prepared by any known pulping process, such as, for example, chemical pulping processes. Two suitable chemical pulping methods include the kraft process and the sulphite process.
  • the hardwood fibers may also be mechanically pulped, thermomechanically pulped, or chemi-thermomechanically pulped.
  • the image layer pulp stock further includes a water soluble di-valent or multi-valent salt.
  • the di-valent or multi-valent salt is present in an amount ranging from about 5 lb per ton of the amount of total fiber(s) in the image layer pulp stock to about 50 lb per ton of the amount of total fiber(s) in the image layer pulp stock.
  • Some examples of the di-valent or multi-valent salt may include a salt of any metals of Group I, Group II, and Group III of the Periodic Table of Elements, as well as a salt of any of the transition metals.
  • metal cations include calcium ions, copper ions, nickel ions, magnesium ions, zinc ions, barium ions, iron ions, aluminum ions, and chromium ions; and some examples of anions for forming the metal salt include chloride ions, iodide ions, bromide ions, nitrate ions, phosphate ions, chlorate ions, acetate ions, propionates, formates, oxalates, and/or combinations thereof.
  • the di-valent or multi-valent salt may be chosen from calcium chloride (CaCl 2 ), magnesium chloride (MgCl 2 ), aluminum chloride (AlCl 3 ), magnesium sulfate (MgSO 4 ), calcium acetate (Ca(CH 3 COO) 2 ), calcium propionate (Ca(C 2 H 5 COO) 2 ), calcium lactate (C 6 H 10 CaO 6 ), calcium nitrate (Ca(NO 3 ) 2 ), magnesium acetate (Mg(CH 3 COO) 2 ), magnesium propionate (Mg(C 2 H 5 COO) 2 ), and combinations thereof.
  • the image layer pulp stock may also contain up to 10 wt % (with respect to total solids) of an additive.
  • Suitable additives may be selected from a group consisting of a dry strength additive, wet strength additive, a filler, a retention aid, a dye, an optical brightening agent (i.e., optical brightener), a surfactant, a sizing agent, a biocide, a defoamer, or a combination thereof.
  • dry strength additives examples include anionic polyacrylamides, cationic polyacrylamides, amphoteric polyacrylamides, polyvinyl alcohol, cationized starch, vegetable galactomannan, and/or combinations thereof.
  • Wet strength additives may be added, such as polyaminepolyamide epichlorohydrin resins.
  • Suitable fillers that may be added include carbonates (e.g., ground calcium carbonate and precipitated calcium carbonate), titanium dioxide, clays (e.g., kaolin clay), silicates, oxides, zeolites, talc, and combinations thereof.
  • carbonates e.g., ground calcium carbonate and precipitated calcium carbonate
  • titanium dioxide e.g., titanium dioxide
  • clays e.g., kaolin clay
  • silicates e.g., oxides, zeolites, talc, and combinations thereof.
  • Any suitable dye may be added, an example of which IRGALITE® Blue Dye (BASF Corp.).
  • retention aids include polyacrylamide-based systems (such as PERCOL® polyacrylamides (BASF Corp.) and the Eka PL Series (Eka Chemicals, AkzoNobel Corp.), and solutions of particles and charged polymers (such as COMPOZIL® Select and Eka NP (Eka Chemicals, AkzoNobel Corp.).
  • polyacrylamide-based systems such as PERCOL® polyacrylamides (BASF Corp.) and the Eka PL Series (Eka Chemicals, AkzoNobel Corp.)
  • solutions of particles and charged polymers such as COMPOZIL® Select and Eka NP (Eka Chemicals, AkzoNobel Corp.).
  • Example optical brighteners include TINOPAL® ABP-A (BASF Corp.), and examples of suitable defoamers include AC-22 available from Performance Process, Inc., and ANTISPUMIN® 7100 available from Evonik-Degussa GmbH.
  • surfactants include those of the Eka DPC Series, available from Eka Chemicals, AkzoNobel Corp.
  • Suitable sizing agents include fatty acids, metal salts of fatty acids, alkyl ketene dimer emulsification products, epoxidized higher fatty acid amides, alkenyl acid anhydride emulsification products and rosin derivatives, alkylsuccinic acid anhydride emulsification products and rosin derivatives, and/or combinations thereof.
  • biocides examples include AQUATREAT® DNM 30 (AkzoNobel Corp), SPECTRUMTM XD3899 (Ashland, Inc.), and MYACIDE® AS and Protectol® DZ (BASF Corp.).
  • the image layer pulp stock may be made by incorporating at least the hardwood fibers into a suitable amount of water to form a slurry.
  • the slurry may contain 99% water and 1% fibers, where 100% of the fibers are the hardwood fibers disclosed herein. If the other fibers are included, they may be added into the slurry.
  • the slurry may be refined.
  • a double disk refiner is used.
  • the double disk refiner is a refining mechanism, which uses a free rotating disk rotor between two non-rotating disks.
  • the rotating disk and the two non-rotating disks are each fit with a refining plate on each side thereof.
  • the rotating disk, and associated refining plates rotate between the two non-rotating disks fit with refining plates.
  • the refiner applies mechanical and hydraulic forces to alter the fibers within the slurry.
  • the refining process may cause one or more of the following: removal of the primary walls, formation of fiber debris, internal and external fibrillation, fiber shortening, and increased fiber flexibility within the slurry.
  • Refining may be accomplished to achieve a desired freeness of pulp (e.g., targeting a certain number according to the Canadian Standard Method (CSF)).
  • CSF Canadian Standard Method
  • refining of the image layer pulp stock may be accomplished in a manner sufficient to target a CSF ranging from about 400 to about 450 for the hardwood fibers.
  • the salt e.g., in solution form
  • any additives can either be added to the slurry before or after refining.
  • the slurry may also be passed through a screen, which removes the larger debris but allows the fibers (and the additives and salt) to pass through the screen.
  • the smaller unwanted particles that remain after the screening are removed by a centrifugal cleaner, which uses centrifugal force and fluid shear to remove the smaller unwanted particles.
  • the smaller particles can be removed using this process, in part because the slurry components separate based on the particles weight and particle shape.
  • This slurry i.e., the image layer pulp stock
  • This slurry i.e., the image layer pulp stock
  • This slurry may be used in any examples of the method 100 shown in FIG. 1 to form examples of the image layer.
  • Examples of the pulp stock for the strength layer(s) include about 99% water.
  • the remaining component in the strength layer(s) pulp stock is the softwood fibers. In some instances, no other components are added. In other instances, other fibers and/or additives may be included in the strength layer pulp stock.
  • the softwood fibers included in the strength layer pulp stock(s) have an average length ranging from about 1.5 mm to about 3.0 mm.
  • the softwood fibers are present in an amount ranging from about 70 wt % to about 100 wt % of the solid components of the strength layer pulp stock.
  • suitable softwood fibers include pulp fibers derived from coniferous trees (gymnosperms), such as varieties of fir, spruce, and pine (e.g., loblolly pine, slash pine, Colorado spruce, balsam fir, and Douglas fir).
  • the pulp stock may also include up to 30 wt % of other fibers other than the softwood fibers. These other fibers may be a different type of fiber as, but have the same length as, the softwood fiber.
  • the other fibers may be natural fibers, virgin fibers, recycled fibers, non-deinkable fibers, unbleached fibers, synthetic fibers, mechanical fibers, or combinations thereof.
  • the strength layer pulp stock may include a bulk of softwood fibers with a low level of hardwood, recycled, or other types of fibers, such as cellulose fibers.
  • the softwood fibers and/or other fibers may be prepared via any known pulping process, such as, for example, chemical pulping processes. Two suitable chemical pulping methods include the kraft process and the sulphite process.
  • the softwood fibers may also be mechanically pulped, thermomechanically pulped, or chemi-thermomechanically pulped.
  • the image layer pulp stock may also contain up to 10 wt % (with respect to total solids) of an additive.
  • suitable additives for the strength layer pulp stock may include the dry strength additive, the wet strength additive, the filler, or a combination thereof. Any of the examples previously described may be used. In other instances, any of the additives (and amounts thereof) previously described for the image layer pulp stock may be used in the strength layer pulp stock.
  • the strength layer pulp stock may be made by incorporating at least the softwood fibers into a suitable amount of water to form a slurry. If the other fibers are included, they may be added into the slurry. As an example, the slurry may contain 99% water and 1% fibers, where 99% of the fibers are the softwood fibers disclosed herein and 1% of the fibers are other fibers.
  • the slurry may be refined. In another example, the slurry may not be refined. If the slurry is refined, the same process as previously described for the image layer slurry may be used.
  • the refining may be accomplished to achieve the desired freeness of pulp as described above (i.e., targeting a certain number according to the Canadian Standard Method (CSF)).
  • CSF Canadian Standard Method
  • refining of the strength layer pulp stock may be accomplished in a manner sufficient to target a CSF ranging from about 300 to about 500 for the softwood fibers.
  • any other desirable additives may be added to the refined or unrefined slurry.
  • the other additive(s) may be added as the slurry is refined.
  • the strength layer slurry may also undergo the same screening and cleaning process previously described for the image layer slurry. This slurry (i.e., the strength layer pulp stock) may be used in any examples of the method 100 shown in FIG. 1 to form examples of the strength layer.
  • the strength and image layer pulp stocks are jetted from respective headboxes of a traditional papermaking machine. Prior to jetting, the respective pulp stocks are introduced into respective headboxes in a suitable manner.
  • a packaging material with an image layer and a strength layer is formed.
  • An example of this packaging material 20 is shown in FIG. 2 .
  • the packaging material 20 includes the strength layer 24 having two opposed surfaces S 1 , S 2 and the image layer 22 in contact with one of the opposed surfaces S 1 of the strength layer 24 .
  • the method 100 includes the step of jetting, from a first headbox, the strength layer pulp stock (shown as “first” pulp stock in FIG. 1 ) onto a wire to form a strength layer precursor. This is shown at step 102 .
  • the strength layer precursor is a wet web of at least the softwood fibers.
  • the method 100 also includes, at step 104 , jetting, from a second headbox, the image layer pulp stock (shown as “second” pulp stock in FIG. 1 ) onto a second wire to form an image layer precursor.
  • the wire upon which the strength layer precursor is formed is different than the second wire upon which the image layer precursor is formed.
  • the image layer precursor is a wet web of at least the hardwood fibers and the salt.
  • the image layer precursor and strength layer precursor are placed into contact with each other. It is desirable that when the precursors are in contact, the image layer precursor should overlie the strength layer precursor. Placing the precursors in contact may be accomplished by moving the respective wires so that respective surfaces of the image layer precursor and the strength layer precursor are adjacent to one another and touch.
  • water removal may be passive, where water is allowed to drain, filter, etc. from the strength layer precursor prior to applying the image layer precursor. Water removal may be accomplished so that the consistency (or concentration) is increased to a desirable level.
  • Consistency is defined as the weight in grams of oven-dry fiber in 100 grams of pulp-water mixture (i.e., pulp stock).
  • TAPPI Test method TAPPI/ANSI T 240 entitled “Consistency (concentration) of pulp suspensions” may be used.
  • the consistency of the initial strength layer pulp stock is around 1% (e.g., including about 99% water and 1% solids).
  • the water begins to drain from the pulp stock, thereby increasing the consistency. It may be desirable to remove (e.g., by draining) a certain amount of the water from the strength layer precursor prior to bringing the image layer precursor in contact therewith.
  • the strength layer precursor may be exposed to drying (e.g., filtering, draining, etc.) in order to obtain a consistency ranging from about 5% to about 30%.
  • desirable strength layer precursor consistency levels Prior to image layer precursor application) include 5%, 10%, 15%, or 20%.
  • a higher consistency i.e., less water in the strength layer precursor
  • This wet-on-wet process is advantageous, in part because subsequent papermaking steps (e.g., removing water, drying, etc.) do not have to be performed separately for each layer of the multi-layered structure.
  • subsequent papermaking steps e.g., removing water, drying, etc.
  • the wet-on-wet process improves the adhesion between the layers by increasing bonding strength due to hydrogen bonding.
  • the remaining water is removed from the image layer precursor and strength layer precursor (as shown at step 128 ).
  • Some remaining water may be removed from the precursors in a press section of the papermaking machine. In an example, water removal is accomplished using rollers under high pressure. The precursors are passed between the rollers to squeeze out as much water as possible. Water removal may also be accomplished using a filtration process. It is to be understood that some water may remain in the precursors after the removal process takes place.
  • the orientation of the precursors during water removal is such that the image layer precursor overlies the strength layer precursor. This is desirable because the water drains generally in a direction toward the surface S 2 of the strength layer precursor. As the water is drained, salt from the image layer precursor may have a tendency to migrate with the water. However, the strength layer precursor aids in keeping most if not all of the salt from moving with the water. This is due, at least in part, to the strength layer low porosity fiber mat creating a barrier layer. The fiber mat enables at least the bulk of the salt to be maintained within the image layer precursor. As discussed above, increased dryness/consistency of the strength layer precursor before coming in contact with image layer precursor will also increase the salt retention. As such, salt retention may be at least partially controlled by controlling the consistency of the strength layer precursor.
  • the strength layer 24 that is ultimately formed may also contain some of the di-valent or multi-valent salt that migrated from the image layer precursor.
  • the di-valent or multi-valent salt present in the final image layer 22 is at least five times the amount of the di-valent or multi-valent salt present in the final strength layer 24 .
  • the final step 130 of this example of method 100 includes drying the strength layer precursor and image layer precursor to form the packaging material, which includes the image layer 22 and the strength layer 24 . Drying may be accomplished in any suitable manner. In an example, a series of steam heated drying cylinders are utilized, and the pressed precursors are passed around these cylinders. Drying removes excess water from the packaging material 20 that is formed; although it is to be understood that some water may still remain in the respective layers 22 , 24 .
  • the packaging material 20 may also be exposed to a calendering.
  • Calendering may be performed in a typical manner, e.g., using heavy steel rollers. The rollers apply pressure to the passing packaging material 20 to smooth and/or enhance the gloss of the packaging material 20 .
  • One or more nips may be used in the calendering process.
  • the packaging material 20 may also be exposed to a reeling process.
  • a reel is used to wind the packaging material 20 to form a roll.
  • An example of image layer 22 may be formed from the image layer pulp stock including water, 100 wt % (with respect to solids in the pulp stock) unbleached hardwood fibers having the length within the range provided herein, CaCl 2 as the salt in an amount of 12 lb per ton of the total fiber in the image layer pulp stock, cationic starch as an additive in an amount of 20 lb per ton of the total fiber in the image layer pulp stock, and AKD (alkyl ketene dimer) as another additive in the amount of 5 lb per ton of the total fiber in the image layer pulp stock.
  • CaCl 2 as the salt in an amount of 12 lb per ton of the total fiber in the image layer pulp stock
  • cationic starch as an additive in an amount of 20 lb per ton of the total fiber in the image layer pulp stock
  • AKD alkyl ketene dimer
  • Another example of the image layer 22 may be formed from the image layer pulp stock including water, 70 wt % unbleached hardwood fibers having the length within the range provided herein, 30 wt % unbleached softwood fibers, CaCl 2 as the salt in an amount of 12 lb per ton of the total fiber in the image layer pulp stock, cationic starch as an additive in an amount of 20 lb per ton of the total fiber in the image layer pulp stock, and AKD as another additive in the amount of 5 lb per ton of the total fiber in the image layer pulp stock).
  • An example of strength layer 24 of the packaging material 20 is formed from the strength layer pulp stock including water and 100 wt % unbleached softwood fibers having the length within the range provided herein.
  • one of the previously described image layer pulp stocks and strength layer pulp stock are jetted separately and put into contact. After the image layer pulp stocks and strength layer pulp stock are placed in contact, they are exposed to water removal, dried, and in some instances calendered/reeled as previously described to form the packaging material 20 having the layers 22 , 24 adhered to one another.
  • one of the previously described image layer pulp stocks and strength layer pulp stock are jetted separately and put into contact once the strength layer consistency (dryness) has reached a desirable level, e.g., 20%.
  • the image layer pulp stocks and strength layer pulp stock are placed in contact, they are exposed to further water removal through filtration, pressing and drying, and in some instances calendered/reeled as previously described to form the packaging material 20 having the layers 22 , 24 adhered to one another.
  • the image layer pulp stock may be jetted directly onto the strength layer pulp stock, and then the pulp stocks are exposed to water removal, drying, etc.
  • the layers 22 , 24 that are formed have approximately the same amount of the fibers, and in some instances salt and/or additives, which are used in the respective pulp stocks, taking into account minor loss due to the water removal process.
  • FIG. 3 An example of this packaging material 20 ′ is shown in FIG. 3 .
  • the packaging material 20 ′ includes the strength layer 24 having the two opposed surfaces S 1 , S 2 , a second strength layer 24 ′ in contact with one of the opposed surfaces S 1 , and the image layer 22 in contact with the second strength layer 24 ′.
  • step 102 may be performed, which forms the strength layer precursor (in this example, the precursor to strength layer 24 ). This step may be performed in the manner previously described.
  • the method 100 also includes step 106 , where a strength layer pulp stock (referred to as the third pulp stock in box 106 in FIG. 1 ) is jetted from another (e.g., third) headbox onto another (e.g., third) wire to form a second strength layer precursor.
  • This second strength layer precursor ultimately forms the second strength layer 24 ′ shown in FIG. 3 (i.e., the middle layer of the multi-layered packaging material 20 ′).
  • the second strength layer pulp stock (i.e., third pulp stock in FIG. 1 ) may include any of the components previously described for the strength layer pulp stock (used in step 102 ) and may be made by the same process.
  • the second strength layer pulp stock may include from about 50 wt % to about 100 wt % of the softwood fibers having the length ranging from about 1.5 mm to about 3.0 mm.
  • the strength layer pulp stock used to form strength layer 24 may be the same as the second strength layer pulp stock used to form the second strength layer 24 ′.
  • each of the strength layer pulp stocks may include the same type and amount of softwood fibers, with or without the same amount and type of additive(s).
  • the strength layer pulp stock used to form strength layer 24 may be different than the second strength layer pulp stock used to form the second strength layer 24 ′.
  • the second strength layer pulp stock may include a different type and length of softwood fibers than are present in the strength layer pulp stock.
  • This example of the method 100 also includes step 104 , which forms the image layer precursor (in this example, the precursor to image layer 22 ). This step may also be performed in the manner previously described.
  • the strength layer precursor, the second strength layer precursor, and the image layer precursor are then placed into contact with each other (as shown at step 108 ). It is to be understood that water from one or both of the strength layer precursors may be allowed to drain so that the precursor(s) have a desired consistency before being placed into contact with the image layer precursor.
  • the image layer precursor should overlie the strength and second strength layer precursors. Placing the precursors in contact may be accomplished by moving the respective wires so that respective surfaces of the image layer precursor and the second strength layer precursor are adjacent to one another and touch, and such that respective surfaces of the second strength layer precursor and the strength layer precursor are adjacent to one another and touch.
  • the second strength layer precursor and the strength layer precursor may be placed into contact first by moving the corresponding wires into an appropriate position. Then the image layer precursor may be placed into contact with the exposed surface of the second strength layer precursor by moving at least the wire upon which the image layer precursor is formed adjacent to the exposed surface.
  • the layering of the precursors is a wet-on-wet process.
  • the layered precursors form a stack, which includes the image layer precursor positioned as one of the outermost layers of the stack.
  • Step 110 of this example of the method 100 includes removing the water from the stack.
  • Water removal may accomplished by any suitable process, including the use of high pressure and roller or filtration.
  • the orientation of the precursors during water removal is such that the image layer precursor overlies both the second strength layer precursor and the strength layer precursor. This is desirable because, as described above, the water drains generally in a direction toward the opposed surface S 2 of the strength layer precursor.
  • salt from the image layer precursor may have a tendency to migrate with the water.
  • the softwood fibers, porosity, and consistency of the strength and second strength layer precursors keep most, if not all, of the salt from moving with the water by forming the fiber mat previously discussed.
  • Step 112 includes drying the stack of the image layer precursor, the second strength layer precursor, and the strength layer precursor to form the packaging material 20 ′.
  • the packaging material 20 ′ may also be exposed to a calendering or reeling process, as described above.
  • An example of image layer 22 may be formed from the image layer pulp stock including water, 100 wt % bleached hardwood fibers having the length within the range provided herein, CaCl 2 as the salt in an amount of 12 lb per ton of the total fiber in the image layer pulp stock, cationic starch as an additive in an amount of 20 lb per ton of the total fiber in the image layer pulp stock, and AKD (alkyl ketene dimer) as another additive in the amount of 5 lb per ton of the total fiber in the image layer pulp stock.
  • CaCl 2 as the salt in an amount of 12 lb per ton of the total fiber in the image layer pulp stock
  • cationic starch as an additive in an amount of 20 lb per ton of the total fiber in the image layer pulp stock
  • AKD alkyl ketene dimer
  • An example of strength layer 24 of the packaging material 20 ′ is formed from the strength layer pulp stock including water and 100 wt % unbleached softwood fibers having the length within the range provided herein.
  • An example of strength layer 24 ′ of the packaging material 20 ′ is formed from the second strength layer pulp stock including water, 50 wt % recycled fibers, 50% bleached chemi-thermomechanical fibers.
  • the second strength layer pulp stock may include the previously listed components as well as a dry strength additive, and may be formed without any refining.
  • the previously described image layer pulp stock, strength layer pulp stock, and one of the second strength layer pulp stocks are jetted separately and the precursors are put into contact (with or without altering the consistency of the strength layer precursor(s)), exposed to water removal, dried, and in some instances calendered/reeled as previously described to form the packaging material 20 ′ having the layers 22 , 24 ′, 24 adhered to one another.
  • the layers 22 , 24 ′, 24 that are formed have approximately the same amount of the fibers, and in some instances salt and/or additives, which are used in the respective pulp stocks, taking into account minor loss due to the water removal process.
  • FIG. 4 An example of this packaging material 20 ′′ is shown in FIG. 4 .
  • the packaging material 20 ′′ includes two strength sub-layers 24 A , 24 B forming the strength layer 24 , and respective image layers 22 , 22 ′ on opposed surfaces S 1 , S 2 of the strength layer 24 .
  • bi-layer structures are formed and then placed into contact with one another.
  • One of the bi-layer structures is formed in steps 102 , 104 , 118 , and 122 ; and another of the bi-layer structures is formed in steps 114 , 116 , 120 , and 124 .
  • step 102 may be performed. This step may be performed as previously described. Step 102 forms the strength layer precursor, which in this example is a precursor to strength sub-layer 24 A and a portion of strength layer 24 . Step 104 may then be performed as previously described to generate the image layer precursor, which is a precursor to the image layer 22 .
  • step 118 the image layer precursor (formed in step 104 ) and the strength layer precursor (formed in step 102 ) are placed into contact to form the bi-precursor structure.
  • the strength layer precursor (formed in step 102 ) may have its consistency increased in the manner previously described herein. Placing these precursors into contact may be accomplished as previously described in reference to step 126 of the first example of the method 100 .
  • step 122 water is removed from the bi-precursor structure in any suitable manner, such as those previously described in reference to step 130 of the first example of the method 100 disclosed herein.
  • Orientation of the bi-precursor structure during water removal is such that the image layer precursor overlies the strength layer precursor. As previously described, this is desirable because the softwood fibers in the strength layer precursor keep most if not all of the salt from moving with the water out of the image layer precursor.
  • step 114 may be performed to generate a second strength layer precursor, which in this example is a precursor to strength sub-layer 24 B and to another portion of strength layer 24 . Since the strength sub-layer 24 B and the strength sub-layer 24 A make up portions of the same strength layer 24 , it is desirable that the second strength layer pulp stock (i.e., third pulp stock in box 114 of FIG. 1 ) have the same composition as the strength layer pulp stock used to form the precursor to the strength sub-layer 24 A (formed in step 102 ). As such, the second strength layer pulp stock (i.e., third pulp stock in box 114 of FIG.
  • the second strength layer pulp stock may, in some instances, have a different type of softwood fiber than the strength layer pulp stock used to form the precursor to the strength sub-layer 24 A .
  • the second strength layer pulp stock (i.e., third pulp stock in box 114 of FIG. 1 ) is jetted from another (e.g., third) headbox onto another (e.g., third) wire to form the second strength layer precursor.
  • Step 116 may then be performed to generate another image layer precursor.
  • the second image layer pulp stock i.e., fourth pulp stock in box 116 of FIG. 1
  • another (e.g., fourth) headbox onto another (e.g., fourth) wire to form the second image layer precursor.
  • This image layer precursor ultimately forms image layer 22 ′.
  • the image layer precursor formed at step 116 may be made using any example of the image layer pulp stock described herein. If it is desirable the final image layer 22 ′ have the same composition as the final image layer 22 , then the image layer pulp stock used in step 104 may be the same as the image layer pulp stock (i.e., fourth pulp stock in box 116 of FIG. 1 ) used in step 116 . However, if it is desirable that the final image layer 22 ′ have a different composition than the final image layer 22 , then the image layer pulp stock used in step 104 may be different than the image layer pulp stock (i.e., fourth pulp stock in box 116 of FIG. 1 ) used in step 116 .
  • the image layer pulp stock (i.e., fourth pulp stock in box 116 of FIG. 1 ) used to form the second image layer precursor in this example of the method 100 , may include water, hardwood fibers (having a length ranging from about 0.5 mm to about 1.5 mm) present in an amount ranging from about 70 wt % to about 100 wt % of total solids, salt, and if desirable, other fibers and/or additives. Suitable amounts for any of these components are previously described in reference to step 104 .
  • step 120 the second image layer precursor (formed in step 116 ) and the second strength layer precursor (formed in step 114 ) are placed into contact to form the other bi-precursor structure.
  • the second strength layer precursor formed in step 116
  • the second strength layer precursor may have its consistency increased in the manner previously described herein. Placing these precursors into contact may be accomplished as previously described in reference to step 126 of the first example of the method 100 .
  • step 124 water is removed from the other bi-precursor structure in any suitable manner, such as those previously described in reference to step 130 of the first example of the method 100 .
  • Orientation of the bi-precursor structure during water removal is such that the second image layer precursor overlies the second strength layer precursor. As previously described, this is desirable because the softwood fibers in the second strength layer precursor keep most if not all of the salt from moving with the water out of the second image layer precursor.
  • Step 132 involves placing the bi-precursor structures in contact so that a stack is formed.
  • the stack has the two strength layer precursors positioned so that they are adjacent to and touch one another.
  • precursors to the sub-layers 24 A and 24 B are formed.
  • the precursors may be compressed together using rollers under high pressure and the resulting packaging material 20 ′′ may be considered to have a single strength layer 24 . This process is similar to processing using a wet press.
  • each of the image layer precursors of the respective bi-precursor structure faces outward. This is desirable when dual-sided printing on the packaging material 20 ′′ is to be performed.
  • Step 134 includes drying the stack of the image layer precursor, the strength layer precursors, and the second image layer precursor to form the packaging material 20 ′′.
  • the packaging material 20 ′′ may also be exposed to a calendering or reeling process, as described above.
  • image layers 22 , 22 ′ may be formed from image layer pulp stocks including water, 100 wt % bleached hardwood fibers having the length within the range provided herein, CaCl 2 as the salt in an amount of 12 lb per ton of the total fiber in the image layer pulp stock, cationic starch as an additive in an amount of 20 lb per ton of the total fiber in the image layer pulp stock, and AKD (alkyl ketene dimer) as another additive in the amount of 5 lb per ton of the total fiber in the image layer pulp stock.
  • the sub-layers 24 A , 24 B of the strength layer 24 may be formed from a single strength layer pulp stock including water and 100 wt % unbleached softwood fibers having the length within the range provided herein.
  • the number and types of pulp stocks that will be used will depend, at least in part, on which layers are desired in the final packaging material 20 , 20 ′, 20 ′′.
  • the packaging material 20 , 20 ′, 20 ′′ will include at least the strength layer 24 and the image layer 22 .
  • Example 1 Two samples of the packaging material disclosed herein were prepared along with a control sample.
  • the control (sample 1), was Mottle White #3 media, which is a commercially available 2 layer packaging paper that does not include any salt. No salt was added to sample 1.
  • Samples 2 and 3 used the same Mottle White #3 media as the packaging material, except that CaCl 2 was added to one of the layers.
  • the amount salt present in teach of samples 1-3 is shown in Table 1 below.
  • the black optical density (KoD) was determined using an X-Rite densitometer. The higher KoD measurement demonstrates an improved printability on the packaging material. As shown in Table 1, samples 2 and 3 both had an improved printability with the addition of CaCl 2 , as compared to sample 1 without any salt.
  • ranges provided herein include the stated range and any value or sub-range within the stated range.
  • a range from about 50 wt % to about 100 wt % should be interpreted to include not only the explicitly recited limits of about 50 wt % to about 100 wt %, but also to include individual values, such as 60 wt %, 75 wt %, 90 wt %, etc., and sub-ranges, such as from about 65.5 wt % to about 95 wt %, from about 55 wt % to about 75 wt %, etc.
  • “about” is utilized to describe a value, this is meant to encompass minor variations (up to +/ ⁇ 10%) from the stated value.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Paper (AREA)
US15/122,039 2014-04-23 2014-04-23 Packaging material and method for making the same Abandoned US20170073902A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2014/035138 WO2015163870A1 (en) 2014-04-23 2014-04-23 Packaging material and method for making the same

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2014/035138 A-371-Of-International WO2015163870A1 (en) 2014-04-23 2014-04-23 Packaging material and method for making the same

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US16/261,537 Division US10760220B2 (en) 2014-04-23 2019-01-29 Packaging material and method for making the same

Publications (1)

Publication Number Publication Date
US20170073902A1 true US20170073902A1 (en) 2017-03-16

Family

ID=54332902

Family Applications (2)

Application Number Title Priority Date Filing Date
US15/122,039 Abandoned US20170073902A1 (en) 2014-04-23 2014-04-23 Packaging material and method for making the same
US16/261,537 Expired - Fee Related US10760220B2 (en) 2014-04-23 2019-01-29 Packaging material and method for making the same

Family Applications After (1)

Application Number Title Priority Date Filing Date
US16/261,537 Expired - Fee Related US10760220B2 (en) 2014-04-23 2019-01-29 Packaging material and method for making the same

Country Status (3)

Country Link
US (2) US20170073902A1 (de)
EP (1) EP3134573B1 (de)
WO (1) WO2015163870A1 (de)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10760220B2 (en) * 2014-04-23 2020-09-01 Hewlett-Packard Development Company, L.P. Packaging material and method for making the same
WO2024039387A1 (en) * 2022-08-19 2024-02-22 Paul Zhang Multi-layer composite pulp product, and system and process for manufacturing same

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11015287B1 (en) 2020-06-30 2021-05-25 International Paper Company Processes for making improved cellulose-based materials and containers
US12157976B2 (en) * 2022-08-03 2024-12-03 World Centric Moisture/oil resistant composite materials

Family Cites Families (60)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1961365A (en) 1931-11-02 1934-06-05 Du Pont Manufacture of multi-ply paper board
US2234457A (en) 1937-10-09 1941-03-11 Bennett Inc Paperboard manufacture
US2286924A (en) * 1938-01-12 1942-06-16 Int Paper Co Manufacture of sheet material
US2942661A (en) * 1956-12-18 1960-06-28 Beloit Iron Works Multi-ply sheet former
US3752734A (en) * 1970-08-12 1973-08-14 Black Clawson Co Multi ply paper machine
JPS513203Y2 (de) * 1972-02-29 1976-01-30
US4071651A (en) 1974-10-10 1978-01-31 Karl Kroyer St. Anne's Limited Treatment of fibrous material
GB8703627D0 (en) * 1987-02-17 1987-03-25 Wiggins Teape Group Ltd Photographic base paper
GB8710428D0 (en) * 1987-05-01 1987-06-03 Beloit Corp Multi-ply web forming apparatus
US4892590A (en) 1988-06-03 1990-01-09 Pfizer Inc. Precipitated calcium carbonate-cationic starch binder as retention aid system for papermaking
GB8906275D0 (en) * 1989-03-18 1989-05-04 Beloit Corp Web former
DE4031038C2 (de) * 1990-10-01 1997-01-23 Voith Sulzer Papiermasch Gmbh Vorrichtung zum Herstellen eines mehrlagigen Papiers oder Kartons
US5055161A (en) 1991-02-21 1991-10-08 Green Bay Packaging Inc. Multiple ply paper product containing an outer ply of reclaimed white office waste
DE19651493A1 (de) * 1996-12-11 1998-06-18 Voith Sulzer Papiermasch Gmbh Siebpartie und Verfahren zum Formen einer mehrlagigen Faserstoffbahn
CA2325852A1 (en) * 1997-04-22 1998-10-29 Beloit Technologies, Inc. A forming apparatus for forming a web
US5851352A (en) 1997-05-12 1998-12-22 The Procter & Gamble Company Soft multi-ply tissue paper having a surface deposited strengthening agent
SE510341C2 (sv) * 1997-08-19 1999-05-17 Sca Research Ab Metod och anordning för formning av en flerskiktsbana
US5916417A (en) 1997-08-22 1999-06-29 International Paper Company Method of making multi-ply paperboard sheet having layers of different fiber properties
US6107014A (en) 1998-06-09 2000-08-22 Eastman Kodak Company Raw stock for photographic paper
JP4694691B2 (ja) 1998-09-03 2011-06-08 ストゥラ エンソ アクチボラグ 紙または板紙の積層体および積層体を製造する方法
US6287424B1 (en) * 1998-09-22 2001-09-11 International Paper Company Method for finishing paperboard to achieve improved smoothness
JP2000118155A (ja) 1998-10-14 2000-04-25 Toppan Printing Co Ltd 熱転写受像シート及びその製造方法
US6207362B1 (en) 1999-09-09 2001-03-27 Eastman Kodak Company Tough durable imaging cellulose base material
DE19951928A1 (de) * 1999-10-28 2001-05-03 Voith Paper Patent Gmbh Blattbildungsvorrichtung
US7070854B2 (en) 2001-03-22 2006-07-04 Kimberly-Clark Worldwide, Inc. Water-dispersible, cationic polymers, a method of making same and items using same
US6797114B2 (en) * 2001-12-19 2004-09-28 Kimberly-Clark Worldwide, Inc. Tissue products
MXPA04007332A (es) 2002-02-02 2005-05-17 Voith Paper Patent Gmbh Metodo para preparar fibras contenidas en una suspension de pulpa.
US6669814B2 (en) 2002-03-08 2003-12-30 Rock-Tenn Company Multi-ply paperboard prepared from recycled materials and methods of manufacturing same
FI116688B (fi) * 2004-02-13 2006-01-31 Metso Paper Inc Monikerrosrainan muodostusosa
JP4250121B2 (ja) 2004-07-02 2009-04-08 富士フイルム株式会社 インクジェット記録用媒体
US7491293B2 (en) * 2004-09-29 2009-02-17 Meadwestvaco Corporation White top paperboard
US7906218B2 (en) * 2004-11-30 2011-03-15 Hewlett-Packard Development Company, L.P. System and a method for inkjet image supporting medium
JP2006219775A (ja) 2005-02-09 2006-08-24 Hokuetsu Paper Mills Ltd 液体容器用原紙
JP4741287B2 (ja) 2005-05-19 2011-08-03 富士フイルム株式会社 インクジェット記録用媒体の製造方法
US8758886B2 (en) * 2005-10-14 2014-06-24 International Paper Company Recording sheet with improved image dry time
FI118605B (fi) * 2005-10-26 2008-01-15 Metso Paper Inc Rainanmuodostusosa ja menetelmä monikerrosrainan valmistamiseksi
US7820874B2 (en) 2006-02-10 2010-10-26 The Procter & Gamble Company Acacia fiber-containing fibrous structures and methods for making same
US20070202283A1 (en) 2006-02-27 2007-08-30 John Meazle Reducing top ply basis weight of white top linerboard in paper or paperboard
JP2010511798A (ja) 2006-12-01 2010-04-15 アクゾ ノーベル ナムローゼ フェンノートシャップ 包装材積層体
US8414738B2 (en) 2007-08-30 2013-04-09 Kimberly-Clark Worldwide, Inc. Multiple ply paper product with improved ply attachment and environmental sustainability
US20110177264A1 (en) 2008-09-26 2011-07-21 Fujifilm Corporation Inkjet recording medium and method of manufacturing the same
US8585866B2 (en) * 2010-07-23 2013-11-19 Oji Holdings Corporation Wire for papermaking of microfibrous cellulose-containing sheet and method for producing microfibrous cellulose-containing sheet
KR101861529B1 (ko) 2010-10-01 2018-06-29 에프피이노베이션스 셀룰로스-강화된 고 무기질 함량 제품 및 그의 제조 방법
US9358576B2 (en) 2010-11-05 2016-06-07 International Paper Company Packaging material having moisture barrier and methods for preparing same
EP2640894B2 (de) 2010-11-17 2020-07-01 Hewlett-Packard Development Company, L.P. Oberflächenleimungszusammensetzung für druckmedien im digitaldruck
US9005738B2 (en) 2010-12-08 2015-04-14 Buckeye Technologies Inc. Dispersible nonwoven wipe material
WO2012105939A1 (en) * 2011-01-31 2012-08-09 Hewlett-Packard Development Company, L.P. Graphic medium and method of making same
WO2012134455A1 (en) * 2011-03-29 2012-10-04 Hewlett-Packard Development Company, L.P. Inkjet media
US10543707B2 (en) * 2011-04-28 2020-01-28 Hewlett-Packard Development Company, L.P. Recording media
CN103502018B (zh) * 2011-04-28 2015-01-14 惠普发展公司，有限责任合伙企业 高速数字喷墨卷筒纸印刷机印刷中使用的介质及其制备方法
WO2013015767A1 (en) 2011-07-22 2013-01-31 Hewlett-Packard Development Company, L.P. Inkjet recording medium
US9267240B2 (en) 2011-07-28 2016-02-23 Georgia-Pacific Products LP High softness, high durability bath tissue incorporating high lignin eucalyptus fiber
US9309627B2 (en) 2011-07-28 2016-04-12 Georgia-Pacific Consumer Products Lp High softness, high durability bath tissues with temporary wet strength
US9180716B2 (en) 2012-07-09 2015-11-10 Hewlett-Packard Development Company, L.P. Recording material
US8968517B2 (en) 2012-08-03 2015-03-03 First Quality Tissue, Llc Soft through air dried tissue
US20170073902A1 (en) * 2014-04-23 2017-03-16 Hewlett-Packard Development Company, L.P. Packaging material and method for making the same
US9719213B2 (en) 2014-12-05 2017-08-01 First Quality Tissue, Llc Towel with quality wet scrubbing properties at relatively low basis weight and an apparatus and method for producing same
US9962981B2 (en) 2015-01-28 2018-05-08 Hewlett-Packard Development Company, L.P. Printable recording media
SE538863C2 (sv) 2015-05-22 2017-01-10 Innventia Ab Process for the production of paper or paperboard, paper or paperboard product obtained and uses thereof
US10280565B2 (en) 2016-02-26 2019-05-07 Ecolab Usa Inc. Drainage management in multi-ply papermaking

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10760220B2 (en) * 2014-04-23 2020-09-01 Hewlett-Packard Development Company, L.P. Packaging material and method for making the same
WO2024039387A1 (en) * 2022-08-19 2024-02-22 Paul Zhang Multi-layer composite pulp product, and system and process for manufacturing same

Also Published As

Publication number Publication date
US10760220B2 (en) 2020-09-01
EP3134573A1 (de) 2017-03-01
EP3134573A4 (de) 2017-05-03
EP3134573B1 (de) 2018-04-04
US20190153676A1 (en) 2019-05-23
WO2015163870A1 (en) 2015-10-29

Similar Documents

Publication Publication Date Title
US10760220B2 (en) Packaging material and method for making the same
JP5288062B2 (ja) 非塗工紙及び塗工紙
JP5555825B2 (ja) 繊維製品の製造方法
JP6297253B2 (ja) 白板紙
JP6117133B2 (ja) 白板紙及びその製造方法
KR20140002777A (ko) 디지털 고속 잉크젯 웨브 프레스 인쇄에 이용되는 매체
JP7698701B2 (ja) 包装用紙
US9855780B2 (en) Print media for inkjet printing
US20240133118A1 (en) Method for manufacturing a barrier film comprising highly refined cellulose
JP6115326B2 (ja) 印刷用塗工紙および印刷用塗工紙の製造方法
JP2018015943A (ja) インクジェット用紙
JP6942623B2 (ja) 耐油紙及びその製造方法
JP6196932B2 (ja) オフセット印刷用塗工紙の製造方法及びオフセット印刷用塗工紙
JP2018131715A (ja) 水分吸収シート用原紙および水分吸収シート
JP5894902B2 (ja) 白板紙の製造方法
JP2020029626A (ja) 透明紙
JP5971856B2 (ja) 中質印刷用紙及びその製造方法
KR20220069098A (ko) 내유지 및 내유지의 제조 방법
US20220002947A1 (en) Book printing paper
EP4524323A1 (de) Verfahren zur herstellung eines papiersubstrats
JP7569295B2 (ja) 包装用紙
JP2011256467A (ja) 耐油紙
JP6697110B2 (ja) インクジェット記録用紙
JP5885643B2 (ja) 中質印刷用紙及びその製造方法
JP2025038803A (ja) 電子レンジ用包装用紙

Legal Events

Date Code Title Description
AS Assignment

Owner name: HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P., TEXAS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:PAL, LOKENDRA;FU, XULONG;ZHOU, XIAOQI;REEL/FRAME:039602/0509

Effective date: 20140506

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION