WO2017018659A8 - 내시효성 및 소부경화성이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법 - Google Patents

내시효성 및 소부경화성이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법 Download PDF

Info

Publication number
WO2017018659A8
WO2017018659A8 PCT/KR2016/006398 KR2016006398W WO2017018659A8 WO 2017018659 A8 WO2017018659 A8 WO 2017018659A8 KR 2016006398 W KR2016006398 W KR 2016006398W WO 2017018659 A8 WO2017018659 A8 WO 2017018659A8
Authority
WO
WIPO (PCT)
Prior art keywords
steel sheet
hot
dip
dip galvanized
excluding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2016/006398
Other languages
English (en)
French (fr)
Other versions
WO2017018659A1 (ko
Inventor
한상호
이제웅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Posco Holdings Inc
Original Assignee
Posco Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020160041648A external-priority patent/KR101795918B1/ko
Application filed by Posco Co Ltd filed Critical Posco Co Ltd
Priority to CN201680043417.3A priority Critical patent/CN107849668B/zh
Priority to EP16830692.6A priority patent/EP3327164B1/en
Priority to JP2018503140A priority patent/JP6619079B2/ja
Priority to US15/743,490 priority patent/US10907233B2/en
Publication of WO2017018659A1 publication Critical patent/WO2017018659A1/ko
Publication of WO2017018659A8 publication Critical patent/WO2017018659A8/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

내시효성 및 소부경화성이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법이 제공된다. 본 발명은, 소지강판 표면에 용융아연도금층이 형성되어 있는 용융아연도금강판으로서, 상기 소지강판은 중량%로, 탄소(C):0.002~0.012%, 망간(Mn):1.6~2.7%, 인(P):0.03% 이하(0%는 제외), 황(S): 0.01% 이하(0%는 제외), 질소(N):0.01% 이하(0%는 제외), 알루미늄(sol.Al): 0.02~0.06%, 크롬(Cr):1.0% 이하(0%는 제외), 잔부 철 및 불가피한 불순물을 포함하여 조성되고, 또한 1.3≤Mn(wt%)/(1.15×Cr(wt%))≤20.5의 관계를 만족하고, 관계식 1에 의해 정의되는 Mneq가 1.9≤Mneq≤3.9를 만족하며, 그 강 미세조직이 면적비로 95% 이상의 페라이트와 잔부 경질 제 2상으로 이루어지며, 관계식 2에 의해 정의되는 페라이트 결정립계에 존재하는 마르텐사이트 점유비율이 90% 이상이며, 그리고 관계식 3에 의해 정의되는, 소지강판 1/4t지점에서 마르텐사이트 상에서의 평균 Mn 농도 wt%(a)와 상기 마르텐사이트 상 주변 1㎛이내의 페라이트 상에서의 평균 Mn 농도 wt%(b)의 차가 0.3wt%이상인 것을 특징으로 하는 내시효성 및 소부경화성이 우수한 용융아연도금강판에 관한 것이다.
PCT/KR2016/006398 2015-07-24 2016-06-16 내시효성 및 소부경화성이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법 Ceased WO2017018659A1 (ko)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CN201680043417.3A CN107849668B (zh) 2015-07-24 2016-06-16 具有优良抗时效性能和烘烤硬化性的热浸镀锌钢板和合金化热浸镀锌钢板及其生产方法
EP16830692.6A EP3327164B1 (en) 2015-07-24 2016-06-16 Hot-dip galvanized steel sheet and hot-dip galvannealed steel sheet with excellent aging-resistance properties and bake hardenability, and method for manufacturing same
JP2018503140A JP6619079B2 (ja) 2015-07-24 2016-06-16 耐時効性及び焼付硬化性に優れた溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板、及びその製造方法
US15/743,490 US10907233B2 (en) 2015-07-24 2016-06-16 Hot-dip galvanized steel sheet and hot-dip galvannealed steel sheet with excellent aging resistance properties and bake hardenability, and method for manufacturing same

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
KR10-2015-0105211 2015-07-24
KR20150105211 2015-07-24
KR1020160041648A KR101795918B1 (ko) 2015-07-24 2016-04-05 내시효성 및 소부경화성이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법
KR10-2016-0041648 2016-04-05

Publications (2)

Publication Number Publication Date
WO2017018659A1 WO2017018659A1 (ko) 2017-02-02
WO2017018659A8 true WO2017018659A8 (ko) 2017-06-29

Family

ID=57884611

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2016/006398 Ceased WO2017018659A1 (ko) 2015-07-24 2016-06-16 내시효성 및 소부경화성이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법

Country Status (1)

Country Link
WO (1) WO2017018659A1 (ko)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107014681A (zh) * 2017-03-17 2017-08-04 唐山钢铁集团有限责任公司 快速评估低碳铝镇静钢抗自然时效性能的方法
KR102064962B1 (ko) * 2017-12-24 2020-02-11 주식회사 포스코 소부경화성 및 내식성이 우수한 냉연강판, 용융 아연계 도금강판 및 그 제조방법

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5058508B2 (ja) * 2005-11-01 2012-10-24 新日本製鐵株式会社 低降伏比型高ヤング率鋼板、溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板及び鋼管、並びにそれらの製造方法
JP5332355B2 (ja) * 2007-07-11 2013-11-06 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
KR20110046689A (ko) * 2009-10-29 2011-05-06 현대제철 주식회사 저항복비 특성이 우수한 고강도 강판 및 그 제조방법
JP5765092B2 (ja) * 2010-07-15 2015-08-19 Ｊｆｅスチール株式会社 延性と穴広げ性に優れた高降伏比高強度溶融亜鉛めっき鋼板およびその製造方法
KR101543857B1 (ko) * 2013-10-31 2015-08-11 주식회사 포스코 가공성이 우수한 복합조직강판 및 그 제조방법

Also Published As

Publication number Publication date
WO2017018659A1 (ko) 2017-02-02

Similar Documents

Publication Publication Date Title
MX2018007347A (es) Amina de acero galvanizada por inmersion en caliente de alta resistencia que tiene excelente calidad de superficie y soldabilidad por puntos, y metodo de manufactura para la misma.
WO2017105026A8 (ko) 화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법
MX388381B (es) Acero de elevada resistencia y procedimiento de fabricacion.
UA124354C2 (uk) Відпущена листова сталь з покриттям, яка характеризується чудовою деформованістю, і спосіб її виготовлення
MX2025000986A (es) Hoja de acero laminada y recubierta para estampacion en caliente, pieza de acero recubierta estampada en caliente y metodos para fabricar la misma
WO2017105025A8 (ko) 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법
MX2019007165A (es) Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma.
WO2016098964A8 (ko) 재질 불균일이 작고 성형성이 우수한 고강도 냉연강판, 용융아연도금강판, 및 그 제조 방법
WO2012091310A3 (en) Hot dip plated steel sheet having excellent plating adhesiveness and method of manufacturing the same
MX395449B (es) Lámina de acero galvanizada de alta resistencia y método para producir la misma.
MX376487B (es) Lamina de acero laminada en frio, metodo de fabricacion y uso de la misma.
MX2016014963A (es) Tira de acero que tiene alta resistencia y alta plasticidad, la tira de acero tiene un recubrimiento a base de zinc en caliente.
WO2017111428A8 (ko) 연성, 구멍가공성 및 표면처리 특성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법
MX2022007458A (es) Hoja de acero laminada en frio y recocida y metodo de fabricacion.
MX374542B (es) Hoja de acero doblemente recocida que tiene resistencia mecánica alta y características de ductilidad, método de fabricación y uso de tales hojas.
MX2016007954A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MY183438A (en) High-strength cold-rolled steel sheet and method for manufacturing the same
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
WO2016105115A8 (ko) 표면품질, 도금밀착성 및 성형성이 우수한 고강도 용융아연도금강판 및 그 제조방법
MX2017004593A (es) Producto plano de acero laminado en frio y recocido por recristalizacion y procedimiento para su fabricacion.
WO2018009041A8 (ko) 균열전파 저항성 및 연성이 우수한 열간성형 부재 및 이의 제조방법
BR112014005641A2 (pt) tira de aço galvanizada por imersão a quente de alta resistência
FI3710612T3 (fi) Menetelmä sulametallin haurastumisresistantin sinkkipäällystetyn teräslevyn valmistamiseksi
MX386195B (es) Lámina de acero laminada en caliente de alto contenido en carbono y método para la producción de la misma.
WO2013032173A3 (ko) 도금밀착성이 우수한 고망간강 및 이로부터 용융아연도금강판을 제조하는 방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16830692

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 15743490

Country of ref document: US

ENP Entry into the national phase

Ref document number: 2018503140

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2016830692

Country of ref document: EP