JP2016215501A - Method of manufacturing concrete block form and method of manufacturing concrete block - Google Patents
Method of manufacturing concrete block form and method of manufacturing concrete block Download PDFInfo
- Publication number
- JP2016215501A JP2016215501A JP2015103311A JP2015103311A JP2016215501A JP 2016215501 A JP2016215501 A JP 2016215501A JP 2015103311 A JP2015103311 A JP 2015103311A JP 2015103311 A JP2015103311 A JP 2015103311A JP 2016215501 A JP2016215501 A JP 2016215501A
- Authority
- JP
- Japan
- Prior art keywords
- concrete block
- epoxy resin
- thick film
- type epoxy
- film type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、その表面において自然的な景観を醸し出すことにより、周囲の自然環境と調和して景観を損ねることのないコンクリートブロックを作製するコンクリートブロック用型枠及びコンクリートブロックの製造方法に関する。 The present invention relates to a concrete block form for producing a concrete block that creates a natural landscape on its surface and does not impair the landscape in harmony with the surrounding natural environment, and a method for manufacturing the concrete block.
近年、その表面において自然的な景観を醸し出すことにより、周囲の自然環境と調和して景観を損ねることのないコンクリートブロックといったものが求められるようになってきていた。そこで、従来は、このようなコンクリートブロックを作製するため、コンクリートブロックの表面に凹凸模様等を形成することで、その表面において自然的な景観を醸し出すようにしたことが知られていた。 In recent years, by creating a natural landscape on its surface, concrete blocks that do not impair the landscape in harmony with the surrounding natural environment have been demanded. Therefore, conventionally, in order to produce such a concrete block, it has been known that an irregular pattern or the like is formed on the surface of the concrete block to create a natural landscape on the surface.
このような表面に凹凸模様等を形成して自然的な景観を醸し出すようにしたコンクリートブロックの製造方法としては、たとえば、特開２０００−４１４０４号公報に開示されている。 As a method for producing a concrete block in which an uneven pattern or the like is formed on such a surface so as to create a natural landscape, it is disclosed in, for example, Japanese Patent Application Laid-Open No. 2000-41404.
これは、まず、印刷版の基板を用意し、この印刷版の基板の表面に、彫刻又はエッチング又は成形法により、所望の凹形状の模様を形成する。そして、印刷版の基板の表面に形成した凹形状の模様に、合成樹脂を充填すると共に、その上にシート材を重ねて張り付け、これらが硬化した後、印刷版の基板より引き剥がすことによって、凹形状の模様に充填した合成樹脂とシート材とからなる凹凸模様付シートを成型する。この凹凸模様付シートの表面には凹凸模様が形成される。次に、このようにして成型された表面に凹凸模様を形成した凹凸模様付シートを、上面が開放した有底箱状となる鋼製のコンクリートブロック用型枠の内面である底面に取り付ける。それから、この凹凸模様付シートを取り付けた鋼製のコンクリートブロック用型枠の内部にコンクリートを流し込み、養生した後に脱型することによって、コンクリートブロックを作製する。これにより、この作製したコンクリートブロックの表面には凹凸模様付シートの凹凸模様が反転した凹凸模様が形成される。 First, a printing plate substrate is prepared, and a desired concave pattern is formed on the surface of the printing plate substrate by engraving, etching, or molding. And, while filling the concave pattern formed on the surface of the printing plate substrate with synthetic resin, overlying and pasting the sheet material thereon, after these are cured, by peeling off from the printing plate substrate, A sheet with a concavo-convex pattern made of a synthetic resin and a sheet material filled in a concave pattern is molded. An uneven pattern is formed on the surface of the sheet with the uneven pattern. Next, the sheet with a concavo-convex pattern in which a concavo-convex pattern is formed on the surface thus molded is attached to the bottom surface, which is the inner surface of a steel concrete block mold having a bottomed box shape with the top surface open. Then, concrete is poured into the steel concrete block formwork to which the uneven textured sheet is attached, cured, and then demolded to prepare a concrete block. Thereby, the uneven | corrugated pattern in which the uneven | corrugated pattern of the sheet | seat with an uneven | corrugated pattern was reversed is formed in the surface of this produced concrete block.
このようにして作製したコンクリートブロックにあっては、その表面に凹凸模様が形成されることにより、自然的な景観を醸し出すようにし、周囲の自然環境と調和して景観を損ねることのないようにしていた。 The concrete block produced in this way is designed to create a natural landscape by forming an uneven pattern on its surface, so as not to damage the landscape in harmony with the surrounding natural environment. It was.
かかる従来の表面に凹凸模様等を形成して自然的な景観を醸し出すようにしたコンクリートブロックの製造方法では、印刷版の基板に所望の凹形状の模様を形成し、そして、この印刷版の基板を用いて凹形状の模様に充填した合成樹脂とシート材とからなる凹凸模様付シートを成型し、さらに、この成型された凹凸模様付シートを鋼製のコンクリートブロック用型枠の内面に取り付け、それから、凹凸模様付シートを取り付けた鋼製のコンクリートブロック用型枠の内部にコンクリートを流し込み、その後に脱型することによって、コンクリートブロックを作製するといった非常に多くの作業が必要となることから、多くの手間と時間が掛かると共に、その作業性も悪くなることで、コンクリートブロックを短期間にかつ安価に作製するといったことができなかった。 In the conventional method for producing a concrete block in which a concavo-convex pattern or the like is formed on the conventional surface to create a natural landscape, a desired concave pattern is formed on the substrate of the printing plate, and the substrate of the printing plate A sheet with a concavo-convex pattern made of a synthetic resin and a sheet material filled into a concave pattern using, and further, this molded concavo-convex pattern sheet is attached to the inner surface of a steel concrete block formwork, Then, since concrete is poured into the steel concrete block formwork with the uneven textured sheet and then demolded, a lot of work such as making a concrete block is necessary, It takes a lot of time and effort, and the workability also deteriorates, so that concrete blocks can be made in a short time and at low cost. It was it could not be.
しかも、鋼製のコンクリートブロック用型枠に凹凸模様付シートを取り付け際、凹凸模様付シートを接着して取り付けていたが、鋼製のコンクリートブロック用型枠に接着するため、どうしても接着性が悪く、長期間使用すると鋼製のコンクリートブロック用型枠から凹凸模様付シートが剥がれてしまうといったことがあり、耐久性という点で問題があった。 In addition, when attaching a concavo-convex pattern sheet to a steel concrete block formwork, the concavo-convex pattern sheet was adhered and attached, but because it adheres to a steel concrete block formwork, the adhesion is inevitably poor. When used for a long period of time, the sheet with the uneven pattern may be peeled off from the steel concrete block mold, which has a problem in terms of durability.
