WO2014118356A1 - Verfahren zum herstellen eines laminats ohne klebstoff - Google Patents

Verfahren zum herstellen eines laminats ohne klebstoff Download PDF

Info

Publication number
WO2014118356A1
WO2014118356A1 PCT/EP2014/051977 EP2014051977W WO2014118356A1 WO 2014118356 A1 WO2014118356 A1 WO 2014118356A1 EP 2014051977 W EP2014051977 W EP 2014051977W WO 2014118356 A1 WO2014118356 A1 WO 2014118356A1
Authority
WO
WIPO (PCT)
Prior art keywords
laminate
thermoplastic layer
fabric
infrared
layers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2014/051977
Other languages
English (en)
French (fr)
Inventor
Michael Gierlings
Thorsten KLOMFASS
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KLOMFASS GIERLINGS & PARTNER GbR
Original Assignee
KLOMFASS GIERLINGS & PARTNER GbR
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KLOMFASS GIERLINGS & PARTNER GbR filed Critical KLOMFASS GIERLINGS & PARTNER GbR
Priority to EP14708491.7A priority Critical patent/EP2951016B1/de
Priority to ES14708491.7T priority patent/ES2654678T3/es
Priority to PL14708491T priority patent/PL2951016T3/pl
Publication of WO2014118356A1 publication Critical patent/WO2014118356A1/de
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Verfahren zum Herstellen eines Laminats (1) ohne Klebstoff mit einem Substrat aus einer thermoplastischen Schicht (11) und mindestens einer darauf aufgebrachten Schicht aus Vliesstoff/Gewebe (12), wobei - eine Wärmezuführung nur in die thermoplastische Schicht (11) über Infrarotstrahlung erfolgt, - die Schichten (11, 12) zu einem Laminat (1) aufeinander gepresst werden und - das Laminat (1) gekühlt wird. wobei nur die thermoplastische Schicht (11) erwärmt wird. Es ist daher Aufgabe der Erfindung, ein Verfahren zur Herstellung eines Laminats (1) zu schaffen, das ohne Einsatz von Klebstoffen funktioniert und eine optimierte Wärmezuführung für die Laminatherstellung ermöglicht. Zur Lösung dieser Aufgabe schlägt die Erfindung ausgehend von einem Laminat (1) der eingangs genannten Art vor, dass durch die Infrarotstrahlung nur die Oberfläche der thermoplastischen Schicht (11) angeschmolzen wird und dass die thermoplastische Schicht (11) während der oberseitigen Wärmezuführung an der Unterseite gekühlt wird.

