CS253790B1 - Preparat for the colouring of flagstones - Google Patents
Preparat for the colouring of flagstones Download PDFInfo
- Publication number
- CS253790B1 CS253790B1 CS857248A CS724885A CS253790B1 CS 253790 B1 CS253790 B1 CS 253790B1 CS 857248 A CS857248 A CS 857248A CS 724885 A CS724885 A CS 724885A CS 253790 B1 CS253790 B1 CS 253790B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- colouring
- composition
- added
- urea
- weight
- Prior art date
Abstract
Description
Vynález řeší složení a způsob přípravy přípravku pro barvení zejména režných dlaždic před výpalem sítotšskovou nebo jinou technikou, který umoonuje vytvoření barevného dekoru o stejné intenzitě probarvení na povrchu i v hloubce střepu do min. 0,5 mm.SUMMARY OF THE INVENTION The present invention solves the composition and method of preparing a composition for dyeing, in particular, gray tiles before firing by screening or other techniques, which allows to create a color decor with the same color intensity on the surface and in the shard depth up to min. 0.5 mm.
Známé přípravky pro barvení keramických výrobků na roztoků nebo suspenzí barvotvorných kovů ve formě solí nebo oxidů neumokňují v případě suspenzí homogenní probarvení střepu do větších hloubek, u roztoků solí pak dochází při nanesení větší vrstvy a zejména po zahřátí, k narušení syrového výlisku vlíeem kysseoosi těchto roztoků, která pocházi z určité volné kyseeooti sooí nebo je důsledkem jejích řydrokytickýcř, koiuppexotvorných nebo oxidačněredukčních reakcí. Přítomnost látek regulující viskozitu, jako derivátů celulózy, škrobu, přírodních či syntetických'polymerů, způsobuje zadržování barvicího média na povrchu výlisku a tím ieřomPkunitu probarvení.'Pro případ poiuití nejběžnějších anoruanických soU není řešena otázka vznikajících exhalací. .Known preparations for coloring ceramic products into solutions or suspensions of coloring metals in the form of salts or oxides do not provoke a homogeneous colouration of the shard to greater depths in the case of suspensions; which originates from or is the result of certain rhazocystic, co-exogenous or oxidation-reducing reactions. The presence of viscosity regulating agents such as cellulose derivatives, starch, natural or synthetic polymers causes retention of the staining medium on the molding surface and hence discolouration. In the case of the use of the most common anorulanic salts, the issue of exhalation is not addressed. .
podle vynálezu přípravky pro barvení režných dlaždic na bázi ulycerínových roztoků solí barvotvořných kovů obsahuj 1-30 % řpoknoktních mmooviny nebo t^e^no^mi^ nebo jejich smě^ěí. Tyto bázické přísady neeuraHzuuí kyselost roztoků solí barvivových kovů, čímž nedochází k narušení základní keramické hmooy. Jako sooí barvotvorných kovů se s výhodou ponu-íje dusičnanů; za pří^omno^i ppkooiiy nedochází ke vzniku oitrózoích plynů, ale rozklad probíhá za vývoje dusíku, oxidu dusoatého, vody a oxidu uhřičitéřo. Potřebné iiskkzity přípravku v rozmezí 0,1-10 Pas podle pkuliré techniky nanášení, se dosáhne změnou obsahu vody, povrchové oapěěí se sníží přídavkem 0,1-5 % ^0^0^1 povrchově aktivní látky, čímž se dosáhne dokonalého přilnutí přípravku k. výlisku a rovnoměrného vsáknouí. Při přípravě přípravku na bázi roztoků dusičnanů za vývoje οί^02:οί^ plynů. BajZfiSujíií látky se dávkuj do roztoků solí tarvotivový^ kovů až po přppadném zahuštění při teplot 2°^110 °C, aby nedocházelo k jejich nežádoucímu rozkladu, resp. těkání.According to the invention, the dyeing compositions based on ulycerin solutions of color-forming metal salts contain 1-30% of squamous or thiourea or mixtures thereof. These basic additives do not reduce the acidity of the dye metal salt solutions, thereby avoiding the disruption of the basic ceramic mass. Nitrates are preferably provided as the coloring metal salt; however, decomposition takes place with the development of nitrogen, nitric oxide, water and carbon dioxide. The required viscosity of the formulation in the range of 0.1-10 Pas according to a spherical application technique is achieved by changing the water content, the surface treatment is reduced by the addition of 0.1-5% ^ 0 ^ 0 ^ 1 surfactant, thereby achieving a perfect adhesion of the formulation to the molding and uniform absorption. In the preparation of a preparation based on nitrate solutions with the development of οί ^O 2: οί ^ gases. BajZfiSujíií substances are metered into the salt solution to tarvotivový s ^ s after Pr P fits concentrate of the beta 2 degrees s ^ 1 10 ° C, b y to avoid their unwanted decomposition, respectively. volatilization.
Předmětem vynálezu je tedy přípravek pro barvení režných dlaždic před výpalem na bázi Ulycerinových roztoků solí bariorvkroých kovů s výhodou dusičnanů, který se vyznačuje tím, že jako celek obsahuje hpptnostoě 1 až 30 % mokčoiny anebo treeřlanklapiol.Accordingly, the present invention provides a pre-firing dye composition based on Ulycerin solutions of barrier metal salts, preferably nitrates, characterized in that it contains as a whole from 1 to 30% of wetland and / or tree-lapiol.
Přípravek pro barvení režných dlaždic podle vynálezu umočnuje rovnoměrné proba^ení keramické hmoty min. do 0,5 mm bez jejího narušení, přikemž vsáknuuí barvy lze uryc^lt zvýšením teploty. S výhodou lze pouužt barev na bázi roztoků dusičnanů barvivových kovu v ko^t^bi^^c^:^ s moOioinou, je^kcž při výpalu oevvzikkií škodlivé exhřláty. Regulace iisk<lzity barev obsahem vody nezpůsobuje nežádoucí zadržování bariorvorného média na povrchu zdobeného palrriáll, účinné snížení povrchového oappěí přídavkem povrchově aktivní látky zameeuje nerovnoměrnému plošnému probarvení a urychluje vsakování barvy do výlisků. Jako barvivových sod je vzhledem k batikujícím příaadám umožněno pouužt vysoce rozpustných chloridů a s výhodou dusičnanů, čímž lze dosáhnout vysoké intenzity probarvení.The dyeing composition for the gray tiles according to the invention allows a uniform penetration of the ceramic mass of min. up to 0.5 mm without disturbing it, and the ink can be absorbed by increasing the temperature. Advantageously, dyes based on dye metal nitrate solutions in the form of a moiety can be used, which is harmful to the exfoliates when fired. The regulation of the color lysis by the water content does not cause undesirable retention of the barrier-forming medium on the decorated ornamental surface, effectively reducing the surface oappiness by the addition of a surfactant prevents uneven surface coloration and accelerates the infiltration of the paint into the moldings. Highly soluble chlorides and preferably nitrates are used as dye soda due to the batting additives, thereby achieving a high color intensity.
Příklady provedeníExamples
1. Ve 300 g 94% u^ce^i-ou se po částech akzρuj;tí za máchání a za zahřívání 500 u hexa- hydrátu cřlkailu Železitéřk, roz^ se uvede k varu a vaříí se do dksažeoé tepoty varu 125° Celsia. Při^dá se 200 g 94% ^ceriou, čími se roz^ юМкИ oa 00a 100 °C po lstech se přidá 100 u tretlonolapiol. SmPs se míchá do rozpuštění hydroxidu želez^tého, vzniklého lkkál^i:^p př·esyceoíp, rozti se исЮк1! pod tupl^u 50 °C a barva se přeiedl do ^l^tři^eno^ (ΡΕ) lahve. ZÍská se 1 barvy o vistozi^ 4,5-5,0 Pas při 20 °C.1. 300 g of 94% u ^ CE ^ i-ou portions akzρuj; three for rinsing and heating at 500 h ydr hexa- and TU lkai c R l R k at Ferric née ^ is brought to the boil and to dksa, EO é boiling interior temperatures of 125 ° Celsius. When ^ d 00 and 2 g of 9 ^ 4% ceria No COMES also be extended юМкИ ^ oa 00a 1 00 ° C at about 100 lstech added at tretlonolapiol. SMPS is stirred until dissolution-iron hydroxide oxide, the resulting L kk l ^ i ^ p p R · y ceoíp es, thaw the исЮк 1! p from tuple-at 50 ° C and b are olor řeiedl P ^ l ^ into three eno ^ ^ (ΡΕ) bottle. ZIS Ka 1 b y o vistozi ARV-4, 5-5, 0 Pas p s 20 ° C.
2. Do 350 u 94% u^yculou se přidá 50 u ppkokioy . a směs se za míchání zahřívá. V průběhu zahříváoí se po částech přidá 500 u hexahydrátu Iusíčoiou oiSeloltéřk a 100 u hexahydrátu dusičnanu kobalrolrého. Vzniklý roztok se za míchání uvede k varu a vaří až do dosaženi teploty varu 140 °C. Zahuštěoý roz^ se юЮк1! oa te^iu 60 °C, při^ se 15° u ppkikiny a směs se míchá do jejího rozpuštění. Pcté se přidá 5 u saponátového přípravku a po nhoppoul0zování se barva převede do PE-lahve. ZÍská se 1 barvy o vis^ziO 4,0-O0 Pas při 20 °C.2. To 350 µl of 94% cellulose, add 50 µl of coccoyl. and the mixture is heated with stirring. During zahříváoí added portionwise at 500 hexahydro y wire Iusíčoiou oiSeloltéřk hexahydrate and 100 y wire nitrate co alrolrého b. The resulting solution was stirred and brought to boil and boiled until a pulse of the L boiling 140 ° C. Of concentrated oy ^ is extended юЮк 1! oa te ^ even 60 ° C, 1 ^ 5 ° for PP to Ikin y and stirred until dissolved. Five times, 5 µl of detergent composition is added and, after interpolating, the color is transferred to a PE bottle. Gain and y 1 Color VIS-ZIO 4 0- 0 O p s 2 Pas 0 ° C.
3. Do 370 g 94% glycerinu se přidá 50 g močoviny a směs se za míchání zahřívá. V průběhu zahřívání se po částech přidá 600 g hexahydrátu dusičnanu kobaltnatého, vzniklý roztok se za míchání uvede к varu a vaří až do dosažení teploty varu 140 °C. Zahuštěný roztok se ochladí na teplotu 60 °C, přidá se 100 g močoviny, 50 g trietanolaminu a směs se míchá do jejího rozpuštění. Přidá se 5 g saponátového přípravku, roztok se ochladí pod teplotu 40 °C a zhomogenizuje se s 200 g barvy podle příkladu 4. Získá se 1,2 kg barvy o viskozitě 4,0-5,0 Pas při 20 °C.3. To 370 g of 94% glycerin is added 50 g of urea and the mixture is heated with stirring. During the heating, 600 g of cobalt nitrate hexahydrate are added in portions, the solution is brought to boiling under stirring and boiled until a boiling point of 140 ° C is reached. The concentrated solution is cooled to 60 ° C, 100 g of urea, 50 g of triethanolamine are added and the mixture is stirred until dissolved. 5 g of detergent composition is added, the solution is cooled below 40 ° C and homogenized with 200 g of the paint of Example 4. 1.2 kg of paint having a viscosity of 4.0-5.0 Pas at 20 ° C are obtained.
4. Ke 250 g 99% glycerinu se přidá 20 g močoviny a za míchání se ve směsi po částech rozpustí 600 g trihydrátu dusičnanu mědnatého zahřátím na teplotu 70 °C. Po ochlazení na teplotu 45 °C se к roztoku přidá 120 g močoviny a směs se míchá do jejího rozpuštění. Poté se přidá 15 g saponátového přípravku a po zhomogenizování se barva převede do PE-lahve. Získá se 1 kg barvy o viskozitě 3,5-4,5 Pas při 20 °C.4. To 250 g of 99% glycerin, 20 g of urea are added and 600 g of copper nitrate trihydrate are dissolved in portions with stirring at 70 ° C while stirring. After cooling to 45 ° C, 120 g of urea are added to the solution, and the mixture is stirred until dissolved. 15 g of detergent is then added and after homogenization the color is transferred to a PE bottle. 1 kg of paint having a viscosity of 3.5-4.5 Pas at 20 ° C is obtained.
Claims (2)