WO2012109651A9 - Délignification et désagrégation simultanées d'une biomasse - Google Patents

Délignification et désagrégation simultanées d'une biomasse Download PDF

Info

Publication number
WO2012109651A9
WO2012109651A9 PCT/US2012/024871 US2012024871W WO2012109651A9 WO 2012109651 A9 WO2012109651 A9 WO 2012109651A9 US 2012024871 W US2012024871 W US 2012024871W WO 2012109651 A9 WO2012109651 A9 WO 2012109651A9
Authority
WO
WIPO (PCT)
Prior art keywords
biomass
solvent
cellulose
alkali
lignin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2012/024871
Other languages
English (en)
Other versions
WO2012109651A1 (fr
Inventor
Rajai ATALLA
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CELLULOSE SCIENCES INTERNATIONAL Inc
Original Assignee
CELLULOSE SCIENCES INTERNATIONAL Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CELLULOSE SCIENCES INTERNATIONAL Inc filed Critical CELLULOSE SCIENCES INTERNATIONAL Inc
Publication of WO2012109651A1 publication Critical patent/WO2012109651A1/fr
Publication of WO2012109651A9 publication Critical patent/WO2012109651A9/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne des procédés et des systèmes de traitement d'une matière lignocellulosique ou d'une biomasse contenant une matière lignocellulosique pour délignifier la matière ou biomasse et la rendre plus accessible pour une modification enzymatique ou chimique. Le système et les procédés consistent à traiter une matière ou biomasse contenant de la lignocellulose avec un alcali dans un système de co-solvants alcool/eau à titre d'exemple. Le traitement désagrège la matière lignocellulosique et en même temps délignifie la matière de départ ou le substrat. L'invention concerne également une fraction liquide contenant une composition de lignine comportant la lignine sous une forme plus proche de son état natif que dans n'importe quelle procédure de laboratoire connue.
PCT/US2012/024871 2011-02-11 2012-02-13 Délignification et désagrégation simultanées d'une biomasse Ceased WO2012109651A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201161442066P 2011-02-11 2011-02-11
US61/442,066 2011-02-11

Publications (2)

Publication Number Publication Date
WO2012109651A1 WO2012109651A1 (fr) 2012-08-16
WO2012109651A9 true WO2012109651A9 (fr) 2013-03-21

Family

ID=45809605

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2012/024871 Ceased WO2012109651A1 (fr) 2011-02-11 2012-02-13 Délignification et désagrégation simultanées d'une biomasse

Country Status (1)

Country Link
WO (1) WO2012109651A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108680657A (zh) * 2018-03-23 2018-10-19 中国农业科学院北京畜牧兽医研究所 蒸汽爆破技术降低秸秆中玉米赤霉烯酮含量的方法及应用

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009124240A1 (fr) 2008-04-03 2009-10-08 Cellulose Sciences International, Inc. Cellulose hautement désordonnée
RU2013117010A (ru) 2010-09-14 2014-10-20 Сельюлоуз Сайенсиз Интернэшнл, Инк. Нано-дезагрегированная целлюлоза
FI3137553T3 (fi) 2014-05-01 2025-02-11 Renmatix Inc Ligniinin jalostaminen ligniinipitoisista jäännöksistä reaktiivisen uuton avulla

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1079008A (fr) 1975-10-24 1980-06-10 Cp Associates Limited Procede de fabrication de pate a papier au solvant
US4395543A (en) * 1981-08-12 1983-07-26 Massachusetts Institute Of Technology Selective solvent extraction of cellulosic material
WO2009124240A1 (fr) * 2008-04-03 2009-10-08 Cellulose Sciences International, Inc. Cellulose hautement désordonnée
AT510346A1 (de) * 2010-09-02 2012-03-15 Annikki Gmbh Ligningewinnung
RU2013117010A (ru) * 2010-09-14 2014-10-20 Сельюлоуз Сайенсиз Интернэшнл, Инк. Нано-дезагрегированная целлюлоза

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108680657A (zh) * 2018-03-23 2018-10-19 中国农业科学院北京畜牧兽医研究所 蒸汽爆破技术降低秸秆中玉米赤霉烯酮含量的方法及应用

Also Published As

Publication number Publication date
WO2012109651A1 (fr) 2012-08-16

Similar Documents

Publication Publication Date Title
US8617851B2 (en) Highly disordered cellulose
Bhatia et al. Production of oligosaccharides and biofuels from Miscanthus using combinatorial steam explosion and ionic liquid pretreatment
Zhao et al. Fast enzymatic saccharification of switchgrass after pretreatment with ionic liquids
Modenbach et al. Enzymatic hydrolysis of biomass at high-solids loadings–a review
Wu et al. Fenton reaction-oxidized bamboo lignin surface and structural modification to reduce nonproductive cellulase binding and improve enzyme digestion of cellulose
Monlau et al. Lignocellulosic materials into biohydrogen and biomethane: impact of structural features and pretreatment
EP2340293B1 (fr) Procédé de production d'huile biologique
Chen et al. Improved xylan hydrolysis of corn stover by deacetylation with high solids dilute acid pretreatment
Haque et al. Effect of dilute alkali on structural features and enzymatic hydrolysis of barley straw (Hordeum vulgare) at boiling temperature with low residence time.
Zhang et al. Stimulatory effect of in-situ detoxification on bioethanol production by rice straw
WO2010059796A2 (fr) Procédé de préparation d'une solution de sucres par saccharification chimique et enzymatique combinée d'une biomasse enrichie en polysaccharides
WO2011063484A1 (fr) Procédé de traitement de biomasse végétale
US9187571B2 (en) Nano-deaggregated cellulose
Liao et al. Production of monosaccharides from poplar by a two-step hydrogen peroxide-acetic acid and sodium hydroxide pretreatment
Valladares-Diestra et al. The potential of imidazole as a new solvent in the pretreatment of agro-industrial lignocellulosic biomass
Meng et al. Alkaline deacetylation-aided hydrogen peroxide-acetic acid pretreatment of bamboo residue to improve enzymatic saccharification and bioethanol production
WO2012109651A9 (fr) Délignification et désagrégation simultanées d'une biomasse
Fan et al. Unveiling the role of lignin feature on bio-ethanol and xylose derived from poplar during combined alkali/ethanol synergistic pretreatment
Corredor Pretreatment and enzymatic hydrolysis of lignocellulosic biomass
US8883469B2 (en) Method for producing ethanol by fermentation from lignocellulosic biomass
Smuga-Kogut et al. Influence of the crystalline structure of cellulose on the production of ethanol from lignocellulose biomass
Patil et al. Bioethanol production from agricultural biomass: Sources of cellulose, pretreatment methods, and future prospects
Qin High consistency enzymatic hydrolysis of lignocellulose
HK1153239B (en) Highly disordered cellulose
Sathitsuksanoh et al. Solvent fractionation of lignocellulosic biomass

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12707177

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12707177

Country of ref document: EP

Kind code of ref document: A1