CN114656830A - 一种通用长效型水性环保脱漆剂及其制备方法和使用方法 - Google Patents
一种通用长效型水性环保脱漆剂及其制备方法和使用方法 Download PDFInfo
- Publication number
- CN114656830A CN114656830A CN202210459825.4A CN202210459825A CN114656830A CN 114656830 A CN114656830 A CN 114656830A CN 202210459825 A CN202210459825 A CN 202210459825A CN 114656830 A CN114656830 A CN 114656830A
- Authority
- CN
- China
- Prior art keywords
- water
- paint
- long
- environmental protection
- paint stripper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种通用长效型水性环保脱漆剂及其制备方法和使用方法，属于脱漆剂领域。一种通用长效型的水性环保脱漆按重量百分比包括，30％‑65％的去离子水、5％‑30％的无机碱、10％‑30％的主溶剂、1％‑10％的助溶剂、5％‑20％的促进剂；与现有技术相比，本申请的一种通用长效型的水性环保脱漆剂，该脱漆剂涂料通用性强；脱漆性能高效持久，使用寿命长，消耗量低；不含二氯甲烷、苯酚、甲酸和低沸点溶剂，安全环保，常温下挥发率低，气味小，稳定性好，能够很好地满足运输和储存要求；成本低，生产设备简单，制备方法简单，使用方法简单，具有很好的经济性。
Description
技术领域
本发明涉及脱漆剂领域，具体涉及一种通用长效型水性环保脱漆剂及其制备方法和使用方法。
背景技术
目前，市场上的水性脱漆剂虽然种类众多，但对于涂料类型的通用性比较差，往往仅适用于部分特定类型的粉末涂料或油漆或水性漆或电泳漆，遇到一些涂料类型多样的涂装返工件，脱漆效果不尽理想。此外，现有市场上的水性脱漆剂多以漆膜溶解型为主，随着使用时间延长和漆膜溶解量累积，脱漆剂的脱漆效力会大幅下降，造成脱漆剂的消耗量显著增加，甚至需要频繁换槽；因此，提出一种通用长效型水性环保脱漆剂及其制备方法和使用方法。
发明内容
针对现有技术的不足，本发明提出了一种通用长效型水性环保脱漆剂及其制备方法和使用方法。
本发明的目的可以通过以下技术方案实现：
一种通用长效型的水性环保脱漆剂，所述通用长效型的水性环保脱漆剂按重量百分比包括，30％-65％的去离子水、5％-30％的无机碱、10％-30％的主溶剂、 1％-10％的助溶剂、5％-20％的促进剂、1％-10％的络合剂、1％-5％的缓蚀剂。
进一步地，所述无机碱为氢氧化钠、氢氧化钾、碳酸钠、碳酸钾中的一种或多种的混合物。
进一步地，所述主溶剂为苯甲醇、二甲基亚砜、环丁砜、N，N-二甲基甲酰胺、吗啉、乙二醇单丁醚、二乙二醇丁醚、乙二醇单甲醚、丙二醇甲醚、丙二醇丙醚、乙二醇苯醚、N-甲基-2-吡咯烷酮、N-羟乙基-2-吡咯烷酮中的一种或多种的混合物。
进一步地，所述助溶剂为乙二醇、聚乙二醇400、丙三醇、二甘醇、环氧丙醇中的一种或多种的混合物。
进一步地，促进剂为糠醇、四氢糠醇、糠基硫醇、糠基聚乙二醇、四氢糠基聚乙二醇、糠胺、四氢糠胺、2-苯基二乙醇胺、十八胺中的一种或多种的混合物。
进一步地，所述络合剂为乙二胺四乙酸二钠、乙二胺四乙酸四钠、柠檬酸钠、草酸钠、葡萄糖酸钠中的一种或多种的混合物。
进一步地，缓蚀剂为单乙醇胺、二乙醇胺、三乙醇胺、二异丙醇胺、三异丙醇胺、五水偏硅酸钠中的一种或多种的混合物。
进一步地,所述去离子水的电阻率大于4MΩ·cm。
另一方面，本发明还提供一种如上述任一项所述的通用长效型的水性环保脱漆剂的制备方法,包括以下步骤：
将无机碱溶于去离子水中形成碱基液；然后向碱基液中依次加入主溶剂、助溶剂、促进剂、络合剂和缓蚀剂；
搅拌使所有组份至完全溶解，得到所述的通用长效型的水性环保脱漆剂。
第三方面，本发明还提供一种如上述任一项所述的通用长效型的水性环保脱漆剂的使用方法，其特征在于,将待脱漆涂装件完全浸没在所述的通用长效型的水性环保脱漆剂中，脱漆温度为70～90℃，脱漆时间为1～60分钟。
本发明的有益效果：
本发明提供的一种通用长效型的水性环保脱漆剂通用性强，能够高效脱除多种常规类型涂料，如基于聚酯树脂、聚氨酯树脂、环氧树脂、丙烯酸树脂、醇酸树脂、氟碳树脂等成膜树脂和不同固化体系的粉末涂料或油漆或水性漆或电泳漆等。
脱漆性能高效持久，使用寿命长，消耗量低。通过去离子水、无机碱、主溶剂、助溶剂、促进剂、络合剂及缓蚀剂等多种组分的科学复配，所述脱漆剂具有出色的漆膜剥离效果和适中的漆膜溶解力，能够较低程度溶解涂层，更大程度上使涂层从基材表面成片剥离脱落下来，逐渐累积沉淀到槽底，从而显著减少脱漆剂的溶解损耗，且通过定期倒槽，过滤清理漆渣，可使脱漆剂始终保持良好的脱漆效力，极大延长脱漆剂的使用寿命。
不含二氯甲烷、苯酚、甲酸和低沸点溶剂。安全环保，常温下挥发率低，气味小，稳定性好，能够很好地满足运输和储存要求。具有很好的经济性。成本低，生产设备简单，制备方法简单，使用方法简单。
脱漆性能高效持久，使用寿命长，消耗量低；不含二氯甲烷、苯酚、甲酸和低沸点溶剂，安全环保，常温下挥发率低，气味小，稳定性好，能够很好地满足运输和储存要求；成本低，生产设备简单，制备方法简单，使用方法简单，具有很好的经济性。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
在本说明书的描述中，参考术语“一个实施例”、“示例”、“具体示例”等的描述意指结合该实施例或示例描述的具体特征、结构、材料或者特点包含于本发明的至少一个实施例或示例中。在本说明书中，对上述术语的示意性表述不一定指的是相同的实施例或示例。而且，描述的具体特征、结构、材料或者特点可以在任何的一个或多个实施例或示例中以合适的方式结合。
一种通用长效型的水性环保脱漆剂，所述通用长效型的水性环保脱漆剂按重量百分比包括，30％-65％的去离子水、5％-30％的无机碱、10％-30％的主溶剂、 1％-10％的助溶剂、5％-20％的促进剂、1％-10％的络合剂、1％-5％的缓蚀剂。
进一步地，所述无机碱为氢氧化钠、氢氧化钾、碳酸钠、碳酸钾中的一种或多种的混合物。
进一步地，所述主溶剂为苯甲醇、二甲基亚砜、环丁砜、N，N-二甲基甲酰胺、吗啉、乙二醇单丁醚、二乙二醇丁醚、乙二醇单甲醚、丙二醇甲醚、丙二醇丙醚、乙二醇苯醚、N-甲基-2-吡咯烷酮、N-羟乙基-2-吡咯烷酮中的一种或多种的混合物。
进一步地，所述助溶剂为乙二醇、聚乙二醇400、丙三醇、二甘醇、环氧丙醇中的一种或多种的混合物。
进一步地，促进剂为糠醇、四氢糠醇、糠基硫醇、糠基聚乙二醇、四氢糠基聚乙二醇、糠胺、四氢糠胺、2-苯基二乙醇胺、十八胺中的一种或多种的混合物。
进一步地，所述络合剂为乙二胺四乙酸二钠、乙二胺四乙酸四钠、柠檬酸钠、草酸钠、葡萄糖酸钠中的一种或多种的混合物。
进一步地，缓蚀剂为单乙醇胺、二乙醇胺、三乙醇胺、二异丙醇胺、三异丙醇胺、五水偏硅酸钠中的一种或多种的混合物。
进一步地,所述去离子水的电阻率大于4MΩ·cm。
实施例1：一种通用长效型的水性环保脱漆剂含有如表1所示组分
表1
| 脱漆剂成分 | 重量百分比 |
| 去离子水 | 50％ |
| 氢氧化钠 | 15％ |
| 苯甲醇 | 10％ |
| 乙二醇 | 5％ |
| 四氢糠胺 | 10％ |
| 葡萄糖酸钠 | 5％ |
| 三乙醇胺 | 5％ |
上述脱漆剂的制备方法为：先将氢氧化钠溶于去离子水中形成碱基液，然后依次加入苯甲醇、乙二醇、四氢糠胺、葡萄糖酸钠和三乙醇胺，搅拌使所有组份完全溶解，得到所述脱漆剂。
上述脱漆剂进行脱漆的使用方法为：将待脱漆涂装件完全浸没在脱漆剂中，温度为80℃，保温60分钟即可。
实施例2：一种通用长效型的水性环保脱漆剂含有如表2所示组分：
表2
| 脱漆剂成分 | 重量百分比 |
| 去离子水 | 30％ |
| 氢氧化钠 | 15％ |
| 氢氧化钾 | 5％ |
| 苯甲醇 | 10％ |
| 丙二醇甲醚 | 10％ |
| 乙二醇 | 2％ |
| 糠醇 | 10％ |
| 四氢糠胺 | 5％ |
| 乙二胺四乙酸二钠 | 10％ |
| 二异丙醇胺 | 3％ |
上述脱漆剂的制备方法为：先将氢氧化钠及氢氧化钾溶于去离子水中形成碱基液，然后依次加入苯甲醇、丙二醇甲醚、乙二醇、糠醇、四氢糠胺、乙二胺四乙酸二钠和二异丙醇胺，搅拌使所有组份完全溶解，得到所述脱漆剂。
上述脱漆剂进行脱漆的使用方法与实施例1相同。
实施例3：一种通用长效型的水性环保脱漆剂含有如表3所示组分
表3
| 脱漆剂成分 | 重量百分比 |
| 去离子水 | 30％ |
| 氢氧化钾 | 15％ |
| 苯甲醇 | 10％ |
| 丙二醇甲醚 | 10％ |
| 乙二醇苯醚 | 5％ |
| 乙二醇 | 8％ |
| 四氢糠醇 | 10％ |
| 四氢糠胺 | 2％ |
| 柠檬酸钠 | 8％ |
| 三异丙醇胺 | 2％ |
上述脱漆剂的制备方法为：先将氢氧化钾溶于去离子水中形成碱基液，然后依次加入苯甲醇、丙二醇甲醚、乙二醇苯醚、乙二醇、四氢糠醇、四氢糠胺、柠檬酸钠和三异丙醇胺，搅拌使所有组份完全溶解，得到所述脱漆剂。
上述脱漆剂进行脱漆的使用方法与实施例1相同。
将相同材料、相同体积、相同表面积的待脱漆涂装件分别涂有聚酯粉末涂料、环氧粉末涂料、聚氨酯油漆、氟碳油漆、醇酸油漆、丙烯酸水性漆、阴极电泳漆。
所用聚酯粉末涂料来自阿克苏诺贝尔粉末涂料
600；
所用环氧粉末涂料来自阿克苏诺贝尔粉末涂料
100；
所用聚氨酯油漆来自贝科工业涂料DJ-291-98001；
所用氟碳油漆来自贝科工业涂料FJ-233-98001；
所用醇酸油漆来自贝科工业涂料AD-621-98001；
所用丙烯酸水性漆来自宣伟涂料
LKD1030；
所用阴极电泳漆来自巴斯夫阴极电泳漆
800。
经过检验，实施例1～3配方所得的脱漆剂，对于6种不同体系的涂料，在 80℃，60分钟的作用时间内，均能够将6种涂料脱除干净无残留，脱漆率100％。具体见表4：
表4
此外，经检验，实施例1～3配方所得脱漆剂经老化后，对于6种不同体系的涂料，在80℃，60分钟的作用时间内，同样能够将6种涂料脱除干净无残留，脱漆率100％。具体见表5：
表5
本发明中，优选无机碱组份，强碱条件下含酯键的涂层(聚酯、聚氨酯、醇酸等)容易发生水解，从而快速剥离脱落。优选含芳香烃官能团的水性溶剂，利用芳香烃官能团的低极性特征来增加与同样低极性涂层(丙烯酸、环氧、氟碳等)间的相似相容效果，从而有利于提高脱漆剂组份对涂层的渗透溶胀作用。优选特定的促进剂和络合剂，可以显著地促进脱漆剂组份对涂层的渗透溶胀剥离。同时也可赋予所述脱漆剂更加高效持久的脱漆效力。优选加温浸泡的使用方法，能够进一步加快各组分间的相互作用，大幅提高脱漆剂对涂层的渗透、溶胀和剥离效果。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。
Claims (10)
1.一种通用长效型的水性环保脱漆剂，其特征在于，所述通用长效型的水性环保脱漆剂按重量百分比包括，30％-65％的去离子水、5％-30％的无机碱、10％-30％的主溶剂、1％-10％的助溶剂、5％-20％的促进剂、1％-10％的络合剂、1％-5％的缓蚀剂。
2.根据权利要求1所述的通用长效型的水性环保脱漆剂，其特征在于，所述无机碱为氢氧化钠、氢氧化钾、碳酸钠、碳酸钾中的一种或多种的混合物。
3.根据权利要求1所述的通用长效型的水性环保脱漆剂，其特征在于，所述主溶剂为苯甲醇、二甲基亚砜、环丁砜、N，N-二甲基甲酰胺、吗啉、乙二醇单丁醚、二乙二醇丁醚、乙二醇单甲醚、丙二醇甲醚、丙二醇丙醚、乙二醇苯醚、N-甲基-2-吡咯烷酮、N-羟乙基-2-吡咯烷酮中的一种或多种的混合物。
4.根据权利要求1所述的通用长效型的水性环保脱漆剂，其特征在于，所述助溶剂为乙二醇、聚乙二醇400、丙三醇、二甘醇、环氧丙醇中的一种或多种的混合物。
5.根据权利要求1所述的通用长效型的水性环保脱漆剂，其特征在于，促进剂为糠醇、四氢糠醇、糠基硫醇、糠基聚乙二醇、四氢糠基聚乙二醇、糠胺、四氢糠胺、2-苯基二乙醇胺、十八胺中的一种或多种的混合物。
6.根据权利要求1所述的通用长效型的水性环保脱漆剂，其特征在于，所述络合剂为乙二胺四乙酸二钠、乙二胺四乙酸四钠、柠檬酸钠、草酸钠、葡萄糖酸钠中的一种或多种的混合物。
7.根据权利要求1所述的通用长效型的水性环保脱漆剂，其特征在于，缓蚀剂为单乙醇胺、二乙醇胺、三乙醇胺、二异丙醇胺、三异丙醇胺、五水偏硅酸钠中的一种或多种的混合物。
8.根据权利要求1所述的通用长效型的水性环保脱漆剂，其特征在于,所述去离子水的电阻率大于4MΩ·cm。
9.一种如权利要求1-8任一项所述的通用长效型的水性环保脱漆剂的制备方法，其特征在于,包括以下步骤：
将无机碱溶于去离子水中形成碱基液；然后向碱基液中依次加入主溶剂、助溶剂、促进剂、络合剂和缓蚀剂；
搅拌使所有组份至完全溶解，得到所述的通用长效型的水性环保脱漆剂。
10.一种如权利要求1-8任一项所述的通用长效型的水性环保脱漆剂的使用方法，其特征在于,将待脱漆涂装件完全浸没在所述的通用长效型的水性环保脱漆剂中，脱漆温度为70～90℃，脱漆时间为1～60分钟。