WO2011076422A1 - Lithiumdisilikat-glaskeramik, verfahren zu deren herstellung und deren verwendung - Google Patents

Lithiumdisilikat-glaskeramik, verfahren zu deren herstellung und deren verwendung Download PDF

Info

Publication number
WO2011076422A1
WO2011076422A1 PCT/EP2010/007918 EP2010007918W WO2011076422A1 WO 2011076422 A1 WO2011076422 A1 WO 2011076422A1 EP 2010007918 W EP2010007918 W EP 2010007918W WO 2011076422 A1 WO2011076422 A1 WO 2011076422A1
Authority
WO
WIPO (PCT)
Prior art keywords
lithium disilicate
oxide
glass ceramic
glass
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2010/007918
Other languages
English (en)
French (fr)
Other versions
WO2011076422A8 (de
Inventor
Bernhard Durschang
Jörn PROBST
Norbert Thiel
Joachim Bibus
Markus Vollmann
Udo Schusser
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Degudent GmbH
Vita Zahnfabrik H Rauter GmbH and Co KG
Fraunhofer Gesellschaft zur Foerderung der Angewandten Forschung eV
Original Assignee
Degudent GmbH
Vita Zahnfabrik H Rauter GmbH and Co KG
Fraunhofer Gesellschaft zur Foerderung der Angewandten Forschung eV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=43664558&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2011076422(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Priority to EP10796296.1A priority Critical patent/EP2516342B1/de
Priority to BR112012015576A priority patent/BR112012015576B1/pt
Priority to CA2785348A priority patent/CA2785348C/en
Priority to JP2012545163A priority patent/JP5698259B2/ja
Priority to RU2012125882/03A priority patent/RU2552284C2/ru
Priority to CN201080063038.3A priority patent/CN102741186B/zh
Priority to US13/518,765 priority patent/US8956987B2/en
Priority to AU2010335472A priority patent/AU2010335472B2/en
Priority to ES10796296.1T priority patent/ES2577610T3/es
Application filed by Degudent GmbH, Vita Zahnfabrik H Rauter GmbH and Co KG, Fraunhofer Gesellschaft zur Foerderung der Angewandten Forschung eV filed Critical Degudent GmbH
Priority to KR1020127019057A priority patent/KR101765125B1/ko
Publication of WO2011076422A1 publication Critical patent/WO2011076422A1/de
Publication of WO2011076422A8 publication Critical patent/WO2011076422A8/de
Anticipated expiration legal-status Critical
Priority to US14/274,235 priority patent/US10219879B2/en
Priority to US14/586,229 priority patent/US9604873B2/en
Priority to US15/401,380 priority patent/US10357343B2/en
Priority to US16/227,429 priority patent/US10765496B2/en
Priority to US17/012,113 priority patent/US20210055157A1/en
Priority to US17/852,126 priority patent/US20230099360A1/en
Ceased legal-status Critical Current

Abstract

Die Erfindung betrifft Glaskeramiken auf Basis des Lithiumdisilikat-Systems, die in einer Zwischenstufe der Kristallisation einfach mechanisch bearbeitbar sind und nach der vollständigen Kristallisation eine hochfeste, hoch transluzente und chemisch stabile Glaskeramik darstellen. Ebenso betrifft die Erfindung ein Verfahren zur Herstellung dieser Glaskeramiken. Verwendung finden die erfindungsgemäßen Glaskeramiken als Dentalmaterial.

Description

Lithiumdisilikat-Glaskeramik, Verfahren zu deren
Herstellung und deren Verwendung
Die Erfindung betrifft Glaskeramiken auf Basis des Lithiumdisilikat-Systems , die in einer Zwischenstufe der Kristallisation einfach mechanisch bearbeitbar sind und nach der vollständigen Kristallisation eine hochfeste, hoch transluzente und chemisch stabile Glaskeramik darstellen. Ebenso betrifft die Erfindung ein Verfahren zur Herstellung dieser Glaskeramiken.
Verwendung finden die erfindungsgemäßen Glaskeramiken als Dentalmaterial.
Lithiumdisilikat-Glaskeramiken sind aus der Literatur gut bekannt und mehrere Patente basieren auf diesem
Glaskeramiksystem. So werden z.B. in der EP-B-536 479 selbstglasierte LithiumdisiIikat-Glaskeramik-Gegenstände für die Herstellung von Tafelgeschirr beschrieben, in der EP-B-536 572 Lithiumdisilikat-Glas- keramiken, die durch das Aufstreuen eines feinteili- gen gefärbten Glases auf ihre Oberfläche als Ausklei¬ dungselemente für Bauzwecke eingesetzt werden können.
Ein Schwerpunkt der patentierten Lithiumdisilikat- glaskeramiken liegt in dentalen Anwendungen. Dies liegt daran, dass die Kristallisation der Lithiumdisilikat kristalle über eine Phase geringerer Festigkeit (Lithiummetasilicat ) erfolgt und das Materialsystem dadurch u.a. Chairside-Verfahren zugänglich ist (siehe S.D. Stookey: "Chemical achining of Photosensitive Glass", Ind. Eng. Chem. , 45, S. 115-118 (1993) and S.D. Stookey: " Photosensitively Opacifi- able Glass" US-A-2 , 684 , 911 (1954)). Untersuchung von Borom, z.B. M.-P. Borom, A.M. Turkalo, R.H. Doremus : "Strength and Microstructure in Lithium Disilicate Glass-Ceramics" , J. Am. Ceream. Soc, 58, Nr. 9-10, S. 385-391 (1975) und M.-P. Borom, A.M. Turkalo, R.H. Doremus: "Verfahren zum Herstellen von Glaskeramiken" DE-A-24 51 121 (1974) zeigen, dass Glaskeramiken, die Lithiummetasilikat als Hauptphase enthalten, eine verringerte Festigkeit im Vergleich zu Glaskeramiken haben, die Lithiumdisilikat als einzige kristalline Phase enthalten.
Dieses Prinzip wurde ausgenutzt, um in einem zweistufigen Kristallisationsprozess zuerst eine Glaskeramik herzustellen, die mechanisch gut bearbeitbar ist, z.B. mittels CAD/CAM-Verfahren, und diese anschließend in einer zweiten Kristallisationsstufe zur Dentalglaskeramik zu prozessieren. Dieses Verfahren ist geeignet, um dentale Restaurationen nach dem sog. chair-side-Verfahren verwenden zu können. Bei diesem Verfahren wird in der Zahnarztpraxis aus einem
Glaskeramikblock nach der ersten Kristallisationsstufe mittels CAD/CAM eine individuell angepasste Kro- ne/Onlay/Inlay herausgefräst, diese in einem Spezial- ofen der zweiten Kristallisationsstufe unterzogen und direkt in der ersten und einzigen Zahnarztsitzung dem Patienten eingesetzt (DE 10 2005 028 637) .
Außerdem wurden in WO-A-95/32678 und US-A-5, 507 , 981 Lithiumdisilikat-Glaskeramiken beschrieben, die durch den Einsatz eines speziellen verpressbaren Tiegels durch Heißpressen zu geformten Dentalprodukten verarbeitet werden können. Weiter sind aus der DE-C-14 21 886 Glaskeramiken auf Basis von S1O2 und Li20 bekannt, welche große Mengen an physiologisch sehr bedenklichem Arsenoxid enthalten. Auch in
US-A-4, 515, 634 und in FR-A-2 655 264 werden zur Herstellung von Dentalkronen und -brücken geeignete Lithiumdisilikat-Glaskeramiken offenbart .
Alle bekannten Lithiumdisilikat-Glaskeramiken zeigen Unzulänglichkeiten bei ihrer Verarbeitung zu geformten Produkten und/oder mechanischen bzw. optischen Eigenschaften und/oder chemischen Stabilität. Insbesondere sind beim Einsatz im Dentalbereich für alle genannten Eigenschaften gleichermaßen hohe Ansprüche zu erfüllen.
