WO2006111445A1 - Resistance ceramique et procede de fabrication - Google Patents

Resistance ceramique et procede de fabrication Download PDF

Info

Publication number
WO2006111445A1
WO2006111445A1 PCT/EP2006/060896 EP2006060896W WO2006111445A1 WO 2006111445 A1 WO2006111445 A1 WO 2006111445A1 EP 2006060896 W EP2006060896 W EP 2006060896W WO 2006111445 A1 WO2006111445 A1 WO 2006111445A1
Authority
WO
WIPO (PCT)
Prior art keywords
ceramic
green body
resistor
carbon fibers
carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2006/060896
Other languages
German (de)
English (en)
Inventor
Alexander Klonczynski
Martin Koehne
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Robert Bosch GmbH
Original Assignee
Robert Bosch GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Robert Bosch GmbH filed Critical Robert Bosch GmbH
Priority to JP2008507035A priority Critical patent/JP2008538541A/ja
Publication of WO2006111445A1 publication Critical patent/WO2006111445A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une résistance céramique pouvant être fabriquée par pyrolyse ou frittage d'un corps de base céramique. Pour de meilleures propriétés mécaniques et/ou électriques, la résistance céramique contient des fibres de carbone.
PCT/EP2006/060896 2005-04-20 2006-03-21 Resistance ceramique et procede de fabrication Ceased WO2006111445A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2008507035A JP2008538541A (ja) 2005-04-20 2006-03-21 セラミック抵抗体およびその製造法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102005018268.2 2005-04-20
DE102005018268A DE102005018268A1 (de) 2005-04-20 2005-04-20 Keramischer Widerstand und Verfahren zu dessen Herstellung

Publications (1)

Publication Number Publication Date
WO2006111445A1 true WO2006111445A1 (fr) 2006-10-26

Family

ID=36581627

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2006/060896 Ceased WO2006111445A1 (fr) 2005-04-20 2006-03-21 Resistance ceramique et procede de fabrication

Country Status (3)

Country Link
JP (1) JP2008538541A (fr)
DE (1) DE102005018268A1 (fr)
WO (1) WO2006111445A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN117923925A (zh) * 2024-01-19 2024-04-26 中国科学院兰州化学物理研究所 一种添加碳纤维的氮化硅导电陶瓷及其制备方法

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102011109578B4 (de) 2011-08-05 2015-05-28 Heraeus Noblelight Gmbh Verfahren zur Herstellung eines elektrisch leitenden Materials, elektrisch leitendes Material sowie Strahler mit elektrisch leitendem Material

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1264476A (fr) * 1968-07-12 1972-02-23
GB1305910A (fr) * 1969-07-28 1973-02-07
US4540674A (en) * 1983-02-08 1985-09-10 Kyushu Refractories Co., Ltd. Silicon nitride composite refractories
EP0372381A2 (fr) * 1988-12-03 1990-06-13 Hoechst Aktiengesellschaft Procédé pour la production de céramique contenant des fibres
EP0536866A1 (fr) * 1991-10-11 1993-04-14 Noritake Co., Limited Matériau nanocomposite renforcé par fibre de carbone à base de nitrure de silicium et procédé de sa production
EP0623571A1 (fr) * 1992-11-26 1994-11-09 Tonen Corporation Procede pour fabriquer des produits en ceramique
EP1248045A2 (fr) * 2001-04-02 2002-10-09 NGK Spark Plug Company Limited Elément de chauffe en céramique et son procédé de fabrication, bougie de préchauffage et détecteur de courant ionique
EP1496033A2 (fr) * 2003-07-07 2005-01-12 Ngk Insulators, Ltd. Corps fritté en nitrure d'aluminium et son procédé de fabrication
DE10333961A1 (de) * 2003-07-25 2005-02-10 Robert Bosch Gmbh Verfahren zur Herstellung einer Precursor-Keramik

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1264476A (fr) * 1968-07-12 1972-02-23
GB1305910A (fr) * 1969-07-28 1973-02-07
US4540674A (en) * 1983-02-08 1985-09-10 Kyushu Refractories Co., Ltd. Silicon nitride composite refractories
EP0372381A2 (fr) * 1988-12-03 1990-06-13 Hoechst Aktiengesellschaft Procédé pour la production de céramique contenant des fibres
EP0536866A1 (fr) * 1991-10-11 1993-04-14 Noritake Co., Limited Matériau nanocomposite renforcé par fibre de carbone à base de nitrure de silicium et procédé de sa production
EP0623571A1 (fr) * 1992-11-26 1994-11-09 Tonen Corporation Procede pour fabriquer des produits en ceramique
EP1248045A2 (fr) * 2001-04-02 2002-10-09 NGK Spark Plug Company Limited Elément de chauffe en céramique et son procédé de fabrication, bougie de préchauffage et détecteur de courant ionique
EP1496033A2 (fr) * 2003-07-07 2005-01-12 Ngk Insulators, Ltd. Corps fritté en nitrure d'aluminium et son procédé de fabrication
DE10333961A1 (de) * 2003-07-25 2005-02-10 Robert Bosch Gmbh Verfahren zur Herstellung einer Precursor-Keramik

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN117923925A (zh) * 2024-01-19 2024-04-26 中国科学院兰州化学物理研究所 一种添加碳纤维的氮化硅导电陶瓷及其制备方法

Also Published As

Publication number Publication date
JP2008538541A (ja) 2008-10-30
DE102005018268A1 (de) 2006-10-26

Similar Documents

Publication Publication Date Title
DE19711829C1 (de) Verfahren zur Herstellung einer faserverstärkten Verbundkeramik
DE60130688T2 (de) Verfahren zur herstellung von mit sic-fasern verstärktem sic-verbundwerkstoff mit hilfe einer heisspresse
DE102013114628B4 (de) Verfahren zum Herstellen von endkonturnah geformten Siliciumcarbid-Keramiken
DE19736560C2 (de) Verfahren zur Herstellung eines porösen Körpers, Körper aus SiC, sowie Verwendung des porösen Körpers
DE69524432T2 (de) Faserverbundkörper auf keramikbasis
DE19860919C1 (de) Keramisches Heizelement und Verfahren zu dessen Herstellung
DE10055082A1 (de) Keramischer Verbundwerkstoff
US7364794B2 (en) Oxidation resistant carbon fiber reinforced carbon composite material and process for producing the same
DE3926077A1 (de) Keramische verbundkoerper und verfahren zu ihrer herstellung
EP1400499A1 (fr) Produit composite en céramique renforcée par des fibres et procédé de préparation
DE69015882T2 (de) Siliciumnitrid-Siliciumkarbidverbundmaterial und Verfahren zu seiner Herstellung.
DE69029227T2 (de) Gleitbauteil
EP1899280B1 (fr) CORPS MOULE CERAMIQUE CONTENANT DU ß-SIC POREUX ET PRESENTANT UN REVETEMENT EN OXYDE D'ALUMINIUM ET PROCEDE POUR LE PRODUIRE
WO2006111445A1 (fr) Resistance ceramique et procede de fabrication
DE19654182A1 (de) Reaktionsgesinterte Keramik und Verfahren zu deren Herstellung
EP2053029B1 (fr) Procédé destiné à la fabrication d'un composant en céramique de carbure
DE3243570A1 (de) Verfahren zum herstellen eines dichten polykristallinen formkoerpers aus sic
EP1657227B1 (fr) Procédé de fabrication d'un materiau céramique en carbure, présentant un gradient défini de distribution de phase, materiau en carbure céramique et élément de construction.
DE69508861T2 (de) Herstellung von Zirkoncarbidkeramik hoher Dichte mit vorkeramischen Polymerbindern
DE10333961A1 (de) Verfahren zur Herstellung einer Precursor-Keramik
EP3676233B1 (fr) Procédé de production d'un matériau composite, le matériau composite produit et son utilisation
WO2006018347A1 (fr) Resistance electrique ceramique
DE19619616A1 (de) Verfahren zum Einstellen der Porosität von keramischen Verbundwerkstoffen aus siliciumorganischen Polymeren
JPH066511B2 (ja) 黒鉛／カーボン繊維複合材料の製造方法
WO2003064346A1 (fr) Materiau composite ceramique, procede de production de ce materiau et bougie crayon de prechauffage comprenant ce materiau

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2008507035

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: RU

WWW Wipo information: withdrawn in national office

Country of ref document: RU

122 Ep: pct application non-entry in european phase

Ref document number: 06725184

Country of ref document: EP

Kind code of ref document: A1

WWW Wipo information: withdrawn in national office

Ref document number: 6725184

Country of ref document: EP