WO1992004170A2 - Methode de fabrication d'objets a partir de materiaux en poudre - Google Patents

Methode de fabrication d'objets a partir de materiaux en poudre Download PDF

Info

Publication number
WO1992004170A2
WO1992004170A2 PCT/CA1991/000317 CA9100317W WO9204170A2 WO 1992004170 A2 WO1992004170 A2 WO 1992004170A2 CA 9100317 W CA9100317 W CA 9100317W WO 9204170 A2 WO9204170 A2 WO 9204170A2
Authority
WO
WIPO (PCT)
Prior art keywords
mold
sintered body
superplastic
lump
pancake
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CA1991/000317
Other languages
English (en)
Other versions
WO1992004170A3 (fr
Inventor
Richard A. Holl
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of WO1992004170A2 publication Critical patent/WO1992004170A2/fr
Publication of WO1992004170A3 publication Critical patent/WO1992004170A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

On mélange et l'on homogénéise des matériaux pâteux, à partir desquels des pièces à l'état vert sont moulées avant d'être frittées, et qui autrement seraient difficiles, voire impossibles, à mélanger à l'état pâteux, en formant une masse que l'on place entre deux plateaux parallèles de surface plane et que l'on aplatit entre ces deux plateaux jusqu'à ce qu'elle devienne une fine galette; on remodèle ensuite ladite galette en une masse ou une boule en remontant ses bords externes vers le centre. Ce cycle de compression-mélange est répété plusieurs fois jusqu'à la fin du processus, à savoir de 10 à 50 fois généralement, et normalement de 20 à 30 fois. Des objets en céramique moulée ayant des surfaces 'à finition brillant' sont ainsi produits de façon économique en mettant à profit une faible déformation de cisaillement superplastique, 5 % au moins, produite par le moulage des objets ayant leurs surfaces de finition en contact avec les surfaces de moule ayant le fini requis. La taille des particules des matériaux céramiques en poudre avec lesquels on commence à travailler est de l'ordre du micron ou moins, et les pièces à l'état vert moulées sont formées grâce à des techniques de malaxage, broyage et mélange qui conservent l'uniformité des matériaux et maintiennent la taille des particules en dessous du micron. Les pièces à l'état vert sont frittées par frittage à vitesse contrôlée aifn de maintenir la taille des grains en dessous de la valeur d'un micron nécessaire à la forgeabilité dans le domaine superplastique. Les pièces frittées sont ensuite moulées comme décrit ci-dessus à une température minimum de 0,5 M, M représentant la température de fusion des matériaux céramiques.
PCT/CA1991/000317 1990-09-04 1991-09-04 Methode de fabrication d'objets a partir de materiaux en poudre Ceased WO1992004170A2 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US57680490A 1990-09-04 1990-09-04
US576,804 1990-09-04

Publications (2)

Publication Number Publication Date
WO1992004170A2 true WO1992004170A2 (fr) 1992-03-19
WO1992004170A3 WO1992004170A3 (fr) 1992-05-29

Family

ID=24306066

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA1991/000317 Ceased WO1992004170A2 (fr) 1990-09-04 1991-09-04 Methode de fabrication d'objets a partir de materiaux en poudre

Country Status (1)

Country Link
WO (1) WO1992004170A2 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0510254A1 (fr) * 1991-03-26 1992-10-28 Kenji Maeda Procédé de pétrissage de béton et appareil à cet effet
EP0843191A1 (fr) * 1996-11-15 1998-05-20 Eastman Kodak Company Réflecteur de lumière intégré et micromoulé en céramique

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2417255A (en) * 1945-10-25 1947-03-11 Frank M Kinnard Clay spreader
US3461821A (en) * 1967-12-15 1969-08-19 Geza Gallus Apparatus for kneading and shaping lumps of dough
GB1557744A (en) * 1976-06-01 1979-12-12 Special Metals Corp Process and apparatus for producing aticles of complex shape
DE3675463D1 (de) * 1985-08-29 1990-12-13 Toshiba Tungaloy Co Ltd Verfahren zur plastischen verformung eines druckgesinterten oder drucklosgesinterten keramikkoerpers und nach diesem verfahren hergestelltes keramikformmaterial.
US4849142A (en) * 1986-01-03 1989-07-18 Jupiter Technologies, Inc. Superplastic forging of zirconia ceramics
US4732719A (en) * 1986-01-03 1988-03-22 Jupiter Technologies, Inc. Superplastic forging nitride ceramics
US5123844A (en) * 1989-06-20 1992-06-23 Agency Of Industrial Science And Technology Living hard tissue replacement prepared by superplastic forming of a calcium phosphate base
EP0585978A3 (fr) * 1989-06-30 1994-03-23 TDK Corporation Matériau de remplacement de tissu dur vivant, sa préparation et préparation d'un corps moulé
DE69002447T2 (de) * 1989-12-26 1993-11-18 Agency Ind Science Techn Verfahren zur Formgebung keramischer Zusammensetzungen.

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0510254A1 (fr) * 1991-03-26 1992-10-28 Kenji Maeda Procédé de pétrissage de béton et appareil à cet effet
US5183332A (en) * 1991-03-26 1993-02-02 Kenji Maeda Kneading method of concrete
US5302018A (en) * 1991-03-26 1994-04-12 Kenji Maeda Concrete kneading apparatus
EP0843191A1 (fr) * 1996-11-15 1998-05-20 Eastman Kodak Company Réflecteur de lumière intégré et micromoulé en céramique

Also Published As

Publication number Publication date
WO1992004170A3 (fr) 1992-05-29

Similar Documents

Publication Publication Date Title
US5335992A (en) Methods and apparatus for the mixing and dispersion of flowable materials
DK172348B1 (da) Fremstillingsmåde til fremstilling af polykrystallinske alfa-aluminiummaterialer
US5227104A (en) High solids content gels and a process for producing them
US5047182A (en) Complex ceramic and metallic shaped by low pressure forming and sublimative drying
JP2937483B2 (ja) スクリーン印刷法による付形物品
EP0968067B1 (fr) Procede de moulage par injection de pieces a base de poudre de ceramique et/ou de metal passant par la formation d'un gel
JP2928486B2 (ja) 定形体成形方法
EP0598828B1 (fr) Procede aqueux de moulage par injection de poudres ceramiques fortement chargees en matieres solides
RO121099B1 (ro) Procedeu pentru fabricarea uneltelor microabrazive
EP2354110B1 (fr) Procédé de fabrication d'un comprimé fritté en nitrure de bore cubique
US4732719A (en) Superplastic forging nitride ceramics
Denham et al. Mechanical behavior of robocast alumina
US20040151892A1 (en) Manufacture of flat surfaced composites comprising powdered fillers in a polymer matrix
US6017839A (en) Ceramic article
US5190898A (en) Pourable molding compound containing sinterable powders
US3857157A (en) Method of producing hot pressed components
EP0288208B1 (fr) Corps en matériau céramique et sa fabrication
Wildman et al. Breakdown of agglomerates in ideal pastes during extrusion
IL44318A (en) Alumina carbide ceramic material
DE19809679A1 (de) Verfahren zur Herstellung eines gesinterten, keramischen Schleifmittels sowie Schleifwerkzeuge mit diesem Schleifmittel
WO1998021272A2 (fr) Fabrication de composite a base de poudre non organique et de polymeres
EP0474346B1 (fr) Procédé pour la préparation d'un moulage de poudre
JP2652144B2 (ja) セラミック生成形体の製造装置
Cannell et al. Processing of Electronic Ceramics
Arrasmith et al. Incipient flocculation molding: a new ceramic forming technique

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): JP KR US

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): AT BE CH DE DK ES FR GB GR IT LU NL SE

AK Designated states

Kind code of ref document: A3

Designated state(s): JP KR US

AL Designated countries for regional patents

Kind code of ref document: A3

Designated state(s): AT BE CH DE DK ES FR GB GR IT LU NL SE