WO2019142803A1 - Résine de matrice, matériau intermédiaire, et article moulé - Google Patents

Résine de matrice, matériau intermédiaire, et article moulé Download PDF

Info

Publication number
WO2019142803A1
WO2019142803A1 PCT/JP2019/001017 JP2019001017W WO2019142803A1 WO 2019142803 A1 WO2019142803 A1 WO 2019142803A1 JP 2019001017 W JP2019001017 W JP 2019001017W WO 2019142803 A1 WO2019142803 A1 WO 2019142803A1
Authority
WO
WIPO (PCT)
Prior art keywords
component
matrix resin
mass
resin
formula
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2019/001017
Other languages
English (en)
Japanese (ja)
Inventor
隼人 小笠原
征司 土屋
小並　諭吉
洋之 中尾
鍋島　泰彦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Chemical Corp
Original Assignee
Mitsubishi Chemical Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Chemical Corp filed Critical Mitsubishi Chemical Corp
Priority to JP2019506461A priority Critical patent/JP6791354B2/ja
Publication of WO2019142803A1 publication Critical patent/WO2019142803A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention fournit une résine de matrice permettant d'élargir une fenêtre de traitement. Plus précisément, l'invention concerne une résine de matrice qui contient au moins un mélange des composants （Ａ－１） à （Ａ－４） suivants. Composant （Ａ－１） : à la fois une résine (méth)acrylate époxy et une résine polyester insaturé qui possèdent au moins un groupe éhyléniquement insaturé dans chaque molécule et présentant un nombre moyen de groupes hydroxyle compris entre 1,8 et 4. Composant （Ａ－2） : un monomère éhyléniquement insaturé. Composant （Ａ－3） : un polyisocyanate présentant une teneur en groupe isocyanate comprise entre 15 et 30,5% en masse , et présentant un nombre moyen de groupes isocyanate compris entre 1,8 et 2,4. Composant （Ａ－4） : un initiateur de polymérisation thermique.
PCT/JP2019/001017 2018-01-16 2019-01-16 Résine de matrice, matériau intermédiaire, et article moulé Ceased WO2019142803A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2019506461A JP6791354B2 (ja) 2018-01-16 2019-01-16 マトリクス樹脂、中間材及び成形品

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018004833 2018-01-16
JP2018-004833 2018-01-16

Publications (1)

Publication Number Publication Date
WO2019142803A1 true WO2019142803A1 (fr) 2019-07-25

Family

ID=67301018

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/001017 Ceased WO2019142803A1 (fr) 2018-01-16 2019-01-16 Résine de matrice, matériau intermédiaire, et article moulé

Country Status (2)

Country Link
JP (1) JP6791354B2 (fr)
WO (1) WO2019142803A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2021193248A1 (fr) * 2020-03-27 2021-09-30
JP2022513473A (ja) * 2018-12-11 2022-02-08 トリマー テクノロジーズ エルエルシー ポリイソシアヌレート系ポリマー及び繊維強化複合材料
CN114729144A (zh) * 2019-12-25 2022-07-08 Dic株式会社 预浸料和成形品
JP2022180095A (ja) * 2021-05-24 2022-12-06 Dic株式会社 ラジカル硬化性樹脂組成物、成形材料、及びそれを用いた成形品
JP2023070793A (ja) * 2021-11-10 2023-05-22 日本ユピカ株式会社 液状組成物及び該液状組成物を用いた繊維強化複合材料

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5667322A (en) * 1979-11-05 1981-06-06 Showa Highpolymer Co Ltd Curable resin composition
JPH03103422A (ja) * 1989-05-11 1991-04-30 Teijin Ltd 複合系硬化性液状樹脂組成物
JP2005154589A (ja) * 2003-11-26 2005-06-16 Dainippon Ink & Chem Inc シートモールディングコンパウンド及びバルクモールディングコンパウンド用樹脂組成物、及びその応用
WO2016039326A1 (fr) * 2014-09-12 2016-03-17 三菱レイヨン株式会社 Matériau de moulage, mélange à mouler en feuille et matériau composite renforcé par des fibres obtenu à l'aide de celui-ci
WO2017175430A1 (fr) * 2016-04-06 2017-10-12 三菱ケミカル株式会社 Composition de résine thermodurcissable, préimprégné en feuille ainsi que procédé de fabrication de celui-ci, et matériau composite renforcé par des fibres
JP2018048238A (ja) * 2016-09-20 2018-03-29 三菱ケミカル株式会社 熱硬化性樹脂組成物、成形材料、繊維強化複合材料、及びシートモールディングコンパウンドの製造方法
WO2019017254A1 (fr) * 2017-07-20 2019-01-24 三菱ケミカル株式会社 Composé pour moulage de feuille, matériau composite renforcé par fibres, et procédé de production d'un matériau composite renforcé par fibres

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5667322A (en) * 1979-11-05 1981-06-06 Showa Highpolymer Co Ltd Curable resin composition
JPH03103422A (ja) * 1989-05-11 1991-04-30 Teijin Ltd 複合系硬化性液状樹脂組成物
JP2005154589A (ja) * 2003-11-26 2005-06-16 Dainippon Ink & Chem Inc シートモールディングコンパウンド及びバルクモールディングコンパウンド用樹脂組成物、及びその応用
WO2016039326A1 (fr) * 2014-09-12 2016-03-17 三菱レイヨン株式会社 Matériau de moulage, mélange à mouler en feuille et matériau composite renforcé par des fibres obtenu à l'aide de celui-ci
WO2017175430A1 (fr) * 2016-04-06 2017-10-12 三菱ケミカル株式会社 Composition de résine thermodurcissable, préimprégné en feuille ainsi que procédé de fabrication de celui-ci, et matériau composite renforcé par des fibres
JP2018048238A (ja) * 2016-09-20 2018-03-29 三菱ケミカル株式会社 熱硬化性樹脂組成物、成形材料、繊維強化複合材料、及びシートモールディングコンパウンドの製造方法
WO2019017254A1 (fr) * 2017-07-20 2019-01-24 三菱ケミカル株式会社 Composé pour moulage de feuille, matériau composite renforcé par fibres, et procédé de production d'un matériau composite renforcé par fibres

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2022513473A (ja) * 2018-12-11 2022-02-08 トリマー テクノロジーズ エルエルシー ポリイソシアヌレート系ポリマー及び繊維強化複合材料
JP7671986B2 (ja) 2018-12-11 2025-05-07 トリマー テクノロジーズ エルエルシー ポリイソシアヌレート系ポリマー及び繊維強化複合材料
CN114729144A (zh) * 2019-12-25 2022-07-08 Dic株式会社 预浸料和成形品
CN114729144B (zh) * 2019-12-25 2024-04-12 Dic株式会社 预浸料和成形品
JPWO2021193248A1 (fr) * 2020-03-27 2021-09-30
WO2021193248A1 (fr) * 2020-03-27 2021-09-30 旭化成株式会社 Matériau composite de résine renforcée par des fibres continues, son procédé de fabrication et produit moulé en résine renforcée par des fibres continues
JP7253112B2 (ja) 2020-03-27 2023-04-05 旭化成株式会社 連続繊維強化樹脂複合材料及びその製造方法、並びに連続繊維強化樹脂成形体
US12441883B2 (en) 2020-03-27 2025-10-14 Asahi Kasei Kabushiki Kaisha Continuous fiber reinforced resin composite material and method of producing same, and continuous fiber reinforced resin molded article
JP2022180095A (ja) * 2021-05-24 2022-12-06 Dic株式会社 ラジカル硬化性樹脂組成物、成形材料、及びそれを用いた成形品
JP7739763B2 (ja) 2021-05-24 2025-09-17 Dic株式会社 ラジカル硬化性樹脂組成物、成形材料、及びそれを用いた成形品
JP2023070793A (ja) * 2021-11-10 2023-05-22 日本ユピカ株式会社 液状組成物及び該液状組成物を用いた繊維強化複合材料
JP7760337B2 (ja) 2021-11-10 2025-10-27 三菱ガス化学ネクスト株式会社 液状組成物及び該液状組成物を用いた繊維強化複合材料

Also Published As

Publication number Publication date
JPWO2019142803A1 (ja) 2020-01-23
JP6791354B2 (ja) 2020-11-25

Similar Documents

Publication Publication Date Title
JP6791354B2 (ja) マトリクス樹脂、中間材及び成形品
US20230139814A1 (en) Sheet molding compound, fiber-reinforced composite material, and method for producing fiber-reinforced composite material
CN111133040B (zh) 预浸渍体用树脂组合物、预浸渍体及成型品
EP3395869B1 (fr) Préimprégné et article moulé
US10920009B2 (en) Thermosetting resin composition, sheet-molding compound and production method therefor, and fiber-reinforced composite material
CN111164137B (zh) 预浸渍体用树脂组合物、预浸渍体及成型品
JP6156612B1 (ja) 加熱圧縮成形用成形材料、それを用いた成形品及びその製造方法
WO2017163899A1 (fr) Préimprégné et article moulé
US10899856B2 (en) Molding material, sheet molding compound and fiber-reinforced composite material
JP5950050B2 (ja) 加熱圧縮成形用成形材料、それを用いた成形品及びその製造方法
WO2021131566A1 (fr) Pré-imprégné et article moulé
JP2018187862A (ja) 炭素繊維強化複合材料成形品の製造方法
JP6673481B2 (ja) 繊維強化成形材料、及び成形体
JPWO2019220846A1 (ja) シートモールディングコンパウンドの製造方法、炭素繊維束、及び炭素繊維束の使用
JP6715666B2 (ja) シートモールディングコンパウンド、その製造方法及び成形品
JP2019085508A (ja) 繊維強化成形材料及びそれを用いた成形品
WO2020230662A1 (fr) Matériau à mouler renforcé par fibres et article moulé l'utilisant
JP7288235B2 (ja) 構造物の補強・補修方法、及び、構造物
JP2025047196A (ja) 硬化性樹脂組成物、繊維強化成形材料及びそれを用いた成形品
JP2025173163A (ja) 繊維強化成形材料及びそれを用いた成形品
WO2025004816A1 (fr) Composition de résine pour préimprégné, préimprégné et article moulé
WO2021187030A1 (fr) Pré-imprégné et article moulé
TW202033599A (zh) 預浸漬物用樹脂組成物、預浸漬物及成形品

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2019506461

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19741541

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19741541

Country of ref document: EP

Kind code of ref document: A1