WO2019074041A1 - Composition de revêtement en poudre, et procédé de formation de film de revêtement - Google Patents

Composition de revêtement en poudre, et procédé de formation de film de revêtement Download PDF

Info

Publication number
WO2019074041A1
WO2019074041A1 PCT/JP2018/037873 JP2018037873W WO2019074041A1 WO 2019074041 A1 WO2019074041 A1 WO 2019074041A1 JP 2018037873 W JP2018037873 W JP 2018037873W WO 2019074041 A1 WO2019074041 A1 WO 2019074041A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder coating
less
coating composition
coating film
solubility parameter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/037873
Other languages
English (en)
Japanese (ja)
Inventor
綾 原
智哉 辻
雅巳 薮田
小川　英明
斎藤　洋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Paint Industrial Coatings Co Ltd
Original Assignee
Nippon Paint Industrial Coatings Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Paint Industrial Coatings Co Ltd filed Critical Nippon Paint Industrial Coatings Co Ltd
Priority to CN201880065853.XA priority Critical patent/CN111164165B/zh
Priority to JP2018555299A priority patent/JP6567783B1/ja
Publication of WO2019074041A1 publication Critical patent/WO2019074041A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La composition de revêtement en poudre de l'invention permet de former un film de revêtement lisse possédant une excellente apparence, et permet en outre de former un film de revêtement possédant une excellente résistance aux chocs et une excellente résistance à l'abrasion. Plus précisément, l'invention concerne une composition de revêtement en poudre qui contient en tant que résine de formation de film de revêtement une résine acrylique (A) et une résine polyester (B). Ladite résine acrylique (A) possède un groupe époxy, et présente un paramètre de solubilité (SP(A)) supérieur ou égal à 9,0 et inférieur ou égal à 12,0, et une masse moléculaire moyenne supérieure ou égale à 500 et inférieure ou égale à 4000. La masse équivalente en époxy dans ladite résine acrylique (A) est supérieure ou égale à ２００ｇ／ｅｑ et inférieure ou égale à ５００ｇ／ｅｑ. Ladite résine polyester (B) possède un groupe carboxyle, et présente un paramètre de solubilité (SP(B)) supérieur ou égal à 9,0 et inférieur ou égal à 11,0. La valeur absolue ｜ＳＰ（Ａ）－ＳＰ（Ｂ）｜obtenue par soustraction du paramètre de solubilité (SP(B)) au paramètre de solubilité (SP(A)), est supérieure ou égale à 0 et inférieure ou égale à 2.
PCT/JP2018/037873 2017-10-13 2018-10-11 Composition de revêtement en poudre, et procédé de formation de film de revêtement Ceased WO2019074041A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201880065853.XA CN111164165B (zh) 2017-10-13 2018-10-11 粉末涂料组合物和涂膜形成方法
JP2018555299A JP6567783B1 (ja) 2017-10-13 2018-10-11 粉体塗料組成物及び塗膜形成方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-199085 2017-10-13
JP2017199085 2017-10-13

Publications (1)

Publication Number Publication Date
WO2019074041A1 true WO2019074041A1 (fr) 2019-04-18

Family

ID=66100583

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/037873 Ceased WO2019074041A1 (fr) 2017-10-13 2018-10-11 Composition de revêtement en poudre, et procédé de formation de film de revêtement

Country Status (3)

Country Link
JP (1) JP6567783B1 (fr)
CN (1) CN111164165B (fr)
WO (1) WO2019074041A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111892860A (zh) * 2020-08-05 2020-11-06 陕西蓝晟新材料研发有限公司 蓄能发光型粉末涂料和生产施工方法
JPWO2021075412A1 (fr) * 2019-10-18 2021-04-22
JP7038250B1 (ja) 2021-11-24 2022-03-17 日本ペイント・インダストリアルコ－ティングス株式会社 艶調整粉体塗料組成物、艶調整硬化塗膜を有する塗装物品及び艶調整硬化塗膜の形成方法
JP2023134864A (ja) * 2022-03-15 2023-09-28 関西ペイント株式会社 粉体塗料の製造方法
EP4273198A4 (fr) * 2020-12-29 2024-12-18 Tiger New Surface Materials (Suzhou) Co., Ltd. Composition de revêtement de poudre d'étalement et couche de revêtement associée

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112680074B (zh) * 2020-12-29 2022-05-06 老虎表面技术新材料（苏州）有限公司 一种消光超低温固化粉末涂料组合物及其涂层
CN112708332A (zh) * 2020-12-29 2021-04-27 老虎表面技术新材料（苏州）有限公司 一种耐候耐高温粉末涂料组合物
CN114163905B (zh) * 2021-12-24 2023-02-14 老虎表面技术新材料（清远）有限公司 一种粉末涂料组合物及其涂层
CN116253684A (zh) * 2023-02-17 2023-06-13 天津工业大学 一种2-十七烷基咪唑及其合成方法

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08319438A (ja) * 1995-02-28 1996-12-03 Morton Internatl Inc 耐候性アクリルコーティング粉末
JP2001064574A (ja) * 1999-08-31 2001-03-13 Nippon Paint Co Ltd 熱硬化性粉体塗料組成物
JP2003342520A (ja) * 2002-05-28 2003-12-03 Mitsui Chemicals Inc 熱硬化性粉体塗料組成物
JP2004050104A (ja) * 2002-07-22 2004-02-19 Mitsui Chemicals Inc 熱硬化複層塗膜およびその形成方法
WO2004056497A1 (fr) * 2002-12-20 2004-07-08 Kansai Paint Co., Ltd. Procede permettant de former un film de revetement sur un substrat d'aluminium
JP2006504832A (ja) * 2002-11-04 2006-02-09 サーフェース スペシャリティーズ、エス．エイ． 酸無水物末端封鎖結晶ポリエステルを含有する粉末被覆組成物
JP2007217622A (ja) * 2006-02-20 2007-08-30 Meiji Natl Ind Co Ltd 高拡散高反射用粉体塗料及びその塗料を用いた反射板
JP2012532936A (ja) * 2009-07-07 2012-12-20 サイテック サーフェース スペシャリティーズ、エス．エイ． 低温硬化粉体コーティング組成物
JP2013076019A (ja) * 2011-09-30 2013-04-25 Dainippon Toryo Co Ltd 粉体塗料組成物

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6313221B1 (en) * 1999-05-28 2001-11-06 Nippon Paint Co., Ltd. Powder coating of epoxy-acrylic resin, polycarboxylic acid, crosslinked particles and liquid resin

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08319438A (ja) * 1995-02-28 1996-12-03 Morton Internatl Inc 耐候性アクリルコーティング粉末
JP2001064574A (ja) * 1999-08-31 2001-03-13 Nippon Paint Co Ltd 熱硬化性粉体塗料組成物
JP2003342520A (ja) * 2002-05-28 2003-12-03 Mitsui Chemicals Inc 熱硬化性粉体塗料組成物
JP2004050104A (ja) * 2002-07-22 2004-02-19 Mitsui Chemicals Inc 熱硬化複層塗膜およびその形成方法
JP2006504832A (ja) * 2002-11-04 2006-02-09 サーフェース スペシャリティーズ、エス．エイ． 酸無水物末端封鎖結晶ポリエステルを含有する粉末被覆組成物
WO2004056497A1 (fr) * 2002-12-20 2004-07-08 Kansai Paint Co., Ltd. Procede permettant de former un film de revetement sur un substrat d'aluminium
JP2007217622A (ja) * 2006-02-20 2007-08-30 Meiji Natl Ind Co Ltd 高拡散高反射用粉体塗料及びその塗料を用いた反射板
JP2012532936A (ja) * 2009-07-07 2012-12-20 サイテック サーフェース スペシャリティーズ、エス．エイ． 低温硬化粉体コーティング組成物
JP2013076019A (ja) * 2011-09-30 2013-04-25 Dainippon Toryo Co Ltd 粉体塗料組成物