Description

Verfahren zum Herstellen eines Laminats ohne Klebstoff Die Erfindung betrifft ein Verfahren zum Herstellen eines Laminats ohne Klebstoff mit einem Substrat aus einer thermoplastischen Schicht und mindestens einer darauf aufgebrachten Schicht aus Vliesstoff/ Gewebe, wobei
- eine Wärmezuführung nur in die thermoplastische Schicht über Infrarotstrahlung erfolgt,
- die Schichten zu einem Laminat aufeinander gepresst werden und
- das Laminat gekühlt wird.
Laminate der genannten Art sind beispielsweise aus der amerikanischen Offenlegungsschrift US 2008/0274307 A1 bekannt. Eine Kaschiervorrichtung verbindet demnach ein poröses Substrat mit einer schmelzbaren oberen Schicht zu einem Laminat, genauer gesagt einem Teppich. Die schmelzbare obere Schicht besteht aus einem Thermoplast und wird vor dem Verbinden mit dem porösen Substrat mittels Infrarotstrahlung erwärmt. Nach der Verbindung der schmelzbaren oberen Schicht mit dem porösen Substrat wird das Laminat gekühlt. Dieses Verfahren hat den Vorteil, dass eine klebstofffreie Verbindung zweier Schichten mittels Erwärmung der thermoplastischen Schicht durch Infrarotstrahlung erfolgt.
Jedoch eignet sich dieses Verfahren nicht zum Verbinden von Schichten für Hygieneartikel. Hygieneartikel weisen üblicherweise dünne Schichten auf. Umso dünner die Schichten sind, desto schneller verlieren sie beim Erwärmen ihre Form und Struktur und verändern somit unkontrollierbar ihre mechanischen Eigenschaften. Bei Teppichen ist eine Änderung der Schichtstruktur und damit der mechanischen Eigenschaften der einzelnen Schichten aufgrund des stark abweichenden Anforderungsprofils gegenüber Hygieneartikeln unbedenklich. Bei Teppichen verwendet man für die Beschichtung erheblich dickere thermoplastische Schichten.
Ein Verfahren zum Herstellen eines Laminats für Hygieneartikel wird in der deutschen Offenlegungsschrift DE 10 2004 042 405 A1 genannt. Diese Offenlegungsschrift beschreibt ein Verfahren zur Herstellung von Vlies-Folien- Laminaten für Hygieneartikel aus einer thermoplastischen Schicht und einem Vliesstoff. Dabei wird die thermoplastische Schicht zusammen mit dem Vliesstoff erwärmt, zu einem Laminat gepresst und durch einen gekühlten Walzenspalt geführt. Die thermoplastische Schicht wird bis zum schmelzflüssigen Zustand erwärmt.
Die vorgenannten Laminate haben den Vorteil, dass eine Verbindung zwischen der thermoplastischen Schicht und einem Vliesstoff frei von Klebstoff sind. Insbesondere für Hygieneartikel ist dies ein bedeutender Vorteil, da sensible Hauttypen negativ auf mögliche migrationsfähige Bestandteile aus Klebstoffen ansprechen. Neben der besseren Gesundheitsverträglichkeit wird die Umwelt im Hinblick auf die Massenproduktion aufgrund des Verzichts auf Klebstoffe erheblich geschont. Ein weiterer wesentlicher Aspekt ist die insgesamt günstigere Herstellung der Hygieneartikel aufgrund der Klebstoffeinsparung.
Die vorbekannten Laminate haben jedoch den Nachteil, dass bei der Erwärmung der Schichten auf den Schmelzpunkt des Vliesstoffes Rücksicht genommen werden muss. Aufgrund dieser Abhängigkeit lässt sich die thermoplastische Schicht nicht in jedem Fall auf die für das Fügen optimale Temperatur erwärmen. Zudem besteht das Problem, dass die thermoplastische Schicht aufgrund der Erwärmung schmelzflüssig wird und somit ihre Struktur vollkommen verliert. Es ist daher Aufgabe der Erfindung, ein Verfahren zur Herstellung eines Laminats für Hygieneartikel zu schaffen, das ohne Einsatz von Klebstoffen funktioniert und eine optimierte Wärmezuführung für die Laminatherstellung ermöglicht. Dabei sollen die Strukturen der einzelnen Schichten nicht beschädigt werden, um ihre mechanischen Eigenschaften in dem herzustellenden Laminat beizubehalten.
Zur Lösung dieser Aufgabe schlägt die Erfindung ausgehend von einem Laminat der eingangs genannten Art vor, dass durch die Infrarotstrahlung nur die Oberfläche der thermoplastischen Schicht angeschmolzen wird und dass die thermoplastische Schicht während der oberseitigen Wärmezuführung an der Unterseite gekühlt wird.
Da nur die thermoplastische Schicht erwärmt wird, lässt sie sich unabhängig vom Schmelzpunkt des Vliesstoffes auf ihre ideale Fügetemperatur erwärmen. Dies gewährleistet eine starke Verbindung des Laminats. Durch die selektive Erwärmung der Oberfläche der thermoplastischen Schicht mittels der Infrarotstrahlung, bleibt die tragende Struktur der thermoplastischen Schicht vollständig erhalten. Da das Vlies nicht erwärmt wird, bleiben dessen mechanischen Eigenschaften im Laminat vollständig erhalten. Die Kühlung kann über ein gekühltes Leitblech, Schwebekühlung, Kühlwalzen oder ähnliche Vorrichtung erfolgen. Durch die unterseitige Kühlung der thermoplastischen Schicht wird gewährleistet, dass sich die tragende Struktur der thermoplastischen Schicht in Folge der Wärmezuführung kaum verändert. Die Kühlung erfolgt folglich vor der Wärmezuführung, während sowie nach dem Pressvorgang. Eine besonders bevorzugte Methode der Erfindung besteht darin, dass als Infrarotstrahlung nahes Infrarot verwendet wird, mit einem Wellenlängenbereich von 1 ,2 bis 2,5 μιτι, insbesondere von 1 ,6 bis 1 ,8 μιτι. Thermoplastische Schichten, z.B. polyolefinische Folien, haben bei einem Wellenbereich von 3,3 μιτι eine besonders gute Absorptionsfähigkeit von Infrarotstrahlung. Allerdings ist die Aufheizdauer bei der vorgenannten Wellenlänge der Infrarotstrahlung relativ lang. Dies verhindert, dass ausschließlich die Oberfläche der thermoplastischen Schicht angeschmolzen wird. Überraschenderweise hat sich herausgestellt, dass sich die thermoplastischen Schichten in dem vorgenannten Wellenbereich ebenfalls schnell erwärmen und den Effekt der selektiven Oberflächenschmelzung der thermoplastischen Schicht ermöglichen. Damit bleibt die Struktur der thermoplastischen Schicht im Wesentlichen erhalten.
Die besten Ergebnisse lassen sich nach Lehre der Erfindung erzielen, wenn als Infrarotquelle stabförmige Infrarotstrahler und/ oder Infrarot-Stiftsockellampen verwendet werden. Diese Infrarotquellen ermöglichen eine gezielte und definierte Wärmezuführung auf die Oberfläche der thermoplastischen Schicht. Es hat sich herausgestellt, dass das Laminat eine besonders qualitative Verbindung aufweist, wenn die Temperatur der Infrarotquelle auf 1800 K bis 2300 K eingestellt wird. Temperaturen unter 1800 K liefern eine schlechte Verbindung, da die Oberfläche der thermoplastischen Schicht nicht hinreichend angeschmolzen wird. Über 2300 K schmilzt die gesamte thermoplastische Schicht an. Um eine Verbindung nach Lehre der Erfindung zu erhalten, ist ein Temperaturintervall der Infrarotquelle gemäß den vorgenannten Werten notwendig.
Ähnliches trifft auf den Abstand zwischen der Infrarotquelle und der thermoplastischen Schicht zu. Dieser sollte auf 3 cm bis 30 cm, insbesondere auf 4 cm bis 7 cm, eingestellt werden. Bei zu kurzem Abstand der Infrarotquelle zu der thermoplastischen Schicht kann sich die Infrarotstrahlung nicht flächig auf der thermoplastischen Schicht verteilen und sorgt für eine zu starke punktuelle Wärmezuführung, die die thermoplastische Schicht an diesen Stellen unkontrolliert aufschmelzen lässt. Bei einem kritischen Abstand von über 30 cm reicht die Strahlungsintensität nicht mehr aus, um die Oberfläche der thermoplastischen Schicht anzuschmelzen. Hier greift das Abstandsgesetz, nach dem die Strahlungsintensität, d.h. die Leistung pro Fläche, mit 1 /r2 abnimmt.
Eine vorteilhafte Methode sieht vor, dass die Schichten über ein Kaschierwerk zu einem Laminat verbunden werden. Prinzipiell werden beim Kaschieren zwei Bahnen miteinander verbunden. Das Kaschierwerk hat den Vorteil, dass die einzelnen Schichten in einem Arbeitsschritt und damit schnell miteinander verbunden werden. Der Vorteil der mehreren, milden Kaschiervorgänge liegt darin, dass sie eine stärkere Verbindung der einzelnen Schichten miteinander ergeben und damit ein qualitativeres Laminat erzeugen. Abhängig vom Einsatz des Laminats ist der Pressvorgang zu wählen.
Eine vorteilhafte Methode der Erfindung besteht darin, dass die thermoplastische Schicht beidseitig mit Vliesstoff/ Gewebe verbunden wird. Durch das ausschließliche Anschmelzen der Oberflächen der thermoplastischen Schicht bleibt deren tragende Struktur im nicht geschmolzenen Teil vollständig erhalten. Dies verleiht dem Laminat eine erhöhte Stabilität, insbesondere gegenüber vollständig erwärmten Laminaten.
Die Erfindung sieht somit ein Laminat vor, das herstellbar ist aus einer thermoplastischen Schicht und Vliesstoff/ Gewebe nach mindestens einem der Ansprüche 1 bis 8. Dadurch, dass die Infrarotstrahlung nur die Oberfläche der thermoplastischen Schicht anschmilzt, bleibt die tragende Struktur der thermoplastischen Schicht vollkommen unberührt. Zudem bleibt die Struktur des Vliesstoffes/ Gewebes vollständig erhalten, da diese nicht erwärmt werden.
Eine besonders bevorzugte Ausführungsform der Erfindung sieht vor, dass die Schichten vor und nach dem Fügeverfahren dehnbar, insbesondere elastisch, sind. Dies wird vor allem dadurch ermöglicht, dass die wesentlichen Strukturen der Schichten keinem Wärmeeinfluss unterliegen. Elastisch bedeutet, dass sich die Schichten aus der Elongation in ihren ursprünglichen Zustand zurückbewegen.
Eine wesentliche Ausführungsform der Erfindung schlägt vor, dass die thermoplastische Schicht Polyethylen, Polypropylen, Polystyrol, Polyamide, Latex oder Gummi, der Vliesstoff Polypropylen-Vlies oder Polyamid-Vlies oder das Gewebe Polypropylen-Gewebe, Polyamid-Gewebe, Polyethylenterephtalat- Gewebe oder Materialien mit ähnlichen Eigenschaften aufweist. Diese Materialien eignen sich insbesondere zum Laminieren nach Lehre der Erfindung. Sie sprechen insbesondere auf die halbe Wellenlänge der eigentlich optimalen Absorptionswellenlänge für polyolefinische Folien an. Ein Ausführungsbeispiel der Erfindung wird im Folgenden anhand der Zeichnung näher erläutert. Es zeigt:
Figur 1 : Prinzipskizze der Vorrichtung eines
Verfahrens zum Herstellen eines Laminats ohne Klebstoff nach Lehre der Erfindung.
Figur 1 zeigt eine Prinzipskizze einer Vorrichtung für ein Verfahren zum Herstellen eines Laminats 1 ohne Klebstoff aus einer thermoplastischen Schicht 1 1 und einem darauf aufgebrachten Vliesstoff 12. Die thermoplastische Schicht 1 1 läuft über ein gekühltes Leitblech 4. Die Wärmezuführung erfolgt über eine Infrarotquelle 2. Die thermoplastische Schicht 1 1 und der Vliesstoff 12 werden an einem Kaschierwerk 3 miteinander zu einem Laminat 1 verbunden. Die thermoplastische Schicht 1 1 wird über den gesamten Prozess über das gekühlte Leitblech 4 gekühlt.
- Patentansprüche -

Claims

Patentansprüche
1. Verfahren zum Herstellen eines Laminats (1) ohne Klebstoff mit einem Substrat aus einer thermoplastischen Schicht (11) und mindestens einer darauf aufgebrachten Schicht aus Vliesstoff/ Gewebe (12), wobei -eine Wärmezuführung nur in die thermoplastische Schicht (11) über
Infrarotstrahlung erfolgt,
-die Schichten (11, 12) zu einem Laminat (1) aufeinander gepresst werden und
- das Laminat (1 ) gekühlt wird, d a d u r c h g e k e n n z e i c h n e t, dass durch die Infrarotstrahlung nur die Oberfläche der thermoplastischen Schicht (11) angeschmolzen wird und dass die thermoplastische Schicht (11) während der oberseitigen Wärmezuführung an der Unterseite gekühlt wird.
2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass als Infrarotstrahlung nahes Infrarot verwendet wird, mit einem Wellenlängenbereich von 1 ,2 bis 2,5 Mikrometern, insbesondere von 1 ,6 bis 1 ,8 Mikrometern.
3. Verfahren nach einem der Ansprüche 1 oder 2, dadurch gekennzeichnet, dass als Infrarotquelle (2) stabförmige Infrarotstrahler und/ oder Infrarot-Stiftsockellampen verwendet werden.
4. Verfahren nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass die Temperatur der Infrarotquelle (2) auf 1800 K bis 2300 K eingestellt wird.
5. Verfahren nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass der Abstand zwischen der Infrarotquelle (2) und der thermoplastischen Schicht (1 1 ) auf 3 bis 30 Zentimeter, insbesondere auf 4 bis 7 Zentimeter, eingestellt wird.
6. Verfahren nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass die Schichten über ein Kaschierwerk (3) oder über mehrere, milde Kaschiervorgänge zu einem Laminat verbunden werden.
7. Verfahren nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass die thermoplastische Schicht beidseitig mit Vliesstoff/ Gewebe (12) verbunden wird.
8. Laminat herstellbar aus thermoplastischer Schicht (1 1 ) und Vliesstoff/ Gewebe (12) nach mindestens einem der Ansprüche 1 bis 7.
9. Laminat nach Anspruch 8, dadurch gekennzeichnet, dass die Schichten (1 1 , 12) vor und nach dem Fügeverfahren dehnbar, insbesondere elastisch, sind.
10. Laminat nach einem der Ansprüche 8 oder 9, dadurch gekennzeichnet, dass die thermoplastische Schicht (1 ) Polyethylen, Polypropylen, Polystyrol, Polyamide, Latex oder Gummi, der Vliesstoff (12) Polypropylen-Vlies oder Polyamid-Vlies oder das Gewebe (12) Polypropylen- Gewebe, Polyamid-Gewebe, Polyethylenterephtalat-Gewebe aufweisen.
PCT/EP2014/051977 2013-02-04 2014-02-03 Verfahren zum herstellen eines laminats ohne klebstoff Ceased WO2014118356A1 (de)