WO2024055674A1 - Procédé de soudage et module photovoltaïque - Google Patents

Procédé de soudage et module photovoltaïque Download PDF

Info

Publication number
WO2024055674A1
WO2024055674A1 PCT/CN2023/102335 CN2023102335W WO2024055674A1 WO 2024055674 A1 WO2024055674 A1 WO 2024055674A1 CN 2023102335 W CN2023102335 W CN 2023102335W WO 2024055674 A1 WO2024055674 A1 WO 2024055674A1
Authority
WO
WIPO (PCT)
Prior art keywords
welding
battery
electrode
pad
soldering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2023/102335
Other languages
English (en)
Chinese (zh)
Inventor
赵德宝
陈鹏
陈军
李华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taizhou Longi Solar Technology Co Ltd
Original Assignee
Taizhou Longi Solar Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taizhou Longi Solar Technology Co Ltd filed Critical Taizhou Longi Solar Technology Co Ltd
Publication of WO2024055674A1 publication Critical patent/WO2024055674A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente demande se rapporte au domaine technique du photovoltaïque solaire. Sont décrits un procédé de soudage et un module photovoltaïque. Le procédé est utilisé pour souder des cellules solaires à contact arrière interdigité. Chaque cellule solaire comprenant une électrode positive et une électrode négative, l'électrode positive et l'électrode négative comprenant chacune une électrode de barre omnibus, une électrode de doigt et un plot de liaison situé sur l'électrode de barre omnibus, l'électrode de barre omnibus croisant l'électrode de doigt. Le procédé consiste à : après l'impression d'un adhésif isolant sur au moins les électrodes de doigt avec différentes polarités sur des bords latéraux d'une électrode positive et d'une électrode négative dans une cellule solaire, imprimer un adhésif électroconducteur sur des plots de liaison, la hauteur d'impression de l'adhésif électroconducteur étant supérieure ou égale à la hauteur d'impression de l'adhésif isolant ; et sur la base de l'adhésif électroconducteur et des plots de liaison, connecter au moins deux batteries en série, de façon à former une chaîne de batteries. Dans la présente demande, un adhésif isolant est imprimé pour recouvrir des lignes de doigt sur le bord d'un plot de liaison, et un adhésif électroconducteur est en outre imprimé sur le plot de liaison, ce qui permet d'éliminer une différence de hauteur formée entre un fil électroconducteur et le plot de liaison en raison de la présence de l'adhésif isolant, et de résoudre le problème de pseudo-soudure d'une batterie.
PCT/CN2023/102335 2022-09-14 2023-06-26 Procédé de soudage et module photovoltaïque Ceased WO2024055674A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN202211117164.3 2022-09-14
CN202211117164.3A CN115632086B (zh) 2022-09-14 2022-09-14 一种焊接方法及光伏组件

Publications (1)

Publication Number Publication Date
WO2024055674A1 true WO2024055674A1 (fr) 2024-03-21

Family

ID=84903558

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2023/102335 Ceased WO2024055674A1 (fr) 2022-09-14 2023-06-26 Procédé de soudage et module photovoltaïque

Country Status (2)

Country Link
CN (2) CN119451268A (fr)
WO (1) WO2024055674A1 (fr)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN118099240A (zh) * 2024-04-29 2024-05-28 浙江爱旭太阳能科技有限公司 一种背接触电池组件及其制作方法和光伏发电系统
CN119403280A (zh) * 2024-12-31 2025-02-07 陕西众森电能科技有限公司 一种背接触电池片的串联方法
CN119630072A (zh) * 2024-12-12 2025-03-14 晶科能源股份有限公司 光伏组件
CN119894164A (zh) * 2025-03-25 2025-04-25 金阳(泉州)新能源科技有限公司 电池片单元、无主栅背接触电池块、电池模组及制备方法
CN120076417A (zh) * 2025-02-25 2025-05-30 隆基绿能科技股份有限公司 一种太阳能电池片及光伏组件
CN120112002A (zh) * 2025-04-30 2025-06-06 晶科能源(海宁)有限公司 背接触光伏电池及光伏组件
CN120640834A (zh) * 2025-08-11 2025-09-12 天津爱旭太阳能科技有限公司 一种背接触电池、电池组件和光伏系统
CN120813120A (zh) * 2025-09-11 2025-10-17 福建金石能源有限公司 一种具有特定金属电极结构的背接触电池和电池组件
AU2025201429B1 (en) * 2024-07-24 2026-02-12 Tongwei Solar (Chengdu) Co., Ltd. Photovoltaic module and manufacturing method thereof
WO2026056610A1 (fr) * 2024-09-14 2026-03-19 浙江爱旭太阳能科技有限公司 Cellule photovoltaïque, ensemble et système
CN121728864A (zh) * 2026-02-11 2026-03-24 Tcl中环新能源科技股份有限公司 一种电池片、电池片的制备方法、电池串及光伏组件

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN119451268A (zh) * 2022-09-14 2025-02-14 泰州隆基乐叶光伏科技有限公司 一种焊接方法及光伏组件
CN118712259A (zh) * 2023-03-27 2024-09-27 武汉帝尔激光科技股份有限公司 一种背接触太阳能电池组件的焊接方法
EP4462487B1 (fr) 2023-05-08 2025-11-05 Jinko Solar Co., Ltd Procédé de fabrication de module photovoltaïque et module photovoltaïque
CN116995109A (zh) * 2023-08-29 2023-11-03 正泰新能科技有限公司 一种低温焊接的背接触光伏组件及其制备方法
CN116913992A (zh) * 2023-09-04 2023-10-20 浙江晶科能源有限公司 一种电池片及光伏组件
CN117219702A (zh) 2023-09-05 2023-12-12 晶科能源(海宁)有限公司 一种光伏组件的制作方法及光伏组件
CN117238984B (zh) * 2023-11-14 2024-03-29 无锡华晟光伏科技有限公司 光伏电池片和光伏组件
CN119545921B (zh) * 2024-04-08 2025-08-12 隆基绿能科技股份有限公司 电池串及光伏组件
CN118039521B (zh) * 2024-04-11 2024-07-02 滁州捷泰新能源科技有限公司 一种电池片细栅绝缘性测试装置、方法及背接触组件制备方法
CN118571972A (zh) * 2024-05-30 2024-08-30 嘉兴隆基光伏科技有限公司 电池串及光伏组件
CN119604082B (zh) * 2024-07-05 2025-09-02 隆基绿能科技股份有限公司 一种光伏组件、光伏组件的制备方法及网版
CN119092576A (zh) * 2024-08-15 2024-12-06 晶科能源股份有限公司 光伏组件
CN119317243B (zh) * 2024-12-18 2025-03-21 金阳(泉州)新能源科技有限公司 背接触太阳能电池及其制备方法、电池组件

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20210098641A1 (en) * 2019-09-27 2021-04-01 Sunpower Corporation Wire-based metallization and stringing for solar cells
CN215988787U (zh) * 2021-06-30 2022-03-08 泰州隆基乐叶光伏科技有限公司 一种太阳能电池及光伏组件
CN216213479U (zh) * 2021-11-10 2022-04-05 浙江爱旭太阳能科技有限公司 一种ibc太阳能电池及其电极结构、电池组件
CN114628542A (zh) * 2022-03-03 2022-06-14 浙江爱旭太阳能科技有限公司 背接触太阳能电池串及其制备方法、电池组件及光伏系统
CN114649443A (zh) * 2022-03-03 2022-06-21 浙江爱旭太阳能科技有限公司 背接触太阳能电池串及其制备方法、电池组件及光伏系统
CN115632086A (zh) * 2022-09-14 2023-01-20 泰州隆基乐叶光伏科技有限公司 一种焊接方法及光伏组件

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102162719B1 (ko) * 2014-01-13 2020-10-07 엘지전자 주식회사 태양전지 모듈
EP2966693B1 (fr) * 2014-07-07 2023-05-03 Shangrao Jinko solar Technology Development Co., LTD Module de cellule solaire
CN106340547A (zh) * 2016-08-31 2017-01-18 浙江尚越新能源开发有限公司 一种用于降低光伏电池成本的焊接结构及焊接方法
CN210040210U (zh) * 2019-01-31 2020-02-07 福建金石能源有限公司 一种无主栅双面发电太阳能电池及其模组
CN114242810B (zh) * 2022-02-24 2022-04-29 广东爱旭科技有限公司 背接触电池的电极结构、电池、组件以及电池系统

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20210098641A1 (en) * 2019-09-27 2021-04-01 Sunpower Corporation Wire-based metallization and stringing for solar cells
CN215988787U (zh) * 2021-06-30 2022-03-08 泰州隆基乐叶光伏科技有限公司 一种太阳能电池及光伏组件
CN216213479U (zh) * 2021-11-10 2022-04-05 浙江爱旭太阳能科技有限公司 一种ibc太阳能电池及其电极结构、电池组件
CN114628542A (zh) * 2022-03-03 2022-06-14 浙江爱旭太阳能科技有限公司 背接触太阳能电池串及其制备方法、电池组件及光伏系统
CN114649443A (zh) * 2022-03-03 2022-06-21 浙江爱旭太阳能科技有限公司 背接触太阳能电池串及其制备方法、电池组件及光伏系统
CN115632086A (zh) * 2022-09-14 2023-01-20 泰州隆基乐叶光伏科技有限公司 一种焊接方法及光伏组件

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN118099240A (zh) * 2024-04-29 2024-05-28 浙江爱旭太阳能科技有限公司 一种背接触电池组件及其制作方法和光伏发电系统
AU2025201429B1 (en) * 2024-07-24 2026-02-12 Tongwei Solar (Chengdu) Co., Ltd. Photovoltaic module and manufacturing method thereof
WO2026056610A1 (fr) * 2024-09-14 2026-03-19 浙江爱旭太阳能科技有限公司 Cellule photovoltaïque, ensemble et système
CN119630072A (zh) * 2024-12-12 2025-03-14 晶科能源股份有限公司 光伏组件
CN119403280A (zh) * 2024-12-31 2025-02-07 陕西众森电能科技有限公司 一种背接触电池片的串联方法
CN120076417A (zh) * 2025-02-25 2025-05-30 隆基绿能科技股份有限公司 一种太阳能电池片及光伏组件
CN119894164A (zh) * 2025-03-25 2025-04-25 金阳(泉州)新能源科技有限公司 电池片单元、无主栅背接触电池块、电池模组及制备方法
CN120112002A (zh) * 2025-04-30 2025-06-06 晶科能源(海宁)有限公司 背接触光伏电池及光伏组件
CN120640834A (zh) * 2025-08-11 2025-09-12 天津爱旭太阳能科技有限公司 一种背接触电池、电池组件和光伏系统
CN120813120A (zh) * 2025-09-11 2025-10-17 福建金石能源有限公司 一种具有特定金属电极结构的背接触电池和电池组件
CN121728864A (zh) * 2026-02-11 2026-03-24 Tcl中环新能源科技股份有限公司 一种电池片、电池片的制备方法、电池串及光伏组件

Also Published As

Publication number Publication date
CN119451268A (zh) 2025-02-14
CN115632086B (zh) 2024-11-08
CN115632086A (zh) 2023-01-20

Similar Documents

Publication Publication Date Title
WO2024055674A1 (fr) Procédé de soudage et module photovoltaïque
CN218730966U (zh) 太阳能电池及太阳能电池模块
CN109786492B (zh) 光伏组件及其制造方法
JP3223119U (ja) 太陽電池セル及び太陽電池モジュール
JP7699717B2 (ja) 裏面接触太陽電池ストリング及びその製造方法、アセンブリ並びにシステム
CN216719958U (zh) 一种太阳能电池片、太阳能电池分片及光伏组件
CN215988787U (zh) 一种太阳能电池及光伏组件
CN114649435A (zh) 一种光伏组件及其制备工艺
CN204857754U (zh) 一种太阳能电池组件
CN215988782U (zh) 一种太阳能电池及光伏组件
CN215988784U (zh) 一种太阳能电池及光伏组件
CN218677162U (zh) 一种太阳能电池串和光伏组件
CN106653878A (zh) Ibc太阳能电池背电极结构及其制备方法
CN110034203A (zh) 一种太阳能电池片的搭接结构及太阳能组件
CN118630072A (zh) 一种背接触电池片及光伏组件
CN210837777U (zh) 一种光伏电池串和光伏组件
WO2025039782A1 (fr) Chaîne de batteries et module photovoltaïque
CN215988781U (zh) 一种太阳能电池及光伏组件
EP4682959A1 (fr) Ensemble de cellules photovoltaïques, son procédé de fabrication et module photovoltaïque
CN108831946A (zh) 一种太阳能光伏组件
CN210897314U (zh) 光伏组件
CN215988783U (zh) 一种太阳能电池及光伏组件
CN209804688U (zh) 一种太阳能电池片的搭接结构及太阳能组件
CN214898458U (zh) 一种背接触太阳能电池串、组件及系统
WO2025214201A1 (fr) Chaîne de batterie et module photovoltaïque

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23864413

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 23864413

Country of ref document: EP

Kind code of ref document: A1