Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
  • H01M50/10—Primary casings; Jackets or wrappings
  • H01M50/183—Sealing members
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D123/00—Coating compositions based on homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Coating compositions based on derivatives of such polymers
  • C09D123/02—Coating compositions based on homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Coating compositions based on derivatives of such polymers not modified by chemical after-treatment
  • C09D123/10—Homopolymers or copolymers of propene
  • C09D123/12—Polypropene
• • H01M2/08—
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/06—Polyethylene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/10—Homopolymers or copolymers of propene
  • C08L23/12—Polypropene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/26—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers modified by chemical after-treatment
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D123/00—Coating compositions based on homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Coating compositions based on derivatives of such polymers
  • C09D123/02—Coating compositions based on homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Coating compositions based on derivatives of such polymers not modified by chemical after-treatment
  • C09D123/04—Homopolymers or copolymers of ethene
  • C09D123/06—Polyethylene
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
  • C09D5/02—Emulsion paints including aerosols
  • C09D5/022—Emulsions, e.g. oil in water
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J123/00—Adhesives based on homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Adhesives based on derivatives of such polymers
  • C09J123/02—Adhesives based on homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Adhesives based on derivatives of such polymers not modified by chemical after-treatment
  • C09J123/04—Homopolymers or copolymers of ethene
  • C09J123/08—Copolymers of ethene
  • C09J123/0846—Copolymers of ethene with unsaturated hydrocarbons containing other atoms than carbon or hydrogen atoms
  • C09J123/0869—Acids or derivatives thereof
  • C09J123/0876—Neutralised polymers, i.e. ionomers
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/052—Li-accumulators
  • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
  • H01M50/10—Primary casings; Jackets or wrappings
  • H01M50/183—Sealing members
  • H01M50/19—Sealing members characterised by the material
  • H01M50/193—Organic material
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
  • H01M50/10—Primary casings; Jackets or wrappings
  • H01M50/183—Sealing members
  • H01M50/19—Sealing members characterised by the material
  • H01M50/198—Sealing members characterised by the material characterised by physical properties, e.g. adhesiveness or hardness
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2201/00—Properties
  • C08L2201/54—Aqueous solutions or dispersions
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M2300/00—Electrolytes
  • H01M2300/0017—Non-aqueous electrolytes
  • H01M2300/0025—Organic electrolyte
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
  • Y02E60/10—Energy storage using batteries

Definitions

• the present disclosure relates to an aqueous sealant composition used for a nonaqueous electrolyte battery.
• Lithium ion secondary batteries are widely used as power sources for small electronic devices such as notebook computers, mobile phones, PDAs, and the like. Further, in recent years, lithium ion secondary batteries are also used for automotive applications. As the usage range of lithium ion secondary batteries expands, demands for the performance and safety of lithium ion secondary batteries (hereinafter sometimes simply referred to as “batteries”) are increasing. These batteries are usually repeatedly used by virtue of charge and discharge operations. However, due to repeated charge and discharge, sometimes volume fluctuation and heat generation occur in the electrodes, and the pressure inside the battery rises, such that the electrolytic solution leaks to the outside.
• a lithium ion secondary battery is housed in a metal container to seal its power generating element, and in order to prevent a short circuit between the positive electrode and the negative electrode, it is necessary to insulate the positive electrode terminal from the negative electrode terminal.
• a gasket made of an insulating material is used in the opening of the metal container containing the power generating element for insulation and sealing between the positive electrode and the negative electrode.
• the insulating material it is well known to use a resin insulating gasket (for example, refer to PTL 1).
• an insulating gasket and a sealant in combination (for example, refer to PTL 2 to 4).
• the sealability between the insulating gasket and the metal container is enhanced by applying a sealant to the insulating gasket or the metal container and then attaching the insulating gasket to the metal container.
• Examples of such a sealant include pitch-based materials such as coal tar, asphalt and the like, and materials obtained by adding a polymer as a modifier to a pitch-based material (for example, refer to PTL 5).
• pitch-based materials such as coal tar, asphalt and the like
• materials obtained by adding a polymer as a modifier to a pitch-based material for example, refer to PTL 5
• a butyl rubber for example, refer to PTL 6
• a diene rubber having a predetermined weight-average molecular weight for example, refer to PTL 7
• a block polymer containing a diene monomer for example, refer to PTL 8 are also proposed.
• VOC volatile organic compounds
• PTL 9 proposes an aqueous sealant composition, however, the performance thereof required for a sealant is insufficient. For example, the strength of the sealant layer formed by the aqueous sealant composition is insufficient compared with a sealant layer obtained by a sealant composition using an organic solvent.
• PTL 10 proposes an aqueous sealant composition not using VOC, however, it is intended for a battery using an aqueous electrolyte solution, and no consideration has been given to a nonaqueous electrolyte battery.
• An objective of the present disclosure is to provide an aqueous sealant composition for a nonaqueous electrolyte battery by which a sealant layer having excellent properties can be obtained.
• the present disclosure provides the following.
• An aqueous sealant composition for a nonaqueous electrolyte battery comprising an aqueous dispersion in an amount of 70 mass % or more and 97 mass % or less by mass of solid content, wherein the aqueous dispersion comprises an olefinic polymer as a main component.
• aqueous sealant composition for a nonaqueous electrolyte battery according to (1) further comprising: a water-soluble polymer in an amount of 3 mass % or more and 30 mass % or less by mass of solid content; and a total solid content concentration of 5 mass % or more and 70 mass % or less.
• aqueous sealant composition for a nonaqueous electrolyte battery according to any one of (1) to (3), wherein the aqueous dispersion is a dispersion of polyethylene or polypropylene in water, or a self-emulsified modified olefinic polymer.
• a sealant layer having excellent properties can be obtained.
• aqueous sealant composition for a nonaqueous electrolyte battery according to the present disclosure.
• the presently disclosed aqueous sealant composition for a nonaqueous electrolyte battery (hereinafter referred to also as “aqueous sealant composition”) comprises an aqueous dispersion in an amount of 70 mass % or more and 97 mass % or less by mass of solid content, wherein the aqueous dispersion comprises an olefinic polymer as a main component.
• the olefinic polymer comprised as a main component in the aqueous dispersion is not particularly limited as long as it is a polymer comprising an olefinic monomer unit obtained by polymerizing an olefinic monomer such as ethylene, propylene or the like.
• the olefinic polymer is preferably comprised in the aqueous dispersion in an amount of 20 mass % or more and 100 mass % or less, and more preferably in an amount of 30 mass % or more and 100 mass % or less by mass of solid content (in terms of solid content).
• the solid content concentration of the aqueous dispersion comprising the olefinic polymer as a main component is preferably 20 mass % or more, more preferably 30 mass % or more, and preferably 70 mass % or less, more preferably 65 mass % or less.
• the olefinic polymer may be a homopolymer of an olefinic monomer, a copolymer of an olefinic monomer, or a copolymer of an olefinic monomer and a monomer other than an olefinic monomer.
• the monomer other than an olefinic monomer is not particularly limited as long as it is copolymerizable with an olefinic monomer, and examples thereof include cyano group-containing vinyl monomers, amino group-containing vinyl monomers, pyridyl group-containing vinyl monomers, alkoxyl group-containing vinyl monomers, aromatic vinyl monomers, and the like. Of these examples, cyano group-containing vinyl monomers and aromatic vinyl monomers are preferable, and aromatic vinyl monomers are more preferable. These monomers copolymerizable with an olefinic monomer can be used alone or in combination of two or more thereof.
• aromatic vinyl monomers examples include styrene, ⁇ -methyl styrene, 2-methyl styrene, 3-methyl styrene, 4-methyl styrene, 2,4-diisopropyl styrene, 2,4-dimethyl styrene, 4-t-butyl styrene, 5-t-butyl-2-methyl styrene, N,N-dimethylaminoethyl styrene, N,N-diethylaminoethylstyrene, and the like.
• aromatic vinyl monomers can be used alone or in combination of two or more thereof.
• olefinic polymer examples include polyethylene, polypropylene (PP), polybutene, polybutadiene, butadiene-isoprene copolymers, polyisoprene, ethylene-vinyl acetate copolymers (EVA), ethylene-ethyl acrylate copolymers, ethylene-propylene polymers (EPR), ethylene-propylene-diene terpolymers (EPDM), styrene-butadiene block copolymer hydrides (SEB, SEBS) and the like, which can be used alone or in combination of two or more thereof.
• PP polypropylene
• PE polybutene
• polybutadiene butadiene-isoprene copolymers
• EVA ethylene-vinyl acetate copolymers
• EPR ethylene-ethyl acrylate copolymers
• EPR ethylene-propylene polymers
• EPDM ethylene-propylene-diene
• polyethylene or polypropylene is preferable as the olefinic polymer.
• aqueous dispersion it is preferable to use polyethylene or polypropylene dispersed in water.
• the olefinic polymer is produced, for example, by polymerizing a monomer composition containing an aforementioned monomer in an aqueous solvent.
• the aqueous solvent is not particularly limited as long as the olefinic polymer can be dispersed, and is selected from aqueous solvents having a boiling point at normal pressure of preferably 80° C. or more and 350° C. or less, more preferably 100° C. or more and 300° C. or less.
• water is preferable as the aqueous solvent from the viewpoint that it is incombustible and a dispersion of an olefinic polymer can be easily obtained. Further, it is also considerable to use water as a main solvent and mix an aqueous solvent other than water therewith, as long as the effect of the present disclosure is not impaired and the dispersion state of the olefinic polymer is secured.
• the polymerization method of the olefinic polymer is not particularly limited, and for example, any of solution polymerization, suspension polymerization, bulk polymerization, and emulsion polymerization may be used.
• the polymerization method may be any of the methods including ionic polymerization, radical polymerization, and living radical polymerization.
• the emulsion polymerization method is particularly preferable from the viewpoint of production efficiency.
• the emulsion polymerization method for example, it is easy to obtain a high molecular weight substance, and since the olefinic polymer can be obtained in a latex state in which it is dispersed in water as it is, a redispersion process becomes unnecessary, and the latex can be used as it is as an aqueous dispersion comprising an olefinic polymer as a main component for preparing a presently disclosed aqueous sealant composition.
• the emulsion polymerization can be carried out by a standard method.
• commonly used polymerization auxiliary materials such as an emulsifier, a polymerization initiator, a molecular weight modifier, a chain transfer agent and the like can be used.
• the olefinic polymer it is preferable to use a modified olefinic polymer which is a partial copolymer of an olefinic polymer and a polymerizable unsaturated organic acid.
• polymerizable unsaturated organic acids include maleic anhydride, acrylic acid, methacrylic acid, and esters thereof. These polymerizable unsaturated organic acids can be used alone or as a combination of two or more thereof.
• a modified olefinic polymer can be obtained by polymerizing a polymerizable unsaturated organic acid and a polyolefin using a polymerization method such as random copolymerization, block copolymerization, graft copolymerization, or the like.
• modified olefinic polymer commercially available olefinic polymers may be used.
• commercially available products include Zaikthene-A-GH, Zaikthene-AC, Zaikthene-NC, Zaikthene-N, Zaikthene-L (that are manufactured by Sumitomo Seika Chemicals Company, Limited), Arrow base SA-1200, Arrow base SB-1200, Arrow base SE-1200, Arrow base SB-1010 (that are manufactured by Unitika Ltd.), High-tech S-3121, High-tech S-3123, High-tech S-3127 (that are manufactured by TOHO Chemical Industry Co., Ltd.), and the like.
• the presently disclosed aqueous sealant composition comprises an aqueous dispersion comprising the olefinic polymer as a main component, in an amount of 70 mass % or more, preferably 80 mass % or more, further preferably 85 mass % or more, and 97 mass % or less, preferably 95 mass % or less, further preferably 93 mass % or less by mass of solid content (in terms of solid content).
• the content percentage of the aqueous dispersion in the aqueous sealant composition is excessively high, it is difficult to obtain a uniform film (sealant layer).
• the content percentage of the aqueous dispersion in the aqueous sealant composition is excessively low, the flexibility of the sealant layer obtained using the aqueous sealant composition decreases. That is, the sealing performance deteriorates.
• the viscosity of the aqueous sealant composition is preferably 10 mPa ⁇ s or more, more preferably 100 mPa ⁇ s or more, and preferably 10,000 mPa ⁇ s or less, more preferably 1,000 mPa ⁇ s or less.
• the viscosity of the aqueous sealant composition is within such a range, it is possible to suppress a phenomenon that the viscosity is excessively high, making it difficult to coat. It is also possible to suppress a phenomenon that the viscosity is excessively low, making it difficult to form a uniform film.
• the viscosity is a viscosity value measured at a liquid temperature of 20° C., using a Brookfield viscometer (B type viscometer).
• the presently disclosed aqueous sealant composition comprises a water-soluble polymer other than the aqueous dispersion comprising the olefinic polymer as a main component.
• water-soluble polymers include polyvinyl alcohol, polyacrylic acid, polystyrene sulfonic acid, and the like.
• polyvinyl alcohol is preferable, and polyvinyl alcohol having a saponification rate of 98 mol % or more, which is said to be fully saponified type, is particularly preferable.
• the aforementioned water-soluble polymers may be used alone or in combination of two or more thereof in any proportion.
• the water-soluble polymer preferably has a 4 mass % aqueous solution viscosity of 4 mPa ⁇ s or more and 500 mPa ⁇ s or less. Note that the viscosity is a viscosity value measured at a liquid temperature of 20° C., using a Brookfield viscometer (B type viscometer).
• the content percentage of the water-soluble polymer in the aqueous sealant composition is preferably 3 mass % or more, more preferably 5 mass % or more, further preferably 7 mass % or more, and preferably 30 mass % or less, more preferably 20 mass % or less, further preferably 15 mass % or less, by mass of solid content (in terms of solid content).
• the content percentage of the water-soluble polymer is within such a range, it is possible to suppress a phenomenon that the content percentage of the water-soluble polymer is excessively high, such that the flexibility of the obtained sealant layer decreases, that is, the sealing performance deteriorates, and it is also possible to suppress a phenomenon that the content percentage of the water-soluble polymer is excessively low, making it difficult to obtain a uniform film (sealant layer).
• the solid content concentration of the presently disclosed aqueous sealant composition is preferably 5 mass % or more, more preferably 20 mass % or more, further preferably 30 mass % or more, particularly 35 mass % or more, and preferably 70 mass % or less, more preferably 60 mass % or less, further preferably 50 mass % or less, particularly 43 mass % or less.
• the total solid content concentration of the aqueous sealant composition can be adjusted by a known method such as concentration using a rotary evaporator.
• additives such as colorants and the like may be added to the presently disclosed aqueous sealant composition.
• a colorant that can be added is preferably one that does not react with an electrolyte solution and does not dissolve in an electrolyte solution, and examples thereof include various organic and inorganic pigments.
• carbon black particularly carbon black having a particle diameter of 0.1 ⁇ m or less such as furnace black, channel black and the like is preferable.
• the amount of such additives such as colorants to be added may be an arbitrary amount as necessary, and is usually 0.01 mass % or more and 20 mass % or less, preferably 0.01 mass % or more and 5 mass % or less, and more preferably 0.02 mass % or more and 3 mass % or less, with respect to the amount of the olefinic polymer (100 mass %).
• the amount of additives is within such a range, it is possible to suppress a phenomenon that the addition amount of additives is excessively large, such that the flexibility of the sealant layer decreases, resulting in cracking.
• the producing method for the presently disclosed aqueous sealant composition is not particularly limited, and for example, a method of adding other components such as a water-soluble polymer and additives to an aqueous dispersion comprising an olefinic polymer as a main component; a method of mixing an aqueous dispersion comprising an olefinic polymer as a main component and an aqueous solution of a water-soluble polymer that were respectively prepared, and then adding other components such as additives thereto; and the like.
• a nonaqueous electrolyte battery using the presently disclosed aqueous sealant composition is such that, a sealant layer formed from the aforementioned aqueous sealant composition is provided between an insulating gasket attached to the opening of a metal container housing the power generating element and the metal container, and/or between the insulating gasket and a sealing body.
• the material of the metal container, the power generating element, and the insulating gasket used for the nonaqueous electrolyte battery may be ones commonly used. That is, the nonaqueous electrolyte battery has its power generating element housed in a metal container and sealed.
• the power generating element may be an electrolyte, active materials for positive electrode and negative electrode, a separator, or the like.
• an electrolyte solution comprising a supporting electrolyte and an organic electrolytic solution solvent is used.
• the supporting electrolyte which constitutes the electrolytic solution for example, a compound which is easily hydrolyzed through reaction with water, such as lithium compounds such as LiPF 6 , LiBF 4 , LiClO 4 and the like, is used.
• a nonaqueous electrolyte solvent for example, a combustible organic compound such as propylene carbonate (PC), ethylene carbonate (EC), diethyl carbonate (DEC) or the like is used.
• the insulating gasket it is preferable to use a material made of a polyolefin resin such as polyethylene, polypropylene, ethylene copolymerized polypropylene or the like, which is generally said to have a high electrolytic solution resistance.
• a polyolefin resin such as polyethylene, polypropylene, ethylene copolymerized polypropylene or the like, which is generally said to have a high electrolytic solution resistance.
• the polyolefin resin it is better to use one having a heat distortion temperature measured by JIS K7207 of preferably 90° C. or more and 200° C. or less, more preferably 90° C. or more and 150° C. or less, and further preferably 95° C. or more and 130° C. or less.
• the heat distortion temperature of the polyolefin resin is within such a range, it is possible to suppress a phenomenon that the heat distortion temperature is excessively high, such that the bending elastic modulus at normal temperature is too high, causing deformation when attaching the insulating gasket, and thus resulting in cracking. It is also possible to suppress a phenomenon that the heat distortion temperature is excessively low, such that the resistance of the insulating gasket at high temperature is poor and the sealability deteriorates.
• a sealant layer of the nonaqueous electrolyte battery can be formed, for example, by the following procedure. Initially, a predetermined amount of the aqueous sealant composition is fed to and applied to the surface of the metal container and/or the surface of the insulating gasket with a metering pump such as an air-driven metering dispenser, a roller pump, a gear pump or the like. After coating, natural drying is carried out while maintaining the horizontally so as to prevent the aqueous sealant composition from biasing, and thereafter the aqueous solvent is removed to form a thin layer.
• a metering pump such as an air-driven metering dispenser, a roller pump, a gear pump or the like.
• the coating method is not limited to the method using a metering pump, and may be manually performed using a brush if the amount of work is small.
• forced drying using a heating device may be performed instead of natural drying, and in this case, drying in a short time becomes possible, enabling an industrially more suitable process.
• the thickness of the sealant layer formed by the above method may be freely selected according to the sizes of the metal container and the insulating gasket, and is usually 0.1 ⁇ m or more and 1000 ⁇ m or less.
• the thickness of the sealant layer is within such a range, it is possible to suppress a phenomenon that the layer thickness is excessively insufficient, such that problems such as electrolyte solution leakage and moisture intrusion may occur and the layer may be cut. It is also possible to suppress a phenomenon that the thickness of the sealant layer is excessively thick, making it difficult to form a layer.
• a lithium ion secondary battery is preferable as the nonaqueous electrolyte battery in which the presently disclosed aqueous sealant composition is used.
• each test piece having a sealant layer formed on an aluminum foil obtained in the examples and comparative examples was measured by a 180° peeling method in accordance with JIS Z0237. More particularly, an aluminum tape with an adhesive was laminated to each test piece cut into a ribbon-like shape having a width of 20 mm, and the peel strength was measured at a tensile rate of 200 mm/min at 23° C. using a tensile tester. The results are listed in Table 1. Note that the greater the peel strength, the better the film strength (strength of the sealant layer).
• Each test piece having a sealant layer formed on an aluminum foil obtained in the examples and comparative examples was immersed in methanol at ⁇ 30° C. for 1 hour and was folded with the sealant layer on the outside immediately after being taken out. The bent portion was observed as to whether cracking, peeling or the like is present. A case in which no cracking, peeling and the like was observed was given an evaluation of “good”, and a case in which cracking, peeling or the like was observed was given an evaluation of “poor”. The results are listed in Table 1.
• aqueous dispersion comprising an olefinic polymer as a main component (manufactured by Sumitomo Seika Chemicals Company, Limited, content of olefinic polymer (in terms of solid content): 100 mass %)
• 5 parts by mass of solid content of a 10 mass % aqueous solution of polyvinyl alcohol (polyvinyl alcohol JF17 manufactured by JAPAN VAM & POVAL CO., LTD., viscosity of a 4 mass % aqueous solution: 4.5 mPa ⁇ s, saponification rate: 98 mol %) was added as a water-soluble polymer to obtain an aqueous sealant composition.
• the total solid content concentration of the obtained aqueous sealant composition was 45 mass %.
• the obtained aqueous sealant composition was cast on an aluminum foil (thickness: 20 ⁇ m) with a doctor blade having a gap of 200 ⁇ m and was then subjected to heat drying at 80° C. for 20 minutes to form a film-like sealant layer to obtain a test piece.
• An aqueous sealant composition was produced in the same manner as in Example 1 except that the amount of Zaikthene NC was changed to 90 parts by mass of solid content and the amount of polyvinyl alcohol was changed to 10 parts by mass of solid content.
• the total solid content concentration of the obtained aqueous sealant composition was 42 mass %.
• test piece was produced in the same manner as in Example 1 except that the above aqueous sealant composition was used.
• An aqueous sealant composition was produced in the same manner as in Example 1 except that as the aqueous dispersion comprising an olefinic polymer as a main component, 90 parts by mass of solid content of Arrow Base SB-1010 (manufactured by Unitika Ltd., content of olefinic polymer (in terms of solid content): 100 mass %) was used instead of Zaikthene NC, and the amount of polyvinyl alcohol was changed to 10 parts by mass of solid content. The total solid content concentration of the obtained aqueous sealant composition was 35 mass %.
• test piece was produced in the same manner as in Example 1 except that the above aqueous sealant composition was used.
• An aqueous sealant composition was produced in the same manner as in Example 1 except that the amount of Zaikthene NC was changed to 50 parts by mass of solid content and the amount of polyvinyl alcohol was changed to 50 parts by mass of solid content.
• the total solid content concentration of the obtained aqueous sealant composition was 20 mass %.
• test piece was produced in the same manner as in Example 1 except that the above aqueous sealant composition was used.
• An aqueous sealant composition was produced in the same manner as in Example 1 except that as the aqueous dispersion comprising an olefinic polymer as a main component, 100 parts by mass of solid content of Arrow Base SB-1010 was used instead of Zaikthene NC, and no polyvinyl alcohol was used. The total solid content concentration of the obtained aqueous sealant composition was 50 mass %.
• test piece was produced in the same manner as in Example 1 except that the above aqueous sealant composition was used.
• Example 3 Example 1 example 2 Aqueous sealant Solid Zaikthene NC (mass %) 95 90 — 50 — composition composition Arrow Base SB-1010 — — 90 — 100 (mass %) Polyvinyl alcohol (mass %) 5 10 10 50 — Total solid content concentration (mass %) 45 42 35 20 50 Evaluation items Wettability (coating film appearance) Good Good Good Poor Poor (cracking) (unevenness) Film strength (peel strength) (N/20 mm) 15 18 25 5 20 Viscosity (mPa ⁇ s) 180 250 220 5300 80 Flexibility (bending tolerance) Good Good Good Poor Poor Sealability 1 mass %> 1 mass %> 1 mass %> 5 mass % 7 mass %
• aqueous sealant composition for a nonaqueous electrolyte battery comprising an aqueous dispersion in an amount of 70 mass % or more and 97 mass % or less by mass of solid content, wherein the aqueous dispersion comprises an olefinic polymer as a main component.

Landscapes

• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Organic Chemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Electrochemistry (AREA)
• Health & Medical Sciences (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Life Sciences & Earth Sciences (AREA)
• Wood Science & Technology (AREA)
• Manufacturing & Machinery (AREA)
• Oil, Petroleum & Natural Gas (AREA)
• Dispersion Chemistry (AREA)
• Sealing Battery Cases Or Jackets (AREA)
• Sealing Material Composition (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Applications Claiming Priority (3)

Related Parent Applications (1)

Related Child Applications (1)

Publications (1)

Family

ID=60041841

Family Applications (2)

Family Applications After (1)

Country Status (8)

Family Cites Families (22)

• 2017
  • 2017-04-14 JP JP2018512107A patent/JP6947170B2/ja active Active
  • 2017-04-14 US US16/090,654 patent/US20190115569A1/en not_active Abandoned
  • 2017-04-14 PL PL17782537.9T patent/PL3444863T3/pl unknown
  • 2017-04-14 HU HUE17782537A patent/HUE067095T2/hu unknown
  • 2017-04-14 WO PCT/JP2017/015379 patent/WO2017179724A1/ja not_active Ceased
  • 2017-04-14 KR KR1020187028618A patent/KR102345644B1/ko active Active
  • 2017-04-14 EP EP17782537.9A patent/EP3444863B1/en active Active
  • 2017-04-14 CN CN201780022362.2A patent/CN108886119B/zh not_active Expired - Fee Related
• 2021
  • 2021-06-28 US US17/359,645 patent/US11649369B2/en active Active

Also Published As

Similar Documents

Legal Events