WO2012169768A9 - Nanoparticules conductrices multicouches et leur procédé de production - Google Patents

Nanoparticules conductrices multicouches et leur procédé de production Download PDF

Info

Publication number
WO2012169768A9
WO2012169768A9 PCT/KR2012/004437 KR2012004437W WO2012169768A9 WO 2012169768 A9 WO2012169768 A9 WO 2012169768A9 KR 2012004437 W KR2012004437 W KR 2012004437W WO 2012169768 A9 WO2012169768 A9 WO 2012169768A9
Authority
WO
WIPO (PCT)
Prior art keywords
conductive
conductive nanoparticles
core
emulsion
shell
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2012/004437
Other languages
English (en)
Korean (ko)
Other versions
WO2012169768A3 (fr
WO2012169768A2 (fr
Inventor
김중현
김병욱
이선종
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KOREA NTCHEM CO Ltd
Original Assignee
KOREA NTCHEM CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KOREA NTCHEM CO Ltd filed Critical KOREA NTCHEM CO Ltd
Priority to CN201280028291.4A priority Critical patent/CN103608284B/zh
Publication of WO2012169768A2 publication Critical patent/WO2012169768A2/fr
Publication of WO2012169768A9 publication Critical patent/WO2012169768A9/fr
Publication of WO2012169768A3 publication Critical patent/WO2012169768A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Cette invention concerne des nanoparticules conductrices multicouches et leur procédé de production, et plus spécifiquement, une nanoparticule conductrice, à structure multicouche comprenant un cœur et plus d'une couche de coque. La nanoparticule conductrice, multicouche est revêtue de plus d'une couche de polymère électroluminescent et conducteur qui fait figure de coque pour la particule polymère conductrice qui, à son tour, fait figure de cœur. Cette invention concerne également leur procédé de production. Les nanoparticules conductrices multicouches selon cette invention font preuve d'une conductivité électrique élevée, la durée du procédé de fabrication du cœur et de plus d'une couche de coque est considérablement réduite, leurs avantages économiques sont démontrés, et leur luminance, aptitude à la mise en œuvre, dispersibilité, élasticité et étirabilité sont toutes excellentes.
PCT/KR2012/004437 2011-06-07 2012-06-05 Nanoparticules conductrices multicouches et leur procédé de production Ceased WO2012169768A2 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN201280028291.4A CN103608284B (zh) 2011-06-07 2012-06-05 多层结构的导电性纳米粒子及其制造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020110054543A KR101890308B1 (ko) 2011-06-07 2011-06-07 다층구조의 전도성 나노입자 및 이의 제조방법
KR10-2011-0054543 2011-06-07

Publications (3)

Publication Number Publication Date
WO2012169768A2 WO2012169768A2 (fr) 2012-12-13
WO2012169768A9 true WO2012169768A9 (fr) 2013-02-14
WO2012169768A3 WO2012169768A3 (fr) 2013-04-04

Family

ID=47296579

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2012/004437 Ceased WO2012169768A2 (fr) 2011-06-07 2012-06-05 Nanoparticules conductrices multicouches et leur procédé de production

Country Status (4)

Country Link
KR (1) KR101890308B1 (fr)
CN (1) CN103608284B (fr)
TW (1) TW201307189A (fr)
WO (1) WO2012169768A2 (fr)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105131901A (zh) * 2015-07-15 2015-12-09 哈尔滨工业大学 均匀核壳复合材料PPy@PANI及其制备方法
KR102463420B1 (ko) 2017-11-02 2022-11-03 현대자동차주식회사 고분자 전해질 연료전지용 전극의 제조방법 및 이에 의해 제조된 전극
FR3095651B1 (fr) * 2019-05-02 2021-12-03 Univ De Pau Et Des Pays De L’Adour Particules nanocomposites conductrices étirables
CN112126375B (zh) * 2020-09-23 2022-07-08 惠科股份有限公司 导电粒子及其制备方法、粘合剂及其应用

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6013404A (en) * 1998-10-09 2000-01-11 Xerox Corporation Toner composition and processes thereof
KR100586659B1 (ko) * 2004-04-01 2006-06-07 주식회사 디피아이 솔루션스 유기 전극 코팅용 조성물 및 이를 이용한 고투명성 유기전극의 제조방법
KR100684913B1 (ko) * 2005-10-06 2007-02-20 연세대학교 산학협력단 티오펜 에멀젼의 산화중합에 의한 폴리티오펜 나노입자와이의 유도체 및 이의 제조방법
KR20070095553A (ko) * 2006-03-21 2007-10-01 삼성전자주식회사 전도성 투명 재료 및 그 제조방법 및 이를 포함하는표시장치
KR100869572B1 (ko) * 2007-01-31 2008-11-21 연세대학교 산학협력단 코어 셀 나노입자 및 이의 제조방법
KR101050523B1 (ko) * 2008-04-04 2011-07-20 주식회사 제이앤드제이 캐미칼 비닐계 또는 아크릴계 고분자 코어 및 전도성 고분자 쉘을 포함하는 코어-쉘 구조의 나노입자의 제조방법
KR101003531B1 (ko) * 2008-07-03 2010-12-28 주식회사 제이앤드제이 캐미칼 폴리티오펜 또는 폴리티오펜 유도체가 전도성 유화제로둘러싸여 있는 나노입자 및 그 제조방법
KR20110050136A (ko) * 2009-11-06 2011-05-13 서울대학교산학협력단 실리카/폴리아닐린 코어/셀 나노입자를 이용한 전기유변유체 및 그 제조방법

Also Published As

Publication number Publication date
CN103608284B (zh) 2016-09-21
CN103608284A (zh) 2014-02-26
KR20120135691A (ko) 2012-12-17
TW201307189A (zh) 2013-02-16
WO2012169768A3 (fr) 2013-04-04
KR101890308B1 (ko) 2018-08-21
WO2012169768A2 (fr) 2012-12-13

Similar Documents

Publication Publication Date Title
US7105237B2 (en) Substituted thieno[3,4-B]thiophene polymers, method of making, and use thereof
Jeon et al. A facile and rapid synthesis of unsubstituted polythiophene with high electrical conductivity using binary organic solvents
TWI300419B (en) Process for the preparation of neutral polyethylenedioxythiophene, and corresponding polyethlenedioxythiophenes
KR100362018B1 (ko) 가용성아닐린전도성중합체
Dey Sadhu et al. Preparation and characterization of polyaniline‐and polythiophene‐based copolymer and its nanocomposite suitable for electro‐optical devices
EP0461182A1 (fr) Formes thermostables de polyaniline electroconductrice.
WO2010005271A2 (fr) Dispersion d’un polymère conducteur dans un solvant organique et son procédé de fabrication
WO2012169768A9 (fr) Nanoparticules conductrices multicouches et leur procédé de production
CA2300009A1 (fr) Solution contenant de la polyaniline et methode de preparation de cette solution
WO2011071295A2 (fr) Composite nanotubes de carbone/liquide ionique polymère, et composite nanotubes de carbone/polymère conducteur préparé à l'aide de ce dernier
KR101050523B1 (ko) 비닐계 또는 아크릴계 고분자 코어 및 전도성 고분자 쉘을 포함하는 코어-쉘 구조의 나노입자의 제조방법
CN103709417B (zh) 一种聚噻吩类衍生物水分散体及其制备方法
JP2014028760A (ja) チオフェン化合物、水溶性導電性ポリマー及びその水溶液、並びにそれらの製造法
WO2010041876A2 (fr) Procédé de préparation de solution de dispersion de solvant organique pour polymère conducteur au moyen de liquide polymère ionique et polymère conducteur préparé par ce procédé
KR100869572B1 (ko) 코어 셀 나노입자 및 이의 제조방법
KR100374719B1 (ko) 가용성 폴리(3,4-에틸렌다이옥시싸이오펜) 분말제조방법
WO2012169767A2 (fr) Procédé de production de nanoparticules conductrices pouvant être dispersées dans l'eau
KR101306634B1 (ko) 폴리(3,4-에틸렌디옥시티오펜):덱스트란 공중합체를 포함하는 조성물 및 그 제조방법
JP2012092265A (ja) チエノチオフェン共重合体組成物
KR101000496B1 (ko) 가용성 폴리(3,4-에틸렌다이옥시싸이오펜) 나노분말의 제조방법
KR101152287B1 (ko) 유-무기 발광 복합체 및 이의 제조방법
JP2003277500A (ja) 導電性ポリアニリン溶液およびその製法
KR102096131B1 (ko) 전기전도성 미립자의 제조방법 및 이를 이용하여 제조된 미립자
WO2011081481A2 (fr) Composition de polymère conducteur contenant un composé fluoré, dispersible dans un solvant organique
KR20010091569A (ko) 폴리아닐린 함유 용액의 제조방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12797383

Country of ref document: EP

Kind code of ref document: A2

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12797383

Country of ref document: EP

Kind code of ref document: A2