WO2019204836A1 - Verfahren zur herstellung eines ringförmigen endlosschlauches - Google Patents

Verfahren zur herstellung eines ringförmigen endlosschlauches Download PDF

Info

Publication number
WO2019204836A1
WO2019204836A1 PCT/AT2018/000029 AT2018000029W WO2019204836A1 WO 2019204836 A1 WO2019204836 A1 WO 2019204836A1 AT 2018000029 W AT2018000029 W AT 2018000029W WO 2019204836 A1 WO2019204836 A1 WO 2019204836A1
Authority
WO
WIPO (PCT)
Prior art keywords
insert
tube
hose
tpe
open end
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/AT2018/000029
Other languages
English (en)
French (fr)
Inventor
Christian Lembacher
Akos KERTESZ
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to PCT/AT2018/000029 priority Critical patent/WO2019204836A1/de
Publication of WO2019204836A1 publication Critical patent/WO2019204836A1/de
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Ein Verfahren zur Herstellung eines ringförmig geschlossenen Endlosschlauches aus einem offenen, aus Kunststoff hergestellten Schlauch (1) mit einem ersten offenen Ende (2) und einem zweiten offenen Ende (3), wobei in einem Schritt i) zumindest ein Einsatz (2a) aus einem anderen Material als das Material des Schlauches (1) zumindest abschnittsweise über das erste offene Ende des Schlauches (1) in diesen eingeführt wird und das zweite offene Ende (3) des Schlauches (1) über den Einsatz (2a) und das erste offene Ende (2) gezogen wird, wobei sich ein in das erste offene Ende (2) übergehender Bereich des Schlauches (1) und ein in das zweite offene Ende (3) übergehender Bereich des Schlauches (1) sich im Bereich des Einsatzes (2) zumindest abschnittsweise überlappen, wobei in einem Schritt ii) die sich überlappenden Bereiche des Schlauches im Bereich des Einsatzes (2) miteinander verschweißt werden, wobei in einem Schritt iii) der Einsatz (2a) durch eine in den Endlosschlauch (1) eingebrachte Öffnung entfernt wird.

Description

Verfahren zur Herstellung eines ringförmigen Endlosschlauches
Die Erfindung betrifft ein Verfahren zur Herstellung eines ringförmig geschlossenen Endlosschlauches aus einem offenen, aus Kunststoff hergestellten Schlauch mit einem ersten offe- nen Ende und einem zweiten offenen Ende.
Weiters betrifft die Erfindung einen Endlosschlauch, insbesondere für einen Schlauch eines Fahrzeuges, wie eines Fahrrads, Motorrads, eines Kraftfahrzeuges oder Luftfahrzeuges.
Ein Verfahren der eingangs genannten Art ist beispielsweise aus der EP2497654B1 bekannt geworden. Bei dem bekannten Verfahren werden freie stimseitige Enden des Schlauches zur Bildung eines geschlossenen Ringes miteinander verschweißt oder verklebt. Dies hat jedoch den Nachteil, dass im Bereich einer Verbindungsstelle der freien Enden eine Naht vorhanden ist, deren mechanische Eigenschaften von jenen des übrigen Schlauches abweichen. Insbesondere weist die Naht eine geringere mechanische Belastbarkeit auf als daran anschließende Bereiche des Schlauches.
Es ist daher eine Aufgabe der Erfindung, die oben genannten Nachteile des Stands der Technik zu überwinden und einen Kunststoffschlauch zu schaffen, der im Bereich einer Verbindungsstelle seiner freien Enden keine mechanische Schwachstelle aufweist.
Diese Aufgabe wird mit einem Verfahren der eingangs genannten Art erfindungsgemäß dadurch gelöst, dass in einem Schritt i) zumindest ein Einsatz zumindest abschnittsweise über das erste offene Ende des Schlauches in diesen eingeführt wird und das zweite offene Ende des Schlauches über den Einsatz und das erste offene Ende gezogen wird, wobei sich ein in das erste offene Ende übergehender Bereich des Schlauches und ein in an das zweite offene Ende übergehender Bereich des Schlauches sich im Bereich des Einsatzes zumindest abschnittsweise überlappen, wobei in einem Schrit ii) die sich überlappenden Bereiche des Schlauches im Bereich des Einsatzes miteinander verschweißt oder verklebt werden, wobei ein einem Schrit iii) der Einsatz durch eine in den Endlosschlauch eingebrachte Öffnung entfernt wird. Die erfindungsgemäße Lösung ermöglicht die Herstellung eines Schlauches ohne eine me chanische Schwächung in einem Stoßbereich des Schlauches Zudem ermöglicht es die Erfindung, auf Grund der Verwendung des Einsatzes die Schlauchenden großflächig miteinander zu verschweißen, ohne Gefahr zu Saufen, dass Innenseiten des Schlauches unge¬ wollt miteinander verschweißt werden, was eine Unbrauchbarkeit des Schlauches zur Folge hätte, da der Einsatz ein Element bildet, durch welches Abschnitte der Innenseite des Schlauches in dem Überlappungsbereich, in dem die Verbindung der Enden des Schlau- ches stattfindet, voneinander getrennt sind.
Bei einer vorteilhaften Variante der Erfindung kann es vorgesehen sein, dass die Öffnung, durch welche der Einsatz in Schritt öl) entnommen wird, in den Schlauch geschnitten wird. Das Schneiden der Öffnung kann beispielsweise durch Stanzen erfolgen.
Um eine gute Fixierung des Einsatzes in dem Schlauch zu ermöglichen, kann es vorgese- hen sein, dass der in Schritt i) eingesetzte Einsatz an zumindest einer Steile einen Querschnittsdurchmesser aufweist, der größer ist, als ein lichter Durchmesser des Schlauches, wobei der Einsatz in Schritt i) so in den Schlauch eingeführt wird, dass der Querschnittsdurchmesser des Einsatzes nach einem Einsetzen in den Schlauch quer zu einer Längserstreckung des Schlauches verläuft.
Alternativ kann der in Schritt i) eingesetzte Einsatz über seine gesamte Länge einen Quer schnittsdurchmesser aufweisen, der kleiner ist als ein lichter Durchmesser des Schlauches, wobei der Einsatz in Schritt i) so in den Schlauch eingeführt wird, dass der Querschnittsdurchmesser des Einsatzes nach einem Einsetzen in den Schlauch quer zu einer Längser- streckung des Schlauches verläuft. Diese Variante der Erfindung ermöglicht es, im Rahmen eines Verbindens der freien Endbereiche des Schlauches zu einem Endlosschlauch dem Schlauch auf einfache Weise gegenüber dem Einsatz zu verdrehen, wodurch der Verbin dungsvorgang vereinfacht wird. Gemäß einer vorteilhaften Variante der Erfindung kann der Einsatz kegelförmig, rohrförmig, dornförmig, stiftförmig oder zylinderförmig ausgebildet sein und entweder massiv sein oder zumindest einen Hohlraum aufweisen.
Bei einer vorteilhaften Weiterbildung der Erfindung kann es vorgesehen sein, dass der Ein¬ satz aus Kunststoff und/oder Holz und/oder Keramik und/oder Gummi und/oder Metall gefer tigt ist und entweder formstabil oder flexibel ausgebildet ist. Weiters kann es von Vorteil sein, wenn das Material des Einsatzes aus einem anderen Material als das Material des Schlauches gefertigt ist und das Material des Einsatzes eine höhere Schmelztemperatur als das Material des Schlauches aufweist.
Vorteilhafterweise kann in Schritt ii) das Schweißen durch Zufuhr von Wärme oder Wärme und Druck oder durch Ultraschallschweißen oder Laserschweißen erfolgen.
Um einen durchgehend geschlossenen Schlauch ohne Loch zu realisieren, kann die Öffnung durch Verschweißen von Randbereächen der Öffnung miteinander verschlossen werden.
