WO2004015014A1 - 低蓄熱性熱可塑性樹脂組成物および成形品 - Google Patents

低蓄熱性熱可塑性樹脂組成物および成形品 Download PDF

Info

Publication number
WO2004015014A1
WO2004015014A1 PCT/JP2003/009997 JP0309997W WO2004015014A1 WO 2004015014 A1 WO2004015014 A1 WO 2004015014A1 JP 0309997 W JP0309997 W JP 0309997W WO 2004015014 A1 WO2004015014 A1 WO 2004015014A1
Authority
WO
WIPO (PCT)
Prior art keywords
inorganic pigment
thermoplastic resin
low heat
heat storage
resin composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2003/009997
Other languages
English (en)
French (fr)
Inventor
Yuuichi Kanayama
Kenichi Noguchi
Yasuo Takahashi
Hideyuki Kurimoto
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Techno UMG Co Ltd
Original Assignee
Techno Polymer Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2003002618A external-priority patent/JP3990294B2/ja
Priority claimed from JP2003041757A external-priority patent/JP3990298B2/ja
Application filed by Techno Polymer Co Ltd filed Critical Techno Polymer Co Ltd
Priority to EP03784541A priority Critical patent/EP1541636A4/en
Priority to US10/522,725 priority patent/US7619031B2/en
Publication of WO2004015014A1 publication Critical patent/WO2004015014A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

熱可塑性樹脂〔A〕100質量部と、赤外線反射特性を有する無機顔料〔B〕0.1～15質量部とを含有する低蓄熱性熱可塑性樹脂組成物およびそれから成る成形品。本発明の低蓄熱性熱可塑性樹脂組成物は、蓄熱が少なく、耐候性および耐衝撃性に優れる暗色系の成形品を与える。

Description

明 細 書 低蓄熱性熱可塑性樹脂組成物および成形クロ口 技術分野
本発明は低蓄熱性熱可塑性樹脂組成物に関する。 詳しくは、 本発明は、 成形 加工性に優れ、 且つ、 蓄熱が少なく、 耐候性おょぴ耐衝撃性に優れる暗色系の 成形品を与える低蓄熱性熱可塑性樹脂組成物およびそれから成る成形品に関す る。
熱可塑性樹脂は、 広く用いられており、 着色された樹脂製品は、 熱可塑性樹 脂と、 染料、 顔料等の着色剤と、 を含む樹脂組成物を成形したものである。 例 えば、 黒色樹脂製品は、 着色剤として、 カーボンブラックを含む樹脂組成物か ら製造される。 しかしながら、 カーボンブラックを含む樹脂製品は、 太陽光に 当たる用途の成形品として用いた場合に、 熱の吸収が大きいために成形品が高 温になり、 変形や収縮が発生するという問題や、 自動車の車内部品として用い た場合、 車内の温度を高めることがあり、 冷房効果が妨げられるといった問題 等がある。 カーボンブラックに代わって、 色の三原色を利用した、 有機顔料あ るいは染料の組み合わせによる黒色系着色が試みられている 、 着色性及び耐 候性が十分ではない。
一方、 熱可塑性樹脂として耐熱性ゴム強化樹脂を用いた場合は、 高温時の変 形や収縮等を軽減することができる力5'、 成形加工性が十分ではなく、 大型ある いは複雑な構造を有する成形品を得ることが困難である場合がある。 発明の開示
本発明者らは、 かかる現状に鑑み、 鋭意検討した結果、 成形加工性に優れ、 且つ、 蓄熱が少なく、 耐候性及ぴ耐衝撃性に優れる成形品を与える低蓄熱性熱 可塑性樹脂組成物を提供できることを見出し、 本発明を完成するに至った。 すなわち、 本発明の要旨は、 熱可塑性樹脂 〔A〕 100質量部と、 赤外線反 射特性を有する無機顔料 〔 B〕 0. 1〜 15質量部とを含有する低蓄熱性熱可 塑性樹脂組成物に存する。
本発明の好ましい態様において、 上記の低蓄熱性熱可塑性樹脂組成物は、 ゴ ム質重合体 (a) の存在下に、 ビニル系単量体成分 （b) を重合して得られる ゴム強化ビニル系樹脂 （Al)'、 又は、 該ゴム強化ビニル系樹脂 （A1) とビ 二ル系単量体成分の （共） 重合体 (A2) との混合物からなり、 上記ゴム質重 合体 (a) の含有量が 3〜 40重量0 /0であるゴム強化熱可塑性樹脂 〔A〕 10 0質量部と、 赤外線反射特性を有する無機顔料 〔 B〕 0. 1〜 15質量部とを 含有する。
本発明の他の好ましい態様において、 上記の低蓄熱性熱可塑性樹脂組成物は、 熱可塑性樹脂 〔A〕 100質量部と、 赤外線反射特性を有する無機顔料 〔B〕 0. 5〜15質量部とを含有し、 下記試験条件で得られる成形品の温度上昇が 50°C以下である。
[試験条件] 温度 25 ± 2 °C、 湿度 50 ± 5 % R Hに調節された室に前記組成 物から成る成形品 （長さ 80mm、 幅 55mm、 厚さ 2. 5 mm) を載置し、 高さ 200mmから、 その表面に赤外線ランプ （出力 1 00 W) を 60分間照 射し、 成形品の表面温度を測定し、 赤外線ランプ照射前の初期温度との差を上 昇温度とする。
本発明の更に他の好ましい態様において、 上記の低蓄熱性熱可塑性樹脂組成 物は、 熱可塑性樹脂 〔A〕 100質量部に対し無機顔料 [C] 0. 01〜10 質量部を含有する。 この場合、 次の条件を満足するのが好ましい。
( i ) 上記無機顔料 〔 B〕 は、 ブロックタイプポリプロピレン 100質量部お よび無機顔料 〔B〕 0. 5質量部から成る成形品の L値が 40未満である。
(ii) 上記無機顔料 〔C〕 は、 ブロックタイプポリプロピレン 100質量部お よび無機顔料 〔C〕 0 . 5質量部から成る成形品の L値が 4 0以上である。
(iii) 上記の低蓄熱性熱可塑性樹脂組成物から成る成形品は L値が 4 0以下で あり、 当該成形品に精機凱旋を照射した際の温度上昇が 5 0 °C以下である。 以下、 本発明を詳細に説明する。
本発明に係わる熱可塑性樹脂 〔A〕 としては特に限定されないが、 ゴム強化 ビニル系樹脂、 ポリオレフィン系樹脂 （ポリエチレン系樹脂、 ポリプロピレン 系樹脂、 エチレン · ひ 一ォレフィン系樹脂等） 、 ポリ塩化ビニル樹脂、 ポリ塩 化ビ二リデン樹脂、 ポリ酢酸ビ二ル樹脂、 飽和ポリエステル系樹脂、 アクリル 系樹脂 （ （メタ） アクリル酸エステル化合物の （共） 重合体等） 、 フッ素樹脂、 スチレン系樹脂 （芳香族ビニル化合物等の （共） 重合体等） 、 エチレン '酢酸 ビニル樹脂、 アクリロニトリル ' スチレン樹脂等が挙げられる。 これらは、 1 種単独であるいは 2種以上を組み合わせて使用することができる。 また、 これ らのうち、 ゴム強化ビニル系樹脂、 ポリ塩ィヒビニル樹脂、 アクリル系樹脂が好 ましく、 ゴム強化ビニル系樹脂が特に好ましい。
上記ゴム強化ビニル系樹脂としては、 特に限定されないが、 例えば、 ゴム質 重合体 （a ) の存在下に、 ビニル系単量体成分 ( b ) を重合して得られるゴム 強化ビニル系樹脂 （A 1 ) をそのまま用いてもよいし、 あるいは、 このゴム強 化ビニル系樹脂 （A 1 ) とビニル系単量体成分の （共） 重合体 (A 2 ) との混 合物からなるものを用いてもよい。
上記ゴム質重合体 ( a ) としては、 ポリブタジエン、 スチレン ' ブタジエン 共重合体、 ブタジェン · アタリロニトリル共重合体、 スチレン ' ブタジェン · スチレンブロック共重合体、 スチレン · イソプレン 'スチレンブロック共重合 体等のジェン系 （共） 重合体並びにそれらの水素添加物、 エチレン ' プロピレ ン · （非共役ジェン） 共重合体、 エチレン · ブテン一 1 · (非共役ジェン） 共 重合体、 イソブチレン · イソプレン共重合体等のエチレン · ひ 一ォレフィ ン共 重合体、 アクリルゴム、 ポリウレタンゴム及びシリコーンゴム等の非ジェン系
(共） 重合体が挙げられる。 更に、 上記スチレン · ブタジエンブロック共重合 体の水素添加物には、 上記プロック共重合体の水素添加物の他に、
ロックとスチレン · ブタジエンランダム共重合体の水素添加物等が含まれる。 上記ゴム質重合体 （a) は、 1種単独であるいは 2種以上を組み合わせて使用 することができる。 本発明においては、 ゴム強化ビニル系樹脂を乳化重合によ り得る場合には、 ラテックス状のゴム質重合体が好ましい。
上記ラテックスを用いる場合の、 ラテックス中のゴム質重合体 (a) の重量 平均粒子径は、 好ましくは 500〜8000Aであり、 更に好ましくは 1 00 0〜5000 Α、 特に好ましくは 1000〜400 OAである。 500 A未満 では成形品の耐衝撃性が劣る傾向にあり、 8000 Aを超えると成形品の表面 光沢が劣る傾向にある。
上記ゴム質重合体 （a) を製造する方法としては、 平均粒子径の調整等を考 慮し、 通常、 乳化重合法が好ましいが、 この場合、 平均粒子径は乳化剤の種類 - 量、 開始剤の種類 '量、 重合時間、 重合温度及び攪拌条件等の製造条件を適宜 選択することにより調整することができる。 また、 粒子径分布の他の調整方法 としては、 異なる粒子径の上記ゴム質重合体 (a) の少なくとも 2種類をブレ ンドする方法でもよい。 .
上記ゴム強化ビニル系樹脂 （ A 1 ) の形成に用いられるビニル系単量体成分
(b) としては特に限定されず、 芳香族ビニル化合物、 （メタ） アクリル酸ェ ステル化合物、 シアン化ビニル化合物、 マレイミ ド系化合物、 酸無水物等が挙 げられる。 これらは、 1種単独であるいは 2種以上を組み合わせて用いること ができる。
上記芳香族ビニル化合物としては、 スチレン、 ひ 一メチルスチレン、 0—メ チルスチレン、 p—メチルスチレン、 tーブチルスチレン、 ビニルトルエン、 メチル一 ひーメチルスチレン、 ジビニルベンゼン、 臭素化スチレン等力挙げら れる。 これらのうち、 スチレン、 a—メチルスチレン、 p—メチルスチレンが 好ましい。 また、 これらは、 1種単独であるいは 2種以上を組み合わせて用い ることができる。 (メタ） ァクリル酸エステルイ匕合物としては、 例えば、 メタタリル酸メチル、 メタクリル酸ェチル、 メタクリル酸プロピル、 メタクリル酸ブチル、 アクリル 酸メチル、 アタリル酸ェチル、 アタリル酸プロピル、 アタリル酸ブチル等力 5挙 げられる。 これらのうち、 メタクリル酸メチルカ ?好ましい。 また、 これらは、 1種単独であるいは 2種以上を組み合わせて用いることができる。
上記シアン化ビニル化合物としては、 アクリロニトリル、 メタクリロニトリ ル等が挙げられ、 これらのうち、 アクリロニトリル力好ましい。 また、 これら は、 1種単独であるいは 2種以上を組み合わせて用いることができる。
上記マレイミ ド系化合物としては、 例えば、 マレイミ ド、 N—メチルマレイ ミ ド、 N—ブチルマレイミ ド、 N—フエニルマレイミ ド、 N— （2—メチルフエ ニル） マレイミ ド、 N— （4—ヒ ドロキシフエニル） マレイミ ド、 N—シクロ へキシルマレイミ ド等が挙げられる。 これらのうち、 N—フエニルマレイミ ド が好ましい。 また、 これらは、 1種単独であるいは 2種以上を組み合わせて用 いることができる。 尚、 マレイミ ド系化合物を導入する他の方法としては、 例 えば、 無水マレイン酸を共重合し、 その後イミ ド化する方法でもよい。
上記酸無水物としては、 例えば、 無水マレイン酸、 無水ィタコン酸、 無水シ トラコン酸等が挙げられる。 また、 これらは、 1種単独であるいは 2種以上を 組み合わせて用いることができる。
上記ビニル系単量体成分 （b ) としては、 芳香族ビニル化合物を含むことが 好ましく、 その場合、 芳香族ビニル化合物 （b l ) と、 それ以外のビニル系単 量体 （b 2 ) との重合割合 （b 1 ) Z ( b 2 ) は、 これらの合計を 1 0 0質量 %とした場合、 好ましくは （1 0〜 9 5 ) 質量％ （5〜9 0 ) 質量％、 より 好ましくは （2 0〜8 5 ) 質量0 /0/ ( 1 5〜8 0 ) 質量0 /0である。 芳香族ビニ ル化合物 （b 1 ) の使用量が少なすぎると、 成形加工性、 成形品の美的外観性 が劣る傾向にあり、 多すぎると、 ビニル系単量体 （b 2 ) の使用による効果が 十分に発揮できない傾向にある。 尚、 上記ビニル系単量体 （b 2 ) としては、 好ましくは （メタ） ァクリル酸エステル化合物、 シアン化ビニル化合物、 マレ ィミ ド化合物等から選ばれた少なくとも 1種である。
また、 本組成物を構成する成分のうち、 無機顔料 〔B〕 を含まない熱可塑性 樹脂 〔A〕 のみを用いて得られる成形品に透明性又は透明感を有する場合には、 無機顔料 〔B〕 を含む本組成物からなる成形品は、 無機顔料 〔B〕 に由来する 色の着色性、 鮮映性が向上する。 透明性あるいは透明感を出すためには、 ゴム 質重合体 ( a ) の屈折率に、 ビニル系単量体 ( b ) の重合体の屈折率を合わせ る又は近づけることで達成できる。 屈折率を合わせる又は近づけるために、 ビ 二ル系単量体成分 （b ) として （メタ） アクリル酸エステル化合物を含むこと が好ましく、 この （メタ） アクリル酸エステル化合物の使用量は、 （メタ） ァ クリル酸エステル化合物を含むビニル系単量体成分 （ b ) の重合体及ぴゴム質 重合体 （a ) の各屈折率の差が小さくなるように選択される。 また、 この場合 の （メタ） アクリル酸エステル化合物としては、 メタクリル酸メチルが好まし い o
上記の場合、 （メタ） アクリル酸エステル化合物と、 それ以外のビニル系単 量体としては、 芳香族ビニル化合物、 シアン化ビニル化合物、 マレイミド化合 物から選ばれた少なくとも 1種である。
尚、 前述のように、 上記ゴム強化ビニル系樹脂は、 上記ゴム強化ビニル系樹 脂 （A 1 ) のみであってもよく、 上記ゴム強化ビニル系樹脂 （A 1 ) と、 ビニ ル系単量体成分の重合によって得られた （共） 重合体 (A 2 ) との混合物であつ てもよい。 この （共） 重合体 （A 2 ) は、 上記ゴム強化ビニル系樹脂 （A 1 ) の形成に用いたビニル系単量体成分 （b ) と全く同じ組成の成分を重合して得 られる重合体であつてもよいし、 異なる組成で同じ単量体成分を重合して得ら れる重合体であってもよいし、 異なる組成で異なる単量体成分を重合して得ら れる重合体であってもよい。 更には、 これらの各重合体が 2種以上の含まれる ものであってもよい。
また、 本発明の目的を損なわない範囲で、 更に以下の単量体ィヒ合物を共重合 させたものとすることができる。 その例としては、 エポキシ基、 ヒドロキシル 基、 アミノ基、 アミ ド基、 カルボン酸基、 ォキサゾリン基等の群から選ばれる 少なくとも 1種の官能基を含有するビニル化合物が挙げられる。 その例として は、 グリシジルメタクリレート、 グリシジルァクリレート、 2—ヒドロキシェ チルメタクリレー ト、 2—ヒドロキシェチルァクリレート、 アクリルアミ ド、 アタリル酸、 メタクリル酸、 ビニルォキサゾリン等が挙げられる。
ここで、 上記ゴム強化ビニル系樹脂が、 上記ゴム強化ビュル系樹脂 （A 1 ) である場合、 このゴム強化ビニル系樹脂 （A 1 ) と、 ビニル系単量体成分の重 合によって得られた （共） 重合体 (A 2 ) とからなる場合、 のいずれにおいて も、 本組成物中のゴム質重合体 ( a ) の含有量は、 好ましくは 3〜4 0質量0 /0、 より好ましくは 5〜 3 5質量0 /0である。 ゴム質重合体 ( a ) の含有量が少なす ぎると、 耐衝撃性が劣る傾向にあり、 多すぎると、 硬度、 剛性力劣る傾向にあ る o
次に、 ゴム強化ビニル系樹脂 （A 1 ) 及び （共） 重合体 (A 2 ) の製造方法 について説明する。
上記ゴム強化ビニル系樹脂 （A 1 ) は、 ゴム質重合体 ( a ) の存在下に、 ビ 二ル系単量体成分 （b ) を、 好ましくは乳化重合、 溶液重合、 塊状重合による 方法で製造することができる。
乳化重合により製造する場合には、 重合開始剤、 連鎖移動剤 （分子量調節剤） 、 乳ィ匕剤、 水等が用いられる。
尚、 ゴム強化ビニル系樹脂 （A 1 ) を製造するために用いられるゴム質重合 体 （a ) 及ぴビニル系単量体成分 （b ) は、 反応系において、 ゴム質重合体全 量の存在下に、 単量体成分を一括添加してもよいし、 分割又は連続添加しても よい。 また、 これらを組み合わせた方法でもよい。 更に、 ゴム質重合体の全量 又は一部を、 重合途中で添加して重合してもよい。
上記重合開始剤としては、 クメンハイドロパーォキサイド、 ジィソプロピル ベンゼンハイドロパーォキサイド、 ノヽ。ラメンタンハイドロパ一ォキサイド等で 代表される有機ハイドロパーォキサイド類と含糖ピロリン酸処方、 スルホキシ レート処方等で代表される還元剤との組み合わせによるレドックス系、 あるい は過硫酸カリウム等の過硫酸塩、 ベンゾィルパーオキサイ ド （B P O ) 、 ラウ ロイルパーオキサイ ド、 t—ブチルパーォキシラウレイ ト、 t _プチルバーオ キシモノ力一ボネ一ト等の過酸化物等力挙げられ、 これらは、 1種単独である いは 2種以上を組み合わせて用いることができる。 更に、 上記重合開始剤は、 反応系に一括又は連続的に添加することができる。 また、 上記重合開始剤の使 用量は、 上記ビニル系単量体成分 （b ) 全量に対し、 通常、 0 . 1〜1 . 5質 量0 /0、 好ましくは 0 . 2〜0 . 7質量％である。
上記連鎖移動剤としては、 ォクチルメルカプタン、 n― ドデシルメルカプタ ン、 t一 ドデシルメルカブタン、 n—へキシルメルカプタン、 n—へキサデシ ルメルカプタン、 n—テトラデシルメルカプタン、 t—テトラデシルメル力プ タン等のメルカプタン類、 ターピノーレン、 a—メチルスチレンのダイマー等 が挙げられ、 これらは、 1種単独であるいは 2種以上を組み合わせて用いるこ とができる。 上記連鎖移動剤の使用量は、 上記ビニル系単量体成分 （b ) 全量 に対して、 通常、 0 . 0 5〜2 . 0質量0 /0である。
乳化重合の場合に使用する乳化剤としては、 高級アルコ一ルの硫酸エステル、 ドデシルベンゼンスルホン酸ナトリゥム等のアルキルべンゼンスルホン酸塩、 ラウリル硫酸ナトリウム等の脂肪族スルホン酸塩、 高級脂肪族力ルポン酸塩、 リン酸系等のァニオン性界面活性剤、 ポリエチレングリコールのアルキルエス テル型、 アルキルエーテル型等のノニオン系界面活性剤等力 s挙げられる。 これ らは、 1種単独であるいは 2種以上を組み合わせて用いることができる。 上記 乳化剤の使用量は、 通常、 上記ビニル系単量体成分 （b ) 全量に対して、 0 . 3〜5 . 0質量0 /0である。
乳化重合により得られたラテックスは、 通常、 凝固剤により凝固させ、 重合 体成分を粉末状とし、 その後、 これを水洗、 乾燥することによって精製される。 この凝固剤としては、 塩化カルシウム、 硫酸マグネシウム、 塩化マグネシウム、 塩ィ匕ナトリウム等の無機塩や、 硫酸、 塩酸等の無機酸、 酢酸、 乳酸等の有機酸 等が用いられる。
溶液重合、 塊状重合による製造方法は、 公知の方法を採用することができる。 上記ゴム強化ビニル系樹脂 （A 1) のグラフト率は、 好ましくは 10〜20 0 %、 更に好ましくは 1 5〜 1 50 %、 特に好ましくは 20〜 1 00 %である。 上記ゴム強化ビニル系樹脂 （A 1) のグラフト率が 10%未満では、 本発明の 樹脂組成物を用いて得られる成形品の外観不良、 衝撃強度の低下を招くことが ある。 また、 200 %を超えると、 加工性が劣る。
ここで、 グラフト率とは、 上記ゴム強化ビニル系樹脂 （A l) 1グラム中の ゴム成分を Xグラム、 上記共重合樹脂 （A 1 ) 1グラムをメチルェチルケトン に溶解させた際の不溶分を yグラムとしたときに、 次式により求められる値で める o
グラフ卜率 (%) = I (y - x) /χί X 1 00
また、 上記ゴム強化ビニル系樹脂 （A 1) のアセトン可溶分の極限粘度 〔7〕 (メチルェチルケトン中、 30°Cで測定） は、 好ましくは 0. 1〜1. O d l /g、 更に好ましくは 0. 2〜0. 9 d 1 /g、 特に好ましくは 0. 3〜0. 7 d 1/gである。 この範囲とすることにより、 成形加工性 （流動性） に優れ、 本発明の樹脂組成物を用いて得られる成形品の耐衝撃性も優れる。
尚、 上記グラフト率 （％) 及び極限粘度 〔 〕 は、 上記ゴム強化ビニル系樹 脂 （A1) を重合するときの、 重合開始剤、 連鎖移動剤、 乳化剤、 溶剤等の種 類や量、 更には重合時間、 重合温度等を変えることにより、 容易に制御するこ と力 sできる。
上記 （共） 重合体 (A2) は、 例えば、 バルク重合、 溶液重合、 乳化重合及 ぴ懸濁重合等により得ることができる。
上記 （共） 重合体 (A2) のアセトン可溶分の極限粘度 〔 〕 （メチルェチ ルケトン中、 30 °Cで測定） は、 好ましくは 0. 1〜 1 · 0 d 1 / g、 より好 ましくは 0. 15〜0. 7 d 1/gである。 極限粘度 〔ク〕 が上記範囲内であ ると、 成形加工性と耐衝撃性の物性バランスに優れる。 尚、 極限粘度 〔 〕 は、 上記ゴム強化ビニル系樹脂 （A 1) と同様にして制御することができる。
上記ゴム強化ビニル系樹脂のァセトン可溶分の極限粘度 〔 〕 （メチルェチ ルケトン中、 30でで測定） は、 好ましくは 0. 1〜 0. 8 d 1 / g、 より好 ましくは 0. 15〜0. 7 d 1/gである。 極限粘度 〔 〕 が上記範囲内であ ると、 成形加工性と耐衝撃性の物性バランスに優れる。
本発明に係わる赤外線反射特性を有する無機顔料 〔B〕 としては、 赤外線を 吸収しにくい性質を有するものであれば特に限定されず、 F e、 C r、 Mn、 Cu、 C o及び N iから選ばれる元素を含む化合物力 s好ましい。 特に、 上記元 素の酸ィ匕物、 複合酸化物等が好ましく、 具体的には、 F e O、 F e O (OH) 、 F e203、 C rO、 C r203、 C r 203 · 2H20、 MnO、 Mn203、 M n 02、 C uO、 Cu20、 C o O、 C o O ' A l 203、 F e (F e， C r ) 20 い (C o, F e) (F e， C r) 20い C u (C r， Mn) 204、 （C u， F e, Mn) (F e, C r， Mn) 204、 （F e， Z n) (Fe, C r) 204、
(F e, Z n) F e 204、 C oA l 2〇い C o (A 1， C r) 204、 C r 20 3 : F e203、 (N i , Co, F e) (F e， C r) 204等が挙げられる。 こ れらのうち、 C r203 : F e203、 (C u, F e, Mn) (F e， Cr， Mn) 204、 F e (F e， C r) 204、 （C o, F e) (F e， C r ) 20い C u
(C r， Mn) 204、 (N i , C o, F e) (F e, C r) 204が好ましい。 また、 上記例示した酸^匕物及び複合酸化物は、 それぞれ 1種単独であるいは 2 種以上を組み合わせて用いることができ、 所望の色に着色された成形品とする こと力 s 'できる。
尚、 上記例示した中で、 C o〇は、 単独で用いた場合、 太陽光が当たったと きに赤外線の強度等によつて成形品の表面に白化が発生したり、 紫外線によつ て揮散したりすることがあるため、 C oOを用いる場合は、 他の無機顔料と組 み合わせて用いること力 子ましい。
本発明においては、 黒系、 深緑系等の暗色系の色の成形品を得るために、 無 機顔科 〔B〕 として F e、 C r及び Mnから選ばれる少なくとも 2種の元素を 含む酸化物を用いることが好ましい。 その例としては、 F e (F e， C r) 2 04、 (C o, F e) (F e， C r) 204、 C u (C r， Mn) 204、 (C u, F e， Mn) (F e， C r, Mn) 204、 （F e, Z n) (F e, C r) 204、 C r 203 ： F e 203等力挙げられる。 これらは、 1種単独であるいは 2種以上 を組み合わせて用いることができる。
黒系、 深緑系等の暗色系の色の成形品とするためには、 上記例示した無機顔 料は、 その合計が、 無機顔料 〔B〕 全体に対して、 好ましくは 60質量％以上、 より好ましくは 70〜 100質量％、 更に好ましくは 80〜 100質量％とな るように含有させることが必要である。 100質量％でない場合の残部は、 他 の顔料 （無機顔料、 有機顔料、 カーボンブラック等） とすることができる。 す なわち、 以下に説明する無機顔料 〔C〕 と効果的に組み合わせることにより、 所望の色に着色された成形品を得ることができる。 また、 黒系、 深緑系のみな らず、 青系、 茶系等の暗色系の色についても、 所望の色に応じて、 1種単独で あるいは色の三原色を利用した複数種の無機顔料の組み合わせによって得るこ とができる。 従来の着色剤は、 有機顔料あるいは染料を組み合わせるものであ り、 成形品が退色、 変色する等耐候性に劣っていたのに対し、 本発明において は、 無機顔料を用いているため、 成形品の退色、 変色等を引き起こすことがな い。 そして、 無機顔料に由来する色を鮮やかに呈し続ける成形品とすることが できる。
上記例示した無機顔料を用いる場合の、 本組成物を構成する熱可塑性樹脂 〔A〕 及び無機顔料 〔B〕 の含有割合は、 熱可塑性樹脂 〔A〕 100質量部に 対して、 無機顔料 〔B〕 が 0. 1〜1 5質量部、 好ましくは 0. 5〜15質量 部であり、 より好ましくは 1. 0〜10質量部、 特に好ましくは 1. 0〜7質 量部である。 無機顔料 〔B〕 の含有量が少なすぎると、 着色鮮映性が劣る傾向 にあり、 一方、 多すぎると、 成形加工性と耐衝撃性力 ?劣る傾向にある。
また、 黒系、 深緑系等の暗色系の色の成形品を得るための他の態様は、 上記 無機顔料 〔B〕 として C 0元素及び N i元素を含む酸ィ匕物を用いること力5、好ま しい。 その例としては、 （N i， C o, F e) (F e, C r) 204等カ挙げら れる。 これらは、 1種単独であるいは 2種以上を組み合わせて用いることがで きる。 また、 他の無機顔料と組み合わせて用いることもできる。
また、 上記無機顔料 〔B〕 として C o元素及び N i元素を含む酸化物を用い る場合、 本組成物中の C 0元素及び N i元素の含有量の比 C oZN iが 5Z9 5〜95Z 5であることが好ましい。 より好ましくは 10/90〜 90/1 0 であり、 更に好ましくは 1 5/85〜85/1 5である。 上記範囲とすること によって、 暗色系着色性及ぴ低蓄熱性に一段と優れた熱可塑性樹脂組成物とす ることができる。
黒系、 深緑系等の暗色系の色の成形品とするためには、 上記例示した無機顔 料は、 その合計が、 無機顔料 〔B〕 全体に対して、 好ましくは 1 5質量％以上、 より好ましくは 20〜 1 00質量％、 更に好ましくは 25〜 100質量％とな るように含有させることが必要である。 1 00質量％でない場合の残部は、 他 の顔料 （無機顔料、 有機顔料、 カーボンブラック等） とすることができる。 す なわち、 以下に説明する無機顔料 〔C〕 と効果的に組み合わせることにより、 所望の色に着色された成形品を得ることができる。 また、 黒系、 深緑系のみな らず、 青系、 茶系等の暗色系の色についても、 所望の色に応じて、 1種単独で あるいは色の三原色を利用した複数種の無機顔料の組み合わせによって得るこ とができる。
上記例示した無機顔料を用いる場合の、 本組成物を構成する熱可塑性樹脂 〔A〕 及び無機顔料 〔B〕 の含有割合は、 熱可塑性樹脂 〔A〕 100質量部に 対して、 無機顔料 〔B〕 が 0. 1〜1 5質量部、 好ましくは 0. 5〜1 5質量 部、 より好ましくは 1. 0〜10質量部、 特に好ましくは 1. 0〜8質量部で ある。 無機顔料 〔B〕 の含有量が少なすぎると、 十分な低蓄熱性を得ることが できず、 着色性も劣る傾向にあり、 一方、 多すぎると、 成形加工性、 耐衝撃性 力5'劣る傾向にある。
尚、 上記いずれの態様においても、 無機顔料 〔B〕 の 1つに C o 0を用いる 場合は、 無機顔料全体を 1 0 0質量％とすると、 C 0 0の含有割合は好ましく は 5 0質量％以下、 より好ましくは 4 0質量％以下、 更に好ましくは 3 0質量 %以下である。 残部は、 他の無機顔料であり、 例えば、 F e ( F e， C r ) 2 04等である。
上記無機顔料 〔B〕 としては、 上記例示したものに加え、 更に、 従来より赤 外線反射特性を有する材料として用いられている T i 02、 有機顔料等を組み 合わせて用いることができる。
尚、 上記無機顔料 〔B〕 は粉末であることが好ましく、 更に好ましくは微粉 末である。 形^は特に限定されないが、 粉末の最大長さは、 好ましくは 5 n m 〜4 0 ^ m, より好ましくは 1 5 n m〜3 0 Λ πιである。 上記範囲とすること によって、 取扱い性と耐衝撃性のバランスに優れる。
無機顔料 〔Β〕 としては、 プロックタイプポリプロピレン 1 0 0質量部及び この無機顔料 〔Β〕 0 . 5質量部からなる組成物より得られる成形品の L値が 好ましくは 4 0未満、 より好ましくは 5〜3 9、 特に好ましくは 5〜 3 5であ る。 上記 L値が高いと、 本発明の目的の暗色系の成形品力 s得られないことがあ る ο
本発明に係わる無機顔料 〔C〕 は特に限定されない。 上記無機顔料 〔B〕 に 含まれるような F e、 C r、 M n、 C o及び N iから選ばれる元素から構成さ れていてもよい。 好ましくはプロックタイプポリプロピレン 1 0 0質量部及び この無機顔料 〔 C〕 0 . 5質量部からなる組成物より得られる成形品の L値が 4 0以上である。 この場合、 さらに上述のようにブロックタイプポリプロピレ ン 1 0 0質量部及びこの無機顔料 〔B〕 0 . 5質量部からなる組成物より得ら れる成形品の L値が好ましくは 4 0未満、 より好ましくは 5〜3 9、 特に好ま しくは 5〜3 5である。
上記無機顔料 〔C〕 としては、 白色系無機顔料、 赤色系無機顔料、 緑色系無 機顔料、 黄色系無機顔料、 茶色系無機顔料、 青色系無機顔料、 紫色系無 ilH料、 銀色系無機顔料、 及びパール色系無機顔料等が挙げられ、 これらは、 1種単独 であるいは 2種以上を組み合わせて用いることができる。
上記白色系無機顔科としては、 Z nO、 T i 02、 A l 203 ' nH20、 〔Z n S+B a S04〕 、 C a S04 · 2 H20, B a S04、 C a C03、 2 P b C 03 · P b (OH) 2等が挙げられる。 これらは、 1種単独であるいは 2種以上 を組み合わせて用いることができる。
上記赤色系無機顔料としては、 C d S ' nC d S e、 P b C r 04 ' mP b M o 04 · n P b S 04等が挙げられる。 これらは、 1種単独であるいは 2種以 上を組み合わせて用いることができる。
上記緑色系無機顔料としては、 Cu (C2H 302) 3、 C u (As 02) 2、 C oO - n Z nO、 B aMn02、 C u2 (OH) 2 (C03) 、 T i一 C o—N i一 Z n系複合酸化物等が挙げられる。 これらは、 1種単独であるいは 2種以 上を組み合わせて用いることができる。
上記黄色系無機顔科としては、 T i 02 · B a 0 · N i 0、 T i 02 · N i 0 · S b 203、 F e 203 ' H20、 P b C r 04、 P b (S b 03) 2、 P b3 (S b 04) 2、 T i -S b-N i系複合酸ィヒ物、 T i一 S b— C r系複合酸化物等が 挙げられる。 これらは、 1種単独であるいは 2種以上を組み合わせて用いるこ とができる。
上記茶色系無機顔料としては、 T i 02 ' S b 203 ' N i O、 Z n— F e系 複合酸化物 （Z ηθ · F e 203等） 、 Z n— F e— C r系複合酸化物 (ZnO · F e 203. C r 203等） 等が挙げられる。 これらは、 1種単独であるいは 2種 以上を組み合わせて用いることができる。
上記青色系無機顔料としては、 C o O ' nA l 203、 C oO - n S nO - m MgO、 N a 6A 16 (S i 04) 6 · 2 N a 3 S 04等が挙げられる。 これらは、 1種単独であるいは 2種以上を組み合わせて用いることができる。
上記紫色系無機顔料としては、 C o 3 (P04) 2、 (NH4) 2Mn02 (P2 07) 2等が挙げられる。 これらは、 1種単独であるいは 2種以上を組み合わせ て用いることができる。 上記銀色系無機顔料としては、 A 1粉末、 亜鉛粉末等が挙げられる。 これら は、 1種単独であるいは 2種以上を組み合わせて用いることができる。
上記パール色系無機顔料としては、 マイ力等が挙げられる。 これらは、 1種 単独であるいは 2種以上を組み合わせて用いることができる。
尚、 上記白色系、 銀色系、 パール色系無機顔料を用いた場合、 所望の色を維 持しつつ、 メタリック調の外観を得ることができる。
上記例示した無機顔料は、 その合計が、 無機顔料 〔C〕 全体に対して、 好ま しくは 1 5質量％以上、 より好ましくは 20〜 100質量％、 更に好ましくは 25〜 100質量％となるように含有させることによって、 そして、 上記無機 顔料 〔B〕 と効果的に組み合わせることにより、 所望の色に着色された成形品 を得ることが、できる。
また、 上記無機顔料 〔C〕 としては、 赤外線反射特性の有無についても特に 限定されない。 赤外線反射特性を有することが好ましい力 赤外線反射特性を 有さないものであってもよい。
本発明の低蓄熱性熱可塑性樹脂組成物において、 上記無機顔料 〔C〕 の含有 割合は、 熱可塑性樹脂 〔A〕 100質量部に対して、 0. 01〜10質量部で あり、 好ましくは 0. 01〜8質量部、 より好ましくは 0. 0 1〜6質量部で ある。 無機顔料 〔C〕 の含有量が少なすぎると、 色調安定性に劣る傾向にあり、 一方、 多すぎると、 色調安定性及び耐衝撃性に劣る傾向にある。
黒色系の成形品を得るための無機顔料 〔B〕 及び無機顔料 〔C〕 の好ましレ 組み合わせは、 F e (F e， C r) 204、 (C o, F e) (F e， Cr) 204、 C u (C r， Mn) 204、 （Cu， F e， Mn) (F e， C r， Mn) 204及 ぴ （N i， C o, F e) (F e， C r) 204から選ばれる無機顔料 〔B〕 と、 T i 02、 T i— C o— N i— Z n系複合酸化物、 Na6A l 6 (S i 04) 6 · 2N a3 S 04及び T i— S b— C r系複合酸化物に例示される無機顔料 〔C〕 との組み合わせ等が挙げられる。
深緑色系の成形品を得るための無機顔料 〔B〕 及び無機顔料 〔C〕 の好まし い組み合わせは、 Fe (F e , C r) 204、 (C o, F e) (Fe， C r ) 2 04、 C u (Cr， Mn) 204、 (C u, Fe， Mn) (F e, C r， Mn) 2 04及び （N i， Co, Fe) (Fe, C r) 204から選ばれる無機顔料 〔B〕 と、 T i 02、 T i— Co—N i— Z n系複合酸化物、 N a6A 16 (S i 04) 6 - 2Na3 S04及び T i _S b_C r系複合酸化物に例示される無機顔料
〔C〕 との組み合わせ等が挙げられる。
また、 濃褐色系の成形品を得るための無機顔料 〔B〕 及び無機顔料 〔C〕 の 好ましい組み合わせは、 Fe (Fe, C r) 2〇4、 （Co, Fe) (Fe， C r ) 204、 C u (C r , Mn) 204、 (C u, F e, Mn) (Fe, C r， M n) 204及び （Ni, Co, Fe) (Fe， C r) 204から選ばれる無機顔料
〔B〕 と、 T i 02及び T i— S b _Ν i系複合酸化物に例示される無機顔料
〔C〕 との組み合わせ等が挙げられる。
また、 本発明の低蓄熱性熱可塑性樹脂組成物を構成する熱可塑性樹脂 〔A〕 、 無機顔料 〔B〕 及び無機顔料 CC) の含有割合は、 熱可塑性樹脂 〔A〕 100 質量部に対して、 無機顔料 〔B〕 力 s'0. 1〜15質量部、 好ましくは 0. 3〜 10質量部、 より好ましくは 0. 5〜8質量部でぁり、 無機顔料 〔〇〕 が0. 01〜 10質量部、 好ましくは 0. 01〜8質量部、 より好ましくは 0. 01 〜6質量部である。 この範囲とすることにより、 成形加工性に優れ、 且つ、 蓄 熱が少なく、 耐候性及ぴ I 衝撃性に優れる暗色系の成形品を得ることができる。 尚、 上記無機顔料 〔C〕 として、 緑色系無機顔料のみを用いることによって、 黒色系あるいは深緑色系の成形品を得ることができる。 具体的には、 T i— C 0— N i _Z n系複合酸化物に例示される緑色系無機顔料である。 上記無機顔 料 〔B〕 、 例えば、 （Ni， Co, Fe) (Fe， C r) 204、 及び、 この緑 色系無機顔料の併用によって、 深みのある暗色系の成形品を得ることができる。
この場合の、 熱可塑性樹脂 〔A〕 、 無機顔料 〔B〕 及び無機顔料 〔C〕 の好 ましい含有割合は、 熱可塑性樹脂 〔A〕 100質量部に対して、 無機顔料 〔B〕 が 0. 1〜15質量部、 好ましくは 0. 3〜10質量部、 より好ましくは 0. 5〜 8質量部であり、 無機顔料 〔C〕 が 0. 01〜1 0質量部、 好ましくは 0. 01〜8質量部、 より好ましくは 0. 01〜6質量部である。
更に、 上記緑色系無機顔料のみによる黒色系と異なる、 より深みのある黒色 系の成形品を得るために、 上記無機顔料 〔C〕 として、 上記緑色系無機顔料に 加え、 白色系無機顔料及び青色系無機顔料を併用することが好ましい。 これら の好ましい無機顔料を例示すると、 緑色系無機顔料として、 Cu 2 (OH) 2
(C 03) 、 C u (C2H 302) 3、 C u (A s 02) 2、 T i _C o_N i - Z n系複合酸化物を、 白色系無機顔料として、 T i〇2を、 青色系無機顔料とし て、 Na6A 16 (S i 04) 6 · 2N a 3 S 04を挙げることができる。 上記無 機顔料 〔B〕 と、 これらの緑色系、 白色系、 青色系無機顔料とを組み合わせる ことによって、 低蓄熱性及ぴ耐候性にも優れた成形品とすることができる。 この場合の、 緑色系、 白色系、 青色系無機顔料の好ましい配合割合は、 所望 の着色を現出するように各量を選択すればよいが、 これらの全体を 1 00質量 部とした場合、 各顔料の配合量は、 緑色系無機顔料を好ましくは 0. 01〜 1 0質量部、 より好ましくは 0. 01〜8質量部用い、 白色系無機顔料を好まし くは 0. 01〜 10質量部、 より好ましくは 0. 01〜8質量部用い、 そして、 青色系無機顔料を好ましくは 0. 01〜10質量部、 より好ましくは 0. 01 〜 8質量部用いることである。
尚、 上記無機顔料 〔C〕 は粉末であることが好ましく、 更に好ましくは微粉 末である。 形状は特に限定されない力 s'、 粉末の最大長さは、 好ましくは 5 nm 〜40/ m、 より好ましくは 1 5 nm〜30 である。 上記範囲とすること によって、 取扱い性と耐衝撃性のバランスに優れる。
本発明の樹脂組成物には、 必要に応じて、 種々の添加剤を含有させることが できる。 例えば、 酸化防止剤、 可塑剤、 着色剤、 難燃剤、 充填剤、 滑剤、 帯電 防止剤等である。 着色剤としては、 成形品'の蓄熱を低く維持できる範囲で、 有 機顔料、 有機染料、 カーボンブラック等を配合することができる。
本発明の樹脂組成物は、 各種押出機、 バンバリ一ミキサー、 ニーダー、 ロー ル等を用い、 各成分を混練りすることによって得られる。 混練りするに際して は、 各成分を一括して混練りしてもよく、 多段添加方式で混練りしてもよい。 このようにして得られた樹脂組成物を用いて、 射出成形、 シート押出、 真空成 形、 発泡成形等によつて各種成形品を作ることができる。
本発明の樹脂組成物は、 下記試験条件で得られる成形品の温度上昇が、 通常 5 0 °C以下、 好ましくは 4 5 °C以下、 更に好ましくは 4 0 °C以下である。 この 試験条件によって、 蓄熱性を評価することができる。
〔試験条件〕
本組成物からなる成形品 （長さ 8 0 mm、 幅 5 5 mm, 厚さ 2 . 5 mm) を、 温度 2 5土 2 °C、 湿度 5 0 ± 5 % R Hに調節された室に載置し、 高さ 2 0 0 m mから、 その表面に赤外線ランプ又は白熱灯 （出力 1 0 0 W) を 6 0分間照射 し、 成形品の表面温度を測定し、 赤外線ランプ又は白熱灯照射前の初期温度と の差を上昇温度とする。
また、 本組成物からなる成形品に、 波長 1 0 0 0〜 1 2 5 0 n mの光を照射 した際の、 この波長範囲における光の反射率の最大値は、 好ましくは 1 5 %以 上であり、 より好ましくは 2 0 %以上、 更に好ましくは 2 5 %以上である。 但 し、 上限は、 通常、 8 0 %である。 上記最大値が高いほど、 低蓄熱性に優れた 成形品といえる。
本発明の樹脂組成物に含まれる無機顔料 〔B〕 はそれぞれ固有の色を有する が、 特に十分な濃度の色を呈色させ且つ鮮映性に優れた成形品とするためには、 熱可塑性樹脂 〔A〕 に対する無機顔料 〔B〕 の含有割合を十分とする以外に、 無機顔料 〔B〕 の含有割合が少なめであっても、 成形品の厚さを大きくする等 によつて達成することができる。
また、 本組成物からなる成形品の色調を L a b方式で表示したときに、 L値 は、 好ましくは 4 0以下であり、 より好ましくは 3 5以下、 更に好ましくは 3 0以下である。 但し、 下限は、 通常、 5である。 L値が小さいほど、 暗色系低 蓄熱性成形品といえる。 本発明の樹脂組成物は、 成形加工性に優れ、 上記成形方法によって得られる 成形品は、 蓄熱が少なく、 耐候性及ぴ耐衝撃性に優れており、 雨どい等の屋外 家屋の構造部材、 自動車内装部品、 エアーコンディショナ一のダクトカバー等 に好適に使用することができる。 発明を実施するための最良の形態
次に、 実施例により、 本発明を具体的に説明するが、 本発明はその要旨を超 えない限り、 以下の実施例により限定されるものではない。 尚、 以下の諸例に おいて、 部及び％は特に断らない限り質量基準である。 また、 使用した評価方 法は以下の通りである。
(1) 成形加工性
流動性 （メルトフローレート） をもつて評価し、 J I S K 7210に準じ て測定した。 測定温度は 220 °C、 荷重は 98N、 単位は g/10分である。
(2) 蓄熱性
温度 25 ± 2 °C、 湿度 50 ± 5 % R Hに調節された室において、 樹脂組成物 を用いて得られた長さ 80mm、 幅 55mm、 厚さ 2. 5 mmの成形品 （試験 片） の表面に、 高さ 200 mmから赤外線ランプ （出力 100W) を照身寸して、 60分後の試験片の表面温度を、 表面温度計を用いて測定した。 単位は。 Cであ る
また、 低蓄熱性の安定性を見るために、 上記測定を 5回行った際に得られた 温度の最大値と最小値の差 Δ Tを求め、 以下の基準に従つて評価した。
A； ΔΤが 3°C以下である。
B ； ΔΤが 3°Cを超えて 5°C未満である。
C ； ΔΤが 5°C以上である。
