WO2017168982A1 - Électrode négative de batterie rechargeable, batterie rechargeable, bloc-batterie, véhicule électrique, système de stockage d'électricité, outil électrique et dispositif électronique - Google Patents

Électrode négative de batterie rechargeable, batterie rechargeable, bloc-batterie, véhicule électrique, système de stockage d'électricité, outil électrique et dispositif électronique Download PDF

Info

Publication number
WO2017168982A1
WO2017168982A1 PCT/JP2017/001838 JP2017001838W WO2017168982A1 WO 2017168982 A1 WO2017168982 A1 WO 2017168982A1 JP 2017001838 W JP2017001838 W JP 2017001838W WO 2017168982 A1 WO2017168982 A1 WO 2017168982A1
Authority
WO
WIPO (PCT)
Prior art keywords
secondary battery
negative electrode
active material
coating layer
carbonate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2017/001838
Other languages
English (en)
Japanese (ja)
Inventor
中村　利一
松本　健
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sony Corp
Original Assignee
Sony Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sony Corp filed Critical Sony Corp
Publication of WO2017168982A1 publication Critical patent/WO2017168982A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une électrode négative de batterie rechargeable qui permet d'obtenir d'excellentes caractéristiques de batterie. Cette électrode négative de batterie rechargeable contient une poudre de matériau actif d'électrode négative, une couche de revêtement formée sur la poudre de matériau actif d'électrode négative, et un agent de liaison, la couche de revêtement contenant un polymère hydrocarboné qui contient au moins un élément choisi dans le groupe constitué par les liaisons éther, les groupes carbonyle, l'acide carboxylique, les sels d'acide carboxylique, l'acide carbonique et les sels d'acide carbonique.
PCT/JP2017/001838 2016-03-31 2017-01-20 Électrode négative de batterie rechargeable, batterie rechargeable, bloc-batterie, véhicule électrique, système de stockage d'électricité, outil électrique et dispositif électronique Ceased WO2017168982A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016-072094 2016-03-31
JP2016072094 2016-03-31

Publications (1)

Publication Number Publication Date
WO2017168982A1 true WO2017168982A1 (fr) 2017-10-05

Family

ID=59964197

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/001838 Ceased WO2017168982A1 (fr) 2016-03-31 2017-01-20 Électrode négative de batterie rechargeable, batterie rechargeable, bloc-batterie, véhicule électrique, système de stockage d'électricité, outil électrique et dispositif électronique

Country Status (1)

Country Link
WO (1) WO2017168982A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2024021125A (ja) * 2022-08-03 2024-02-16 プライムアースＥｖエナジー株式会社 組電池の製造方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5540826B2 (fr) * 1975-06-24 1980-10-20
JP2004335379A (ja) * 2003-05-09 2004-11-25 Sony Corp 電池用負極、非水電解質電池
JP2005285706A (ja) * 2004-03-31 2005-10-13 Hitachi Maxell Ltd 有機電解液電池
JP2009029677A (ja) * 2007-07-27 2009-02-12 Sumitomo Metal Ind Ltd 黒鉛質粉末とその製造方法
WO2015098023A1 (fr) * 2013-12-26 2015-07-02 三洋電機株式会社 Électrode négative pour batterie rechargeable à électrolyte non aqueux
JP2015156293A (ja) * 2014-02-20 2015-08-27 三菱マテリアル株式会社 リチウムイオン二次電池用及びリチウムイオンキャパシタ用の負極
JP2015525437A (ja) * 2012-05-25 2015-09-03 ネグゼオン・リミテッドＮｅｘｅｏｎ Ｌｔｄ 複合粒子

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5540826B2 (fr) * 1975-06-24 1980-10-20
JP2004335379A (ja) * 2003-05-09 2004-11-25 Sony Corp 電池用負極、非水電解質電池
JP2005285706A (ja) * 2004-03-31 2005-10-13 Hitachi Maxell Ltd 有機電解液電池
JP2009029677A (ja) * 2007-07-27 2009-02-12 Sumitomo Metal Ind Ltd 黒鉛質粉末とその製造方法
JP2015525437A (ja) * 2012-05-25 2015-09-03 ネグゼオン・リミテッドＮｅｘｅｏｎ Ｌｔｄ 複合粒子
WO2015098023A1 (fr) * 2013-12-26 2015-07-02 三洋電機株式会社 Électrode négative pour batterie rechargeable à électrolyte non aqueux
JP2015156293A (ja) * 2014-02-20 2015-08-27 三菱マテリアル株式会社 リチウムイオン二次電池用及びリチウムイオンキャパシタ用の負極

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2024021125A (ja) * 2022-08-03 2024-02-16 プライムアースＥｖエナジー株式会社 組電池の製造方法
JP7589198B2 (ja) 2022-08-03 2024-11-25 トヨタバッテリー株式会社 組電池の製造方法

Similar Documents

Publication Publication Date Title
JP6706461B2 (ja) 二次電池用負極活物質、二次電池用負極、二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP6809487B2 (ja) リチウムイオン二次電池用正極活物質、リチウムイオン二次電池用正極、リチウムイオン二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP5924237B2 (ja) リチウムイオン二次電池用活物質、リチウムイオン二次電池用電極、リチウムイオン二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP2013218875A (ja) 正極活物質、正極、二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
CN110832678A (zh) 二次电池、电池包、电动车辆、电力储存系统、电动工具及电子设备
WO2013145913A1 (fr) Substance active d'électrode positive, électrode positive, cellule secondaire, bloc-cellule, véhicule électrique, système de stockage d'énergie, outil électrique et équipement électronique
JP7056638B2 (ja) 二次電池用負極、二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP6763410B2 (ja) 二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP6686650B2 (ja) 二次電池、電池パック、電動車両、電力貯蔵システム、電動工具及び電子機器
JP2014112476A (ja) 二次電池用活物質、二次電池用電極、二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
WO2014112420A1 (fr) Matériau actif pour batteries secondaires, électrode pour batteries secondaires, batterie secondaire, bloc-batterie, véhicule électrique, système de stockage d'énergie électrique, outil électrique, et dispositif électronique
JP2015064937A (ja) 二次電池用負極、二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JPWO2017094396A1 (ja) 二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP6597793B2 (ja) 二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP6257087B2 (ja) 二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP6874777B2 (ja) 二次電池用負極、二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JP2015156280A (ja) 二次電池用活物質、二次電池用電極、二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
JPWO2017085994A1 (ja) 二次電池、電池パック、電動車両、電力貯蔵システム、電動工具および電子機器
WO2017168982A1 (fr) Électrode négative de batterie rechargeable, batterie rechargeable, bloc-batterie, véhicule électrique, système de stockage d'électricité, outil électrique et dispositif électronique
US11532821B2 (en) Negative electrode for lithium ion secondary battery, lithium ion secondary battery, battery pack, electric vehicle, power storage system, power tool, and electronic device
WO2017168983A1 (fr) Batterie secondaire, châssis de batterie, véhicule électrique, système de stockage d'énergie, outil électrique et dispositif électronique
WO2015194314A1 (fr) Matière active pour batteries secondaires, électrode pour batteries secondaires, batterie secondaire, bloc-batterie, véhicule électrique, système de stockage d'énergie électrique, outil électrique et dispositif électronique

Legal Events

Date Code Title Description
NENP Non-entry into the national phase

Ref country code: DE

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17773532

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 17773532

Country of ref document: EP

Kind code of ref document: A1