DD221994A1 - HYDROPHOBIC GIP BONDING AGENT FOR USE IN MOISTURE - Google Patents
HYDROPHOBIC GIP BONDING AGENT FOR USE IN MOISTURE Download PDFInfo
- Publication number
- DD221994A1 DD221994A1 DD25923484A DD25923484A DD221994A1 DD 221994 A1 DD221994 A1 DD 221994A1 DD 25923484 A DD25923484 A DD 25923484A DD 25923484 A DD25923484 A DD 25923484A DD 221994 A1 DD221994 A1 DD 221994A1
- Authority
- DD
- German Democratic Republic
- Prior art keywords
- weight
- parts
- gypsum
- hydrophobic
- water
- Prior art date
Abstract
Die Erfindung, ein hydrophobes Gipsbindemittel, wird insbesondere für den Einbau und Ausbau von Gipskartonplatten für Feuchträumen verwendet. Es handelt sich um eine Zweikomponentenmischung mit dem Feststoffanteil eines hydrophoben Branntgipses oder Gipshalbhydrates und/oder angeregten Anhydrits. Der Flüssiganteil besteht aus einer wässrigen Montanwachsemulsion und einem Emulgator. Durch Änderung der Konsistenz lässt sich das hydrophobe Gipsbindemittel entsprechend den Erfordernissen als Fugenfüller, Ansetzbinder, Spachtel-, Verguss- oder Ausgleichsmasse zum Ausbau von Feuchträumen einsetzen.The invention, a hydrophobic gypsum binder, is used in particular for the installation and removal of plasterboard for wet rooms. It is a two-component mixture with the solids content of a hydrophobic gypsum or gypsum hemihydrate and / or excited anhydrite. The liquid fraction consists of an aqueous Montanwachsemulsion and an emulsifier. By changing the consistency, the hydrophobic gypsum binder can be used according to the requirements as a joint filler, Ansetzbinder, filler, potting or leveling compound for the expansion of wet rooms.
Description
Die Erfindung betrifft einen Fugenfüller, eine Spachtel-, Verguß- oder Ausgleichsmasse und/oder Ansetzbinder, insbesondere für den Ausbau von Feuchträumen unter Verwendung von zwei Komponenten, einem Calciumsulfatbindemittel und/oder angeregtem Anhydrit bzw. hydrophoben Branntgips und einer Dispersion.The invention relates to a joint filler, a filler, potting or leveling compound and / or Ansetzbinder, especially for the expansion of wet rooms using two components, a calcium sulfate binder and / or excited anhydrite or hydrophobic gypsum and a dispersion.
A|s Haftbinder oder Fugerifüller für Gipskärtonplattensowie von klein- und großformatigen Gipselementen gelangen geeignete Massen überwiegend auf Calciumsulfatbasis zum Einsatz. Dies trifft auch für Spachtel- und Ausgleichsmassen zur Herstellung ebener Oberflachen zu. So wird nach DD Nr.53604 ein doppelt gebrannter Gips — Alaungipsbinder — und bei DD Nr.73730 ein normaler Gips mit Harnstoff-Formaldehyd modifiziert und zum Verbinden oder Ausbessern der verschiedensten Gipsplatten eingesetzt. ; '..·.'Acrylic binders or fugger fillers for gypsum stains as well as small and large-sized gypsum elements use suitable masses mainly based on calcium sulphate. This also applies to leveling and leveling compounds for the production of flat surfaces. Thus, according to DD No. 53604, a double-fired gypsum - Alaungipsbinder - and in DD No. 73730 a normal gypsum with urea-formaldehyde modified and used for joining or repairing a variety of gypsum boards. ; '.. ·.'