また、最近では、コンクリートブロックの表面の明度を下げることで、自然的な景観を醸し出すようにするといったことも考えられていたが、従来のコンクリートブロックの製造方法によって作製したコンクリートブロックにあっては、その表面に形成する凹凸模様がある程度大きなものしか形成することができなかったため、コンクリートブロックの表面の明度を下げて自然的な景観を醸し出すといったことができなかった。 Recently, it has been considered to create a natural landscape by lowering the lightness of the surface of the concrete block. However, in the case of a concrete block produced by a conventional method for producing a concrete block, However, since only the uneven pattern formed on the surface could be formed to a certain extent, the brightness of the surface of the concrete block could not be lowered to create a natural landscape.
そこで、本発明は、これらの点に鑑み、自然的な景観を醸し出すことができ、周囲の自然環境と調和して景観を損ねることのないコンクリートブロックを、短期間にかつ安価に作製することができ、しかも、耐久性といった点で良好なものにして長期間にわたって使用することができるコンクリートブロック用型枠及びコンクリートブロックの製造方法を提供することを、その課題とする。 Therefore, in view of these points, the present invention can produce a natural landscape, and can produce a concrete block that does not impair the landscape in harmony with the surrounding natural environment in a short time and at a low cost. It is another object of the present invention to provide a concrete block formwork and a method for producing a concrete block that can be used for a long period of time with good durability.
第一の発明は、内部にコンクリートを流し込み、養生した後に脱型することにより、コンクリートブロックを作製する鋼製のコンクリートブロック用型枠において、その内面の一部又は全部に、塗装用ローラー又は刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層を設けたコンクリートブロック用型枠である。 According to a first aspect of the present invention, there is provided a steel concrete block form for producing a concrete block by pouring concrete into the interior and then removing the mold, followed by coating roller or brush on a part or all of the inner surface thereof. Is a formwork for a concrete block provided with an ultra-thick film type epoxy resin paint layer coated with an ultra-thick film type epoxy resin paint and having a fine uneven pattern or streak pattern formed on the surface thereof.
第二の発明は、第一の発明において、超厚膜形エポキシ樹脂塗料を塗装して設ける超厚膜形エポキシ樹脂塗装層を、３００μｍ以上の厚さにしたコンクリートブロック用型枠である。 A second invention is a concrete block form according to the first invention, wherein the ultra-thick film type epoxy resin coating layer provided by coating the ultra-thick film type epoxy resin paint has a thickness of 300 μm or more.
第三の発明は、第一又は第二の発明において、超厚膜形エポキシ樹脂塗料に無機粒子材を混ぜ合わせ、この無機粒子材を混ぜ合わせた超厚膜形エポキシ樹脂塗料を塗装用ローラー又は刷毛を用いて塗装するようにしたコンクリートブロック用型枠である。 According to a third invention, in the first or second invention, the ultra-thick film type epoxy resin paint is mixed with an inorganic particle material, and the ultra-thick film type epoxy resin paint mixed with the inorganic particle material is used as a coating roller or It is a concrete block form that is painted with a brush.
第四の発明は、第一乃至第三のいずれかの発明において、内面の一部又は全部における超厚膜形エポキシ樹脂塗料を塗装して超厚膜形エポキシ樹脂塗装層を設ける箇所に、この超厚膜形エポキシ樹脂塗装層を設ける前、ショットブラストによる粗面処理加工を施すようにしたコンクリートブロック用型枠である。 According to a fourth aspect of the present invention, in any one of the first to third aspects, the super thick film type epoxy resin paint is applied to a part or all of the inner surface to provide the super thick film type epoxy resin coating layer. This is a concrete block form in which a rough surface treatment is performed by shot blasting before providing an ultra-thick film type epoxy resin coating layer.
第五の発明は、鋼製のコンクリートブロック用型枠の内面の一部又は全部に、塗装用ローラー又は刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層を設けると共に、この超厚膜形エポキシ樹脂塗装層を設けたコンクリートブロック用型枠の内部にコンクリートを流し込み、養生を行った後に脱型を行うことにより、表面に細かな凹凸模様又は筋模様を形成したコンクリートブロックを作製するようにしたコンクリートブロックの製造方法である。 According to a fifth aspect of the present invention, a super-thick film type epoxy resin paint is applied to a part or all of the inner surface of a steel concrete block form using a coating roller or brush, and a fine uneven pattern or A super thick film type epoxy resin coating layer with streaks is provided, and concrete is poured into a concrete block formwork provided with this super thick film type epoxy resin coating layer. After curing, demolding is performed. By this, it is the manufacturing method of the concrete block which produced the concrete block which formed the fine uneven | corrugated pattern or the streak pattern on the surface.
第六の発明は、第五の発明において、鋼製のコンクリートブロック用型枠の内面の一部又は全部に、超厚膜形エポキシ樹脂塗料を塗装して超厚膜形エポキシ樹脂塗装層を設ける前、この超厚膜形エポキシ樹脂塗装層を設ける箇所に、ショットブラストによる粗面処理加工を施すようにしたコンクリートブロックの製造方法である。 A sixth invention is the fifth invention, wherein a super-thick film type epoxy resin coating layer is provided on a part or all of the inner surface of the steel concrete block mold by providing a super-thick film type epoxy resin coating layer. This is a method for manufacturing a concrete block in which a rough surface treatment process is performed by shot blasting at a location where this ultra-thick film type epoxy resin coating layer is provided.
本発明によれば、鋼製のコンクリートブロック用型枠において、その内面の一部又は全部に、塗装用ローラー又は刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層を設けるようにしたことで、このコンクリートブロック用型枠を用いて作製したコンクリートブロックの表面にこれらの模様が転写され、細かな凹凸模様又は筋模様を形成することができ、コンクリートブロックの表面の細かな凹凸模様又は筋模様から自然的な景観を醸し出すことができ、さらに、この細かな凹凸模様又は筋模様により、コンクリートブロックの表面の明度を下げることによっても、自然的な風合いがより一層増して、さらなる自然的な景観を醸し出すことができ、周囲の自然環境と調和して景観を損ねることのないコンクリートブロックを作製することができる。 According to the present invention, in a steel concrete block formwork, a part or all of the inner surface thereof is coated with an ultra-thick film type epoxy resin paint using a coating roller or brush, and fine irregularities are formed on the surface. By providing an ultra-thick film type epoxy resin coating layer with a pattern or streak pattern, these patterns are transferred to the surface of the concrete block made using this concrete block formwork, and a fine uneven pattern Or a streaked pattern can be formed, and a natural landscape can be created from the fine uneven pattern or the streaky pattern on the surface of the concrete block. By reducing the brightness, the natural texture can be further increased, creating a more natural landscape, and the surrounding natural environment. It can be manufactured without concrete blocks of compromising the landscape in harmony.
