CN104194574B - A kind of high fire-retardance high adhesion paint - Google Patents
A kind of high fire-retardance high adhesion paint Download PDFInfo
- Publication number
- CN104194574B CN104194574B CN201410510017.1A CN201410510017A CN104194574B CN 104194574 B CN104194574 B CN 104194574B CN 201410510017 A CN201410510017 A CN 201410510017A CN 104194574 B CN104194574 B CN 104194574B
- Authority
- CN
- China
- Prior art keywords
- parts
- retardance
- adhesion paint
- fire
- high adhesion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
nullThe invention discloses a kind of high fire-retardance high adhesion paint，Its raw material includes by weight: epoxy resin 83 86 parts，Terpene resin 35 38 parts，10 13 parts of phenolic resin，Sodium carboxymethylcellulose 2.2 2.5 parts，Sodium tripolyphosphate 3.5 3.8 parts，Cithrol 2.6 2.9 parts，Aluminum-zirconium coupling agent TL 41.2 1.5 parts，Precipitated calcium carbonate 27 30 parts，Nano-attapulgite 13 16 parts，Aerosil 14 17 parts，Mica powder 10 13 parts，Bisphenol-A double (diphenyl phosphoester) 34 parts，Guanidine Sulfamate 99 16 19 parts，1.5 hydrate zinc borates 25 28 parts，Toughener 5.2 5.6 parts，1.2 1.5 parts of curing agent，Defoamer 1.5 1.8 parts，Levelling agent 1.6 1.9 parts，Mould inhibitor 1 1.3 parts，Pigment 2.2 2.5 parts，Solvent 65 70 parts.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of high fire-retardance high adhesion paint.
Background technology
In recent years, due to a large amount of uses of ornament materials, this fire is in rising trend.Prepare novel not
Combustion, difficult combustion ornament materials, paid much attention to by national departments concerned.Therefore anti-flaming dope becomes research
Focus, but existing anti-flaming dope remains some shortcomings, by the catalysis carbon-forming effect of film with reality
Now fire-retardant to base material prior art, the dehydration catalyst decomposition temperature of employing is higher and low temperature active is poor, is coated with
The fire resistance of material is not good enough.During because fire occurs, film forming matter is often thermally decomposed prior to dehydration catalyst,
Produce more flammable VOC, affect formation and the structure of layer of charcoal, and then impact is to base
The protective effect of material.
Summary of the invention
The technical problem that basic background technology exists, the present invention proposes a kind of high fire-retardance high adhesion paint,
There is heat-proof combustion-resistant performance and the adhesive force of excellence, and corrosion-resistant and anti-thixotroping ability is outstanding.
A kind of high fire-retardance high adhesion paint that the present invention proposes, its raw material includes by weight:
Preferably, the weight ratio of epoxy resin, terpene resin and phenolic resin is 84-85:36-37:11-12.
Preferably, in terms of ring and ball method, the softening point of terpene resin is 85-100 DEG C.
Preferably, its raw material includes by weight:
The present invention as major ingredient, makes the present invention have with Blending Modification of Epoxy Resin using terpene resin, phenolic resin
There are the adhesive force of excellence, water-fast, oil resistant, weather-proof and heat-proof combustion-resistant performance, also improve heat-resisting, light resistance
Energy；Precipitated calcium carbonate, nano-attapulgite, aerosil, mica powder and 1.5 hydrate zinc borates add
In major ingredient and solvent, by sodium tripolyphosphate, the auxiliary of cithrol, can be uniformly dispersed in
Between major ingredient molecule, then make each component compatibility of raw material good by aluminum-zirconium coupling agent TL-4, this is greatly improved
The performance high temperature resistant, corrosion resistant of invention and anti-thixotroping ability；And bisphenol-A-bis-(diphenyl phosphoesters), ammonia
Base sulfonic acid guanidine, 1.5 hydrate zinc borates cooperatively form flame-retardant system, and wherein Guanidine Sulfamate 99 is as nitrogenated flame retardant,
Bisphenol-A-bis-(diphenyl phosphoester) is as phosphorus flame retardant, and the two coordinates the oxygen that the present invention is greatly improved to refer to
Number, improves the fire resistance of the present invention, and 1.5 hydrate zinc borates decomposable asymmetric choice net during burning produces water,
The smog in combustion process can be suppressed to be formed.
Detailed description of the invention
Below, by specific embodiment, technical scheme is described in detail.
Embodiment 1
A kind of high fire-retardance high adhesion paint that the present invention proposes, its raw material includes by weight:
Wherein the softening point (in terms of ring and ball method) of terpene resin is 95 DEG C.
Embodiment 2
A kind of high fire-retardance high adhesion paint that the present invention proposes, its raw material includes by weight:
Wherein the softening point (in terms of ring and ball method) of terpene resin is 90 DEG C.
Embodiment 3
A kind of high fire-retardance high adhesion paint that the present invention proposes, its raw material includes by weight:
Wherein the softening point (in terms of ring and ball method) of terpene resin is 85 DEG C.
Embodiment 4
A kind of high fire-retardance high adhesion paint that the present invention proposes, its raw material includes by weight:
Wherein the softening point (in terms of ring and ball method) of terpene resin is 100 DEG C.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention not office
Being limited to this, any those familiar with the art is in the technical scope that the invention discloses, according to this
The technical scheme of invention and inventive concept thereof in addition equivalent or change, all should contain the protection in the present invention
Within the scope of.
Claims (4)
1. a high fire-retardance high adhesion paint, it is characterised in that its raw material includes by weight:
High fire-retardance high adhesion paint the most according to claim 1, it is characterised in that epoxy resin, terpene
The weight ratio of olefine resin and phenolic resin is 84-85:36-37:11-12.
High fire-retardance high adhesion paint the most according to claim 1 or claim 2, it is characterised in that with ring and ball method
Meter, the softening point of terpene resin is 85-100 DEG C.
High fire-retardance high adhesion paint the most according to claim 1 or claim 2, it is characterised in that its raw material is pressed
Weight portion includes: