CN106221663A - 大理石能量固化胶、表面处理保护材料及其制备方法 - Google Patents
大理石能量固化胶、表面处理保护材料及其制备方法 Download PDFInfo
- Publication number
- CN106221663A CN106221663A CN201610774533.4A CN201610774533A CN106221663A CN 106221663 A CN106221663 A CN 106221663A CN 201610774533 A CN201610774533 A CN 201610774533A CN 106221663 A CN106221663 A CN 106221663A
- Authority
- CN
- China
- Prior art keywords
- marble
- energy
- poly
- curable glue
- surface process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
大理石能量固化胶、表面处理保护材料及其制备方法，它涉及建筑材料技术领域；它由如下重量份数的原料组成：已二醇二丙烯酸酯10%‑50%、二缩三丙二醇二丙烯酸酯10%‑50%、三羟甲基丙烷三丙烯酸酯10%‑50%、三甲基苯甲酰基二苯基氧化膦1%‑5%、羟基环已基甲酮10%‑50%、光引发剂10%‑50%、高官聚氨酷丙烯酸酯10%‑50%、脂肪族聚酯型10%‑50%、改性烯酸酯类聚合物消泡剂10%‑50%、氟改牲聚硅氧烷聚合物10%‑50%。本发明提高了施工效率，提高石材的密度、光泽度以及表面保护性能，达到防水、防污、耐腐蚀的目的。
Description
技术领域
本发明涉及建筑材料技术领域，具体涉及大理石能量固化胶、表面处理保护材料及其制备方法。
背景技术
现在石材行业均采用树脂及其改性产品、属自干或热干型及仍使用部分不环保的辅助原料及其制备方法。
发明内容
本发明的目的在于针对现有技术的缺陷和不足，提供一种环保型的、能提高石材的密度、光泽度以及表面保护性能、达到防水、防污、耐腐蚀的目的的大理石能量固化胶、表面处理保护材料及其制备方法。
为实现上述目的，本发明采用的技术方案是：大理石能量固化胶及表面处理保护材料，它由如下重量份数的原料组成：已二醇二丙烯酸酯10% - 50%、二缩三丙二醇二丙烯酸酯10% - 50%、三羟甲基丙烷三丙烯酸酯10% - 50%、三甲基苯甲酰基二苯基氧化膦1% -5%、羟基环已基甲酮10% - 50%、光引发剂10% - 50%、高官聚氨酷丙烯酸酯10% - 50%、脂肪族聚酯型10% - 50%、改性烯酸酯类聚合物消泡剂10% - 50%、氟改牲聚硅氧烷聚合物10% -50%。
大理石能量固化胶、表面处理保护材料的制备方法，它包含如下步骤：
1、按已二醇二丙烯酸酯10% - 50%、二缩三丙二醇二丙烯酸酯10% - 50%、三羟甲基丙烷三丙烯酸酯10% - 50%、三甲基苯甲酰基二苯基氧化膦1% - 5%、羟基环已基甲酮10% -50%、光引发剂10% - 50%、高官聚氨酷丙烯酸酯10% - 50%、脂肪族聚酯型10% - 50%、改性烯酸酯类聚合物消泡剂10% - 50%、氟改牲聚硅氧烷聚合物10% - 50%进行备料；将上述组分的已二醇二丙烯酸酯、二缩三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯混合在一起搅拌1-10分钟；
2、往上述步骤1所得的溶液加入高官聚氨酷丙烯酸酯、脂肪族聚酯型混合在一起搅拌5-20分钟；
3、最后加入光引发剂、羟基环已基甲酮、改性烯酸酯类聚合物消泡剂、氟改牲聚硅氧烷聚合物混合在一起搅拌2-10分钟，即成。
进一步地，上述所有步骤的操作温度在20-50度之间。
本发明产生的有益效果为：本发明所述的大理石能量固化胶、表面处理保护材料及其制备方法，环保，提高了施工效率，提高石材的密度、光泽度以及表面保护性能，达到防水、防污、耐腐蚀的目的，直接降低生产成本及节省多项间接成本。
具体实施方式
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对上述技术方案进行详细的说明。
实施例1
大理石能量固化胶、表面处理保护材料的制备方法，它包含如下步骤：
1、按已二醇二丙烯酸酯15%、二缩三丙二醇二丙烯酸酯12%、三羟甲基丙烷三丙烯酸酯10%、三甲基苯甲酰基二苯基氧化膦3%、羟基环已基甲酮10%、光引发剂10%、高官聚氨酷丙烯酸酯10%、脂肪族聚酯型10%、改性烯酸酯类聚合物消泡剂10%、氟改牲聚硅氧烷聚合物10%进行备料；将上述组分的已二醇二丙烯酸酯、二缩三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯混合在一起搅拌5分钟；
2、往上述步骤1所得的溶液加入高官聚氨酷丙烯酸酯、脂肪族聚酯型混合在一起搅拌10分钟；
3、最后加入光引发剂、羟基环已基甲酮、改性烯酸酯类聚合物消泡剂、氟改牲聚硅氧烷聚合物混合在一起搅拌5分钟，即成。
本实施例中，上述所有步骤的操作温度为20-50摄氏度。
实施例2
大理石能量固化胶、表面处理保护材料的制备方法，它包含如下步骤：
1、按已二醇二丙烯酸酯11%、二缩三丙二醇二丙烯酸酯11%、三羟甲基丙烷三丙烯酸酯12%、三甲基苯甲酰基二苯基氧化膦2%、羟基环已基甲酮11%、光引发剂11%、高官聚氨酷丙烯酸酯11%、脂肪族聚酯型11%、改性烯酸酯类聚合物消泡剂10%、氟改牲聚硅氧烷聚合物10%进行备料；将上述组分的已二醇二丙烯酸酯、二缩三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯混合在一起搅拌8分钟；
2、往上述步骤1所得的溶液加入高官聚氨酷丙烯酸酯、脂肪族聚酯型混合在一起搅拌15分钟；
3、最后加入光引发剂、羟基环已基甲酮、改性烯酸酯类聚合物消泡剂、氟改牲聚硅氧烷聚合物混合在一起搅拌8分钟，即成。
本实施例中，上述所有步骤的操作温度为20-50摄氏度。
实施例3
大理石能量固化胶、表面处理保护材料的制备方法，它包含如下步骤：
1、按已二醇二丙烯酸酯10%、二缩三丙二醇二丙烯酸酯10%、三羟甲基丙烷三丙烯酸酯11%、三甲基苯甲酰基二苯基氧化膦3%、羟基环已基甲酮11%、光引发剂11%、高官聚氨酷丙烯酸酯11%、脂肪族聚酯型11%、改性烯酸酯类聚合物消泡剂11%、氟改牲聚硅氧烷聚合物11%进行备料；将上述组分的已二醇二丙烯酸酯、二缩三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯混合在一起搅拌10分钟；
2、往上述步骤1所得的溶液加入高官聚氨酷丙烯酸酯、脂肪族聚酯型混合在一起搅拌20分钟；
3、最后加入光引发剂、羟基环已基甲酮、改性烯酸酯类聚合物消泡剂、氟改牲聚硅氧烷聚合物混合在一起搅拌10分钟，即成。
本实施例中，上述所有步骤的操作温度为20-50摄氏度。
本具体实施方式产生的有益效果为：本具体实施方式所述的大理石能量固化胶、表面处理保护材料及其制备方法，环保，提高了施工效率，提高石材的密度、光泽度以及表面保护性能，达到防水、防污、耐腐蚀的目的，直接降低生产成本及节省多项间接成本。
以上显示和描述了本发明的基本原理和主要特征以及本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.大理石能量固化胶及表面处理保护材料，其特征在于它由如下重量份数的原料组成：已二醇二丙烯酸酯10% - 50%、二缩三丙二醇二丙烯酸酯10% - 50%、三羟甲基丙烷三丙烯酸酯10% - 50%、三甲基苯甲酰基二苯基氧化膦1% - 5%、羟基环已基甲酮10% - 50%、光引发剂10% - 50%、高官聚氨酷丙烯酸酯10% - 50%、脂肪族聚酯型10% - 50%、改性烯酸酯类聚合物消泡剂10% - 50%、氟改牲聚硅氧烷聚合物10% - 50%。
2.大理石能量固化胶、表面处理保护材料的制备方法，其特征在于：
(1)、按已二醇二丙烯酸酯10% - 50%、二缩三丙二醇二丙烯酸酯10% - 50%、三羟甲基丙烷三丙烯酸酯10% - 50%、三甲基苯甲酰基二苯基氧化膦1% - 5%、羟基环已基甲酮10% -50%、光引发剂10% - 50%、高官聚氨酷丙烯酸酯10% - 50%、脂肪族聚酯型10% - 50%、改性烯酸酯类聚合物消泡剂10% - 50%、氟改牲聚硅氧烷聚合物10% - 50%进行备料；将上述组分的已二醇二丙烯酸酯、二缩三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯混合在一起搅拌1-10分钟；
(2)、往上述步骤(1)所得的溶液加入高官聚氨酷丙烯酸酯、脂肪族聚酯型混合在一起搅拌5-20分钟；
(3)、最后加入光引发剂、羟基环已基甲酮、改性烯酸酯类聚合物消泡剂、氟改牲聚硅氧烷聚合物混合在一起搅拌2-10分钟，即成。
3.根据权利要求2所述的大理石能量固化胶、表面处理保护材料的制备方法，其特征在于：上述所有步骤的操作温度在20-50度之间。