(3) 耐衝撃性
アイゾット衝撃強度をもって評価した。 J I S K71 10の 2号型試,験片 を成形し、 アイゾット衝撃強度を測定した。 単位は、 k jZm2である。 (4) 耐候性
長さ 80mm、 幅 55 mm, 厚さ 2. 5 mmの試験片を、 サンシャインゥェ ザ一才メーター （スガ試験機社製） を用いて、 降雨サイクル 18分 /120分、 ブラックパネル温度 63 °Cとして 1000時間暴露し、 暴露前後の色調変化値 ΔΕを算出した。
ΔΕは、 多光源分光測定計 （スガ試験機社製） を用いて変色度 L a b (L ； 明度、 a ；赤色度、 b ；黄色度） を測定し、 次式により算出した。
- f 〔 （I^— LJ 2+ (a i-a2) 2+ (b
Figure imgf000021_0001
2〕
(式中、 aい は、 暴露前の値を、 L2、 a 2、 b 2は暴露後の値を示 す。 )
Δ Eの値は、 小さい方が色の変化が小さく、 色調が優れていることを示す。 評価基準は以下の通りである。
A； ΔΕが 5以下である。
B ； ΔΕが 5を超えて 10未満である。
C； 厶£カ 10以上である。
(5) 着色鮮映性
長さ 80 mm, 幅 55mm、 厚さ 2. 5 mmの試験片を目視で評価した。 評 価基準は以下の通りである。
A；優れている。
B； Aに比べてやや劣る。
C；劣る。
(6) "直
長さ 80mm、 幅 55mm、 厚さ 2. 5 mmの試験片を用い、 多光源分光測 定計 （スガ試験機社製） により L値を求めた。
(7) 反射率
長さ 80mm、 幅 55 mm, 厚さ 2. 5 mmの試験片を用い、 赤外線反射率 測定計 （島津製作所社製） により測定した。 照射した赤外線の波長範囲は 20 0〜2500 nmである。 1 000〜 1 2 50 n mの波長範囲における反射率 の最大値を求めた。
製造例 1 〔ゴム強化ビニル系樹脂 （A1— 1) の製造〕
攪拌機を備えたガラス製反応器に、 イオン交換水 75部、 ロジン酸カリウム 0. 5部、 t— ドデシルメルカブタン 0. 1部、 ポリブタジエンラテックス
(平均粒子径； 2 700人、 ゲル含率； 90%) 3 2部 （固形分換算） 、 スチ レン一ブタジエン共重合ラテックス （スチレン含率 25%、 平均粒子径 550 OA) 8部、 スチレン 1 5部及びアクリロニトリル 5部を入れ、 窒素気流中で 攪拌しながら昇温した。 内温が 45 °Cに達した時点でピロリン酸ナトリウム 0. 2部、 硫酸第 1鉄 7水和物 0. 0 1部及ぴブドウ糖 0. 2部をイオン交換水 2 0部に溶解した溶液を加えた。 その後、 クメンハイド口パーオキサイ ド 0. 0 7部を加えて重合を開始し、 1時間重合させた。 次いで、 イオン交換水 50部、 ロジン酸カリウム 0. 7部、 スチレン 30部、 アクリロニトリル 10、 tード デシルメルカプタン 0. 05部及びクメンハイ ドロパーォキサイド 0. 0 1部 を 3時間かけて連続的に添加した。 1時間重合させた後、 2， 2 ' ーメチレン —ビス （4—エチレン一 6_ t—ブチルフエノール） 0. 2部を添加し重合を 完結させた。 反応生成物のラテックスを凝固、 水洗した後、 乾燥してゴム強化 ビニル系樹脂 （A 1— 1 ) を得た。 グラフト率は 72 %、 ァセトン可溶分の極 限粘度 〔 〕 は 0. 4 7 d l/gであった。
製造例 2 〔ゴム強化ビニル系樹脂 （A 1—2) の製造〕
まず、 スチレン 73部及びアクリロニトリル 27部を混合して、 単量体混合 物を調製した。
攪拌機を備えたガラス製反応器に、 アクリル酸 n—ブチル 99部及ぴァリル メタクリレート 1部を乳化重合して得られた重量平均粒子径が 284 n mであ るアタリル系ゴム質重合体ラテックス 1 00部 （固形分換算） とィォン交換水 1 1 0部を仕込み、 窒素気流中で攪拌しながら昇温した。 内温が 40°Cに達し た時点で、 ピロリン酸ナトリウム 1. 2部及びプドウ糖 0. 3部をィォン交換 水 20部に溶解した水溶液 （以下、 「 R E D水溶液」 という。 ） のうちの 86 %分と、 t一ブチルハイドロパーオキサイ ド 0. 4部、 不均化口ジン酸カリゥ ム 2. 4部をイオン交換水 30部に溶解した水溶液 （以下、 「CAT水溶液」 という。 ） のうちの 30 %分と、 を反応器に入れ、 その直後に上記単量体混合 物及び C A T水溶液をそれぞれ、 3時間及び 3時間 30分に渡つて連続添加し、 重合を開始した。 重合開始から 75°Cまで昇温し、 その後、 75°Cに保持した。 重合を開始して 180分後に RED水溶液の残り 14%分を反応器に仕込み、 60分間、 同温度で保持した後に重合を終了した。 以下、 上記 （A1— 1) と 同様にして、 ゴム強化ビニル系樹脂 （A 1— 2) を得た。 グラフト率は 50%、 アセトン可溶分の極限粘度 〔 〕 は、 0. 45 d l/gであった。
製造例 3 〔ゴム強化ビニル系樹脂 （A 1— 3) の製造〕
リボン型攪拌翼、 助剤連続添加装置及び温度計を装備したステンレス製ォー トクレーブに、 エチレン ' プロピレン系ゴム質重合体 （J SR製、 商品名 「E P 84」 ） 20部、 スチレン 56部、 アクリロニトリル 24部及ぴトルエン 1 10部を仕込み、 内温を 75 °Cに昇温して、 オートクレーブ内容物を 1時間攪 拌して均一溶液とした。 その後、 t—ブチルパーォキシイソプロピルカーボネ一 ト 0. 45部を添加し、 内温を更に上昇させ、 100°Cとした後、 この温度に 保ちながら、 攪拌回転数 100 r pmとして重合反応を行った。 重合反応が開 始してから 4時間目から内温を 120°Cとし、 この温度に保ちながら更に 2時 間反応を行つて終了した。 グラフト率は 55 %であつた。 内温を 100 °Cまで 冷却した後、 ォクタデシル _ 3 - (3， 5—ジ一 t—プチルー 4—ヒドロキシ フエノール） 一プロピオネート 0. 2部を添加した後、 内容物をォートクレー ブより抜き出し、 水蒸気蒸留により未反応物と溶媒を留去し、 40mm y5ベン ト付き押出機でシリンダー温度を 220°C、 真空度を 70 OmmH gとして、 揮発分を実質的に脱揮させ、 ペレッ ト化した。 ゴム強化ビニル系樹脂 （A 1 -3) のグラフト率は 55 %、 ァセトン可溶分の極限粘度 〔 〕 は、 0. 5 d 1 /gであった。 製造例 4 〔共重合体 (A2) の製造〕
スチレン 75部、 アクリロニトリル 25部を用いて、 塊状重合でビニル系重 合体 (A2-1) を得た。 極限粘度 〔7〕 は、 0. 45 d 1/gであった。 以下の諸例において、 着色剤としては下記のものを用いた。
(1) 無機顔料 〔B〕
B- 1 ； F e及ぴ C rの複合酸化物： 日本フヱ口一社製の商品 「フヱローカラー 42— 703 A」 （化学組成は、 C r 2〇 3 ； 88〜 91 %、 F e 203； 7〜 1 0%であり、 色は黒色である。 ）
B-2 ； F e—Mnの複合酸化物： 日本フヱ口一社製の商品 「フェローカラー 42 - 350 A」
B-3 ； Cu-C r-Mnの複合酸化物： 日本フヱロー社製の商品 「フェロー カラー 42— 303 B」
B-4 ； N i -C o-F e-C rの複合酸化物：川村化学工業社製の商品 「 A E 801ブラック」
(2) 無機顔料 〔C〕
C一 1 ； T i 02 ：石原産業社製の商品 「CR— 60— 2」
C-2 ； T i -C i -N i -Z n系複合酸化物：川村化学社製の商品 「MD 1
00」
C一 3 ；群青：東京新日本化成社製の商品 「NUB 1 FL0W」
C-4 ； T i -S b-N i系複合酸化物：川村化学社製の商品 「B R 1 0 0」
(3) 有機顔料 〔D〕 等
D- 1 ； ペリレン系有機顔料： B AS F社製の商品 「P a l i o g e n R e d 391 1 HD」
D— 2 ； イソインドリン系有機顔料：大日精化社製の商品 「D I SCOAL L 443」
D-3 ； シァニン系有機顔科：住友化学社製の商品 「S um i t 0 n e C y a n i n e B l u e GH」
D— 4 ； カーボンブラック
尚、 上記無機顔料 〔B〕 又は 〔C〕 を含む成形品の L値を調べるため、 ブロッ クタイブポリプロピレン （商品名 「BC 6 C」 、 日本ポリケム社製） 1 0 0部 と、 上記無機顔料 〔B〕 又は 〔C〕 0. 5部と、 からなる組成物を調製し、 そ の成形品を作製し、 上記の方法で L値を得た。 その結果を表 1に示す。
Figure imgf000025_0001
実施例 1〜 9及び比較例 1〜 5
各成分を、 表 1及び表 2に示す配合割合でミキサーにより 3分間混合した後、 50mm ^5押出機でシリンダー設定温度 1 80〜 200 °Cで溶融混練り押出し、 ペレツトを得た。 得られたペレツトを十分に乾燥し、 評価用の試験片を得た。 この試験片を用いて下記評価を上記記載の方法で行つた。 評価結果を表 2及び 表 3に示す。
表 2
実施例
1 2 3 4 5 6 7
A 1 - 1 50 50 50 - - 50 50 可塑性 A 1 - 2 一 一 一
熱 40 - 一 - 榭脂 A 1 - 3 一 - 一 一 100 一 一
A2 - 1 50 50 50 60 50 50
B- 1 2 5 2.8 2 2 - - 無機 顔 料 B-2 - - 0.2 - - 2 -
〔B〕 B-3 - - 一 - - - 2
B-4
D - 1
有機 顔 料 D- 2 一 - 一 一 - - - CD] D-3 一 ― 一 ― ― ― ―
D-4 - ― - 一 ― ― - 無機顔料由来の ― ― ― 一 ― ― 一 Co/Ni比
罕 成形品の色 甲罕 Eg 黑;^ 黑ポ 黑糸 黑术 黑糸 成形加工性
17 18 17 18 18 17 18 (g/10分）
評 蓄熱性 58 51 53 55 53 53 54 耐衝撃性 (kJ/m2) 24 22 22 23 25 22 23
L値 25 10 15 23 28 30 32 価
反射率 （％) 17 28 22 16 18 20 20 耐候性 A A A A A A A 着色鮮映性 A A A A A A A 表 3
実施例 比較例
8 9 1 2 3 4 5
A 1 - 1 50 50 50 50 一 一 - 熱可塑性 A 1 - 2 - . - 一 一 40 40 - 樹脂 A 1 - 3 - - 一 - - - 100
A2 - 1 50 50 50 50 60 60 ―
B— 1 無機顔料 B- 2
〔B〕 B- 3 - 一 - - 一
B- 4 3 5
D- 1 0.1ο 有機顔料 D-2 - 一 - 0.2 - 0.2 一
CD) D- 3 ― ― ― 0.25 ― 0.25 ―
D— 4 ― 一 0.3 一 0.3 一 0.3 無機顔料由来の
50/50 50/50 一 一 ― - 一 Co/Ni比
成形品の色 黑 黒^ 黑^ 黑糸 黑糸 黑^ 成形加工性
18 18 16 18 16 18 16 (g/10分）
評 蓄熱性 53 50 80 57 80 57 81 耐衝撃性 (kJ/m2) 22 21 21 22 20 20 20
L値 16 13 16 23 14 26 18 価
反射率 (%) 25 32 2 26 3 27 1 耐候性 A A A C A B A 着色鮮映性 A A A B A C A 表 3 より、 比較例 1、 3及び 5は、 着色剤としてカーボンブラックを用いた 例であり、 耐候性及び着色鮮映性に優れるが、 温度上昇 （蓄熱性一 2 5 °C) が それぞれ 5 5 °C、 5 5 °C及び 5 6 °Cと高く、 いずれも蓄熱性に劣っている。 ま た、 比較例 2及び 4は、 有機顔料を用いて着色した例であり、 蓄熱性は十分で あるが、 耐候性及び着色鮮映性に劣っている。
一方、 表 1の実施例 1乃至 9は、 いずれも成形加工性、 蓄熱性、 耐衝撃性、 耐侯性及び着色鮮映性のバランスに優れる。
尚、 本発明は、 上記実施例に限定されるものではなく、 目的、 用途に応じて 種々の態様をとることができる。 本発明の樹脂組成物は、 所定の熱可塑性樹脂
〔A〕 及び無機顔料 〔B〕 を含有するものであるから、 上記実施例のように、 熱可塑性樹脂及び無機顔料を別々に準備するのではなく、 グラフトしているビ 二ル系単量体成分の重合体及ぴ無機顔料がゴム質重合体を被覆しているような 状態の複合化熱可塑性樹脂を原料としてもよいし、 ビニル系単量体成分の （共） 重合体を無機顔料の存在下で合成し、 無機顔料を被覆した （共） 重合体を用い てもよい。
実施例 1 0〜 1 7、 比較例 6〜 7及び参考例 1〜 5
各成分を、 表 4〜 7に示す配合割合でミキサーにより 3分間混合した後、 5 0 mm ?5押出機でシリンダー設定温度 1 8 0〜 2 0 0。(：で溶融混練り押出し、 ペレツ トを得た。 得られたペレツトを十分に乾燥し、 評価用の試験片を得た。 この試験片を用いて各種評価を上記記載の方法で行つた。 評価結果を表 4〜 7 に示す。
表 4
実施例 1 0 1 1 12 13
A 1 - 1 50 一 一 一
A 1 -2 一 40 一 40 熱可塑性樹脂
A 1 -3 一 _ 100 一
1
A 2 - 1 50 60 _ 60
B— 1 _ 一 _
B - 2 _
無機顔料 〔B〕
B-3
B-4 4.0 4.0 4.0 4.0
C一 1 0.2 0.2 0.2
C-2 0.4 0.4 0.4 0.4 無機顔料 〔C〕
C一 3 0.3 0.3 0.3 無機顔料由来の Co/Ni比 70/30 70/30 70/30 70/30 成形品の色 黒色系 黒色系 黒色系 黒色系 成形加工性 （g/10分） 17 20 18 19
<皿度 しノ 53 52 50 55 蓄熱性
評 安定性 A A A A 耐衝撃性 （kJ/m2) 24 22 23 24 価 "直 23 22 21 20 反射率 （％) 37 38 38 36 耐候性 A A A A 着色鮮映性 A A A A 表 5
実施例 14 1 5 1 6 17
A 1 - 1 一 ― 一 一
A 1 - 2 40 40 40 40 熱可塑性樹脂
A 1 - 3 一 一 ― 一
A2 - 1 60 60 60 60
B- 1 2.0 一 一 一
B- 2 1.0 一 ―
無機顔料 〔B〕
B-3 一 3.0 一 一
B- 4 一 一 1.0 7.0
C一 1 0.5 0.1 0.2 0.2
C-2 0.4 1.5 0.2 0.2 無機顔料 〔C〕
C- 3 1.0 一 0.2
C-4 0.2 一 0.2 一 無機顔料由来の Co/Ni比 90/5 100/0 80/20 70/30 成形品の色 黒色系 黒色系 黒色系 黒色系 成形加工性 （g/10分） 18 19 20 17 温度 (°c) 54 55 54 50 蓄熱性
B f 安定性 A A A A 耐衝撃性 （kJ/m2) 21 23 22 20 価 "直 30 26 33 15 反射率 (%) 30 31 27 41 耐候性 A A A A 着色鮮映性 A A A A 表 6
参考例 1 参考例 2 比較例 6 比較例 7
A 1 - 1 一 - 一 -
A 1— 2 40 40 一 40 熱可塑性樹脂
A 1 -3 - - 100 -
A 2 - 1 60 60 一 60
B- 1 - - - 一
B - 2 - 一 一 - 無機顔料 〔B〕
B - 3 一 一 - -
B-4 3.0 3.0 - 0.08
C一 1 - - - 0.3
C- 2 - - - 0.1 無機顔料 〔C〕
C一 3 一 - - 0.4
C一 4 一 - - -
D— 1 - 0.3 0.15 -
D- 2 - - 0.2 - 有機含量 CD]
D— 3 - - 0.25 -
D-4 0.5 0.5 - - 無機顔料由来の Co/Ni比 70/30 70/30 一 50/50 成形品の色 黒色系 黒色系 黒色系 黒色系 成形加工性 （g/10分） 17 20 19 22
}jm.i¾. (。し) 80 79 58 70 蓄熱性
評 安定性 A A A B 耐衝撃性 （kJ/mz) 21 19 22 23 価 "直 15 13 24 50 反射率 (%) 3 2 35 17 耐候性 A B C A 着色鮮映性 A C C A 7
参考例 3 参考例 4 参考例 5
A 1 - 1 - 一 -
A 1 -2 40 40 40 熱可塑性樹脂
A 1 -3 - - -
A 2 - 1 60 60 60
B- 1 一 - 2.1
B— 2 - - 1.0 無機顔料 〔B〕
B- 3 - - 一
B-4 3.0 2.0 -
C一 1 11 一 -
C- 2 0.2 一 - 無機顔料 〔c〕
C一 3 0.2 一 一
C-4 - - 一
D— 1 - - 一
D- 2 - - - 有機含量 CD]
D-3 - - -
D-4 - - 0.3 無機顔料由来の Co/Ni比 70/30 70/30 - 成形品の色 黒色系 黒色系 黒色系 成形加工性 （g/10分） 25 26 16 温度 ro 51 50 80 蓄熱性
