WO2009128302A1 - Matériau pour plaque d'impression lithographique, et procédé de production d'une plaque d'impression lithographique - Google Patents

Matériau pour plaque d'impression lithographique, et procédé de production d'une plaque d'impression lithographique Download PDF

Info

Publication number
WO2009128302A1
WO2009128302A1 PCT/JP2009/054289 JP2009054289W WO2009128302A1 WO 2009128302 A1 WO2009128302 A1 WO 2009128302A1 JP 2009054289 W JP2009054289 W JP 2009054289W WO 2009128302 A1 WO2009128302 A1 WO 2009128302A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid
bis
compound
group
acrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2009/054289
Other languages
English (en)
Japanese (ja)
Inventor
孝彰 黒木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Konica Minolta Medical and Graphic Inc
Original Assignee
Konica Minolta Medical and Graphic Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Konica Minolta Medical and Graphic Inc filed Critical Konica Minolta Medical and Graphic Inc
Publication of WO2009128302A1 publication Critical patent/WO2009128302A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention porte sur un matériau pour plaque d'impression lithographique, qui comprend : un support ; une couche photosensible comprenant (A) un composé ayant une liaison à insaturation éthylénique, (B) un amorceur de photopolymérisation, (C) un liant polymère et (D) un colorant sensibilisant, la couche photosensible contenant un composé (E) ayant une liaison à insaturation éthylénique, une liaison thiouréthanne (-SCONH-) et une structure d'amine tertiaire dans sa molécule, en tant que composé (A) ayant une liaison à insaturation éthylénique. Le matériau pour plaque d'impression lithographique présente une grande sensibilité et une excellente durabilité de l'impression.
PCT/JP2009/054289 2008-04-17 2009-03-06 Matériau pour plaque d'impression lithographique, et procédé de production d'une plaque d'impression lithographique Ceased WO2009128302A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2008107618 2008-04-17
JP2008-107618 2008-04-17

Publications (1)

Publication Number Publication Date
WO2009128302A1 true WO2009128302A1 (fr) 2009-10-22

Family

ID=41199002

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2009/054289 Ceased WO2009128302A1 (fr) 2008-04-17 2009-03-06 Matériau pour plaque d'impression lithographique, et procédé de production d'une plaque d'impression lithographique

Country Status (1)

Country Link
WO (1) WO2009128302A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019107323A1 (fr) * 2017-11-28 2019-06-06 三井化学株式会社 (méth)acrylate et son utilisation
WO2025169863A1 (fr) * 2024-02-05 2025-08-14 三井化学株式会社 Composé de (méth)acrylate de thiouréthane, composition monomère, composition durcissable et matériau dentaire

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005104842A (ja) * 2003-09-26 2005-04-21 Mitsui Chemicals Inc 新規なチオウレタン骨格を有する（メタ）アクリレート
JP2007163648A (ja) * 2005-12-12 2007-06-28 Konica Minolta Medical & Graphic Inc 感光性平版印刷版材料
WO2008023603A1 (fr) * 2006-08-23 2008-02-28 Showa Denko K.K. Composé de thiouréthane et composition de résine photosensible
EP1903393A2 (fr) * 2006-09-25 2008-03-26 FUJIFILM Corporation Composition durcissable, filtre couleur et son procédé de fabrication
WO2008146685A1 (fr) * 2007-05-23 2008-12-04 Showa Denko K.K. Composé uréthane réactif ayant une liaison éther, composition durcissable et produit durci

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005104842A (ja) * 2003-09-26 2005-04-21 Mitsui Chemicals Inc 新規なチオウレタン骨格を有する（メタ）アクリレート
JP2007163648A (ja) * 2005-12-12 2007-06-28 Konica Minolta Medical & Graphic Inc 感光性平版印刷版材料
WO2008023603A1 (fr) * 2006-08-23 2008-02-28 Showa Denko K.K. Composé de thiouréthane et composition de résine photosensible
EP1903393A2 (fr) * 2006-09-25 2008-03-26 FUJIFILM Corporation Composition durcissable, filtre couleur et son procédé de fabrication
WO2008146685A1 (fr) * 2007-05-23 2008-12-04 Showa Denko K.K. Composé uréthane réactif ayant une liaison éther, composition durcissable et produit durci

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019107323A1 (fr) * 2017-11-28 2019-06-06 三井化学株式会社 (méth)acrylate et son utilisation
CN111225933A (zh) * 2017-11-28 2020-06-02 三井化学株式会社 (甲基)丙烯酸酯及其用途
EP3719048A4 (fr) * 2017-11-28 2021-08-18 Mitsui Chemicals, Inc. (méth)acrylate et son utilisation
CN111225933B (zh) * 2017-11-28 2022-10-04 三井化学株式会社 (甲基)丙烯酸酯及其用途
US12441821B2 (en) * 2017-11-28 2025-10-14 Mitsui Chemicals, Inc. (Meth)acrylate and use thereof
WO2025169863A1 (fr) * 2024-02-05 2025-08-14 三井化学株式会社 Composé de (méth)acrylate de thiouréthane, composition monomère, composition durcissable et matériau dentaire

Similar Documents

Publication Publication Date Title
JP2007310057A (ja) 感光性組成物、感光性平版印刷版材料、及びそれらの製造方法
WO2009128302A1 (fr) Matériau pour plaque d'impression lithographique, et procédé de production d'une plaque d'impression lithographique
US5340685A (en) Light-sensitive composition containing diazo resin, polyurethane resin and fluorine atom-containing copolymer surfactant
JPWO2008010400A1 (ja) 感光性平版印刷版材料
JPWO2007129576A1 (ja) 感光性平版印刷版材料
JPWO2007072689A1 (ja) エチレン性不飽和結合含有化合物、感光性組成物、感光性平版印刷版材料、及びそれを用いた印刷方法
JP2006215241A (ja) 感光性平版印刷版材料及びそれを用いた製版方法
JP2009229499A (ja) 感光性平版印刷版材料および平版印刷版材料の製版方法
JP2005200683A (ja) 平版印刷版用アルミニウム支持体及びその製造方法、平版印刷版材料及び画像形成方法
JPWO2008084599A1 (ja) 感光性平版印刷版材料
JP2007233127A (ja) 感光性平版印刷版材料
JP2005221542A (ja) 感光性組成物、感光性平版印刷版及び平版印刷版の記録方法
JP2008090130A (ja) 感光性平版印刷版材料
JP2005331802A (ja) 感光性平版印刷版の製版方法
JP2007163840A (ja) 感光性組成物、感光性平版印刷版材料および平版印刷版材料の画像形成方法
JPWO2007102322A1 (ja) 感光性平版印刷版材料
JP4419682B2 (ja) 感光性平版印刷版の製版方法
JP2007065548A (ja) 感光性組成物、感光性平版印刷版材料および平版印刷版材料の画像形成方法
JP2006154074A (ja) 感光性平版印刷版材料
JP2009031632A (ja) 感光性組成物および感光性平版印刷版材料
JP2007298645A (ja) 感光性平版印刷版の処理方法
JP2007171754A (ja) 感光性平版印刷版材料及びそれを用いた製版方法
JP2008129132A (ja) 感光性平版印刷版材料
JP2006259109A (ja) 感光性平版印刷版材料の製版方法
JP2008175873A (ja) 感光性平版印刷版材料

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09733255

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

NENP Non-entry into the national phase

Ref country code: JP

122 Ep: pct application non-entry in european phase

Ref document number: 09733255

Country of ref document: EP

Kind code of ref document: A1