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2021075412A1 (fr) * 2019-10-18 2021-04-22
CN111892860A (zh) * 2020-08-05 2020-11-06 陕西蓝晟新材料研发有限公司 蓄能发光型粉末涂料和生产施工方法
EP4273198A4 (fr) * 2020-12-29 2024-12-18 Tiger New Surface Materials (Suzhou) Co., Ltd. Composition de revêtement de poudre d'étalement et couche de revêtement associée
JP7038250B1 (ja) 2021-11-24 2022-03-17 日本ペイント・インダストリアルコ－ティングス株式会社 艶調整粉体塗料組成物、艶調整硬化塗膜を有する塗装物品及び艶調整硬化塗膜の形成方法
JP2023077199A (ja) * 2021-11-24 2023-06-05 日本ペイント・インダストリアルコーティングス株式会社 艶調整粉体塗料組成物、艶調整硬化塗膜を有する塗装物品及び艶調整硬化塗膜の形成方法
JP2023134864A (ja) * 2022-03-15 2023-09-28 関西ペイント株式会社 粉体塗料の製造方法

Also Published As

Publication number Publication date
CN111164165A (zh) 2020-05-15
JP6567783B1 (ja) 2019-08-28
CN111164165B (zh) 2021-11-09
JPWO2019074041A1 (ja) 2019-11-14

Similar Documents

Publication Publication Date Title
JP6567783B1 (ja) 粉体塗料組成物及び塗膜形成方法
JP5010806B2 (ja) 粉体塗料組成物及びアルミホイールの塗装方法
US5907006A (en) Compositions for the coating of substrates of matt appearance
US11512221B2 (en) Powder paint composition
US20080085965A1 (en) Thermosetting Powder Coating Composition
JP6817289B2 (ja) 高耐久性ばねおよびその塗装方法
JPH06293867A (ja) 艶消粉体塗料組成物、塗装方法および塗膜
JP5175509B2 (ja) 粉体塗料組成物
JPH11300271A (ja) 複層粉体塗膜の形成方法
JP4217380B2 (ja) 多層被覆を有する支持体およびその製造方法
JP2013119582A (ja) 金属亜鉛含有の粉体塗料組成物
JP2002233819A (ja) 鋼材の粉体塗装方法および粉体塗装鋼材
JP4234474B2 (ja) 粉体塗料組成物
JP6814857B1 (ja) 粉体塗料組成物、その製造方法及びそれを用いた塗膜形成方法
JP2024057339A (ja) 粉体塗料組成物の製造方法、塗膜形成方法及び調色方法
JP7730616B2 (ja) エポキシ樹脂粉体塗料
JP7038250B1 (ja) 艶調整粉体塗料組成物、艶調整硬化塗膜を有する塗装物品及び艶調整硬化塗膜の形成方法
JP4197164B2 (ja) 熱硬化型粉体塗料、塗装鉄系資材及び塗装鉄系資材の製造方法
JP2003003122A (ja) 熱硬化型粉体塗料及び熱硬化粉体塗膜形成方法
JP6254191B2 (ja) 耐食性ｔｇｉｃプライマーコーティング
JP2025158842A (ja) 粉体塗料組成物、塗膜、塗装品および粉体塗料組成物の製造方法
JP2002275420A (ja) 熱硬化型粉体塗料及び熱硬化粉体塗膜形成方法
JP2004131663A (ja) 光輝性粉体塗料組成物及びその塗膜形成方法
JP2003176453A (ja) 粉体流動に優れた粉体塗料
EP1230986A1 (fr) Procede d'application de revetement pulverulent a base de fluororesine thermodurcissable

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2018555299

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18866006

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18866006

Country of ref document: EP

Kind code of ref document: A1