CN1521145A - 建筑卫生陶瓷用金属光泽结晶釉 - Google Patents
建筑卫生陶瓷用金属光泽结晶釉 Download PDFInfo
- Publication number
- CN1521145A CN1521145A CNA031180906A CN03118090A CN1521145A CN 1521145 A CN1521145 A CN 1521145A CN A031180906 A CNA031180906 A CN A031180906A CN 03118090 A CN03118090 A CN 03118090A CN 1521145 A CN1521145 A CN 1521145A
- Authority
- CN
- China
- Prior art keywords
- glaze
- ceramic
- oxide
- crystalline glaze
- crystalline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种建筑卫生陶瓷用金属光泽结晶釉，它以氧化锌、氧化硅或氧化钛为釉的成晶物质，以低温熔块、硼酸为形成釉玻璃体的熔剂原料，以氧化铜、氧化铁、氧化锰、氧化钛等金属氧化物为着色剂，通过普通的陶瓷釉料生产工艺进行制备，施于建筑卫生陶瓷的表面，通过适合的快速连续烧成，采用短保温育晶周期的特殊温度曲线，使釉面形成具有金属光泽的微晶玻璃层，这样它既有金属光泽的装饰效果，又具有微晶玻璃的机械强度，可广泛应用于各种建筑陶瓷、卫生陶瓷洁具的表面装饰。
Description
本发明属于一种建筑卫生陶瓷装饰用新釉质。
在建筑卫生陶瓷领域目前普遍采用玻璃质色釉装饰，这些色釉具有和坯体配合较好，花色繁多，价格低廉等特点，但它存在釉面较软，不能形成金属光泽等缺陷。结晶釉技术在日用艺术陶瓷中也应用，但它只是在釉面上分布着星形、针状或花叶形粗大聚晶体的一种装饰釉，亦不能形成全釉面的金属色泽。现在随着人们对建筑卫生陶瓷装饰艺术要求的不断提高，各企业不断推出各种仿石材的产品，但都尚未开发出仿金属光泽的建筑卫生陶瓷产品。
本发明的目的是研制一种仿金、银、铜等金属表面光泽的建筑卫生陶瓷用新釉料。
本发明的技术内容主要是解决釉的配方问题，根据泰曼析晶理论，熔体析晶首先要有处于过饱和状态的成晶物质，以形成晶核；其次是熔体冷却时，须在该物质的析晶温度范围内进行保温，以使晶核发育成长，而保温温度和保温时间的不同选择，又可以控制晶花的大小和形状。仿金属光泽结晶釉在一定的烧成制度下，能产生晶花，晶花规格包括大、中、小、微晶花，晶花单位数量、分布密度可以通过晶种比例、釉料量、烧成制度等工艺措施得以控制。大、中、小、晶花由于晶片的光线折射作用，产生反光效果，通过金属氧化物着色，形成各种颜色的光泽。本发明就是利用晶花的这种反光特性，从配方上研制出适合建筑卫生陶瓷成瓷范围的结晶釉配方，其中氧化锌、氧化硅和氧化钛为上述釉的成晶物质；低温熔炔、硼酸为形成釉玻璃体的熔剂原料；氧化铜、氧化铁、氧化锰、氧化钛等为着色剂，使釉玻璃和晶花着色。由于本发明结晶层较厚，晶粒分布均布，相当于在坯体表面形成一个微晶玻璃层，大大提高了釉层的机械强度，从而把釉面砖提升到了抛光砖的档次水平。
本发明的目的是这样实现的：将结晶釉的成晶物质，形成釉玻璃体的熔剂原料及金属氧化物着色剂按一定比例混合，通过一般陶瓷用釉的制备方式进行制作而成。
金色光泽结晶釉料配方重量百分组成是：
低温熔块：30～75％ 硼酸：0.1～3％ 氧化锌：20～35％
氧化钛：1～35％ 氧化铜：0.1～0.5％
铜色光泽结晶釉料配方重量百分组成是：
低温熔块：30～75％ 硼酸0.1～3％ 氧化锌：20～35％
氧化钛：1～35％ 氧化铁：0.5～5％ 氧化锰：0.5～3％
银色光泽结晶釉料配方重量百分组成是：
低温熔块30～75％，硼酸0.1～0.3％，氧化锌20～35％
氧化铜0.1～2.5％
该组配方用的低温熔块包括玻璃、硼熔块、铅熔块和铅硼熔块的一种。
与现有技术相比，本发明有下列特点：
1、利用了结晶釉中晶花晶片的反光效果，生产出具有金属光泽的釉面，使得建筑卫生陶瓷的表面装饰效果更丰富，是一个全新的领域。
2、由于该结晶釉相当于在坯体上形成了一层微晶玻璃，大大提高了釉面的机械强度，如施于地板砖上，将把釉面砖提升到抛光砖的档次水平。
实施例一：金色光泽结晶釉料配方重量百分组成是：
低温熔块：65％ 硼酸：2％ 氧化锌：26％
氧化钛：6.6％ 氧化铜：0.4％
实施例二：铜色光泽结晶釉料配方重量百分组成是：
低温熔块：65％ 硼酸：2％ 氧化锌：26％
氧化钛：4％ 氧化铁：1.5％ 氧化锰：1.5％
实施例三：银色光泽结晶釉料配方重量百分组成是：
低温熔块：65％ 硼酸：2.5％ 氧化锌：31％
氧化铜：1.5％
上述釉料制备工艺控制指标为：
1、釉料细度：万孔筛余0.01～1.5％
2、釉料浓度：15～75％
3、施釉厚度：0.01～5.0mm
4、施釉方式：淋、浸、喷、甩釉均可。
将上述釉料施于地板砖上进行烧成时，其烧成辊道窑的升温曲线是：
常温→800～1300℃ 20～60mim；
800～1300℃→ 600～1220℃ 1～60mim；
在600～1220℃保温时间：5～120mim。
Claims (4)
1、一种建筑卫生陶瓷用金属光泽结晶釉，其特征在于：该结晶釉料的基本百分组成份及配比为：
原 料： 配比(wt％)
低温熔块： 30～75％
硼 酸: 0.1～3％
氧 化 锌： 20～35％
2、根据权利要求1所述的建筑卫生陶瓷用金属光泽结晶釉，其特征在于：呈金色光泽的结晶釉是在其基本配比中加入了1～35％氧化钛和0.1～0.5％氧化铜。
3、根据权利要求1所述的建筑卫生陶瓷用金属光泽结晶釉，其特征在于：呈铜色光泽的结晶釉是在其基本配比中加入了1～35％氧化钛、0.5～5％氧化铁和0.5～3％氧化锰。
4、根据权利要求1所述的建筑卫生陶瓷用金属光泽结晶釉，其特征在于：呈银色光泽的结晶釉是在其基本配比中加入0.1～2.5％的氧化铜。