WO2017179812A1 - 스파이럴 필라멘트 및 이를 이용한 칫솔 - Google Patents

스파이럴 필라멘트 및 이를 이용한 칫솔 Download PDF

Info

Publication number
WO2017179812A1
WO2017179812A1 PCT/KR2017/001955 KR2017001955W WO2017179812A1 WO 2017179812 A1 WO2017179812 A1 WO 2017179812A1 KR 2017001955 W KR2017001955 W KR 2017001955W WO 2017179812 A1 WO2017179812 A1 WO 2017179812A1
Authority
WO
WIPO (PCT)
Prior art keywords
spiral filament
monofilament
spiral
filament
teeth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2017/001955
Other languages
English (en)
French (fr)
Inventor
강기태
김성진
황소희
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BBC Co Ltd
Original Assignee
BBC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BBC Co Ltd filed Critical BBC Co Ltd
Publication of WO2017179812A1 publication Critical patent/WO2017179812A1/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

본 발명은 치아와 치아 사이, 그리고 치아와 잇몸 사이의 플라크를 효과적으로 제거할 수 있는 스파이럴 필라멘트에 관한 것으로, 단면 형상이 다각형이고, 다각형의 각 모서리가 나선형을 이루도록 비틀어지게 형성된다. 이때, 스파이럴 필라멘트는 다각형의 각 모서리가 1㎝ 당 2 ~ 4회 비틀어진 형태를 가지며, 다각형의 각 모서리 중 적어도 하나가 다른 색상으로 형성된다. 또한, 스파이럴 필라멘트는 단부로 갈수록 단면적이 줄어드는 테이퍼 형상으로 형성된다.

Description

스파이럴 필라멘트 및 이를 이용한 칫솔
본 발명은 스파이럴 필라멘트 및 이를 이용한 칫솔에 관한 것으로, 더욱 자세하게는 치아와 치아 사이, 그리고 치아와 잇몸 사이의 플라크를 효과적으로 제거할 수 있는 스파이럴 필라멘트 및 이를 이용한 칫솔에 관한 것이다.
건강한 치아를 유지하기 위해서는 플라크(plaque) 제거가 중요하다. 플라크를 효과적으로 제거하기 위해서는 칫솔모가 구강 내의 모든 영역까지 도달해야 하며, 특히 치아와 칫솔모 사이에 적절한 마찰 운동이 이루어져야 한다.
통상의 칫솔모를 구성하는 필라멘트는 합성수지재 모노 필라멘트로 원형 단면의 봉 형상으로 제작된다. 이러한 모노 필라멘트는 외주면이 매끈한 곡면으로 형성되어 양치질을 할 때 적절한 측면 마찰력을 얻을 수 없다. 다시 말해, 양치질을 할 때 모노 필라멘트의 끝부분에서만 유효한 마찰력이 발생하게 된다.
전술한 형태의 칫솔모를 사용할 경우 치아의 표면에 형성된 플라크는 제거될 수 있지만 치아와 치아 사이, 그리고 치아와 잇몸 사이의 플라크는 쉽게 제거되지 않는다. 이에, 사람들은 과도한 힘을 주어 칫솔질을 하게 되는데, 과도한 칫솔질은 잇몸을 자극하여 잇몸질환을 유발하게 된다. 특히, 양치질을 할 때 가해진 힘은 칫솔모를 변형시켜 세정력을 저하시킨다.
대한민국공개특허공보 제2014-0109055호(2014.09.15.)에는 모노 필라멘트의 표면에 마찰턱을 형성하여 측면 마찰력을 향상시킨 칫솔모가 개시되어 있다.
상기 칫솔모는, 원뿔형상의 상측에 위치한 첨부가 형성되어 기립상태에서 치아와 접촉되면서 이물질을 제거하는 상부솔과, 원뿔형상의 하측에 원주방향을 따라 마찰턱이 형성되어 휘어진 상태에서 치아와 접촉되면서 이물질을 제거하는 메인 측부솔과, 상기 메인 측부솔에 상협하광의 원통형상이 연결되어 하측에 원주방향에 따른 마찰턱이 형성되고 휘어진 상태에서 치아와 접촉되면서 이물질을 제거하는 보조측부솔이 다수개 연속하여 형성된 단위 칫솔모를 포함한다.
상술한 구조의 칫솔모는 단위 칫솔모를 따라 형성된 다수의 마찰턱으로 인해 측면 마찰력이 향상되고, 이를 통해 치간 및 치경의 플라크를 쉽게 제거할 수 있다. 하지만, 양치질 후 칫솔을 세정하더라도 마찰턱에 끼인 이물질이 쉽게 제거되지 않아 부패의 우려가 있으며, 마찰턱으로 인해 수분의 제거가 어려워 미생물 또는 세균이 번식될 우려가 있다.
본 발명은 전술한 종래 기술의 문제점을 해결하기 위한 것으로서 치아와 치아 사이, 그리고 치아와 잇몸 사이의 플라크를 효과적으로 제거할 수 있는 스파이럴 필라멘트를 제공하는데 그 목적이 있다.
또한, 본 발명은 양치질을 할 때 무리한 힘을 가하더라도 쉽게 벌어지지 않아 칫솔모의 내구성을 향상시킬 수 있는 스파이럴 필라멘트를 제공하는데 그 목적이 있다.
또한, 본 발명은 스파이럴 필라멘트를 이용한 칫솔의 제공을 추가적인 목적으로 한다.
상기 목적을 달성하기 위한 본 발명에 의한 스파이럴 필라멘트는 칫솔모를 구성하는 모노 필라멘트이며, 상기 모노 필라멘트는 단면 형상이 다각형이고, 다각형의 각 모서리가 나선형을 이루도록 비틀어진 형태를 갖는다.
또한, 상기 모노 필라멘트는 단면 형상이 사각형일 수 있으며, 단부로 갈수록 단면적이 줄어드는 테이퍼 형상일 수 있다.
또한, 상기 모노 필라멘트는 모서리 중 적어도 하나가 다른 색상을 가질 수 있다.
상술한 바와 같이 구성된 본 발명은 다각형의 각 모서리가 나선형을 이루도록 비틀어진 형태를 가지므로, 필라멘트의 측면에 나선형의 홈이 일정한 간격으로 반복된다. 따라서 양치질을 할 때 나선형의 홈에 의해 측면 마찰력이 증가하게 되어 치아와 치아 사이, 그리고 치아와 잇몸 사이의 플라크를 효과적으로 제거할 수 있다.
또한, 본 발명의 스파이럴 필라멘트는 각 모서리가 나선형을 이루도록 비틀어진 형태이므로, 양치질을 할 때 과도한 힘이 인가되더라도 쉽게 휘어지거나 벌어지지 않아 칫솔모의 내구성을 향상시킬 수 있다.
도 1은 본 발명의 일 실시예에 따른 스파이럴 필라멘트의 사시도.
도 2는 본 발명의 일 실시예에 따른 스파이럴 필라멘트의 일부를 확대한 도면.
도 3과 도 4는 본 발명의 일 실시예에 따른 스파이럴 필라멘트의 일부를 현미경으로 확대한 사진.
도 5와 도 6은 본 발명의 일 실시예에 따른 스파이럴 필라멘트의 변형례를 도시한 도면.
첨부된 도면을 참조하여 본 발명에 따른 실시예를 상세히 설명한다. 이하, 본 발명에 따른 실시예를 설명함에 있어, 그리고 각 도면의 구성요소들에 참조부호를 부가함에 있어, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 한 동일한 부호를 부가하였다.
도 1에 도시된 바와 같이, 칫솔(1)은, 칫솔모(10)가 식모되는 헤드(20)와, 손잡이 역할을 하는 핸들(30)로 이루어진다.
헤드(20)와 핸들(30)은 폴리프로필렌, 폴리에틸렌, 폴리에틸렌테레프탈레이트, 폴리시클로헥실렌디메틸렌테레프탈레이트, 포화 폴리에스테르 수지, 폴리메타크릴산 메틸, 프로피온산 셀룰로오스, 폴리우레탄, 폴리아미드, ABS(아크로니트릴ㅇ부타디엔ㅇ스티렌) 등의 합성수지로 제작될 수 있다. 특히, 엘라스토머(elastomer) 등의 수지를 핸들(30)에 부분 또는 전체적으로 적용할 경우 미끄럼을 방지할 수 있으며 파지성을 향상시킬 수 있다.
칫솔모(10)는 헤드(20)의 식모면(22)에 식모된 다수의 필라멘트(100)로 구성된다. 칫솔모(10)를 구성하는 필라멘트(100)는 다발의 형태로 묶여 식모되는데, 도 1에 도시된 것처럼 원형으로 묶여 식모되거나 타원형, 장공형, 다각형으로 묶여 식모될 수 있다.
필라멘트(100)는 U자 형상으로 벤딩된 후 고정편(미도시)에 의해 식모면(22)에 고정되거나 열융착을 통해 식모면(22)에 직접 고정될 수 있다.
필라멘트(100)의 재질은 폴리부틸렌테레프탈레이트, 폴리에틸렌테레프탈레이트, 폴리트리메틸렌테레프탈레이트, 폴리사이클로헥산디메틸렌테레프탈레이트 중에서 선택된 1종 또는 2종 이상일 수 있다. 또는, 올레핀계 열가소성 엘라스토머, 스틸렌계 열가소성 엘라스토머, 우레탄계 열가소성 엘라스토머 중에서 선택되는 1종 또는 2종 이상일 수 있다.
전술한 폴리테레프탈레이트계 재질의 필라멘트(100)는 강성이 우수하여 세정력을 향상시킬 수 있고, 열가소성 엘라스토머계 재질은 탄성이 우수하여 잇몸이 손상되는 것을 방지할 수 있다.
또한, 필라멘트(100)는, 나일론 수지, 실리콘 수지, 러버 수지, 생분해성 수지 중 어느 하나의 재질로 제작될 수 있다.
도 2를 참조하여 본 실시예에 따른 스파이럴 필라멘트(100)의 형상을 살펴보면 다음과 같다.
스파이럴 필라멘트(100)는 사각형의 단면 형상을 가지며, 4개의 모서리가 나선형을 이루도록 비틀어진 형태를 갖는다. 스파이럴 필라멘트(100)의 각 모서리 사이에는 나선형의 홈(110)이 형성되는데, 나선형의 홈(110)은 스파이럴 필라멘트(100)를 따라 일정한 간격으로 반복된다. 이때, 스파이럴 필라멘트(100)는 한 변의 길이가 0.1 ~ 0.31㎜로 형성된다.
스파이럴 필라멘트(100)에 형성된 나선형의 홈(110)은 측면 마찰력을 증가시켜 양치질을 할 때 치아와 치아 사이, 그리고 치아와 잇몸 사이의 플라크가 효과적으로 제거될 수 있도록 한다. 특히, 스파이럴 필라멘트(100)의 비틀림 응력은 양치질을 할 때 인가되는 힘을 흡수하여 스파이럴 필라멘트(100)가 쉽게 휘어지거나 벌어지는 것을 방지한다.
본 실시예에서는 스파이럴 필라멘트(100)의 단면 형상을 사각형으로 예시하고 있으나 반드시 이에 한정되는 것은 아니며, 삼각형을 포함하는 다각형으로 형성될 수 있다.
본 실시예의 스파이럴 필라멘트(100)는 4개의 모서리가 1㎝ 당 2 ~ 4회(바람직하게는 2.5회) 비틀어지도록 형성된다(도 3 및 도4 참조). 스파이럴 필라멘트(100)의 비틀림이 2회 미만일 경우 내구성은 증가하지만 플라크를 효과적으로 제거할 수 없으며, 비틀림이 4회를 초과할 경우 플라크의 제거효율은 우수하나 비틀림 한계를 벗어나 외력에 취약한 문제가 있다.
도 5에 도시된 바와 같이, 본 실시예에서는 스파이럴 필라멘트(100)는 단부가 테이퍼지게 형성될 수 있다. 즉, 스파이럴 필라멘트(100)의 단면적이 상단 또는/및 하단으로 갈수록 단면적이 줄어드는 형상으로 형성할 수 있다. 이때, 스파이럴 필라멘트(100)의 테이퍼진 길이는 4 ~ 12㎜인 것이 바람직하다.
이와 같이, 스파이럴 필라멘트(100)의 단부를 테이퍼지게 가공할 경우 치아와 치아 사이, 치아와 잇몸 사이의 플라크를 더욱 효과적으로 제거할 수 있다.
스파이럴 필라멘트(100)의 단부를 테이퍼지게 가공하기 위해서는 화학적 가공방법이 사용된다. 예컨대, 스파이럴 필라멘트(100)의 일단(또는 양단)을 알칼리 또는 산성 용액에 담가 테이퍼 형태로 가공할 수 있다.
도 6에 도시된 바와 같이, 본 실시예에서는 스파이럴 필라멘트(100)는 사각형의 각 모서리 중 적어도 하나가 다른 색상을 가질 수 있다. 스파이럴 필라멘트(100)의 한쪽 모서리에 안료를 혼입하여 다른 색상을 갖도록 할 경우 사용자로 하여금 심미감을 불러일으킬 수 있다. 특히, 온도에 따라 색이 변하는 안료를 사용하면 아이들의 호기심을 자극하여 양치질을 즐겁게 할 수 있도록 도움을 줄 수 있다.
본 실시예에 따른 스파이럴 필라멘트로 구성된 칫솔모의 내구성을 다음의 방법으로 측정하였다.
칫솔모의 내구성은 필라멘트의 벌어짐(A)을 측정하는 wearing test를 말한다. 즉, 본 실시예에 따른 스파이럴 필라멘트(도 1의 100)가 식모된 칫솔을 치아와 유사한 형태의 요철에 초당 2회의 속도로 왕복시킨 후 아래의 수학식 1로 계산하였고, 그 결과는 아래의 표1에 나타내었다.
[수학식 1]
A = {(L2 - L1) / L1} × 100
A : 필라멘트의 벌어짐(%)
L1 : 실험 전 필라멘트의 길이(㎜)
L2 : 실험 후 필라멘트의 길이(㎜)
[실시예 1]
실시예 1의 스파이럴 필라멘트는 폴리부틸렌테레프탈레이트 재질이고 정사각형 단면을 가지며 각 모서리가 1㎝ 당 2.5회 비틀어지게 가공되었다. 이때, 스파이럴 필라멘트의 단부는 도 2와 같은 형태를 갖는다.
[실시예 2]
실시예 2의 스파이럴 필라멘트는 폴리부틸렌테레프탈레이트 재질이고 정사각형 단면을 가지며 각 모서리가 1㎝ 당 2.5회 비틀어지게 가공되었다. 이때, 스파이럴 필라멘트의 단부는 도 3과 같이 테이퍼진 형태를 갖는다.
[비교예 1]
비교예 1의 필라멘트는 폴리부틸렌테레프탈레이트 재질의 원기둥 형상을 가진 일반 필라멘트이다.
왕복 횟수(회) 벌어짐(%)
실시예 1 10,000 0
20,000 1.3
50,000 10.2
실시예 2 10,000 0
20,000 1.5
50,000 12.3
비교예 1 10,000 0
20,000 18.2
50,000 42.6
이상 본 발명을 바람직한 실시예를 통하여 설명하였는데, 상술한 실시예는 본 발명의 기술적 사상을 예시적으로 설명한 것에 불과하며, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 다양한 변화가 가능함은 이 분야에서 통상의 지식을 가진 자라면 이해할 수 있을 것이다. 따라서 본 발명의 보호범위는 특정 실시예가 아니라 특허청구범위에 기재된 사항에 의해 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술적 사상도 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.

Claims (11)

  1. 칫솔모를 구성하는 모노 필라멘트에 있어서,
    상기 모노 필라멘트는 단면 형상이 다각형이고, 다각형의 각 모서리가 나선형을 이루도록 비틀어진 것을 특징으로 하는 스파이럴 필라멘트.
  2. 청구항 1에 있어서,
    상기 모노 필라멘트는 단면 형상이 사각형인 것을 특징으로 하는 스파이럴 필라멘트.
  3. 청구항 2에 있어서,
    상기 모노 필라멘트는 단부로 갈수록 단면적이 줄어드는 테이퍼 형상인 것을 특징으로 하는 스파이럴 필라멘트.
  4. 청구항 3에 있어서,
    상기 모노 필라멘트는 모서리 중 적어도 하나가 다른 색상을 가진 것을 특징으로 하는 스파이럴 필라멘트.
  5. 청구항 4에 있어서,
    상기 모노 필라멘트는 각 모서리가 1㎝ 당 2 ~ 4회 비틀어진 것을 특징으로 하는 스파이럴 필라멘트.
  6. 청구항 5에 있어서,
    상기 모노 필라멘트는 한 변의 길이가 0.1 ~ 0.31㎜인 것을 특징으로 하는 스파이럴 필라멘트.
  7. 청구항 6에 있어서,
    상기 모노 필라멘트의 테이퍼진 길이는 4 ~ 12㎜인 것을 특징으로 하는 스파이럴 필라멘트.
  8. 청구항 7에 있어서,
    상기 모노 필라멘트는, 폴리부틸렌테레프탈레이트, 폴리에틸렌테레프탈레이트, 폴리트리메틸렌테레프탈레이트, 폴리사이클로헥산디메틸렌테레프탈레이트 중에서 선택된 1종 또는 2종 이상의 재질로 제작된 것을 특징으로 하는 스파이럴 필라멘트.
  9. 청구항 7에 있어서,
    상기 모노 필라멘트는, 올레핀계 열가소성 엘라스토머, 스틸렌계 열가소성 엘라스토머, 우레탄계 열가소성 엘라스토머 중에서 선택되는 1종 또는 2종 이상의 재질로 제작된 것을 특징으로 하는 스파이럴 필라멘트.
  10. 청구항 7에 있어서,
    상기 모노 필라멘트는, 나일론 수지, 실리콘 수지, 러버 수지, 생분해성 수지 중 어느 하나의 재질로 제작된 것을 특징으로 하는 스파이럴 필라멘트.
  11. 청구항 1 내지 청구항 10 중 어느 한 항에 따른 스파이럴 필라멘트를 이용한 칫솔.
PCT/KR2017/001955 2016-04-12 2017-02-22 스파이럴 필라멘트 및 이를 이용한 칫솔 Ceased WO2017179812A1 (ko)