WO2011126263A2 - 점착제 조성물, 점착시트 및 터치 패널 - Google Patents

점착제 조성물, 점착시트 및 터치 패널 Download PDF

Info

Publication number
WO2011126263A2
WO2011126263A2 PCT/KR2011/002356 KR2011002356W WO2011126263A2 WO 2011126263 A2 WO2011126263 A2 WO 2011126263A2 KR 2011002356 W KR2011002356 W KR 2011002356W WO 2011126263 A2 WO2011126263 A2 WO 2011126263A2
Authority
WO
WIPO (PCT)
Prior art keywords
pressure
sensitive adhesive
adhesive composition
present
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2011/002356
Other languages
English (en)
French (fr)
Other versions
WO2011126263A3 (ko
Inventor
이용훈
이억형
한학림
최원구
송민석
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LX Hausys Ltd
Original Assignee
LG Hausys Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LG Hausys Ltd filed Critical LG Hausys Ltd
Priority to US13/635,195 priority Critical patent/US20130004695A1/en
Priority to JP2013502504A priority patent/JP2013527861A/ja
Priority to EP11766114.0A priority patent/EP2557135B1/en
Priority to CN201180015300.1A priority patent/CN102906207B/zh
Publication of WO2011126263A2 publication Critical patent/WO2011126263A2/ko
Publication of WO2011126263A3 publication Critical patent/WO2011126263A3/ko
Anticipated expiration legal-status Critical
Priority to US14/454,767 priority patent/US20140349055A1/en
Ceased legal-status Critical Current

Abstract

본 발명은 점착제 조성물, 점착 시트 및 터치 패널에 관한 것이다. 본 발명에서는, 첨가제로서 저분자량체를 사용하지 않고, 점착제 조성물, 구체적으로 터치패널용 점착제 조성물을 조성한다. 본 발명에서는, 경화 공정 또는 인쇄회로기판의 조립 공정 등에서의 내열성이 탁월하고, 광특성, 젖음성, 재단성, 작업성, 휨 억제 특성 및 내구성 등의 물성이 우수한 점착제 조성물, 점착시트 및 터치패널을 제공할 수 있다.

Description

점착제 조성물, 점착시트 및 터치 패널
본 발명은, 점착제 조성물, 점착시트 및 터치 패널에 관한 것이다.
최근, 휴대전화 또는 PHS 단말기 등의 모바일형 단말기 및 PDA 단말기 등과 같은 이동통신 단말기는 큰 시장을 형성하고 있다. 이동통신 단말기에서 추구되는 기술적 목표는 박형화, 경량화, 저전력 소비화, 고해상도화 및 고휘도화 등을 들 수 있다.
특히, 입력 장치로서 터치패널 또는 터치스크린을 탑재한 단말기는, 경량화 및 깨짐 방지의 관점에서 투명 전도성 플라스틱 필름, 예를 들면 폴리에틸렌테레프탈레이트(PET) 필름을 기재로 하고, 그 일면에 ITO(Indium Tin Oxide) 등의 도전성 박막을 형성한 필름을 점착제층에 의해 전도성 유리, 보강재 또는 데코 필름 등에 적층한 구조를 가지고 있다.
터치스크린 또는 터치패널에서 투명 도전성 필름의 부착에 사용되는 점착제에는 데코 필름에 의한 인쇄 단차를 흡수할 수 있는 단차 흡수성; 고온 또는 고습 조건과 같은 가혹 조건에 노출되었을 경우, 컬(curl)이나 기포 등의 발생을 억제할 수 있는 내구성; 재단 시에 삐침이나 눌림을 억제할 수 있는 재단성; 및 각종 기재에 대한 우수한 접착성 등의 물성이 요구되고, 그 외에도 광특성 및 작업성 등의 다양한 물성이 요구된다.
특히, 터치패널 또는 터치스크린의 제조 시에, 점착제 조성물을 경화하기 위한 공정은 140℃ 이상의 온도에서 2 시간 이상 진행되고, 또한 인쇄회로기판(PCB; Printed Circuit Board)의 조립 공정 시에 이방 도전성 필름(ACF; Anisotropic Conductive Foil)을 접착하는 공정도 약 120℃ 이상의 고온에서 진행된다. 이 과정에서, 점착제 조성물 또는 점착제의 내열성이 떨어지면, 점착제와 피착체(ex. 투명 도전성 필름 등)의 사이에서 에어포켓(air pocket), 기포, 들뜸 또는 컬(Curl)이 유발되는 문제가 있다.
한국공개특허공보 제2006-0043847호는, 터치패널에 사용되는 투명 점착제로서, 중량평균분자량이 50만 내지 90만인 고분자량 아크릴계 중합체 및 중량평균분자량이 3,000 내지 6,000인 저분자량 올리고머를 포함하는 점착제 조성물을 개시한다.
그러나, 상기 문헌에서 개시하는 점착제는, 내열성이 크게 떨어져서 약 100℃ 이상의 고온 공정에 적용 시에, 점착제와 피착체의 사이에서 에어 포켓 또는 기포가 유발되거나, 패널의 휨, 들뜸 또는 컬(curl) 등이 쉽게 유발되는 문제점이 있다.
본 발명은 점착제 조성물, 점착시트 및 터치 패널을 제공하는 것을 목적으로 한다.
본 발명은 상기 과제를 해결하기 위한 수단으로서, 베이스 수지; 및 다관능성 가교제를 포함하고, 하기 일반식 1의 조건을 만족하는 점착제 조성물을 제공한다.
[일반식 1]
X1 ≥ 6 kg/cm2
상기 일반식 1에서 X1은 상기 점착제 조성물의 시트상 경화물인 점착제의 일면을 ITO PET 필름에서 ITO 면의 반대면에 부착하고, 그 다른 면을 유리 기판에 부착한 후, 상온에서 24시간 동안 방치한 다음, 140℃의 온도에서 0.8 mm/sec의 크로스헤드 속도(crosshead speed)로 측정한 동적 전단 강도(dynamic shear strength)를 나타낸다.
본 발명은 상기 과제를 해결하기 위한 다른 수단으로서, 본 발명에 따른 점착제 조성물의 경화물을 포함하는 점착제층을 가지는 터치 패널용 점착시트를 제공한다.
본 발명은 상기 과제를 해결하기 위한 또 다른 수단으로서, 투명 플라스틱 기판; 및 상기 투명 플라스틱 기판의 상부에 형성되고, 본 발명에 따른 점착제 조성물의 경화물을 포함하는 점착제층을 가지는 터치 패널을 제공한다.
본 발명에서는 올리고머와 같은 저분자량체를 사용하지 않고, 점착제 조성물, 구체적으로는 터치 패널용 점착제 조성물을 조성한다. 이에 따라 본 발명에서는, 터치패널 제조 시의 경화 공정 또는 인쇄회로기판의 조립 공정에서의 고온 조건에서 우수한 내열성을 가지는 점착제 조성물 또는 점착제를 제공할 수 있다. 또한, 본 발명에서는, 각종 피착체에 대한 젖음성, 광특성, 재단성, 작업성 및 내구성이 우수하고, 패널의 휨, 들뜸 및 컬(curl) 등을 유발하지 않는 점착제 조성물 또는 점착제를 제공할 수 있다.
도 1은 본 발명에서 점착제의 동적 전단력을 측정하는 과정을 나타내는 도면이다.
도 2는 본 발명에서 점착제의 정적 전단 유지 시간을 측정하는 과정을 나타내는 도면이다.
도 3은 본 발명의 일 태양에 따른 점착시트의 단면도를 나태내는 도면이다.
도 4는 본 발명의 다른 태양에 따른 점착시트의 단면도를 나타내는 도면이다.
도 5는 본 발명의 일 태양에 따라서 구성된 터치 패널을 예시적으로 나타내는 도면이다.
본 발명은 베이스 수지; 및 다관능성 가교제를 포함하고, 하기 일반식 1의 조건을 만족하는 점착제 조성물에 관한 것이다.
[일반식 1]
X1 ≥ 6 Kg/cm2
상기 일반식 1에서 X1은 상기 점착제 조성물의 시트상 경화물인 점착제의 일면을 ITO PET 필름에서 ITO 면의 반대면에 부착하고, 그 다른 면을 유리 기판에 부착한 후, 상온에서 24시간 동안 방치한 다음, 140℃의 온도에서 0.8 mm/sec의 크로스헤드 속도로 측정한 동적 전단강도를 나타낸다.
이하, 본 발명의 점착제 조성물을 구체적으로 설명한다.
본 발명의 점착제 조성물은, 베이스 수지 및 다관능성 가교제를 포함하며, 특정 조건에서 수행한 동적 전단력 시험(dynamic shear teat)에서, 동적 전단력(dynamic shear strength)이 상기 일반식 1의 조건을 만족한다. 즉, 본 발명의 점착제는, 140℃의 온도 및 0.8 mm/sec의 크로스헤드 속도의 조건에서 측정한 동적 전단력이 6 kg/cm2 이상이며, 바람직하게는 6.5 kg/cm2 내지 15 kg/cm2, 보다 바람직하게는 6.5 kg/cm2 내지 10 kg/cm2일 수 있다.
본 발명에서, 상기 점착제의 동적 전단력은, 본 발명의 점착제 조성물로 점착제를 제조한 후, 상기 점착제에 대하여 140℃의 온도 및 0.8 mm/sec의 크로스헤드 속도의 조건에서 측정할 수 있다.
구체적으로, 첨부된 도 1은 본 발명에서 점착제의 동적 전단력을 측정하는 방법을 나타내는 모식도이다. 도 1에 나타난 바와 같이, 본 발명에 따른 점착제 조성물로 제조된 점착제층(11)을 유리 기판(12) 및 일면에 ITO면(13)이 형성되어 있는 PET 필름(14), 즉 ITO PET 필름(15) 사이에 부착시켜 시편을 제조한다. 이 경우, 점착제층(11)은 ITO PET필름(15)의 ITO면(13)의 반대면에 부착된다. 이 때, 상기 점착제층(11)의 유리 기판(12) 및 ITO PET 필름(15)에 대한 부착은 ASTM D1002에 근거하여, 2kg의 롤러로 5회 왕복하여 수행할 수 있다. 또한, 상기에서 시험에 적용되는 점착제층(11)은 그 크기가 1 in × 1 in × 50 ㎛(가로×세로×두께)일 수 있다. 상기 도 1에 나타난 바와 같은 시편(10)을 제조한 후, 상온에서 24시간 동안 방치한 다음, 140 ℃의 온도에서 0.8mm/sec의 크로스헤드 속도로 동적 전단력을 측정한다. 더욱 상세하게는, 인장 시험기를 사용하여, 유리 기판(12) 및 ITO PET필름(15)을 서로 반대 방향(도 1에 나타난 화살표 방향)으로 각각 0.8 mm/sec의 크로스헤드 속도로 인장하면서, 상기 유리 기판(12) 및/또는 ITO PET필름(15)이 점착제(11)로부터 분리되는 시점에서 상기 점착제(11)의 동적 전단력을 측정할 수 있다.
본 발명에서는, 점착제의 동적 전단력을 6.0 kg/cm2 이상으로 제어함으로써, 각종 피착체에 대한 젖음성, 광특성, 재단성, 작업성 및 내구성이 우수하면서, 특히 탁월한 내열성을 가져, 고온 조건에서 휨, 들뜸 및 컬(curl) 등을 유발하지 않는 점착제를 제공할 수 있다.
본 발명의 점착제 조성물은 또한, 하기의 일반식 2의 조건을 만족할 수 있다.
[일반식 2]
X2 ≥ 10 분
상기 일반식 2에서 X2는 상기 점착제 조성물의 시트상 경화물인 점착제의 일면을 ITO PET 필름에서 ITO 면의 반대면에 부착하고, 그 다른 면을 유리 기판에 부착한 후, 상온에서 24시간 동안 방치한 다음, 140℃의 온도에서 상기 ITO PET 필름에 2 kg의 하중을 인가하여 측정한 유지 시간, 즉 정적 전단 유지시간(static shear maintenance time)을 의미한다.
첨부된 도 2는 본 발명에서 점착제의 정적 전단 유지 시간을 측정하는 과정을 나타내는 도면이다.
첨부된 도 2에 나타난 바와 같이, 본 발명에서, 상기 점착제의 정적 전단 유지 시간은, 본 발명의 점착제 조성물로부터 점착제(11)를 제조한 후, 상기 점착제(11)를 소정 피착체, 구체적으로는 유리 기판(12) 및 ITO PET 필름(15)의 사이에 부착하고, 상기 피착체에 소정의 하중을 인가하여 측정할 수 있다. 구체적으로, 도 2에 나타난 바와 같이, 본 발명에 따른 점착제 조성물로부터 제조된 점착제층(11)을 유리 기판(12) 및 일면에 ITO면(13)이 형성되어 있는 PET 필름(14), 즉ITO PET 필름(15)의 사이에 부착시켜 시편을 제조한다. 이 경우, 점착제층(11)은 ITO PET필름(15)의 ITO면(13)의 반대면에 부착된다. 이 때, 상기 점착제층의 유리 기판(12) 및 ITO PET 필름(15)에 대한 부착은 ASTM D1002에 근거하여, 2kg의 롤러로 5회 왕복하여 수행할 수 있다. 상기에서 시험에 적용되는 점착제층(11)은 그 크기가 1 in × 1 in × 50 ㎛(가로×세로×두께)일 수 있다. 상기 도 2에 나타난 바와 같은 시편(20)을 제조한 후, 상온에서 24시간 동안 방치한 다음, 140℃의 온도에서, 상기 ITO PET필름(15)에 무게가 2 Kg인 추(21)를 달아, 하중을 인가하여 정적 전단 유지시간을 측정한다. 더욱 상세하게는, 상기와 같이 하중이 인가된 상태에서, ITO PET필름(15) 또는 유리 기판(12)이 점착제층(11)으로부터 분리될 때까지의 시간을 측정하여, 상기 정적 전단 유지 시간을 측정할 수 있다.
본 발명에서 정적 전단 유지 시간은, 10 분 이상, 바람직하게는 15분 이상, 보다 바람직하게는 20분 이상일 수 있다. 본 발명에서는, 점착제의 정적 전단 유지 시간을 10분 이상으로 제어함으로써, 특히 탁월한 내열성을 가져, 고온 조건에서 휨, 들뜸 및 컬(curl) 등을 유발하지 않는 점착제를 제공할 수 있다.
본 발명에서 상기 정적 전단 유지 시간의 상한은 특별히 제한되지 않으며, 예를 들면, 약 80분 이하, 바람직하게는 60분 이하, 보다 바람직하게는 50분 이하의 범위에서 제어할 수 있다.
상기와 같은 본 발명에 따른 점착제 조성물에 포함되는 베이스 수지의 종류는, 특별히 제한하지 않으며, 예를 들면, 아크릴계 수지, 고무계 수지, 우레탄계 수지, 실리콘계 수지 또는 EVA(Ethylene Vinyl Acetate)계 수지 등과 같은 통상의 점착성 수지를 사용할 수 있다. 본 발명의 일 태양에서는, 상기 베이스 수지로서, 투명성 등의 광학적 특성이 우수하고, 산화 및 황변(yellowing) 등에 대한 저항성이 탁월한 아크릴계 수지를 사용할 수 있다.
본 발명에서 베이스 수지로서 아크릴계 수지를 사용할 경우, 상기 아크릴계 수지의 중량평균분자량은 100만 이상일 수 있다. 상기에서 아크릴계 수지의 중량평균분자량은, GPC(gel permeation chromatography)에 의해 측정한, 폴리스티렌 환산 수치를 의미한다. 본 발명에서는 중량평균분자량이 100만 이상인 아크릴계 수지를 사용하여, 탁월한 내열성 및 내구성을 나타내고, 재박리 시 피착체로의 전사로 인한 오염을 유발하지 않는 점착제를 제공할 수 있다. 본 발명에 있어서, 상기 아크릴계 수지의 중량평균분자량이 100만 미만인 경우, 내열성이 감소되고, 재단성과 같은 작업성이 악화될 우려가 있다.
본 발명에서 상기 아크릴계 수지의 중량평균분자량의 상한은 특별히 제한되지 않으나, 코팅성 등을 고려하여, 300만 이하, 바람직하게는 250만 이하의 범위에서 제어할 수 있다.
본 발명에서 상기 아크릴계 수지는, 예를 들면, (메타)아크릴산 에스테르계 단량체 및 가교성 단량체를 포함하는 단량체 혼합물의 중합체일 수 있다.
본 발명에서 사용될 수 있는 (메타)아크릴산 에스테르계 단량체의 종류는 특별히 한정되지 않으며, 예를 들면, 알킬 (메타)아크릴레이트를 사용할 수 있다. 이 경우, 단량체에 포함되는 알킬기가 지나치게 길어지면, 경화물의 응집력이 저하되고, 유리전이온도나 점착성의 조절이 어려워질 우려가 있으므로, 탄소수가 1 내지 14, 바람직하게는 탄소수가 1 내지 8인 알킬기를 갖는 알킬 (메타)아크릴레이트를 사용할 수 있다. 이와 같은 단량체의 예로는 메틸 (메타)아크릴레이트, 에틸 (메타)아크릴레이트, n-프로필 (메타)아크릴레이트, 이소프로필 (메타)아크릴레이트, n-부틸 (메타)아크릴레이트, t-부틸 (메타)아크릴레이트, sec-부틸 (메타)아크릴레이트, 펜틸 (메타)아크릴레이트, 2-에틸헥실 (메타)아크릴레이트, 2-에틸부틸 (메타)아크릴레이트, n-옥틸 (메타)아크릴레이트, 이소옥틸 (메타)아크릴레이트, 이소보닐 (메타)아크릴레이트 또는 이소노닐 (메타)아크릴레이트 등을 들 수 있고, 본 발명에서는 상기 중 일종 또는 이종 이상의 혼합을 사용할 수 있다.
본 발명에서 단량체 혼합물에 포함되는 가교성 단량체는, 분자 구조 내에 공중합성 관능기(ex. 탄소-탄소 이중 결합) 및 가교성 관능기를 동시에 포함하는 단량체를 의미하고, 상기 단량체는 중합체에 다관능성 가교제와 반응할 수 있는 가교성 관능기를 부여할 수 있다.
본 발명에서 사용할 수 있는 가교성 단량체의 예로는 히드록시기 함유 단량체, 카복실기 함유 단량체 또는 질소 함유 단량체 등을 들 수 있으며, 이 중에서 일종 또는 이종 이상의 혼합을 사용할 수 있다. 본 발명에서는, 특히 상기 가교성 단량체로서, 카복실기 함유 단량체를 사용하는 것이 바람직하지만, 이에 제한되는 것은 아니다.
상기에서 히드록시기 함유 단량체의 예로는, 2-히드록시에틸 (메타)아크릴레이트, 2-히드록시프로필 (메타)아크릴레이트, 4-히드록시부틸 (메타)아크릴레이트, 6-히드록시헥실 (메타)아크릴레이트, 8-히드록시옥틸 (메타)아크릴레이트, 2-히드록시에틸렌글리콜 (메타)아크릴레이트 또는 2-히드록시프로필렌글리콜 (메타)아크릴레이트 등을 들 수 있고; 카복실기 함유 단량체의 예로는 아크릴산, 메타크릴산, 2-(메타)아크릴로일옥시 아세트산, 3-(메타)아크릴로일옥시 프로필산, 4-(메타)아크릴로일옥시 부틸산, 아크릴산 이중체, 이타콘산 또는 말레산 등을 들 수 있으며; 질소 함유 단량체의 예로는 2-이소시아네이토에틸 (메타)아크릴레이트, 3-이소시아네이토프로필 (메타)아크릴레이트, 4-이소시아네이토부틸 (메타)아크릴레이트, (메타)아크릴아미드, N-비닐 피롤리돈 또는 N-비닐 카프로락탐 등을 들 수 있으나, 이에 제한되는 것은 아니다.
