WO2001069223A2 - Ameliorations apportees a l'etude de la corrosion - Google Patents

Ameliorations apportees a l'etude de la corrosion Download PDF

Info

Publication number
WO2001069223A2
WO2001069223A2 PCT/GB2001/001097 GB0101097W WO0169223A2 WO 2001069223 A2 WO2001069223 A2 WO 2001069223A2 GB 0101097 W GB0101097 W GB 0101097W WO 0169223 A2 WO0169223 A2 WO 0169223A2
Authority
WO
WIPO (PCT)
Prior art keywords
sample
electrical contacts
environment
location
voltage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/GB2001/001097
Other languages
English (en)
Other versions
WO2001069223A3 (fr
Inventor
Brian Hands
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sellafield Ltd
Original Assignee
British Nuclear Fuels PLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from GB0005948A external-priority patent/GB0005948D0/en
Priority claimed from GB0005942A external-priority patent/GB0005942D0/en
Application filed by British Nuclear Fuels PLC filed Critical British Nuclear Fuels PLC
Priority to AU2001240814A priority Critical patent/AU2001240814A1/en
Publication of WO2001069223A2 publication Critical patent/WO2001069223A2/fr
Publication of WO2001069223A3 publication Critical patent/WO2001069223A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un procédé et un dispositif de suivi précis du comportement à la corrosion d'un matériau lorsque celui-ci est exposé à un environnement. Le procédé et le dispositif décrits dans cette invention s'articulent autour de la méthode de la signature de champ. Plus particulièrement, l'invention concerne un procédé permettant d'étudier la corrosion d'un matériau dans un environnement donné. Ce procédé consiste à fabriquer un échantillon d'essai à partir d'un échantillon du matériau; à disposer au moins deux contacts électriques entrant en contact avec une surface interne de l'échantillon d'essai; à mettre une surface externe de l'échantillon en contact avec l'environnement; à mesurer la tension entre les contacts électriques susmentionnés à un moment, puis à une ou à plusieurs reprise(s). Une surface externe de l'échantillon est en contact avec l'environnement à une ou à plusieurs reprise(s), et un courant est envoyé à travers l'échantillon au moment de la mesure de la tension. Ces mesures de tension fournissent des informations relatives à l'effet de l'environnement sur l'échantillon, avec le temps. Pendant les mesures de tension, la surface interne de l'échantillon sur laquelle les contacts électriques sont disposés est physiquement isolée de l'environnement au moins d'un joint d'étanchéité.
PCT/GB2001/001097 2000-03-14 2001-03-13 Ameliorations apportees a l'etude de la corrosion Ceased WO2001069223A2 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2001240814A AU2001240814A1 (en) 2000-03-14 2001-03-13 Improvements in and relating to investigating corrosion

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
GB0005942.8 2000-03-14
GB0005948A GB0005948D0 (en) 2000-03-14 2000-03-14 Improvememnts in and relating to investigating corrosion
GB0005948.5 2000-03-14
GB0005942A GB0005942D0 (en) 2000-03-14 2000-03-14 Improvements in and relating to investigating corrosion

Publications (2)

Publication Number Publication Date
WO2001069223A2 true WO2001069223A2 (fr) 2001-09-20
WO2001069223A3 WO2001069223A3 (fr) 2002-01-24

Family

ID=26243857

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2001/001097 Ceased WO2001069223A2 (fr) 2000-03-14 2001-03-13 Ameliorations apportees a l'etude de la corrosion

Country Status (2)

Country Link
AU (1) AU2001240814A1 (fr)
WO (1) WO2001069223A2 (fr)

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6861853B2 (en) 2000-03-14 2005-03-01 British Nuclear Fuels Plc Investigating corrosion
WO2005036152A1 (fr) * 2003-09-17 2005-04-21 General Electric Company Systeme et procede de surveillance de defauts dans des structures
US6888359B2 (en) 2000-03-14 2005-05-03 British Nuclear Fuels Plc Investigating current
US6982563B2 (en) 2000-11-09 2006-01-03 British Nuclear Fuels Plc Monitoring of corrosion induced loss of material by means of a plurality of electrical resistance measurements (field signature method, electrical resistance tomography)
CN105372322A (zh) * 2015-12-18 2016-03-02 中国石油大学(华东) 一种应用于电场指纹法的多方向电流采集系统
CN105572211A (zh) * 2015-12-18 2016-05-11 中国石油大学(华东) 一种应用于电场指纹法管道检测的多方向电流采集系统
CN106370586A (zh) * 2016-10-08 2017-02-01 国网浙江省电力公司电力科学研究院 一种高压隔离开关触头触指在线盐雾试验装置
CN116609245A (zh) * 2022-02-16 2023-08-18 波音公司 用于在暴露于极端条件之后测试材料的方法及系统

