CN103614024A - Organism-resistant waterproof coating - Google Patents
Organism-resistant waterproof coating Download PDFInfo
- Publication number
- CN103614024A CN103614024A CN201310517161.3A CN201310517161A CN103614024A CN 103614024 A CN103614024 A CN 103614024A CN 201310517161 A CN201310517161 A CN 201310517161A CN 103614024 A CN103614024 A CN 103614024A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof coating
- raw material
- add
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an organism-resistant waterproof coating. The organism-resistant waterproof coating comprises, by weight, 70-80 parts of an aqueous acrylic emulsion, 1-2 parts of dipropylene glycol, 1-2 parts of sebacic acid, 1-2 parts of monoethanolamine, 1-2 parts of sodium nitrate, 2-3 parts of dimethyl methyl phosphonate, 1-2 parts of tourmalinite powder, 1-2 parts of lithium carbonate, 1-2 parts of copper oxide, 1-2 parts of zinc oxide, 15-20 parts of vermiculite powder, 0.6-1 part of Pesticide Emulsifier No.600, 6-10 parts of a bonding assistant and 5-20 parts of deionized water. The waterproof coating has a good bacterium resistance, and can prevent the attachment of marine organisms, such as shellfishes and algae, so the coating is suitable for sea ports or near water materials, has a good waterproof property and a strong organism resistance.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of antibiotic waterproof coating.
Background technology
Brushing, on building surface, forms thin film through the volatilization of solvent or moisture or the chemical reaction of two kinds of components, makes building surface and water isolated, thereby plays the effect of waterproof, sealing, and the thick liquid of these brushings is called waterproof paint.The waterproofing membrane that waterproof paint forms after solidifying has certain extensibility, elastoplasticity, splitting resistance, impermeability and weathering resistance, can play waterproof, prevent blending provide protection.Waterproof paint has good thermal adaptability, easy and simple to handle, for ease of maintenaince with maintenance.
Summary of the invention
The object of the invention is just to provide a kind of antibiotic waterproof coating.
The present invention is achieved by the following technical solutions:
An antibiotic waterproof coating, it is comprised of the raw material of following weight parts:
Aqueous acrylic emulsion 70-80, dipropylene glycol 1-2, SA 1-2, monoethanolamine 1-2, SODIUMNITRATE 1-2, dimethyl methyl phosphonate 2-3, tourmaline powder 1-2, Quilonum Retard 1-2, cupric oxide 1-2, zinc oxide 1-2, vermiculite power 15-20, styroyl phenol polyethenoxy ether 0.6-1, adhesive aid 6-10, deionized water 5-20;
Described adhesive aid is comprised of the raw material of following weight parts:
Eva emulsion 40-45, aluminum isopropylate 3-5, polyamide wax micropowder 3-4, silane resin acceptor kh-550 1-2, stearic acid direactive glyceride 2-4, urea 2-3, nano-sized carbon 0.1-1;
Above-mentioned aluminum isopropylate is heated to 130-135 ℃, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, stirring reaction 10-15 minute at 100-120 ℃, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 200-300 rev/min of dispersed with stirring 3-4 minute, mixes with particle obtained above and each raw material of residue, fully ball milling, obtains described adhesive aid.
A preparation method for antibiotic waterproof coating, comprises the following steps:
Above-mentioned cupric oxide, zinc oxide, vermiculite power are mixed, the deionized water that adds dipropylene glycol and above-mentioned weight 50-60%, 200-300 rev/min of dispersed with stirring 4-6 minute, add adhesive aid, fully mix and add each raw material of residue, high-speed stirring, to mixing, obtains described antibiotic waterproof coating.
Advantage of the present invention is:
Waterproof paint bacteria resistance of the present invention is good, can stop marine organisms as shellfish, algae adhere to, and therefore goes for harbour or nearly water material, good waterproof performance, and biological resistance is strong.
Embodiment
Embodiment 1
An antibiotic waterproof coating, it by following weight parts (kilogram) raw material form:
Aqueous acrylic emulsion 80, dipropylene glycol 2, SA 2, monoethanolamine 2, SODIUMNITRATE 1, dimethyl methyl phosphonate 2, tourmaline powder 2, Quilonum Retard 2, cupric oxide 1, zinc oxide 1, vermiculite power 20, styroyl phenol polyethenoxy ether 0.6, adhesive aid 6-10, deionized water 5-20;
Described adhesive aid is comprised of the raw material of following weight parts:
Eva emulsion 45, aluminum isopropylate 5, polyamide wax micropowder 4, silane resin acceptor kh-550 1, stearic acid direactive glyceride 2-4, urea 2, nano-sized carbon 0.1;
Above-mentioned aluminum isopropylate is heated to 135 ℃, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, at 120 ℃, stirring reaction is 15 minutes, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 300 revs/min of dispersed with stirring 4 minutes, mix with particle obtained above and each raw material of residue, fully ball milling, obtains described adhesive aid.
A preparation method for antibiotic waterproof coating, comprises the following steps:
Above-mentioned cupric oxide, zinc oxide, vermiculite power are mixed, add the deionized water of dipropylene glycol and above-mentioned weight 60%, 300 revs/min of dispersed with stirring 6 minutes, add adhesive aid, fully mix and add each raw material of residue, high-speed stirring, to mixing, obtains described antibiotic waterproof coating.
Performance test:
Tensile strength: >=1.5MPa;
Unit elongation: >=300%;
Not saturating: 0.3MPa (hour waterproof).
Claims (2)
1. an antibiotic waterproof coating, is characterized in that what it was comprised of the raw material of following weight parts:
Aqueous acrylic emulsion 70-80, dipropylene glycol 1-2, SA 1-2, monoethanolamine 1-2, SODIUMNITRATE 1-2, dimethyl methyl phosphonate 2-3, tourmaline powder 1-2, Quilonum Retard 1-2, cupric oxide 1-2, zinc oxide 1-2, vermiculite power 15-20, styroyl phenol polyethenoxy ether 0.6-1, adhesive aid 6-10, deionized water 5-20;
Described adhesive aid is comprised of the raw material of following weight parts:
Eva emulsion 40-45, aluminum isopropylate 3-5, polyamide wax micropowder 3-4, silane resin acceptor kh-550 1-2, stearic acid direactive glyceride 2-4, urea 2-3, nano-sized carbon 0.1-1;
Above-mentioned aluminum isopropylate is heated to 130-135 ℃, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, stirring reaction 10-15 minute at 100-120 ℃, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 200-300 rev/min of dispersed with stirring 3-4 minute, mixes with particle obtained above and each raw material of residue, fully ball milling, obtains described adhesive aid.
2. a preparation method for antibiotic waterproof coating as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned cupric oxide, zinc oxide, vermiculite power are mixed, the deionized water that adds dipropylene glycol and above-mentioned weight 50-60%, 200-300 rev/min of dispersed with stirring 4-6 minute, add adhesive aid, fully mix and add each raw material of residue, high-speed stirring, to mixing, obtains described antibiotic waterproof coating.