본 발명에 있어서, 상기 단량체 혼합물은, (메타)아크릴산 에스테르계 단량체 80 중량부 내지 99.9 중량부 및 가교성 단량체 0.1 중량부 내지 20 중량부, 바람직하게는 (메타)아크릴산 에스테르계 단량체 90 중량부 내지 99.9 중량부 및 가교성 단량체 0.1 중량부 내지 20 중량부를 포함할 수 있다. 본 발명에서는, 상기 단량체 혼합물 내에서 단량체 간의 중량 비율을 상기와 같이 제어함으로써, 우수한 신뢰성, 취급성, 내구성 및 재박리성을 가지며, 초기 접착력 감소로 인한 박리 또는 들뜸의 발생을 효과적으로 억제할 수 있는 점착제를 제공할 수 있다.
본 명세서에서 특별히 달리 규정하지 않는 한, 단위 「중량부」는 「중량 비율」을 의미한다.
본 발명에서 상기 단량체 혼합물은 또한, 중합체의 유리전이온도의 조절 및 기타 기능성 부여의 관점에서, 하기 화학식 1로 표시되는 공단량체를 추가로 포함할 수 있다.
[화학식 1]
Figure PCTKR2011002356-appb-I000001
상기 화학식 1에서, R1 내지 R3는 각각 독립적으로 수소 또는 알킬을 나타내고, R4는 시아노; 알킬로 치환 또는 비치환된 페닐; 아세틸옥시; 또는 COR5를 나타내며, 이 때 R5는 알킬 또는 알콕시알킬로 치환 또는 비치환된 아미노 또는 글리시딜옥시를 나타낸다.
상기 식의 R1 내지 R5의 정의에서 알킬 또는 알콕시는 탄소수 1 내지 8의 알킬 또는 알콕시를 의미하며, 바람직하게는 메틸, 에틸, 메톡시, 에톡시, 프로폭시 또는 부톡시이다.
본 발명에서 사용할 수 있는 화학식 1의 단량체의 구체적인 예로는 (메타)아크릴로니트릴, N-메틸 (메타)아크릴아미드 또는 N-부톡시 메틸 (메타)아크릴아미드와 같은 질소 함유 단량체; 스티렌 또는 메틸 스티렌과 같은 스티렌계 단량체; 글리시딜 (메타)아크릴레이트; 또는 비닐 아세테이트와 같은 카르복실산 비닐 에스테르 등의 일종 또는 이종 이상을 들 수 있으나, 이에 제한되는 것은 아니다. 상기와 같은 단량체가 본 발명의 단량체 혼합물에 포함될 경우에는, 그 함량은, 상기 (메타)아크릴산 에스테르계 단량체 또는 가교성 단량체의 함량 대비 20 중량부 이하인 것이 바람직하다. 상기 함량이 20 중량부를 초과하면, 유연성 및/또는 박리력이 저하될 우려가 있다.
본 발명에서, 전술한 각각의 성분을 포함하는 단량체 혼합물을 중합시켜, 아크릴계 수지를 제조하는 방법은 특별히 한정되지 않는다. 본 발명에서는, 예를 들면 용액 중합, 광중합, 벌크 중합, 서스펜션 중합 또는 에멀션 중합과 같은 일반적인 중합법을 사용할 수 있다. 본 발명에서는 투명성, 내수성, 비용 등의 관점에서, 특히 용액 중합법을 사용하여 아크릴계 수지를 제조하는 것이 바람직하지만, 이에 제한되는 것은 아니다.
본 발명의 점착제 조성물은 다관능성 가교제를 추가로 포함하며, 상기 다관능성 가교제의 사용량에 따라 경화물의 응집력 및 점착 특성 등의 물성을 조절할 수 있다.
본 발명에서 사용될 수 있는 다관능성 가교제의 종류는 특별히 한정되지 않으며, 예를 들면, 이소시아네이트계 화합물, 에폭시계 화합물, 아지리딘계 화합물 및 금속 킬레이트계 화합물과 같은 일반적인 가교제를 사용할 수 있다. 상기에서 이소시아네이트계 화합물의 예로는 톨리렌 디이소시아네이트, 크실렌 디이소시아네이트, 디페닐메탄 디이소시아네이트, 헥사메틸렌 디이소시아네이트, 이소보론 디이소시아네이트, 테트라메틸크실렌 디이소시아네이트, 나프탈렌 디이소시아네이트 및 하나 이상의 이소시아네이트 화합물과 폴리올(ex. 트리메틸롤 프로판)과의 반응물로 이루어진 군으로부터 선택된 하나 이상을 들 수 있고; 에폭시계 화합물의 예로는 에틸렌글리콜 디글리시딜에테르, 트리글리시딜에테르, 트리메틸올프로판 트리글리시딜에테르, N,N,N’,N’-테트라글리시딜 에틸렌디아민 및 글리세린 디글리시딜에테르로 이루어진 군으로부터 선택된 하나 이상을 들 수 있으며; 아지리딘계 화합물의 예로는 N,N’-톨루엔-2,4-비스(1-아지리딘카르복사미드), N,N’-디페닐메탄-4,4’-비스(1-아지리딘카르복사미드), 트리에틸렌 멜라민, 비스이소프로탈로일-1-(2-메틸아지리딘) 및 트리-1-아지리디닐포스핀옥시드로 이루어진 군으로부터 선택된 하나 이상을 들 수 있다. 또한, 상기 금속 킬레이트계 화합물의 예로는, 알루미늄, 철, 아연, 주석, 티탄, 안티몬, 마그네슘 및/또는 바나듐과 같은 다가 금속이 아세틸 아세톤 또는 아세토초산 에틸 등에 배위하고 있는 화합물을 사용할 수 있으나, 이에 제한되는 것은 아니다.
본 발명에서 상기 다관능성 가교제는 베이스 수지 100 중량부에 대하여, 0.01 중량부 내지 10 중량부, 바람직하게는 0.01 중량부 내지 5 중량부로 포함될 수 있다. 본 발명에서 다관능성 가교제의 함량이 0.01 중량부 미만이면, 경화물의 응집력이 떨어져 고온 신뢰성 측정시 기포가 발생할 우려가 있고, 10 중량부를 초과하면, 점착제의 경화도가 너무 높아 접착력 및 박리력이 저하되어, 층간 박리나 들뜸 현상이 발생하는 등 내구신뢰성이 저하될 우려가 있다
본 발명의 점착제 조성물은 또한 전술한 성분에 추가로 실란계 커플링제를 포함할 수 있다. 이와 같은 커플링제는 경화물 및 피착체, 특히 유리 기판간의 밀착성 및 접착 안정성을 향상시켜, 내열성 및 내습성을 개선할 수 있다. 또한, 상기 실란계 커플링제는 적절히 첨가될 경우, 경화물의 고온 및/또는 고습 하에서의 접착 신뢰성을 향상시킬 수 있다.
본 발명에서 사용할 수 있는 실란계 커플링제의 종류는 특별히 한정되지 않으며, 예를 들면 γ-글리시독시프로필트리메톡시 실란, γ-글리시독시프로필메틸디에톡시 실란, γ-글리시독시프로필트리에톡시 실란, 3-머캅토프로필트리메톡시 실란, 비닐트리메톡시 실란, 비닐트리에톡시 실란, γ-메타크릴록시프로필트리메톡시 실란, γ-메타크릴록시프로필트리에톡시 실란, γ-아미노프로필트리메톡시 실란, γ-아미노프로필트리에톡시 실란, 3-이소시아네이트프로필트리에톡시 실란 또는 γ-아세토아세테이트프로필트리메톡시 실란 등의 일종 또는 이종 이상의 혼합을 사용할 수 있다.
본 발명에서, 상기 실란계 커플링제는 베이스 수지 100 중량부에 대하여 0.005 중량부 내지 5 중량부로 점착제 조성물에 포함될 수 있다. 실란계 커플링제의 함량이 0.005 중량부 미만이면, 커플링제의 첨가로 인한 효과가 미미할 우려가 있고, 5 중량부를 초과하면, 기포 또는 박리 현상이 발생하는 등 내구신뢰성이 저하될 우려가 있다.
본 발명의 점착제 조성물은 또한, 점착 성능의 조절의 관점에서, 점착성 부여 수지를 추가로 포함할 수 있다.
본 발명에서 사용할 수 있는 점착성 부여 수지의 종류는 특별히 한정되지 않으며, 예를 들면 히드로카본계 수지 또는 그 수소첨가물; 로진 수지 또는 그 수소첨가물; 로진 에스테르 수지 또는 그 수소첨가물; 테르펜 수지 또는 그 수소첨가물; 테르펜 페놀 수지 또는 그 수소첨가물; 중합 로진 수지 또는 중합 로진 에스테르 수지 등의 일종 또는 이종 이상의 혼합물을 사용할 수 있다.
본 발명에서 상기 점착성 부여 수지는, 베이스 수지 100 중량부에 대하여, 1 중량부 내지 100 중량부의 양으로 포함될 수 있다. 상기 함량이 1 중량부 미만이면, 점착성 부여 수지의 첨가로 인한 효과가 미미할 우려가 있고, 100 중량부를 초과하면, 상용성 또는 응집력 향상 효과가 저하될 우려가 있다.
본 발명의 점착제 조성물은 또한, 발명의 효과에 영향을 미치지 않는 범위에서, 에폭시 수지, 가교제, 자외선 안정제, 산화 방지제, 조색제, 보강제, 충진제, 소포제, 계면 활성제 및 가소제로 이루어진 군으로부터 선택된 하나 이상의 첨가제를 추가로 추가로 포함할 수 있다.
본 발명은 또한, 전술한 본 발명에 따른 점착제 조성물의 경화물을 포함하는 점착제층을 가지는 터치 패널용 점착시트에 관한 것이다.
첨부된 도 3은 본 발명의 일 태양에 따른 점착시트(30)의 단면도를 나태내는 도면이다. 본 발명의 점착시트(30)는 도 3에 나타난 바와 같이, 본 발명의 점착제 조성물의 시트상 경화물을 포함하는 점착제층(11)을 가진다.
본 발명에서 점착제 조성물을 경화시켜, 상기 점착제층을 제조하는 방법은 특별히 제한되지 않는다. 본 발명에서는, 예를 들면 상기 점착제 조성물 또는 그를 사용하여 제조한 코팅액을, 바코터 등의 통상의 수단으로 적절한 공정 기재에 도포하고, 경화시키는 방법으로 점착제층을 제조할 수 있다.
본 발명에서 상기 경화 과정은, 점착제 조성물 또는 코팅액 내부에 포함된 휘발 성분 또는 반응 잔류물과 같은 기포 유발 성분을 충분히 제거한 후, 수행하는 것이 바람직하다. 이에 따라 점착제의 가교 밀도 또는 분자량 등이 지나치게 낮아 탄성률이 떨어지고, 고온 상태에서 점착 계면에 존재하는 기포들이 커져 내부에서 산란체를 형성하는 문제점 등을 방지할 수 있다.
또한, 상기에서 점착제 조성물 또는 코팅액을 경화시키는 방법은 특별히 한정되지 않고, 예를 들면, 코팅층에 적절한 열을 인가하거나, 소정 조건에서 숙성(aging)하는 공정을 거쳐 경화 공정을 수행할 수 있다.
본 발명의 점착시트에서 상기와 같이 형성된 점착제층은 두께가 15㎛ 내지 60㎛, 바람직하게는 20㎛ 내지 60㎛일 수 있다. 본 발명에서는 점착제층의 두께를 전술한 범위로 제어함으로써, 박형의 터치패널 또는 터치스크린에 적용 가능하면서도, 우수한 내열성, 광특성, 재단성, 작업성, 젖음성 및 내구성 등을 가지는 점착 시트를 제공할 수 있다.
본 발명의 점착시트는, 필요에 따라서 상기 점착제층의 일면 또는 양면에 형성된 이형 필름을 추가로 포함할 수 있다. 첨부된, 도 4는 본 발명의 다른 태양에 따른 점착시트를 나타내는 도면으로, 도 4에 나타난 바와 같이, 본 발명의 점착 시트(40)는 상기 점착제층(11)의 양면에 형성된 이형 필름(41a, 41b)을 추가로 포함할 수 있다.
