CN114875687A - 一种生物基可降解渗透水刺布聚氨酯合成革贴面成品 - Google Patents
一种生物基可降解渗透水刺布聚氨酯合成革贴面成品 Download PDFInfo
- Publication number
- CN114875687A CN114875687A CN202210553465.4A CN202210553465A CN114875687A CN 114875687 A CN114875687 A CN 114875687A CN 202210553465 A CN202210553465 A CN 202210553465A CN 114875687 A CN114875687 A CN 114875687A
- Authority
- CN
- China
- Prior art keywords
- bio
- scraper
- synthetic leather
- cloth
- polyurethane resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请涉及一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，涉及合成革制作技术领域，成品的基布选用粘胶锦纶混纺水刺无纺布，第一步直接在基布上涂布。先将石墨烯、苎麻纤维粉、羧甲基纤维素、葡萄糖酸钙及DMF加入真空搅拌釜中进行搅拌，然后加入生物基可降解聚氨酯树脂进行搅拌，真空脱泡后再进行过滤以备用制得涂布工作浆料。第二步使涂布浆料中的生物基可降解聚氨酯树脂在基布的表面凝固。第三部清水水洗，洗净DMF。第四步用烘箱预热烫平烘干定型得到底胚。第五步将溶剂型生物基可降解聚氨酯涂刮到离型纸上放入烘箱加热形成薄膜，然后用上述复合物与之前的底胚贴合，再烘干得到成品。本申请具有减小对周边环境造成污染，并保护人员健康的效果。
Description
技术领域
本申请涉及合成革制作技术领域，尤其是涉及一种生物基可降解渗透水刺布聚氨酯合成革贴面成品。
背景技术
目前，由于皮革用途十分广泛，如用于鞋靴制作、家具制作、箱包制作等等均大量用到各种皮革，模拟天然革的组成和结构并可作为其代用材料的塑料制品。通常以经浸渍的无纺布为网状层，微孔聚氨脂层作为粒面层制得。其正、反面都与皮革十分相似，并具有一定的透气性，比普通人造革更接近天然革。
相关技术中，大多数合成革采用以100％化学合成纤维(涤纶、尼龙) 的无纺布作为底基，涂覆合成树脂及各种塑料添加制成，由于化学纤维的可降解难度大，易对环境产生污染，且大多数化学纤维由于对皮肤的不可亲和性造成穿着不舒适。并且合成革制造过程中大多使用二甲基甲酰胺类有机物作为主要溶剂，这就使得合成革制造中会产生大量的二甲基甲酰胺的废水以及废气，在处理合成革的时候，会使用燃烧或者将合成革进行填埋的方法处理合成革。
针对上述中的相关技术，发明人认为合成革生物降解缓慢，在使用后不管是通过燃烧还是填埋的方法处理合成革，都会造成周边环境污染，并危害人员健康。
发明内容
为了改善合成革生物降解缓慢，在使用后不管是通过燃烧还是填埋的方法处理合成革，都会造成周边环境污染，并危害人员健康的问题，本申请提供一种生物基可降解渗透水刺布聚氨酯合成革贴面成品。
本申请提供的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品采用如下的技术方案：
