WO2020256476A1 - Composition adhésive à base de radicaux, film protecteur de plaque polarisante la comprenant, plaque polarisante comprenant ce film protecteur, et dispositif d'affichage d'images comprenant cette plaque polarisante - Google Patents

Composition adhésive à base de radicaux, film protecteur de plaque polarisante la comprenant, plaque polarisante comprenant ce film protecteur, et dispositif d'affichage d'images comprenant cette plaque polarisante Download PDF

Info

Publication number
WO2020256476A1
WO2020256476A1 PCT/KR2020/007979 KR2020007979W WO2020256476A1 WO 2020256476 A1 WO2020256476 A1 WO 2020256476A1 KR 2020007979 W KR2020007979 W KR 2020007979W WO 2020256476 A1 WO2020256476 A1 WO 2020256476A1
Authority
WO
WIPO (PCT)
Prior art keywords
radical
adhesive composition
protective film
polarizing plate
based adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2020/007979
Other languages
English (en)
Korean (ko)
Inventor
김동욱
김희정
권윤경
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LG Chem Ltd
Original Assignee
LG Chem Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LG Chem Ltd filed Critical LG Chem Ltd
Priority to CN202080038287.0A priority Critical patent/CN113906114B/zh
Priority to JP2021571877A priority patent/JP7395096B2/ja
Publication of WO2020256476A1 publication Critical patent/WO2020256476A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne une composition adhésive à base de radicaux, un film protecteur pour plaque polarisante la comprenant, une plaque polarisante comprenant ce film protecteur, et un dispositif d'affichage d'images comprenant cette plaque polarisante.
PCT/KR2020/007979 2019-06-20 2020-06-19 Composition adhésive à base de radicaux, film protecteur de plaque polarisante la comprenant, plaque polarisante comprenant ce film protecteur, et dispositif d'affichage d'images comprenant cette plaque polarisante Ceased WO2020256476A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202080038287.0A CN113906114B (zh) 2019-06-20 2020-06-19 自由基接着剂组合物、包括该自由基接着剂组合物的偏光板用保护膜、包括其的偏光板及包括该偏光板的图像显示装置
JP2021571877A JP7395096B2 (ja) 2019-06-20 2020-06-19 ラジカル系接着剤組成物、それを含む偏光板用保護フィルム、それを含む偏光板、及びそれを含む画像表示装置

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR10-2019-0073558 2019-06-20
KR20190073558 2019-06-20

Publications (1)

Publication Number Publication Date
WO2020256476A1 true WO2020256476A1 (fr) 2020-12-24

Family

ID=74040577

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2020/007979 Ceased WO2020256476A1 (fr) 2019-06-20 2020-06-19 Composition adhésive à base de radicaux, film protecteur de plaque polarisante la comprenant, plaque polarisante comprenant ce film protecteur, et dispositif d'affichage d'images comprenant cette plaque polarisante

Country Status (5)

Country Link
JP (1) JP7395096B2 (fr)
KR (1) KR102294150B1 (fr)
CN (1) CN113906114B (fr)
TW (1) TWI788677B (fr)
WO (1) WO2020256476A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114958235A (zh) * 2021-02-26 2022-08-30 太仓斯迪克新材料科技有限公司 柔性光学胶膜的制备方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050239916A1 (en) * 2004-04-27 2005-10-27 Day David E Polyester-polyether hybrid urethane acrylate oligomer for UV curing pressure sensitive adhesives
KR20070111988A (ko) * 2006-05-19 2007-11-22 린텍 가부시키가이샤 광학 기능성 필름 접합용 점착제, 광학 기능성 필름 및 그제조 방법
US20170253780A1 (en) * 2014-11-18 2017-09-07 Henkel Ag & Co. Kgaa Photo-curable adhesive composition, preparation and use thereof
KR20170116969A (ko) * 2016-04-12 2017-10-20 주식회사 엘지화학 광학용 점착 조성물
KR20170131496A (ko) * 2015-03-25 2017-11-29 닛토덴코 가부시키가이샤 편광 필름용 경화형 접착제 조성물, 편광 필름 및 그 제조 방법, 광학 필름 그리고 화상 표시 장치

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2562554B2 (ja) * 1993-03-08 1996-12-11 東リ株式会社 光−放射線硬化性樹脂組成物およびそれを被覆してなる床材
KR101072371B1 (ko) * 2010-09-20 2011-10-11 주식회사 엘지화학 편광판용 접착제 및 이를 포함하는 편광판
JP2012102226A (ja) * 2010-11-09 2012-05-31 Bridgestone Corp 接着性樹脂組成物
JP5630256B2 (ja) * 2010-12-24 2014-11-26 Dic株式会社 紫外線硬化型粘着剤用樹脂組成物、粘着剤及び積層体
TW201317315A (zh) * 2011-08-26 2013-05-01 Denki Kagaku Kogyo Kk 固化性樹脂組成物
JP5382277B2 (ja) * 2011-10-19 2014-01-08 Ｄｉｃ株式会社 活性エネルギー線硬化型樹脂組成物、接着剤及び積層フィルム
JP5843206B2 (ja) * 2013-04-25 2016-01-13 デンカ株式会社 仮固定用接着剤組成物、それを用いた構造体及び部材の仮固定方法
KR101495437B1 (ko) 2013-07-22 2015-02-24 주식회사 포스코 분진비산 방지 기능을 갖는 웨잉호퍼 채탄용 게이트장치
JP2015094823A (ja) * 2013-11-11 2015-05-18 コニカミノルタ株式会社 セルロースエステルフィルムを有する偏光板
JP6613586B2 (ja) * 2015-03-18 2019-12-04 東洋インキＳｃホールディングス株式会社 活性エネルギー線重合性樹脂組成物及び積層体
CN104698754B (zh) * 2015-03-23 2018-11-13 江南大学 一种基于pcdl型聚氨酯丙烯酸酯制备的光刻胶组合物
JP6063514B2 (ja) * 2015-04-24 2017-01-18 デンカ株式会社 部材の仮固定方法及び構造体

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050239916A1 (en) * 2004-04-27 2005-10-27 Day David E Polyester-polyether hybrid urethane acrylate oligomer for UV curing pressure sensitive adhesives
KR20070111988A (ko) * 2006-05-19 2007-11-22 린텍 가부시키가이샤 광학 기능성 필름 접합용 점착제, 광학 기능성 필름 및 그제조 방법
US20170253780A1 (en) * 2014-11-18 2017-09-07 Henkel Ag & Co. Kgaa Photo-curable adhesive composition, preparation and use thereof
KR20170131496A (ko) * 2015-03-25 2017-11-29 닛토덴코 가부시키가이샤 편광 필름용 경화형 접착제 조성물, 편광 필름 및 그 제조 방법, 광학 필름 그리고 화상 표시 장치
KR20170116969A (ko) * 2016-04-12 2017-10-20 주식회사 엘지화학 광학용 점착 조성물

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114958235A (zh) * 2021-02-26 2022-08-30 太仓斯迪克新材料科技有限公司 柔性光学胶膜的制备方法
CN114958235B (zh) * 2021-02-26 2023-12-19 太仓斯迪克新材料科技有限公司 柔性光学胶膜的制备方法

Also Published As

Publication number Publication date
KR102294150B1 (ko) 2021-08-27
JP7395096B2 (ja) 2023-12-11
JP2022536080A (ja) 2022-08-12
CN113906114B (zh) 2023-01-03
TW202106827A (zh) 2021-02-16
KR20200145760A (ko) 2020-12-30
TWI788677B (zh) 2023-01-01
CN113906114A (zh) 2022-01-07

Similar Documents

Publication Publication Date Title
WO2013133539A1 (fr) Composition adhésive destinée à un polariseur et polariseur l'utilisant
WO2013028047A2 (fr) Adhésif
WO2011105878A2 (fr) Composition adhésive
WO2011105875A2 (fr) Plaque de polarisation
WO2011105874A2 (fr) Lame polarisante
KR101768283B1 (ko) 편광판용 접착제 조성물
WO2016104979A1 (fr) Composition adhésive, film adhésif formé à partir de celle-ci, et élément d'affichage le comprenant
WO2011105876A2 (fr) Lame polarisante
WO2016068423A1 (fr) Dispositif d'affichage flexible
WO2014035117A1 (fr) Plaque de polarisation
KR102158870B1 (ko) 광학 필름용 접착제, 이를 포함하는 편광판 및 이를 포함하는 화상표시장치
WO2018159923A1 (fr) Film de fenêtre, stratifié de film de fenêtre le comprenant et dispositif d'affichage d'image
WO2020162677A1 (fr) Composition adhésive à radicaux libres, couche adhésive, plaque polarisante et dispositif d'affichage d'image
WO2011065779A2 (fr) Composition adhésive
WO2019059630A2 (fr) Composition adhésive et plaque de polarisation dotée d'une couche adhésive formée au moyen de ladite composition
WO2018159918A1 (fr) Substrat de fenêtre de couverture et dispositif d'affichage d'image comprenant celui-ci
KR20200124651A (ko) 편광 필름 및 그 제조 방법, 광학 필름, 그리고 화상 표시 장치
WO2016159645A1 (fr) Plaque de polarisation et dispositif d'affichage optique la comprenant
KR102519260B1 (ko) 광학용 점착제 조성물 및 이것을 사용한 점착 필름, 점착 시트
KR20230149802A (ko) (메타)아크릴계 수지 조성물 및 (메타)아크릴계 수지 필름
WO2020256476A1 (fr) Composition adhésive à base de radicaux, film protecteur de plaque polarisante la comprenant, plaque polarisante comprenant ce film protecteur, et dispositif d'affichage d'images comprenant cette plaque polarisante
WO2019103515A1 (fr) Plaque polarisante et dispositif d'affichage d'image la comprenant
KR102758367B1 (ko) 적층체 및 이를 포함하는 화상 표시 장치
KR102760405B1 (ko) 접착제 조성물, 이를 포함하는 편광판용 보호 필름, 이를 포함하는 편광판 및 이를 포함하는 화상 표시 장치
WO2019163749A1 (fr) Film polarisant, son procédé de fabrication, film optique et dispositif d'affichage d'image

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20825896

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021571877

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20825896

Country of ref document: EP

Kind code of ref document: A1