WO2024258700A1 - Catalyseur à haute stabilité à contrôle de sédiments améliorée - Google Patents

Catalyseur à haute stabilité à contrôle de sédiments améliorée Download PDF

Info

Publication number
WO2024258700A1
WO2024258700A1 PCT/US2024/032521 US2024032521W WO2024258700A1 WO 2024258700 A1 WO2024258700 A1 WO 2024258700A1 US 2024032521 W US2024032521 W US 2024032521W WO 2024258700 A1 WO2024258700 A1 WO 2024258700A1
Authority
WO
WIPO (PCT)
Prior art keywords
catalyst
vol
pores
metal
heavy hydrocarbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2024/032521
Other languages
English (en)
Inventor
Ke-Wei Huang
Wu ZHENWEI
David Anthony GRISAFE
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shell Internationale Research Maatschappij BV
Shell USA Inc
Original Assignee
Shell Internationale Research Maatschappij BV
Shell USA Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shell Internationale Research Maatschappij BV, Shell USA Inc filed Critical Shell Internationale Research Maatschappij BV
Publication of WO2024258700A1 publication Critical patent/WO2024258700A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un catalyseur à lit bouillonnant utilisé pour convertir un hydrocarbure lourd et réguler le rendement de sédiments à un niveau minimal. Ledit catalyseur comprend un extrudat ayant un mélange décortiqué d'un oxyde inorganique, au moins un métal du groupe VIB du tableau périodique des éléments, et au moins un métal du groupe VIII du tableau périodique des éléments. Le ou les métaux du groupe VIB sont présents en une quantité supérieure à 7,5 % en poids, et le catalyseur présente une structure poreuse telle que 8 % en volume à 18 % en volume du volume poreux total est présent dans des pores d'un diamètre supérieur à 5000, et 63 % en volume à 80 % en volume du volume poreux total est présent dans des pores d'un diamètre inférieur à 250.
PCT/US2024/032521 2023-06-14 2024-06-05 Catalyseur à haute stabilité à contrôle de sédiments améliorée Ceased WO2024258700A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202363508040P 2023-06-14 2023-06-14
US63/508,040 2023-06-14

Publications (1)

Publication Number Publication Date
WO2024258700A1 true WO2024258700A1 (fr) 2024-12-19

Family

ID=91616497

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2024/032521 Ceased WO2024258700A1 (fr) 2023-06-14 2024-06-05 Catalyseur à haute stabilité à contrôle de sédiments améliorée

Country Status (1)

Country Link
WO (1) WO2024258700A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7169294B2 (en) 2001-01-05 2007-01-30 Nippon Ketjen Co., Ltd. Hydroprocessing catalyst and use thereof
US7820036B2 (en) 2006-08-03 2010-10-26 Shell Oil Company Highly stable heavy hydrocarbon hydrodesulfurization catalyst and methods of making and use thereof
US8969242B2 (en) 2011-09-01 2015-03-03 Advanced Refining Technologies Llc Catalyst support and catalysts prepared therefrom
US9879187B2 (en) 2012-04-26 2018-01-30 Shell Oil Company Hydroprocessing catalyst, method of making, and process for treating heavy hydrocarbon feedstocks
US20220062871A1 (en) 2020-09-01 2022-03-03 Shell Oil Company Heavy hydrocarbon hydroprocessing catalyst and methods of making and using thereof

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7169294B2 (en) 2001-01-05 2007-01-30 Nippon Ketjen Co., Ltd. Hydroprocessing catalyst and use thereof
US7820036B2 (en) 2006-08-03 2010-10-26 Shell Oil Company Highly stable heavy hydrocarbon hydrodesulfurization catalyst and methods of making and use thereof
US8969242B2 (en) 2011-09-01 2015-03-03 Advanced Refining Technologies Llc Catalyst support and catalysts prepared therefrom
US9879187B2 (en) 2012-04-26 2018-01-30 Shell Oil Company Hydroprocessing catalyst, method of making, and process for treating heavy hydrocarbon feedstocks
US20220062871A1 (en) 2020-09-01 2022-03-03 Shell Oil Company Heavy hydrocarbon hydroprocessing catalyst and methods of making and using thereof

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
J. AM. CHEM. SOC., vol. 60, 1938, pages 309 - 316

Similar Documents

Publication Publication Date Title
US10569254B2 (en) Catalyst support and catalysts prepared therefrom
RU2342995C2 (ru) Катализаторы гидроконверсии и способы их изготовления и применения
US9879187B2 (en) Hydroprocessing catalyst, method of making, and process for treating heavy hydrocarbon feedstocks
KR102025447B1 (ko) 저비용 고활성 수소첨가처리 촉매
US20100276339A1 (en) Process and catalyst for the hydroconversion of a heavy hydrocarbon feedstock
CA2853105C (fr) Catalyseur d'hydrotraitement s'activant tout seul et procede pour le traitement de charges d'hydrocarbures lourds
US12605699B2 (en) Heavy hydrocarbon hydroprocessing catalyst and methods of making and using thereof
US10570346B2 (en) Ebullated bed process for high conversion of heavy hydrocarbons with a low sediment yield
WO2024258700A1 (fr) Catalyseur à haute stabilité à contrôle de sédiments améliorée
WO2026006039A1 (fr) Catalyseur auto-activateur stable pour valorisation d'hydrocarbures lourds en lit fixe
TW202605132A (zh) 用於固定床重烴升級之穩定自活化催化劑

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24735109

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE