CS252013B1 - Polypropylene products with increased light stability and whiteness - Google Patents
Polypropylene products with increased light stability and whiteness Download PDFInfo
- Publication number
- CS252013B1 CS252013B1 CS843031A CS303184A CS252013B1 CS 252013 B1 CS252013 B1 CS 252013B1 CS 843031 A CS843031 A CS 843031A CS 303184 A CS303184 A CS 303184A CS 252013 B1 CS252013 B1 CS 252013B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- weight
- whiteness
- compounds
- polypropylene products
- polypropylene
- Prior art date
Abstract
Výrobky z polypropylénu so zvýšenou světelnou stálosťou a belosťou, obsahujúce do 2 % hmotnostných oxidu titaničitého a ďalej 0,005 až 0,2 % hmotnostných optického stilbenbenzotriazolového zjasňovacieho prostriedku, 0,01 až 0,5 % hmotnostných aspoň jedného stabilizátora, obsahujúceho stéricky chráněný dusík, a/alebo 0,01 až 0,5 pere. hmotnostných trilauryltritiofosfitu, pričom obsah jednotlivých zložiek je vztiahnutý na hmotnost celej zmesi.Polypropylene products with increased light fastness and whiteness, containing up to 2% by weight of titanium dioxide and further 0.005 to 0.2% by weight of a stilbene benzotriazole optical brightener, 0.01 to 0.5% by weight of at least one stabilizer containing sterically protected nitrogen, and/or 0.01 to 0.5% by weight of trilauryl trithiophosphite, the content of the individual components being based on the weight of the entire mixture.
Description
252013
Vynález sa týká výrobkov z polypropylé-nu so zvýšenou světelnou stálosťou a belos-ťou za použitia optických zjasňovacích pro-striedkov na báze stilbenbenzotriazolu.
Zvýšenie bělosti polypropylénových vý-robkov sa bežne dosahuje prídavkom mato-vacích prostrledkov, například oxidu titani-čitého, a optických zjasňovacích prostrled-kov. Váčšina optických zjasňovacích pro-striedkov, i keď je účinná, vykazuje nízkésvětelné stálosti, najma u polypropyléno-vých vláken, i keď u ostatných polymérovsú tieto stálosti vysoké. Přitom nedochádzak migrácii zjasňovacieho prostriedku na po-vrch. Najvyšší stupeň bělosti a najlepšiestálosti na svetle sa dosahujú optickýmizjasňovacími prostriedkami na báze stilben-benzotriazolu. Účinnost je závislá i od kon-centrácie zjasňovacieho prostriedku. Tátosa pohybuje obvykle v hraniciach od 0,1 %do 0,5 % hmotnostných. U zjasňovacích prostriedkov na báze stil- benbenzotriazolu je táto hranica znížená,pričom optimálně koncentrácie sa pohybu-jú od 0,005 % do 0,2 % hmotnostných. I keď zjasňovacie prostrledky na báze stil-benbenzotriazolu sú najvhodnejšie, bežnesa nedosahujú světelné stálosti, požadova-né spracovatel'mi, a pohybujú sa na úrovni
4. až 5. stupňa modrej stupnice, čo je stu-peň nízký a teda nevyhovujúci. Uvedené ne-dostatky odstraňuje předložený vynález.Predmetom vynálezu sú výrobky z polypro-pylénu so zvýšenou světelnou stálosťou abelosťou, obsahujúce do 2 % hmotnostnýchoxidu titaničitého a 0,005 % až 0,2 % hmot-nostných optického stilbenbenzotriazolovéhozjasňovacieho prostriedku, vyznačujúce satým, že ďalej obsahujú (1) 0,01 % až 0,5 %hmotnostných aspoň jedného zo stabilizá-torov, obsahujúcich stéricky chráněný du-sík, zvoleného zo skupiny, zahrňujúcej zlú-čeniny obecného vzorca A
~t~ Bu.
OH (A)
kde t-Bu je terciárny butyl, zlúčeniny nabáze 2, 2, 6, 6-tetrametyl piperidínu, obec-ného vzorca B
(B) kde Y je vodík alebo metyl, A je acyl odvodený od nasýtenej alebo
nenasýtenej karboxylovej kyseliny so 6 až18 atómami uhlíka alebo ich zmes a zlúče-niny obecného vzorca C 232013
CH^ ch3 C CM,I ° 6
kde n je číslo, odpovedajúce priemernej mo-lekulovej hmotnosti 1 500 až 3 000 a/alebo(2) 0,01 % až 0,5 % hmotnostných trilau-ryltritiofosfitu, pričom obsah jednotlivýchzložiek je vztiahnutý na hmotnost celej zme-si.
Za použitia kombinácie stabilizátorov po-dlá vynálezu sa světelné stálosti zvýšia mi-nimálně o dva stupně modrej stupnice. Pře stabilizáciu polypropylénu sa použí-vají! rožne skupiny tepelných a světelnýchstabilizátorov, účinkom ktorých sa zvyšu-je odolnost výrobkov z polypropylénu vočistárnuíiu. Například stabilizátory na bázebenzotriazolu, benzofenonu, fenolu. Zistilisme však, že tieto stabilizátory, ktoré sa.dodnes obecne používajú, neovplyvňujú vpodstatě stálosti na svetle opticky zjasně-ného polypropylénu. Priaznivý vplyv sa pre-javuje len prídavkom uvedených stabilizá-torov, kedy možno hovořit o sinergickom e-fekte týchto stabilizátorov. Příklad 1
Boli připravené vlákna z polypropylénu,ku ktorému bol přidaný stabilizačný systém,pozostávajúci z trilauryltritiofosfitu, aj z lá-tok zo stéricky chráněným dusíkom. Obsahoxidu titaničitého bol 0,5 % hmotnostnýcha obsah optického stilbenbenzotriazolovéhozjasňovacieho prostriedku (Hostalux KSN) 0,0,5 % hmotnostných. Vlákna boli hodno-tené z hladiska stupňa bělosti na přístrojiElrephomat DFC 5 v porovnaní so síranombarnatým ako štandardom a z hradiska sve-telnej stability na přístroji Xenotest 450 ahodnotené podl'a modrej stupnice. Zloženiapolymérov a výsledky hodnotenia stupňabělosti a svetlostability sú uvedené v tabul’-ke č. 1 a 2.
Stálosti na svetle u všetkých připrave-ných a hodnotených vzoriek s obsahom. fos-fitického stabilizátora alebo stabilizátorov,obsahujúcich stéricky chráněný dusík, jed-noznačné vykazovali stálosti zodpovedajú-ce 7. stupňu modrej stupnice a vyššie, kdeznačí: TLTTP — tritauryltritiofosfit Y1 — zmes oktananu zinočnatého a 4,4‘-bu-tylidén-bis (3-metyl-6-terc.butylf enyl-di-3--decylfosfit) (Mark Q 158) X2 — stabilizátor obecného vzorca B, kdeY je vodík a A je acyl od kyseliny propio-novej X3 — stabilizátor obecného vzorca C, kden odpovedá priemernej molekulovej hmot-nosti 2 000 (Chimasorb 944) XI — stabilizátor obecného vzorca A(Good-rite 3 114) Y2 — stabilizátor benztriazolový (Tinuvin327)
W BASF — bělost podía BASF W B — bělost podlá Bergera WS — bělost podl'a Stensbyho. 252013
Tabulka č. 1 Názov zložky Obsah zložiek(hmotnostně %) Polypropylén značky Tatren HPF 99,5 99,5 99,6 99,7 99,4 99,4 TLTTP 0,3 0,3 — — — — Y1 -- 0,1 0,2 — — — Y2 0,1 0,1 0,1 0,2 — — 2,6-diterc.butyl-p-krezol 0,1 — 0,1 0,1 0,1 0,1 XI — — — — 0,05 0,05 X2 — — — — 0,3 — Stěaran vápenatý — — — — 0,1 0,1 bis-diterc.butylperoxid — — — — 0,05 0,05 X3 — — — — — 0,3 Číslo vzorky 1 2 3 4 5 6 Tabulka č. 2 Vzorka W BASF WB WS Svetlostabilita BaSO4 95,2 95,5 97,4 — 1 94,7 93,1 99,4 7 2 92,8 90,8 99,1 7 3 94,4 93,3 98,4 6 4 86,8 85,4 95,3 5—6 5 93,9 91,2 100,5 8—7 6 95,1 92,8 100,6 8—7 Příklad 2 zotriazolového optického zjasňovacieho pro- striedku a stabilizačný systém lzoženia u- Bolí připravené vlákna z polypropylénu, vedeného v tabulke č. 1. Výsledky stupňa obsahujúce 0,5 % hmotnostných oxidu tita- bělosti a svetlostability sú uvedené v tabu!- ničitého, 0,15 % hmotnostných stilbenben- ke č. 3. Tabulka č. 3 Vzorka W WB WS Svetlostabilita BASF BaSO4 95,3 95,5 97,5 _ 1 95,0 93,5 100,1 7 2 93,0 91,1 99,7 7 3 94,6 93,7 99,4 6 4 87,0 85,6 95,8 5—6 5 94,2 91,5 101,2 8—7 6 95,4 93,1 101,4 8—7
252013
BACKGROUND OF THE INVENTION The present invention relates to polypropylene products with enhanced light fastness and whiteness using optical brightening agents based on stilbenzotriazole.
An increase in the whiteness of the polypropylene articles is commonly achieved by the addition of matting agents such as titanium dioxide and optical brighteners. The optical brightening agent, although effective, exhibits low light fastnesses, especially for polypropylene fibers, although these are high in other polymers. There is no migration of the brightener to the surface. The highest degree of whiteness and lightness is achieved by optical brightening agents based on stilbenzotriazole. Efficiency also depends on the concentration of the brightener. Typically, the titanium ranges from 0.1% to 0.5% by weight. For stilbenzotriazole-based brighteners, this limit is reduced, with optimum concentrations ranging from 0.005% to 0.2% by weight. Although stilbenzotriazole-based brightening agents are most suitable, they do not normally achieve the light fastness required by the processors and are at the level of
4 to 5 degrees blue scale, which is low and therefore unsatisfactory. SUMMARY OF THE INVENTION The present invention relates to polypropylene products having increased lightfastness and abrasion, containing up to 2% by weight of titanium oxide and 0.005% to 0.2% by weight of an optical stilbene benzotriazole brightener, further comprising: 1) 0.01% to 0.5% by weight of at least one of the stabilizers comprising a sterically protected radical selected from the group consisting of compounds of Formula A
~ t ~ Bu.
OH (A)
wherein t-Bu is tertiary butyl, the compound is 2,2,2,6-tetramethyl piperidine of the general formula B
(B) wherein Y is hydrogen or methyl, A is acyl derived from saturated or
unsaturated carboxylic acid of 6 to 18 carbon atoms or a mixture thereof and compounds of formula C 232013
CH 2 CH 3 C CM, I ° 6
wherein n is a number corresponding to an average molecular weight of 1,500 to 3,000 and / or (2) 0.01% to 0.5% by weight of trilaryltrithiophosphite, the content of the individual components being based on the weight of the total.
Using the combination of stabilizers of the invention, the light fastnesses are increased by at least two degrees of blue. Pre-stabilization of polypropylene is used! spit groups of heat and light stabilizers, which increase the resistance of polypropylene products to purification. For example, basebenzotriazole, benzophenone, phenol stabilizers. However, it has been found that these stabilizers, which are generally used today, do not substantially affect the light-fastness of the optically brightened polypropylene. The beneficial effect is shown only by the addition of said stabilizers, whereby the sinergic e-infection of these stabilizers can be mentioned. Example 1
Polypropylene fibers were prepared, to which a stabilizing system consisting of trilauryl tritiophosphite and also from a sterically protected nitrogen was added. The titanium tetroxide content was 0.5% by weight and the content of the optical stilbene benzotriazole brightener (Hostalux KSN) was 0.0.5% by weight. The fibers were evaluated for whiteness on the Elrephomat DFC 5 instrument compared to the sulphonate standard and the light stability on the Xenotest 450 and rated on the blue scale. The composition of the polymers and the results of grading and lightness rating are shown in Tables 1 and 2.
Lightfastness of all prepared and evaluated content samples. phospholytic stabilizer or stabilizers containing sterically protected nitrogen clearly exhibited a 7-degree blue scale stability and higher, indicating: TLTTP-tritauryltrithiophosphite Y1 - a mixture of zinc octanate and 4,4'-butylidene bis ( 3-methyl-6-tert-butylphenyl-di-3-decylphosphite) (Mark Q 158) X2 - stabilizer of general formula B where Y is hydrogen and A is acyl from propionic acid X3 - stabilizer of formula C, corresponds to an average molecular weight of 2,000 (Chimasorb 944) XI - a stabilizer of formula A (Good-rite 3 114) Y2 - a benzotriazole stabilizer (Tinuvin327)
W BASF - whiteness according to BASF WB - whiteness according to Berger WS - whiteness according to Stensby. 252013
Table 1 Name of component Ingredients content (% by weight) Polypropylene Tatren HPF 99.5 99.5 99.6 99.7 99.4 99.4 TLTTP 0.3 0.3 - - - - Y1 - 0, 1 0,2 - - - Y2 0,1 0,1 0,1 0,2 - - 2,6-di-tert-butyl-p-cresol 0,1 - 0,1 0,1 0,1 0,1 XI - - - - 0,05 0,02 X2 - - - - 0,3 - Calcium stearate - - - - 0,1 0,1 bis-di-tert-butyl peroxide - - - - 0,05 0,03 X3 - - - - - 0.3 Sample number 1 2 3 4 5 6 Table No. 2 Sample W BASF WB WS Lightfastness BaSO4 95.2 95.5 97.4 - 1 94.7 93.1 99.4 7 2 92.8 90 , 8 99.1 7 3 94.4 93.3 98.4 6 4 86.8 85.4 95.3 5—6 5 93.9 91.2 100.5 8—7 6 95.1 92.8 100.68-7 Example 2 of a zotriazole optical brightener and a stabilizing system of lozenge. Prepared polypropylene fibers as shown in Table 1. The results of the step containing 0.5% w / w of titanium dioxide and lightfastness are given in 0.15% by weight of stiffener 3. Table 3 Sample W WB WS Lightfastness BASF BaSO4 95.3 95.5 97.5 _ 1 95.0 93.5 100.1 7 2 93.0 91.1 99.7 7 3 94.6 93,7 99,4 6 4 87,0 85,6 95,8 5—6 5 94,2 91,5 101,2 8—7 6 95,4 93,1 101,4 8–7
Claims (1)