そして、このようなコンクリートブロック用型枠の内面の一部又は全部に、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層を設ける作業も、塗装用ローラー又は刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装するだけの手間や時間がほとんど掛からない極めて単純かつ容易な作業にすることができ、これにより、このコンクリートブロック用型枠を用いることによって、従来のような多くの手間と時間が掛かる作業が不要となり、またその作業性も向上することから、コンクリートブロックを短期間にかつ安価に作製することができる。 In addition, a part of or the entire inner surface of such a concrete block formwork is provided with an ultra-thick film type epoxy resin coating layer having a fine concavo-convex pattern or streaks formed on its surface. It is possible to make the work extremely simple and easy with little effort and time just to apply the ultra-thick film type epoxy resin paint, and by using this concrete block formwork, Such a time-consuming and time-consuming work is unnecessary, and the workability is improved, so that a concrete block can be produced in a short time and at a low cost.
また、このコンクリートブロック用型枠の内面の一部又は全部に設ける超厚膜形エポキシ樹脂塗装層にあっても、劣化しにくい高耐久性の塗料である超厚膜形エポキシ樹脂塗料を塗装して設けるようにしたことから、この超厚膜形エポキシ樹脂塗装層が剥がれてなくなるといったことを大幅に低減することができ、これにより、鋼製のコンクリートブロック用型枠の表面を保護するため、耐久性といった点で良好なものにし、コンクリートブロック用型枠として長期間にわたって使用することができる。 Also, even with the ultra-thick film type epoxy resin coating layer provided on part or all of the inner surface of the concrete block formwork, the ultra-thick film type epoxy resin paint, which is a highly durable paint that does not easily deteriorate, is applied. It is possible to greatly reduce that this ultra-thick film type epoxy resin coating layer is not peeled off, thereby protecting the surface of the steel concrete block formwork, It is good in terms of durability and can be used as a concrete block form for a long period of time.
本発明のコンクリートブロック用型枠及びコンクリートブロックの製造方法の一実施形態について説明する。 An embodiment of a concrete block mold and a method for producing a concrete block according to the present invention will be described.
なお、ここで作製するコンクリートブロックとしては、河川、ダムや湖沼等の緩傾斜面に多数敷設し、この緩傾斜面に護岸を構築するのに使用する護岸用のコンクリートブロック１であって、たとえば、図１に示すように、その全体形状を、正方形の薄厚の直方体状とするもので、その大きさを、前後長さ及び左右長さが約５００ｍｍ、高さを約１００ｍｍとする。ただし、このコンクリートブロック１については、その全体形状及び大きさは、これに限定されるものではなく、長方形、台形、三角形、六角形、あるいは円形等の直方体状とするもの等、その他のものでも良く、また、護岸用のコンクリートブロック１に限定されるものでもなく、その他のコンクリートブロックでも良い。 The concrete block produced here is a concrete block 1 for revetment that is laid on many gently inclined surfaces such as rivers, dams and lakes, and is used to construct a revetment on this gently inclined surface. As shown in FIG. 1, the overall shape is a rectangular thin rectangular parallelepiped shape, and the size is about 500 mm in the front and rear length and the left and right length, and the height is about 100 mm. However, the concrete block 1 is not limited in its overall shape and size, and may be a rectangular shape, a trapezoidal shape, a triangular shape, a hexagonal shape, a rectangular shape such as a circular shape, or the like. Moreover, it is not limited to the concrete block 1 for revetment, and other concrete blocks may be used.
コンクリートブロック用型枠について述べると、このコンクリートブロック用型枠１０としては、鋼製の型枠であって、図２、図３に示すように、正方形の板状の底面板１１と、この底面板１１の４辺に立設する４つの板状の側面板１２とから上方が開放した有底箱状となっており、底面板１１は、その大きさを、前後長さ及び左右長さが約５００ｍｍ強とする。また、４つの板状の側面板１２は、その大きさを、横の長さが約５００ｍｍ強、縦の長さが１００ｍｍ強とする。 The concrete block mold 10 will be described. The concrete block mold 10 is a steel mold, as shown in FIG. 2 and FIG. The bottom plate 11 has a bottomed box shape that is open upward from four plate-like side plates 12 standing on the four sides of the face plate 11. About 500 mm. The four plate-like side plates 12 have a horizontal length of about 500 mm and a vertical length of over 100 mm.
そして、底面板１１と４つの側面板１２にあっては、図４に示すように、それぞれ分離可能にしており、使用する際、これらを組み立てて、上方が開放した有底箱状となるコンクリートブロック用型枠１０を作るようにする。 As shown in FIG. 4, the bottom plate 11 and the four side plates 12 are separable. When used, the bottom plate 11 and the four side plates 12 are assembled to form a bottomed box-like concrete that opens upward. The block mold 10 is made.
なお、このコンクリートブロック用型枠１０については、これに限定されるものではなく、作製するコンクリートブロック１に応じた形状及び大きさのものであれば、他のものでも良い。また、１つのコンクリートブロック用型枠１０で２つのコンクリートブロック１が作製できるもの、さらには３つ以上の複数のコンクリートブロック１が作製できるものでも良い。 The concrete block mold 10 is not limited to this, and may be any other shape as long as it has a shape and size corresponding to the concrete block 1 to be produced. Moreover, the thing which can produce the two concrete blocks 1 with the one form 10 for concrete blocks, Furthermore, the thing which can produce the some 3 or more concrete block 1 may be used.
そして、このようになるコンクリートブロック用型枠１０において、その内面の一部である底面板１１の上面に、塗装用ローラー２０を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層２１を設ける。なお、この塗装用ローラー２０において、その円筒状のローラー部は、細い繊維状樹脂が絡みあって作られた多孔質形状のもの、あるいはスポンジ材料にて作られた多孔質形状のもの、あるいはその他の多孔質形状のものでも良い。ただし、円筒状のローラー部を細い繊維状樹脂が絡みあって作られた多孔質形状のものにした場合は、その他のものと比べて、一回の塗装で超厚膜形エポキシ樹脂塗料を厚膜に極めて良好に塗ることができる。 Then, in the concrete block mold 10 thus formed, the super thick film type epoxy resin paint is applied to the upper surface of the bottom plate 11 which is a part of the inner surface by using the coating roller 20, and the surface is finely coated. An ultra-thick film type epoxy resin coating layer 21 having an uneven pattern is provided. In addition, in this painting roller 20, the cylindrical roller portion has a porous shape made of entangled thin fibrous resins, a porous shape made of a sponge material, or others. The porous shape may be used. However, if the cylindrical roller part is made of a porous shape made of entangled thin fibrous resin, the thick film type epoxy resin paint is thickened by a single coating compared to other types. It can be applied very well to the film.
これについて具体的に述べると、まず、コンクリートブロック用型枠１０の内面の一部である底面板１１の上面において、超厚膜形エポキシ樹脂塗料を塗装して超厚膜形エポキシ樹脂塗装層２１を設ける前、この超厚膜形エポキシ樹脂塗装層２１を設ける箇所に、ショットブラストによる粗面処理加工を施すようにする。このショットブラストとは、粒状の投射材を底面板１１の上面に噴射して衝突させ、底面板１１の上面すなわち超厚膜形エポキシ樹脂塗装層２１を設ける箇所を粗面にするものであって、後で行う鋼製のコンクリートブロック用型枠への超厚膜形エポキシ樹脂塗料の付着を良くし、良好に塗装できるようにするための下地加工処理である。 More specifically, first, an ultra-thick film type epoxy resin paint is applied to the upper surface of the bottom plate 11 which is a part of the inner surface of the concrete block mold 10 to form an ultra-thick film type epoxy resin coating layer 21. Before the surface is provided, the rough surface processing by shot blasting is performed on the portion where the ultra-thick film type epoxy resin coating layer 21 is provided. This shot blasting is a method in which a granular projection material is sprayed onto the upper surface of the bottom plate 11 to collide with it, and the upper surface of the bottom plate 11, that is, a portion where the super thick film type epoxy resin coating layer 21 is provided is roughened. This is a ground processing for improving the adhesion of the ultra-thick film type epoxy resin paint to the steel concrete block form to be performed later, and enabling the coating to be performed satisfactorily.
その後、図５に示すように、このショットブラストによる粗面処理加工を施して粗面にした底面板１１の上面に、塗装用ローラー２０を用いて超厚膜形エポキシ樹脂塗料を塗装し、超厚膜形エポキシ樹脂塗装層２１を設ける。このとき、図６に示すように、この超厚膜形エポキシ樹脂塗装層２１の表面には塗装用ローラー２０によって生じる細かな凹凸模様が形成される。なお、この形成された細かな凹凸模様の実例については、図７に示す。 Thereafter, as shown in FIG. 5, a super-thick film type epoxy resin paint is applied to the upper surface of the bottom plate 11 which has been roughened by shot blasting using a coating roller 20. A thick film type epoxy resin coating layer 21 is provided. At this time, as shown in FIG. 6, a fine uneven pattern generated by the coating roller 20 is formed on the surface of the ultra-thick film type epoxy resin coating layer 21. An example of the fine concavo-convex pattern formed is shown in FIG.
また、超厚膜形エポキシ樹脂塗料については、エポキシ樹脂、顔料、硬化材及び溶剤を主な原料とし、ＶＯＣ（揮発性有機化合物）が低く環境に優しい塗料であって、しかも、粘性が極めて高く、一回の塗装で３００μｍ以上の厚膜に塗装することができ、省工程といった面で優れており、また、乾湿及び温度変化にも極めて強く劣化しにくい高耐久性の塗料である。なお、この超厚膜形エポキシ樹脂塗料とは、一般名称であって、たとえば、公益社団法人日本道路協会の「鋼道路橋防食便覧（平成２６年３月）」やその他のものにも一般名称として使用されている。 In addition, the ultra-thick film type epoxy resin paint is an environmentally friendly paint with a low VOC (volatile organic compound), mainly made of epoxy resin, pigment, curing material and solvent, and extremely high viscosity. It is a highly durable paint that can be applied to a thick film of 300 μm or more by a single coating, is excellent in terms of process savings, and is extremely resistant to deterioration due to dry and wet conditions and temperature. In addition, this super-thick film type epoxy resin paint is a general name, for example, “Japanese Steel Road Bridge Corrosion Handbook (March 2014)” by the Japan Road Association and other names. It is used as
また、超厚膜形エポキシ樹脂塗料を塗装して設ける超厚膜形エポキシ樹脂塗装層２１については、３００μｍ以上の厚さになるように、塗装用ローラー２０を用いて超厚膜形エポキシ樹脂塗料を塗装する。なお、この超厚膜形エポキシ樹脂塗装層２１の厚さについては、３００μｍよりも薄くても良いが、３００μｍより薄いと、コンクリートブロック用型枠１０として使用したときの耐久性といった点、また、作製したコンクリートブロック１の表面に細かな凹凸模様を良好に形成するといった点を考慮すると、３００μｍ以上の厚さにするのが好ましい。 In addition, the ultra-thick film type epoxy resin coating layer 21 provided by coating the ultra-thick film type epoxy resin paint is applied to the super thick film type epoxy resin paint by using the coating roller 20 so as to have a thickness of 300 μm or more. Paint. In addition, about the thickness of this super-thick film type epoxy resin coating layer 21, it may be thinner than 300 μm, but if it is thinner than 300 μm, the point of durability when used as a concrete block formwork 10, Considering the point that a fine uneven pattern is satisfactorily formed on the surface of the produced concrete block 1, it is preferable to set the thickness to 300 μm or more.
そして、コンクリートブロック用型枠１０の底面板１１の上面において、超厚膜形エポキシ樹脂塗料を塗装して超厚膜形エポキシ樹脂塗装層２１を設けた後、数日間静置することにより、この超厚膜形エポキシ樹脂塗装層２１を乾燥させて完全硬化させる。このようにして、コンクリートブロック用型枠１０の内面の一部である底面板１１の上面に、その表面に細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層２１を設けるようにする。 Then, on the upper surface of the bottom plate 11 of the concrete block mold 10, after applying an ultra-thick film type epoxy resin paint and providing an ultra-thick film type epoxy resin coating layer 21, this is left to stand for several days. The ultra-thick film type epoxy resin coating layer 21 is dried and completely cured. In this way, the super thick film type epoxy resin coating layer 21 having a fine uneven pattern formed on the surface thereof is provided on the upper surface of the bottom plate 11 which is a part of the inner surface of the concrete block mold 10.
また、コンクリートブロック用型枠１０の内面の一部である底面板１１の上面に、超厚膜形エポキシ樹脂塗料を塗装するとき、塗装用ローラー２０を用いていたが、この代わりに、刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装しても良く、このように刷毛を用いた場合、図８に示すように、超厚膜形エポキシ樹脂塗装層２１の表面には刷毛によって生じる筋模様が形成される。 In addition, when the super-thick film type epoxy resin paint is applied to the upper surface of the bottom plate 11 which is a part of the inner surface of the concrete block mold 10, the painting roller 20 was used. If the brush is used in this way, as shown in FIG. 8, the surface of the ultra-thick film type epoxy resin coating layer 21 has streaks caused by the brush. Is formed.
なお、コンクリートブロック用型枠１０において、内面の一部である底面板１１の上面に、超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層２１を設けていたが、ここだけに限定されるものではなく、この底面板１１の上面と共に４つの側面板１２の内側の面にも、超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層２１を設けるように、すなわち、コンクリートブロック用型枠１０の内面の全部に、超厚膜形エポキシ樹脂塗装層２１を設けるようにしても良い。 In the concrete block mold 10, an ultra-thick film in which a super-thick film type epoxy resin paint is applied to the upper surface of the bottom plate 11 which is a part of the inner surface, and a fine uneven pattern or a streak pattern is formed on the surface. The epoxy resin coating layer 21 is provided. However, the present invention is not limited to this. The super-thick film epoxy resin paint is applied to the inner surface of the four side plates 12 as well as the upper surface of the bottom plate 11. Then, an ultra-thick film type epoxy resin coating layer 21 having fine irregularities or streaks formed on the surface thereof is provided, that is, the entire inner surface of the concrete block mold 10 is coated with an ultra-thick film type epoxy resin. The layer 21 may be provided.
次に、このコンクリートブロック用型枠１０を用いたコンクリートブロック１の製造方法について述べると、前述したように、その内面の一部である底面板１１の上面に、塗装用ローラー２０を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層２１を設け、そして、この超厚膜形エポキシ樹脂塗装層２１を設けた底面板１１と、４つの側面板１２を組み立てて、上方が開放した有底箱状となるコンクリートブロック用型枠１０を作る。 Next, the manufacturing method of the concrete block 1 using the concrete block form 10 will be described. As described above, the superposition of the bottom plate 11 which is a part of the inner surface of the concrete block 1 is performed using the coating roller 20. A thick film type epoxy resin coating is applied, and a super thick film type epoxy resin coating layer 21 is formed on the surface of which a fine uneven pattern is formed. Then, the four side plates 12 are assembled to form a concrete block mold 10 having a bottomed box shape with the upper part opened.
それから、この上方が開放した有底箱状となるコンクリートブロック用型枠１０において、図９（ａ）に示すように、その内部にコンクリートを流し込み、図９（ｂ）に示すように、コンクリートブロック用型枠１０の上端までコンクリートを流し込む。 Then, in the concrete block mold 10 having a bottomed box shape with the upper part opened, concrete is poured into the concrete block as shown in FIG. 9 (a), and the concrete block as shown in FIG. 9 (b). Concrete is poured to the upper end of the formwork 10.
そして、コンクリートブロック用型枠１０の上端までコンクリートを流し込んだ後、図９（ｃ）に示すように、振動機を用い、この振動機のバイブレーション作用によりコンクリートの締固めを行うと共に、コテならしにより表面の仕上げ等も行う。 Then, after pouring the concrete to the upper end of the concrete block mold 10, as shown in FIG. 9 (c), using a vibrator, the concrete is compacted by the vibration action of the vibrator, and the iron is leveled. To finish the surface.
その後、所定の期間、養生を行う。これは、蒸気による養生を行い、コンクリートの硬化を促進する。 Thereafter, curing is performed for a predetermined period. This cures with steam and promotes hardening of the concrete.
そして、この養生を行った後に脱型を行う。この脱型としては、まず、図１０（ｄ）に示すように、コンクリートブロック用型枠１０の４つの側面板１２を外し、その後、図１０（ｅ）に示すように、コンクリートブロック１を持ち上げて、コンクリートブロック用型枠１０の底面板１１より外すことにより、コンクリートブロック用型枠１０よりコンクリートブロック１を取り外すものである。そして、持ち上げたコンクリートブロック１を上下反転させて、図１０（ｆ）に示すように、地面に載置する。 And after performing this curing, demolding is performed. As this demolding, first, as shown in FIG. 10 (d), the four side plates 12 of the concrete block mold 10 are removed, and then the concrete block 1 is lifted as shown in FIG. 10 (e). The concrete block 1 is removed from the concrete block mold 10 by removing it from the bottom plate 11 of the concrete block mold 10. Then, the lifted concrete block 1 is turned upside down and placed on the ground as shown in FIG.
これによって、このコンクリートブロック１の表面である上面には、コンクリートブロック用型枠１０の底面板１１の上面に設けた超厚膜形エポキシ樹脂塗装層２１の表面に形成した細かな凹凸模様が転写されることで、表面に細かな凹凸模様又は筋模様を形成したコンクリートブロック１を作製することができる。 As a result, a fine uneven pattern formed on the surface of the super-thick film type epoxy resin coating layer 21 provided on the upper surface of the bottom plate 11 of the concrete block mold 10 is transferred to the upper surface which is the surface of the concrete block 1. By doing so, the concrete block 1 which formed the fine uneven | corrugated pattern or the streak pattern on the surface can be produced.
このようにして作製したコンクリートブロック１にあっては、表面に細かな凹凸模様又は筋模様が形成されることで、この細かな凹凸模様又は筋模様から自然的な景観を醸し出すことができると共に、細かな凹凸模様又は筋模様を形成することによって、その表面の明度を下げることもでき、このように表面の明度を下げることにより、自然的な風合いがより一層増して、さらなる自然的な景観を醸し出すことができる。 In the concrete block 1 produced in this way, a fine concavo-convex pattern or streak pattern is formed on the surface, so that a natural landscape can be brought out from this fine concavo-convex pattern or streak pattern, The surface brightness can be lowered by forming fine uneven patterns or streaks, and by reducing the surface brightness in this way, the natural texture is further increased and a further natural landscape is created. It can be brewed.
以上のように、自然的な景観を醸し出すようにしたコンクリートブロック１を作製するためのコンクリートブロック用型枠１０にあっては、その内面の一部又は全部に、塗装用ローラー２０又は刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層２１を設けるようにするが、このときの作業としては、塗装用ローラー２０又は刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装するだけの手間や時間がほとんど掛からない極めて単純かつ容易な作業にすることができ、これにより、このコンクリートブロック用型枠１０を用いることによって、コンクリートブロック１を短期間にかつ安価に作製することができる。 As described above, in the concrete block mold 10 for producing the concrete block 1 that creates a natural landscape, the coating roller 20 or the brush is used for a part or all of the inner surface thereof. Then, an ultra-thick film type epoxy resin paint is applied, and an ultra-thick film type epoxy resin coating layer 21 having fine irregularities or streaks formed on its surface is provided. It is possible to make the work very simple and easy with little effort and time to apply the ultra-thick film type epoxy resin paint using the roller 20 or the brush, and thus the concrete block mold 10 is used. Thus, the concrete block 1 can be manufactured in a short time and at a low cost.
また、鋼製のコンクリートブロック用型枠１０に塗装して超厚膜形エポキシ樹脂塗装層２１を設けるための塗料として、粘性が極めて高く、乾湿及び温度変化にも極めて強く劣化しにくい高耐久性の塗料である超厚膜形エポキシ樹脂塗料を用いたことで、この超厚膜形エポキシ樹脂塗料が剥がれたりあるいは劣化したりして、コンクリートブロック用型枠１０の内面の一部又は全部に設けた超厚膜形エポキシ樹脂塗装層２１がなくなるといったことを大幅に低減することができ、これにより、コンクリートブロック用型枠１０における耐久性といった点で良好なものにし、コンクリートブロック用型枠１０として長期間にわたって使用することができ、しかも、そのメンテナンスの面でも極めて容易なものにすることができる。 In addition, as a paint for coating the steel concrete block mold 10 to provide the super-thick film type epoxy resin coating layer 21, it has a very high viscosity and is extremely durable against drought and humidity and temperature changes. By using the ultra-thick film type epoxy resin paint, which is a paint of the above, the super thick film type epoxy resin paint is peeled off or deteriorated, and is provided on a part or all of the inner surface of the concrete block mold 10. It is possible to greatly reduce the absence of the ultra-thick film type epoxy resin coating layer 21, thereby improving the durability of the concrete block mold 10, and as a concrete block mold 10. It can be used over a long period of time, and it can be made extremely easy in terms of maintenance.
また、コンクリートブロック用型枠１０における超厚膜形エポキシ樹脂塗装層２１の表面に形成する細かな凹凸模様又は筋模様については、塗装用ローラー２０又は刷毛を用いて作業者が超厚膜形エポキシ樹脂塗料を塗装することから、塗装する際の作業者の手加減により多種多様な凹凸模様又は筋模様を形成することができ、コンクリートブロック用型枠１０を用いて作製するコンクリートブロック１の表面にも、多種多様な凹凸模様又は筋模様を形成することができる。これにより、それぞれの現場に応じてコンクリートブロック１の表面の細かな凹凸模様又は筋模様を変更することも可能となり、それぞれの現場において最も適した形のコンクリートブロック１といったものを作製することができる。 Moreover, about the fine uneven | corrugated pattern or streaks formed in the surface of the ultra-thick film type epoxy resin coating layer 21 in the mold 10 for concrete blocks, an operator uses the roller 20 for painting or a brush, and an operator uses an ultra-thick film type epoxy. Since the resin paint is applied, a wide variety of uneven patterns or streaks can be formed by the operator's control when applying the paint, and also on the surface of the concrete block 1 produced using the concrete block mold 10. A wide variety of concavo-convex patterns or streaks can be formed. Thereby, it becomes possible to change the fine uneven pattern or the streaks on the surface of the concrete block 1 according to each site, and the concrete block 1 having the most suitable shape in each site can be produced. .
次に、本発明のコンクリートブロック用型枠の別の例について説明すると、このコンクリートブロック用型枠は、前述のものと同様、底面板１１と４つの側面板１２とから上方が開放した有底箱状となり、その内面の一部である底面板１１の上面に、塗装用ローラー２０を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層２１を設けるが、このとき、塗装する超厚膜形エポキシ樹脂塗料において、無機粒子材を混ぜ合わせて使用するようにする。 Next, another example of the concrete block mold according to the present invention will be described. The concrete block mold has a bottom with an open top from the bottom plate 11 and the four side plates 12 as described above. Ultra-thick film form that is box-shaped and is coated with an ultra-thick film type epoxy resin paint on the upper surface of the bottom plate 11 that is a part of its inner surface using a coating roller 20 to form a fine uneven pattern on the surface. The epoxy resin coating layer 21 is provided. At this time, in the ultra-thick film type epoxy resin paint to be coated, inorganic particle materials are mixed and used.
この無機粒子材としては、たとえば、硅砂等の砂であり、その平均粒度を０．３〜１．２ｍｍとするものである。そして、この無機粒子材である砂を超厚膜形エポキシ樹脂塗料に混ぜ合わせる際の混合率は、質量比で、超厚膜形エポキシ樹脂塗料１．０に対して砂０．６〜１．０である。なお、無機粒子材は、砂に限定されるものではなく、粒状のガラスや鉄、アルミニウム等の他のものでも良い。 As this inorganic particle material, for example, sand such as cinnabar sand, the average particle size is 0.3 to 1.2 mm. And the mixing rate at the time of mixing the sand which is this inorganic particle material with an ultra-thick film type epoxy resin paint is 0.6-1. 0. The inorganic particle material is not limited to sand, but may be other materials such as granular glass, iron, and aluminum.
そして、このように超厚膜形エポキシ樹脂塗料に無機粒子材である砂を混ぜ合わせと、粘性がさらに高くなり、これにより、鋼製のコンクリートブロック用型枠１０の内面の一部に、砂を混ぜ合わせた超厚膜形エポキシ樹脂塗料を塗装用ローラー２０又は刷毛を用いて塗装し、超厚膜形エポキシ樹脂塗装層２１を設けると、この超厚膜形エポキシ樹脂塗装層２１の表面に尖った細かな凹凸模様が形成される。なお、この形成された尖った細かな凹凸模様の実例については、図１１に示す。 And, when sand, which is an inorganic particle material, is mixed with the ultra-thick film type epoxy resin paint in this way, the viscosity is further increased, so that a part of the inner surface of the steel concrete block mold 10 is sanded. When a super-thick film type epoxy resin coating layer 21 is provided by coating a super-thick film type epoxy resin paint using a coating roller 20 or a brush, the surface of the super-thick film type epoxy resin coating layer 21 is provided. A sharp fine uneven pattern is formed. Note that an example of the formed fine fine uneven pattern is shown in FIG.
これによっても、このコンクリートブロック１の表面には、コンクリートブロック用型枠１０の底面板１１の上面に設けた超厚膜形エポキシ樹脂塗装層２１の表面に形成した尖った細かな凹凸模様が転写されることで、表面に尖った細かな凹凸模様又は筋模様を形成したコンクリートブロック１を作製することができる。 Also by this, a sharp fine uneven pattern formed on the surface of the super-thick film type epoxy resin coating layer 21 provided on the upper surface of the bottom plate 11 of the concrete block mold 10 is transferred to the surface of the concrete block 1. By doing so, the concrete block 1 which formed the fine uneven | corrugated pattern or the streak pattern sharpened on the surface is producible.
１…コンクリートブロック、１０…コンクリートブロック用型枠、１１…底面板、１２…側面板、２０…塗装用ローラー、２１…超厚膜形エポキシ樹脂塗装層 DESCRIPTION OF SYMBOLS 1 ... Concrete block, 10 ... Concrete block formwork, 11 ... Bottom plate, 12 ... Side plate, 20 ... Paint roller, 21 ... Super-thick film type epoxy resin coating layer
本発明は、その表面において自然的な景観を醸し出すことにより、周囲の自然環境と調和して景観を損ねることのないコンクリートブロックを作製するコンクリートブロック用型枠の製造方法及びコンクリートブロックの製造方法に関する。 The present invention relates to a method for manufacturing a concrete block mold and a method for manufacturing a concrete block, which creates a concrete block in harmony with the surrounding natural environment by producing a natural landscape on the surface thereof and does not impair the landscape. .
そこで、本発明は、これらの点に鑑み、自然的な景観を醸し出すことができ、周囲の自然環境と調和して景観を損ねることのないコンクリートブロックを、短期間にかつ安価に作製することができ、しかも、耐久性といった点で良好なものにして長期間にわたって使用することができるコンクリートブロック用型枠の製造方法及びコンクリートブロックの製造方法を提供することを、その課題とする。 Therefore, in view of these points, the present invention can produce a natural landscape, and can produce a concrete block that does not impair the landscape in harmony with the surrounding natural environment in a short time and at a low cost. Further, it is an object of the present invention to provide a method for manufacturing a concrete block mold and a method for manufacturing a concrete block that can be used for a long period of time with good durability.
第一の発明は、内部にコンクリートを流し込み、養生した後に脱型することにより、コンクリートブロックを作製するようになる鋼製のコンクリートブロック用型枠の製造方法において、コンクリートブロック用型枠の内面の一部又は全部に、多孔質形状のローラー部を有した塗装用ローラーを用いて手作業により超厚膜形エポキシ樹脂塗料を塗装し、その表面に塗装用ローラーによって生じる細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層を設けるコンクリートブロック用型枠の製造方法である。 The first invention, pouring concrete therein, by demolding after curing, in the manufacturing method of the steel concrete blocks for formwork made as to prepare a concrete block, the inner surface of the concrete blocks for formwork Part or all of the surface was coated with an ultra-thick epoxy resin coating by hand using a coating roller having a porous roller portion, and a fine uneven pattern generated by the coating roller was formed on the surface. a method for producing a concrete block mold frame Ru provided super thick film type epoxy resin paint layer.
第二の発明は、第一の発明において、超厚膜形エポキシ樹脂塗料を塗装して設ける超厚膜形エポキシ樹脂塗装層を、３００μｍ以上の厚さにするコンクリートブロック用型枠の製造方法である。 The second invention is a method for producing a concrete block mold according to the first invention, wherein the super thick film type epoxy resin coating layer provided by coating the super thick film type epoxy resin paint is made to have a thickness of 300 μm or more. is there.
第三の発明は、第一又は第二の発明において、超厚膜形エポキシ樹脂塗料に無機粒子材を混ぜ合わせ、この無機粒子材を混ぜ合わせた超厚膜形エポキシ樹脂塗料を塗装用ローラーを用いて塗装するコンクリートブロック用型枠の製造方法である。 According to a third invention, in the first or second invention, the super thick film type epoxy resin paint is mixed with an inorganic particle material, and the super thick film type epoxy resin paint mixed with the inorganic particle material is coated with a roller for painting. It is the manufacturing method of the form for concrete blocks used and painted.
第四の発明は、第一乃至第三のいずれかの発明において、内面の一部又は全部における超厚膜形エポキシ樹脂塗料を塗装して超厚膜形エポキシ樹脂塗装層を設ける箇所に、この超厚膜形エポキシ樹脂塗装層を設ける前、ショットブラストによる粗面処理加工を施すコンクリートブロック用型枠の製造方法である。 According to a fourth aspect of the present invention, in any one of the first to third aspects, the super thick film type epoxy resin paint is applied to a part or all of the inner surface to provide the super thick film type epoxy resin coating layer. This is a method for producing a concrete block mold which is subjected to rough surface treatment by shot blasting before providing an ultra-thick film type epoxy resin coating layer.
第五の発明は、鋼製のコンクリートブロック用型枠の内面の一部又は全部に、多孔質形状のローラー部を有した塗装用ローラーを用いて手作業により超厚膜形エポキシ樹脂塗料を塗装し、その表面に塗装用ローラーによって生じる細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層を設けると共に、この超厚膜形エポキシ樹脂塗装層を設けるコンクリートブロック用型枠の内部にコンクリートを流し込み、養生を行った後に脱型を行うことにより、表面に細かな凹凸模様を形成したコンクリートブロックを作製するコンクリートブロックの製造方法である。 The fifth aspect of the invention is that a super-thick film type epoxy resin paint is manually applied to a part or all of an inner surface of a steel concrete block formwork using a coating roller having a porous roller portion. and, the fine uneven pattern was formed super thick film type epoxy resin coated layer provided with that caused by paint roller to the surface, the concrete inside the ultra-thick film-type epoxy resin paint layer concrete blocks for formwork Ru provided This is a method for producing a concrete block in which a concrete block having a fine concavo-convex pattern formed on the surface is produced by performing mold removal after pouring and curing.
第六の発明は、第五の発明において、鋼製のコンクリートブロック用型枠の内面の一部又は全部に、超厚膜形エポキシ樹脂塗料を塗装して超厚膜形エポキシ樹脂塗装層を設ける前、この超厚膜形エポキシ樹脂塗装層を設ける箇所に、ショットブラストによる粗面処理加工を施すコンクリートブロックの製造方法である。 A sixth invention is the fifth invention, wherein a super-thick film type epoxy resin coating layer is provided on a part or all of the inner surface of the steel concrete block mold by providing a super-thick film type epoxy resin coating layer. Previously, it is a method for manufacturing a concrete block in which a rough surface treatment process is performed by shot blasting at a place where the super thick film type epoxy resin coating layer is provided.
本発明によれば、コンクリートブロック用型枠の製造方法において、コンクリートブロック用型枠の内面の一部又は全部に、多孔質形状のローラー部を有した塗装用ローラーを用いて手作業により超厚膜形エポキシ樹脂塗料を塗装し、その表面に塗装用ローラーによって生じる細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層を設けるようにしたことで、このコンクリートブロック用型枠を用いて作製したコンクリートブロックの表面にこれらの模様が転写され、細かな凹凸模様を形成することができ、コンクリートブロックの表面の細かな凹凸模様から自然的な景観を醸し出すことができ、さらに、この細かな凹凸模様により、コンクリートブロックの表面の明度を下げることによっても、自然的な風合いがより一層増して、さらなる自然的な景観を醸し出すことができ、周囲の自然環境と調和して景観を損ねることのないコンクリートブロックを作製することができる。 According to the present invention, in the method for manufacturing a concrete block formwork , a part of or the entire inner surface of the concrete block formwork is manually thickened by using a painting roller having a porous roller portion. Fabricated using this concrete block form by coating a film-type epoxy resin paint and providing an ultra-thick film-type epoxy resin coating layer on the surface with a fine uneven pattern generated by a painting roller. These patterns are transferred to the surface of the concrete block, and a fine uneven pattern can be formed, and a natural landscape can be created from the fine uneven pattern on the surface of the concrete block. By reducing the lightness of the concrete block surface due to the pattern, the natural texture is further increased. Can strike a natural landscape, can be manufactured that no concrete blocks damaging the landscape in harmony with the surrounding natural environment.
