ATE283936T1 - Verfahren zum isothermischen hartlöten von einkristallinen gegenständen - Google Patents

Verfahren zum isothermischen hartlöten von einkristallinen gegenständen

Info

Publication number
ATE283936T1
ATE283936T1 AT01111652T AT01111652T ATE283936T1 AT E283936 T1 ATE283936 T1 AT E283936T1 AT 01111652 T AT01111652 T AT 01111652T AT 01111652 T AT01111652 T AT 01111652T AT E283936 T1 ATE283936 T1 AT E283936T1
Authority
AT
Austria
Prior art keywords
gamma
base material
isothermal
single crystalline
tliqidus
Prior art date
Application number
AT01111652T
Other languages
English (en)
Inventor
Alexander Schnell
Maxim Dr Konter
John Dr Fernihough
Original Assignee
Alstom Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Alstom Technology Ltd filed Critical Alstom Technology Ltd
Application granted granted Critical
Publication of ATE283936T1 publication Critical patent/ATE283936T1/de

Links

Classifications

    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01D—NON-POSITIVE DISPLACEMENT MACHINES OR ENGINES, e.g. STEAM TURBINES
    • F01D5/00—Blades; Blade-carrying members; Heating, heat-insulating, cooling or antivibration means on the blades or the members
    • F01D5/005—Repairing methods or devices
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/24—Selection of soldering or welding materials proper
    • B23K35/30—Selection of soldering or welding materials proper with the principal constituent melting at less than 1550°C
    • B23K35/3033—Ni as the principal constituent
    • B23K35/304—Ni as the principal constituent with Cr as the next major constituent
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23P—METAL-WORKING NOT OTHERWISE PROVIDED FOR; COMBINED OPERATIONS; UNIVERSAL MACHINE TOOLS
    • B23P6/00—Restoring or reconditioning objects
    • B23P6/002—Repairing turbine components, e.g. moving or stationary blades, rotors
    • B23P6/007—Repairing turbine components, e.g. moving or stationary blades, rotors using only additive methods, e.g. build-up welding
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C19/00—Alloys based on nickel or cobalt
    • C22C19/03—Alloys based on nickel or cobalt based on nickel
    • C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C19/00—Alloys based on nickel or cobalt
    • C22C19/03—Alloys based on nickel or cobalt based on nickel
    • C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
    • C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
    • C22C19/057—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W with the maximum Cr content being less 10%
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C19/00—Alloys based on nickel or cobalt
    • C22C19/03—Alloys based on nickel or cobalt based on nickel
    • C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
    • C22C19/058—Alloys based on nickel or cobalt based on nickel with chromium without Mo and W
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • C30B29/10—Inorganic compounds or compositions
    • C30B29/52—Alloys
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B33/00—After-treatment of single crystals or homogeneous polycrystalline material with defined structure
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
    • F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
    • F05D2300/00—Materials; Properties thereof
    • F05D2300/60—Properties or characteristics given to material by treatment or manufacturing
    • F05D2300/607—Monocrystallinity
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T29/00—Metal working
    • Y10T29/49—Method of mechanical manufacture
    • Y10T29/49316—Impeller making
    • Y10T29/49318—Repairing or disassembling
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T29/00—Metal working
    • Y10T29/49—Method of mechanical manufacture
    • Y10T29/49718—Repairing
    • Y10T29/49721—Repairing with disassembling
    • Y10T29/49723—Repairing with disassembling including reconditioning of part
    • Y10T29/49725—Repairing with disassembling including reconditioning of part by shaping
    • Y10T29/49726—Removing material
    • Y10T29/49728—Removing material and by a metallurgical operation, e.g., welding, diffusion bonding, casting
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T29/00—Metal working
    • Y10T29/49—Method of mechanical manufacture
    • Y10T29/49718—Repairing
    • Y10T29/49732—Repairing by attaching repair preform, e.g., remaking, restoring, or patching
    • Y10T29/49734—Repairing by attaching repair preform, e.g., remaking, restoring, or patching and removing damaged material
    • Y10T29/49737—Metallurgically attaching preform
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T29/00—Metal working
    • Y10T29/49—Method of mechanical manufacture
    • Y10T29/49718—Repairing
    • Y10T29/49746—Repairing by applying fluent material, e.g., coating, casting

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • General Engineering & Computer Science (AREA)
  • Inorganic Chemistry (AREA)
  • Turbine Rotor Nozzle Sealing (AREA)
  • Ceramic Products (AREA)
  • Crystals, And After-Treatments Of Crystals (AREA)
  • Inorganic Compounds Of Heavy Metals (AREA)
AT01111652T 2001-05-14 2001-05-14 Verfahren zum isothermischen hartlöten von einkristallinen gegenständen ATE283936T1 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
EP01111652A EP1258545B1 (de) 2001-05-14 2001-05-14 Verfahren zum isothermischen Hartlöten von einkristallinen Gegenständen

Publications (1)

Publication Number Publication Date
ATE283936T1 true ATE283936T1 (de) 2004-12-15

Family

ID=8177415

Family Applications (1)

Application Number Title Priority Date Filing Date
AT01111652T ATE283936T1 (de) 2001-05-14 2001-05-14 Verfahren zum isothermischen hartlöten von einkristallinen gegenständen

Country Status (6)

Country Link
US (1) US6629368B2 (de)
EP (1) EP1258545B1 (de)
JP (1) JP2003049253A (de)
AT (1) ATE283936T1 (de)
CA (1) CA2385821C (de)
DE (1) DE60107541T2 (de)

Families Citing this family (50)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1160352B1 (de) 2000-05-31 2009-04-22 ALSTOM Technology Ltd Verfahren zum Einstellen der Grösse von Kühllöchern eines Bauteils einer Gasturbine
ATE283936T1 (de) * 2001-05-14 2004-12-15 Alstom Technology Ltd Verfahren zum isothermischen hartlöten von einkristallinen gegenständen
US6503349B2 (en) * 2001-05-15 2003-01-07 United Technologies Corporation Repair of single crystal nickel based superalloy article
EP1295970A1 (de) * 2001-09-22 2003-03-26 ALSTOM (Switzerland) Ltd Beschichtung aus der Legierung MCrAlY-Typ
EP1398393A1 (de) * 2002-09-16 2004-03-17 ALSTOM (Switzerland) Ltd Verfahren zur Wiederherstellung von Eigenschaften
US20080017694A1 (en) * 2003-09-24 2008-01-24 Alexander Schnell Braze Alloy And The Use Of Said Braze Alloy
US20050082348A1 (en) * 2003-10-17 2005-04-21 Maier Robert L. Method for bonding glass or metal fluoride optical materials to metal
EP1561536A1 (de) * 2004-02-03 2005-08-10 Siemens Aktiengesellschaft Reparatur-Lotverfahren zum Reparieren eines Bauteils, welches ein Basismaterial mit einer gerichteten Mikrostruktur umfasst
US7222422B2 (en) * 2004-02-16 2007-05-29 General Electric Company Method for refurbishing surfaces subjected to high compression contact
US7259350B2 (en) * 2004-08-26 2007-08-21 United Technologies Corporation Turbine component crack repair using cathodic arc and/or low pressure plasma spraying and HIP
JP2009502503A (ja) * 2005-07-22 2009-01-29 シーメンス アクチエンゲゼルシヤフト 方向性ミクロ組織の母材を有する部品の修復方法とその部品
EP1759806B1 (de) * 2005-09-06 2011-10-26 Siemens Aktiengesellschaft Verfahren zur Reparatur eines Risses mittels Hartlöten
JP4909992B2 (ja) * 2005-09-08 2012-04-04 インキュメッド・リミテッド・ライアビリティ・カンパニー チタンベースのメッシュをチタンベースの基板に接合するための方法
US7536783B2 (en) * 2005-10-13 2009-05-26 Siemens Energy, Inc. Turbine vane airfoil reconfiguration method
US8353444B2 (en) * 2005-10-28 2013-01-15 United Technologies Corporation Low temperature diffusion braze repair of single crystal components
EP1790744A1 (de) 2005-11-28 2007-05-30 Siemens Aktiengesellschaft Verfahren zum Reparieren von Rissen in Bauteilen und Lotmaterial zum Löten von Bauteilen
EP1790745A1 (de) 2005-11-28 2007-05-30 Siemens Aktiengesellschaft Verfahren zum Reparieren von Rissen in Bauteilen und Lotmaterial zum Löten von Bauteilen
US7156280B1 (en) * 2005-12-15 2007-01-02 General Electric Company Braze alloy compositions
US7731809B2 (en) * 2006-01-18 2010-06-08 Honeywell International Inc. Activated diffusion brazing alloys and repair process
DE102006026704A1 (de) * 2006-06-08 2007-12-13 Mtu Aero Engines Gmbh Verfahren zur Herstellung oder Reparatur von Turbinen- oder Triebwerksbauteilen, sowie Bauteil, nämlich Turbinen- oder Triebwerksbauteil
US8342386B2 (en) * 2006-12-15 2013-01-01 General Electric Company Braze materials and processes therefor
US20080179381A1 (en) * 2007-01-25 2008-07-31 United Technologies Corporation Diffusion braze repair of single crystal alloys
DE102007004443A1 (de) * 2007-01-26 2008-07-31 Rösler, Joachim, Prof. Dr. Lötverfahren
US7946471B2 (en) 2007-02-06 2011-05-24 Siemens Aktiengesellschaft Brazing composition and brazing method for superalloys
WO2008100336A1 (en) * 2007-02-13 2008-08-21 The Trustees Of Stevens Institute Of Technology Data hiding based messages and advertisements
US8186056B2 (en) * 2007-06-28 2012-05-29 Siemens Energy, Inc. Turbine vane restoration system
EP2053145A1 (de) * 2007-10-19 2009-04-29 Siemens Aktiengesellschaft Verfahren zur Entfernung einer metallischen Schicht mittels FIC in einem Zwischenschritt
DE102008025848A1 (de) * 2008-05-29 2009-12-03 Mtu Aero Engines Gmbh Verfahren zur Reparatur von einkristallinen Hochdruckturbinenschaufeln durch Diffusionslöten
EP2138258B1 (de) * 2008-06-23 2022-08-24 Siemens Energy Global GmbH & Co. KG Verfahren zum Löten mit mehrstufigem Temperaturprofil
JP5439041B2 (ja) * 2009-06-02 2014-03-12 三菱重工業株式会社 燃焼器構成部材の製造方法、並びに、燃焼器構成部材、ガスタービン用燃焼器及びガスタービン
US20130045129A1 (en) * 2010-04-12 2013-02-21 Michael Ott Solder alloy, soldering method and component
US9056372B2 (en) * 2010-10-12 2015-06-16 Alstom Technology Ltd Extending useful life of a cobalt-based gas turbine component
EP2679333B1 (de) 2011-02-22 2019-05-08 Mitsubishi Heavy Industries Compressor Corporation Herstellungsverfahren für ein laufrad
CH705321A1 (de) 2011-07-19 2013-01-31 Alstom Technology Ltd Lötfolie zum Hochtemperaturlöten und Verfahren zum Reparieren bzw. Herstellen von Bauteilen unter Verwendung dieser Lötfolie.
CH705327A1 (de) 2011-07-19 2013-01-31 Alstom Technology Ltd Lot zum Hochtemperaturlöten und Verfahren zum Reparieren bzw. Herstellen von Bauteilen unter Verwendung dieses Lotes.
KR101872931B1 (ko) 2011-09-30 2018-07-02 한국전력공사 단결정 초내열 합금의 재생열처리 방법
US8640942B1 (en) * 2013-03-13 2014-02-04 Siemens Energy, Inc. Repair of superalloy component
US8925792B1 (en) * 2013-06-14 2015-01-06 General Electric Company Joining process for superalloys
US9914182B2 (en) * 2015-09-17 2018-03-13 Honeywell International Inc. Methods for fabricating gas turbine engine components using a stepped transient liquid phase joining process
JP6746458B2 (ja) * 2016-10-07 2020-08-26 三菱日立パワーシステムズ株式会社 タービン翼の製造方法
EP3441180A1 (de) * 2017-08-11 2019-02-13 General Electric Company Verfahren zur reparatur von superlegierungen
RU2742963C1 (ru) * 2017-11-13 2021-02-12 Сименс Акциенгезелльшафт Способ производства трудно свариваемых материалов
CN109434233A (zh) * 2018-11-02 2019-03-08 中国航发北京航空材料研究院 一种单晶涡轮导向叶片裂纹钎焊修复前的表面清理方法
US11077512B2 (en) 2019-02-07 2021-08-03 General Electric Company Manufactured article and method
CN111408805B (zh) * 2020-03-05 2021-09-17 西安陕鼓动力股份有限公司 一种钎焊及性能热处理同炉的叶轮制造工艺方法
CN114769772B (zh) * 2022-03-29 2023-04-28 北京科技大学 一种提升gh3536/gh4738合金接头强度的真空钎焊方法
CN114769771B (zh) * 2022-03-29 2023-09-05 北京科技大学 一种减少焊缝微裂纹缺陷的镍基高温合金钎焊加工工艺
CN114799395B (zh) * 2022-03-29 2023-02-21 北京科技大学 提高接头强度稳定性的异种镍基高温合金真空钎焊方法
EP4279620A1 (de) 2022-05-20 2023-11-22 MTU Aero Engines AG Lotmischung zur anwendung in einem verfahren zum löten eines bauteils, additivlegierung, lötverfahren und bauteil
CN116638222B (zh) * 2023-06-20 2025-10-10 北京航空航天大学 一种含锆钎料及其制备方法和应用

Family Cites Families (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3155491A (en) 1961-12-26 1964-11-03 Gen Electric Brazing alloy
US4188237A (en) 1978-02-02 1980-02-12 University Of Dayton Method for cleaning metal parts with elemental fluorine
US4328044A (en) 1978-02-02 1982-05-04 University Of Dayton Method for cleaning metal parts
US4381944A (en) 1982-05-28 1983-05-03 General Electric Company Superalloy article repair method and alloy powder mixture
US4643782A (en) 1984-03-19 1987-02-17 Cannon Muskegon Corporation Single crystal alloy technology
US5071486A (en) 1986-02-06 1991-12-10 University Of Dayton Process for removing protective coatings and bonding layers from metal parts
US5156321A (en) 1990-08-28 1992-10-20 Liburdi Engineering Limited Powder metallurgy repair technique
US5437737A (en) * 1994-02-07 1995-08-01 United Technologies Corporation Repair coating for superalloy articles, such as gas turbine engine components
US5584948A (en) * 1994-09-19 1996-12-17 General Electric Company Method for reducing thermally induced porosity in a polycrystalline nickel-base superalloy article
US5666643A (en) * 1995-02-23 1997-09-09 General Electric Company High temperature braze material
DE19617093C2 (de) * 1996-04-29 2003-12-24 Alstom Paris Wärmebehandlungsverfahren für Werkstoffkörper aus Nickel-Basis-Superlegierungen
DE19624055A1 (de) 1996-06-17 1997-12-18 Abb Research Ltd Nickel-Basis-Superlegierung
US5728227A (en) 1996-06-17 1998-03-17 General Electric Company Method for removing a diffusion coating from a nickel base alloy
DE19624056A1 (de) 1996-06-17 1997-12-18 Abb Research Ltd Nickel-Basis-Superlegierung
US5743322A (en) * 1996-06-27 1998-04-28 General Electric Company Method for forming an article extension by casting using a ceramic mold
US5732467A (en) 1996-11-14 1998-03-31 General Electric Company Method of repairing directionally solidified and single crystal alloy parts
US5822852A (en) 1997-07-14 1998-10-20 General Electric Company Method for replacing blade tips of directionally solidified and single crystal turbine blades
CN1280648A (zh) * 1997-10-27 2001-01-17 西门子西屋动力公司 包括接合到超级合金基底上的薄蒙皮的涡轮机部件
AU5314898A (en) * 1997-10-30 1999-05-24 Abb Research Ltd High temperature protective coating
DE69717870T2 (de) * 1997-10-30 2003-08-21 Alstom (Switzerland) Ltd., Baden Nickelbasislegierung
EP1001055B1 (de) * 1998-11-10 2004-02-25 ALSTOM Technology Ltd Gasturbineteil
DE59904846D1 (de) * 1999-05-20 2003-05-08 Alstom Switzerland Ltd Nickel-Basis-Superlegierung
JP4201954B2 (ja) * 2000-03-28 2008-12-24 株式会社東芝 Ｎｉ基単結晶超合金からなるガスタービン翼の補修方法およびその装置
US6193141B1 (en) * 2000-04-25 2001-02-27 Siemens Westinghouse Power Corporation Single crystal turbine components made using a moving zone transient liquid phase bonded sandwich construction
US6508000B2 (en) * 2001-02-08 2003-01-21 Siemens Westinghouse Power Corporation Transient liquid phase bonding repair for advanced turbine blades and vanes
ATE283936T1 (de) * 2001-05-14 2004-12-15 Alstom Technology Ltd Verfahren zum isothermischen hartlöten von einkristallinen gegenständen
US6503349B2 (en) * 2001-05-15 2003-01-07 United Technologies Corporation Repair of single crystal nickel based superalloy article

Also Published As

Publication number Publication date
DE60107541T2 (de) 2005-12-08
EP1258545A1 (de) 2002-11-20
CA2385821A1 (en) 2002-11-14
US6629368B2 (en) 2003-10-07
JP2003049253A (ja) 2003-02-21
CA2385821C (en) 2010-12-21
DE60107541D1 (de) 2005-01-05
EP1258545B1 (de) 2004-12-01
US20030066177A1 (en) 2003-04-10

Similar Documents

Publication Publication Date Title
DE60107541D1 (de) Verfahren zum isothermischen Hartlöten von einkristallinen Gegenständen
Bürgel et al. Recrystallization in single crystals of nickel base superalloys
DE50010577D1 (de) Verfahren und vorrichtung zur herstellung einer lotverbindung
CA2399210A1 (en) Welding superalloy articles
DE10191096T1 (de) Temperaturkompensierter Kristalloszillator und Verfahren zum Kompensieren der Temperatur desselben
DE60217196D1 (de) Nickel-Basis-Hartlötmaterial und Verfahren zum Reparieren durch Hartlöten
DE69428242D1 (de) Aluminiumlegierung zum Hartlöten; Folie zum Hartlöten von Wärmetauschern und Verfahren zur Herstellung von Wärmetauschern
DE3868060D1 (de) Rasch erstarrte silizium enthaltende aluminiumlegierungen zur verwendung bei hoeheren temperaturen.
DE50211098D1 (de) Superelastisches bauelement aus einer kupferlegierung und verfahren zum einprägen und konservieren einer krümmung vorgegebener geometrie
DK0946232T4 (da) Krystallisationsfremgangsmåde
DE602004007628D1 (de) Verfahren zum straggiessen
SE9004081D0 (sv) Saett att tillverka vaermeoeverfoeringsorgan samt verktyg foer att genomfoera saettet
MX9400159A (es) Metodo para la preparacion de amidas.
SE0401597L (sv) Stödlister för borrhuvuden
ATE389039T1 (de) Verfahren zum abkühlen von schmelzflüssigem metall bei der fraktionierten kristallisation
EP1072354A3 (de) Turbinenschaufel und Verfahren zu deren Herstellung
BR0005933A (pt) Superfìcie de artigo com fios de metal e método para fabricação
DE69828662D1 (de) Hartlotwerkstoff und Verfahren zum Hartlöten bei niedriger Temperatur
DE60303144D1 (de) Verfahren zur fraktionierten kristallisation eines metalls
ATE397503T1 (de) Verfahren und vorrichtung zum aufbereiten einer schmelze einer legierung für einen giessvorgang
DE60016413D1 (de) Verfahren zum löten mit bleifreiem lötmaterial
US4339867A (en) Method for fixturing workpieces for heat effected joining of same
JPS5647212A (en) Processing method for brazing alloy
ATE158736T1 (de) Löten
ATE297893T1 (de) Verfahren zur herstellung von pyrrolidonen

Legal Events

Date Code Title Description
RER Ceased as to paragraph 5 lit. 3 law introducing patent treaties