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3070482D1 (en) * 1980-05-08 1985-05-15 Ici Plc Corrosion monitoring process and apparatus for use therein
CA1153884A (fr) * 1980-09-03 1983-09-20 Alvin D. Goolsby Methode de determination du degre de corrosion a l'interieur d'un pipeline ou d'une canalisation
EP0150552B2 (fr) * 1984-05-17 1992-12-23 SSL Limited Sonde à résistance électrique pour la mesure de corrosion
DE3819026A1 (de) * 1988-06-03 1989-12-14 Pfaudler Werke Ag Sondenanordnung
US5171517A (en) * 1990-12-10 1992-12-15 General Electric Company Method for monitoring corrosion on a member in a nuclear reactor core

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6861853B2 (en) 2000-03-14 2005-03-01 British Nuclear Fuels Plc Investigating corrosion
US6888359B2 (en) 2000-03-14 2005-05-03 British Nuclear Fuels Plc Investigating current
US6982563B2 (en) 2000-11-09 2006-01-03 British Nuclear Fuels Plc Monitoring of corrosion induced loss of material by means of a plurality of electrical resistance measurements (field signature method, electrical resistance tomography)
WO2005036152A1 (fr) * 2003-09-17 2005-04-21 General Electric Company Systeme et procede de surveillance de defauts dans des structures
US6922641B2 (en) 2003-09-17 2005-07-26 General Electric Company System and method for monitoring defects in structures
CN100504368C (zh) * 2003-09-17 2009-06-24 通用电气公司 监控结构中缺陷的系统和方法
CN105372322A (zh) * 2015-12-18 2016-03-02 中国石油大学(华东) 一种应用于电场指纹法的多方向电流采集系统
CN105572211A (zh) * 2015-12-18 2016-05-11 中国石油大学(华东) 一种应用于电场指纹法管道检测的多方向电流采集系统
CN105372322B (zh) * 2015-12-18 2016-08-24 中国石油大学(华东) 一种应用于电场指纹法的多方向电流采集系统
CN106370586A (zh) * 2016-10-08 2017-02-01 国网浙江省电力公司电力科学研究院 一种高压隔离开关触头触指在线盐雾试验装置
CN106370586B (zh) * 2016-10-08 2023-07-07 国网浙江省电力公司电力科学研究院 一种高压隔离开关触头触指在线盐雾试验装置
CN116609245A (zh) * 2022-02-16 2023-08-18 波音公司 用于在暴露于极端条件之后测试材料的方法及系统

Also Published As

Publication number Publication date
AU2001240814A1 (en) 2001-09-24
WO2001069223A3 (fr) 2002-01-24

Similar Documents

Publication Publication Date Title
US5728943A (en) Method and system for detection and prevention of stress corrosion cracking in buried structures
US20250216320A1 (en) Laboratory apparatus for hydrogen permeation electrochemical measurements under high pressure, temperature and tensile stress
US6861853B2 (en) Investigating corrosion
US6982563B2 (en) Monitoring of corrosion induced loss of material by means of a plurality of electrical resistance measurements (field signature method, electrical resistance tomography)
WO2001069223A2 (fr) Ameliorations apportees a l'etude de la corrosion
US7387031B1 (en) Method for monitoring corrosion damage to a metal sample
US6772622B2 (en) Disbonded coating cathodic protection monitoring coupon
DE102012223390B4 (de) Mobile Korrosions- und Materialprüfeinrichtung für Korrosions- und Scalinguntersuchungen
Zehra et al. Corrosion Monitoring and Inspection Techniques in Industrial Environments
Ukpaka et al. Effect of environmental parameters on corrosion of metal steel in stagnant fresh water using finite element approach
US10690586B2 (en) Rapid detection and quantification of surface and bulk corrosion and erosion in metals and non-metallic materials with integrated monitoring system
SU996723A1 (ru) Способ контрол коррозионного состо ни обсадных колонн
Lu Discussions of general methods for measurement and monitoring of corrosion in the oil & gas industry
Lee et al. Anoxic Corrosion Experiment of Canister Materials in a Deep Borehole
Gartland et al. Innovations Developed through the 1980'Ies in Offshore CP Design, Computer Modeling and CP Inspection
CN119269378A (zh) 一种可监测带抽油杆的油套管腐蚀与结垢的装置及方法
Rocchini A computer code for detecting deterioration of organic coatings through impedance measurements
CN111398152A (zh) 直流杂散电流对管道的干扰腐蚀试验装置
Dean Corrosion monitoring for industrial processes
Tan Principles and issues in structural health monitoring using corrosion sensors
DD203974A1 (de) Einrichtung zur untersuchung der korrosionsbestaendigkeit
Guma et al. Advances in Corrosion Monitoring Techniques
Powell Internal Corrosion Monitoring Using Coupons and ER Probes: A Practical Focus on the Most Commonly Used, Cost‐Effective Monitoring Techniques
Terry et al. Development and deployment of advanced corrosion monitoring systems for high-level waste tanks.
Kumar et al. AC Impedance Spectra of Pipes Buried in Soil

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
AK Designated states

Kind code of ref document: A3

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A3

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP