WO2024253471A1 - Dispositif électrochimique à haute densité d'énergie comprenant des particules à base de silicium - Google Patents

Dispositif électrochimique à haute densité d'énergie comprenant des particules à base de silicium Download PDF

Info

Publication number
WO2024253471A1
WO2024253471A1 PCT/KR2024/007827 KR2024007827W WO2024253471A1 WO 2024253471 A1 WO2024253471 A1 WO 2024253471A1 KR 2024007827 W KR2024007827 W KR 2024007827W WO 2024253471 A1 WO2024253471 A1 WO 2024253471A1
Authority
WO
WIPO (PCT)
Prior art keywords
active material
negative electrode
electrochemical device
material layer
negative
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2024/007827
Other languages
English (en)
Korean (ko)
Inventor
김창현
최근호
김정환
조석규
이건희
조형민
이강택
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ubatt Inc
Original Assignee
Ubatt Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ubatt Inc filed Critical Ubatt Inc
Publication of WO2024253471A1 publication Critical patent/WO2024253471A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un dispositif électrochimique pouvant satisfaire une densité d'énergie élevée de 250 Wh/kg ou plus et d'excellentes caractéristiques de durée de vie et une excellente stabilité en même temps. Le dispositif électrochimique selon la présente invention comprend : une électrode positive ; une électrode négative ; et un électrolyte, et l'électrode négative comprend : un collecteur de courant d'électrode négative ; et une couche de matériau actif d'électrode négative formée sur le collecteur de courant d'électrode négative et comprenant un échafaudage de liant poreux et des particules de matériau actif d'électrode négative, les particules de matériau actif d'électrode négative comprenant des particules à base de silicium.
PCT/KR2024/007827 2023-06-07 2024-06-07 Dispositif électrochimique à haute densité d'énergie comprenant des particules à base de silicium Ceased WO2024253471A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR20230072763 2023-06-07
KR10-2023-0072763 2023-06-07

Publications (1)

Publication Number Publication Date
WO2024253471A1 true WO2024253471A1 (fr) 2024-12-12

Family

ID=93796276

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2024/007827 Ceased WO2024253471A1 (fr) 2023-06-07 2024-06-07 Dispositif électrochimique à haute densité d'énergie comprenant des particules à base de silicium

Country Status (2)

Country Link
KR (1) KR20240174508A (fr)
WO (1) WO2024253471A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20090055305A (ko) * 2007-11-28 2009-06-02 삼성에스디아이 주식회사 리튬 이차 전지용 음극 및 이를 포함하는 리튬 이차 전지
KR20170010421A (ko) * 2017-01-17 2017-01-31 삼성에스디아이 주식회사 음극, 이를 포함하는 리튬전지, 바인더 조성물 및 전극제조방법
KR20210030142A (ko) * 2019-09-09 2021-03-17 주식회사 엘지화학 음극 및 상기 음극을 포함하는 이차 전지
JP2021048146A (ja) * 2015-03-24 2021-03-25 日本電気株式会社 高安全性・高エネルギー密度電池

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102086783B1 (ko) 2019-03-27 2020-03-09 광주과학기술원 리튬 이차 전지용 후막 전극 및 리튬 이차 전지

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20090055305A (ko) * 2007-11-28 2009-06-02 삼성에스디아이 주식회사 리튬 이차 전지용 음극 및 이를 포함하는 리튬 이차 전지
JP2021048146A (ja) * 2015-03-24 2021-03-25 日本電気株式会社 高安全性・高エネルギー密度電池
KR20170010421A (ko) * 2017-01-17 2017-01-31 삼성에스디아이 주식회사 음극, 이를 포함하는 리튬전지, 바인더 조성물 및 전극제조방법
KR20210030142A (ko) * 2019-09-09 2021-03-17 주식회사 엘지화학 음극 및 상기 음극을 포함하는 이차 전지

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
GUO JUCHEN, WANG CHUNSHENG: "A polymer scaffold binder structure for high capacity silicon anode of lithium-ion battery", CHEMICAL COMMUNICATIONS, vol. 46, no. 9, 27 January 2010 (2010-01-27), UK , pages 1428 - 1430, XP093246964, ISSN: 1359-7345, DOI: 10.1039/b918727h *

Also Published As

Publication number Publication date
KR20240174508A (ko) 2024-12-17

Similar Documents

Publication Publication Date Title
WO2018221827A1 (fr) Matière active d'électrode négative, électrode négative comprenant cette matière active et batterie secondaire comprenant cette électrode négative
WO2020080831A1 (fr) Électrode à structure tridimensionnelle et élément électrochimique la comprenant
WO2018135915A1 (fr) Procédé de fabrication d'une batterie secondaire au lithium présentant des caractéristiques améliorées de stockage à haute température
WO2019151724A1 (fr) Batterie secondaire au lithium présentant de meilleures caractéristiques de stockage à haute température
WO2020085823A1 (fr) Procédé de fabrication d'anode pour batterie secondaire au lithium
WO2020180125A1 (fr) Batterie secondaire au lithium
WO2020076091A1 (fr) Procédé de fabrication d'électrode négative pour batterie secondaire au lithium
WO2019139271A1 (fr) Électrode négative de batterie secondaire au lithium et batterie secondaire au lithium la comprenant
WO2020263023A1 (fr) Électrode pour batterie secondaire au lithium ayant des conditions de composition spécifique et batterie secondaire au lithium la comprenant
WO2023059151A1 (fr) Composition d'électrode négative, électrode négative pour batterie secondaire au lithium comprenant celle-ci, batterie secondaire au lithium comprenant une électrode négative et procédé de préparation de la composition d'électrode négative
WO2017074109A1 (fr) Cathode pour pile rechargeable, son procédé de préparation, et pile rechargeable au lithium la comprenant
WO2018236166A1 (fr) Batterie secondaire au lithium
WO2020213962A1 (fr) Additif de solution électrolytique non aqueuse pour batterie secondaire au lithium et solution électrolyte non aqueuse pour batterie secondaire au lithium, et batterie secondaire au lithium les comprenant
WO2024253469A1 (fr) Dispositif électrochimique à haute densité d'énergie contenant du phosphate de fer et de lithium
WO2022250324A1 (fr) Additif d'électrode positive et électrode positive pour batterie secondaire au lithium le contenant
WO2022250323A1 (fr) Bouillie d'électrode positive et électrode positive pour batterie secondaire au lithium l'utilisant
WO2021194097A1 (fr) Batterie secondaire au lithium
WO2024158223A1 (fr) Dispositif électrochimique à haute densité d'énergie
WO2020091448A1 (fr) Accumulateur au lithium
WO2024253471A1 (fr) Dispositif électrochimique à haute densité d'énergie comprenant des particules à base de silicium
WO2023200105A1 (fr) Séparateur pour batterie au lithium rechargeable et batterie au lithium rechargeable le comprenant
WO2023224190A1 (fr) Additif, électrolyte le comprenant pour batterie secondaire au lithium, électrode positive et batterie secondaire au lithium
WO2023059072A1 (fr) Batterie secondaire au lithium
WO2024253470A1 (fr) Dispositif électrochimique comprenant une électrode positive de haute capacité
WO2022149740A1 (fr) Électrolyte pour batterie au lithium et batterie au lithium le comprenant

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24819622

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE