ES2269889T3 - Aleacion de nb-ta-zr para uso para dispositivos de stent. - Google Patents
Aleacion de nb-ta-zr para uso para dispositivos de stent. Download PDFInfo
- Publication number
- ES2269889T3 ES2269889T3 ES03020304T ES03020304T ES2269889T3 ES 2269889 T3 ES2269889 T3 ES 2269889T3 ES 03020304 T ES03020304 T ES 03020304T ES 03020304 T ES03020304 T ES 03020304T ES 2269889 T3 ES2269889 T3 ES 2269889T3
- Authority
- ES
- Spain
- Prior art keywords
- alloys
- stent
- alloy
- devices
- stent devices
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Aleación que consiste esencialmente en: 80-90 % de Nb, 0,5-5 % de Zr y 5-19,5 % de Ta.
Description
Aleación de
Nb-Ta-Zr para uso para dispositivos
de Stent.
El invento se refiere a aleaciones para
dispositivos de Stent (cánulas intraluminales), que consisten en
niobio (Nb), tántalo (Ta) y zirconio (Zr), así como a dispositivos
de Stent a base de tales aleaciones.
Los dispositivos de Stent son de por sí
conocidos y se describen p.ej. en los documentos de patentes de los
EE.UU. US-A-5.628.787,
US-A-5.630.840 y en el documento de
solicitud de patente europea
EP-A-0.873.734. Junto a un acero
inoxidable, y aleaciones de níquel y tántalo, se propusieron también
aleaciones de niobio y zirconio para dispositivos de Stent,
situándose el contenido de Nb por encima de 90%, preferiblemente por
encima de 95 o bien 98% (véase el documento de solicitud de patente
internacional WO 02/43787).
El documento de patente británica GB 933.712 A
describe aleaciones de Nb-Ta muy resistentes al
calor con
15 - 75% de Ta, 17 - 75% de Nb y por lo menos otro metal seleccionado entre el conjunto formado por Zr, W, Mo y Ta, pudiendo estar contenido el Zr en 0,245 - 6%.
15 - 75% de Ta, 17 - 75% de Nb y por lo menos otro metal seleccionado entre el conjunto formado por Zr, W, Mo y Ta, pudiendo estar contenido el Zr en 0,245 - 6%.
Se plantea la misión de poner a disposición unas
aleaciones, que satisfagan los elevados requisitos en lo que se
refiere a la biocompatibilidad, no contengan alérgenos conocidos,
tengan unas buenas propiedades mecánicas, y que sean visibles en la
imagen de rayos X e identificables en la tomografía de espín
nuclear.
Por fin, se encontró que unos dispositivos de
Stent, a base de las aleaciones de Nb, Ta y Zr descritas más
adelante, reúnen sorprendentemente las siguientes propiedades: una
buena biocompatibilidad junto con unas muy buenas propiedades
mecánicas, una opacidad frente a los rayos X y una identificabilidad
en el tomógrafo de espín nuclear por causa de las propiedades
magnéticas. No están presentes componentes problemáticos tales como
níquel, la opacidad frente a los rayos X no es demasiado grande como
en el caso de aleaciones con un contenido muy alto de Ta, y la
identificabilidad con procedimientos de espín nuclear es una gran
ventaja dada la creciente propagación de este método.
La aleación reivindicada tiene las siguientes
proporciones
Aleaciones preferidas tienen las siguientes
proporciones:
| 4. | 80 - 90% de Nb, | 0,5 - 5% de Zr, | 5 - 19,5% de Ta. |
Son especialmente ventajosas unas aleaciones con
un contenido de niobio comprendido entre 80 y 90%. En este caso,
tienen consecuencias el aumento de la visibilidad con rayos X y el
mejoramiento de las propiedades mecánicas - con la posibilidad de
reducir el diámetro de los puentes de unión de los dispositivos de
Stent.
Unas aleaciones, en las que está presente más
cantidad de tántalo que de zirconio, son asimismo formas preferidas
de realización del invento.
Ejemplos de aleaciones especialmente preferidas
son:
| 3. | 90% de Nb, | 1% de Zr, | 9% de Ta, | |
| 4. | 85% de Nb, | 1% de Zr, | 14% de Ta. |
El invento se refiere también a unos
dispositivos de Stent a base de las aleaciones descritas, en
particular a unos dispositivos de Stent, en los que los puentes de
unión poseen una sección transversal relativamente pequeña.
La fabricación de las aleaciones y la de los
dispositivos de Stent a partir de ellas se efectúan según
procedimientos habituales, que son conocidos para un experto en la
especialidad.
Claims (2)
1. Aleación que consiste esencialmente en
- 80 - 90% de Nb,
- 0,5 - 5% de Zr y
- 5 - 19,5% de Ta.
2. Dispositivo de Stent a base de una aleación
que consiste esencialmente en
- 80 - 90% de Nb,
- 0,5 - 5% de Zr y
- 5 - 19,5% de Ta.