WO2011003052A1 - Sous-couche de toiture - Google Patents

Sous-couche de toiture Download PDF

Info

Publication number
WO2011003052A1
WO2011003052A1 PCT/US2010/040863 US2010040863W WO2011003052A1 WO 2011003052 A1 WO2011003052 A1 WO 2011003052A1 US 2010040863 W US2010040863 W US 2010040863W WO 2011003052 A1 WO2011003052 A1 WO 2011003052A1
Authority
WO
WIPO (PCT)
Prior art keywords
sheet material
composite sheet
substrate
film layer
roof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2010/040863
Other languages
English (en)
Inventor
Arthur H. Cashin
Brian Hickie
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fiberweb LLC
Original Assignee
Fiberweb LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fiberweb LLC filed Critical Fiberweb LLC
Priority to US13/379,561 priority Critical patent/US20120096791A1/en
Publication of WO2011003052A1 publication Critical patent/WO2011003052A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un matériau (10) en feuille composite qui s'avère particulièrement utile en tant que matériau de sous-couche dans des applications de toiture. En particulier, la présente invention concerne un matériau (10) en feuille composite caractérisé en ce qu'il est souple, relativement léger, résistant à l'eau tout en étant perméable à la vapeur d'eau et résistant aux déchirures. De plus, le matériau (10) en feuille composite comprend une surface extérieure antidérapante (18) capable de contribuer à empêcher que des ouvriers ne glissent pendant l'installation du système de toiture. Des modes de réalisation du matériau en feuille composite peuvent contribuer à conférer à une toiture / structure, par exemple un toit en bardeaux, une résistance au feu telle que le toit puisse répondre aux exigences de résistance au feu de la norme ASTM E 108-07a, Classe A.
PCT/US2010/040863 2009-07-02 2010-07-02 Sous-couche de toiture Ceased WO2011003052A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US13/379,561 US20120096791A1 (en) 2009-07-02 2010-07-02 Roofing Underlayment

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US22272209P 2009-07-02 2009-07-02
US61/222,722 2009-07-02

Publications (1)

Publication Number Publication Date
WO2011003052A1 true WO2011003052A1 (fr) 2011-01-06

Family

ID=42711763

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2010/040863 Ceased WO2011003052A1 (fr) 2009-07-02 2010-07-02 Sous-couche de toiture

Country Status (2)

Country Link
US (1) US20120096791A1 (fr)
WO (1) WO2011003052A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20210285219A1 (en) * 2020-03-12 2021-09-16 Milliken & Company Composite roofing membrane
US20220333383A1 (en) * 2021-04-20 2022-10-20 Milliken & Company Metal roofing system
EP4171949A1 (fr) * 2020-06-26 2023-05-03 Borealis AG Structure composite non tissée présentant une excellente perméabilité à la vapeur d'eau
US12146322B2 (en) 2020-04-23 2024-11-19 Milliken & Company Bitumen roofing composite

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9896846B2 (en) * 2014-12-17 2018-02-20 Southeastern Metals Manufacturing Company, Inc. Low slope roofing system
CA2945924C (fr) * 2015-10-19 2023-03-21 Keene Building Products Co., Inc. Dispositif de jauge de lit de mortier, systeme et methode
US11597185B2 (en) * 2018-05-10 2023-03-07 Avenex Coating Technologies, Inc. Fire resistant non-breathable roofing underlayment
MX2020012010A (es) 2018-05-11 2021-01-29 Owens Corning Intellectual Capital Llc Lamina transpirable reforzada.
US20200063445A1 (en) * 2018-08-21 2020-02-27 Benecke-Kaliko Ag Do it yourself deck membrane
EP3921150A4 (fr) * 2019-02-10 2022-10-19 Holcim Technology Ltd Membranes de toiture thermoplastiques pour systèmes de toiture entièrement collés
CA3084635C (fr) * 2019-06-24 2025-04-01 Owens Corning Intellectual Capital, Llc Doublure inférieure d’une toiture munie de noyau non tissé hydrophobe
US11821220B2 (en) * 2019-09-18 2023-11-21 Dupont Safety & Construction, Inc. Composite structural board and wall systems containing same
EP4133137A4 (fr) * 2020-05-22 2024-05-15 Daramic, LLC Matériaux de construction comprenant des membranes microporeuses
CN117321260A (zh) * 2021-04-06 2023-12-29 欧文斯科宁知识产权资产有限公司 具有调整性能的涂覆非织造垫

Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3338992A (en) 1959-12-15 1967-08-29 Du Pont Process for forming non-woven filamentary structures from fiber-forming synthetic organic polymers
US4116892A (en) 1975-03-31 1978-09-26 Biax-Fiberfilm Corporation Process for stretching incremental portions of an orientable thermoplastic substrate and product thereof
US4153664A (en) 1976-07-30 1979-05-08 Sabee Reinhardt N Process for pattern drawing of webs
US4153751A (en) 1975-03-31 1979-05-08 Biax-Fiberfilm Corporation Process for stretching an impregnated film of material and the microporous product produced thereby
US4285100A (en) 1975-03-31 1981-08-25 Biax Fiberfilm Corporation Apparatus for stretching a non-woven web or an orientable polymeric material
US5865926A (en) 1996-02-15 1999-02-02 Clopay Plastic Products Company, Inc. Method of making a cloth-like microporous laminate of a nonwoven fibrous web and thermoplastic film having air and moisture vapor permeabilities with liquid-barrier properties
DE19900656A1 (de) * 1999-01-11 2000-07-13 Kloeber Johannes Diffusionsoffene Unterspannbahn
US20040029469A1 (en) 2002-03-15 2004-02-12 Reemay, Inc. Microporous composite sheet material
US20050097857A1 (en) * 2003-11-06 2005-05-12 Building Materials Investment Corporation Breathable non-asphaltic roofing underlayment
WO2006138053A2 (fr) * 2005-06-17 2006-12-28 Building Materials Investment Corporation Sous-couche de toiture non-asphaltique permeable a l'air, dont la permeabilite a l'air peut etre adaptee
US20070178784A1 (en) * 2006-01-27 2007-08-02 Jones Gregory K Microporous breathable building and construction materials comprising coated woven and/or nonwoven fabrics, and method
US20080193716A1 (en) * 2006-12-15 2008-08-14 Trevor Arthurs Anti-Slip roofing underlayment
WO2009059402A1 (fr) * 2007-11-05 2009-05-14 Ibco Srl Matériau en feuille à surface anti-glissante constitué de bandes et de monofilaments
WO2009059403A1 (fr) * 2007-11-05 2009-05-14 Ibco Srl Matériau antidérapant en feuilles avec bandes torsadées
US20100056004A1 (en) 2007-03-05 2010-03-04 Jennifer Marie Galvin Skid resistant roof underlayment

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2897109A (en) * 1955-05-31 1959-07-28 Kimberly Clark Co Plastic film product
US5099627A (en) * 1990-09-28 1992-03-31 Benjamin Obdyke Incorporated Ventilated roof construction and method
US5422172A (en) * 1993-08-11 1995-06-06 Clopay Plastic Products Company, Inc. Elastic laminated sheet of an incrementally stretched nonwoven fibrous web and elastomeric film and method
US6187696B1 (en) * 1997-12-03 2001-02-13 E. I. Du Pont De Nemours And Company Breathable composite sheet structure
US6641896B2 (en) * 2000-12-21 2003-11-04 The Garland Company, Inc. Water resistant fire retardant roof underlayment sheet material
US7658040B2 (en) * 2004-02-23 2010-02-09 Huber Engineered Woods Llc Panel for sheathing system and method
US8178449B2 (en) * 2009-07-17 2012-05-15 Building Materials Investment Corp. Fire resistant slipsheet

Patent Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3338992A (en) 1959-12-15 1967-08-29 Du Pont Process for forming non-woven filamentary structures from fiber-forming synthetic organic polymers
US4116892A (en) 1975-03-31 1978-09-26 Biax-Fiberfilm Corporation Process for stretching incremental portions of an orientable thermoplastic substrate and product thereof
US4153751A (en) 1975-03-31 1979-05-08 Biax-Fiberfilm Corporation Process for stretching an impregnated film of material and the microporous product produced thereby
US4285100A (en) 1975-03-31 1981-08-25 Biax Fiberfilm Corporation Apparatus for stretching a non-woven web or an orientable polymeric material
US4153664A (en) 1976-07-30 1979-05-08 Sabee Reinhardt N Process for pattern drawing of webs
US5865926A (en) 1996-02-15 1999-02-02 Clopay Plastic Products Company, Inc. Method of making a cloth-like microporous laminate of a nonwoven fibrous web and thermoplastic film having air and moisture vapor permeabilities with liquid-barrier properties
DE19900656A1 (de) * 1999-01-11 2000-07-13 Kloeber Johannes Diffusionsoffene Unterspannbahn
US20040029469A1 (en) 2002-03-15 2004-02-12 Reemay, Inc. Microporous composite sheet material
US20050097857A1 (en) * 2003-11-06 2005-05-12 Building Materials Investment Corporation Breathable non-asphaltic roofing underlayment
WO2006138053A2 (fr) * 2005-06-17 2006-12-28 Building Materials Investment Corporation Sous-couche de toiture non-asphaltique permeable a l'air, dont la permeabilite a l'air peut etre adaptee
US20070178784A1 (en) * 2006-01-27 2007-08-02 Jones Gregory K Microporous breathable building and construction materials comprising coated woven and/or nonwoven fabrics, and method
US20080193716A1 (en) * 2006-12-15 2008-08-14 Trevor Arthurs Anti-Slip roofing underlayment
US20100056004A1 (en) 2007-03-05 2010-03-04 Jennifer Marie Galvin Skid resistant roof underlayment
WO2009059402A1 (fr) * 2007-11-05 2009-05-14 Ibco Srl Matériau en feuille à surface anti-glissante constitué de bandes et de monofilaments
WO2009059403A1 (fr) * 2007-11-05 2009-05-14 Ibco Srl Matériau antidérapant en feuilles avec bandes torsadées

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20210285219A1 (en) * 2020-03-12 2021-09-16 Milliken & Company Composite roofing membrane
US12146322B2 (en) 2020-04-23 2024-11-19 Milliken & Company Bitumen roofing composite
EP4171949A1 (fr) * 2020-06-26 2023-05-03 Borealis AG Structure composite non tissée présentant une excellente perméabilité à la vapeur d'eau
US20220333383A1 (en) * 2021-04-20 2022-10-20 Milliken & Company Metal roofing system
US11987985B2 (en) * 2021-04-20 2024-05-21 Milliken & Company Metal roofing system

Also Published As

Publication number Publication date
US20120096791A1 (en) 2012-04-26

Similar Documents

Publication Publication Date Title
US20120096791A1 (en) Roofing Underlayment
US7972981B2 (en) Microporous composite sheet material
CA2671555C (fr) Materiaux en feuille pour le batiment et la construction, ayant une resistance elevee au glissement humide et une resistance elevee a la penetration d'eau, et procedes pour les fabriquer
US7984591B2 (en) Impact resistant sheet material
US8497010B2 (en) Breathable low-emissivity metalized sheets
JP5308828B2 (ja) 被覆された織布及び／または不織布を含む、微多孔質で通気性の建築及び建設材料、並びに方法
EP1710337B1 (fr) Mats non-tissés de fibres polymères et leur procédé de fabrication
US8323770B2 (en) Breathable non-asphaltic roofing underlayment having tailorable breathability
CA3115398C (fr) Feuille composite
CN101460304A (zh) 具有一层或多层增强稀松布层的建筑施工复合材料
KR100715373B1 (ko) 저연신율포를 포함하는 통기성 재료 및 그의 제조 방법
US20030199217A1 (en) Housewrap with drainage channels
CA3115310A1 (fr) Feuille composite
WO2007149144A1 (fr) Enveloppes de drainage protectrices
US20170326835A1 (en) Breathable laminate housewrap and underlayment
CN121399317A (zh) 防风型闪纺片材

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10734604

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 13379561

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10734604

Country of ref document: EP

Kind code of ref document: A1