Gemäß einer vorteilhaften Weiterbildung der Erfindung, kann es vorgesehen sein, dass in die Öffnung ein Ventil eingesetzt wird. Diese Variante der Erfindung ermöglicht die Herstellung eines Endlosschlauches, der als Fahrzeugschlauch, insbesondere Fahrrad-, Motorrad- oder Kraftfahrzeugschlauch, gedacht ist, wesentlich zu vereinfachen, da das Ventil direkt in die bereits vorhandene Öffnung eingesetzt werden kann.
Als besonders vorteilhaft sowohl hinsichtlich der Belastbarkeit des fertigen Endlosschlauches in seinem bestimmungsgemäßen Betrieb als auch hinsichtlich der Entforrnbarkeit des Endlosschlauches von dem Einsatz hat es sich erwiesen, dass der in Schritt i) verwendete offene Schlauch aus einem thermoplastischen Elastomer, insbesondere TPU, TPE-A, TPE- E, TPE-O, TPE-S, TPE-U, TPE-V oder einem nicht thermoplastischen Kunststoff, bei spielsweise einem Silikonelastomer, insbesondere einem LSR (Liquid Silicone Rubber) Material, hergestellt ist. Die oben genannte Aufgabe lässt sich auch mit einem Endlosschlauch der eingangs ge- nannten Art erfindungsgemäß dadurch lösen, dass er aus einem thermoplastischen Elastomer, insbesondere TPU, TPE-A, TPE-E, TPE-O, TPE-S, TPE-U, TPE-V oder einem nicht thermoplastischen Kunststoff, beispielsweise einem Silikonelastomer, insbesondere einem LSR (Liquid Silicone Rubber) Material, und nach einem Verfahren gemäß einem der Ansprüche 1 bis 9 hergestellt ist, wobei der Endlosschlauch im Bereich einer Verbindungsstelle, an welcher das erste offene Ende und das zweite offene Ende miteinander verbunden sind, eine größere Wandstärke, insbesondere eine 1 ,1 bis 2-fache Wandstärke, als in anderen Bereichen aufweist.
Die Erfindung samt weiteren Vorteilen wird i Folgenden anhand einiger nicht einschränkender Ausführungsbeispiele, welche in den Zeichnungen dargestellt sind näher erläutert. In den Zeichnungen zeigen in schematisch grob vereinfachter Form:
Fig. 1 zwei offene Enden eines Schlauches mit einem dazwischen angeordneten Einsatz;
Fig. 2 den Schlauch aus Fig. 1 in einem zu einem Endlosschlauch verbundenen Zustand;
Fig. 3 den Schlauch aus Fig. 2 während eines Schweißens in einem Verbindungsbereich;
Fig. 4 den Schlauch aus Fig. 3, wobei der Schlauch um den Einsatz nach einem ersten Schweißschritt verdreht ist;
Fig. 5 ein nochmaliges Schweißen des Schlauches in dem Verbindungsbereich nach dem Verdrehen des Schlauches um den Einsatz;
Fig. 6 den Schlauch aus Fig. 1 nach dem Schweißen des Verbindungsbereiches;
Fig. 7 den Schlauch aus Fig. 6 mit einer aus einem Schweißbereich herausgeschnittenen Öffnung zur Entnahme des Einsatzes. Fig. 8 den Schlauch aus Fig. 6 mit einer neben einem Schweißbereich herausgeschnitenen Öffnung zur Entnahme des Einsatzes und
Fig 9 den Schlauch aus Fig 7 während des Herausnehmens des Einsatzes aus der Öff¬ nung.
Gemäß Fig. 1 kommen bei einem erfindungsgemäßen Verfahren zur Herstellung eines ring förmig geschlossenen Endlosschlauches ein offener, aus Kunststoff hergestellter Schlauch 1 mit einem ersten offenen Ende 2 und einem zweiten offenen Ende 3 sowie ein Einsatz 2a zur Verwendung. Bei dem erfindungsgemäßen EndSosschlauch handelt es sich besonders bevorzugt um einen Schlauch für einen Reifen eines Fahrzeugs, wie beispielsweise eines Fahrrads, Motorrads oder eines Kraftfahrzeugs.
Der Schlauch 1 selbst kann beispielsweise durch Extrusion, Blasformen etc. hergestellt sein. Als Rohmaterial für den Schlauch 1 kann ein Schlauch großer Länge dienen, der beispielsweise zu einer Rolle aufgewickelt sein kann. Von diesem Schlauch großer Länge kann dann der Schlauch 1 in der gewünschten Länge abschnitten werden. In einem Schritt i) vorhergehenden Schritt kann der offene Schlauch 1 auf eine Länge abgelängt werden, die kleiner als der Umfang des ringförmig geschlossenen Endlosschlauches ist. Es ist jedoch auch möglich, den Schlauch 1 so abzulängen, dass seine Länge dem Umfang des Endlosschlauches entspricht
Als besonders günstig hat es sich herausgestellt, wenn der Kunststoff, aus welchem der Schlauch 1 hergestellt ist, ein thermoplastisches Elastomer, beispielsweise auf Polyurethan- basis, insbesondere TPE-U (Thermoplastische Elastomere auf Urethanbasis), TPE-A
(Thermoplastische Copolyamide), TPE-E (Thermoplastische Polyesterelastomere), TPE-0 (Thermoplastische Elastomere auf Ölefinbasis), TPE-S (Styroi-BSockcopoiymere), TPE-V (Vernetzte thermoplastische Elastomere auf Olefinbasis). Alternativ können auch nicht thermoplastische Kunststoffe wie Silikonelastomere verwendet werden, insbesondere LSR (Liquid Silicone Rubber) Materialien. Wie aus Fig. 2 ersichtlich ist wird in einem Schritt i) der Einsatz 2aa zumindest abschnitts weise über das erste offene Ende 2 des Schlauches 1 in diesen eingeführt. Das zweite offe¬ ne Ende 3 des Schlauches 1 wird sodann über den Einsatz 2a und das erste offene Ende 2 gezogen. Ein in das erste offene Ende 2 übergehender Bereich 4 des Schlauches 1 und ein in an das zweite offene Ende 3 übergehender Bereich 5 des Schlauches 1 überlappen sich hierbei im Bereich des Einsatzes 2 zumindest abschnittsweise.
Der Einsatz 2a kann kegelförmig, rohrförmig, dornförmsg, stiftförmig oder zylinderförmig ausgebildet sein. Zudem kann der Einsatz 2a entweder massiv ausgebildet sein oder auch einen oder mehrere Hohlräume aufweisen. Weiters kann der Einsatz 2a aus Kunststoff und/oder Holz und/oder Keramik und/oder Gummi und/oder Metall gefertigt ist und entweder formstabil oder flexibel ausgebildet sein. Der Einsatz 2a verhindert ein ungewolltes Verbin- den von Abschnitten der Innenseite des Schlauches 1 bei einem Verschweißen der Berei che 4 und 5 verhindert und bietet bei einem Verkleben ausreichend mechanische Abstüt zung der Bereiche 4 und 5. Bei einem Verschweißen kann der Einsatz 2a beispielsweise flexibel ausgeführt sein, während bei einem Verkleben ein formstabiler Einsatz von Vorteil sein kann.
Der Einsatz 2a kann an zumindest einer Stelle einen Querschnittsdurchmesser aufweist, der größer ist als ein lichter Durchmesser des Schlauches 1 , wobei der Einsatz 2a in Schritt i) so in den Schlauch eingeführt wird, dass der Querschnittsdurchmesser des Einsatzes nach einem Einsetzen in den Schlauch 1 quer zu einer Längserstreckung des Schlauches 1 ver-
Alternativ kann der Einsatz 2a aber auch über seine gesamte Länge einen Querschnittsdurchmesser aufweisen, der kleiner ist als der lichte Durchmesser des Schlauches 1 ist, wobei der Einsatz 2a in Schritt i) ebenfalls so in den Schlauch eingeführt werden kann, dass der Querschnittsdurchmesser des Einsatzes nach einem Einsetzen in den Schlauch 1 quer zu einer Längserstreckung des Schlauches 1 verläuft. Gemäß Fig. 3 werden in einem Schritt ii) die sich überlappenden Bereiche 4, 5 des Schlau ches im Bereich des Einsatzes 2 mittels eines Schweißgerätes 7 miteinander verschweißt. Das Schweißen kann durch Zufuhr von Wärme oder Wärme und Druck oder durch Ultraschallschweißen oder Laserschweißen erfolgt. Alternativ zu einem Verschweißen kann auch ein Verkleben erfolgen.
Der fertig gestellte Endlosschlauch kann in einem durch die Bereiche 4 und 5 definierten Verbindungsbereich eine größere Wandstärke, insbesondere eine 1 ,1 bis 2-fache Wandstärke, aufweisen als in anderen Bereichen.
Wie in Fig. 4 dargestelit, kann der Schlauch 1 nach einem ersten Schweißen um den Ein satz 2a gedreht werden und wie in Fig. 5 gezeigt nach dem Drehen neuerlich verschweißt werden. Diese Variante der Erfindung hat den Vorteil, dass sich auch mit einem fix positio nierten Schweißgerät ein einfaches Verschweißen der Bereiche 4 und 5 erreichen lässt.
Fig. 6 zeigt den Verbindungsbereich des Endlosschlauches nach dem Verbinden der Berei che 4 und 5, wobei sich der Einsatz 2a noch im Inneren des Schlauches befindet.
In einem Schritt iii) wird der Einsatz 2a durch eine in den Endlosschlauch 1 eingebrachte Öffnung 8 entfernt, wie es in Fig. 9 gezeigt ist.
Die Öffnung 8, durch welche der Einsatz in Schritt iii) entnommen wird, kann in den
Schlauch 1 geschnitten werden. Das Schneiden kann beispielsweise mittels einer Stanzvorrichtung oder eines Lasers erfolgen. In Fig 7 ist dargestelit, dass die Öffnung 6 in dem Be- reich einer Schweißstelle angeordnet sein kann, während in Fig. 8 dargestellt ist, dass die Öffnung 6 auch neben einer Schweißstelle eingebracht sein kann.
Der Einsatz 2a kann ein oder mehrteilig sein (zwei oder mehrere Teile). Die Verwendung eines mehrteiligen Einsatzes 2 hat den Vorteil, dass er leichter aus der Öffnung 8 entnommen werden kann, da er vor der Entnahme aus dem Schlauch 1 geteilt werden. Die Ver- Wendung eines thermoplastischen Elastomers für den Schlauch 1 ermöglicht ein besonders einfaches Entfernen des Einsatzes 2 durch die Öffnung 6. So kann beispielsweise ein Endbereich der Öffnung 6 über eine Stirnkante des Einsatzes 2 gezogen und der Einsatz 2a durch die Öffnung 8 entnommen werden.
Die Öffnung 6 kann durch Verschweißen von Randbereichen der Öffnung 6 miteinander verschlossen werden, falls ein Endlosschlauch 1 ohne Öffnung 6 gewünscht ist. Darüber hinaus kann in die Öffnung 6 auch ein Ventil eingesetzt werden.

Claims

Patentansprüche
1. Verfahren zur Herstellung eines ringförmig geschlossenen Endlosschlauches aus ei nem offenen, aus Kunststoff hergestellten Schlauch (1) mit einem ersten offenen Ende (2) und einem zweiten offenen Ende (3), dadurch gekennzeichnet, dass in einem Schritt i) zumindest ein Einsatz (2a) zumindest abschnittsweise über das erste offene Ende (2) des Schlauches (1) in diesen eingeführt wird und das zweite offene Ende (3) des Schlauches (1) über den Einsatz (2a)und das erste offene Ende (2) gezogen wird, wobei sich ein in das erste offene Ende (2) übergehender Bereich (4) des Schlauches (1) und ein in an das zweite offene Ende (3) übergehender Bereich (5) des Schlauches (1) sich im Bereich des Einsatzes (2) zumindest abschnittsweise überlappen, wobei in einem Schritt ü) die sich überlappenden Bereiche (4, 5) des Schlauches im Bereich des Einsatzes (2) miteinander verschweißt oder verklebt werden, wobei ein einem Schritt iii) der Einsatz (2a)durch eine in den Endlosschlauch (1) eingebrachte Öffnung (6) entfernt wird.
2. Verfahren nach Anspruch 1 , dadurch gekennzeichnet, dass die Öffnung (8), durch welche der Einsatz in Schritt iii) entnommen wird, in den Schlauch (1) geschnitten wird.
3. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass der in Schritt i) eingesetzte Einsatz (2a)an zumindest einer Stelle einen Querschnittsdurchmesser aufweist, der größer ist als ein lichter Durchmesser des Schlauches (1), wobei der Einsatz (2a) in Schritt i) so in den Schlauch eingeführt wird, dass der Ouerschnifis- durchmesser des Einsatzes nach einem Einsetzen in den Schlauch (1) quer zu einer Längserstreckung des Schlauches (1) verläuft.
4. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass der in Schritt i) eingesetzte Einsatz (2a) über seine gesamte Länge einen Querschnittsdurchmesser aufweist, der kleiner ist als ein lichter Durchmesser des Schlauches (1), wobei der
Einsatz (2a)\n Schritt i) so in den Schlauch eingeführt wird, dass der Querschnitts- durchmesser des Einsatzes nach einem Einsetzen in den Schlauch (1 ) quer zu einer Längserstreckung des Schlauches (1) verläuft
5 Verfahren nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass der Einsatz (2a) kegelförmig, rohrförmig, dornförmig, stiftförmig oder zylinderförmig ausge bildet ist und entweder massiv ist oder zumindest einen Hohiraum aufweist
6. Verfahren nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass der Einsatz aus Kunststoff und/oder Holz und/oder Keramik und/oder Gummi und/ oder Metall gefertigt ist und entweder formstabil oder flexibel ausgebildet ist
7. Verfahren nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass in
Schritt ii) das Schweißen durch Zufuhr von Wärme oder Wärme und Druck oder durch Ultraschallschweißen oder Laserschweißen erfolgt.
8. Verfahren nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass die Öff nung (6) durch Verschweißen von Randbereichen der Öffnung (8) miteinander ver- schlossen wird oder in die Öffnung (6) ein Ventil eingesetzt wird.
9 Verfahren nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass der in Schrit i) verwendete offene Schlauch (2) aus einem thermoplastischen Elastomer, insbesondere TPU, TPE-A, TPE-E, TPE-O, TPE-S, TPE-U, TPE-V oder einem nicht thermoplastischen Kunststoff, beispielsweise einem Silikonelastomer, insbesondere einem LSR (Liquid Silicone Rubber) Material, hergesielft ist. 0, Endlosschlauch, insbesondere für einen Schlauch eines Fahrzeuges, wie eines Fahrrads, Motorrads, eines Kraftfahrzeuges oder Luftfahrzeuges, dadurch gekennzeich net, dass er aus einem thermoplastischen Elastomer, insbesondere TPU, TPE-A, TPE-E, TPE-O, TPE-S, TPE-U, TPE-V oder einem nicht thermoplastischen Kunststoff, beispielsweise einem Silikonelastomer, insbesondere einem LSR (Liquid Silico- ne Rubber) Material, und nach einem Verfahren gemäß einem der Ansprüche 1 bis 9 hergestellt ist, wobei der Endlosschlauch im Bereich einer Verbindungsstelle, an wel cher das erste offene Ende (4) und das zweite offene Ende (5) miteinander verbun- den sind, eine größere Wandstärke, insbesondere eine 1 , 1 bis 2-fache Wandstärke, als in anderen Bereichen aufweist.
PCT/AT2018/000029 2018-04-24 2018-04-24 Verfahren zur herstellung eines ringförmigen endlosschlauches Ceased WO2019204836A1 (de)