WO2025113865A1

WO2025113865A1 - Sheet containing polyurethane layers, preparation method and use

Info

Publication number: WO2025113865A1
Application number: PCT/EP2024/078297
Authority: WO
Inventors: João Nuno FERREIRA DA MOTA; Maria Julieta Silva Magalhães; Ivone Marisa DA SILVA MAIA; Pedro Diogo MACIEL FERREIRA; Sara Patricia Da Silva Marques; Filipe Miguel DA SILVA RIBEIRO; Helena Isabel Pereira Da Costa Aguilar Ribeiro
Original assignee: Tmg - Tecidos Plastificados E Outros Revestimentos Para A Industria Automovel SA
Current assignee: Tmg - Tecidos Plastificados E Outros Revestimentos Para A Industria Automovel SA
Priority date: 2023-11-28
Filing date: 2024-10-08
Publication date: 2025-06-05
Anticipated expiration: 2026-05-28

Abstract

A sheet comprising a support layer, an intermediate layer containing polyurethane having a gel content of at least 20 %, and a cover layer containing thermoplastic polyurethane having a gel content of less than 10 %, wherein the support layer is a textile layer and the intermediate layer is a compact layer, wherein the support layer and the intermediate layer only partly interpenetrate each other in their thickness direction to form a compound structure, wherein the thickness of the intermediate layer above the compound structure is at least 20 μm; a method of preparing the sheet; and the use of the sheet as a surface material in the interior of a vehicle.

Description

Sheet containing polyurethane layers, preparation method and use

Field of the invention

The present invention relates to a sheet comprising a support layer, an intermediate layer containing polyurethane having a high gel content, and a cover layer containing polyurethane having a very low gel content, a method of preparing the sheet, and the use of the sheet as a surface material such as an artificial leather in a vehicle.

Background art

EP 3 533 601 A1 discloses a composite structure comprising a low-density foam layer, a textile layer, and a thermoplastic cover layer comprising polyolefin or polyvinylchloride (PVC) and optionally comprising thermoplastic elastomers. The composite structure shows good tearing properties and haptics and is improved in terms of wrinkle formation and handling during processing, especially during sewing.

EP 1 927466 A1 discloses a flexible composite structure comprising a support layer such as a textile layer, one or more polyurethane layers, and a lacquer layer.

Problem to be solved by the invention

The problem underlying the present invention was to combine the properties of thinness and good appearance with the properties of softness and flexibility to achieve good haptics and handling during a cut and sew process and press lamination/thermal edge wrapping.

Summary of the invention

The problem underlying the present invention was solved by providing the sheet according to the present invention.

The present application covers the following preferred aspects.

[1] A sheet comprising a support layer, an intermediate layer containing a polyurethane having a gel content of at least 20 % as component (A), and a cover layer containing a thermoplastic polyurethane having a gel content of less than 10 %, preferably less than 5 % as component (a), wherein the support layer, which is preferably a textile layer, and the intermediate layer, which is preferably a compact layer, only partly interpenetrate each other in their thickness direction to form a compound structure, wherein the thickness of the intermediate layer above the compound structure is at least 20 pm. [1 -1] The sheet according to aspect [1] which is suitable for preparing a sewn product obtainable by sewing the sheet and is preferably suitable for preparing a sewn product by folding the sheet, placing two A-side parts or B-side parts of the sheet together to provide a contact area, and sewing the two parts of the sheet in the contact area; or the sheet according to aspect [1], which is suitable for preparing a wrapped product obtainable by using the sheet in a process of edge wrapping a substrate, preferably thermally edge wrapping a substrate.

[1 -2] The sheet according to any of the preceding aspects, wherein the thickness of the intermediate layer above the compound structure is at least 100 pm.

[1 -3] The sheet according to any of the preceding aspects, wherein the content of component (A) in the intermediate layer is at least 20 mass%, and the content of component (a) in the cover layer is at least 50 mass%.

[1 -4] The sheet according to any of the preceding aspects, wherein the extent of support layer interpenetration, defined as [(thickness of the compound structure)/(thickness of the support layer)] x 100 %, is 0.5 % to 10 %, preferably 0.5 % to 2 %.

[1 -5] The sheet according to any of the preceding claims, wherein the extent of intermediate layer interpenetration, defined as [(thickness of the compound structure)/(thickness of the intermediate layer)] x 100 %, is 5 % to 50 %, preferably 10 % to 20 %.

[1 -6] The sheet according to any of the preceding aspects, wherein the part of the support layer being part of the compound structure has at least 80 %, preferably at least 90 %, of the area density of the support layer not being part of the compound structure, as observed by microscopy of a cross-section of the sheet.

[1 -7] The sheet according to any of the preceding aspects, wherein the sheet, has a seam strength of at least 400 N according to TPJLR.52.417, wherein 100 mm x 150 mm specimens are stitched and the seam strength is assessed by applying a load at a rate of 300 mm/min and recording the maximum load in Newtons at the time of break, wherein the stitch is a simple lock stitch length of 4.2 mm - 5.1 mm (5 - 6 stitches per 25 mm) and runs approximately 10 mm from the cut edges of the test samples.

[1 -8] The sheet according to any of the preceding aspects, wherein the cover layer is coated with a silicone layer having a thickness of at least 30 pm and the silicone layer is coated with a lacquer layer having a thickness of less than 30 pm.

[1 -9] The sheet according to any of the preceding aspects, wherein the sheet preferably shows no damages and no changes after 100,000 flexing cycles at room temperature, after 10,000 flexing cycles at -10 °C after exposed to VDA oils, and after 100,000 flexing cycles after exposed to VDA oils at room temperature; or wherein the sheet preferably shows no damages and no changes after 10,000 flexing cycles at -10 °C after exposed to VDA oils, after 30,000 flexing cycles after 168 hours at 100 °C and 10,000 flexing cycles at -20°C after 336 hours at 100 °C.

[1 -10] The sheet according to any of the preceding aspects, wherein the support layer is invisible from the A-side of the sheet in daylight and absence of backlight.

[1 -11] The sheet according to any of the preceding aspects, wherein the intermediate layer and the cover layer are compact layers.

[1 -12] The sheet according to any of the preceding aspects, wherein the cover layer contains a thermoplastic elastomer (TPE) in addition to the thermoplastic polyurethane (TPU), wherein the total content of TPE and TPU preferably makes up at least 80 mass% of the total mass of the cover layer.

[1 -13] The sheet according to any of the preceding aspects, wherein the sheet can be folded to form a double-layer structure, in which two A-sides of the composite structure are layered on each other and contact each other at the folding edge, and the double-layer structure can be unfolded to its initial state.

[1 -14] The sheet according to aspect [1 -13], wherein the sheet shows no visible damage or change at the folding edge after folding and unfolding.

[1 -15] The sheet according to a combination of aspects [1], [1 -11], and [1 -13],

[1 -16] The sheet according to a combination of aspects [1 -12] and [1 -15],

[1 -17] The sheet according to any of the preceding aspects, wherein the cover layer contains a foamed sublayer.

[1 -18] The sheet according to any of the preceding aspects, wherein the sheet has a bending stiffness of less than 0.5 N, preferably less than 0.2 N, wherein 30 mm x 50 mm specimens are bended up to 30° at a bending rate of 1.5° per second and the bending force in Newtons is assessed at 30°.

[2] The sheet according to any of the preceding aspects, wherein the support layer is a textile layer and the intermediate layer is a compact layer.

[2-1] The sheet according to aspect [2], wherein the textile layer contains or consists of one or more kinds of fibers selected from the group consisting of polyester, polypropylene, polyamide, cotton or other natural fibers

[2-2] The sheet according to a combination of aspects [2] and [1 -15], preferably [2] and [1 - 16],

[3] The sheet according to any of the preceding aspects, wherein the intermediate layer has a thickness of 20 to 300 pm. [4] The sheet according to any of the preceding aspects, wherein the support layer is a textile layer having a thickness of 200 to 1200 pm, the intermediate layer has a thickness of 50 to 300 pm, and the cover layer has a thickness of 100 to 600 pm.

[5] The sheet according to any of the preceding aspects, wherein the support layer has a thickness of at least 800 pm, preferably 800 to 1000 pm, and the compound structure has a thickness of less than 40 pm, preferably 5 to 30 pm.

[5-1] A combination of aspects [5], [4], and [1 -4] is preferred.

[6] The sheet according to any of the preceding aspects, which does not contain polyvinylchloride and does not contain a plasticizer.

[7] The sheet according to any of the preceding aspects, wherein the cover layer contains a thermoplastic styrenic elastomer as component (b).

[7-1] The sheet according to aspect [7], wherein the cover layer contains a compatibilizer as component (c). [7-2] The sheet according to aspect [7-1], wherein component (c) is a copolymer containing polyurethane blocks and styrenic polymer blocks. [7-3] The sheet according to aspect [7-1] or [7-2], wherein the content of each of the polyurethane and the thermoplastic styrenic elastomer in the cover layer is at least 20 mass%, preferably at least 30 mass%.

[8] The sheet according to any of the preceding aspects, wherein (i) the intermediate layer and the cover layer are directly bonded to each other or (ii) at least one additional layer is arranged between the intermediate layer and the cover layer.

[8-1] A combination of aspects [8](i) and [1 -1] is preferred. [8-2] A combination of aspects

[8] (i) and [1 -4] is more preferred. [8-3] A combination of aspects [8-2] and [1 -3] is even more preferred. [8-4] A combination of aspects [8-1] and [1 -7] is preferred. [8-5] The sheet according to any of the preceding aspects, wherein the sheet consists of a textile layer as the support layer, the intermediate layer, the cover layer, and an optional lacquer layer.

[9] The sheet according to any of the preceding aspects, wherein component (a) is aromatic.

[9-1] The sheet according to any of the preceding aspects, wherein each urethane unit of component (a) contains an aromatic group. [9-2] The sheet according to any of the preceding aspects, wherein component (a) is derived from an aromatic diisocyanate. [9-3] The sheet according to any of the preceding aspects, wherein the cover layer contains a lower sublayer and an upper sublayer, wherein component (a) is contained in the upper sublayer and is aromatic.

[10] The sheet according to any of the preceding aspects, wherein the cover layer contains a lower sublayer and an upper sublayer, wherein the lower sublayer is directly bonded to the intermediate layer and has a hardness Shore A according to DIN 53505 of at most 70, and the upper layer has a hardness Shore A according to DIN 53505 of at least 75.

[11] The sheet according to aspect [10], wherein the lower sublayer and the upper sublayer differ in their hardness Shore A according to DIN 53505 by at least 10.

[12] A method of preparing a sheet according to any of aspects [1] to [11], comprising

(i) a step of providing a two-component polyurethane system, (ii) a step of providing a layered structure composed of the support layer and a layer of the two-composition polyurethane system, (iii) a step of curing to obtain the support layer coated with the intermediate layer containing polyurethane having a gel content of at least 20 %; or

(i) a step of providing a polyurethane layer of a polyurethane composition based on water and/or solvent and containing polyurethane having a gel content of at least 20 %, and at least partly removing the water and/or solvent; (ii) a step of providing a layered structure composed of the support layer and the polyurethane layer, (iii) a step of removing remaining water and/or solvent to obtain the intermediate layer; and, after either set of steps (i) to (iii) above, (iv) a step of applying molten cover layer raw material containing molten component (a) onto the intermediate layer, and (v) a step of solidifying the cover layer raw material to obtain the sheet.

[13] A sewn product obtainable by sewing the sheet according to any of aspects [1] to [11] or a wrapped product obtainable by using the sheet according to any of aspects [1] to [11] in a process of edge wrapping a substrate, preferably thermally edge wrapping a substrate, wherein the substrate is preferably an interior part of a vehicle such as a door panel.

[13-1] A method of preparing a sewn product comprising sewing a sheet according to any of aspects [1] to [11],

[13-2] The method according to aspect [13-1], comprising folding the sheet, placing the A- side or the B-side surfaces of the sheet together to provide a contact area, and sewing the two parts of the sheet in the contact area.

[13-3] A method of preparing a wrapped product according to aspect [13] comprising wrapping the sheet around the edge of a substrate.

[14] The use of a sheet according to any of aspects [1] to [11] as an artificial leather.

[14-1] The use of a sheet according to any of aspects [1] to [11] in a cut and sew process or in a thermal wrapping process.

[15] The use of a sheet according to any of aspects [1] to [11] or the sewn product or wrapped product according to aspect [13] as a cover material in the interior of a vehicle. Advantages of the invention

The sheet according to the invention is thin and soft and exhibits a low wrinkle formation when bent. These properties make the sheet easy to handle and allow easy needle penetration for cut and sew applications.

The intermediate layer is thin enough and interpenetrates the support layer to a low extent to keep the sheet flexible, yet thick enough to keep the support layer invisible from the A- side of the sheet.

The sheet is improved in terms of wrinkle formation and handling in a cut and sew process and a wrapping process due to the compact material construction. The sheet is furthermore improved in terms of textile backing indentation on the A-surface of the material due to the presence of the intermediate layer acting as a barrier to TPU penetration in the textile support.

The sheet is close to a monomaterial since both the intermediate layer and the cover layer contain polyurethane (PU).

The method of preparing the sheet may combine two coating technologies, i.e., indirect transfer coating and extrusion, to achieve the desired physical properties rendering the sheet suitable for cut&sew and edge wrapping.

The sheet is improved in terms of flexibility and elongation and thus, the sheet shows advantageous haptics and complies with specifications for seat applications (flexing endurance) and fits the requirements for edge wrapping of trim parts (bending stiffness).

The combined use of a textile support layer and thin upper layers renders the sheet more lightweight than prior art sheets.

The sheet can be advantageously used either as a trim material in the interior of a vehicle and as material for seat covers, depending on the sheet embodiment.

Embodiments of the invention

The sheet of the present invention may consist of or contain the support layer, the intermediate layer, and the cover layer described herein. The support layer is arranged at the B-side and the cover layer is arranged at the A-side of the sheet. Herein, the terms "A-side" and "B-side" either refer to the sheet as a whole or to an individual layer, and the terms "above" and "below" the sheet or a layer denote a position at the A-side and the B-side, respectively, of the sheet or layer. The support layer and the intermediate layer interpenetrate each other and are thus directly bonded to each other. The other layers contained in the sheet are layered on each other either directly, e.g., the A-side of the intermediate layer contacts the B-side of the cover layer without any material such as an adhesive disposed between them, or indirectly, i.e., having layer(s) or an adhesive disposed between them. The cover layer may optionally be coated with a lacquer layer. The sheet is a layer structure itself. Additional layers or structures may be arranged at the B-side of the support layer.

Herein, the terms "the sheet", "the support layer", "the intermediate layer", and "the cover layer" refer to "the sheet according to the present invention", "the support layer contained in the sheet according to the present invention", "the intermediate layer contained in the sheet according to the present invention", and "the cover layer contained in the sheet of the present invention", respectively, unless explicitly stated otherwise.

The support layer is directly bonded to the intermediate layer. The layers may interpenetrate each other since the support layer contains voids, e.g. in the case of a foam or a textile. The interpenetrated structure is herein referred to as a compound structure. The compound structure consists of a part of the support layer and a part of the intermediate layer in their thickness direction. In each case, the term "a part" means that the respective layer is not included in the compound structure over the whole thickness direction of the respective layer. In other words, a full interpenetration is excluded, and both the intermediate layer and the support layer have a non-interpenetrated layer part in the thickness direction. As a result, the support layer such as the textile layer is not exposed at the A-side of the intermediate layer surface, and the intermediate layer is not exposed at the B-side of the support layer surface. In a preferred embodiment, the non-exposed A-side of the intermediate layer is thick enough and/or contains pigments to render the support layer invisible from the A-side of the sheet. Thus, invisibility of the support layer may be achieved even if the cover layer has high light transmittance. Herein, invisible means that the structure cannot be seen by a user when looking at the A-side of the sheet in daylight and absence of B-side backlight. At the same time, the thickness of the intermediate layer and/or the pigment concentration may be adjusted to allow a hidden-until-lit property described below.

The cover layer may contain a structural element at its B-side, i.e., between the cover layer and the intermediate layer. In that case, the cover layer is preferably bonded to the intermediate layer by using an adhesive. The structural element may have optical properties. The structural element may be an opaque or colored pattern that forms a graphic design, image, or logo to serve decorative or indicative purposes. For instance, the structural element may be a very thin printed structure visible through the cover layer. Examples for applying the pattern are inkjet printing, screen printing, laser printing, or laser etching.

Preferably, the sheet is suitable for preparing a sewn product obtainable by sewing at least two sheets or two parts of the same sheet. The sewn product may be prepared by folding the sheet, placing two A-side parts or B-side parts of the sheet together and sewing the two parts of the sheet in the contact area. In order for the sheet according to the invention to have the desired properties, e.g. easy processability when sewing, the sheet must not be too hard. For suitability for sewing, it is also important that the sheet has a suitable stitch tearout force. This is preferably at least 40 N according to DIN EN ISO 23910. In one embodiment, the sheet is both suitable as a tearable coating for an airbag cover without a material weakening and suitable for preparing a sewn product obtainable by sewing at least two layers of the sheet. The sheet is flexible and preferably shows no damages and changes after 500,000 flexing cycles, more preferably after 1,000,001 flexing cycles in a test according to DIN 53 351.

The sheet may be opaque or translucent. Generally, a translucent structure allows the transmittance of more visible light than an opaque structure when light is emitted from the same light source and hits the structures. Herein, the meaning of the term "translucency" covers the meaning of "transparency". In general, transparency is the physical property of allowing light to pass through the material without being scattered. Translucency is a superset of transparency and allows light to pass through and allows scattering. In other words, a translucent medium allows the transport of light while a transparent medium not only allows the transport of light but allows for image formation. Transparent materials appear clear. Since the value of the light transmittance is affected by absorption, scattering, reflection and the like, the exact light transmittance values of the different components of the sheet may vary depending on the type of light source, the composition and thickness of the various layers. The light transmittance also differs for different wavelength ranges. The light transmittance of the layer structures described in the present application, i.e., the individual layers or any of the composite structures, respectively, is determined as follows: Equipment: Datacolor, model 850; Lamp: Xenon. The total transmittance is measured according to the user's guide provided by the manufacturer. A white plaque (e.g. Spectralon® plaque) is used as an optical standard for transmission calibration and measurement. The white plaque is placed at the front aperture plate. The sample to be measured is placed between the sphere opening and the sensor. The transmittance is determined within the range of 400 to 700 nm at the wavelength X_max of the maximum transmittance peak for the sample. The light transmittance [%] of a sample is defined as 100 % x (transmittance value measured at X_max in the presence of the layer structure)/(transmittance value measured at X_max in the absence of the layer structure). The light transmission means the permeability for light emitted at a position facing the B-side of the sheet or layer and detected at a position facing the A-side surface of the sheet or layer. The light transmittance of the sheet refers to the whole sheet if all layers are translucent. The light transmittance of the sheet may be 1 % to 100 %, 1 % to 90 %, 1 % to 50%, or 5 to 50 %, preferably 1% to 30%, more preferably 2 to 20%. A low light transmittance such as 1 % to 50 % may be advantageous for hidden-until-lit applications. To enable a hidden-until- lit property of hiding the elements arranged under the cover layer when no light source is activated, the light transmittance of the sheet is preferably 1 to 50%, more preferably 1 to 30% at max. In case a hidden-until-lit property is not desired, the light transmittance of the sheet may be 10 to 90%, preferably 20 to 80% at _max.

The sheet may contain additives such as UV stabilisers, pigments, heat stabilizers, flame retardants, processing aids (rheology modifiers, defoamers, levelling agents), compatibilizer agents. These additives may be contained in the cover layer, intermediate layer, and the optional lacquer layer. Pigments may be selected from carbon black, organic red, organic yellow, phthalocyanine blue, and titanium white, either used in waterborne and/or solvent based dispersions or thermoplastic masterbatches. If uniform color and high transparency of the sheet is desired, the pigments are preferably small to reduce light scattering. The particle size of the pigments is preferably less than 10 pm, more preferably less than 1 pm, even more preferably less than 100 nm. A heat stabilizer helps preserve the properties of a polymer at elevated temperatures. Various heat stabilizers like metallic salts (stabilize PVC), organometallic compounds, non-metallic organic stabilizers, organophosphites and epoxies can be used. Organophosphites protect polymers during the manufacturing process. Phenolic antioxidants protect the polymer during its usable life. Phenolic antioxidants are radical scavengers which prevent thermal degradation of polymers. Their effectiveness increases when used in combination with phosphites, thioethers and light stabilizers. Other examples of antioxidants are sterica lly hindered phenols such as butylated hydroxytoluene (2,6-di-tert-butyl-4-methylphenol, BHT), butylated hydroxyanisole (BHA), tertiary- butylhydroquinone (TBHQ) and gallates. In particular, halogenated polymers such as poly(vinyl chloride) (PVC) may require the use of heat stabilizers.

A UV stabiliser as an additive may achieve the object of maintaining the desired light transmittance after an exposure to UV radiation. UV radiation ranges between wavelengths of 280 and 400 nm. Polymers are sensitive to certain wavelengths of UV radiation. For instance, a UV sensitive polymer is aromatic polyurethane. Suitable UV stabilizers may be Ultraviolet Absorbers and Hindered Amine Light Stabilizers (HALS). Rutile titanium oxide is effective in the 300-400 nm range but is not very useful in the very short wavelength UVB range below 315. Hydroxybenzophenone and hydroxyphenylbenzotriazole have the advantage of being particularly suitable for transparent applications. Other UV absorbers include oxanilides for polyamides, benzophenones for PVC and benzotriazoles and hydroxyphenyltriazines. Hindered Amine Light Stabilizers (HALS) share the 2, 2,6,6- tetramethylpiperidine ring structure. HALS are particularly effective in polyolefins and polyurethane. Any of these compounds may be combined. Some of these combinations have synergistic effect. For example, benzotriazoles are often combined with HALS. In the present invention, the terms "comprises," "comprising," "including," and "having," are inclusive and therefore specify the presence of stated features, steps, layers and/or components, but do not preclude the presence or addition of one or more other features, steps, layers, components, and/or groups thereof. The method steps, processes, and operations described herein are not to be construed as necessarily requiring their performance in the particular order discussed or illustrated, unless specifically identified as an order of performance. It is also to be understood that additional steps may be employed.

Whenever it is mentioned in the context of this description that individual compositions or layers are based on a certain material, this should be interpreted as the respective material forming the main constituent of the composition or layer, wherein other constituents may also be present in small quantities. In embodiments, the term "based on" a certain material means a content of more than 50 mass%, preferably 90 mass%, and more preferably 95 mass%.

As used herein, the singular forms "a," "an," and "the" may be intended to include the plural forms as well, unless the context clearly indicates otherwise. For instance, components are generally described in the singular form, such as "a" component or "containing a" component. Such singular form formulations are meant to include more than one of the indicated component, unless indicated otherwise.

The term "and/or" includes any and all combinations of one or more of the associated listed items. Percentages (%) are percentages by mass (% by mass) unless explicitly indicated otherwise. The standards and norms mentioned refer to the latest version available at the time this application was filed, unless indicated otherwise.

In the present invention, the gel content is measured according to ASTM D2765-16 (except for placing the sample in xylene for 24 h instead of 12 h). A sample is weighed (initial weight) and placed in xylene for 24 hours at 180 °C, the dissolved material is separated and the weight of the remaining material is determined (final weight); gel content [%] = [(final weight)/(initial weight)] x 100 %.

Support layer

The support layer may have a thickness of 200 to 6000 pm, preferably 200 to 1200 pm, more preferably 800 to 1000 pm. It may be made of any material. For instance, the support layer may be a textile layer or a foam layer having open cells or closed cells. The support layer is preferably flexible and thin. Preferably the support layer consists of a textile layer. Examples of a textile layer are knitted fabrics, woven textiles, non-woven textiles, glass fiber textiles, spunlace, or a spacer fabric. A knitted fabric is a flexible material made by creating an interlocking bundle of yarns or threads, which are produced by spinning raw fibers into long and twisted lengths. A textile is not compact and comprises a large volume ratio of hollow spaces that are usually filled with air. The density of the textile layer is preferably 50 to 300 kg/m³.

The textile layer of the support layer may contain or consist of one or more kinds of fibers selected from the group consisting of polyester, polypropylene, polyamide, cotton and natural fibers, or combinations thereof.

The support layer may consist of several layers. For instance, the support layer may comprise a textile layer being bonded to the intermediate layer and having a thickness of 0.3 to 5 mm, a foam layer having a thickness of 0.5 to 10 mm and a density or preferably 30 to 300 kg/m³, and, optionally, a textile layer having a thickness of 0.3 to 2.5 mm in this order, wherein each of the textile layers is preferably directly bonded to the foam layer. The direct bonding excludes an additional layer or adhesive layer between the textile layer and foam layer. Hence, the sheet may contain several layers without containing any adhesive layer. The foam layer may have adhesive properties so that it can adhere firmly to an A-side or B- side textile without the addition of another adhesive.

In embodiments, an adhesive layer may be arranged between the textile layer and the foam layer and/or between the foam layer and the optional textile layer. The adhesive may be a polyolefinic adhesive, a polyurethane adhesive, an acrylic adhesive, or a hot melt adhesive based on polyurethane (PUR). The adhesive may be used in a thickness of 40 pm. The support layer may contain a textile layer, an adhesive layer, a foam layer, an adhesive layer, and a textile layer in this order.

The B-side of the support layer may contain additional layers, e.g., a foam layer or a layer of polyvinylchloride, and/or functional elements such as touch sensors. In the case of functional elements, the sheet may be translucent and the B-side of the cover layer or the B- side of the support layer may contain opaque areas.

Intermediate layer

The intermediate layer contains polyurethane having a gel content of at least 20 % as component (A).

Component (A) may be obtained by curing a two-component polyurethane system, which may be a high-solid system. It may contain a diol polyurethane prepolymer and a chain extender, e.g., a diisocyanate. The prepolymer may be prepared from the raw materials mentioned below in relation to component (a) of the cover layer. Alternatively, the two- component polyurethane system may contain diisocyanate polyurethane prepolymers and diamines as crosslinkers. The raw materials are selected to meet the requirements of having a viscosity suitably high for achieving the desired low extent of interpenetration into the support layer and to yield the desired gel content in the cured polyurethane. To achieve the desired gel content, the system may be based on triols or triisocyanates to some extent. The two-component system may contain a polymerization catalyst which may remain in the final intermediate layer as component (B). The content of component (B) in the intermediate layer is preferably less than 1 mass%.

Alternatively, component (A) may be based on a one-component polyurethane system, which is a composition containing component (A) and water and/or solvent. The intermediate layer is obtained by drying the one-component system by removing the water and/or solvent. Residual water and/or solvent may be contained in the final intermediate layer as component (C). The content of component (C) in the intermediate layer is preferably less than 5 mass%, more preferably less than 1 mass%.

Component (A) may be based on a combination of one-component and a two-component polyurethane system.

The intermediate layer is preferably a compact layer. Herein, a compact layer preferably has a density of higher than 800 kg/m³ and more preferably higher than 850 kg/m³. The intermediate layer preferably has a thickness of more than 20 pm to 300 pm.

The intermediate layer may contain a thermoplastic elastomer (TPE) and optionally a compatibilizer as described and in the amounts mentioned in relation to the cover layer below. Furthermore, the intermediate layer may contain usual additives such as plasticizers, stabilizers, anti-aging agent (e.g. antioxidants), fillers and pigments (silica, TiC , CaCOs, Mg(OH)2, carbon black, mica, kaolin, clay, coal dust, lignin, talc, BaSC , AI(OH)3, ZnO, and MgO), flame retardants (e.g. antimony trioxide or zinc hydroxystannate), waxes, colorants, compatibilizers and other auxiliary substances (e.g. viscosity aids, adhesion promoters, etc.). Example of UV stabilisers are those mentioned above.

Compound structure

The sheet contains a compound structure. The compound structure as such is not a layer but is defined by the interaction between the support layer and the intermediate layer. Preferably, this interaction is exclusively a physical interaction and excludes chemical interactions such as chemical bonds. The compound structure consists of a part of the support layer and a part of the intermediate layer interpenetrating each other. The extent of intermediate layer interpenetration is low, preferably 5 % to 50 %, more preferably 10 % to 20 %, and is defined as follows: Extent of interpenetration [%] = [(thickness of the compound structure)/(thickness of the intermediate layer)] x 100 %. The thickness of the intermediate layer is defined as the thickness of the thickness of the compound structure plus the thickness of the part of the intermediate layer not being part of the compound structure, i.e., plus the thickness of the intermediate layer above the compound structure. Similarly, the extent of support layer interpenetration is low, preferably 0.5 % to 10%, more preferably 0.5 % to 2 %, and is defined as follows: Extent of interpenetration [%] = [(thickness of the compound structure)/(thickness of the support layer)] x 100 %. The thickness of the support layer is defined as the thickness of the compound structure plus the thickness of the part of the support layer not being part of the compound structure, i.e., plus the thickness of the support layer below the compound structure.

The compound structure may be characterized by the structure of a cross-section of the sheet perpendicular to the layer plane, as observed with a microscope. In one embodiment, the reaction conditions, e.g., the viscosity of the intermediate layer raw material and the applied pressure, may be adjusted such that the density of the support layer is only slightly reduced in the lamination step. Preferably, no or almost no pressure is applied such that the support layer is not or almost not compressed during lamination. As a result, the part of support layer being part of the compound structure has at least 80 % of the area density of the support layer not being part of the compound structure. The density of the support layer may be adjusted such that the compound structure is composed of similar ratios of support layer and cover layer. The compound structure may consist of 30 to 70 % of the support layer material and 70 to 30 % of the cover layer material. The percentages may be determined on a weight basis or by simply determining the respective areas by microscopy of a cross-section of the sheet perpendicular to the layer plane. The process of lamination may be adjusted such that the hollow spaces (which are usually filled with gas such as air) in the textile layer of the support layer are (almost) completely filled with cover layer composition to obtain a compact compound structure.

Cover layer

The cover layer contains thermoplastic polyurethane having a gel content of less than 10 % as component (a). The cover layer shows thermoplastic properties and has a thickness of preferably 100 pm to 600 pm, more preferably 50 pm to 300 pm. The cover layer is a compact layer or a hybrid layer (comprising a compact layer and a foamed layer). Preferably, the cover layer is compact. The cover layer may consist of one or more layers. Preferably, the cover layer consists of a single layer or two sublayers. In the case of two or more sublayers, the components recited herein may be contained in one or more or all sublayers. For instance, the aromatic component (a) may be contained only or at least in the upper sublayer of a cover layer consisting of two sublayers. The cover layer of the sheet may have a grain and/or may be coated with a lacquer layer.

The cover layer may contain usual additives such as those mentioned above in relation to the intermediate layer. The cover layer may be translucent. The optical properties of polymers are determined by their structure. Generally, amorphous polymers provide transparency while crystalline polymers provide opacity, particularly in thicker products such as injection molded end products. Crystallinity reduces the transparency by causing refraction and reflection of light and light scattering on the boundaries between the crystalline and amorphous regions. The light transmittance of semicrystalline polymers can be improved through additive technology. Crystalline structures are generally very ordered and are thus strong and rigid. On the other hand, amorphous polymers are characterized by a relatively low resistance to heat, toughness at low temperatures and low dimensional stability. Hence, it may be preferred that the polymers are not too amorphous and have a certain degree of crystallinity. In the present invention, the degree of crystallinity may be adjusted to achieve a desired balance of optical properties and other physical properties such as flexibility. In particular, the addition of rubber components may decrease the crystallinity.

The cover layer consists of or contains thermoplastic polyurethane (TPU) having a gel content of less than 10 %, preferably less than 5 % as the component (a) of the cover layer. The thermoplastic property requires that the overall degree of crosslinking is not too high. The gel content is preferably 0 % to 5 %. TPU is a thermoplastic elastomer comprising linear segmented block copolymers composed of hard and soft segments. A polyurethane is prepared from polyisocyanates such as diisocyanates and polyols such as diols. The polyol may be aliphatic or aromatic. An aliphatic group can be branched or unbranched and may have a carbon number of 1 to 10, in particular 1 to 6. It can be a methyl, ethyl, propyl, butyl, pentyl and/or hexyl group. The cycloaliphatic group can, for example, be based on a cyclopropyl, cyclobutyl, cyclopentyl, dicyclohexylmethane, cyclohexyl and/or isophorone group. The heterocyclic groups include the furfuryl group. The polyol may be a polymer with a molecular weight of 200 to 12,000, in particular 250 to 2,000. Examples are polyester polyols, polyether polyols, polythioether polyols, polycarbonate polyols and aliphatic polyacetals containing hydroxyl groups and aliphatic polycarbonates containing hydroxyl groups, or mixtures of at least two of these polyols. The TPU may contain groups derived from compounds containing reactive groups other than hydroxy groups, e.g., compounds having thiol groups or amine groups.

In one embodiment, the component (a) contains aromatic groups and is thus an aromatic TPU. For instance, the TPU may be prepared by using aromatic isocyanates such as toluene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), and naphthalene diisocyanate (NDI). The content of aromatic groups in the TPU may be more than 3 mass% or even more than 5 mass%. Aromatic TPU has a high glass transition temperature and is rather brittle, whereas aliphatic TPU has a low glass transition temperature and is flexible. Hence, aromatic TPU renders the cover layer stiffer and thus less suitable for cut and sew applications. The use of TPS (thermoplastic styrenic elastomer) renders the cover layer more flexible and compensates the effect of aromatic TPU.

The cover layer may contain a thermoplastic elastomer (TPE) as component (b). A TPE is defined as an elastomer showing thermoplastic behaviour. The term "thermoplastic" denotes polymers or polymer compositions that show thermoplastic properties, in particular thermoreversibility. TPE behaves rubber-elastically in the range of usual service temperatures. TPE is a copolymer or an elastomer alloy, i.e., a physical mix of polymers that consists of materials with both thermoplastic and elastomeric properties. The desired properties can be obtained by varying the mixing ratios. Generally, there are the following generic classes of TPEs (designations according to ISO 18064): Styrenic block copolymer (TPS), thermoplastic polyolefin elastomer (TPO), thermoplastic vulcanizate (TPV), thermoplastic polyurethane (TPU), thermoplastic copolyester (TPC), melt processing rubbers, and thermoplastic polyamide (TPA). The TPE may belong to one generic class or may be a blend of TPEs from two or more classes. Also, the TPE may be selected from one class and may be one kind of TPE of one class or a blend of two or more kinds of TPEs of one class.

Preferably, component (b) is a thermoplastic styrenic elastomer (TPS). TPS does not contain urethane units and is thus different from component (a). TPS has soft elastomer and a hard thermoplastic component and may be a styrenic block copolymer and preferably styrene- butadiene-styrene block copolymer (SBS) or styrene-ethylene-butene-styrene block copolymer (SEBS), i.e., polystyrene-poly(ethylene/butylene)-polystyrene.

The content of TPE as the component (b) in the cover layer may be more than 20 %. The total content of thermoplastic polymers, e.g., TPU and TPE, in the cover layer is preferably at least 80 %, more preferably at least 90 %. Preferably, the total content of polymers in the cover layer consists of thermoplastic polymers and more preferably makes up at least 80 mass%, more preferably at least 90 mass% of the total mass of the cover layer.

The cover layer may contain a compatibilizer as the component (c). The compatibilizer enables or facilitates the preparation of a homogenous blend of components (a) and (b). In the case of TPS as component (b), component (c) is preferably a copolymer containing polyurethane blocks and styrenic polymer blocks, wherein the styrenic polymer blocks may be polymers of hydrogenated styrene-diene. The total of components (a) to (c) preferably makes up at least 90 mass% of the cover layer.

Lacquer layer

The lacquer layer is an optional layer on the uppermost layer such as the cover layer of the sheet. The lacquer may be a conventional material. The thickness of the lacquer layer may preferably be 1 to 30 pm, more preferably 3 to 10 pm. The lacquer layer is applied directly on top of the uppermost layer as a finish and a protection against chemical agents, physical damage such as scratches or abrasion, and UV radiation. The lacquer layer can further reduce the surface adhesion. Conventional lacquers used for artificial leather for the interior of vehicles can be employed, such as a lacquer layer based on a silicone-containing aliphatic polyurethane. The lacquer layer usually consists of one or more, preferably up to four, transparent layers of lacquer. The lacquer layer is preferably elastic. The properties of the lacquer layer such as elasticity and translucence may be adjusted to correspond to the respective properties of the cover layer.

The lacquer layer may be an opaque layer or a translucent layer. Preferably, the lacquer layer is translucent and does not affect the translucency of the other layers of the sheet.

Manufacturing method

The sheet according to the present invention may be prepared by a first method using a two-component polyurethane system as a raw material of component (A) or by a second method using a one-component system containing component (A) in water and/or solvent.

The first method comprises (i) a step of providing a layer of a two-component polyurethane system as a raw material of component (A), (ii) a step of applying the support layer thereon, and (iii) a step of curing to obtain the intermediate layer containing component (A). Alternatively, the first method comprises (i) a step of providing the support layer, (ii) a step of applying a layer of a two-component polyurethane system as a raw material of component (A) on the support layer, e.g., by knife coating, and then said step (iii).

The second method comprises (i) a step of providing a polyurethane layer of a composition containing component (A) and water and/or solvent and at least partly removing the water and/or solvent; (ii) a step of applying the support layer on the polyurethane layer, (iii) a step of removing remaining water and/or solvent to obtain the intermediate layer. Alternatively, the second method comprises (i) a step of providing the support layer, (ii) a step of applying the polyurethane layer on the support layer, and then said step (iii).

After steps (i) to (iii), each method continues with (iv) a step of applying molten cover layer raw material containing molten component (a) onto the intermediate layer, wherein the molten cover layer raw material is preferably prepared in an extruder, and (v) a step of solidifying the cover layer raw material to obtain the sheet.

In each of the first or the second method, step (ii) is carried out such that the molten cover layer raw material and the support layer, e.g., a textile layer, only partly interpenetrate each other. To that end, the parameters such as the viscosity of the two-component or one- component polyurethane system are suitably adjusted. In a one-component system, the viscosity can be adjusted e.g. by varying the content of water and/or solvent. In a two- component system, the viscosity can be adjusted e.g. by varying the length of the prepolymers or using rheology modifying additives.

Examples

The following Table 1 describes components of exemplary layers. Table 1

Sheets of Example 1 and References 1 and 2 were prepared. The sheet of Example 1 contained a support layer, a PU intermediate layer, and a cover layer according to the present invention. The sheet of Reference 1 contained a support layer, a PVC adhesive, a PVC foam layer, and a PVC compact layer. The sheet of Reference 2 contained a support layer, a PVC adhesive, a PVC intermediate layer, and a cover layer containing thermoplastic polyurethane.

The cover layer was prepared by using a TPU material having a gel content of 3.6 %, and the PU intermediate layer was prepared by using a combination of high-solid PU having a gel content of 32.7 % and a high-solid PU having a gel content of 64.9 %.

The difference between the sheet of Example 1 and the sheet of References 1 and 2 was the composition of the layer interposed between the support layer and the cover layer, i.e., the intermediate layer. Table 2 shows the test results. Flexing tests were carried out after exposure to VDA oils. Table 2

Claims

1. A sheet comprising a support layer, an intermediate layer containing polyurethane having a gel content of at least 20 %, and a cover layer containing thermoplastic polyurethane having a gel content of less than 10 %, wherein the support layer is a textile layer and the intermediate layer is a compact layer, wherein the support layer and the intermediate layer only partly interpenetrate each other in their thickness direction to form a compound structure, wherein the thickness of the intermediate layer above the compound structure is at least 20 pm.

2. The sheet according to claim 1, wherein the intermediate layer has a thickness of more than 20 pm to 300 pm.

3. The sheet according to any of the preceding claims, wherein the support layer is a textile layer having a thickness of 200 to 1200 pm, the intermediate layer has a thickness of more than 50 pm to 300 pm, and the cover layer has a thickness of 100 to 600 pm.

4. The sheet according to any of the preceding claims, wherein the support layer has a thickness of at least 800 pm and the compound structure has a thickness of less than 40 pm.

5. The sheet according to any of the preceding claims, which does not contain polyvinylchloride and does not contain a plasticizer.

6. The sheet according to any of the preceding claims, wherein the cover layer contains a thermoplastic styrenic elastomer.

7. The sheet according to any of the preceding claims, wherein the intermediate layer and the cover layer are directly bonded to each other or at least one additional layer is arranged between the intermediate layer and the cover layer.

8. The sheet according to any of the preceding claims, wherein the polyurethane in the cover layer is aromatic.

9. The sheet according to any of the preceding claims, wherein the cover layer contains a lower sublayer and an upper sublayer, wherein the lower sublayer is directly bonded to the intermediate layer and has a hardness Shore A according to DIN 53505 of at most 70, and the upper layer has a hardness Shore A according to DIN 53505 of at least 75.

10. The sheet according to claim 9, wherein the lower sublayer and the upper sublayer differ in their hardness Shore A according to DIN 53505 by at least 10.

11. A method of preparing a sheet according to any of claims 1 to 10, comprising

(i) a step of providing a polyurethane layer of a polyurethane composition based on water and/or solvent and containing polyurethane having a gel content of at least 20 %, and at least partly removing the water and/or solvent; (ii) a step of providing a layered structure composed of the support layer and the polyurethane layer, (iii) a step of removing remaining water and/or solvent to obtain the intermediate layer; and, after either set of steps (i) to (iii) above, (iv) a step of applying molten cover layer raw material containing polyurethane having a gel content of less than 10 % onto the intermediate layer, and (v) a step of solidifying the cover layer raw material to obtain the sheet.

12. A sewn product obtainable by sewing the sheet according to any of claims 1 to 10 or a wrapped product obtainable by using the sheet according to any of claims 1 to 10 in a process of edge wrapping a substrate.

13. The use of a sheet according to any of claims 1 to 10 as an artificial leather.

14. The use of a sheet according to any of claims 1 to 10 or the sewn product or wrapped product according to claim 12 as a cover material in the interior of a vehicle.