Ausgehend hiervon war es Aufgabe der vorliegenden Erfindung, eine Glaskeramik bereitzustellen, die verbesserte mechanische und optische Eigenschaften sowie eine verbesserte chemische Stabilität gegenüber den aus dem Stand der Technik bekannten (Glas- ) Keramiken auf eist .
Diese Aufgabe wird durch die Lithiumdisilikat-Glas- keramik mit den Merkmalen des Anspruchs 1, sowie durch das Verfahren zur Herstellung dieser Glaskeramik mit den Merkmalen des Anspruchs 9 gelöst. In Anspruch 12 werden erfindungsgemäße Verwendungen ange- geben. Ebenso wird ein geformtes Dentalprodukt mit den Merkmalen des Anspruchs 13 bereitgestellt . Die weiteren abhängigen Ansprüche zeigen vorteilhafte Weiterbildungen auf.
Im Rahmen der vorliegenden Erfindung wurden Glaszu¬ sammensetzungen entwickelt, die sich in einem zweistufigen Herstellungsprozess darstellen lassen, nach der ersten Kristallisationsstufe, insbesondere mittels CAD/CAM gut zu bearbeiten sind und nach einer sehr kurzen zweiten Kristallisationsstufe sowohl hochtransparent und hochfest sind als auch bessere chemische Beständigkeiten aufweisen, als die bekannten Lithiumdisilikat-Glaskeramiken .
Überraschenderweise hat sich gezeigt, dass die Zugabe von rÜ2 zu bestimmten Glaszusammensetzungen zu Glaskeramiken führt, die in einer Kristallisations Zwischenstufe sehr gut bearbeitbar sind und im Endzustand hervorragende Festigkeitswerte, außerordentliche Transluzenz und deutlich erhöhte chemische
Beständigkeiten aufweisen.
Es zeigte sich, dass sich bis zu 20 Gew.-% eines Stabilisators ausgewählt aus der Gruppe bestehend aus ZrÜ2, Hf02 oder Mischungen hiervon, in das Glas einbauen lässt, ohne die Struktur signifikant zu beeinflussen. Entgegen allen Erwartungen kristallisiert der Stabilisator hierbei nicht als eigene Kristallphase aus, sondern verbleibt in der Restglasphase. Durch den hohen Anteil in der amorphen Phase werden in dieser Phase die mechanischen und chemischen
Beständigkeiten enorm verbessert, was auch zu verbes¬ serten Eigenschaften im Endprodukt führt. Insbesondere die chemische Beständigkeit lässt sich über die Zusammensetzung der Restglasphase verbes¬ sern, da die Glasphase eine deutliche höhere Löslichkeit aufweist als das Lithiumdisilikat und somit die Schwachstelle bezüglich chemischem Angriff darstellt. Die extrem hohe Löslichkeit des Stabilisators (Zr02) in der Glasphase ist insbesondere beachtenswert, da z.B. Zirkonoxid bei vielen silikatischen Glaskeramiken als Keimbildner fungiert, d.h. bei einer Temperaturbehandlung als erste Phase auskristallisiert und an diesen Zr02-Kristallen sich die eigentlich angestrebte Kristallphase erleichtert und feinkristallin ausscheidet .
Durch die hohen Anteile des Stabilisators, die im Wesentlichen in der amorphen Phase verbleiben, ist der kristalline Anteil entsprechend begrenzt. Hierdurch und durch die geringe Kristallitgröße der Lithium- disilikatkristalle entsteht eine gute Transluzenz der Materialien nach der zweiten Kristallisation. Die Transluzenz wird jedoch auch noch dadurch verbessert, dass der Brechungsindex der Glasphase wiederum durch den Stabilisator erhöht wird und sich dadurch dem Brechungsindex des Lithiumdisilikats anpasst . Bei Glaskeramiken, bei denen der Brechungsindex der amorphen Matrixphase mit dem Brechungsindex der kristallinen Phase/Phasen übereinstimmt, findet man sehr gute Transluzenzeigenschaften, relativ unabhängig von der Kristallitgröße. In den erfindungsgemäßen Glaskeramiken sind also alle drei Punkte zur Erzeugung einer höchst transluzenten Glaskeramik erfüllt: limitierter Kristallphasenanteil,
kleine Kristalle (< 500 nm) ,
angepasster Brechungsindex von amorpher und kristalliner Phase. Der hohe Anteil des Stabilisators wirkt sich in der Glaskeramik also in einer verbesserten chemischen Beständigkeit, höheren Festigkeitswerten und
einer in mehrerer Hinsicht verbesserten
Transluzenz zu entsprechenden Glaskeramiken ohne bzw. mit geringem Zr02- oder Hf02-Anteil aus.
Die erfindungsgemäßen Glaskeramiken können vorzugsweise mittels eines Verfahrens hergestellt werden, bei dem
(a) ein Ausgangsglas hergestellt wird, das die Komponenten der Glaskeramik enthält,
(b) das Ausgangsglas einer ersten Wärmebehandlung bei einer ersten Temperatur unterworfen wird, um eine Glaskeramik herzustellen, welche
Lithiummetasilikat als einzige bzw. Hauptkristallphase aufweist und
(c) diese Glaskeramik einer zweiten Wärmebehandlung unterzogen wird, bei der das Lithiummetasilikat mit Si02 aus der Glasphase in Lithiumdisilikat umgewandelt wird und anschließend
Lithiumdisilikat als einzige oder Haupt kristall- phase vorliegt.
Die Kristallisation zum Lithiummetasilikat findet vorzugsweise bei Temperaturen zwischen 620 °C und 800 °C statt, mit Zeiten zwischen 1 und 200 Minuten, bevorzugt zwischen 650 °C und 750 °C für 10 bis 60 Minuten . Die Kristallisation zum Lithiumdisilikat findet vor¬ zugsweise bei Temperaturen zwischen 800 °C und
1040 °C statt, mit Zeiten von 5 bis 200 Minuten, be¬ vorzugt zwischen 800 °C und 870 °C für 5 bis 30 Minu- ten .
Anhand der nachfolgenden Beispiele soll der erfindungsgemäße Gegenstand näher erläutert werden, ohne diesen auf die hier gezeigten speziellen Ausführungs- formen einschränken zu wollen.
Beispiele 1 bis 6
In den Beispielen 1 bis 6 sind Zusammensetzungen von hochzirkonoxidhaltigen Gläsern angegeben, die durch eine zweistufige Temperaturbehandlung erst zu gut mechanisch bearbeitbaren Lithiummetasilicat- Glaskeramiken und anschließend zu hoch-transluzenten, hoch-festen und chemisch stabilen Lithiumdisilicat- Glaskeramiken überführt werden.
Die Zusammensetzungen mit ihren Bestandteilen sind in Tabelle 1 dargestellt.
Tabelle 1
Bl B2 B3 B4 B5 B6
Si02 66, 9 65, 8 65, 5 63, 7 63, 5 63, 5
Li20 13, 9 13,7 13, 6 13, 2 14,4 12, 9
Zr02 10,0 10,0 12, 0 11,7 12, 7 13, 5
A1203 3,2 3,1 3,1 3,0 3,3 3, 5
P205 3,0 3,0 3, 0 2,9 3,1 3,4
K20 2,9 2,9 2,9 2,8 3,0 3,2
Ce02 - 1,0 - 2,0 - -
Er203 - 0,2 - 0,3 - -
Tb203 - 0,3 - 0,3 - - Die Gläser wurden bei 1500 °C erschmolzen und in Me¬ tallformen zu Blocks gegossen. Die Blocks wurden bei 560 °C im Ofen entspannt und langsam abgekühlt. Für die unterschiedlichen Charakterisierungsverfahren wurden die Glasblocks zerteilt und einer ersten Kristallisationsbehandlung unterzogen. Hierfür wurden die Gläser für 10 bis 120 Minuten bei 600 °C bis 750 °C ausgelagert. Hierdurch wurden Glaskeramiken mit Festigkeitswerten von 150 MPa bis 220 MPa hergestellt. Als Kristallphase wurde hierbei ausschließlich
Lithiummetasilicat festgestellt. In diesem Zustand ist eine Bearbeitung mittels CAD/CAM-Methoden sehr gut möglich.
Mit einer zweiten kurzen Kristallisation bei 800 °C bis 950 °C für 3 bis 15 Minuten findet eine Umkris- tallisation des Lithiummetasilikates mit amorphem Si02 aus der Glasphase zum Lithiumdisilikat statt und es kommt zu einer Festigkeitserhöhung auf 300 MPa bis 450 MPa. Neben der Lithiumdisilikatphase kann hierbei eine zirkonoxidhaltige Nebenkristallphase entstehen. Außerdem können noch geringe Reste von Lithiummetasilikat vorliegen. Die eindeutige Hauptkristallphase ist das Lithiumdisilikat.
In Tabelle 2 sind die Kristallisationsbedingungen von einzelnen Gläsern sowie die entstehenden Kristallphasen und Festigkeitswerte dargestellt. Tabelle 2
Figure imgf000010_0001