Anders verhalten sich Elemente, die durch Silikone, Paraffinwachsemulsionen, Ceresine, Ozokerite, Bitumen oder Harzemulsionen rnit mehr oder weniger Erfolg imprägniert bzw. hydrophobiert wurden. Haftbinder, Fugen-, Spachtel- und Aüsgleichsmassen müssen für diese Elemente, die in Räumen mit hohen relativen Luftfeuchten zum Einsatz gelangen, beständig sein und gleichzeitig einen guten Haftverbund erreichen. Dies läßt sich durch teuere Kunstharze oder z. B. durch mit Silikonen modifizierten Gipsbindern erreichen. Ein dauernder Schutz wird aber durch diese silikonhaltigen Massen nicht erreicht und es wird demzufolge immer eine nachträgliche Oberflächenvergütung durch Fliesen oder Folien empfohlen. Problematisch wird es, wenn man aus ökonomischen Gründen Gipsbäuplatten und -elemente mit ihren imprägnierten Fugen nur mit einem Anstrichsystem versieht. Will man Rohrdurchführungen z.B. in Gipskartonplatten abdichten, werden nur Kunstharze als Ein- oder Zweikomporientenmaterial in Feuchträumen mit Erfolg eingesetzt. Unökonomisch wird bereits der Einsatz dieser Abdichtungsmassen zur Fugenverfüllung.The behavior of elements impregnated or rendered hydrophobic by silicones, paraffin wax emulsions, ceresins, ozokerites, bitumen or resin emulsions is different. Adhesive binders, grout, putty and casting compounds must be resistant to these elements, which are used in rooms with high relative humidities, and at the same time achieve a good bond. This can be achieved by expensive synthetic resins or z. B. achieve by using silica-modified gypsum binder. A permanent protection is not achieved by these silicone-containing compounds and it is therefore always recommended a subsequent surface treatment by tiles or films. The problem arises when, for economic reasons, plasterboard panels and elements with their impregnated joints are only provided with a paint system. If one wants to pipe passages e.g. in gypsum plasterboard, only synthetic resins are used as one- or Zweikomporientenmaterial in wet rooms with success. The use of these sealing compounds for joint filling is already uneconomical.
Es sind weiterhin wasserabstoßende Mittel wie Silikate, Stearate und Silikone bekannt, die auf Gipsformteile und das Fugenmaierial aufgestochen oder aufgespritzt werden, um eine wasserabweisende Wirkung an der Oberfläche zu erzielen. Urn aber einen durchgängigen Schutz mit ökonomisch vertretbaren Einsatzmaterialien auf Calciumsulfatbasis zu erreichen, sind für das vorgesehene Einsatzgebiet keine Bindemittel bekannt.There are also known water repellents such as silicates, stearates and silicones, which are pierced or sprayed onto plaster moldings and Fugenmaierial to achieve a water-repellent effect on the surface. Urn but to achieve a consistent protection with economically acceptable calcium sulfate based feedstocks, no binders are known for the intended application.
Für den Einsatz insbesondere von hydrophoben Gipskärtonplatten nach DD Nr. 160516 ist eine wasserabweisende Abdichtungsmasse für Rohrdurchführungen und Fugen, eine Verguß- oder Ausgleichsmasse sowie ein Ansetzbinder für den ökonomischen Einsatz in Feuchträumen zu entwickeln, der gleichgünstige hydrophobe Eigenschaften wie die Gipskärtonplatten aufweist. '.' .For the use in particular of hydrophobic gypsum stains according to DD No. 160516, a water-repellent sealing compound for pipe penetrations and joints, a potting or leveling compound and a Ansetzbinder for economic use in wet rooms to develop, which has the same hydrophobic properties as the gypsum stains. '.' ,
Da die verschiedensten modifizierten Einkomponentenmischungen auf Calciumsulfatbasis für das vorgesehene Einsatzgebiet In Räumen mit hohen relativen Luftfeuchten zu keiner erfolgversprechenden Lösung führten, wurde nach DD CO4B/238002/8 ein hydrophober Branntgips entwickelt. Dieser läßt sich durch seine hydrophoben Eigenschaften nicht wie der übliche Gips ohne weiteres ins Anmachwasser einstreuen. Deswegen wurde ein Gemisch aus Anmachwasser und einer Emulsion des Hydrophobierungsmittels des hydrophoben Gipses nach DD Nr. 160516 eingesetzt und eine gute Benetzbarkeit des hydrophoben Branntgipses erreicht; Überraschenderweise wurde gefunden, daß normale Branntgipse und/oder mehr oder weniger angeregtes Anhydrit in Abhängigkeit des Wasser-Gips-Verhältnisses ebenfalls mit dieser Emulsion nach dem Abbinden bestimmte wasserresistente Eigenschaften ausweisen und zum Verfugen, als Haftbinder, als Ausgleichsmasse für Gipselemente beim Ausbau von Feuchträumen für Wände, Decken und Fußböden Verwendung finden können. Hydrophober Branntgips oder normales bzw. modifiziertes Calciumsulfatbindemittel und/oder angeregtes Anhydrit wird in eine feindisperse wäßrige Morrtanwächsemulsion eingerührt und in entsprechender Konsistenz dem Verwendungszweck angepaßt. Die Emulsion hat einen Gehalt von 6-35 Gewichtsteilen Montanwachs, vorzugsweise von 10-25 Gewichtsteilen Montanwachs, 1-7 Gewichtsteilen Emulgator, insbesondere 3-5 Gewichtsteile Emulgator, Äthylenoxidabdukte auf Basis von Alkylphenolen und längerkettigen Fettalkoholehund Wasser ergänzend zu 100 Gewichtsteilen.Since the most varied modified one-component mixtures based on calcium sulfate for the intended application in rooms with high relative humidities led to no promising solution, according to DD CO4B / 238002/8 a hydrophobic burnt gypsum was developed. This can not be sprinkled by its hydrophobic properties as the usual gypsum easily in the mixing water. Therefore, a mixture of mixing water and an emulsion of the hydrophobing agent of the hydrophobic gypsum according to DD No. 160516 was used and achieved a good wettability of the hydrophobic gypsum; Surprisingly, it was found that normal spirits and / or more or less excited anhydrite depending on the water-gypsum ratio also identify with this emulsion after setting certain water-resistant properties and grouting, as a bonding agent, as a balancing composition for plaster elements in the expansion of wet rooms for Walls, ceilings and floors can be used. Hydrophobic gypsum or normal or modified calcium sulfate binder and / or excited anhydrite is stirred into a finely dispersed aqueous Morrtanwächsemulsion and adapted in accordance with the intended use in accordance with consistency. The emulsion has a content of 6-35 parts by weight of montan wax, preferably 10-25 parts by weight of montan wax, 1-7 parts by weight of emulsifier, more preferably 3-5 parts by weight of emulsifier, alkylphenol-based ethylene oxide abutments and longer chain fatty alcohol and water in addition to 100 parts by weight.
Zur Modifizierung der Feststoffkomponente können Zusatzstoffe wie Quarzsand bestimmter Körnung, Kieselsäuregel als Magerungsmittel, die verschiedensten Zelluloseverbindungen und quellstarke Alginate als Plastifikatoren, Abbinderegulierer, Inertstoffe in Form von Fasern, wie z.B. Glasfasern zur Verbesserung des Austrocknungsverhaltens und zur Erhöhung der Stabilität größerer Fugen, quellreduzierende Mittel wie u.a. Kaliumsulfat eingesetzt werden. Auch Spezialkitte, entsprechend den Zusammensetzungen, nach DD Nr. 153817 haben trotz ihrer Geschmeidigkeit als Kitt für Gipsbaustoffe den Nachteil einer erhöhten Wasserlöslichkeit durch ihre Anteile von Stärkeklebestoffen. Das bereits sehr niedrige Wasser-Gips-Verhältnis, vor allem in den Mischungen m|t Anhydrit/Bariumsulfat, mit seinen guten Festigkeiten wird durch die erfindungsgemäße Montanwachsemulsiori wasserbeständiger und ist z.B.im Dünnbettverfahren einsetzbar.For modifying the solid component, additives such as quartz sand of certain grains, silica gel as a leaning agent, various cellulose compounds and high-swelling alginates as plasticizers, setting regulators, inert materials in the form of fibers, e.g. Glass fibers to improve the drying behavior and to increase the stability of larger joints, source-reducing agents such as u.a. Potassium sulfate can be used. Even special cements, according to the compositions, according to DD No. 153817, despite their suppleness as putty for gypsum building materials, have the disadvantage of increased water solubility due to their proportions of starch adhesives. The already very low water-gypsum ratio, especially in the mixtures m / t anhydrite / barium sulfate, with its good strengths, becomes more water-resistant by the montan wax emulsion according to the invention and can be used, for example, in the thin-bed process.
-2- 259 234-2- 259 234
Anhand von Ausführungsbeispielen werden die Anteile der Feststoff- und der Flüssigkomponente zum Erhalt von spachtel- bis zu gießfähigen Massen dargestellt, wobei von einer Grundrezeptur der Montanwachsemulsion ausgegangen wird. Bekannte Zusatzstoffe zur Spezifizierung bestimmter Eigenschaften, u.a. Plastizität, Quellen und Schwinden, Austrocknungsverhalten und angepaßte Erstarrungszeiten in Abhängigkeit des Einsatzes des Zweikomponentenbindemitteis bleiben unberücksichtigt. Prüfergebnisse über die Wasseraufnahme nach direkter Lagerung der Probekörper (Massekonstanz) irn Wasser und Angaben über die Erstarrungszeiten vervollständigen die Beispiele.By way of examples, the proportions of the solid and the liquid component to obtain spatulas to pourable masses are shown, starting from a basic formulation of Montanwachsemulsion. Known additives for specifying certain properties, i.a. Plasticity, swelling and shrinkage, drying behavior and adapted solidification times depending on the use of the two-component binder are not considered. Test results on the water absorption after direct storage of the specimens (mass constancy) in water and information on the solidification times complete the examples.
5 Masseteile Gipshalbhydrat5 parts by weight of gypsum hemihydrate
2 Masseteile Montanwachsemulsion ·2 parts by weight of montan wax emulsion ·
Erstarrungsbeginn: 4min, Erstarrungsende: 14min Wasseraufnahme nach Wasserlagerung 15min: 3,7Ma.-% 60min: 4,8Ma.-% 120m'in:5,6Ma.-%Start of solidification: 4min, solidification end: 14min water absorption after water storage 15min: 3,7Ma .-% 60min: 4,8Ma .-% 120m'in: 5,6Ma .-%
5 Masseteile Gipshalbhydrat 1 Masseteil Montanwachsemulsion5 parts by weight of gypsum hemihydrate 1 part by weight of montan wax emulsion
1 Masseteil Wasser1 part by weight of water
Erstarrungsbeginn: 4,25min, Erstarrungsende: 15min Wasseraufnahme nach WasserlagerungStart of solidification: 4,25min, solidification end: 15min water absorption after water storage
15min: 7,3Ma.-% '. '..15min: 7,3Ma .-% '. '..
60min: 8,3Ma.-% 120min: 8,8 Ma.-%60min: 8,3Ma .-% 120min: 8,8 Ma .-%
4,44 Masseteile Gipshalbhydrat4.44 parts by weight of gypsum hemihydrate
2 Masseteile Montanwachsemulsion2 parts by weight montan wax emulsion
Erstarrungsbeginn: 6min, Erstarrungsende: T6,5min ,.Start of solidification: 6min, solidification end: T6,5min,.
Wasseraufnahme nach Wasserlagerung 15min: 4,8Ma.-% 60min: 5,4Ma.-% 120min: 6,1 Ma.-%Water absorption after water storage 15min: 4.8Ma .-% 60min: 5.4Ma .-% 120min: 6.1 Ma .-%
4,44 Masseteile Gipshylbhydrat '4.44 parts by weight of gypsum hydride '
1 Masseteil Montanwachsemulsion '1 part by weight of montan wax emulsion
1 Masseteil Wasser . " Erstarrungsbeginn: 7min, Erstarrungsende: 17min Wasseraufnahme nach Wasserlagerung 15min: 7,4Ma.-%1 part by weight of water. "Start of solidification: 7min, solidification end: 17min water absorption after water storage 15min: 7,4Ma .-%
60 min: 9,5 Ma.-% 60 minutes: 9.5% by mass
120min: 10,3Ma.-%120min: 10.3Ma .-%
3,64 Masseteile Gipshalbhydrat3.64 parts by weight of gypsum hemihydrate
2 Masseteile Montanwachsemulsion 2 parts by weight montan wax emulsion
Erstarrungsbeginn: 9min, Erstarrungsende': 18min ' ' ,'Start of solidification: 9min, end of freezing ': 18min' ','
Wasseraufnahme nach Wasserlagerung 15min: 6,1 Ma.-%Water absorption after storage for 15 minutes: 6.1% by mass
60min: 8,6Ma.-% -60min: 8,6Ma .-% -
120min: 9,1 Ma.-% ' , -120min: 9,1 Ma .-% ', -
3,64 Masseteile Gipshalbhydrat 1 Masseteil Montanwachsemulsion3.64 parts by weight of gypsum hemihydrate 1 part by weight of montan wax emulsion
1 Masseteil Wasser '1 part of mass water '
Erstarrungsbeginn: 10,7min, Erstarrungsende: 23,6min Wasseraufnahme nach Wasserlagerung 15min: 9,4Ma.-% 60min: 14,1 Ma.-% 120 min: 16,4Ma.-%Start of solidification: 10,7min, solidification end: 23,6min water absorption after water storage 15min: 9,4Ma .-% 60min: 14,1 Ma .-% 120 min: 16,4Ma .-%
5 Masseteile Gipshalbhydrat 0,66 Masseteile Montanwachsemulsion 1,34 Masseteile Wasser5 parts by weight of gypsum hemihydrate 0.66 parts by weight of montan wax emulsion 1.34 parts by weight of water
Erstarrungsbeginn: 4,7min,,Erstarrungsende: 19,7min Wasseraufnahme nach Wasserlagerung 15min: 9,6Ma.-%Start of solidification: 4,7min ,, solidification end: 19,7min water absorption after water storage 15min: 9,6Ma .-%
60min: 13,0Ma.-% 120min: 13,9Ma.-%60min: 13.0Ma .-% 120min: 13.9Ma .-%
3,33 Masseteile Gipshalbhydrat 2 Masseteile Montanwachsemulsion Erstarrungsbeginn; 12min, Erstarrungsende: 27min VVeseeraufnahme nach Wasserlagerung ?I5?min:7,0Ma.^% λ ; V. . .:.' .-.· .3.33 parts by weight of gypsum hemihydrate 2 parts by weight montan wax emulsion solidification beginning; 12min, end of solidification: 27min VVese uptake after storage in water? I5? Min: 7,0Ma. ^% Λ; V. .:. ' .-. ·.
60min:7,äMa:-% '. : ' '60min: 7, ÄMa: -% '. : ' '
12ÖWin: ^ ; ' ' '12ÖWin: ^ ; '''
2,85 Masseteile Gipshalbhydrat 2. Masseteije Montanwachsemulsion Erstiarrüngsbeginn: 15min,Erstarrungsende: 31 min VVesseraufnahme nach Wasserlagerung2.85 parts by weight of gypsum hemihydrate 2. Masseteije Montanwachsemulsion Erstiarrüngsbeginn: 15min, solidification end: 31 min Vvesseraufnahme after water storage
Ö0;min: 1O,iBMa.-% :Ö0; min: 10, iBMa .-%:
120rrtin: 11,0Ma;-%120rrtin: 11,0Ma; -%
Bei den Beispielen 1 bis 4,6,7 und 9 enthält die Emulsion 10% Montanwachs und 8% Athylenoxidabdukt auf Basis von Alkylphenolen, beim Beispiel 5 sind 12% Montanwachs und 3% Athylenoxidabdukt auf Basis von Alkylphenolen und beim Beispiel 8 25% Montanwachs und 3,5Äthylenoxidabdukte auf Basis von Alkylphenolen und längerkettigen Fettalkoholen entHalten. :' ·-. ,, ..- '.. .. ' . /'. '. .' .' . '..In Examples 1 to 4, 6, 7 and 9, the emulsion contains 10% montan wax and 8% alkylene-based ethylene oxide abutment; in Example 5, 12% montan wax and 3% alkylphenol-based ethylene oxide abutment and in Example 8 25% montan wax and Contain 3,5-ethylene oxide starting materials based on alkylphenols and longer-chain fatty alcohols. : '- -. ,, ..- '.. ..'. / '. '. . ' . ' , '..
Claims (3)