一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，所述合成革贴面成品的基布选用粘胶、锦纶混纺的水刺无纺布；所述成品的制备步骤为：第一步为直接在基布上涂布具有生物基可降解聚氨酯树脂的涂布浆料；第二步为凝固，使涂布浆料中的生物基可降解聚氨酯树脂在基布的表面凝固；第三步为用清水水洗基布，洗净基布上的DMF；第四步以120-160℃预热、烫平、烘干、定型得到所述底胚；第五步将溶剂型生物基可降解聚氨酯树脂涂刮到离型纸上，然后将涂刮有生物基可降解聚氨酯树脂的离型纸放入烘箱加热形成薄膜；第六步将薄膜与所述底胚贴合，再烘干得到成品。涂布浆料为生物基可降解聚氨酯树脂60-70份，聚氨酯树脂30-40份，DMF100 份，羧甲基纤维素5-10份，超细石墨烯5-10份，苎麻纤维粉5-10份，葡萄糖酸钙2-5份。
可选的，所述涂布浆料的制备流程为先将超细石墨烯、苎麻纤维粉、羧甲基纤维素、葡萄糖酸钙及DMF加入真空搅拌釜中以500-800r/min搅拌30min，之后加入生物基可降解聚氨酯树脂，生物基可降解聚氨酯树脂以1000-1500r/min搅拌60-120min，之后真空脱泡60-120min，最后用 180-200目过滤以备用，制得涂布浆料。
可选的，在第二步中，凝固的具体步骤为在温度为20-25℃的条件下，对基布的两侧均进行1-2h的冷风风干凝固工序。
可选的，在第三步中，水洗基布的具体步骤为基布以0.5m/s的运动速度依次经过一号水池、二号水池、三号水池中，经过水池时基布浸没于水池中；一号水池中为食盐水，二号水池和三号水池均为清水。
可选的，在第四步中，烫平基布的时间为1-3min，烘干基布的温度为120-160℃，且基布的烘干时间为4-8min，定型基布的温度为120℃ -160℃，时间为5-9s。
可选的，在第五步中，所述离型纸依次经过一号刮机、二号刮机、三号刮机，所述一号刮机、二号刮机、三号刮机上分别包括一号刮刀、二号刮刀以及三号刮刀，所述一号刮刀距离所述离型纸的间距为7-9cm,所述二号刮刀距离所述离型纸的间距为1-3cm,所述三号刮刀距离所述离型纸的间距为0.2-0.6cm。
可选的，在第五步中，所述烘箱加热离型纸的温度为120-160℃。
可选的，在第六步中，烘干贴合的所述薄膜与底胚的温度为30-50℃。
可选的，所述水刺无纺布中粘胶、锦纶混纺的比例为1:1。
综上所述，本申请包括以下至少一种生物基可降解渗透水刺布聚氨酯合成革贴面成品有益技术效果：
运用中，合成革贴面成品的基布选用粘胶锦纶混纺水刺无纺布，第一步直接在基布上涂布，涂布材料为生物基可降解聚氨酯树脂、普通聚氨酯树脂、DMF、羧甲基纤维素、超细石墨烯、苎麻纤维粉以及葡萄糖酸钙。先将石墨烯、苎麻纤维粉、羧甲基纤维素、葡萄糖酸钙及DMF加入真空搅拌釜中进行搅拌，然后加入生物基可降解聚氨酯树脂进行搅拌，真空脱泡后再进行过滤以备用制得涂布工作浆料。第二步使涂布浆料中的生物基可降解聚氨酯树脂在基布的表面凝固。第三部清水水洗，洗净DMF。第四步用烘箱预热烫平烘干定型就得到了底胚。第五步将溶剂型生物基可降解聚氨酯涂刮到离型纸上放入烘箱加热形成薄膜，然后用上述复合物与之前的底胚贴合，再烘干得到成品。
具体实施方式
为使本申请实施例的目的、技术方案和优点更加清楚，下面将对本申请实施例的技术方案进行清楚、完整地描述。显然，所描述的实施例是本申请的一部分实施例，而不是全部的实施例。基于所描述的本申请的实施例，本领域普通技术人员在无需创造性劳动的前提下所获得的所有其它实施例，都属于本申请保护的范围。
除非另作定义，此处使用的技术术语或者科学术语应当为本申请所属领域内具有一般技能的人士所理解的通常意义。本申请专利申请说明书以及权利要求书中使用的“一个”或者“一”等类似词语，不表示数量限制，而是表示存在至少一个。
本申请实施例公开一种生物基可降解渗透水刺布聚氨酯合成革贴面成品。
合成革是一种模拟天然革的组成和结构并可作为其代用材料的塑料制品，合成革在制备过程中，通常以经浸渍后的无纺布为网状层，微孔聚氨脂层作为粒面层制得。设计人员改进后，一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，成品的基布选用粘胶、锦纶混纺的水刺无纺布，且水刺无纺布中粘胶、锦纶混纺的比例为1:1。
实施例1：
合成革贴面成品的制备步骤为：
第一步：直接在基布上涂布具有生物基可降解聚氨酯树脂的涂布浆料；涂布浆料为生物基可降解聚氨酯树脂60份，聚氨酯树脂30份，DMF100份，羧甲基纤维素5份，超细石墨烯5份，苎麻纤维粉5份，葡萄糖酸钙2份。
所述涂布浆料的制备流程为先将超细石墨烯、苎麻纤维粉、羧甲基纤维素、葡萄糖酸钙及DMF加入真空搅拌釜中以500r/min搅拌30min，之后加入生物基可降解聚氨酯树脂，生物基可降解聚氨酯树脂以1000r/min 搅拌60min，之后真空脱泡60min，最后用180目过滤以备用，制得涂布浆料。
生物基可降解聚氨酯树脂为生物基改性聚氨酯树脂，由水性生物基改性高固含多元醇以及生物基改性异氰酸酯组成，水性生物基改性高固含多元醇、生物基改性异氰酸酯的比例为2：3。
将水性生物基改性高固含多元醇与生物基改性异氰酸酯按比例充分混合后，在115℃温度下烘烤10min，制得生物基改性聚氨酯树脂。
第二步：使涂布浆料中的生物基可降解聚氨酯树脂在基布的表面凝固，且凝固的具体步骤为在温度为20℃的条件下，对基布的两侧均进行1h的冷风风干凝固工序。
第三步：用清水水洗基布，洗净基布上的DMF，水洗基布的具体步骤为基布以0.5m/s的运动速度依次经过一号水池、二号水池、三号水池中，经过水池时基布浸没于水池中；一号水池中为食盐水，二号水池和三号水池均为清水。
需要说明的是，浸好浆料的基布通过设置动力辊装置进行连续输送，整个装置设置在所有水池的正上方，并且，由于第一水池、第二水池、第三水池之间相互隔开，基布在一定动力下运行时，整体呈波浪状，每两个动力辊之间的基布呈圆弧状，基布位于圆弧状的底部浸没于水池中，基布浸没于水池中的时间根据动力辊的运行速度来确定，动力辊的运动方式也可采取规律的间歇式运动，每一次运动的时长大于静止的时长，这样可使得基布每变动一次位置后便可相对延长在水池中浸没的时长，提高基布中 DMF的去除效果。
而且，由于基布呈圆弧状，浸没在水池中的基布由于倾斜角度的存在，在重力作用下，基布中的DMF会逐渐汇集在圆弧的底部，便于水池中的溶液和DMF充分混合。
动力辊每运转一次，基布浸没于水池中的幅长都是一致的，该幅长可以通过设定动力辊的运行速度和运行时间来控制，优化的，基布沿运行方向上以水面为对称面对称设置，浸没于水池中的幅长称为下半弧段，外露于水面上的幅长称为上半弧段，举例说明，每次运行后，上半弧段外露于水面上之后便会转换至浸没于水池中，此时为下半弧段，如此设置，当一个下半弧段在第一水池中进行第一次清洗之后，从第一水池露出变成上半弧段，再转变成下半弧段进入第二水池中进行第二次清洗，同理可得，之后同样以下半弧段进入第三水池进行第三次清洗。这样一来，整个基布均分成多段幅长一致的上半弧段或者下半弧段，处于下半弧段时便可进行对基布中DMF的清洗，处于上半弧段时便可在重力作用下使得基布中的DMF 汇集在下半弧段中，所有基布都能充分地被多次水洗，提高基布中DMF的去除效率。
而且此种水洗的方式好处在于，当基布运行过程中逐渐离开水池时，由于即将上行，此时，基布呈倾斜状态，水分在重力作用下会掉落，由于 DMF可以溶于水，内部的残余的DMF会随着水分在重力作用下与基布分离，更好地提高基布中DMF的去除效果。
综述，合理调整动力辊的工作参数以及布局基布的运行状态，便可使得基布进行连续式的多次清洗，也正是因为这样，基布的DMF的去除效果最好。
第四步：对基布进行预热、烫平、烘干、定型得到底胚，以120℃预热，烫平基布的时间为1min，烘干基布的温度为120℃，且基布的烘干时间为4min，定型基布的温度为120℃，时间为5s。
第五步：将溶剂型生物基可降解聚氨酯树脂涂刮到离型纸上，然后将涂刮有生物基可降解聚氨酯树脂的离型纸放入烘箱加热形成薄膜；所述离型纸依次经过一号刮机、二号刮机、三号刮机，所述一号刮机、二号刮机、三号刮机上分别包括一号刮刀、二号刮刀以及三号刮刀，所述一号刮刀距离所述离型纸的间距为9cm,所述二号刮刀距离所述离型纸的间距为3cm, 所述三号刮刀距离所述离型纸的间距为0.6cm。所述烘箱加热离型纸的温度为120℃。
在使用的过程中，如果将生物基可降解聚氨酯树脂一步到位的涂刮在离型纸，容易导致气泡的形成，通过一号刮刀、二号刮刀以及三号刮刀与离型纸之间不同间距，使得生物基可降解聚氨酯树脂涂刮在离型纸上的效果得以提升，防止气泡的出现。
第六步：将薄膜与所述底胚贴合，再进行烘干，且烘干所述薄膜与底胚的温度为30℃，最后得到成品。
对半成品合成革表面完整度进行检验，方法一：用碳12同位素法测定有机物质含量大于35％；方法二：用荧光光谱仪测定重金属含量低于欧盟标准；方法三：用气像液像质谱仪测定DMF含量低于欧盟标准；方法四：用丛林测试法测定14天耐老化不破损。最后将合格的成品合成革进行收卷处理。
实施例2：
合成革贴面成品的制备步骤为：
第一步：直接在基布上涂布具有生物基可降解聚氨酯树脂的涂布浆料；涂布浆料为生物基可降解聚氨酯树脂65份，聚氨酯树脂35份，DMF100份，羧甲基纤维素7.5份，超细石墨烯7.5份，苎麻纤维粉7.5份，葡萄糖酸钙3.5份。
所述涂布浆料的制备流程为先将超细石墨烯、苎麻纤维粉、羧甲基纤维素、葡萄糖酸钙及DMF加入真空搅拌釜中以650r/min搅拌30min，之后加入生物基可降解聚氨酯树脂，生物基可降解聚氨酯树脂以1250r/min 搅拌90min，之后真空脱泡90min，最后用190目过滤以备用，制得涂布浆料。
生物基可降解聚氨酯树脂为生物基改性聚氨酯树脂，由水性生物基改性高固含多元醇以及生物基改性异氰酸酯组成，水性生物基改性高固含多元醇、生物基改性异氰酸酯的比例为2：3。
将水性生物基改性高固含多元醇与生物基改性异氰酸酯按比例充分混合后，在115℃温度下烘烤10min，制得生物基改性聚氨酯树脂。
第二步：使涂布浆料中的生物基可降解聚氨酯树脂在基布的表面凝固，且凝固的具体步骤为在温度为22.5℃的条件下，对基布的两侧均进行1.5h 的冷风风干凝固工序。
第三步：用清水水洗基布，洗净基布上的DMF，水洗基布的具体步骤为基布以0.5m/s的运动速度依次经过一号水池、二号水池、三号水池中，经过水池时基布浸没于水池中；一号水池中为食盐水，二号水池和三号水池均为清水。
需要说明的是，浸好浆料的基布通过设置动力辊装置进行连续输送，整个装置设置在所有水池的正上方，并且，由于第一水池、第二水池、第三水池之间相互隔开，基布在一定动力下运行时，整体呈波浪状，每两个动力辊之间的基布呈圆弧状，基布位于圆弧状的底部浸没于水池中，基布浸没于水池中的时间根据动力辊的运行速度来确定，动力辊的运动方式也可采取规律的间歇式运动，每一次运动的时长大于静止的时长，这样可使得基布每变动一次位置后便可相对延长在水池中浸没的时长，提高基布中 DMF的去除效果。
而且，由于基布呈圆弧状，浸没在水池中的基布由于倾斜角度的存在，在重力作用下，基布中的DMF会逐渐汇集在圆弧的底部，便于水池中的溶液和DMF充分混合。
动力辊每运转一次，基布浸没于水池中的幅长都是一致的，该幅长可以通过设定动力辊的运行速度和运行时间来控制，优化的，基布沿运行方向上以水面为对称面对称设置，浸没于水池中的幅长称为下半弧段，外露于水面上的幅长称为上半弧段，举例说明，每次运行后，上半弧段外露于水面上之后便会转换至浸没于水池中，此时为下半弧段，如此设置，当一个下半弧段在第一水池中进行第一次清洗之后，从第一水池露出变成上半弧段，再转变成下半弧段进入第二水池中进行第二次清洗，同理可得，之后同样以下半弧段进入第三水池进行第三次清洗。这样一来，整个基布均分成多段幅长一致的上半弧段或者下半弧段，处于下半弧段时便可进行对基布中DMF的清洗，处于上半弧段时便可在重力作用下使得基布中的DMF 汇集在下半弧段中，所有基布都能充分地被多次水洗，提高基布中DMF的去除效率。
而且此种水洗的方式好处在于，当基布运行过程中逐渐离开水池时，由于即将上行，此时，基布呈倾斜状态，水分在重力作用下会掉落，由于 DMF可以溶于水，内部的残余的DMF会随着水分在重力作用下与基布分离，更好地提高基布中DMF的去除效果。
综述，合理调整动力辊的工作参数以及布局基布的运行状态，便可使得基布进行连续式的多次清洗，也正是因为这样，基布的DMF的去除效果最好。
第四步：对基布进行预热、烫平、烘干、定型得到底胚，以140℃预热，烫平基布的时间为2min，烘干基布的温度为140℃，且基布的烘干时间为6min，定型基布的温度为140℃，时间为7s。
第五步：将溶剂型生物基可降解聚氨酯树脂涂刮到离型纸上，然后将涂刮有生物基可降解聚氨酯树脂的离型纸放入烘箱加热形成薄膜；所述离型纸依次经过一号刮机、二号刮机、三号刮机，所述一号刮机、二号刮机、三号刮机上分别包括一号刮刀、二号刮刀以及三号刮刀，所述一号刮刀距离所述离型纸的间距为8cm,所述二号刮刀距离所述离型纸的间距为2cm, 所述三号刮刀距离所述离型纸的间距为0.4cm。所述烘箱加热离型纸的温度为140℃。
在使用的过程中，如果将生物基可降解聚氨酯树脂一步到位的涂刮在离型纸，容易导致气泡的形成，通过一号刮刀、二号刮刀以及三号刮刀与离型纸之间不同间距，使得生物基可降解聚氨酯树脂涂刮在离型纸上的效果得以提升，防止气泡的出现。
第六步：将薄膜与所述底胚贴合，再进行烘干，且烘干所述薄膜与底胚的温度为40℃，最后得到成品。
对半成品合成革表面完整度进行检验，方法一：用碳12同位素法测定有机物质含量大于35％；方法二：用荧光光谱仪测定重金属含量低于欧盟标准；方法三：用气像液像质谱仪测定DMF含量低于欧盟标准；方法四：用丛林测试法测定14天耐老化不破损。最后将合格的成品合成革进行收卷处理。
实施例3：
合成革贴面成品的制备步骤为：
第一步：直接在基布上涂布具有生物基可降解聚氨酯树脂的涂布浆料；涂布浆料为生物基可降解聚氨酯树脂70份，聚氨酯树脂40份，DMF100份，羧甲基纤维素10份，超细石墨烯10份，苎麻纤维粉10份，葡萄糖酸钙5 份。
所述涂布浆料的制备流程为先将超细石墨烯、苎麻纤维粉、羧甲基纤维素、葡萄糖酸钙及DMF加入真空搅拌釜中以800r/min搅拌30min，之后加入生物基可降解聚氨酯树脂，生物基可降解聚氨酯树脂以1500r/min 搅拌120min，之后真空脱泡120min，最后用200目过滤以备用，制得涂布浆料。
生物基可降解聚氨酯树脂为生物基改性聚氨酯树脂，由水性生物基改性高固含多元醇以及生物基改性异氰酸酯组成，水性生物基改性高固含多元醇、生物基改性异氰酸酯的比例为2：3。
将水性生物基改性高固含多元醇与生物基改性异氰酸酯按比例充分混合后，在115℃温度下烘烤10min，制得生物基改性聚氨酯树脂。
第二步：使涂布浆料中的生物基可降解聚氨酯树脂在基布的表面凝固，且凝固的具体步骤为在温度为25℃的条件下，对基布的两侧均进行2h的冷风风干凝固工序。
