WO2017102645A1 - Procédé de production de composés monoaromatiques - Google Patents

Procédé de production de composés monoaromatiques Download PDF

Info

Publication number
WO2017102645A1
WO2017102645A1 PCT/EP2016/080628 EP2016080628W WO2017102645A1 WO 2017102645 A1 WO2017102645 A1 WO 2017102645A1 EP 2016080628 W EP2016080628 W EP 2016080628W WO 2017102645 A1 WO2017102645 A1 WO 2017102645A1
Authority
WO
WIPO (PCT)
Prior art keywords
mpa
polyaromatics
catalyst
process according
zeolite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2016/080628
Other languages
English (en)
Inventor
Luis ARAMBURO
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SABIC Global Technologies BV
Original Assignee
SABIC Global Technologies BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SABIC Global Technologies BV filed Critical SABIC Global Technologies BV
Publication of WO2017102645A1 publication Critical patent/WO2017102645A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un procédé de production de composés monoaromatiques à partir d'une charge d'hydrocarbures comprenant des composés polyaromatiques et des composés monoaromatiques, comprenant : a) la mise en contact de la charge d'hydrocarbures en présence d'hydrogène avec un catalyseur d'hydrotraitement pour réduire les constituants soufrés et azotés et saturer au moins l'un des cycles aromatiques des composés polyaromatiques de la charge d'hydrocarbures afin d'obtenir des composés polyaromatiques partiellement déshydrogénés, b) la mise en contact de l'effluent obtenu à l'étape a) avec un catalyseur de déshydrogénation sélectif pour la déshydrogénation sélective des espèces naphténiques monocycliques de l'effluent obtenu à l'étape a), le catalyseur de déshydrogénation comprenant un matériau aluminosilicate ou un matériau silicate ayant une structure inversée d'ossature mordénite (MFI) dans laquelle un ou plusieurs métaux de transition sont déposés sélectivement à l'intérieur de la structure de pores de la structure MFI et c) la mise en contact de l'effluent obtenu à l'étape b) en présence d'hydrogène avec un catalyseur d'ouverture de cycle pour l'ouverture des cycles aromatiques saturés des composés polyaromatiques partiellement déshydrogénés de l'effluent obtenu à l'étape b).
PCT/EP2016/080628 2015-12-16 2016-12-12 Procédé de production de composés monoaromatiques Ceased WO2017102645A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP15200340.6 2015-12-16
EP15200340 2015-12-16

Publications (1)

Publication Number Publication Date
WO2017102645A1 true WO2017102645A1 (fr) 2017-06-22

Family

ID=54850088

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2016/080628 Ceased WO2017102645A1 (fr) 2015-12-16 2016-12-12 Procédé de production de composés monoaromatiques

Country Status (1)

Country Link
WO (1) WO2017102645A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019212765A1 (fr) * 2018-05-01 2019-11-07 Exxonmobil Research And Engineering Company Composition de catalyseur à métal noble ayant une activité de saturation aromatique améliorée et son utilisation
CN110614117A (zh) * 2019-09-10 2019-12-27 中国石油大学(北京) Co-Silicalite-1催化剂及其制备方法与应用
CN116651434A (zh) * 2023-07-28 2023-08-29 金发科技股份有限公司 一种低碳烷烃脱氢催化剂及其制备方法和应用

Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1148955A (en) * 1966-05-17 1969-04-16 Mobil Oil Corp Selective catalysis
FR2087391A5 (en) * 1970-05-15 1971-12-31 Inst Francais Du Petrole Prepn. of aromatics esp. BTX - from pyrolysis and steam-cracked naphthas
US3702886A (en) 1969-10-10 1972-11-14 Mobil Oil Corp Crystalline zeolite zsm-5 and method of preparing the same
US4061724A (en) 1975-09-22 1977-12-06 Union Carbide Corporation Crystalline silica
US4654454A (en) * 1984-08-09 1987-03-31 The British Petroleum Company P.L.C. Selective dealumination of zeolites
US4943366A (en) * 1985-06-03 1990-07-24 Mobil Oil Corporation Production of high octane gasoline
US20070062848A1 (en) 2005-09-20 2007-03-22 Nova Chemicals (International) S.A. Aromatic saturation and ring opening process
US20080051615A1 (en) * 2006-08-24 2008-02-28 Stavens Elizabeth L Process for the production of benzene, toluene, and xylenes
US20120000819A1 (en) * 2009-03-30 2012-01-05 Jx Nippon Oil & Energy Corporation Method of producing alkylbenzene and catalyst used therefor
US20120029257A1 (en) * 2010-07-28 2012-02-02 Chevron U.S.A. Inc. Process for the production of para-xylene
US8962900B2 (en) 2010-10-22 2015-02-24 Sk Innovation Co., Ltd. Method for producing valuable aromatics and light paraffins from hydrocarbonaceous oils derived from oil, coal or wood
WO2015128317A1 (fr) * 2014-02-25 2015-09-03 Saudi Basic Industries Corporation Procédé de production de btx à partir d'un mélange d'hydrocarbures en c5-c12

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1148955A (en) * 1966-05-17 1969-04-16 Mobil Oil Corp Selective catalysis
US3702886A (en) 1969-10-10 1972-11-14 Mobil Oil Corp Crystalline zeolite zsm-5 and method of preparing the same
FR2087391A5 (en) * 1970-05-15 1971-12-31 Inst Francais Du Petrole Prepn. of aromatics esp. BTX - from pyrolysis and steam-cracked naphthas
US4061724A (en) 1975-09-22 1977-12-06 Union Carbide Corporation Crystalline silica
US4654454A (en) * 1984-08-09 1987-03-31 The British Petroleum Company P.L.C. Selective dealumination of zeolites
US4943366A (en) * 1985-06-03 1990-07-24 Mobil Oil Corporation Production of high octane gasoline
US20070062848A1 (en) 2005-09-20 2007-03-22 Nova Chemicals (International) S.A. Aromatic saturation and ring opening process
US20080051615A1 (en) * 2006-08-24 2008-02-28 Stavens Elizabeth L Process for the production of benzene, toluene, and xylenes
US20120000819A1 (en) * 2009-03-30 2012-01-05 Jx Nippon Oil & Energy Corporation Method of producing alkylbenzene and catalyst used therefor
US20120029257A1 (en) * 2010-07-28 2012-02-02 Chevron U.S.A. Inc. Process for the production of para-xylene
US8962900B2 (en) 2010-10-22 2015-02-24 Sk Innovation Co., Ltd. Method for producing valuable aromatics and light paraffins from hydrocarbonaceous oils derived from oil, coal or wood
WO2015128317A1 (fr) * 2014-02-25 2015-09-03 Saudi Basic Industries Corporation Procédé de production de btx à partir d'un mélange d'hydrocarbures en c5-c12

Non-Patent Citations (9)

* Cited by examiner, † Cited by third party
Title
"Atlas of Zeolite Framework Types", 2001, ELSEVIER
"Atlas of Zeolite Framework Types", vol. 16, 2001, ELSEVIER, article "Molecular Sieves in Kirk-Othmer Encyclopedia of Chemical Technology", pages: 811 - 853
"Molecular Sieves", vol. 3, 2002, pages: 204 - 255
ACS NANO, vol. 4, 2013, pages 3698
ALFKE ET AL.: "Oil Refining, Ullmann's Encyclopedia of Industrial Chemistry", 2007
ANGEW. CHEM., INT. ED., vol. 49, 2010, pages 10074
E. M. FLANIGEN ET AL.: "Silicalite, A New Hydrophobic Crystalline Silica Molecular Sieve", NATURE, vol. 271, February 1978 (1978-02-01), pages 512 - 516
HAN, APPLIED SURFACE SCIENCE, vol. 257, no. 22, pages 9525 - 9531
VAN SANTEN: "Catalysis: An Integrated Approach", pages: 468 - 469

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019212765A1 (fr) * 2018-05-01 2019-11-07 Exxonmobil Research And Engineering Company Composition de catalyseur à métal noble ayant une activité de saturation aromatique améliorée et son utilisation
CN110614117A (zh) * 2019-09-10 2019-12-27 中国石油大学(北京) Co-Silicalite-1催化剂及其制备方法与应用
CN116651434A (zh) * 2023-07-28 2023-08-29 金发科技股份有限公司 一种低碳烷烃脱氢催化剂及其制备方法和应用

Similar Documents

Publication Publication Date Title
KR101539613B1 (ko) 촉매와, 이 촉매를 이용하여 탄화수소 공급원료로부터경방향족 탄화수소 및 경알칸의 제조방법
US10723959B2 (en) Process for producing aromatics from a heavy hydrocarbon feed
CN100422122C (zh) 用于烷烃芳构化的催化剂、其制备方法及其应用
DE68923351T2 (de) Zeolith ssz-26.
JP5202329B2 (ja) Ｅｕｏゼオライトと、１０ｍｒゼオライトと、１２ｍｒゼオライトとを含む触媒および芳香族ｃ８化合物の異性化におけるその使用
DE69533361T2 (de) Umsetzung von kohlenwasserstoffen
US10738246B2 (en) Process for producing aromatics from a heavy hydrocarbon feed
US9266100B2 (en) Pre-carburized molybdenum-modified zeolite catalyst and use thereof for the aromatization of lower alkanes
KR20000016112A (ko) 금속-함유 제올라이트 촉매, 그의 제조방법 및탄화수소 전환을위한 그의 용도
JP2010523657A (ja) ゲルマニウム−ゼオライト触媒を用いたアルカンの芳香族化
WO2017093056A1 (fr) Procédé de production de gpl et de btx à partir d'une charge d'hydrocarbures lourds
WO2010116603A1 (fr) Procédé de fabrication d'alkyl benzènes et catalyseur utilisé dans ce procédé
JP2016525447A (ja) Ｅｕｏ型のゼオライトの改変、および芳香族ｃ８化合物の異性化におけるその使用
JP5330056B2 (ja) １環芳香族炭化水素の製造方法
KR20190059283A (ko) 알킬방향족 전환 촉매
US10494581B2 (en) Process for producing LPG from a heavy hydrocarbon feed
US11433379B2 (en) Modified USY zeolitic catalyst for isomerization of alkylated aromatics, and method for isomerization of alkylated aromatics
EP3356036B1 (fr) Procédé permettant de produire du gpl à partir d'une charge d'hydrocarbures lourds
US10864505B2 (en) Process for preparing hydrocracking catalyst
CN110088244A (zh) 由c5-c12烃混合物生产btx的方法
RU2834021C1 (ru) Способ и установка для переработки бензиновых фракций
CN118667579B (zh) 一种c10+重芳烃轻质化方法
JP2024544207A (ja) ９個の炭素原子を有する芳香族化合物を転化するデバイスおよび方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16806198

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16806198

Country of ref document: EP

Kind code of ref document: A1