Claims

Patentansprüche
1. Lithiumdisilikat-Glaskeramik enthaltend mindes¬ tens 10 Gew.-% eines Stabilisators zur Erhöhung der chemischen und mechanischen Stabilität, wobei der Stabilisator im Wesentlichen in der amorphen Phase vorliegt.
2. Lithiumdisilikat-Glaskeramik nach Anspruch 1, dadurch gekennzeichnet, dass der Stabilisator ausgewählt ist aus der Gruppe bestehend aus Zirkonoxid, Hafniumoxid und Mischungen hiervon.
3. Lithiumdisilikat-Glaskeramik nach Anspruch 1 oder 2 mit folgender Zusammensetzung:
55 bis 70 Gew.-% Si02,
10 bis 15 Gew.-% Li02,
10 bis 20 Gew.-% des Stabilisators ausgewählt aus der Gruppe bestehend aus Zr02, Hf02 oder Mischungen hiervon,
0,1 bis 5 Gew.-% K20,
0,1 bis 5 Gew.-% A1203,
0 bis 10 Gew.-% an Zusatzstoffen sowie
0 bis 10 Gew.-% an Farbstoffen.
4. Lithiumdisilikat-Glaskeramik nach einem der vorhergehenden Ansprüche,
dadurch gekennzeichnet, dass die Farbstoffe glasfärbende Oxide und/oder Farbkörper sind. Lithiumdisilikat-Glaskeramik nach einem der vor¬ hergehenden Ansprüche,
dadurch gekennzeichnet, dass die glasfärbenden Oxide ausgewählt sind aus der Gruppe der Oxide von Eisen, Titan, Cer, Kupfer, Chrom, Kobalt, Nickel, Mangan, Selen, Silber, Indium, Gold Seltenerdmetallen, insbesondere Neodym, Praesodym, Samarium und Europium.
Lithiumdisilikat-Glaskeramik nach einem der vorhergehenden Ansprüche,
dadurch gekennzeichnet, dass die Farbkörper dotierte Spinelle sind.
Lithiumdisilikat-Glaskeramik nach einem der vor¬ hergehenden Ansprüche,
dadurch gekennzeichnet, dass die Zusatzstoffe ausgewählt sind aus der Gruppe bestehend aus Boroxid, Phosphoroxid, Fluor, Natriumoxid, Bari¬ umoxid, Strontiumoxid, Magnesiumoxid, Zinkoxid, Calciumoxid, Yttriumoxid, Titanoxid, Nioboxid, Tantaloxid, Lanthanoxid und Mischungen hiervon.
Lithiumdisilikat-Glaskeramik nach einem der vor¬ hergehenden Ansprüche mit folgender Zusammensetzung :
58 bis 64 Gew.-% Si02,
11 bis 13 Gew.-% Li02,
10 bis 15 Gew.-% des Stabilisators ausgewählt aus der Gruppe bestehend aus Zr02, Hf02 oder Mischungen hiervon,
2 bis 5 Gew.-% K20,
2 bis 5 Gew.-% Al203,
2 bis 5 Gew.-% P205 sowie 0 bis 5 Gew.-% an Zusatzstoffen sowie
0 bis 10 Gew.-% an Farbstoffen.
Verfahren zur Herstellung einer Lithiumdisili- kat-Glaskeramik nach einem der vorhergehenden Ansprüche, bei dem
a) ein Ausgangsglas hergestellt wird, das die Komponenten der Glaskeramik enthält,
b) das Ausgangsglas einer ersten Wärmebehandlung zur Herstellung einer Glaskeramik, die
Lithiummetasilicat als Hauptkristallphase aufweist, unterworfen wird,
c) die Glaskeramik aus b) einer zweiten Wärmebehandlung unterworfen wird, bei der das Lithiummetasilicat mit Si02 aus der Glasphase in Li- thiumdisilicat umgewandelt wird und anschließend Lithiumdisilicat als Hauptkristallphase vorliegt .
Verfahren nach Anspruch 9,
dadurch gekennzeichnet, dass die erste Wärmebehandlung bei einer Temperatur von 620 °C bis 800 °C über einen Zeitraum von 1 bis 200 min, insbesondere von 650 °C bis 750 °C über einen Zeitraum von 10 bis 60 min, erfolgt.
Verfahren nach einem der Ansprüche 9 oder 10, dadurch gekennzeichnet, dass die zweite Wärmebehandlung bei einer Temperatur von 800 °C bis 1040 °C über einen Zeitraum von 5 bis 200 min, insbesondere von 650 °C bis 750 °C über einen Zeitraum von 5 bis 30 min erfolgt.
12. Verwendung der Lithiumdisilikat-Glaskeramik nach einem der Ansprüche 1 bis 8 als Dentalmaterial oder als Komponente eines Dentalmaterials. 13. Geformtes Dentalprodukt enthaltend eine Lithium¬ disilikat-Glaskeramik nach einem der Ansprüche 1 bis 8, insbesondere in Form eines Inlays, eines Onlays, einer Brücke, eines Stiftaufbaus , einer Verblendung, einer (Teil) kröne.
PCT/EP2010/007918 2009-12-23 2010-12-23 Lithiumdisilikat-glaskeramik, verfahren zu deren herstellung und deren verwendung Ceased WO2011076422A1 (de)