WO2003033191A2 - Procede de production de lingots creux constitues d'un materiau metallique ou d'une pluralite de materiaux metalliques - Google Patents

Procede de production de lingots creux constitues d'un materiau metallique ou d'une pluralite de materiaux metalliques Download PDF

Info

Publication number
WO2003033191A2
WO2003033191A2 PCT/IB2002/004124 IB0204124W WO03033191A2 WO 2003033191 A2 WO2003033191 A2 WO 2003033191A2 IB 0204124 W IB0204124 W IB 0204124W WO 03033191 A2 WO03033191 A2 WO 03033191A2
Authority
WO
WIPO (PCT)
Prior art keywords
metallic material
ingot
liquid state
ingot mould
substantially cylindrical
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2002/004124
Other languages
English (en)
Other versions
WO2003033191A3 (fr
Inventor
Giorgio Enrico Falck
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Corinox Srl
Original Assignee
Corinox Srl
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from IT2001MI002098A external-priority patent/ITMI20012098A1/it
Priority claimed from IT2002MI001165A external-priority patent/ITMI20021165A1/it
Application filed by Corinox Srl filed Critical Corinox Srl
Priority to AU2002343118A priority Critical patent/AU2002343118A1/en
Priority to EP02779780A priority patent/EP1461175A2/fr
Priority to US10/491,884 priority patent/US20050067129A1/en
Publication of WO2003033191A2 publication Critical patent/WO2003033191A2/fr
Anticipated expiration legal-status Critical
Publication of WO2003033191A3 publication Critical patent/WO2003033191A3/fr
Ceased legal-status Critical Current

Abstract

L'invention concerne un procédé de production de lingots creux ou polymétalliques à partir d'un premier matériau métallique. Ce procédé consiste à couler un premier matériau métallique à l'état liquide dans un moule de lingot doté d'un fond thermo-isolé, à ne permettre qu'une solidification partielle de ce premier matériau métallique, d'où l'obtention d'une zone sensiblement cylindrique dans laquelle ce premier matériau se trouve encore à l'état liquide au centre du moule de lingot, puis à évacuer le premier matériau se trouvant encore à l'état liquide de cette zone sensiblement cylindrique, d'où la formation d'une cavité sensiblement cylindrique dans le lingot. Le refroidissement subséquent du matériau métallique déjà solidifié restant dans le moule de lingot permet d'obtenir un lingot doté d'une cavité traversante cylindrique parfaitement coaxiale par rapport au lingot ainsi formé.
PCT/IB2002/004124 2001-10-11 2002-10-09 Procede de production de lingots creux constitues d'un materiau metallique ou d'une pluralite de materiaux metalliques Ceased WO2003033191A2 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
AU2002343118A AU2002343118A1 (en) 2001-10-11 2002-10-09 A method for the production of hollow metallic ingots or compound metallic ingots
EP02779780A EP1461175A2 (fr) 2001-10-11 2002-10-09 Procede de production de lingots creux constitues d'un materiau metallique ou d'une pluralite de materiaux metalliques
US10/491,884 US20050067129A1 (en) 2001-10-11 2002-10-09 Method for the production of hollow ingots of a metallic material or of a plurality of metallic materials

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
ITMI2001A002098 2001-10-11
IT2001MI002098A ITMI20012098A1 (it) 2001-10-11 2001-10-11 Procedimento per la produzione di lingotti metallici con anima di acciaio inossidabile
IT2002MI001165A ITMI20021165A1 (it) 2002-05-30 2002-05-30 Procedimento per la produzione di lingotti cavi in materiale metallico o polimetallici
ITMI2002A001165 2002-05-30

Publications (2)

Publication Number Publication Date
WO2003033191A2 true WO2003033191A2 (fr) 2003-04-24
WO2003033191A3 WO2003033191A3 (fr) 2004-07-22

Family

ID=26332788

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2002/004124 Ceased WO2003033191A2 (fr) 2001-10-11 2002-10-09 Procede de production de lingots creux constitues d'un materiau metallique ou d'une pluralite de materiaux metalliques

Country Status (3)

Country Link
EP (1) EP1461175A2 (fr)
AU (1) AU2002343118A1 (fr)
WO (1) WO2003033191A2 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8074704B2 (en) 2009-03-27 2011-12-13 Titanium Metals Corporation Method and apparatus for semi-continuous casting of hollow ingots and products resulting therefrom

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB760501A (en) * 1954-02-15 1956-10-31 English Steel Corp Ltd Improvements in the manufacture of hollow ingots and castings
GB1189724A (en) * 1967-06-01 1970-04-29 Otani Koei Company Ltd Method of Casting Steel Ingots and products therefrom
JPS5584260A (en) * 1978-12-20 1980-06-25 Hitachi Ltd Centrifugal casting method
DE3134758A1 (de) * 1981-09-02 1983-03-17 Kocks Technik Gmbh & Co, 4010 Hilden Verfahren zum herstellen von metallischen hohlbloecken
US4546527A (en) * 1981-12-01 1985-10-15 Kubota Ltd. Composite sleeve for use in rolling rolls for H-section steel and channel steel
GB2121781B (en) * 1982-05-25 1986-03-12 Standard Telephones Cables Ltd Casting hollow bodies e.g. of glass
DE59008036D1 (de) * 1989-05-16 1995-01-26 Mannesmann Ag Verfahren zur herstellung von plattierten hohlblöcken.
JP2898749B2 (ja) * 1990-07-04 1999-06-02 株式会社クボタ 高耐摩耗ロール材およびその製造法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8074704B2 (en) 2009-03-27 2011-12-13 Titanium Metals Corporation Method and apparatus for semi-continuous casting of hollow ingots and products resulting therefrom

Also Published As

Publication number Publication date
WO2003033191A3 (fr) 2004-07-22
AU2002343118A1 (en) 2003-04-28
EP1461175A2 (fr) 2004-09-29

Similar Documents

Publication Publication Date Title
JPS62104652A (ja) 複合インゴツトの連続鋳造方法とその装置
US3206808A (en) Composite-ingot casting system
US4919191A (en) Molten-metal forming method and apparatus which are bottom-loading, bottom-pouring and bottom-unloading
JP4099062B2 (ja) 電気放電を移動させることによる溶融金属の処理
US4211270A (en) Method for continuous casting of metallic strands at exceptionally high speeds
RU2459684C2 (ru) Непрерывная разливка реакционноспособных металлов при использовании покрытия из стекла
US6006821A (en) Method and apparatus for melting and pouring specialty metals
US3610320A (en) Unit for manufacturing hollow metal ingots
JPH06320252A (ja) 加熱・冷却通路孔を有する成形用金型の製造方法
US20050067129A1 (en) Method for the production of hollow ingots of a metallic material or of a plurality of metallic materials
EP1461175A2 (fr) Procede de production de lingots creux constitues d'un materiau metallique ou d'une pluralite de materiaux metalliques
US3990498A (en) Method of continuous casting
JPH06263B2 (ja) 連続鋳造法
US6179042B1 (en) Non-hot crack bottom block for casting aluminum ingot
RU2312738C1 (ru) Способ литья по выплавляемым моделям с кристаллизацией под давлением и устройство для его осуществления
US4307770A (en) Mold assembly and method for continuous casting of metallic strands at exceptionally high speeds
JP4113967B2 (ja) 金属インゴット鋳造装置及び鋳造方法
JPS63157739A (ja) 高融点金属の中空鋳塊の製造装置
JPH0531568A (ja) プラズマ溶解鋳造方法
FI124847B (fi) Jatkuvavalusuulake, muottiosa, jatkuvavalumenetelmä sekä jatkuvavalusuulakkeella, muottiosalla tai jatkuvavalumenetelmällä valmistetun tangon, langan tai putken käyttö aihiona
WO2021192875A1 (fr) Buse en graphite destinée au piquage de fond et procédé de coulée d'alliage ti-al
EP0110854A1 (fr) Procédé et dispositif pour couler des lingots
CN112512725A (zh) 尤其在立式铸造设备中用于铸钢的连铸方法
US4901783A (en) Continuous casting apparatus
US3381073A (en) Process for casting articles

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BY BZ CA CH CN CO CR CU CZ DE DM DZ EC EE ES FI GB GD GE GH HR HU ID IL IN IS JP KE KG KP KR LC LK LR LS LT LU LV MA MD MG MN MW MX MZ NO NZ OM PH PL PT RU SD SE SG SI SK SL TJ TM TN TR TZ UA UG US UZ VN YU ZA ZM

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ UG ZM ZW AM AZ BY KG KZ RU TJ TM AT BE BG CH CY CZ DK EE ES FI FR GB GR IE IT LU MC PT SE SK TR BF BJ CF CG CI GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2002779780

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 2002779780

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 10491884

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP

WWW Wipo information: withdrawn in national office

Ref document number: 2002779780

Country of ref document: EP