\" 安定性 B C B 耐衝撃 1 (kJ/m ) 12 22 19 価 "直 53 30 18 反射率 （％) 36 35 1 耐候性 A A A 着色鮮映性 A A A 表 6より、 比較例 6は、 無機顔料 〔B〕 及び 〔C〕 を含有せず有機顔料のみ で着色した例であり、 温度上昇は 3 3 °C ( 5 8 - 2 5 = 3 3 ) と優れるが、 耐 候性及び着色鮮映性に劣っていた。 参考例 1、 2及び 5は、 無機顔料 〔B〕 を 含有するが、 無機顔料 〔C〕 を含有しない例であり、 温度上昇がそれぞれ、 5 5 °C、 5 4 °C、 5 5 °Cと高くなつた。 参考例 2は有機顔料を含有し耐候性が十 分ではなく、 着色鮮映性に劣る。 参考例 5は、 低蓄熱性の安定性が十分ではな かった。 無機顔料 〔B〕 を含有するが、 無機顔料 〔C〕 を含有しない参考例 4 は、 温度上昇が低く、 反射率も高いが、 低蓄熱性の安定性に劣る。 比較例 7は、 無機顔料 〔B〕 の含有量が 0 . 0 8部と少ない例であり、 L値が 5 0と高く、 低蓄熱性の安定性が十分ではなかった。 参考例 3は、 無機顔料 〔C〕 の含有量 の合計が 1 1 . 4部と多い例であり、 L値が 5 3と高く、 また、 耐衝撃性に劣 る o
—方、 表 4〜 5より、 実施例 1 0〜 1 7は温度上昇が 2 5〜 3 0 °Cと良好で あり、 低蓄熱性の安定性が十分であり、 L値が 1 5〜 3 3と小さく、 耐候性、 着色鮮映性に優れる。
尚、 本発明は、 上記実施例に限定されるものではなく、 目的、 用途に応じて 種々の態様をとることができる。 本発明の樹脂組成物は、 所定の熱可塑性樹脂 〔A〕 、 無機顔料 〔B〕 、 及び 〔C〕 を含有するものであるから、 上記実施例 のように、 熱可塑性樹脂及び無機顔料を別々に準備するのではなく、 グラフト しているビニル系単量体成分の重合体及び無機顔料がゴム質重合体を被覆して いるような状態の複合化熱可塑性樹脂を原料としてもよいし、 ビニル系単量体 成分の （共） 重合体を無機顔料の存在下で合成し、 無機顔料を被覆した （共） 重合体を用いてもよい。
また、 本発明には含まれないが、 上記無機顔料 〔C〕 の代わりに、 上記無機 顔料 〔B〕 と併用する無機顔料 （以下、 「無機顔料 〔D〕 」 ともいう。 ） とし て、 赤外線反射特性を有さず、 ブロックタイプポリプロピレン 1 0 0質量部及 ぴこの無機顔料 〔D〕 0 . 5質量部からなる組成物より得られる成形品の L値 が、 例えば、 4 0未満、 好ましくは 3 5以下である条件を満たすものを用いて も、 成形加工性に優れ、 且つ、 蓄熱が少なく、 耐候性及び耐衝撃性に優れる暗 色系の成形品を与える低蓄熱性熱可塑性樹脂組成物を得ることができる。 この 場合の、 熱可塑性樹脂 〔A〕 、 無機顔料 〔B〕 及び無機顔料 〔D〕 の含有割合 は、 上記で説明した熱可塑性樹脂 〔A〕 、 無機顔料 〔B〕 及び無機顔料 〔C〕 の含有割合と同様とすることができる。 産業上の利用可能性
本発明の低蓄熱性熱可塑性樹脂組成物は、 これを用いて成形する際の加工性 に優れ、 得られる成形品は、 所望の色を正確に実現し、 熱の吸収が安定して少 なく、 変形、 収縮が発生しにくい。 更には、 耐候性及び耐衝撃性にも優れる。 特に、 無機顔料 〔B〕 が F e、 C r、 M n、 C u、 C o及ぴ N iから選ばれる 少なくとも 1種の元素の化合物である場合には、 無機顔料 〔C〕 と併用した際 の暗色系着色のバランスをとりやすく、 成形品の低蓄熱性に優れる。 なかでも、 C 0元素及び N i元素を含む酸化物であり、 本組成物中の C 0元素及び N i元 素の含有量の比 C o ZN iが 5 Z 9 5〜 9 5 5である場合には、 低蓄熱性に 優れ且つ L値が 4 0以下である暗色系の鮮映な成形品を得ることができる。
また、 本組成物からなる成形品に、 波長 1 0 0 0〜 1 2 5 0 n mの光を照射 した際の、 この波長範囲における光の反身ォ率の最大値が 1 5 %以上である場合 には、 優れた低蓄熱性熱可塑性樹脂組成物とすることができる。
上記熱可塑性樹脂 〔A〕 として、 ゴム質重合体 ( a ) の存在下に、 ビニル系 単量体成分 （b ) を重合して得られるゴム強化ビニル系樹脂 （A 1 ) 、 又は、 このゴム強化ビニル系樹脂 （A 1 ) とビニル系単量体成分の （共） 重合体 (A 2 ) との混合物を用いる場合には、 特に成形加工性に優れ、 且つ、 蓄熱が少な く、 耐候性及び耐衝撃性に優れる成形品を得ることができる。 また、 上記ビニ ル系単量体成分に芳香族ビニル化合物を含む場合には、 成形加工性、 表面外観 1生に優れる。 また、 本発明の成形品は、 熱の吸収が少なく、 高温時の変形、 収縮が発生し にくレ。 更には、 耐候性及び耐衝撃性にも優れる。
本発明の低蓄熱性熱可塑性樹脂組成物および成形品は、 上述の通り、 工業的 に高い価値を有するものである。

Claims

請 求 の 範 囲
1. 熱可塑性樹脂 〔A〕 100質量部と、 赤外線反射特性を有する無機顔料 〔B〕 0. 1〜 1 5質量部とを含有する低蓄熱性熱可塑性樹脂組成物。
2. 熱可塑性樹脂 〔A〕 が、 ゴム質重合体 (a) の存在下に、 ビニル系単量体 成分 （b) を重合して得られるゴム強化ビニル系樹脂 （A 1) 、 又は、 該ゴム 強化ビニル系樹脂 （A 1) とビニル系単量体成分の （共） 重合体 (A2) との 混合物からなる請求項 1に記載の低蓄熱性熱可塑性樹脂組成物。
3. 熱可塑性樹脂 〔A〕 中のゴム質重合体 （a) の含有量が 3〜40重量0 /0で ある請求項 1又は 2に記載の低蓄熱性熱可塑性樹脂組成物。
4. 温度 25 ± 2 °C、 湿度 50 ± 5 % R Hに調節された室に前記組成物からな る成形品 （長さ 80mm、 幅 55 mm, 厚さ 2. 5mm) を載置し、 高さ 20 0mmから、 その表面に赤外線ランプ （出力 100W) を 60分間照射し、 成 形品の表面温度を測定し、 赤外線ランプ照射前の初期温度との差を上昇温度と した場合、 当該上昇温度が 50 °C以下である請求項 1〜 3の何れかに記載の低 蓄熱性熱可塑性樹脂組成物。
5. ビニル系単量体成分 （b) が芳香族ビニル化合物を含有する請求項 1〜4 の何れかに記載の低蓄熱性熱可塑性樹脂組成物。
6. 無機顔料 〔B〕 が、 F e、 C r、 Mn、 Cu、 Co及ぴ N iから選択され る少なくとも 1種の元素を含有する化合物である請求項 1〜 5の何れかに記載 の低蓄熱性熱可塑性樹脂組成物。
7. 無機顔料 〔B〕 は、 F e、 C r及び Mnから選択される少なくとも 2種の 元素を含有する酸化物である請求項 6に記載の低蓄熱性熱可塑性樹脂組成物。
8. 無機顔料 〔B〕 は、 C 0元素及び N i元素を含有する酸ィヒ物であり、 本組 成物中の C 0元素及び N i元素の含有量の比 C o/N iが 5/95〜95/5 である請求項 6又は 7に記載の低蓄熱性熱可塑性樹脂組成物。
9. さらに、 熱可塑性樹脂 〔A〕 100質量部に対し無機顔料 〔C〕 0. 01 〜 1 0質量部を含有する請求項 1〜 8の何れかに記載の低蓄熱性熱可塑性樹脂 組成物。
1 0 . 無機顔料 〔 B〕 、 ブロックタイプポリプロピレン 1 0 0質量部およぴ 無機顔料 〔B〕 0 . 5質量部から成る成形品の L値が 4 0未満である条件を満 たし無機顔料 〔 C〕 が、 プロックタイプポリプロピレン 1 0 0質量部およぴ無 機顔料 〔C〕 0 . 5質量部から成る成形品の L値が 4 0以上である条件を満た す請求項 9に記載の低蓄熱性熱可塑性樹脂組成物。
1 1 . 無機顔料 〔c〕 力 白色系無機顔料、 赤色系無機顔料、 緑色系無 料、 黄色系無機顔料、 茶色系無機顔料、 青色系無機顔料、 紫色系無機顔料、 銀色系 無機顔料およびパール色系無機顔料から選択される少なくとも 1種である請求 項 9又は 1 0に記載の低蓄熱性熱可塑性樹脂組成物。
1 2 . 無機顔料 〔C〕 として、 緑色系無機顔料を使用する請求項 1 1に記載の 低蓄熱性熱可塑性樹脂組成物。
1 3 . 無機顔料 〔C〕 として、 更に、 白色系無機顔料および青色系無機顔料を 使用する請求項 1 2に記載の低蓄熱性熱可塑性樹脂組成物。
1 4 . 前記組成物から成る成形品の色調を L a b方式で表示したときに、 L値 が 4 0以下である請求項 1〜 1 3の何れかに記載の低蓄熱性熱可塑性樹脂組成 物。
1 5 . 前記組成物から成る成形品に、 波長 1 0 0 0〜 1 2 5 0 n mの光を照射 した際の、 当該波長範囲における当該光の反射率の最大値が 1 5 %以上である 請求項 1〜 1 4の何れかに記載の低蓄熱性熱可塑性樹脂組成物。
1 6 . 請求項 1〜 1 5の何れかに記載の低蓄熱性熱可塑性樹脂組成物から成る 成形ロロ。
PCT/JP2003/009997 2002-08-07 2003-08-06 低蓄熱性熱可塑性樹脂組成物および成形品 Ceased WO2004015014A1 (ja)