본 발명에서 사용되는 상기 이형 필름의 구체적인 종류는 특별히 한정되지 않고, 예를 들면, 이 분야의 일반적인 플라스틱 필름을 사용할 수 있다. 본 발명에서는, 예를 들면, 상기 이형 필름으로서, 폴리에틸렌테레프탈레이트 필름, 폴리테트라플로오루에틸렌 필름, 폴리에틸렌 필름, 폴리프로필렌 필름, 폴리부텐 필름, 폴리부타디엔 필름, 염화비닐 공중합체 필름, 폴리우레탄 필름, 에틸렌-비닐 아세테이트 필름, 에틸렌-프로필렌 공중합체 필름, 에틸렌-아크릴산 에틸 공중합체 필름, 에틸렌-아크릴산 메틸 공중합체 필름 또는 폴리이미드 필름 등을 사용할 수 있다. 또한, 본 발명의 상기 이형 필름의 일면 또는 양면에는 적절한 이형 처리를 수행할 수도 있다. 이형 처리에 사용되는 이형제의 예로는 알키드계, 실리콘계, 불소계, 불포화 에스테르계, 폴리올레핀계 또는 왁스계 등을 사용할 수 있고, 이 중 내열성 측면에서 알키드계, 실리콘계 또는 불소계 이형제를 사용하는 것이 바람직하지만, 이에 제한되는 것은 아니다.
본 발명에서 상기와 같은 이형 필름의 두께는 특별히 한정되지 않고, 적용되는 용도에 따라서 적절히 선택될 수 있다. 예를 들면, 본 발명에서 상기 이형 필름의 두께는 20 ㎛ 내지 80 ㎛, 바람직하게는 30 ㎛ 내지 70 ㎛ 정도일 수 있다.
본 발명은 또한, 투명 플라스틱 기판; 및 상기 투명 플라스틱 기판의 상부에 형성되고, 전술한 본 발명에 따른 점착제 조성물의 경화물을 포함하는 점착제층을 가지는 터치 패널에 관한 것이다.
본 발명의 터치 패널의 구체적인 구조는, 본 발명에 따른 점착제 조성물을 사용하여 구성되는 한, 특별히 제한되지 않는다.
첨부된 도 5는, 본 발명의 일 태양에 따라서 구성된 터치 패널을 예시적으로 나타낸 도면이다.
도 5 에 나타난 바와 같이, 본 발명에 따른 점착제층(11)을 윈도우 필름(51), 전도성 적층체(53) 및 투명 플라스틱 기판(54)의 부착에 사용하여 본 발명의 터치 패널(50)을 구성할 수 있다.
도 5에 나타난 바와 같이, 본 발명의 터치 패널(50)은 본 발명에 따른 점착제층(11)을 이용하여 전도성 적층체(53)의 하부에 투명 플라스틱 기판(54)이 부착되고, 기재 필름(52a)의 양면에 본 발명에 따른 점착제층(11)을 형성시켜 제조한 양면 점착시트(52)를 이용하여 상기 전도성 적층체(53)의 상부에 윈도우 필름(51)이 적층된 구조를 가질 수 있다. 상기에서 전도성 적층체(53)는, 일면에 도전층(53e)이 형성된 2 장의 투명 전도성 플라스틱 필름(53c, 53d)이 상기 도전층(53e)이 서로 대향되도록 이격 배치되어, 양면 점착테이프(DAT)(53d)의 양면에 부착된 은 페이스트층(53c)을 통해 적층되어 있을 수 있다.
도 5에 나타난 구조의 터치패널(50)에서 투명 플라스틱 기판(54)으로는, 예를 들면, 폴리카보네이트계 투명 기판, 아크릴 수지계 투명 기판(ex. 폴리메틸메타크릴레이트 투명 기판), 폴리에스테르계 투명 기판(ex. 폴리에틸렌테레프탈레이트 투명 기판) 또는 트리아세틸셀룰로오스계 투명 기판 등을 들 수 있으며, 이 중 폴리카보네이트계 투명 기판을 사용하는 것이 바람직하지만, 이에 제한되는 것은 아니다.
상기와 같은 투명 플라스틱 기판은 단독으로 또는 2종 이상이 조합되어 사용될 수 있고, 상기 기판은 단층 형태이거나, 2층 이상의 다층 형태로 구성될 수 있다.
본 발명에서, 상기 투명 플라스틱 기판의 두께는 특별히 제한되지 않는다. 특히, 본 발명의 점착제는, 전술한 바와 같은 탁월한 내열성을 가지기 때문에, 상기 투명 플라스틱 기판의 두께를 얇게 구성하는 경우에도, 고온 조건 등에서의 휨이나 컬 등의 발생을 방지할 수 있다. 본 발명에서 상기 투명 플라스틱 기판은, 예를 들면, 약 100 ㎛ 내지 3.0 mm, 바람직하게는 약 250 ㎛ 내지 2.0 mm, 보다 바람직하게는 약 500 ㎛ 내지 1.0 mm의 두께를 가질 수 있다.
본 발명에서, 상기 터치패널(50)을 구성하는 각 소재, 즉 윈도우 필름, 투명 전도성 플라스틱 필름, 기재 필름, 양면 점착테이프 또는 은 페이스트 등의 종류는 특별히 제한되지 않고, 이 분야에서 공지되어 있는 소재를 제한 없이 채용할 수 있다.
[실시예]
이하 본 발명에 따르는 실시예 및 본 발명에 따르지 않는 비교예를 통하여 본 발명을 보다 상세히 설명하나, 본 발명의 범위가 하기 제시된 실시예에 의해 제한되는 것은 아니다.
제조예 1. 아크릴계 수지(A)의 제조
질소 가스가 환류되고, 온도 조절이 용이하도록 냉각 장치를 설치한 1L 반응기에, 부틸 아크릴레이트(BA) 65 중량부, 메틸 아크릴레이트(MA) 25 중량부 및 아크릴산(AA) 10 중량부를 포함하는 단량체 혼합물을 투입한 다음, 용제로서 에틸 아세테이트(EAc) 100 중량부를 투입하였다. 이어서, 산소 제거를 위해 질소 가스를 1 시간 정도 퍼징하고, 온도를 62℃로 유지한 상태에서, 혼합물을 균일하게 한 다음, 반응 개시제로서 에틸 아세테이트에 50%의 농도로 희석시킨 아조비스이소부티로니트릴(AIBN) 0.03 중량부를 투입하였다. 이어서, 상기 혼합물을 8 시간 정도 반응시켜 중량평균분자량이 120만인 아크릴계 수지(A)를 제조하였다.
제조예 2. 아크릴계 수지(B)의 제조
제조예 1의 경우와 동일한 단량체 조성을 사용하되, 반응 개시제의 함량 등의 반응 조건을 적절히 조절하여, 중량평균분자량이 150만인 아크릴계 수지(B)를 제조하였다.
제조예 3. 아크릴계 수지(C)의 제조
제조예 1의 경우와 동일한 단량체 조성을 사용하되, 반응 개시제의 함량 등의 반응 조건을 적절히 조절하여, 중량평균분자량이 70만인 아크릴계 수지(C)를 제조하였다.
제조예 4. 아크릴계 수지(D)의 제조
제조예 1의 경우와 동일한 단량체 조성을 사용하되, 반응 개시제의 함량 등의 반응 조건을 적절히 조절하여, 중량평균분자량이 80만인 아크릴계 수지(D)를 제조하였다.
제조예 5. 아크릴계 저분자량체(E)의 제조
단량체 혼합물로서, 시클로헥실 메타크릴레이트(CHMA) 90 중량부 및 아크릴산(AA) 10 중량부를 포함하는 혼합물을 사용하고, 제조예 1의 제조 조건을 적절히 변경 채용하여, 중량평균분자량이 5000인 아크릴계 저분자량체(E)를 제조하였다.
실시예 1.
제조예 1에서 제조된 아크릴계 수지(A) 100 중량부에 대하여, 다관능성 가교제로서, 2관능성 아지리딘계 가교제 0.4 중량부를 배합하여 점착제 조성물을 제조하고, 이를 용제로 적절히 희석하여 코팅액을 제조하였다. 이어서, 제조된 코팅액을 이형처리된 폴리에틸렌테레프탈레이트(PET) 필름(두께: 50 ㎛)의 이형처리면에 건조 후 두께가 약 50 ㎛가 되도록 코팅하였다. 그 후, 약 100 ℃의 온도에서 약 5 분 이상 건조시키고, 적정 조건에서 숙성시켜 두께가 50 ㎛인 점착제층을 형성하였다. 이어서, 점착제층 상에 두께가 50 ㎛이고, 이형처리가 수행된 PET 필름을 이형처리면이 점착제층에 부착되도록 압착하여, 점착 시트를 제조하였다.
실시예 2.
제조예 2에서 제조된 아크릴계 수지(B) 100 중량부에 대하여, 다관능성 가교제로서, 2관능성 아지리딘계 가교제 0.4 중량부를 배합하여 점착제 조성물을 제조한 것을 제외하고는, 실시예 1과 동일한 방법으로 점착시트를 제조하였다.
비교예 1.
제조예 3에서 제조된 아크릴계 수지(C) 100 중량부에 대하여, 다관능성 가교제로서, 2관능성 아지리딘계 가교제 0.4 중량부를 배합하여 점착제 조성물을 제조한 것을 제외하고는, 실시예 1과 동일한 방법으로 점착시트를 제조하였다.
비교예 2.
제조예 4에서 제조된 아크릴계 수지(D) 100 중량부에 대하여, 제조예 5에서 제조된 아크릴계 저분자량체(E) 20 중량부, 다관능성 가교제로서, 2관능성 아지리딘계 가교제 0.4 중량부를 배합하여 점착제 조성물을 제조한 것을 제외하고는, 실시예 1과 동일한 방법으로 점착시트를 제조하였다.
실시예 및 비교예에서 제조된 점착시트에 대하여, 하기 제시된 방법으로 그 물성을 측정하였다.
1. 동적 전단력
점착제의 동적 전단력은 도 1에 나타난 바와 같은 방식으로 평가하였다. 구체적으로, 실시예 및 비교예에서 제조된 점착 시트를 1 in × 1 in × 50 ㎛(가로×세로×두께)의 크기로 재단하였다. 이어서, 이형 필름을 박리하고, 점착제층(11)을 유리 기판(12) 및 일면에 ITO 면이 형성된 PET 필름, 즉 ITO PET 필름(15)의 사이에 도 1에 나타난 바와 같이 부착시켰다. 이 때, 점착제의 부착은 ASTM D1002에 근거하여, 2 Kg의 롤러를 5회 왕복 하여 수행하였다. 그 후, 140 ℃의 온도에서 인장 시험기를 사용하여, 상기 ITO PET 필름(15) 및 유리 기판(12)을 도 1에 나타난 화살표 방향으로 각각 0.8 mm/sec의 크로스헤드 속도로 인장하면서, ITO PET 필름(15) 또는 유리 기판(12)이 점착제(11)로부터 분리되는 시점에서의 동적 전단력을 평가하였다.
2. 정적 전단 유지시간
점착제의 정적 전단 유기시간은 도 2에 나타난 바와 같은 시편을 제조하여 평가하였다. 구체적으로, 실시예 및 비교예에서 제조된 점착 시트를 1 in × 1 in × 50 ㎛(가로×세로×두께)의 크기로 재단하였다. 그 후, 이형 필름을 박리하고, 점착제층(11)을 유리 기판(12) 및 ITO PET 필름(15)의 사이에 도 2에 나타난 바와 같이 부착시켰다. 이 때, 점착제층(11)의 부착은 ASTM D1002에 근거하여, 2 Kg의 롤러를 5회 왕복하여 수행하였다. 그 후, 140 ℃의 온도에서 상기 ITO PET 필름(15)에 2 Kg의 추(21)를 단 후, 상기 ITO PET 필름(15) 또는 유리 기판(12)이 점착제(11)로부터 분리되는 시점의 시간을 측정하여, 정적 전단 유지시간을 측정하였다.
3. 재단성
실시예 및 비교예에서 제조된 점착 시트를 10 cm × 10 cm (가로×세로)의 크기로 재단한 후, 칼을 이용해 상기 시편의 중앙부의 위치를 십자 모양으로 그어 절단한 후, 상기 절단 부위를 기준으로 양면에서 점착 시트를 벌릴 때에, 발생하는 소섬유(fibril)의 양을 측정하여 하기 기준으로 재단성을 평가하였다.
<재단성 평가 기준>
◎: 소섬유(fibril)가 발생하지 않음
○: 소섬유(fibril)가 약간 발생
△: 소섬유(fibril)가 상당히 발생
X: 소섬유(fibril)가 다량 발생
4. 휨 특성 평가
실시예 및 비교예에서 제조된 점착시트에서 이형 필름을 제거하고, 점착제층을 하드코팅층이 일면에 형성된 폴리카보네이트 필름의 하드코팅면에 부착하고, 다시 일면에 ITO층이 형성된 PET 필름을 상기 ITO층이 점착제층에 부착되도록 압착하여 시편을 제작하였다. 그 후, 제작된 시편을 140℃의 오븐에서 24시간 동안 방치한 다음, 휨(curl) 발생 정도를 비교하여, 하기 기준으로 휨 특성을 평가하였다.
<휨 특성 평가 기준>
◎: 기준면으로부터 휨 발생 높이가 5mm 미만
○: 기준면으로부터 휨 발생 높이가 7mm 미만
△: 기준면으로부터 휨 발생 높이가 9mm 미만
X: 기준면으로부터 휨 발생 높이가 11mm 미만
5. 내구성 측정
실시예 및 비교예에서 제조된 점착시트에서 이형 필름을 제거하고, 하드코팅된 폴리카보네이트 필름의 하드코팅면에 점착제층을 부착하였다. 그 후, 일면에 ITO층이 형성된 PET 필름을 상기 ITO층이 점착제층에 부착되도록 압착하여 시편을 제작하였다. 그 후, 상기 시편을 80℃의 오븐에서 24시간 동안 방치한 후, 기포, 들뜸 및/또는 에어 포켓 발생 여부를 관찰하여 내구성을 평가하였다. 또한, 상기 시편을 140℃의 오븐에서 24시간 동안 방치한 후, 동일한 방법으로 그 내구성을 평가하였다.
<내구성 평가 기준>
◎: 들뜸, 박리 또는 기포의 발생이 전혀 없음
○: 들뜸, 박리 또는 기포의 발생이 약간 있음
△: 들뜸, 박리 또는 기포의 발생이 상당히 있음
X: 들뜸, 박리 또는 기포의 발생이 많이 있음
6. 점착제의 스며나옴 평가
실시예 및 비교예에서 제조된 점착 시트를 5 cm × 5 cm (가로×세로)의 크기로 재단하였다. 그 후, 140℃에서 점착 시트의 이형 필름면에 8 kg의 추를 12 시간 동안 가압하고, 테두리에 점착제가 스며나오는지를 관찰하여 평가하였다.
<스며나옴 특성 평가 기준>
○ : 테두리로부터 점착제가 스며나오지 않음
X: 테두리로부터 점착제가 스며나옴
상기와 같은 물성 측정 결과를 하기의 표 1에 정리하여 기재하였다.
표 1
구분 실시예 비교예
1 2 1 2
동적 전단력(kg/cm2) 9.2 7.0 5.0 1.5
정적 전단 유지시간(분) 40 20 3 1
재단성 ◎ ◎ △ ○
휨 특성 ◎ ◎ △ ○
내구성(80℃) ◎ ◎ ○ ○
내구성(140℃) ○ ◎ X X
점착제 스며나옴 ○ ○ X X
상기 표 1의 결과로부터 알 수 있는 바와 같이, 본 발명의 실시예의 경우, 우수한 재단성을 가지면서, 고온 조건에서의 내구성 및 휨 특성이 모두 우수하고, 점착제의 스며나옴도 발생하지 않았다. 반면, 비교예의 경우, 재단성, 휨 특성 및 내구성이 모두 열악하였고, 점착제의 스며나옴도 다량 유발됨을 확인할 수 있었다.

Claims (16)

  1. 베이스 수지; 및 다관능성 가교제를 포함하고,
    하기 일반식 1의 조건을 만족하는 점착제 조성물:
    [일반식 1]
    X1 ≥ 6 Kg/cm2
    상기 일반식 1에서 X1은 상기 점착제 조성물의 시트상 경화물인 점착제의 일면을 ITO PET 필름에서 ITO 면의 반대면에 부착하고, 그 다른 면을 유리 기판에 부착한 후, 상온에서 24시간 동안 방치한 다음, 140℃의 온도에서 0.8 mm/sec의 크로스헤드 속도로 측정한 동적 전단강도를 나타낸다.
  2. 제 1 항에 있어서,
    X1이 6.5 kg/cm2 내지 15 kg/cm2인 점착제 조성물.
  3. 제 1 항에 있어서,
    하기 일반식 2의 조건을 만족하는 점착제 조성물:
    [일반식 2]
    X2 ≥ 10 분
    상기 일반식 2에서 X2는 상기 점착제 조성물의 시트상 경화물인 점착제의 일면을 ITO PET 필름에서 ITO 면의 반대면에 부착하고, 그 다른 면을 유리 기판에 부착한 후, 상온에서 24시간 동안 방치한 다음, 140℃의 온도에서 상기 ITO PET 필름에 2 kg의 하중을 인가하여 측정한 유지 시간을 의미한다.
  4. 제 3 항에 있어서,
    X2가 15 분 내지 50 분인 점착제 조성물.
  5. 제 1 항에 있어서,
    베이스 수지는 중량평균분자량이 100만 이상인 아크릴계 수지인 점착제 조성물.
  6. 제 5 항에 있어서,
    아크릴계 수지는 (메타)아크릴산 에스테르계 단량체 및 가교성 단량체를 포함하는 단량체 혼합물의 중합체인 점착제 조성물.
  7. 제 6 항에 있어서,
    가교성 단량체가 히드록실기 함유 단량체, 카복실기 함유 단량체 또는 질소 함유 단량체인 점착제 조성물.
  8. 제 1 항에 있어서,
    다관능성 가교제는 이소시아네이트 화합물, 에폭시 화합물, 아지리딘 화합물 및 금속 킬레이트 화합물로 이루어진 군으로부터 선택된 하나 이상인 점착제 조성물.
  9. 제 1 항에 있어서,
    다관능성 가교제는 베이스 수지 100 중량부에 대하여 0.01 중량부 내지 10 중량부로 포함되는 점착제 조성물.
  10. 제 1 항에 있어서,
    실란 커플링제를 추가로 포함하는 점착제 조성물.
  11. 제 1 항에 있어서,
    점착성 부여 수지를 추가로 포함하는 점착제 조성물.
  12. 제 1 항 내지 제 11 항 중 어느 한 항에 따른 점착제 조성물의 경화물을 포함하는 점착제층을 가지는 터치 패널용 점착시트.
  13. 제 12 항에 있어서,
    점착제층은 두께가 15 ㎛ 내지 60 ㎛인 터치 패널용 점착시트.
  14. 제 12 항에 있어서,
    점착제층의 일면 또는 양면에 형성된 이형 필름을 추가로 포함하는 터치 패널용 점착시트.
  15. 투명 플라스틱 기판; 및
    상기 투명 플라스틱 기판의 상부에 형성되고, 제 1 항 내지 제 11 항 중 어느 한 항에 따른 점착제 조성물의 경화물을 포함하는 점착제층을 가지는 터치 패널.
  16. 제 15 항에 있어서,
    투명 플라스틱 기판이 폴리카보네이트계 기판인 터치 패널.
PCT/KR2011/002356 2010-04-05 2011-04-05 점착제 조성물, 점착시트 및 터치 패널 Ceased WO2011126263A2 (ko)