WO2024199366A1 - Tube de pompe péristaltique et son procédé de fabrication - Google Patents

Tube de pompe péristaltique et son procédé de fabrication Download PDF

Info

Publication number
WO2024199366A1
WO2024199366A1 PCT/CN2024/084461 CN2024084461W WO2024199366A1 WO 2024199366 A1 WO2024199366 A1 WO 2024199366A1 CN 2024084461 W CN2024084461 W CN 2024084461W WO 2024199366 A1 WO2024199366 A1 WO 2024199366A1
Authority
WO
WIPO (PCT)
Prior art keywords
peristaltic pump
pump tube
accordance
silicone
polyalkylsiloxane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2024/084461
Other languages
English (en)
Inventor
Guojia PAN
Daye SUN
Qi Zhu
Michael J. Tzivanis
Haiyan HONG
Chun Li
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Saint Gobain Performance Plastics Corp
Original Assignee
Saint Gobain Performance Plastics Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Saint Gobain Performance Plastics Corp filed Critical Saint Gobain Performance Plastics Corp
Priority to CN202480021869.6A priority Critical patent/CN121002315A/zh
Priority to EP24778152.9A priority patent/EP4689395A4/fr
Priority to JP2025555899A priority patent/JP2026511613A/ja
Publication of WO2024199366A1 publication Critical patent/WO2024199366A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Un tube de pompe péristaltique (100) comprend une composition de silicone comprenant un matériau de silicone de base, un accélérateur, un agent de durcissement et un catalyseur, le matériau de silicone de base comprenant un mélange d'un premier élastomère de silicone et d'un second élastomère de silicone, le premier élastomère de silicone ayant un duromètre Shore A qui est différent d'un duromètre Shore A du second élastomère de silicone ; le tube de pompe péristaltique (100) étant utilisé avec une pompe péristaltique à des vitesses de rotation supérieures à 600 rotations par minute, et la composition de silicone augmentant avantageusement la durée de vie de pompe du tube de pompe péristaltique (100).
PCT/CN2024/084461 2023-03-30 2024-03-28 Tube de pompe péristaltique et son procédé de fabrication Ceased WO2024199366A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN202480021869.6A CN121002315A (zh) 2023-03-30 2024-03-28 蠕动泵管及制造方法
EP24778152.9A EP4689395A4 (fr) 2023-03-30 2024-03-28 Tube de pompe péristaltique et son procédé de fabrication
JP2025555899A JP2026511613A (ja) 2023-03-30 2024-03-28 蠕動ポンプチューブ及び作製方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202363493183P 2023-03-30 2023-03-30
US63/493,183 2023-03-30

Publications (1)

Publication Number Publication Date
WO2024199366A1 true WO2024199366A1 (fr) 2024-10-03

Family

ID=92907558

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2024/084461 Ceased WO2024199366A1 (fr) 2023-03-30 2024-03-28 Tube de pompe péristaltique et son procédé de fabrication

Country Status (4)

Country Link
EP (1) EP4689395A4 (fr)
JP (1) JP2026511613A (fr)
CN (1) CN121002315A (fr)
WO (1) WO2024199366A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080293878A1 (en) * 2005-12-01 2008-11-27 Wacker Chemie Ag Ionically and/or Organometallically Functionalized Silicone Polymers Crosslinkable to High-Strength Elastomers
US20150252918A1 (en) * 2014-03-10 2015-09-10 Saint-Gobain Performance Plastics Corporation Multilayer flexible tube and methods for making same
US20180080585A1 (en) * 2016-09-19 2018-03-22 Contitech Mgw Gmbh Fluoroelastomer/epdm hose for cold-side charge air applications
US20200346426A1 (en) * 2019-04-30 2020-11-05 Saint-Gobain Performance Plastics Corporation Dissipative peristaltic pump tubing
US20210094253A1 (en) * 2019-09-27 2021-04-01 Saint-Gobain Performance Plastics Corporation Multilayer tube and method for making same

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006224532A (ja) * 2005-02-18 2006-08-31 Seiko Epson Corp チューブポンプ及び液体噴射装置
US20080166509A1 (en) * 2007-01-08 2008-07-10 Saint-Gobain Performance Plastics Corporation Silicone tubing formulations and methods for making same
BR112015002341A2 (pt) * 2012-08-14 2017-07-04 Saint Gobain Performance Plastics Corp aparelho e método para fazer um artigo de silicone
WO2015048455A1 (fr) * 2013-09-27 2015-04-02 Saint-Gobain Performance Plastics Corporation Article en silicone, tube et procédé de formation d'article
KR20230025408A (ko) * 2020-06-24 2023-02-21 다우 실리콘즈 코포레이션 실리콘 탄성중합체 조성물

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080293878A1 (en) * 2005-12-01 2008-11-27 Wacker Chemie Ag Ionically and/or Organometallically Functionalized Silicone Polymers Crosslinkable to High-Strength Elastomers
US20150252918A1 (en) * 2014-03-10 2015-09-10 Saint-Gobain Performance Plastics Corporation Multilayer flexible tube and methods for making same
US20180080585A1 (en) * 2016-09-19 2018-03-22 Contitech Mgw Gmbh Fluoroelastomer/epdm hose for cold-side charge air applications
US20200346426A1 (en) * 2019-04-30 2020-11-05 Saint-Gobain Performance Plastics Corporation Dissipative peristaltic pump tubing
US20210094253A1 (en) * 2019-09-27 2021-04-01 Saint-Gobain Performance Plastics Corporation Multilayer tube and method for making same

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP4689395A4 *

Also Published As

Publication number Publication date
EP4689395A1 (fr) 2026-02-11
EP4689395A4 (fr) 2026-02-11
JP2026511613A (ja) 2026-04-14
CN121002315A (zh) 2025-11-21

Similar Documents

Publication Publication Date Title
JP2010515806A (ja) シリコーンチューブ処方物及びその生産方法
CN113164647B (zh) 低温固化的有机硅润滑涂料
US20110152786A1 (en) Medical devices including a non-polar silicone matrix and a radiation resistant component
EP3234431B1 (fr) Tube composite et son procédé de fabrication et d'utilisation
EP3397882A1 (fr) Tube composite et son procédé de fabrication et d'utilisation
WO2024199366A1 (fr) Tube de pompe péristaltique et son procédé de fabrication
JP2016530394A (ja) シリコーン物品、チューブ及び物品形成方法
WO2025231124A1 (fr) Article et procédé de fabrication
US9133340B2 (en) Radiation resistant silicone formulations and medical devices formed of same
US7939014B2 (en) Radiation resistant silicone formulations and medical devices formed of same
TWI763756B (zh) 可固化聚矽氧組成物
US20230167257A1 (en) Article and method of making
EP3555213B1 (fr) Composition à base de silicone et article fabriqué avec celle-ci

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24778152

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 202517084359

Country of ref document: IN

ENP Entry into the national phase

Ref document number: 2025555899

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2025555899

Country of ref document: JP

WWP Wipo information: published in national office

Ref document number: 202517084359

Country of ref document: IN

WWE Wipo information: entry into national phase

Ref document number: 2024778152

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2024778152

Country of ref document: EP

Effective date: 20251030

ENP Entry into the national phase

Ref document number: 2024778152

Country of ref document: EP

Effective date: 20251030

ENP Entry into the national phase

Ref document number: 2024778152

Country of ref document: EP

Effective date: 20251030

ENP Entry into the national phase

Ref document number: 2024778152

Country of ref document: EP

Effective date: 20251030

ENP Entry into the national phase

Ref document number: 2024778152

Country of ref document: EP

Effective date: 20251030

ENP Entry into the national phase

Ref document number: 2024778152

Country of ref document: EP

Effective date: 20251030

ENP Entry into the national phase

Ref document number: 2024778152

Country of ref document: EP

Effective date: 20251030

ENP Entry into the national phase

Ref document number: 2024778152

Country of ref document: EP

Effective date: 20251030

WWP Wipo information: published in national office

Ref document number: 2024778152

Country of ref document: EP