CN106739300A - The good colored terylene high strength yarn of elasticity - Google Patents
The good colored terylene high strength yarn of elasticity Download PDFInfo
- Publication number
- CN106739300A CN106739300A CN201611209127.XA CN201611209127A CN106739300A CN 106739300 A CN106739300 A CN 106739300A CN 201611209127 A CN201611209127 A CN 201611209127A CN 106739300 A CN106739300 A CN 106739300A
- Authority
- CN
- China
- Prior art keywords
- elasticity
- high strength
- strength yarn
- colored terylene
- good colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of good colored terylene high strength yarn of elasticity, described elastic good colored terylene high strength yarn includes the regenerated celulose fibre layer of the superiors, the thickener in intermediate layer and undermost natural plant fibre layer are combined, the regenerated celulose fibre layer is CUP, the natural plant fibre layer is tencel, described regenerated celulose fibre layer accounts for 15% the 20% of the good colored terylene high strength yarn totality component of elasticity, described thickener accounts for 19% the 25% of the good colored terylene high strength yarn totality component of elasticity, described natural plant fibre layer accounts for 60% the 65% of the good colored terylene high strength yarn totality component of elasticity.The present invention provides a kind of elasticity good colored terylene high strength yarn, has the advantages that intensity is high, heat-resisting good and elastic strong.
Description
Technical field
The present invention relates to a kind of good colored terylene high strength yarn of elasticity.
Background technology
Terylene also cry high-strength line, polyamide filament sewing thread be called nylon wire, we would generally be referred to as（Pearly-lustre line）Polyster fibre sewing thread
Be have terylene long fine or short fibre is twisted, wear-resisting, washing shrinkage is low, chemical stability is good.But fusing point is low, easily melts at a high speed, block up
Plug pinprick, easily broken string, polyester thread is because its intensity is high, wearability is good, washing shrinkage is low, hygroscopicity and heat-resist, corrosion-resistant, no
Easily go rotten, be widely used in the garment sewing of cotton goods, chemical fibre and blend fabric the advantages of will not damage by worms.Additionally,
It also has that color and luster is complete, good color fastness, colour-fast, nondiscolouring, it is sun-resistant the features such as, polyster fibre sewing thread and polyamide filament sewing thread
Difference, the point of terylene light one stick together, the cigarette of hair black, smell not weight, without elastic force, the sewing thread of polyamide fibre is lighted has been also one
Stick together, emit the cigarette of white, to pull up elastic smell heavier.Abrasion resistance is high, and light fastness is good, mould proof, 100 degree of left sides of degree of staining
The right side, low temperature dyeing.Because its linear slit high, durable, sealing of strength is calm, different sewing industrial products extensively can be suited the need for and quilt
Widely use.
Having many uses for terylene, is largely used to product in manufacture clothing and industry.Flame-resistant terylene is because with anti-flammability, answering
With wide range, in addition to fabrics for industrial use, building interior trim, vehicles interior trim etc. play the effect that can not be substituted, go back
Many effects are played in protective garment field.According to fire retardant protective clothing national Specification, metallurgy, forestry, chemical industry, stone
The departments such as oil, fire-fighting should use fire retardant protective clothing.China should be using the number of fire retardant protective clothing more than million, fire retardant protective clothing
Market potential is huge.In addition to pure flame-resistant terylene, can produce fire-retardant, waterproof, refuse oily, antistatic according to the particular/special requirement of user
Deng multifunctional series products.Waterproof, oil-repellent finiss such as are carried out to flame retardant polyester fabric, the feature of flame-retardant clothing can be improved；Using
Flame-resistant terylene interweaves with producing anlistatig flame-retardant textile with conductive fiber；Blending is carried out using fire resistance fibre and high-performance fiber
Interweave, high-performance refractory fabric can be produced；Using fiber blends such as fire resistance fibre and cotton, viscose glues, to improve the comfortable of protective garment
Property, while reducing secondary burn.
The content of the invention
The present invention is provided a kind of has the advantages that intensity is high, heat-resisting good and the strong elastic good colored terylene of elasticity is high-strength
Silk.
The technical scheme is that：A kind of good colored terylene high strength yarn of elasticity, described elastic good colored terylene
High strength yarn includes regenerated celulose fibre layer, the thickener in intermediate layer and the layer combination of undermost natural plant fibre of the superiors
Form, the regenerated celulose fibre layer is CUP, the natural plant fibre layer is tencel, described regenerated cellulose
Fibrage accounts for the 15%-20% of the good colored terylene high strength yarn totality component of elasticity, and described thickener accounts for good coloured of elasticity and washs
The 19%-25% of synthetic fibre high strength yarn totality component, described natural plant fibre layer accounts for the good colored terylene high strength yarn of elasticity and totally divides
The 60%-65% of amount.
In a preferred embodiment of the present invention, the thickener is hydroxypropyl methyl cellulose.
In a preferred embodiment of the present invention, it is high-strength that described regenerated celulose fibre layer accounts for the good colored terylene of elasticity
The 18% of the overall component of silk, described thickener accounts for the 20% of the good colored terylene high strength yarn totality component of elasticity, and described is natural
Plant fiber layer accounts for the 62% of the good colored terylene high strength yarn totality component of elasticity.
A kind of good colored terylene high strength yarn of elasticity of the invention, has the advantages that intensity is high, heat-resisting good and elastic strong.
Specific embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly being defined so as to be made to protection scope of the present invention.
Wherein, described elastic good colored terylene high strength yarn includes regenerated celulose fibre layer, the intermediate layer of the superiors
Thickener and undermost natural plant fibre layer combine, regenerated celulose fibre layer is CUP, described
Natural plant fibre layer is tencel, and described regenerated celulose fibre layer accounts for the good colored terylene high strength yarn totality component of elasticity
15%-20%, described thickener accounts for the 19%-25% of the good colored terylene high strength yarn totality component of elasticity, described natural plants
Fibrage accounts for the 60%-65% of the good colored terylene high strength yarn totality component of elasticity.
Further illustrate, the thickener is hydroxypropyl methyl cellulose, described regenerated celulose fibre layer accounts for elasticity
The 18% of good colored terylene high strength yarn totality component, described thickener accounts for the good colored terylene high strength yarn totality component of elasticity
20%, described natural plant fibre layer accounts for the 62% of the good colored terylene high strength yarn totality component of elasticity.
Further illustrating, tencel has dry, wet strength high, and dry and wet is by force than 85%.With swellability higher：Dry and wet
Volume 1：1.4；Under unique fibrillation characteristic, i.e. tencel fiber are acted in hygrometric state by mechanical friction, can be along fiber axial direction
Divide fibril, by the way that unique peach face style can be obtained after treatment.Good spinnability：Pure can spin, also can with cotton, hair, silk,
The fiber blends such as fiber crops, chemical fibre, cashmere interweave.It is applicable all kinds of machines of spinning, stocking yarn.It has cotton " comfortableness, terylene it is " strong
Degree ", " unique sense of touch " of " the luxurious aesthetic feeling " of wool fabric and silk and " softness is hung down and is fallen ", no matter in the state of dry or wet,
Great toughness.In a wet state, it is the cellulose fibre that the first wet strength outclass cotton.Absolutely pure natural material
Material, adds the manufacturing process of environmental protection, allows life style with conservation of nature environment as this, and the demand of modern consumer is catered to completely,
And environmental protection, can be rated as the green fiber of 21 century.
Further illustrating, CUP is a kind of regenerated celulose fibre, it is that the native celluloses such as cotton linter is former
Material is dissolved in the liquor ammoniae fortis of Kocide SD or alkaline cupric salt, is made into spinning solution, the CUP element molecularization in coagulating bath
Learn thing disintegrating and regeneration and go out cellulose, the hydrate cellulose of generation is to obtain CUP through post-processing.The section of CUP is in
Circle, without skin-core structure, fiber can bear high elongation, and obtained monofilament is thinner, so fabric is soft, gloss is soft,
There is silky touch.The hygroscopicity of CUP is approached with viscose fiber, and its official regain is 11%, in general atmosphere condition next time
Damp rate can reach 12%--13%, and under identical dyeing condition, the dyeing affinity of CUP is big compared with viscose fiber, colouring compared with
It is deep.The dry of CUP is approached by force with viscose fiber, but wet is higher than by force viscose fiber, and wearability is also superior to viscose rayon.Due to
Fiber is soft, and gloss is suitable, conventional to make high-grade silk weaving or knitted fabric.Its wearability is more excellent, good hygroscopicity, great pendency
Sense, wearability is similar to silk, meets environmentally friendly dress ornament trend.The present invention provides a kind of elasticity good colored terylene high strength yarn,
Have the advantages that intensity is high, heat-resisting good and elastic strong.
Specific embodiment of the invention, but protection scope of the present invention is not limited thereto, it is any to be familiar with this area
Technical staff disclosed herein technical scope in, the change or replacement that can be expected without creative work should all be contained
Cover within protection scope of the present invention.Therefore, the protection model that protection scope of the present invention should be limited with claims
Enclose and be defined.
Claims (3)
1. the good colored terylene high strength yarn of a kind of elasticity, it is characterised in that：Described elastic good colored terylene high strength yarn includes
The superiors regenerated celulose fibre layer, the thickener in intermediate layer and undermost natural plant fibre layer combine, it is described
Regenerated celulose fibre layer is CUP, and the natural plant fibre layer is tencel, and described regenerated celulose fibre layer is accounted for
The 15%-20% of the good colored terylene high strength yarn totality component of elasticity, described thickener accounts for the good colored terylene high strength yarn of elasticity
The 19%-25% of overall component, described natural plant fibre layer accounts for the 60%- of the good colored terylene high strength yarn totality component of elasticity
65%。
2. the good colored terylene high strength yarn of elasticity according to claim 1, it is characterised in that：The thickener is hydroxypropyl
Methylcellulose.
3. the good colored terylene high strength yarn of elasticity according to claim 1, it is characterised in that：Described regenerated cellulose is fine
Dimension layer accounts for the 18% of the good colored terylene high strength yarn totality component of elasticity, and it is high-strength that described thickener accounts for the good colored terylene of elasticity
The 20% of the overall component of silk, described natural plant fibre layer accounts for the 62% of the good colored terylene high strength yarn totality component of elasticity.