WO2001096105A2 - Matiere polymere matricielle moulable, produit composite moule et son procede de production - Google Patents

Matiere polymere matricielle moulable, produit composite moule et son procede de production Download PDF

Info

Publication number
WO2001096105A2
WO2001096105A2 PCT/US2001/015965 US0115965W WO0196105A2 WO 2001096105 A2 WO2001096105 A2 WO 2001096105A2 US 0115965 W US0115965 W US 0115965W WO 0196105 A2 WO0196105 A2 WO 0196105A2
Authority
WO
WIPO (PCT)
Prior art keywords
moldable
binder
catalyst
resin
matrix polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2001/015965
Other languages
English (en)
Other versions
WO2001096105A3 (fr
Inventor
William G. Hager
Timothy W. Ramey
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Owens Corning
Original Assignee
Owens Corning
Owens Corning Fiberglas Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Owens Corning, Owens Corning Fiberglas Corp filed Critical Owens Corning
Priority to AU2001263223A priority Critical patent/AU2001263223A1/en
Publication of WO2001096105A2 publication Critical patent/WO2001096105A2/fr
Publication of WO2001096105A3 publication Critical patent/WO2001096105A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une matière polymère matricielle moulable utile dans la fabrication d'articles de renforcement destinés à être utilisés dans la production d'articles composites moulés. La matière polymère matricielle moulable comprend une résine polymère matricielle moulable ainsi qu'une composition catalytique. L'invention concerne également un produit composite moulé produit à partir de la matière polymère matricielle moulable et un liant à cordon.
PCT/US2001/015965 2000-06-15 2001-05-16 Matiere polymere matricielle moulable, produit composite moule et son procede de production Ceased WO2001096105A2 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2001263223A AU2001263223A1 (en) 2000-06-15 2001-05-16 Moldable matrix polymer material, molded composite product and method for makingsame

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US59623000A 2000-06-15 2000-06-15
US09/596,230 2000-06-15

Publications (2)

Publication Number Publication Date
WO2001096105A2 true WO2001096105A2 (fr) 2001-12-20
WO2001096105A3 WO2001096105A3 (fr) 2002-03-07

Family

ID=24386496

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2001/015965 Ceased WO2001096105A2 (fr) 2000-06-15 2001-05-16 Matiere polymere matricielle moulable, produit composite moule et son procede de production

Country Status (2)

Country Link
AU (1) AU2001263223A1 (fr)
WO (1) WO2001096105A2 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2003078343A3 (fr) * 2002-03-13 2004-01-15 Ppg Ind Ohio Inc Produit en fibres de verre renfermant des liants de cordon
US6849332B1 (en) * 1999-03-30 2005-02-01 Owens Corning Fiberglas Technology, Inc. String binders and method for making same
US7455674B2 (en) 2002-01-31 2008-11-25 Smith & Nephew Plc High strength bioresorbables containing poly-glycolic acid
US7524891B2 (en) 2001-07-04 2009-04-28 Smith & Nephew Plc Biodegradable polymer systems
US9120919B2 (en) 2003-12-23 2015-09-01 Smith & Nephew, Inc. Tunable segmented polyacetal
US9770534B2 (en) 2007-04-19 2017-09-26 Smith & Nephew, Inc. Graft fixation
US9815240B2 (en) 2007-04-18 2017-11-14 Smith & Nephew, Inc. Expansion moulding of shape memory polymers

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5520814B2 (ja) 2007-04-19 2014-06-11 スミス アンド ネフュー インコーポレーテッド マルチモーダル形状記憶ポリマー

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4006048A (en) * 1975-08-14 1977-02-01 Westinghouse Electric Corporation Reverse printed high-pressure laminates
EP0074325A1 (fr) * 1981-09-04 1983-03-16 The Goodyear Tire & Rubber Company Procédé pour mouler une matière plastique renforcée de fibres longues
JPH0662840B2 (ja) * 1987-08-25 1994-08-17 武田薬品工業株式会社 不飽和ポリエステル組成物
US6579616B1 (en) * 1999-03-30 2003-06-17 Owens Corning Fiberglas Technology, Inc. String binders

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6849332B1 (en) * 1999-03-30 2005-02-01 Owens Corning Fiberglas Technology, Inc. String binders and method for making same
US7524891B2 (en) 2001-07-04 2009-04-28 Smith & Nephew Plc Biodegradable polymer systems
US7455674B2 (en) 2002-01-31 2008-11-25 Smith & Nephew Plc High strength bioresorbables containing poly-glycolic acid
WO2003078343A3 (fr) * 2002-03-13 2004-01-15 Ppg Ind Ohio Inc Produit en fibres de verre renfermant des liants de cordon
CN1329330C (zh) * 2002-03-13 2007-08-01 Ppg工业俄亥俄公司 掺加丝线粘合剂的纤维玻璃制品
US9120919B2 (en) 2003-12-23 2015-09-01 Smith & Nephew, Inc. Tunable segmented polyacetal
US9815240B2 (en) 2007-04-18 2017-11-14 Smith & Nephew, Inc. Expansion moulding of shape memory polymers
US9770534B2 (en) 2007-04-19 2017-09-26 Smith & Nephew, Inc. Graft fixation

Also Published As

Publication number Publication date
AU2001263223A1 (en) 2001-12-24
WO2001096105A3 (fr) 2002-03-07

Similar Documents

Publication Publication Date Title
US6579616B1 (en) String binders
US5998029A (en) Nonaqueous sizing system for glass fibers and injection moldable polymers
JP2000516162A (ja) 繊維―強化熱可塑性複合体物品を成形するための繊維およびワイヤ―被覆複合ストランドの化学処理剤
WO2007032988A1 (fr) Faisceaux de fibres de verre destines a des mats et procedes de fabrication de ceux-ci
WO2001096105A2 (fr) Matiere polymere matricielle moulable, produit composite moule et son procede de production
US10351695B2 (en) Sizing compositions, sized reinforcing products and methods for making reinforced thermoset composites
US6849331B1 (en) Polyester resin string binder
CZ190294A3 (en) Process of treating a textile product process of treating a textile product
US5587034A (en) Process for pultruding fiber reinforced furan composites
WO2001096077A1 (fr) Liants filamentaires et procede de fabrication de ceux-ci
EP1615857A1 (fr) Formulation d'encollage pour extrusion par etirage phenolique et son procede de fabrication
WO2002042235A2 (fr) Liant de cordon d'epoxyurethanne
US6828024B1 (en) Epoxy film former string binder
WO2003020658A1 (fr) Liants filamentaires epoxy urethane remplis de carbonate de calcium
WO2002018289A1 (fr) Liant de cordon a polymere en poudre thermodurci, composites resultants, et procedes de fabrication
MXPA01009348A (es) Aglutinante lineal
AU647320B1 (en) Process for pultruding fiber reinforced furan composites
WO2002068356A1 (fr) Materiau particulaire reparti entre les fibres assemblees d'un brin et charge de collage augmentee resultante
MXPA99000589A (es) Procedimiento para producir hilos de vidrio ensimados y productos resultan
WO1996000655A1 (fr) Mat impregne de resine resistant a la corrosion

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
AK Designated states

Kind code of ref document: A3

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A3

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
NENP Non-entry into the national phase

Ref country code: JP