第三步：用清水水洗基布，洗净基布上的DMF，水洗基布的具体步骤为基布以0.5m/s的运动速度依次经过一号水池、二号水池、三号水池中，经过水池时基布浸没于水池中；一号水池中为食盐水，二号水池和三号水池均为清水。
需要说明的是，浸好浆料的基布通过设置动力辊装置进行连续输送，整个装置设置在所有水池的正上方，并且，由于第一水池、第二水池、第三水池之间相互隔开，基布在一定动力下运行时，整体呈波浪状，每两个动力辊之间的基布呈圆弧状，基布位于圆弧状的底部浸没于水池中，基布浸没于水池中的时间根据动力辊的运行速度来确定，动力辊的运动方式也可采取规律的间歇式运动，每一次运动的时长大于静止的时长，这样可使得基布每变动一次位置后便可相对延长在水池中浸没的时长，提高基布中DMF的去除效果。
而且，由于基布呈圆弧状，浸没在水池中的基布由于倾斜角度的存在，在重力作用下，基布中的DMF会逐渐汇集在圆弧的底部，便于水池中的溶液和DMF充分混合。
动力辊每运转一次，基布浸没于水池中的幅长都是一致的，该幅长可以通过设定动力辊的运行速度和运行时间来控制，优化的，基布沿运行方向上以水面为对称面对称设置，浸没于水池中的幅长称为下半弧段，外露于水面上的幅长称为上半弧段，举例说明，每次运行后，上半弧段外露于水面上之后便会转换至浸没于水池中，此时为下半弧段，如此设置，当一个下半弧段在第一水池中进行第一次清洗之后，从第一水池露出变成上半弧段，再转变成下半弧段进入第二水池中进行第二次清洗，同理可得，之后同样以下半弧段进入第三水池进行第三次清洗。这样一来，整个基布均分成多段幅长一致的上半弧段或者下半弧段，处于下半弧段时便可进行对基布中DMF的清洗，处于上半弧段时便可在重力作用下使得基布中的DMF 汇集在下半弧段中，所有基布都能充分地被多次水洗，提高基布中DMF的去除效率。
而且此种水洗的方式好处在于，当基布运行过程中逐渐离开水池时，由于即将上行，此时，基布呈倾斜状态，水分在重力作用下会掉落，由于 DMF可以溶于水，内部的残余的DMF会随着水分在重力作用下与基布分离，更好地提高基布中DMF的去除效果。
综述，合理调整动力辊的工作参数以及布局基布的运行状态，便可使得基布进行连续式的多次清洗，也正是因为这样，基布的DMF的去除效果最好。
第四步：对基布进行预热、烫平、烘干、定型得到底胚，以160℃预热，烫平基布的时间为3min，烘干基布的温度为160℃，且基布的烘干时间为8min，定型基布的温度为160℃，时间为9s。
第五步：将溶剂型生物基可降解聚氨酯树脂涂刮到离型纸上，然后将涂刮有生物基可降解聚氨酯树脂的离型纸放入烘箱加热形成薄膜；所述离型纸依次经过一号刮机、二号刮机、三号刮机，所述一号刮机、二号刮机、三号刮机上分别包括一号刮刀、二号刮刀以及三号刮刀，所述一号刮刀距离所述离型纸的间距为7cm,所述二号刮刀距离所述离型纸的间距为1cm, 所述三号刮刀距离所述离型纸的间距为0.2cm。所述烘箱加热离型纸的温度为160℃。
在使用的过程中，如果将生物基可降解聚氨酯树脂一步到位的涂刮在离型纸，容易导致气泡的形成，通过一号刮刀、二号刮刀以及三号刮刀与离型纸之间不同间距，使得生物基可降解聚氨酯树脂涂刮在离型纸上的效果得以提升，防止气泡的出现。
第六步：将薄膜与所述底胚贴合，再进行烘干，且烘干所述薄膜与底胚的温度为50℃，最后得到成品。
对半成品合成革表面完整度进行检验，方法一：用碳12同位素法测定有机物质含量大于35％；方法二：用荧光光谱仪测定重金属含量低于欧盟标准；方法三：用气像液像质谱仪测定DMF含量低于欧盟标准；方法四：用丛林测试法测定14天耐老化不破损。最后将合格的成品合成革进行收卷处理。
以上均为本申请的较佳实施例，并非依此限制本申请的保护范围，故：凡依本申请的结构、形状、原理所做的等效变化，均应涵盖于本申请的保护范围之内。
Claims (9)
1.一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：所述成品的基布选用粘胶、锦纶混纺的水刺无纺布；
所述合成革贴面成品的制备步骤为：第一步为直接在基布上涂布具有生物基可降解聚氨酯树脂的涂布浆料；第二步为凝固，使涂布浆料中的生物基可降解聚氨酯树脂在基布的表面凝固；第三步为用清水水洗基布，洗净基布上的DMF；第四步以120-160℃预热、烫平、烘干、定型得到所述底胚；第五步将溶剂型生物基可降解聚氨酯树脂涂刮到离型纸上，然后将涂刮有生物基可降解聚氨酯树脂的离型纸放入烘箱加热形成薄膜；第六步将薄膜与所述底胚贴合，再烘干得到成品。
涂布浆料为生物基可降解聚氨酯树脂60-70份，聚氨酯树脂30-40份，DMF100份，羧甲基纤维素5-10份，超细石墨烯5-10份，苎麻纤维粉5-10份，葡萄糖酸钙2-5份。
2.根据权利要求1所述的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：所述涂布浆料的制备流程为先将超细石墨烯、苎麻纤维粉、羧甲基纤维素、葡萄糖酸钙及DMF加入真空搅拌釜中以500-800r/min搅拌30min，之后加入生物基可降解聚氨酯树脂，生物基可降解聚氨酯树脂以1000-1500r/min搅拌60-120min，之后真空脱泡60-120min，最后用180-200目过滤以备用，制得涂布浆料。
3.根据权利要求1所述的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：在第二步中，凝固的具体步骤为在温度为20-25℃的条件下，对基布的两侧均进行1-2h的冷风风干凝固工序。
4.根据权利要求1所述的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：在第三步中，水洗基布的具体步骤为基布以0.5m/s的运动速度依次经过一号水池、二号水池、三号水池中，经过水池时基布浸没于水池中；一号水池中为食盐水，二号水池和三号水池均为清水。
5.根据权利要求1所述的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：在第四步中，烫平基布的时间为1-3min，烘干基布的温度为120-160℃，且基布的烘干时间为4-8min，定型基布的温度为120℃-160℃，时间为5-9s。
6.根据权利要求1所述的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：在第五步中，所述离型纸依次经过一号刮机、二号刮机、三号刮机，所述一号刮机、二号刮机、三号刮机上分别包括一号刮刀、二号刮刀以及三号刮刀，所述一号刮刀距离所述离型纸的间距为7-9cm,所述二号刮刀距离所述离型纸的间距为1-3cm,所述三号刮刀距离所述离型纸的间距为0.2-0.6cm。
7.根据权利要求1所述的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：在第五步中，所述烘箱加热离型纸的温度为120-160℃。
8.根据权利要求1所述的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：在第六步中，烘干贴合的所述薄膜与底胚的温度为30-50℃。
9.根据权利要求1所述的一种生物基可降解渗透水刺布聚氨酯合成革贴面成品，其特征在于：所述水刺无纺布中粘胶、锦纶混纺的比例为1:1。