CN109652995A - A kind of preparation process of washable stamp lining lining - Google Patents
A kind of preparation process of washable stamp lining lining Download PDFInfo
- Publication number
- CN109652995A CN109652995A CN201811293894.2A CN201811293894A CN109652995A CN 109652995 A CN109652995 A CN 109652995A CN 201811293894 A CN201811293894 A CN 201811293894A CN 109652995 A CN109652995 A CN 109652995A
- Authority
- CN
- China
- Prior art keywords
- lining
- base fabric
- stamp
- washable
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention proposes a kind of preparation processes of washable stamp lining lining, successively the following steps are included: base fabric weaving, the pre-treatment of overflow pine formula, no-station pole canopy sizing, flat screen printing, fixation sizing, two point dispensing, bake and bank up with earth processing, winding inspection processing, product uses the high-elastic silk fiber of 50D/48F through broadwise, through plain weave encryption institutional framework weaving at base fabric, base fabric is handled through the anti-splitting of 4 grades of water repellents, stamp processing is given by fabric flower pattern after being formed, double-dot coating is carried out using water-fastness PA glue and is formed；Product good hand touch, bonding force is strong, resistance to dry, washing, not strike-through.The product and fabric pressing, that is, integral, clothes without plus lining fabric, not only reduced clothing making process, but also attractive and durable, and in addition the bonding intensity of its extra-heavy, just cooperated fashionable dress style now, style and the changeable trend of materials；Product had not only had adhesive function but also the dual function effect of alternative lining silk, had catered to the demand in market.
Description
[technical field]
The present invention relates to the field of fabric, especially a kind of preparation process of washable stamp lining lining.
[background technique]
Arbitrarily, comfortably, environmental protection, be new concept 21 century clothes proposed naturally, along with global warming greenhouse effect
It answers.Clothes mostly use softr thin type fabric and soft, good permeability liner, are subject to advanced production technology, make people
Wear more natural, activity of being more convenient for.But the yarn institutional framework of light and thin type lining cloth is sparse, easily causes the case where hooking silk hair
It is raw, and the texture and flexibility of lining cloth are reduced, therefore propose a kind of preparation process of washable stamp lining lining.
[summary of the invention]
The object of the invention is to solve the problems of the prior art, a kind of preparation work of washable stamp lining lining is proposed
Skill, the product good hand touch of this technique production, bonding force is strong, resistance to do, wash not strike-through, product and fabric pressing, that is, integral, clothes
Dress had not only reduced clothing making process, but also attractive and durable without adding lining fabric.
To achieve the above object, the invention proposes a kind of preparation processes of washable stamp lining lining, comprising the following steps:
A: base fabric weaving: base fabric is weaved using warp, weft yarn through plain weave encryption institutional framework；
B: overflow pine formula pre-treatment: preliminary drying preshrunk processing is carried out to base fabric, then under the control of high temperature and pressure overflow machine
The preshrunk setting treatment that relaxes is carried out to base fabric, temperature is 65~75 DEG C, and ambient humidity is 45~55%；
C: drying sizing no-station pole canopy sizing: is carried out to base fabric by the way of loose formula preshrunk sizing；
D: flat screen printing: base fabric is sent to printing machine and carries out stamp arrangement；
E: fixation sizing: through no-station pole canopy drying fixation after stamp, and final finishing molding is washed；
F: two point dispensing: double-dot coating is carried out using water-fastness PA glue and forms hot melt adhesive layer, base fabric is sent into after cooling and is dried
Room；
G: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 90~130
DEG C, drying time is 5~7 minutes, and the temperature of the second drying chamber is 130~170 DEG C, and drying time is 4~5 minutes, third drying chamber
Temperature be 170~180 DEG C, drying time be 2~3 minutes；
H: winding inspection processing: base fabric being wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding,
And it carries out the qualified product of quality, appearance to be packaged as finished product.
Preferably, being passed through in the step a, weft yarn is all made of the high-elastic silk fiber of 50D/48F.
It is handled preferably, carrying out the anti-splitting of 4 grades of water repellents to base fabric before the step c no-station pole canopy sizing.
Preferably, the mesh number of cylinder is CP40 in the step f, the aperture of cylinder is 0.26-0.29mm, the thickness of cylinder
Degree is 0.16-0.18mm.
Preferably, carrying out double-dot coating using the ultra-fine microdot electrostatic coating technology of high mesh in the step f.
Preferably, antistatic agent is added in the PA glue in the step f in process of production.
Preferably, base fabric in the step d, selvage guide same speed, with tension under conditions of enter printing system.
Beneficial effects of the present invention: the present invention proposes a kind of preparation process of washable stamp lining lining, and product is adopted through broadwise
With the high-elastic silk fiber of 50D/48F, through plain weave encryption institutional framework weaving at base fabric, base fabric is handled through the anti-splitting of 4 grades of water repellents, through fixed
Stamp processing is given by fabric flower pattern after type, double-dot coating is carried out using water-fastness PA glue and is formed；Product good hand touch, bonding force
By force, resistance to dry, washing, not strike-through.The product and fabric pressing, that is, integral, clothes without plus lining fabric, both reduce clothing making
Process, and attractive and durable just cooperates fashionable dress style now, style and the changeable tide of materials in addition the bonding intensity of its extra-heavy
Stream；Product had not only had adhesive function but also the dual function effect of alternative lining silk, had catered to the demand in market.
Feature and advantage of the invention will be described in detail by embodiment.
[specific embodiment]
A kind of preparation process of washable stamp lining lining of the present invention, comprising the following steps:
A: base fabric weaving: base fabric warp, weft yarn using the high-elastic silk fiber of 50D/48F through plain weave encryption institutional framework weaving and
At；
B: overflow pine formula pre-treatment: preliminary drying preshrunk processing is carried out to base fabric, then under the control of high temperature and pressure overflow machine
The preshrunk setting treatment that relaxes is carried out to base fabric, temperature is 65~75 DEG C, and ambient humidity is 45~55%；
C: drying sizing no-station pole canopy sizing: is carried out to base fabric by the way of loose formula preshrunk sizing；
D: flat screen printing: base fabric, selvage guide same speed, with tension under conditions of enter printing system carry out stamp it is whole
Reason；
E: fixation sizing: through no-station pole canopy drying fixation after stamp, and final finishing molding is washed；
F: two point dispensing: carrying out double-dot coating using water-fastness PA glue and form hot melt adhesive layer, quiet using the ultra-fine microdot of high mesh
Electrocoat technology carries out double-dot coating, and base fabric is sent into drying chamber after cooling；
G: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 90~130
DEG C, drying time is 5~7 minutes, and the temperature of the second drying chamber is 130~170 DEG C, and drying time is 4~5 minutes, third drying chamber
Temperature be 170~180 DEG C, drying time be 2~3 minutes；
H: winding inspection processing: base fabric being wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding,
And it carries out the qualified product of quality, appearance to be packaged as finished product.
The anti-splitting of 4 grades of water repellents is carried out to base fabric before the step c no-station pole canopy sizing to handle.Cylinder in the step f
Mesh number is CP40, and the aperture of cylinder is 0.26-0.29mm, cylinder with a thickness of 0.16-0.18mm.PA glue in the step f
Antistatic agent is added in process of production.
Technical performance index:
1, peel strength: before washing >=22N/5 × 10cm washing after >=20N/5 × 10cm；
2, xeothermic change in size: through to -1.5~+0.3 broadwise -1.0~+0.4；
3, change in size is washed: through to -1.0~+0.4 broadwise -1.0~+0.4；
4, solid carbon dioxide washes cosmetic variation >=4 grade；
5, free formaldehyde :≤75ppm is discharged.
A kind of preparation process of washable stamp lining lining of the present invention, has the advantage that
1, product is all made of the high-elastic silk fiber of 50D/48F through broadwise, weaves through plain weave encryption institutional framework.Again through 4
The anti-splitting processing of grade water repellent, gives stamp processing by fabric flower pattern after being formed.
Product uses the high-elastic silk fiber of 50D/48F through broadwise, through plain weave encryption institutional framework weaving at base fabric, fabric feeling
It is smooth, drapability is good, very without wrinkle.Due to the thin easy hook silk of fabric, by using computer pair on high temperature and pressure overflow machine
Temperature, time, nozzle exit pressure are accurately controlled, make cloth cover it is smooth, it is bright and clean, without hook silk.Using loose formula preshrunk shaping technology
Suitable for the drying sizing of such ultrathin microfibre stockinette, fiber pore can be made even closer, to generate bulk light
Clean appearance.
Then base fabric is sent to flat screen printing machine and carries out stamp arrangement, we wear cloth route by rationally introducing, and borrows
The friction of assistant director of a film or play's cloth roller and tension-adjusting gear and fabric, it is appropriate adjust it is elastic before entering printing roller, make base fabric with
Selvage guide obtains uniform elongation.Same speed, with tension under conditions of enter printing system, the flower of setting can be obtained
Type, it is i.e. plastic after fixation is washed.The base fabric of variation and new technique bring richer expressive force to lining cloth, frivolous
Base fabric stamps colorful pattern, in conjunction with color-grading and comparison, feeling that is beautiful and having cheerful and light-hearted pleasure；Collocation imbibition again
The stamp of effect, dim color sense, the stamp with elegant as silk, bright and clean base fabric bring pleasing to lining cloth
It is new to feel.
2, double-dot coating is carried out using water-fastness PA glue to form, develop the ultra-fine microdot electrostatic implanted prosthetics of high mesh, it is single in this way
The volume of position particle rubber powder is smaller, and weight is lighter；With the original feel of fabric is neither influenced after fabric pressing, and embody lining cloth
Supporting role.
Since fabric is frivolous, bleed phenomenon is easily generated during the pressing of clothes processing, influences appearance, the hand of clothes
The service life of sense and pressing machine.Feel problem not only can solve with the method for high mesh microdot coating using water-fastness PA glue,
Also the problem of can solve part bleed simultaneously, by adjustment to base fabric type selecting, arrangement, coating processing technology and formula and right
The research of compatibility between raw material, selects high mesh electrostatic coating technology, finer and closely woven between glue point, and neither influences after fabric pressing
The original feel of fabric, and embody the supporting role of lining cloth；Not only dry cleaning resistance but also water-fastness, if realizing lining cloth seemingly has nothing, with
The transparent texture of fabric one integrated mass.
Above-described embodiment is the description of the invention, is not limitation of the invention, after any pair of simple transformation of the present invention
Scheme all belong to the scope of protection of the present invention.
Claims (7)
1. a kind of preparation process of washable stamp lining lining, it is characterised in that: the following steps are included:
A: base fabric weaving: base fabric is weaved using warp, weft yarn through plain weave encryption institutional framework；
B: overflow pine formula pre-treatment: preliminary drying preshrunk processing is carried out to base fabric, then to base under the control of high temperature and pressure overflow machine
Cloth carries out the preshrunk setting treatment that relaxes, and temperature is 65~75 DEG C, and ambient humidity is 45~55%；
C: drying sizing no-station pole canopy sizing: is carried out to base fabric by the way of loose formula preshrunk sizing；
D: flat screen printing: base fabric is sent to printing machine and carries out stamp arrangement；
E: fixation sizing: through no-station pole canopy drying fixation after stamp, and final finishing molding is washed；
F: two point dispensing: double-dot coating is carried out using water-fastness PA glue and forms hot melt adhesive layer, base fabric is sent into drying chamber after cooling；
G: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 90~130 DEG C, is dried
The dry time is 5~7 minutes, and the temperature of the second drying chamber is 130~170 DEG C, and drying time is 4~5 minutes, the temperature of third drying chamber
It is 170~180 DEG C, drying time is 2~3 minutes；
H: winding inspection processing: base fabric is wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding, and will
The qualified product of quality, appearance carries out being packaged as finished product.
2. a kind of preparation process of washable stamp lining lining as described in claim 1, it is characterised in that: passed through in the step a,
Weft yarn is all made of the high-elastic silk fiber of 50D/48F.
3. a kind of preparation process of washable stamp lining lining as described in claim 1, it is characterised in that: the step c without
The anti-splitting of 4 grades of water repellents is carried out to base fabric before power sizing to handle.
4. a kind of preparation process of washable stamp lining lining as described in claim 1, it is characterised in that: circle in the step f
The mesh number of net is CP40, and the aperture of cylinder is 0.26-0.29mm, cylinder with a thickness of 0.16-0.18mm.
5. a kind of preparation process of washable stamp lining lining as described in claim 1, it is characterised in that: adopted in the step f
Double-dot coating is carried out with the ultra-fine microdot electrostatic coating technology of high mesh.
6. a kind of preparation process of washable stamp lining lining as described in claim 1, it is characterised in that: in the step f
Antistatic agent is added in PA glue in process of production.
7. a kind of preparation process of washable stamp lining lining as described in claim 1, it is characterised in that: base in the step d
Cloth, selvage guide same speed, with tension under conditions of enter printing system.