そして、このようなコンクリートブロック用型枠の内面の一部又は全部に、その表面に細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層を設ける作業も、多孔質形状のローラー部を有した塗装用ローラーを用いて手作業により超厚膜形エポキシ樹脂塗料を塗装するだけの手間や時間がほとんど掛からない極めて単純かつ容易な作業にすることができ、これにより、このコンクリートブロック用型枠を用いることによって、従来のような多くの手間と時間が掛かる作業が不要となり、またその作業性も向上することから、コンクリートブロックを短期間にかつ安価に作製することができる。 In addition, the work of providing an ultra-thick film type epoxy resin coating layer having a fine concavo-convex pattern on a part or all of the inner surface of such a concrete block formwork also has a porous roller portion. With this coating roller, it can be made extremely simple and easy with little effort and time to apply the ultra-thick film type epoxy resin paint by hand. By using this, a lot of time-consuming and time-consuming work as in the prior art becomes unnecessary, and the workability is improved, so that a concrete block can be produced in a short time and at a low cost.
本発明のコンクリートブロック用型枠の製造方法及びコンクリートブロックの製造方法の一実施形態について説明する。 An embodiment of a method for producing a concrete block mold and a method for producing a concrete block according to the present invention will be described.
コンクリートブロック用型枠１０の製造方法は、コンクリートブロック用型枠１０の内面の一部である底面板１１の上面に、塗装用ローラー２０を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層２１を設ける。なお、この塗装用ローラー２０において、その円筒状のローラー部は、細い繊維状樹脂が絡みあって作られた多孔質形状のもの、あるいはスポンジ材料にて作られた多孔質形状のもの、あるいはその他の多孔質形状のものでも良い。ただし、円筒状のローラー部を細い繊維状樹脂が絡みあって作られた多孔質形状のものにした場合は、その他のものと比べて、一回の塗装で超厚膜形エポキシ樹脂塗料を厚膜に極めて良好に塗ることができる。 The manufacturing method of the concrete block mold 10 is to apply an ultra-thick film type epoxy resin paint on the upper surface of the bottom plate 11 which is a part of the inner surface of the concrete block mold 10 by using a coating roller 20. An ultra-thick film type epoxy resin coating layer 21 having a fine uneven pattern formed on the surface is provided. In addition, in this painting roller 20, the cylindrical roller portion has a porous shape made of entangled thin fibrous resins, a porous shape made of a sponge material, or others. The porous shape may be used. However, if the cylindrical roller part is made of a porous shape made of entangled thin fibrous resin, the thick film type epoxy resin paint is thickened by a single coating compared to other types. It can be applied very well to the film.
以上のように、自然的な景観を醸し出すようにしたコンクリートブロック１を作製するためのコンクリートブロック用型枠１０の製造方法にあっては、コンクリートブロック用型枠１０の内面の一部又は全部に、塗装用ローラー２０又は刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層２１を設けるようにするが、このときの作業としては、塗装用ローラー２０又は刷毛を用いて手作業により超厚膜形エポキシ樹脂塗料を塗装するだけの手間や時間がほとんど掛からない極めて単純かつ容易な作業にすることができ、これにより、このコンクリートブロック用型枠１０を用いることによって、コンクリートブロック１を短期間にかつ安価に作製することができる。 As mentioned above, in the manufacturing method of the concrete block mold 10 for producing the concrete block 1 that brings out a natural landscape, a part or all of the inner surface of the concrete block mold 10 is provided. The super thick film type epoxy resin paint is applied by using the painting roller 20 or the brush, and the super thick film type epoxy resin coating layer 21 in which a fine uneven pattern or a streak pattern is formed on the surface is provided. As the work at this time, it can be an extremely simple and easy work that takes almost no time and effort to apply the ultra-thick film type epoxy resin paint manually by using the painting roller 20 or the brush, Thereby, the concrete block 1 can be produced in a short time and at low cost by using the form 10 for the concrete block.
次に、本発明のコンクリートブロック用型枠の製造方法の別の例について説明すると、このコンクリートブロック用型枠は、前述のものと同様、底面板１１と４つの側面板１２とから上方が開放した有底箱状となり、その内面の一部である底面板１１の上面に、塗装用ローラー２０を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様を形成した超厚膜形エポキシ樹脂塗装層２１を設けるが、このとき、塗装する超厚膜形エポキシ樹脂塗料において、無機粒子材を混ぜ合わせて使用するようにする。 Next, another example of the method for producing a concrete block mold according to the present invention will be described. The concrete block mold is open upward from the bottom plate 11 and the four side plates 12 as described above. A super-thick film type epoxy resin paint is applied to the upper surface of the bottom plate 11 which is a part of the inner surface of the bottom plate 11 using a coating roller 20 to form a fine uneven pattern on the surface. A thick film type epoxy resin coating layer 21 is provided. At this time, in the super thick film type epoxy resin paint to be coated, inorganic particle materials are mixed and used.
Claims (6)
その内面の一部又は全部に、塗装用ローラー２０又は刷毛を用いて超厚膜形エポキシ樹脂塗料を塗装し、その表面に細かな凹凸模様又は筋模様を形成した超厚膜形エポキシ樹脂塗装層２１を設けたことを特徴とするコンクリートブロック用型枠。 In the concrete block form made of steel for producing the concrete block 1 by pouring concrete into the interior and removing the mold after curing,
An ultra-thick film type epoxy resin coating layer in which a fine uneven pattern or streaks are formed on the surface of a part or all of the inner surface by applying a super-thick film type epoxy resin paint using a painting roller 20 or a brush. 21. A concrete block formwork characterized by comprising 21.
Before the super-thick film type epoxy resin coating layer 21 is applied to a part or all of the inner surface of the steel concrete block mold 10 to provide the super-thick film type epoxy resin coating layer 21, this super thick film type epoxy resin coating is applied. 6. The method for producing a concrete block according to claim 5, wherein a rough surface treatment by shot blasting is performed at a place where the layer 21 is provided.