JP2003200517A - Molded products - Google Patents
Molded productsInfo
- Publication number
- JP2003200517A JP2003200517A JP2001400278A JP2001400278A JP2003200517A JP 2003200517 A JP2003200517 A JP 2003200517A JP 2001400278 A JP2001400278 A JP 2001400278A JP 2001400278 A JP2001400278 A JP 2001400278A JP 2003200517 A JP2003200517 A JP 2003200517A
- Authority
- JP
- Japan
- Prior art keywords
- lining
- inner layer
- elastic
- molded product
- outer layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【課題】 蒸散性に優れ、且つ着用時の触感がソフトな
モールド成形品の提供。
【解決手段】 少なくとも表地及び裏地から構成される
内層と不織布を含む外層とからなり、内層の表地に凹凸
が形成されており、内層の裏地と外層の不織布とが点状
に接着されている、モールド成形品。
(57) [Problem] To provide a molded article having excellent transpiration and a soft touch when worn. SOLUTION: An inner layer composed of at least a surface material and a lining, and an outer layer including a nonwoven fabric, an unevenness is formed on a surface material of the inner layer, and the lining of the inner layer and the nonwoven fabric of the outer layer are adhered in a point-like manner. Molded products.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、モールド成形品に
関する。特に、蒸散性に優れ且つソフトな触感を有する
モールド成形品に関する。TECHNICAL FIELD The present invention relates to a molded article. In particular, it relates to a molded product having excellent transpiration property and having a soft touch.
【０００２】[0002]
【従来の技術】従来より、ブラジャーカップ、肩パッ
ト、腰パット等のモールド成形品においては、不織布又
は発泡ウレタンのような材料が用いられてきた。しかし
ながら、かかる不織布や発泡ウレタンからなるモールド
成形品においては、着用及び洗濯を繰り返すことで、へ
たりが生じ、保型性が低下してしまうため、改善が望ま
れていた。2. Description of the Related Art Conventionally, materials such as non-woven fabric or urethane foam have been used in molded articles such as brassiere cups, shoulder pads and waist pads. However, in a molded product made of such a non-woven fabric or urethane foam, repeated wear and washing causes fatigue and deterioration in shape retention, and therefore improvement has been desired.
【０００３】そこで、ブラジャー等のモールドカップに
おける保型性低下を向上させる試みが、特開平１１−１
７２５０５号公報及び特開２０００−２２６７０４号公
報等において提案されている。これらの公報には、編物
からなる外層部と、不織布又は合成樹脂発泡体からなる
内層部とを有する二層構造のモールド加工衣料品が記載
されている。Therefore, an attempt to improve the deterioration of the shape retention of a mold cup such as a brassiere has been made in JP-A-11-1.
No. 72505 and Japanese Patent Laid-Open No. 2000-226704. These publications describe a two-layered molded garment having an outer layer part made of a knitted fabric and an inner layer part made of a nonwoven fabric or a synthetic resin foam.
【０００４】[0004]
【発明が解決しようとする課題】確かに、上記公報に記
載されるブラジャーカップ等のモールド加工衣料品にお
いては保型性の低下を防止できるが、蒸散性が不充分、
すなわち着用時に蒸れ易いということが分かってきた。
また、身体と接触する内層部に不織布を用いた場合に
は、着用した際ブラジャーカップの触感が硬いという問
題もあった。Certainly, in the case of molded clothing such as brassiere cups described in the above publication, it is possible to prevent the deterioration of the shape retention property, but the transpiration property is insufficient,
That is, it has been found that it is easy to get stuffy when worn.
In addition, when a non-woven fabric is used for the inner layer portion that comes into contact with the body, there is a problem that the brassiere cup feels hard when worn.
【０００５】本発明は、上記問題点を解決すべくなされ
たものであって、その目的とするところは、蒸散性に優
れ、且つ着用時の触感がソフトなモールド成形品を提供
することにある。The present invention has been made to solve the above problems, and an object of the present invention is to provide a molded article which is excellent in transpiration and has a soft touch when worn. .
【０００６】[0006]
【課題を解決するための手段】本発明は、少なくとも表
地及び裏地から構成される内層と、不織布を含む外層と
からなるモールド成形品であって、内層の表地に凹凸が
形成されており、内層の裏地と外層の不織布とが点状に
接着されていることを特徴とする。The present invention is a molded product comprising an inner layer composed of at least a surface material and a lining material, and an outer layer containing a non-woven fabric, wherein unevenness is formed on the surface material of the inner layer. The lining and the non-woven fabric of the outer layer are adhered in a dot shape.
【０００７】また、本発明においては、モールド成形品
の内層が、非弾性伸縮糸からなる表地、弾性伸縮糸から
なる裏地、及び表地と裏地との間に配される中綿を、裏
地を構成する弾性伸縮糸により一体化した伸縮性キルテ
ィング状生地であることが好ましい。Further, in the present invention, the inner layer of the molded product constitutes the lining, the outer layer made of non-elastic elastic yarn, the lining made of elastic elastic yarn, and the batting arranged between the outer layer and the lining. It is preferable that the elastic quilted cloth is made by elastic elastic yarns.
【０００８】更にまた、本発明においては、内層の表地
が身体側表面を形成していることが好ましい。Furthermore, in the present invention, it is preferable that the outer layer of the inner layer forms the body-side surface.
【０００９】[0009]
【発明の実施の形態】以下、本発明のモールド成形品に
ついて説明する。図１は、本発明のモールド成形品の一
例であるモールドカップを模式的に示した概略断面図で
ある。モールドカップ１は、表地及び裏地から構成され
る内層２と、不織布を含む外層３とからなっている。BEST MODE FOR CARRYING OUT THE INVENTION The molded article of the present invention will be described below. FIG. 1 is a schematic cross-sectional view schematically showing a mold cup which is an example of the molded product of the present invention. The mold cup 1 is composed of an inner layer 2 composed of a front material and a lining material, and an outer layer 3 containing a non-woven fabric.
【００１０】本発明のモールド成形品に用いられる内層
は、少なくとも表地及び裏地から構成されており、ま
た、表地に凹凸が形成されている必要がある。凹凸の形
状に関しては、特に制限はなく、ドーム状、ひし形状、
亀甲状、かまぼこ状等といったいずれの形状でもよい。
また、表地及び裏地の構成についても、特に制限はな
く、織物、編物のいずれであってもよいが、通気性、加
工性の点から編物であることが好ましい。更に、本発明
においては、得られる成形品にクッション性を付与しソ
フト感を高めるため、表地をキルティング状の生地とす
ることが好ましい。The inner layer used in the molded article of the present invention is composed of at least a surface material and a lining material, and it is necessary that unevenness is formed on the surface material. There is no particular limitation on the shape of the unevenness, and the dome shape, the rhombus shape,
It may have any shape such as a turtle shell shape or a kamaboko shape.
Further, the constitution of the outer material and the lining material is not particularly limited, and may be either a woven fabric or a knitted fabric, but a knitted fabric is preferable from the viewpoint of breathability and processability. Further, in the present invention, it is preferable that the surface material is a quilted cloth in order to impart cushioning properties to the obtained molded article and enhance the softness.
【００１１】本発明においては、得られるモールド成形
品のソフト感をより向上させるため、内層を伸縮性キル
ティング状生地にすることが特に好ましい。ここで、伸
縮性キルティング状生地とは、非弾性伸縮糸からなる表
地、弾性伸縮糸からなる裏地、及び表地と裏地との間に
配される中綿からなり、表地、裏地及び中綿が裏地を構
成する弾性伸縮糸により連結され一体化されたものであ
る。In the present invention, in order to further improve the softness of the obtained molded product, it is particularly preferable that the inner layer is a stretchable quilted cloth. Here, the stretchable quilting fabric is composed of a non-elastic stretchable yarn outer material, an elastic stretchable yarn lining, and a batting disposed between the outer lining and the lining. The elastic elastic yarns are connected and integrated.
【００１２】なお、ここでいう「弾性伸縮糸」とは、芯
部にポリウレタン繊維を用い、鞘部に短繊維を用いた芯
鞘構造糸、芯部にポリウレタン繊維を、鞘部にフィラメ
ントを配し、撚りを掛けたもの、フィラメント又は紡績
糸とポリウレタン繊維を交撚したものなどである。ま
た、ポリウレタン繊維の代わりにポリウレタン繊維にフ
ィラメントを巻き付けた糸を用いても良い。ポリウレタ
ン繊維は弾性伸縮性を有し、通常３〜４倍に引き伸ばさ
れて芯鞘構造糸等を形成している。一方、ここでいう
「非弾性伸縮糸」とは、ポリウレタン繊維を含まない糸
のことであって、弾性伸縮率が小さいものである。例え
ば、ポリエステル、アクリル、ナイロン、レーヨン等の
フィラメントや、天然繊維、化学繊維、合成繊維の紡績
糸などである。The term "elastic stretchable yarn" as used herein means a core-sheath structure yarn in which polyurethane fibers are used in the core portion and short fibers are used in the sheath portion, polyurethane fibers are arranged in the core portion, and filaments are arranged in the sheath portion. And twisted, and filaments or spun yarns and polyurethane fibers are twisted together. Further, instead of the polyurethane fiber, a thread obtained by winding a filament on the polyurethane fiber may be used. Polyurethane fibers have elastic elasticity and are usually stretched 3 to 4 times to form core-sheath structure yarns and the like. On the other hand, the “non-elastic stretchable yarn” here means a yarn that does not contain polyurethane fibers and has a small elastic stretch ratio. For example, filaments of polyester, acrylic, nylon, rayon, etc., spun yarns of natural fibers, chemical fibers, and synthetic fibers are available.
【００１３】具体的には、伸縮性キルティング状生地の
表地は、ポリエステル繊維、ナイロン繊維及びアクリル
繊維等の非弾性伸縮糸から編成されていることが好まし
い。モールド成形品のリサイクルの点から、伸縮性キル
ティング状生地の表地としてポリエステル繊維を用いる
ことが特に好ましい。なお、上記非弾性伸縮糸から構成
される表地は、織物、編物のいずれであってもよいが、
通気性、加工性の点から編物であることが好ましい。Specifically, the surface material of the stretchable quilted cloth is preferably knitted from non-elastic stretchable yarns such as polyester fiber, nylon fiber and acrylic fiber. From the viewpoint of recycling the molded product, it is particularly preferable to use polyester fiber as the outer material of the stretchable quilted fabric. The outer material made of the non-elastic stretchable yarn may be woven or knitted,
A knitted fabric is preferable in terms of breathability and processability.
【００１４】一方、伸縮性キルティング状生地の裏地
は、弾性伸縮糸から構成されていれば特に限定されない
が、芯鞘構造を有する弾性伸縮糸を用いることが好まし
い。例えば、ポリウレタン繊維（スパンデックス）を芯
部とし、鞘部としてポリエステル等の短繊維を用いたも
のである。なお、表地同様、上記弾性伸縮糸から構成さ
れる裏地は、織物、編物のいずれであってもよいが、裏
地がほぼ平らとなるようなものが好ましい。また、通気
性、加工性の点から編物であることが好ましい。なお、
裏地を構成する糸は、全てが弾性伸縮糸である必要はな
く、生地が弾性伸縮性を有するのであれば、非弾性伸縮
糸と交互に配したものであってもよい。On the other hand, the lining of the stretchable quilted fabric is not particularly limited as long as it is made of elastic stretchable yarn, but it is preferable to use elastic stretchable yarn having a core-sheath structure. For example, a polyurethane fiber (spandex) is used as a core portion and a short fiber such as polyester is used as a sheath portion. As with the outer material, the lining made of the elastic stretchable yarn may be a woven fabric or a knitted fabric, but it is preferable that the lining be substantially flat. In addition, a knitted fabric is preferable in terms of breathability and processability. In addition,
All the yarns constituting the lining need not be elastic stretch yarns, and may be alternately arranged with non-elastic stretch yarns as long as the fabric has elastic stretchability.
【００１５】また、伸縮性キルティング状生地の中綿に
は、アクリル、ナイロン、ポリエステル等の合成繊維が
好適である。ここで、中綿としては、クッション性や通
気性に優れていることが求められるため、バルキー性の
有る紡績糸やウーリー加工糸又はコンジュゲート糸のよ
うな嵩高性を有するものを用いることが好ましい。ま
た、毛羽立ちやソフト性という点からは、フィラメント
糸を用いることが好ましい。Further, synthetic fibers such as acrylic, nylon and polyester are suitable for the batting of the stretchable quilted cloth. Here, since the batting is required to have excellent cushioning properties and breathability, it is preferable to use bulky spun yarns, wooly textured yarns, or conjugate yarns having bulkiness. From the viewpoint of fluffing and softness, it is preferable to use filament yarn.
【００１６】このように、伸縮性キルティング状生地
は、表地と裏地と中綿との三層構造体である。織成・編
成時に、裏地を構成する弾性伸縮糸が表地を構成する糸
と交差することで、表地・中綿・裏地を連結一体化し、
キルティング状としている。As described above, the stretchable quilted cloth is a three-layered structure including the outer material, the lining and the batting. At the time of weaving / knitting, the elastic stretchable yarns that make up the lining intersect the yarns that make up the outer material, connecting and integrating the outer material, batting, and lining,
Quilted.
【００１７】伸縮性キルティング状生地においては、上
述の通り、表地に非弾性伸縮糸が、裏地に弾性伸縮糸が
用いられていることにより、裏地はほぼ平面のままであ
るが、表地は中綿と共に２つのキルティング間で大きく
湾曲する。したがって、得られる伸縮性キルティング状
生地は、表地に凹凸が形成されると共に柔らかいクッシ
ョン性を有するものとなる。また、表地、裏地及び中綿
からなる三層構造体を裏地を構成する弾性伸縮糸を用い
て一体化していることにより、良好な伸縮性を保つこと
が可能となり、結合部分も硬くならなくなる。更に、縦
方向、緯方向共に伸縮性を有するようになるため、モー
ルド加工時における加工性が非常に良好となる。In the stretchable quilted fabric, as described above, the non-elastic stretchable yarn is used for the outer material and the elastic stretchable yarn is used for the inner material, so that the inner material remains almost flat, but the outer material together with the batting. Greatly bends between the two quilts. Therefore, the resulting stretchable quilted cloth has a soft cushioning property with unevenness formed on the outer material. Further, since the three-layer structure composed of the outer material, the lining and the batting is integrated by using the elastic stretchable yarn which constitutes the lining, it is possible to maintain good stretchability and the joint portion does not become hard. Furthermore, since it has elasticity in both the longitudinal direction and the weft direction, the workability during molding is very good.
【００１８】次に、本発明のモールド成形品における外
層は、不織布からなっている。不織布を構成する繊維と
しては、例えば、ポリエステル繊維、ナイロン繊維、ア
クリル繊維等が挙げられる。本発明においては、これら
の中でも、耐久性及びリサイクル性の点からポリエステ
ル繊維を用いることが好ましい。また、不織布の製造方
法については、従来から知られている方法に従えばよ
い。また、不織布に少量の熱融着性繊維を混入しても良
い。熱融着性繊維はモールド加工時に加熱されること
で、不織布を形成する繊維を熱融着繊維が融着し、モー
ルド成形品の保型性を更に高めることが可能となる。Next, the outer layer in the molded article of the present invention is made of a non-woven fabric. Examples of fibers constituting the non-woven fabric include polyester fibers, nylon fibers, acrylic fibers and the like. Of these, polyester fibers are preferably used in the present invention from the viewpoint of durability and recyclability. In addition, the method for producing the nonwoven fabric may follow the conventionally known method. Further, a small amount of heat-fusible fiber may be mixed in the non-woven fabric. By heating the heat-fusible fibers during the molding process, the fibers forming the non-woven fabric are fused with the heat-fusible fibers, and it becomes possible to further improve the shape retention of the molded article.
【００１９】続いて、本発明のモールド成形品において
は、図２に示すように、上記した内層の裏地と外層の不
織布とが点状に接着した構造になっている。すなわち、
図２には、表地２１、中綿２２及び裏地２３から構成さ
れる伸縮性キルティング状生地２０を内層として用いた
モールド成形品１において、伸縮性キルティング状生地
２０の裏地２３と不織布３とが接着剤４により点状に接
着している状態が模式的に示されている。このように、
内層と外層とを点状に接着させることにより、得られる
モールド成形品の通気性を良好にすることが可能とな
る。Subsequently, in the molded product of the present invention, as shown in FIG. 2, the lining of the inner layer and the non-woven fabric of the outer layer are adhered in a dot shape. That is,
In FIG. 2, in a molded product 1 using an elastic quilted cloth 20 composed of a front material 21, a batting 22 and a lining 23 as an inner layer, the lining 23 of the elastic quilted cloth 20 and the nonwoven fabric 3 are adhesive. 4 schematically shows a state in which dots are adhered. in this way,
By adhering the inner layer and the outer layer in a dot shape, it becomes possible to improve the air permeability of the obtained molded product.
【００２０】ここで、内層の裏地と外層の不織布とを点
状に接着する方法としては、例えば、内層の裏地又は外
層の不織布の一方又は両方に接着剤を点状に塗布し、両
者を後述するモールド成形することよって接着させる方
法が挙げられる。また、内層の裏地又は外層の不織布の
一方又は両方に固体状接着剤を面状に散布し、両者をモ
ールド成形することによって接着させる方法を挙げるこ
ともできる。なお、接着剤としては、衣料用に通常用い
られる接着剤を使用すればよく、特に制限はない。Here, as a method for adhering the inner layer lining and the outer layer non-woven fabric in a dot form, for example, an adhesive is applied in a dot form to one or both of the inner layer lining and the outer non-woven fabric, and both are described below. A method of adhering by molding is used. In addition, a method may also be mentioned in which a solid adhesive is applied in a planar manner on one or both of the inner layer lining and the outer layer nonwoven fabric, and both are bonded by molding. As the adhesive, an adhesive usually used for clothing may be used without any particular limitation.
【００２１】内層の裏地と外層の不織布とを接着する更
なる方法としては、内層の裏地と外層の不織布との間
に、例えばメッシュ状又はくもの巣状の熱可塑性繊維シ
ートを介在させ、モールド成形による熱可塑性繊維シー
トの溶融により内層の裏地と外層の不織布とを点状に接
着する方法でもよい。As a further method for adhering the inner layer lining and the outer layer non-woven fabric, for example, a mesh-shaped or cobweb-shaped thermoplastic fiber sheet is interposed between the inner layer lining and the outer layer non-woven fabric, and a mold is formed. Alternatively, a method may be used in which the lining of the inner layer and the non-woven fabric of the outer layer are adhered in spots by melting the thermoplastic fiber sheet by molding.
【００２２】本発明のモールド成形品を衣料用の用途等
に用いた場合、凹凸が形成されている内層の表地を身体
表面側にすると、モールド成形品のキルティング状の部
分には凹部が存在しているため、身体表面との間に隙間
が生じる。このため、モールド成形品が身体表面全体に
わたって密着するという現象が起こらなくなる。また、
このモールド成形品と身体表面との間の隙間を通じて、
着用者から発せられる熱や湿気が発散されることにな
る。したがって、モールド成形品において、この凹凸を
有する表地を身体表面側にした場合、通気性及び蒸散性
を向上させることが可能となる。When the molded article of the present invention is used for clothing or the like, if the outer layer of the inner layer having the irregularities is placed on the body surface side, a recess is present in the quilted part of the molded article. Therefore, there is a gap between the body surface and the body surface. Therefore, the phenomenon that the molded product adheres to the entire body surface does not occur. Also,
Through the gap between this molded product and the body surface,
The heat and moisture emitted by the wearer will be dissipated. Therefore, in the molded article, when the surface material having the unevenness is provided on the body surface side, it becomes possible to improve the air permeability and the transpiration property.
【００２３】続いて、本発明のモールド成形品の製造方
法について説明する。本発明においては、予め製造した
内層及び外層を重ね合わせ、モールド成形することで、
所定の形状を有するモールド成形品を製造する。Next, a method of manufacturing the molded product of the present invention will be described. In the present invention, by stacking the inner layer and the outer layer produced in advance and molding,
A molded product having a predetermined shape is manufactured.
【００２４】ここで、内層と外層とを重ね合わせる前に
は、内層の裏地と外層の不織布とが点状に接着するよう
な前処理を行うことが好ましい。すなわち、本発明にお
いては、上記したように、内層の裏地又は外層の不織布
の一方又は両方に接着剤を点状に塗布（若しくは固体状
接着剤を面状に散布）するか、又は内層の裏地と外層の
不織布との間に熱可塑性繊維シートを介在させた後に、
内層と外層とを重ね合わせ、モールド成形を行うことが
好ましい。なお、本発明においては、内層の裏地と外層
の不織布とが既に点状に接着している積層構造体を用い
て、モールド成形することも可能である。Here, before the inner layer and the outer layer are superposed on each other, it is preferable to perform a pretreatment so that the inner layer lining and the outer layer non-woven fabric are adhered in a dot shape. That is, in the present invention, as described above, one or both of the inner layer lining and the outer layer non-woven fabric is coated with an adhesive in a dot form (or a solid adhesive is spread on a surface), or the inner layer lining is applied. After interposing a thermoplastic fiber sheet between the outer layer and the nonwoven fabric of the outer layer,
Molding is preferably performed by stacking the inner layer and the outer layer. In addition, in the present invention, it is also possible to mold using a laminated structure in which the lining of the inner layer and the nonwoven fabric of the outer layer are already adhered in a dot shape.
【００２５】また、本発明においては、内層及び外層を
重ね合わせる前に、それぞれを所定の形状に成形してお
くことも可能である。Further, in the present invention, it is also possible to form each of the inner layer and the outer layer into a predetermined shape before superposing them.
【００２６】本発明のモールド成形品は、用途に応じ
て、カップ状等の色々な形状にすることができる。具体
的な用途としては、ブラジャーカップ、肩パット、腰パ
ット、サポーター、靴の基材、マット資材等として用い
られる。The molded product of the present invention can be formed into various shapes such as a cup shape depending on the application. Specific applications include brassiere cups, shoulder pads, waist pads, supporters, shoe base materials, and mat materials.
【００２７】特に、本発明のモールド成形品を、ブラジ
ャーカップ、肩パット、腰パット、サポーター等のよう
な衣料用途に用いた場合、身体表面側を伸縮性キルティ
ング状生地の表地とすると、伸縮性キルティング状生地
のボリューム感及びクッション性のため、着用感がソフ
トであると共に、着用者の肌に心地よくフィットするモ
ールド成形品となる。また、本発明のモールド成形品
は、内層と外層の二重構造であるため、良好な保型性を
有するという効果も有している。In particular, when the molded article of the present invention is used for clothing such as brassiere cups, shoulder pads, waist pads, supporters, etc., when the body surface side is used as the outer material of the elastic quilted cloth, the elastic properties are improved. Due to the volume and cushioning properties of the quilted fabric, the molded product has a soft wearing feel and a comfortable fit to the wearer's skin. Further, since the molded product of the present invention has a double structure of an inner layer and an outer layer, it has an effect of having good shape retention.
【００２８】また、本発明のモールド成形品は、特定の
内層及び外層を点状に接着させるという構成を有するこ
とにより、蒸散性に非常に優れている。更に、本発明の
モールド成形品は、良好な通気性を有すると共に、不織
布のみからなる従来の成形品と同等の透湿性も有してい
る。Further, the molded article of the present invention is very excellent in transpiration property because it has a structure in which the specific inner layer and outer layer are adhered in spots. Further, the molded product of the present invention has good air permeability and also has moisture permeability equivalent to that of a conventional molded product composed only of nonwoven fabric.
【００２９】更にまた、本発明のモールド成形品は、内
層及び外層を構成する原料のうち、裏地を構成するポリ
ウレタン繊維を除く他の全てをポリエステル繊維とする
ことができ、このことにより、得られるモールド成形品
の黄変を防ぐことが可能になると同時に、リサイクル性
に優れた成形品とすることができる。Furthermore, in the molded article of the present invention, all of the raw materials constituting the inner layer and the outer layer except the polyurethane fiber constituting the lining can be made of polyester fiber, which is obtained. It becomes possible to prevent yellowing of the molded product, and at the same time, it is possible to obtain a molded product having excellent recyclability.
【００３０】[0030]
【実施例】以下、実施例及び比較例により、本発明をよ
り具体的に説明することにするが、これは単なる例示で
あって、本発明を制限するものではない。EXAMPLES The present invention will be described in more detail with reference to examples and comparative examples, but these are merely examples and do not limit the present invention.
【００３１】[0031]
【実施例１】表地として弾性伸縮性を有しないポリエス
テル８４デシテックスのフィラメントヤーンを用い、裏
地として弾性伸縮性を有するコアスパンヤーン英式綿番
手３０（芯部がスパンデックス４５デシテックスで、鞘
部がポリエステル短繊維）を用い、中綿としてポリエス
テル８４デシテックスのウーリー加工糸を用いて、編み
立てした。得られた編物を染色加工し、厚み２．２５ｍ
ｍ、生地目付け約４９０ｇ／ｍ2の伸縮性キルティング
状生地を得た。得られた伸縮性キルティング状生地を内
層とし、また、ポリエステル６．６デシテックスの糸を
使った厚み２０ｍｍ、目付け２００ｇ／ｍ2の不織布を
外層として用い、不織布に点状に接着剤を塗布した後、
伸縮性キルティング状生地と重ね合わせ、更に金型に入
れモールド加工して、モールド成形品を得た。Example 1 A core spun yarn English cotton count 30 (with a core of spandex 45 dtex and a sheath of polyester) having elastic stretchable core 84 yarn as a lining and a polyester 84 decitex filament yarn having no elastic stretch as the outer material Short fibers), and wooly yarn of polyester 84 decitex was used as batting and knitted. The knitted fabric obtained is dyed and processed to a thickness of 2.25 m.
Thus, a stretchable quilted cloth having a fabric weight of about 490 g / m 2 was obtained. After applying the stretchable quilted fabric as an inner layer, and using a non-woven fabric of polyester 6.6 decitex with a thickness of 20 mm and a basis weight of 200 g / m 2 as an outer layer, a dot-like adhesive was applied to the non-woven fabric. ,
The stretchable quilted fabric was overlaid, and then put into a mold and molded to obtain a molded product.
【００３２】[0032]
【比較例１】ポリエステル６．６デシテックスの糸を使
った厚み２０ｍｍ、目付け４００ｇ／ｍ2の不織布を、
実施例1と同一の金型に入れモールド加工して、モール
ド成形品を得た。[Comparative Example 1] A non-woven fabric with a thickness of 20 mm and a basis weight of 400 g / m 2 using polyester 6.6 decitex yarn was used.
It was put in the same mold as that of Example 1 and subjected to molding to obtain a molded product.
【００３３】[0033]
【比較例２】厚み２０ｍｍ、目付け２３ｋｇ／ｍ3の発
泡ウレタンを、実施例1と同一の金型に入れモールド加
工して、モールド成形品を得た。Comparative Example 2 A foamed urethane having a thickness of 20 mm and a basis weight of 23 kg / m 3 was placed in the same mold as in Example 1 and was molded to obtain a molded product.
【００３４】実施例１、並びに比較例１及び２で得られ
たモールド成形品を、所定の大きさに切断して蒸散性測
定用の試料とし、この試料の重量を測定した。次に、予
め重量の分かっている時計皿を用意し、この中に水を１
ｃｃ滴下し、時計皿の上部を覆うように試料を乗せて全
体の初期重量（Ｗｏ）を測定した。その後、この水が入
っている時計皿の上部に試料を乗せたものを、温度２０
℃及び湿度６５％の部屋に放置し、一定時間（ｔ）経過
後の重量（Ｗｔ）を随時測定し、下記式により時計皿か
らの水分の蒸散率を求めた。
蒸散率（％）＝［（Ｗｏ−Ｗ）−（Ｗｔ−Ｗ）］／（Ｗ
ｏ−Ｗ）×１００
Ｗ：試料及び時計皿の重量の合計
Ｗｏ：初期の試料、時計皿及び水の重量の合計
Ｗｔ：一定時間（ｔ）経過の試料、時計皿及び水の重量
の合計
なお、蒸散率が１００％となる時間が速いものほど、水
分の蒸散速度が速く、蒸散性に優れた（蒸れにくい）試
料であるといえる。The molded articles obtained in Example 1 and Comparative Examples 1 and 2 were cut into a predetermined size to prepare a sample for measuring transpiration, and the weight of this sample was measured. Next, prepare a watch glass of known weight in advance, and add water to it.
The initial weight (Wo) of the whole was measured by dropping cc and placing the sample so as to cover the upper part of the watch glass. After that, place the sample on top of the watch glass containing this water at a temperature of 20
After being left in a room at 65 ° C and a humidity of 65%, the weight (Wt) after a lapse of a fixed time (t) was measured at any time, and the evaporation rate of water from the watch glass was determined by the following formula. Evaporation rate (%) = [(Wo-W)-(Wt-W)] / (W
o-W) × 100 W: total weight of sample and watch glass Wo: total weight of initial sample, watch glass and water Wt: total weight of sample, watch glass and water after a certain time (t) has passed It can be said that the faster the evaporation rate is 100%, the faster the water evaporation rate, and the more excellent the evaporation property (the less likely it is to evaporate).
【００３５】実施例１、並びに比較例１および２の蒸散
性試験の結果を図３に示す。この図から明らかな通り、
本発明のモールド成形品は、従来の不織布又は発泡ウレ
タンのような材料に比べて蒸散性が非常に良好である。The results of the transpiration test of Example 1 and Comparative Examples 1 and 2 are shown in FIG. As you can see from this figure,
The molded article of the present invention has very good transpiration property as compared with the conventional materials such as nonwoven fabric or urethane foam.
【００３６】[0036]
【発明の効果】本発明のモールド成形品は、蒸散性及び
透湿性に優れている。特に、モールド成形品の身体側を
クッション性のある凹凸形状とすることによって、触感
がソフトで、且つ蒸散性に優れたモールド成形品とする
ことができるので、衣料用途に用いた場合、心地よい着
用感が得られる。The molded product of the present invention is excellent in transpiration property and moisture permeability. In particular, by making the body side of the molded product into an uneven shape with cushioning properties, it is possible to obtain a molded product that is soft to the touch and has excellent transpiration, so when used for clothing, it is comfortable to wear. You can get a feeling.
【図１】本発明のモールド成形品の一実施態様を示す概
略断面図である。FIG. 1 is a schematic sectional view showing an embodiment of a molded product of the present invention.
【図２】モールド成形品の内層と外層とが点状に接着し
ている状態を模式的に示した図である。FIG. 2 is a view schematically showing a state where the inner layer and the outer layer of the molded product are adhered in a dot shape.
【図３】モールド成形品の蒸散性を示すグラフである。FIG. 3 is a graph showing the transpiration property of a molded product.
【符号の説明】 １ モールド成形品（モールドカップ） ２ 内層 ３ 外層 ４ 接着剤 ２０ 伸縮性キルティング状生地 ２１ 表地 ２２ 中綿 ２３ 裏地[Explanation of symbols] 1 Molded product (mold cup) 2 inner layer 3 outer layers 4 adhesive 20 stretchable quilted fabric 21 outer material 22 batting 23 Lining
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｂ３２Ｂ 7/12 Ｂ３２Ｂ 7/12 Ｆターム(参考） 3B035 AA05 AA07 AA21 AB03 AC02 AC13 4F100 AK41 BA03 BA10A BA10C BA32 CB00 DD01A DG11A DG11B DG15C EC092 EJ203 GB72 HB21A JD04 JK07B JK08B JK17 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) B32B 7/12 B32B 7/12 F term (reference) 3B035 AA05 AA07 AA21 AB03 AC02 AC13 4F100 AK41 BA03 BA10A BA10C BA32 CB00 DD01A DG11A DG11B DG15C EC092 EJ203 GB72 HB21A JD04 JK07B JK08B JK17
Claims (3)
内層と、不織布を含む外層とからなるモールド成形品で
あって、内層の表地に凹凸が形成されており、内層の裏
地と外層の不織布とが点状に接着されていることを特徴
とする、前記モールド成形品。1. A molded product comprising an inner layer composed of at least a surface material and a lining material, and an outer layer containing a non-woven fabric, wherein unevenness is formed on the outer material of the inner layer, and the inner lining material and the non-woven material of the outer layer The molded article is characterized in that it is adhered in a dot shape.
性伸縮糸からなる裏地、及び表地と裏地との間に配され
る中綿を、裏地を構成する弾性伸縮糸により一体化した
伸縮性キルティング状生地であることを特徴とする、請
求項1記載のモールド成形品。2. Elasticity in which an inner layer is made up of an elastic material which is a non-elastic elastic yarn, a lining which is made of elastic elastic yarn, and a batting which is arranged between the outer material and the lining, which are integrated by the elastic elastic yarn which constitutes the lining 2. The molded product according to claim 1, which is a quilted cloth.
ことを特徴とする、請求項1又は２記載のモールド成形
品。3. The molded product according to claim 1, wherein the outer layer of the inner layer forms a body-side surface.