WO2014178000A1 - Structure stratifiée - Google Patents

Structure stratifiée Download PDF

Info

Publication number
WO2014178000A1
WO2014178000A1 PCT/IB2014/061078 IB2014061078W WO2014178000A1 WO 2014178000 A1 WO2014178000 A1 WO 2014178000A1 IB 2014061078 W IB2014061078 W IB 2014061078W WO 2014178000 A1 WO2014178000 A1 WO 2014178000A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer resin
polyolefin polymer
paper
density
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2014/061078
Other languages
English (en)
Inventor
Jacob Robert Blok
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CLONDALKIN GROUP INVESTMENTS BV
Original Assignee
CLONDALKIN GROUP INVESTMENTS BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CLONDALKIN GROUP INVESTMENTS BV filed Critical CLONDALKIN GROUP INVESTMENTS BV
Priority to EP14727927.7A priority Critical patent/EP2991829A1/fr
Publication of WO2014178000A1 publication Critical patent/WO2014178000A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Cette invention concerne un procédé de production d'une structure stratifiée comprenant les étapes consistant à recevoir une bande continue de papier haute densité ayant une surface spécialement traitée par des moyens chimiques et/ou mécaniques, la densité du papier haute densité étant ≥0,8 gramme par centimètre cube, à appliquer par extrusion une couche de résine à base d'un polymère de polyoléfine facile à cristalliser ou une multitude de couches de résines polyoléfiniques sur la bande continue de papier haute densité, et à appliquer une pression sur le papier haute densité revêtu de résine à base d'un polymère de polyoléfine et à induire ainsi la cristallisation du polymère, pour former ainsi une zone très cristalline dans la couche polymère, la couche polymère présentant des propriétés élevées de barrière aux gaz et aux arômes.
PCT/IB2014/061078 2013-05-01 2014-04-29 Structure stratifiée Ceased WO2014178000A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP14727927.7A EP2991829A1 (fr) 2013-05-01 2014-04-29 Structure stratifiée

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB1307899.3A GB2513622A (en) 2013-05-01 2013-05-01 A laminate structure
GB1307899.3 2013-05-01

Publications (1)

Publication Number Publication Date
WO2014178000A1 true WO2014178000A1 (fr) 2014-11-06

Family

ID=48627160

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2014/061078 Ceased WO2014178000A1 (fr) 2013-05-01 2014-04-29 Structure stratifiée

Country Status (3)

Country Link
EP (1) EP2991829A1 (fr)
GB (1) GB2513622A (fr)
WO (1) WO2014178000A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10612193B2 (en) 2017-06-15 2020-04-07 Dow Global Technologies Llc Paper coated with a functional polyolefin film
EP3862182A1 (fr) * 2020-02-07 2021-08-11 Danapak Flexibles A/S Papier revêtu de polymère à double face

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005053955A1 (fr) * 2003-12-03 2005-06-16 Commonwealth Scientific And Industrial Research Organisation Procedes de production de materiau d'emballage servant au transport et au stockage de marchandises perissables

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1119279A (en) * 1966-10-03 1968-07-10 Dow Chemical Co An improved process for coating substrates
US4188442A (en) * 1976-12-28 1980-02-12 Toyo Kagaku Kabushiki Kaisha Adhesive tape
JPH04172448A (ja) * 1990-11-07 1992-06-19 Konica Corp ハロゲン化銀カラー写真感光材料
EP0976545B1 (fr) * 1998-07-30 2005-09-28 Fuji Photo Film Co., Ltd. Support pour papier photographique et sa production
US6273984B1 (en) * 1998-11-20 2001-08-14 Eastman Kodak Company Lamination with curl control
US20020176973A1 (en) * 2001-05-23 2002-11-28 Loparex, Inc. Laminates including cellulosic materials and processes for making and usng the same

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005053955A1 (fr) * 2003-12-03 2005-06-16 Commonwealth Scientific And Industrial Research Organisation Procedes de production de materiau d'emballage servant au transport et au stockage de marchandises perissables

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10612193B2 (en) 2017-06-15 2020-04-07 Dow Global Technologies Llc Paper coated with a functional polyolefin film
EP3862182A1 (fr) * 2020-02-07 2021-08-11 Danapak Flexibles A/S Papier revêtu de polymère à double face
WO2021156354A1 (fr) * 2020-02-07 2021-08-12 Danapak Flexibles A/S Feuille d'emballage

Also Published As

Publication number Publication date
GB201307899D0 (en) 2013-06-12
GB2513622A (en) 2014-11-05
EP2991829A1 (fr) 2016-03-09

Similar Documents

Publication Publication Date Title
CN102481763B (zh) 有密封涂层的热机械稳定的可热封膜,含有该膜的层压包装材料,由所述层压包装材料形成的包装容器和所述膜的制造方法
JP6486104B2 (ja) 多層バリアフィルム、そのフィルムを含むパッケージングラミネート、そのパッケージングラミネートから形成されるパッケージング容器、及びそのフィルムの製造方法
EP2956303B2 (fr) Stratifié d'emballage, son procédé de fabrication et récipient d'emballage produit à partir du récipient d'emballage
EP4253047A1 (fr) Matériau d'emballage stratifié et récipient d'emballage fabriqué à partir de celui-ci
US20200391489A1 (en) Recyclable Packaging Laminate with Improved Heat Resistance for Sealing
US9610755B2 (en) Packaging and method of making packaging
EP3194164B1 (fr) Verpackungslaminat, verfahren zur herstellung davon und aus dem verpackungslaminat hergestellter verpackungsbehälter
CN106715110B (zh) 一种用于层合包装材料的方法
EP1082220A1 (fr) Materiau d'emballage stratifie, procede de fabrication dudit materiau et recipients d'emballage produits a partir dudit materiau
WO2016194002A1 (fr) Stratifié formant barrière au toucher doux et velouté
US9789670B2 (en) Heat-sealable laminate and method for producing same
EP2991829A1 (fr) Structure stratifiée
JPH11240535A (ja) 紙容器用セミマテリアル、紙容器用セミマテリアルの製造法、紙容器用包材及び紙容器
JP4129899B2 (ja) 紙容器用包装材料の製造法
JP2004330420A (ja) 紙容器用積層体及びその製造方法
JP2003231224A (ja) 積層シート及びその製造方法
EP4371755B1 (fr) Matériau d'emballage stratifié, procédé pour sa fabrication et récipients d'emballage le comprenant
AU733002C (en) A method of and apparatus for use in manufacturing a packaging laminate
JP2001191411A (ja) 紙容器用セミマテリアルの製造法及び紙容器用包材
JP2025143103A (ja) 積層体及び包装容器

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14727927

Country of ref document: EP

Kind code of ref document: A1

REEP Request for entry into the european phase

Ref document number: 2014727927

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2014727927

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE