WO2006032189A1 - Carte en fibre de verre double face et procédé de fabrication idoine - Google Patents

Carte en fibre de verre double face et procédé de fabrication idoine Download PDF

Info

Publication number
WO2006032189A1
WO2006032189A1 PCT/CN2005/001476 CN2005001476W WO2006032189A1 WO 2006032189 A1 WO2006032189 A1 WO 2006032189A1 CN 2005001476 W CN2005001476 W CN 2005001476W WO 2006032189 A1 WO2006032189 A1 WO 2006032189A1
Authority
WO
WIPO (PCT)
Prior art keywords
mold
glass fiber
double
mixture
drier
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2005/001476
Other languages
English (en)
Chinese (zh)
Inventor
Waihon Lo
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN200580000356.4A priority Critical patent/CN1819928B/zh
Publication of WO2006032189A1 publication Critical patent/WO2006032189A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L’invention concerne une carte en fibre de verre double face et le procédé de fabrication idoine. La carte est principalement utilisée comme plaque frontale, et composée de résine, d’un séchant, d’un accélérant, de fibre de verre et d’une matière de remplissage, etc. La matière de remplissage peut être une carte routière en chinois/anglais et un dessin, des fleurs et de l’herbe, des fournitures quotidiennes, un matériau de construction, des vêtements, des bijoux, des articles sur papier, un journal, un magazine, des livres, des photos, une horloge, de la poudre lumineuse, du gravier lumineux, une bande laser ou leur mélange. Le procédé comprend les phases d’utilisation d’un moule, de versement des matériaux dans le moule après mélange de ceux-ci au rythme voulu, avant injection de la matière de remplissage, puis chauffage et refroidissement, etc.
PCT/CN2005/001476 2004-09-21 2005-09-15 Carte en fibre de verre double face et procédé de fabrication idoine Ceased WO2006032189A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN200580000356.4A CN1819928B (zh) 2004-09-21 2005-09-15 双面玻璃纤维板制作方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN 200410082630 CN1751881A (zh) 2004-09-21 2004-09-21 双面各款云石玻璃纤维板的制造方法
CN200410082630.4 2004-09-21

Publications (1)

Publication Number Publication Date
WO2006032189A1 true WO2006032189A1 (fr) 2006-03-30

Family

ID=34352379

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2005/001476 Ceased WO2006032189A1 (fr) 2004-09-21 2005-09-15 Carte en fibre de verre double face et procédé de fabrication idoine

Country Status (3)

Country Link
CN (2) CN1751881A (fr)
HK (1) HK1066691A2 (fr)
WO (1) WO2006032189A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103982022A (zh) * 2014-06-04 2014-08-13 广西启利新材料科技股份有限公司 一种玻纤毡与玻纤网叠合的砂浆底胎

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TW201124578A (en) * 2010-01-12 2011-07-16 Hsu Tai Glass Fiber Co Ltd Manufacturing method of glass fiber cotton and product thereof.
CN102733583A (zh) * 2012-05-03 2012-10-17 新乡市鼎鑫机械有限公司 一种生产pvc地板的新方法
CN103407267B (zh) * 2013-04-16 2016-01-06 浙江未来家木业有限公司 一种玻璃纤维地板的加工方法
CN104890258A (zh) * 2015-05-29 2015-09-09 南通澳兰德复合材料有限公司 一种耐腐阻燃单孔板型材的制作工艺
CN113183375B (zh) * 2020-01-14 2023-09-01 杭州亚态农科技有限公司 一种内含三维内饰物的水晶生态板材的制作方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4374170A (en) * 1981-11-09 1983-02-15 Ford Motor Company Room temperature cure polyester laminates
CN1476992A (zh) * 2003-07-11 2004-02-25 宏 刘 仿镂空雕装饰品的制作方法

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN2136128Y (zh) * 1992-09-18 1993-06-16 曾小琪 镭射装饰塑料板
CN2159892Y (zh) * 1993-03-09 1994-03-30 王柏林 聚酯彩色主体花纹装饰板
US5639411A (en) * 1994-12-21 1997-06-17 Holli-Nee Corporation Process for expanding glass fiber laminates and panels formed thereby
CN2267152Y (zh) * 1996-11-04 1997-11-12 尹明君 塑钢装饰板、画
CN2461330Y (zh) * 2001-02-13 2001-11-28 陈木财 通风鞋垫
CN2581209Y (zh) * 2002-05-23 2003-10-22 金坚 一种带浮雕效果的艺术制品
CN1509904A (zh) * 2002-12-23 2004-07-07 廉长江 用树脂材料仿木刻字艺术壁挂

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4374170A (en) * 1981-11-09 1983-02-15 Ford Motor Company Room temperature cure polyester laminates
CN1476992A (zh) * 2003-07-11 2004-02-25 宏 刘 仿镂空雕装饰品的制作方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103982022A (zh) * 2014-06-04 2014-08-13 广西启利新材料科技股份有限公司 一种玻纤毡与玻纤网叠合的砂浆底胎

Also Published As

Publication number Publication date
CN1819928A (zh) 2006-08-16
CN1751881A (zh) 2006-03-29
HK1094507A1 (zh) 2007-03-30
CN1819928B (zh) 2010-05-12
HK1066691A2 (en) 2005-03-04

Similar Documents

Publication Publication Date Title
US6588163B2 (en) Relief engraved doorplate
WO2006032189A1 (fr) Carte en fibre de verre double face et procédé de fabrication idoine
CN2173696Y (zh) 复合仿石板
US20050100717A1 (en) Decorative structures, decorative panels and method of making same
KR100898206B1 (ko) 인테리어용패널 및 그 제작방법
HK1094507B (en) Double-sided fiber glass board and its production know-how
CN109336467A (zh) 一种可塑透光石的制造方法及可塑透光石
JP2009502707A (ja) 複合材パネルの製造方法
CN102039618A (zh) 一种复合装饰板的制造方法
KR100857583B1 (ko) 대리석의 표면에 크랙 문양이 형성되는 가구용 상판 제조방법
KR100385771B1 (ko) 인조석 판재의 제조방법
CN201132818Y (zh) 一种玻璃马赛克
CN215423348U (zh) 一种新型艺术画树脂桌
CN201099025Y (zh) 高分子晶玉装饰板
CN205800633U (zh) 剪纸装饰幕墙
CN214727100U (zh) 装饰面板及空调器
CN2116597U (zh) 闪光板
JP7787506B1 (ja) セラミック天板材
CN201080020Y (zh) 彩纹强化玻璃
TWI231276B (en) Method for manufacturing transparent artistic panel
CN2246590Y (zh) 一种浮起的三维工艺品
KR101991478B1 (ko) 자개를 이용한 다용도 적층 시트 제조 방법 및 이에 의해 제조된 다용도 적층 시트
CN201377154Y (zh) 带孔的金属表层复合装饰板
KR100833817B1 (ko) 트로피 받침대에 부착사용되는 문자판 결합구 및 그제조방법
CN2386107Y (zh) 带感光层的建筑装潢板材

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 20058003564

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KP KR KZ LC LK LR LS LT LU LV LY MA MD MG MK MN MW MX MZ NA NG NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU LV MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase