WO2019079995A1 - Procédé de scellement hermétique de verre à vide plat - Google Patents

Procédé de scellement hermétique de verre à vide plat

Info

Publication number
WO2019079995A1
WO2019079995A1 PCT/CN2017/107620 CN2017107620W WO2019079995A1 WO 2019079995 A1 WO2019079995 A1 WO 2019079995A1 CN 2017107620 W CN2017107620 W CN 2017107620W WO 2019079995 A1 WO2019079995 A1 WO 2019079995A1
Authority
WO
WIPO (PCT)
Prior art keywords
sealing
glass
temperature
assembly
vacuum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2017/107620
Other languages
English (en)
Chinese (zh)
Inventor
宋驁天
杜争
叶岩
曹雪峰
王墨涵
郑剑锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Pavo-Tech Development Co Ltd
Original Assignee
Shenzhen Pavo-Tech Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Pavo-Tech Development Co Ltd filed Critical Shenzhen Pavo-Tech Development Co Ltd
Priority to CN201780015498.0A priority Critical patent/CN109415253B/zh
Priority to PCT/CN2017/107620 priority patent/WO2019079995A1/fr
Publication of WO2019079995A1 publication Critical patent/WO2019079995A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un procédé de scellement hermétique de verre à vide plat, comprenant : dans une chambre à vide, le chauffage d'un élément pré-assemblé comprenant un verre plat, un matériau de scellement, et un élément de support, la mise sous vide de la chambre à vide en même temps pour éliminer l'air à l'intérieur de l'élément pré-assemblé, puis l'application d'une pression perpendiculaire à la direction horizontale du verre à l'élément pré-assemblé pour mettre en oeuvre le scellement hermétique, et enfin, le refroidissement et la solidification pour obtenir un verre à vide plat scellé. Le procédé est un procédé en une étape : l'application d'une pression à l'intérieur d'une chambre à vide pour fabriquer un flux de matériau pour former une structure stable, et la réalisation d'un chauffage et d'un scellement, ce qui permet de mettre en oeuvre l'exécution simultanée du scellement et de la mise sous vide. Par comparaison à la technologie classique, le procédé améliore l'efficacité de production. En faisant s'écouler le matériau d'étanchéité, lorsqu'il est ramolli, au moyen d'un procédé de pressage à chaud pour former une structure stable évitant la concentration des contraintes, un rendement supérieur à celui de la technologie classique est obtenu.
PCT/CN2017/107620 2017-10-25 2017-10-25 Procédé de scellement hermétique de verre à vide plat Ceased WO2019079995A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201780015498.0A CN109415253B (zh) 2017-10-25 2017-10-25 一种平板真空玻璃的封接方法
PCT/CN2017/107620 WO2019079995A1 (fr) 2017-10-25 2017-10-25 Procédé de scellement hermétique de verre à vide plat

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN2017/107620 WO2019079995A1 (fr) 2017-10-25 2017-10-25 Procédé de scellement hermétique de verre à vide plat

Publications (1)

Publication Number Publication Date
WO2019079995A1 true WO2019079995A1 (fr) 2019-05-02

Family

ID=65463379

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2017/107620 Ceased WO2019079995A1 (fr) 2017-10-25 2017-10-25 Procédé de scellement hermétique de verre à vide plat

Country Status (2)

Country Link
CN (1) CN109415253B (fr)
WO (1) WO2019079995A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110054421A (zh) * 2019-05-16 2019-07-26 天津南玻节能玻璃有限公司 一种干法夹层玻璃生产设备及夹层玻璃的生产方法
CN114436546A (zh) * 2022-03-03 2022-05-06 刘浩 一种真空玻璃封接工艺
CN114804661A (zh) * 2022-04-08 2022-07-29 中国建筑材料科学研究总院有限公司 一种玻璃封接方法及真空玻璃
CN115974427A (zh) * 2022-11-30 2023-04-18 四川英诺维新材料科技有限公司 一种真空玻璃用全自动真空封接方法
CN116217096A (zh) * 2023-03-07 2023-06-06 福耀高性能玻璃科技(福建)有限公司 真空玻璃封口方法及装置
CN117509129A (zh) * 2023-12-20 2024-02-06 武汉国创科光电装备有限公司 一种用于显示面板加工的转送装置及喷墨打印系统
CN118623609A (zh) * 2024-08-12 2024-09-10 天津文洲机械有限公司 用于玻璃烘干风冷的立式传动机构及玻璃烘干风冷一体机

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111847904A (zh) * 2019-04-26 2020-10-30 山东晟芳铭玻璃科技有限公司 真空玻璃制备方法
CN111847903B (zh) * 2019-04-26 2024-08-27 山东晟芳铭玻璃科技有限公司 封装装置
CN110894141A (zh) * 2019-12-18 2020-03-20 深圳孔雀科技开发有限公司 一种真空玻璃连续封接方法
CN111302299B (zh) * 2020-02-20 2023-08-22 北京晨晶电子有限公司 一种焊接密封系统及焊接密封工艺
CN112777952A (zh) * 2021-02-07 2021-05-11 东莞帕萨电子装备有限公司 真空玻璃用连续加工装置及加工方法
CN112759282B (zh) * 2021-02-07 2025-01-07 东莞帕萨电子装备有限公司 真空玻璃焊接腔及真空玻璃加工设备
CN114163145B (zh) * 2021-11-01 2023-12-01 中国科学院上海光学精密机械研究所 带金属电极的石英基底的封接方法及其专用夹具
CN114195372A (zh) * 2021-12-16 2022-03-18 重庆英诺维节能环保科技有限公司 一种真空玻璃的退火冷却方法
CN115420273A (zh) * 2022-08-31 2022-12-02 张雷 一种激光陀螺中谐振腔与反射镜的装配工艺
CN117776556B (zh) * 2023-12-27 2026-04-21 四川英诺维新材料科技有限公司 一种真空玻璃封接装置
CN117776557A (zh) * 2023-12-27 2024-03-29 四川英诺维新材料科技有限公司 一种真空玻璃封接工艺

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102863158A (zh) * 2011-07-05 2013-01-09 洛阳兰迪玻璃机器股份有限公司 真空玻璃封接方法及装置
US20130255317A1 (en) * 2007-12-14 2013-10-03 Guardian Industries Corp. Evacuation and port sealing techniques for vacuum insulating glass units, and/or vacuum oven for accomplishing the same
KR101378043B1 (ko) * 2012-11-13 2014-03-26 주식회사 이건창호 고진공을 갖는 진공유리패널 제조장치 및 제조방법
CN104743916A (zh) * 2013-12-25 2015-07-01 戴长虹 密封槽封边金属焊接的平面真空玻璃及其制作方法
CN105293877A (zh) * 2015-11-05 2016-02-03 金弼 一种复合玻璃的制造方法及设备
CN107216021A (zh) * 2017-06-15 2017-09-29 朱盛菁 一种真空玻璃及其加工方法

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104003629A (zh) * 2011-07-05 2014-08-27 洛阳兰迪玻璃机器股份有限公司 真空玻璃封接方法
CN105541132B (zh) * 2015-12-15 2019-01-04 洛阳兰迪玻璃机器股份有限公司 一种钢化真空玻璃的制作方法及其生产线

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130255317A1 (en) * 2007-12-14 2013-10-03 Guardian Industries Corp. Evacuation and port sealing techniques for vacuum insulating glass units, and/or vacuum oven for accomplishing the same
CN102863158A (zh) * 2011-07-05 2013-01-09 洛阳兰迪玻璃机器股份有限公司 真空玻璃封接方法及装置
KR101378043B1 (ko) * 2012-11-13 2014-03-26 주식회사 이건창호 고진공을 갖는 진공유리패널 제조장치 및 제조방법
CN104743916A (zh) * 2013-12-25 2015-07-01 戴长虹 密封槽封边金属焊接的平面真空玻璃及其制作方法
CN105293877A (zh) * 2015-11-05 2016-02-03 金弼 一种复合玻璃的制造方法及设备
CN107216021A (zh) * 2017-06-15 2017-09-29 朱盛菁 一种真空玻璃及其加工方法

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110054421A (zh) * 2019-05-16 2019-07-26 天津南玻节能玻璃有限公司 一种干法夹层玻璃生产设备及夹层玻璃的生产方法
CN110054421B (zh) * 2019-05-16 2024-04-16 天津南玻节能玻璃有限公司 一种干法夹层玻璃生产设备及夹层玻璃的生产方法
CN114436546A (zh) * 2022-03-03 2022-05-06 刘浩 一种真空玻璃封接工艺
CN114436546B (zh) * 2022-03-03 2024-04-26 刘浩 一种真空玻璃封接工艺
CN114804661A (zh) * 2022-04-08 2022-07-29 中国建筑材料科学研究总院有限公司 一种玻璃封接方法及真空玻璃
CN114804661B (zh) * 2022-04-08 2023-10-27 中国建筑材料科学研究总院有限公司 一种玻璃封接方法及真空玻璃
CN115974427A (zh) * 2022-11-30 2023-04-18 四川英诺维新材料科技有限公司 一种真空玻璃用全自动真空封接方法
CN116217096A (zh) * 2023-03-07 2023-06-06 福耀高性能玻璃科技(福建)有限公司 真空玻璃封口方法及装置
CN117509129A (zh) * 2023-12-20 2024-02-06 武汉国创科光电装备有限公司 一种用于显示面板加工的转送装置及喷墨打印系统
CN118623609A (zh) * 2024-08-12 2024-09-10 天津文洲机械有限公司 用于玻璃烘干风冷的立式传动机构及玻璃烘干风冷一体机

Also Published As

Publication number Publication date
CN109415253A (zh) 2019-03-01
CN109415253B (zh) 2022-04-22

Similar Documents

Publication Publication Date Title
WO2019079995A1 (fr) Procédé de scellement hermétique de verre à vide plat
RU2690981C1 (ru) Способ изготовления и производственная линия одного типа закаленного вакуумного стекла
US20260071480A1 (en) Manufacturing of vacuum insulated glazing unit
JP6456290B2 (ja) レーザによる低温気密封止
JP6695427B2 (ja) 強化真空ガラスの製造方法及びその生産ライン
WO2016078593A1 (fr) Vitre sous vide et son procédé de production
JP6806887B2 (ja) 真空断熱ガラスパネル組立体の製造方法及び装置
WO2001016045A1 (fr) Procede de fabrication de vitrage sous vide et systeme mecanique d'application
CN103373805B (zh) 钢化、半钢化真空玻璃及其制造方法
EP3070060A1 (fr) Procédé de fabrication de verre trempé sous vide
CN106573835A (zh) 真空复层玻璃的制造方法、以及真空复层玻璃
CN102951820A (zh) 真空玻璃及其制备方法
US10465436B2 (en) Evacuation head with ceramic heater for VIG unit manufacture
JP4510296B2 (ja) シールされた真空の二重ガラス窓及びその製造方法
EP3821101A1 (fr) Fabrication d'ensembles de feuilles de verre au moyen d'un matériau d'étanchéité de bord préchauffé
CN105632902B (zh) 一种利用半导体制冷片进行高低温可控晶圆键合的方法
CN102953439B (zh) 凸面真空隔热板及其制备方法
CN112777953A (zh) 一种钢化真空玻璃的制作方法及其生产线
CN102092923A (zh) 一种真空玻璃排气口气密封接方法和装置
CN112777954A (zh) 有抽气口的钢化真空玻璃及其制作方法和生产线
CN105082662B (zh) 一种减少柔性基体上高熔点金属薄膜产生裂纹的方法
CN111411329A (zh) 平面锂靶材组件的制造方法和设备
JP2003059399A (ja) 画像表示装置の製造方法及び製造装置
CN110894141A (zh) 一种真空玻璃连续封接方法
JP2003141995A (ja) ガス放電パネルの製造方法およびその製造装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17930150

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17930150

Country of ref document: EP

Kind code of ref document: A1

32PN Ep: public notification in the ep bulletin as address of the adressee cannot be established

Free format text: NOTING OF LOSS OF RIGHTS PURSUANT TO RULE 112(1) EPC (EPO FORM 1205A DATED 16-09-2020)

122 Ep: pct application non-entry in european phase

Ref document number: 17930150

Country of ref document: EP

Kind code of ref document: A1