CN101638822A - Union yarn of terylene fibers, viscose fibers and bamboo fibers, and production method thereof - Google Patents
Union yarn of terylene fibers, viscose fibers and bamboo fibers, and production method thereof Download PDFInfo
- Publication number
- CN101638822A CN101638822A CN200910184111A CN200910184111A CN101638822A CN 101638822 A CN101638822 A CN 101638822A CN 200910184111 A CN200910184111 A CN 200910184111A CN 200910184111 A CN200910184111 A CN 200910184111A CN 101638822 A CN101638822 A CN 101638822A
- Authority
- CN
- China
- Prior art keywords
- fibers
- viscose
- terylene
- bamboo
- blended yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a union yarn of terylene fibers, viscose fibers and bamboo fibers, and a production method thereof. The union yarn comprises the following components by mass percentage: 78-85%of terylene fibers, 5-15% of viscose fibers and 5-15% of bamboo fibers. Since the union yarn of terylene fibers, viscose fibers and bamboo fibers fully combines the favorable properties of terylene fibers, viscose fibers and bamboo fibers, the respective defects are eliminated. The fabrics made of the union yarn have the advantages of high acid resistance, alkaline resistance, strength, heat resistance, elasticity, wrinkling resistance, wear resistance, hydroscopic property, ventilation property and dyeing property and can resist bacteria, prevent bacteria and resist ultraviolet radiation.
Description
Technical field
The present invention relates to a kind of blended yarn and production method thereof, specifically, relate to a kind of terylene, viscose glue and bamboo fiber blended yarn and production method thereof, belong to the spinning engineering field.
Background technology
Polyster fibre, viscose and bamboo fibre all belong to common spinning material, and their characteristic is as follows respectively.
Polyster fibre: (1) is acidproof not alkaline-resisting; (2) intensity is big: high nearly 1 times of the strength ratio cotton of polyster fibre, and higher 3 times than wool, so dacron is durable; (3) good heat resistance: can be 70～170 ℃ of uses, be that heat resistance and heat endurance are best in the synthetic fiber; (4) good springiness, crease resistance are good: the elasticity of terylene is near wool, and crease resistance surpasses other fibers, and fabric does not wrinkle, and conformality is good; (5) ABRASION RESISTANCE is good: the ABRASION RESISTANCE of terylene is only second to polyamide fibre, occupies second in synthetic fiber.(6) hygroscopicity is low, gas permeability is poor, dyeability is poor: the terylene structure is tight, the degree of crystallinity height, and inner big molecule does not have the hydrophily gene, so wettability power is low, the dyeing difficulty.Terylene regain under the general atmosphere condition has only 0.4%.
Viscose: (1) is alkaline-resisting and not acidproof; (2) intensity is little: the viscose brute force is lower, the about 1.6～2.7cN/tex of fracture strength, and the ratio of elongation cotton fiber of viscose is big, and extension at break splits about 10%～24%.Particularly the wet strength of viscose is lower, only is about 50% of dry strength; (3) good heat resistance, light resistance are good; (4) poor flexibility, crease resistance are poor: and viscose elasticity is relatively poor.So SPUN RAYON FABRIC is not water-fast washes, fabric is not well-pressed, wrinkle resistance is poor, but quality softness; (5) wear no resistance; (6) good hygroscopicity, dyeability are good: viscose is a cellulose fibre, and its big molecules align is not tight, so it has hygroscopicity preferably, regain reaches about 13% under the general atmosphere condition;
Bamboo fibre: (1) is acid and alkali-resistance not; (2) intensity is big: (3) good heat resistance: the heat resistance of bamboo fibre is better than common viscose fiber; (4) good springiness, crease resistance are good: (5) ABRASION RESISTANCE is good; (6) good hygroscopicity, good permeability, dyeability are good: bamboo fibre belongs to regenerated celulose fibre, and its structure is a porous crack network structure, and its hygroscopicity gas permeability is better than other viscose, gives a kind of perspire feel cool of people.Bamboo fibre has porous crack network structure, can be in water instantaneous swollen, make REACTIVE DYES this water-soluble fabulous and dyestuff that molecule is less can be adsorbed in bamboo fibre rapidly, and can in bamboo fibre, spread rapidly, the rate of just dying is higher, and time of half dyeing is shorter, therefore, the bamboo fibre chromaticity of reactive dye is good, and its balance dye uptake is higher, and time of half dyeing is short, bright in colour, good level-dyeing property, the degree of fixation height, fastness is good.In addition, bamboo fibre also has the performance of the not available natural antibacterial bacteriostatic antiultraviolet of other fibers.
More than three kinds of fibers all have separately merits and demerits, its fabric of making that spins separately also has corresponding advantages and shortcoming, so cause Application Areas narrow, relevant blended yarn and production method thereof is not arranged as yet at present, its advantage is concentrated, and elimination shortcoming separately.
Summary of the invention
The purpose of this invention is to provide a kind of new terylene, viscose glue and bamboo fiber blended yarn, make it to have terylene, the overall merit of viscose glue and bamboo fibre, eliminate their shortcomings separately simultaneously.
Terylene of the present invention, viscose glue and bamboo fiber blended yarn comprise following component according to mass percent: polyster fibre 75-85%, viscose 5-15%, bamboo fibre 5-15%.
Preferably, terylene of the present invention, viscose glue and bamboo fiber blended yarn comprise following component according to mass percent: polyster fibre 80%, viscose 10%, bamboo fibre 10%.
The specification of said polyster fibre is 1.4D * 38mm, and the specification of viscose is 2D * 51mm, and the specification of bamboo fibre is 5D * 51mm.
The production method of terylene of the present invention, viscose glue and bamboo viscose fiber blended yarn may further comprise the steps:
(1) blowing: three kinds of raw materials mixed are made volume by scutcher;
(2) comb and parallel cotton fibers prior to spinning: will roll up by carding machine and to make the carded sliver respectively;
(3) drafting: the carded sliver is merged ripe bar by drawing frame;
(4) rove: ripe the drawing-off that will merge by Speed frames attenuates and becomes the rove bar;
(5) spun yarn: by fine spining machine is the yarn of certain number with roving-drafting;
(6) winder: by bobbin winder with spinning volume cheese coning;
(7) the packing finished product blended yarn of weighing.
The product parameters of blended yarn of the present invention is as shown in table 1:
Table 1
| Project | Technical parameter | Project | Technical parameter |
| Yarn count | ??20 | Tekes | ??29.5 |
| Single twist multiplier | ??280 | The twist (individual/1M) | ??520 |
| Single thread force | ??810CN | Bar is done CV% | ??12.5％ |
| ??-50％ | ??0 | ??+50％ | ??10 |
| ??+200％ | ??5 | Rove CV% | ??5.2 |
| Drafting CV% | ??2.9 | Comb and parallel cotton fibers prior to spinning CV% | ??5.2 |
Terylene of the present invention, viscose glue and bamboo fiber blended yarn are because terylene, viscose glue and the bamboo fibre good characteristic of fully having mixed, eliminated self-defect separately, therefore the fabric made from blended yarn of the present invention has good acid-fast alkali-proof, intensity, heat resistance, elasticity, crease resistance, ABRASION RESISTANCE, hygroscopicity, gas permeability and dyeability, can also the antibacterial bacteriostatic antiultraviolet, specifically:
(1) owing to contains the polyster fibre component, therefore the fabric made from blended yarn of the present invention has good acid resistance, intensity, heat resistance, elasticity, crease resistance, ABRASION RESISTANCE, the shortcoming that overcome that viscose is not acidproof, intensity is little, poor flexibility, crease resistance are poor, wears no resistance has overcome the not acid proof shortcoming of bamboo fibre;
(2) owing to contain the viscose component, therefore the fabric made from blended yarn of the present invention has good alkali resistance, heat resistance, hygroscopicity and dyeability, overcome that polyster fibre is not alkaline-resisting, hygroscopicity is low, the shortcoming of dyeability difference, also overcome the not alkaline-resisting shortcoming of bamboo fibre;
(3) owing to contain the bamboo fibre component, therefore the fabric made from blended yarn of the present invention has good intensity, heat resistance, elasticity, crease resistance, ABRASION RESISTANCE, hygroscopicity, gas permeability and dyeability, overcome that the polyster fibre hygroscopicity is low, gas permeability is poor, the shortcoming of dyeability difference, overcome the shortcoming that viscose intensity is little, elasticity weak, crease resistance is poor, wear no resistance, also increased the advantage of antibacterial bacteriostatic anti-uv for blended yarn of the present invention.
Owing to have above advantage, the textile applications that blended yarn of the present invention is made is very extensive, can be applied to following field:
(1) woven weaving face fabric: characteristic such as can utilize blended yarn rigidity height of the present invention, ABRASION RESISTANCE is good, color and luster is beautiful, develop the good fabric of some stiffness drapability;
(2) sweater knitted underwear: can utilize blended yarn of the present invention to have natural antibacterial biocidal property, hygroscopicity, gas permeability, develop all kinds of large circle machines, straight-bar machines, rib knitting machine product;
(3) medical sanitary product: because blended yarn of the present invention has the natural antibacterial biocidal property, but the nurse of production hospital clothes, operation dress, mouth mask, gauze, bandage, patient's bed quilts etc. can effectively prevent the propagation of germ;
(4) decoration, daily product: because the various characteristics of blended yarn of the present invention can also be produced various adornments, as carpet, summer sleeping mat, toy, towel, bath towel, sheet, quilt cover, curtain, seat cushions etc.
The specific embodiment
The present invention is further illustrated below in conjunction with embodiment, but the scope of protection of present invention is not limited to the scope that embodiment represents.
Embodiment 1
In the present embodiment, the raw material of terylene, viscose glue and bamboo fiber blended yarn composition and production method step are as follows:
1, raw material and percentage by weight:
Polyster fibre 1.4D * 38mm, percentage by weight 80%
Viscose 2D * 51mm, percentage by weight 10%
Bamboo fibre 5D * 51mm, percentage by weight 10%
2, production method:
(1) blowing: three kinds of raw materials mixed are made volume by scutcher;
(2) comb and parallel cotton fibers prior to spinning: will roll up by carding machine and to make the carded sliver respectively;
(3) drafting: the carded sliver is merged ripe bar by drawing frame;
(4) rove: ripe the drawing-off that will merge by Speed frames attenuates and becomes the rove bar;
(5) spun yarn: by fine spining machine is the yarn of certain number with roving-drafting;
(6) winder: by bobbin winder with spinning volume cheese coning;
(7) the packing finished product blended yarn of weighing.
3, become yarn count: 29.5tex (20S).
Embodiment 2
In the present embodiment, the raw material of terylene, viscose glue and bamboo fiber blended yarn composition and production method step are as follows:
1, raw material and percentage by weight:
Polyster fibre 1.4D * 38mm, percentage by weight 75%
Viscose 2D * 51mm, percentage by weight 15%
Bamboo fibre 5D * 51mm, percentage by weight 10%
2, method: identical with embodiment 1
3, become yarn count: 29.5tex (20S).
Embodiment 3
In the present embodiment, the raw material of terylene, viscose glue and bamboo fiber blended yarn composition and production method step are as follows:
1, raw material and percentage by weight:
Polyster fibre 1.4D * 38mm, percentage by weight 85%
Viscose 2D * 51mm, percentage by weight 10%
Bamboo fibre 5D * 51mm, percentage by weight 5%
2, method: identical with embodiment 1
3, become yarn count: 29.5tex (20S).
Embodiment 4
In the present embodiment, the raw material of terylene, viscose glue and bamboo fiber blended yarn composition and production method step are as follows:
1, raw material and percentage by weight:
Polyster fibre 1.4D * 38mm, percentage by weight 80%
Viscose 2D * 51mm, percentage by weight 5%
Bamboo fibre 5D * 51mm, percentage by weight 15%
2, method: identical with embodiment 1
3, become yarn count: 29.5tex (20S).
Claims (4)
1, terylene, viscose glue and bamboo fiber blended yarn is characterized in that, comprise following component according to mass percent: polyster fibre 75-85%, viscose 5-15%, bamboo fibre 5-15%.
2, terylene according to claim 1, viscose glue and bamboo fiber blended yarn is characterized in that, comprise following component according to mass percent: polyster fibre 80%, viscose 10%, bamboo fibre 10%.
3, terylene according to claim 2, viscose glue and bamboo fiber blended yarn is characterized in that, the specification of said polyster fibre is 1.4D * 38mm, and the specification of viscose is 2D * 51mm, and the specification of bamboo fibre is 5D * 51mm.
4, according to the production method of claim 1 or 2 or 3 described terylene, viscose glue and bamboo fiber blended yarn, it is characterized in that, may further comprise the steps:
(1) blowing: three kinds of raw materials mixed are made volume by scutcher;
(2) comb and parallel cotton fibers prior to spinning: will roll up by carding machine and to make the carded sliver respectively;
(3) drafting: the carded sliver is merged ripe bar by drawing frame;
(4) rove: ripe the drawing-off that will merge by Speed frames attenuates and becomes the rove bar;
(5) spun yarn: by fine spining machine is the yarn of certain number with roving-drafting;
(6) winder: by bobbin winder with spinning volume cheese coning;
(7) the packing finished product blended yarn of weighing.