WO2014201558A1 - Matériau isolant phonique et son procédé de fabrication - Google Patents

Matériau isolant phonique et son procédé de fabrication Download PDF

Info

Publication number
WO2014201558A1
WO2014201558A1 PCT/CA2014/050566 CA2014050566W WO2014201558A1 WO 2014201558 A1 WO2014201558 A1 WO 2014201558A1 CA 2014050566 W CA2014050566 W CA 2014050566W WO 2014201558 A1 WO2014201558 A1 WO 2014201558A1
Authority
WO
WIPO (PCT)
Prior art keywords
insulating material
fibers
sound insulating
fibrous layer
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CA2014/050566
Other languages
English (en)
Inventor
David Simard
Dorine GIRIN
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GESTION SOPREMA CANADA Inc
PROTEC-STYLE Inc
Original Assignee
GESTION SOPREMA CANADA Inc
PROTEC-STYLE Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GESTION SOPREMA CANADA Inc, PROTEC-STYLE Inc filed Critical GESTION SOPREMA CANADA Inc
Publication of WO2014201558A1 publication Critical patent/WO2014201558A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un matériau isolant phonique destiné à être appliqué sur une surface. Le matériau comprend une couche de substrat ; une première couche fibreuse et une seconde couche fibreuse. La première couche fibreuse est fixée à la couche de substrat et comprend des fibres creuses. La seconde couche fibreuse est fixée à la première couche fibreuse et comprend également les fibres creuses. La densité et le poids de base de la seconde couche fibreuse ont chacun une valeur différente de la densité et du poids de base de la première couche fibreuse, respectivement.
PCT/CA2014/050566 2013-06-17 2014-06-17 Matériau isolant phonique et son procédé de fabrication Ceased WO2014201558A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201361835803P 2013-06-17 2013-06-17
US61/835,803 2013-06-17

Publications (1)

Publication Number Publication Date
WO2014201558A1 true WO2014201558A1 (fr) 2014-12-24

Family

ID=52103742

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA2014/050566 Ceased WO2014201558A1 (fr) 2013-06-17 2014-06-17 Matériau isolant phonique et son procédé de fabrication

Country Status (1)

Country Link
WO (1) WO2014201558A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017088043A1 (fr) * 2015-11-27 2017-06-01 Protec-Style Inc. Matériau d'isolation non tissé
CN108231052A (zh) * 2017-12-22 2018-06-29 高州创建铸造有限公司 一种用于大型锅炉引风机钢质烟囱的消声器
CN115853398A (zh) * 2022-12-14 2023-03-28 福耀高性能玻璃科技(福建)有限公司 一种真空玻璃用微支柱及真空玻璃

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6572723B1 (en) * 2000-06-30 2003-06-03 Owens Corning Fiberglas Technology, Inc. Process for forming a multilayer, multidensity composite insulator
US6669265B2 (en) * 2000-06-30 2003-12-30 Owens Corning Fiberglas Technology, Inc. Multidensity liner/insulator
JP4167505B2 (ja) * 2003-02-03 2008-10-15 株式会社フジコー 多密度構成のフェルト吸音材
US20090242325A1 (en) * 2008-03-27 2009-10-01 Dell Seven, Inc. Acoustically insulating product

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6572723B1 (en) * 2000-06-30 2003-06-03 Owens Corning Fiberglas Technology, Inc. Process for forming a multilayer, multidensity composite insulator
US6669265B2 (en) * 2000-06-30 2003-12-30 Owens Corning Fiberglas Technology, Inc. Multidensity liner/insulator
JP4167505B2 (ja) * 2003-02-03 2008-10-15 株式会社フジコー 多密度構成のフェルト吸音材
US20090242325A1 (en) * 2008-03-27 2009-10-01 Dell Seven, Inc. Acoustically insulating product

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017088043A1 (fr) * 2015-11-27 2017-06-01 Protec-Style Inc. Matériau d'isolation non tissé
CN108231052A (zh) * 2017-12-22 2018-06-29 高州创建铸造有限公司 一种用于大型锅炉引风机钢质烟囱的消声器
CN115853398A (zh) * 2022-12-14 2023-03-28 福耀高性能玻璃科技(福建)有限公司 一种真空玻璃用微支柱及真空玻璃
WO2024124941A1 (fr) * 2022-12-14 2024-06-20 福耀高性能玻璃科技(福建)有限公司 Micro-pilier pour verre sous vide, et verre sous vide

Similar Documents

Publication Publication Date Title
CN1274897C (zh) 隔音隔热的无纺合成片材
US8322487B1 (en) Acoustically coupled non-woven composite
AU2010205258B2 (en) Soundproof panel and soundproof structure
US8544218B2 (en) Acoustically insulating product
KR101760771B1 (ko) 다층 천정 타일
US20120240486A1 (en) Acoustic Panel
EP2736711B1 (fr) Revêtement mural absorbant acoustique
EP2748385B1 (fr) Revêtement mural pour confort thermique et acoustique
EP2356283A1 (fr) Panneau acoustique résistant au feu et à l affaissement
AU2011226914B1 (en) An acoustic panel
CN102869843A (zh) 隔音地板构造及隔音地板构成部件以及地板冲击音的降低方法
JP7538719B2 (ja) 防音材の吸音特性の制御方法
CN111757966B (zh) 复合声学层
WO2014201558A1 (fr) Matériau isolant phonique et son procédé de fabrication
RU186830U1 (ru) Нетканый звукопоглощающий композитный многослойный материал
EP3619376B1 (fr) Système de sol flottant
RU2353423C1 (ru) Защитный термокомпенсирующий мембранный материал
JP7186045B2 (ja) 防音材
KR20260046376A (ko) 흡음 멤브레인 및 그의 용도
JP2022162917A (ja) 積層パネル

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14814140

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14814140

Country of ref document: EP

Kind code of ref document: A1